Patent Application
20080105042
Dip-Pen Nanolithographic® (DPN)® printing has been developed in various embodiments as a scanning probe-based technique that uses, at least in some embodiments, a coated sharp tip such as an atomic force microscope (AFM) tip to pattern surfaces on, for example, the sub-50 nm to many micrometer length scale (see, for example, Piner et al. Science 283, 661-663 (1999)). This novel printing technique in its various embodiments can combine soft matter compatibility with the high resolution of scanning probe and AFM methods, thereby affording unique opportunities to use micro- and nano-patterned substrates in a variety of fields ranging from molecular electronics to biomedicine. However, an obstacle in commercially utilizing DPN printing for some applications has been its relatively low throughput (see, for example, Hong et al. Science 288, 1808-1811 (2000); Salaita et al. Small 1, 940-945 (2005)), a limitation associated with the field of scanning probe lithography in general (see, for example, Gates et al. Chem. Rev. 105, 1171-1196 (2005); Tseng et al., J. Vac. Sci. & Tech. B 23, 877-894 (2005)). In particular, the DPN method is generally used as a serial method rather than a parallel method, and the exponential complexity and cost arising from individually addressed feedback systems can constrain its accessibility and the rate of patterning. Therefore, a commercial need exists to improve throughput of the DPN method while maintaining its simplicity.
In many cases, the lithography has been to date carried out with one pen on one instrument to transfer a patterning compound or material to the surface. However, one approach has been to use multiple pen systems wherein multiple pens operate in parallel on one instrument. For example, WO 00/41213 to Mirkin et al. describes use of a plurality of tips with a single device, referring to U.S. Pat. No. 5,666,190 to Quate et al. (Stanford) for descriptions of cantilever arrays and nanolithographic application. In addition, WO 01/91855 to Mirkin et al. describes working examples with a plurality of tips, wherein a linear array of eight tips were obtained from a larger wafer block of tips and affixed to a ceramic tip carrier and mounted to an AFM tip holder with epoxy glue.
Salatia et al. Small, 2005, 1, No. 10, 940-945 describe parallel printing with 250 pen arrays, 26 pen arrays, and blocks of 26 pen arrays. U.S. Pat. No. 6,642,129 to Liu et al. describes parallel individually addressable probes for nanolithography including linear arrays and two dimensional arrays. The review by Ginger et al. Angew. Chem. Int. Ed. 43, 30-45 (2004)) describes 10,000 pen systems.
Massively parallel nanoarray platforms have been noted including a system with 1.2 million pens per four inch diameter wafer. See, for example, Demers et al., Genetic Engineering News, vol. 23, no. 15, Sep. 1, 2003, 32.
Parallel probes have also been developed by IBM. See for example, Vettiger et al., IBM J. Res. Dev. 2000, 44, 323; King et al., J. Microelectromech. Syst. 2002, 11, 765. See also U.S. Pat. No. 5,835,477 to Binnig et al.
However, a need yet exists to improve this approach in view of, for example, the difficulties associated with fabricating large numbers of pens in a confined space including in two dimensional arrays and in adapting the pens to a larger or customized instrument to control the printing process. For example, leveling and alignment of massive numbers of cantilevers and tips is an engineering challenge. The pens must be efficiently produced so that as many of the pens as possible are usable. Fabrication should be convenient, and the pens should be robust for commercial use with a variety of patterning compounds and materials. High rates of patterning structures, including nanostructures, are needed at high resolution and registration. While multiple pen systems have been used for patterning, the number of dots generated by contact has typically been the same as the number of pens. Otherwise, no registration exists between the two sets of dots. A need exists to better demonstrate the writing capabilities of large pen systems including better registration and alignment.
The present invention comprises a plurality of different embodiments.
For example, one embodiment comprises a two-dimensional array of a plurality of cantilevers, the cantilevers comprising tips at the cantilever ends, wherein the array is adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface.
Another embodiment comprises an article comprising: (i) a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers extending from the base row, wherein each of the cantilevers comprise tips at the cantilever end away from the base row, wherein the array is adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface; and (ii) a support for the array.
Another embodiment comprises an article comprising: (i) a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers extending from the base row, wherein each of the cantilevers comprise tips at the cantilever end away from the base row, wherein the array is adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface.
In another embodiment, the invention provides an article comprising: a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers, wherein each of the cantilevers comprise tips at the cantilever end away from the base, and wherein the tips have an apex height relative to the cantilever of at least, for example, four microns, and a support for the array.
Another embodiment provides an article comprising: a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers, wherein each of the cantilevers comprise tips at the cantilever end away from the base, and wherein the tips are coated with metal on the tip side of the cantilever and the cantilevers are bent at an angle of at least, for example, 10° from their base.
In another embodiment, the invention provides, for example, a method of making an article, wherein the article comprises a two-dimensional array of a plurality of cantilevers, and a support for the array, the method comprising: (i) forming a two dimensional array comprising a plurality of cantilevers comprising tips at their ends, wherein the cantilevers are supported on a sacrificial support structure; (ii) forming an array support comprising a plurality of base rows which are adapted for bonding to the two dimensional array comprising a plurality of cantilevers; (iii) bonding the cantilevers to the base rows; and (iv) removing the support structure to release the cantilevers and form the array.
Still further, another embodiment is a method comprising (1) micromachining a two dimensional array of cantilevers wherein the cantilevers are adapted to bond with a device which both supports the cantilevers and can also couple the cantilevers to an instrument for motion, and (2) bonding the cantilevers to the device.
Also provided are instruments comprising the two dimensional arrays and support structures and methods of building and using the instruments, including for fabrication of micron-scale and nanometer scale structures.
Also provided are patterned substrates made from the arrays, devices, and instruments described herein.
Also provided are methods for fast patterning of nanostructures including, for example, at least 100,000 or at least 1,000,000 nanostructures per minute.
In a preferred embodiment, a solution is provided to the throughput limitation through the use of novel 55,000-pen two-dimensional arrays in the context of parallel DPN printing experiments for patterning, for example, gold substrates with sub-100 nm resolution over large, square centimeter areas.
This new approach to parallel scanning probe lithography over large areas can be contrasted with the work of others, which has focused on the production of linear and two-dimensional cantilever arrays with independent feedback systems, for the controlled oxidation (see, for example, Minne et al. J. Vac. Sci. & Tech. B 14, 2456-2461 (1996); Minne et al. Appl. Phys. Lett. 73, 1742-1744 (1998)) or melting of an underlying substrate (see, for example, Vettiger et al. IEEE Trans. Nanotechnology 1, 39-55 (2002)).
Notably, if feedback is not used, the lack of feedback systems coupled with the ability to pattern a surface with molecule-based inks can make this massively parallel DPN capability highly accessible and attractive for high throughput nanofabrication experiments and commercialization involving, for example, both soft organic and hard inorganic materials. It can be particularly useful, for example, for fabricating combinatorial libraries of structures and duplicates of a desired nanostructure or particular type of nanopatterned substrate.
References will be made in detail to the preferred embodiments, examples of which are illustrated in the accompanying drawings. While the many facets of the invention will be described in conjunction with the preferred embodiments, it will be understood that they are not intended to limit the invention to those embodiments. On the contrary, the invention is intended to cover alternatives, modifications and equivalents, which may be included within the spirit and scope of the invention as defined by the appended claims and equivalents thereof.
Priority U.S. provisional application Ser. No. 60/792,950 filed Apr. 19, 2006 to Mirkin et al. is hereby incorporated by reference.
For practice of the various embodiments described herein, lithography, microlithography, and nanolithography instruments, pen arrays, active pens, passive pens, inks, patterning compounds, kits, ink delivery, software, and accessories for direct-write printing and patterning can be obtained from Nanolnk, Inc., Chicago, Ill. Software includes INKCAD software (Nanolnk, Chicago, Ill.), providing user interface for lithography design and control. E-Chamber can be used for environmental control. Dip Pen Nanolithography™ and DPN™ are trademarks of Nanolnk, Inc.
The following patents and co-pending applications related to direct-write printing with use of cantilevers, tips, and patterning compounds are hereby incorporated by reference in their entirety and can be used in the practice of the various embodiments described herein, including inks, patterning compounds, software, ink delivery devices, and the like:
All references cited in 1-20 above are incorporated by reference and the teachings therein can be adapted for use with the various embodiments described herein.
DPN methods are also described in Ginger et al., “The Evolution of Dip-Pen Nanolithography,” Angew. Chem. Int. Ed. 2004, 43, 30-45, including description of high-throughput parallel methods.
Direct write methods, including DPN printing and pattern transfer methods, are described in for example Direct-Write Technologies, Sensors, Electronics, and Integrated Power Sources, Pique and Chrisey (Eds), 2002.
The direct-write nanolithography instruments and methods described herein are particularly of interest for use in preparing bioarrays, nanoarrays, and microarrays based on peptides, proteins, nucleic acids, DNA, RNA, viruses, biomolecules, and the like. See, for example, U.S. Pat. No. 6,787,313 for mass fabrication of chips and libraries; U.S. Pat. No. 5,443,791 for automated molecular biology laboratory with pipette tips; U.S. Pat. No. 5,981,733 for apparatus for the automated synthesis of molecular arrays in pharmaceutical applications. Combinatorial arrays can be prepared. See also, for example, U.S. Pat. Nos. 7,008,769; 6,573,369; and 6,998,228 to Henderson et al.
Scanning probe microscopy is reviewed in Bottomley, Anal. Chem., 1998, 70, 425R-475R. Also, scanning probe microscopes are known in the art including probe exchange mechanisms as described in, for example, U.S. Pat. No. 5,705,814 (Digital Instruments).
One embodiment is an article comprising: (i) a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers extending from the base row, wherein each of the cantilevers comprise tips at the cantilever end away from the base row, wherein the arrays are adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface; and (ii) a support for the array. One particular embodiment is illustrated in the non-limiting working examples and figures.
One embodiment also provides an article comprising: (i) a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers, wherein each of the cantilevers comprise tips at the cantilever end away from the base, wherein the number of cantilevers is greater than 250, and wherein the tips have an apex height relative to the cantilever of at least, for example, four microns, and (ii) a support for the array. One particular embodiment is illustrated in the non-limiting working examples and figures.
Another embodiment provides an article comprising: a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers, wherein each of the cantilevers comprise tips at the cantilever end away from the base, wherein the number of cantilevers is greater than 250, and wherein the tips are coated with metal on the tip side of the cantilever and the cantilevers are bent at an angle of, for example, at least 10° from their base. One particular embodiment is illustrated in the non-limiting working examples and figures.
Two-dimensional arrays of cantilevers are known in the art. For example, the two-dimensional array can be a series of rows and columns, providing length and width, preferably substantially perpendicular to each other. The arrays can comprise a first dimension and a second dimension. The two-dimensional array can be a series of one dimensional arrays disposed next to each other to build the second dimension. The two dimensions can be perpendicular. The cantilevers can comprise a free end and a bound end. The cantilevers can comprise tips at or near the free end, distal from the bound end. The cantilevers of one row can point in the same direction as the cantilevers on the next row, or the cantilevers of one row can point in the opposite direction as the cantilevers on the next row.
The two-dimensional arrays can be fabricated by combining two parts, each part having a surface which is patterned in two dimensions and adapted to be mated with each other in the two dimensions.
One important variable is the fraction or percentage of the cantilevers in the array which can actually function for the intended purposes. In some cases, some cantilevers can be imperfectly formed, or can be otherwise damaged after formation. A cantilever yield reflects this percentage of usable cantilevers. Preferably, the array is characterized by a cantilever yield of at least 75%, or at least 80%, or at least 90%, or at least 95%, or more preferably, at least about 98%, or more preferably at least 99%. In characterizing the cantilever yield, cantilevers at the ends of rows may be neglected which are damaged by processing of edges compared to internal cantilevers. For example, the central 75% can be measured. In many cases, the fabrication will be better done in the middle rather than the edge as edge effects are known in wafer fabrication. Defect density can increase in some cases as one moves from the center to the edge.
The array can be adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface. For example, the cantilever arms should not contact the surface and can be accordingly adapted such as by, for example, bending. The tips can be adapted for this as well including, for example, long tips. Factors which can be useful to achieve this result include use of long tips, bending of the cantilever arms, tip leveling, row leveling, and leveling of the cantilevers in all dimensions. One or more combination of factors can be used.
The cantilever tips can be longer than usual in the art. For example, the tips can have an apex height relative to the cantilever of at least four microns on average, and if desired, the tips can have an apex height relative to the cantilever of at least seven microns on average. In addition, tip apex height can be at least 10 microns, or at least 15 microns, or at least 20 microns. No particular upper limit exists and technology known in the art and improving can be used. This long length can help ensure that only tips are contacting the surface. Apex height can be taken as an average of many tip apex heights, and in general, apex height is engineered not to vary substantially from tip to tip. Methods known in the art can be used to measure tip apex height including methods shown in the working examples.
In measuring parameters for the array, average measurements can be used. Average measurements can be obtained by methods known in the art including for example review of representative images or micrographs. The entire array does not need to be measured as that can be impractical.
Tipless cantilevers can be used in some embodiments, although not a preferred embodiment. For example, one embodiment provides an article comprising: (i) a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers extending from the base row, wherein each of the cantilevers are tipless cantilevers, wherein the cantilevers are bent at an angle from their base.
In addition, the cantilevers can be bent including bent towards the surface to be patterned. Methods known in the art can be used to induce bending. The cantilevers can be bent at an angle away from the base and the support. The cantilevers can comprise multiple layers adapted for bending of cantilevers. For example, differential thermal expansion or cantilever bimorph can be used to bend the cantilevers. Cantilever bending can be induced by using at least two different materials. Alternatively, the same materials can be used but with different stresses to provide cantilever bending. Another method is depositing on the cantilever comprising one material a second layer of the same material but with an intrinsic stress gradient. Alternatively, the surface of the cantilever can be oxidized. The cantilevers can be bent at an angle for example of at least 5° from their base, or at least 10° from their base, or at an angle of at least 15° from their base. Methods known in the art can be used to measure this including the methods demonstrated in the working examples. Average value for angle can be used. The cantilevers can be bent on average about 10 microns to about 50 microns, or about 15 microns to about 40 microns. This distance of bending can be measured by methods known in the art including the methods demonstrated in the working examples. Average distance can be used. The bending can result in greater tolerance to substrate roughness and morphology and tip misalignment within the array so that for example a misalignment of about ±20 microns or less or about ±10 microns or less can be compensated.
To facilitate bending, the cantilevers can comprise multiple layers such as two principle layers and optional adhesion layers and can be for example bimorph cantilevers. The cantilevers can be coated with metal or metal oxide on the tip side of the cantilever. The metal is not particularly limited as long as the metal or metal oxide is useful in helping to bend the cantilevers with heat. For example, the metal can be a noble metal such as gold.
In preferred embodiments, the array can be adapted so that the cantilevers are both bent toward the surface and also comprise tips which are longer than normal compared to tips used merely for imaging.
The tips can be fabricated and sharpened before use and can have an average radius of curvature of, for example, less than 100 nm. The average radius of curvature can be, for example, 10 nm to 100 nm, or 20 nm to 100 nm, or 30 nm to 90 nm. The shape of the tip can be varied including for example pyramidal, conical, wedge, and boxed. The tips can be hollow tips or contain an aperture including hollow tips and aperture tips formed through microfabrication with microfluidic channels passing to end of tip. Fluid materials can be stored at the end of the tips or flow through the tips.
The tip geometry can be varied and can be for example a solid tip or a hollow tip. WO 2005/115630 (PCT/US2005/014899) to Henderson et al. describes tip geometries for depositing materials onto surfaces which can be used herein.
The two dimensional array can be characterized by a tip spacing in each of the two dimensions (e.g., length dimension and width dimension). Tip spacing can be taken, for example, from the method of manufacturing the tip arrays or directly observed from the manufactured array. Tip spacing can be engineered to provide high density of tips and cantilevers. For example, tip density can be at least 10,000 per square inch, or at least 40,000 per square inch, or at least 70,000 per square inch. The array can be characterized by a tip spacing of less than 300 microns in a first dimension of the two dimensional array and less than 300 microns in a second dimension of the two dimensional array. To achieve even higher density, the tip spacing can be, for example, less than about 200 microns in one dimension and less than about 100 microns, or less than about 50 microns, in another dimension. Alternatively, the tip spacing can be for example less than 100 microns in one dimension and a less than 25 microns in a second direction. The array can be characterized by a tip spacing of 100 microns or less in at least one dimension of the two dimensional array. In one embodiment, tip spacing can be about 70 microns to about 110 microns in one dimension, and about 5 microns to about 35 microns in the second dimension. There is no particular lower limit on tip spacing as fabrication methods will allow more dense tip spacing over time. Examples of lower limits include 1 micron, or 5 microns, or 10 microns so for example tip spacings can be one micron to 300 microns, or one micron to 100 micron.
The number of cantilevers on the two dimensional array is not particularly limited but can be at least about three, at least about five, at least about 250, or at least about 1,000, or at least about 10,000, or at least about 50,000, or at least about 55,000, or at least about 100,000, or about 25,000 to about 75,000. The number can be increased to the amount allowed for a particular instrument and space constraints for patterning. A suitable balance can be achieved for a particular application weighing for example factors such as ease of fabrication, quality, and the particular density needs.
The tips can be engineered to have consistent spacing for touch the surface consistently. For example, each of the tips can be characterized by a distance D spanning the tip end to the support, and the tip array is characterized by an average distance D′ of the tip end to the support, and for at least 90% of the tips, D is within 50 microns of D′. In another embodiment, for at least 90% of the tips, D is within 10 microns of D′. The distance between the tip ends and the support can be for example about 10 microns to about 50 microns. This distance can comprise for example the additive combination of base row height, the distance of bending, and the tip height.
Base row length is not particularly limited. For example, the base rows can have an average length of at least about 1 mm. Average length for base row can be, for example, about 0.1 mm to about 30 mm, or about 0.1 mm to about 15 mm, or about 0.1 mm to about 5 mm, or about 0.5 mm to about 3 mm.
The base rows can have a height with respect to the support of at least about 5 microns. This height is not particularly limited but can be adapted for use with the appropriate cantilever bending.
Cantilever force constant is not particularly limited. For example, the cantilevers can have an average force constant of about 0.001 N/m to about 10 N/m, or alternatively, an average force constant of about 0.05 N/m to about 1 N/m, or alternatively an average force constant of about 0.1 N/m to about 1 N/m, or about 0.1 N/m to about 0.6 N/m.
A variety of methods can be used for bonding the cantilevers to the base, and the methods are not particularly limited. Bonding methods are described for example in Madou, Fundamentals of Microfabrication, 2nd Ed., pages 484-494 which describes for example field-assisted thermal bonding, also known as anodic bonding, electrostatic bonding, or the Mallory process. Methods which provide low processing temperature can be used. For example, the cantilevers can be bound to the base by a non-adhesive bonding. Bonding examples include electrostatic bonding, field-assisted thermal bonding, silicon fusion bonding, thermal bonding with intermediate layers, eutectic bonding, gold diffusion bonding, gold thermocompression bonding, adhesive bonding, and glass frit bonding.
The cantilevers can be engineered so they are not adapted for feedback including force feedback. Alternatively, at least one cantilever can be adapted for feedback including force feedback. Or substantially all of the cantilevers can be adapted for feedback including force feedback. For example, over 90%, or over 95%, or over 99% of the cantilevers can be adapted for feedback including force feedback.
The cantilevers can be bound to the base by electrostatic binding.
The cantilevers can be made from materials used in AFM probes including for example silicon, polycrystalline silicon, silicon nitride, or silicon rich nitride. The cantilevers can have a length, width, and height or thickness. The length can be for example about 10 microns to about 80 microns, or about 25 microns to about 65 microns. The width can be for example 5 microns to about 25 microns, or about 10 microns to about 20 microns. Thickness can be for example 100 nm to about 700 nm, or about 250 nm to about 550 nm. Tipless cantilevers can be used in the arrays, the methods of making arrays, and the methods of using arrays.
The cantilevers can be supported on the base rows, and the base rows in turn can be supported on a larger support for the array. The base rows can extend from the larger support for the array. The array support can be characterized by a surface area which is about two square cm or less, or alternatively about 0.5 square cm to about 1.5 square cm. The size can be adjusted as needed for coupling with an instrument.
Arrays can be adapted for passive pen or active pen use. Control of each tip can be carried out by piezoelectric, capactive, or thermoelectric actuation, for example.
The arrays can be adapted for integration of tip coating and ink delivery. For example, microfluidics can be used to control inking and coating of the tips. Tips can be dipped into devices or ink can be delivered directly through internal regions of the tip for hollow tip embodiments.
The tips can be coated with a patterning compound or ink material. The coating is not particularly limited; the patterning compound or ink material can be disposed at the tip end. Patterning compounds and materials are known in the art of nanolithographic printing and include organic compounds and inorganic materials, chemicals, biological materials, non-reactive materials and reactive materials, molecular compounds and particles, nanoparticles, materials that form self assembled monolayers, soluble compounds, polymers, ceramics, metals, magnetic materials, metal oxides, main group elements, mixtures of compounds and materials, conducting polymers, biomolecules including nucleic acid materials, RNA, DNA, PNA, proteins and peptides, antibodies, enzymes, lipids, carbohydrates, and even organisms such as viruses. The references described in the INTRODUCTION section describe many patterning compounds which can be used. Sulfur-containing compounds including thiols and sulfides can be used.
The methods by which the tips can be coated can include for example solution dipping or vacuum evaporation, as well as the microfluidic methods noted above. See U.S. patent application Ser. No. 10/705,776 filed Nov. 12, 2003, now published as 2005/0035983 on Feb. 17, 2005.
Another embodiment comprises a method of making two dimensional arrays. For example, an embodiment comprises a method of making article, wherein the article comprises a two-dimensional array of a plurality of cantilevers, and a support for the array, the method comprising: (i) forming a two dimensional array comprising a plurality of cantilevers comprising tips at their ends, wherein the cantilevers are supported on a sacrificial support structure; (ii) forming an array support comprising a plurality of base rows which are adapted for bonding to the two dimensional array comprising a plurality of cantilevers; (iii) bonding the cantilevers to the base rows; and (iv) removing the support structure to release the cantilevers and form the array. The non-limiting working examples below provide one method for executing these steps. See
In some embodiments, tipless cantilevers can be fabricated.
The above description for the article comprising the two dimensional arrays and support can be also applied to the methods making the two dimensional arrays. For example, in the method of making, the tips can be adapted to prevent substantial contact of non-tip components of the array when the tips are brought into contact with a substantially planar surface. In the method of making, the tips can have an apex height relative to the cantilever of at least four microns, or at least seven microns. In the method of making, the method can further comprise the step of bending the cantilevers at an angle away from the support. For example, the method can comprise bending the cantilevers at an angle of at least 100 away from the support. In the method of making, the tips can have an apex height relative to the cantilever of at least four microns, and wherein the cantilevers are bent at an angle away from the support. Also, in the method of making, the tips can have an apex height relative to the cantilever of at least seven microns, and wherein the cantilevers are bent at an angle of at least 100 away from the support.
Microfabrication methods are described extensively in for example Madou, Fundamentals of Microfabrication, 2nd Ed., CRC Press, 2002; and Van Zant, Microchip Fabrication, 5th Ed., 2004.
In one part of the fabrication method, the two dimensional array can be formed by microfabrication and micromachining methods. The sub-product can comprise the cantilevers supported on a sacrificial support which can be later removed before use. Microfabrication steps including wafers, oxidation, patterning, etching, deposition, deep reactive ion etching (Bosch process) and other steps known for making cantilevers and tips can be used.
In another part of the fabrication method, an array support is formed which is adapted for bonding to the two dimensional array of cantilevers. It can be also adapted for coupling the two dimensional array of cantilevers to the instrument for movement. Base rows can be formed which extend out from the surface of the array support and provide support for the cantilevers upon fabrication.
The cantilevers can be bonded to the base rows. An example of a bonding method is electrostatic bonding.
The sacrificial support for the cantilevers can be removed to free up or release the cantilevers. Methods known in the art can be used to execute this step.
The working examples also provide a method for annealing pen arrays and the parameters described therein can be modified. For example, the 5 nm Ti adhesion layer can be 2 nm to 20 nm thick, and the 25 nm gold layer can be 5 nm to 100 nm thick. The annealing temperature can be for example 150° C. to about 500° C., and the time for annealing can be for example 30 minutes to 250 minutes.
Also provided is a method comprising (1) micromaching a two dimensional array of cantilevers wherein the cantilevers are adapted to bond with a device which both supports the cantilevers and can also couple the cantilevers to an instrument for motion, and (2) bonding the cantilevers to the device. The device can be called a handle wafer. One side is for bonding to the cantilevers. The other side is for coupling to a larger instrument. The working examples below, for example, also illustrate this embodiment.
Level can be carried out to provide leveling in each dimension of the two dimensional array. Leveling can help with adapting the array so only tips contact the surface. The working examples below provide an example of leveling the cantilevers before the two dimensional array of cantilevers are mounted onto an instrument. For example, gravity forces and forces near to gravity forces can be used to level the cantilevers on a sacrificial substrate. External force can be used. Other forces can be used as needed for a particular two dimensional array. For example, forces can be about 0.2 nN/tip to about 2,000 nN/tip, or about 2 nN/tip or about 200 nN/tip, or about 20 nN/tip. The sacrificial substrate can be made as flat as possible and practical for a given application.
The adhesive mounting method also allows one to improve leveling and avoid use of a feedback system if desired.
Optical microscopy can be used to facilitate leveling.
One embodiment provides a method comprising: (i) preparing a two-dimensional array of a plurality of cantilevers, wherein the array comprises a plurality of base rows, each base row comprising a plurality of cantilevers extending from the base row, wherein each of the cantilevers comprise tips at the cantilever end away from the base row, (ii) contacting tips of the array with a sacrificial substrate under pressure, (iii) forming an aligned array on the substrate, and (iv) attaching the aligned array to an instrument adapted for motion of the array. The pressure can be generated either externally or with gravity. The attaching can be an adhesive or mechanical attaching. The method can further comprise removing the sacrificial substrate from the tips of the array.
Mounting of arrays to the instrument can be achieved by one or more mechanisms operating individually or in combination. For example, mounting can be carried out with use of mechanical coupling, friction fit or magnetic coupling. Adhesives and glues can be used including fast curing and UV curing systems. Epoxy glue is described below including its use as a gap filler or space filler.
Adhesive mounting can be used to couple the supported two dimensional arrays to an instrument which provides x motion, y motion, z motion, or combinations thereof including x, y, z motion. Motion is provided which allows for high resolution patterning and high resolution such as found with for example scanning probe instruments.
The instrumentation can be also adapted to have the pens stand still and have the substrates move in x, y, and/or z motion.
In a preferred embodiment, the bonding agent functions to both mount the two dimensional array to the instrument and also the facilitate leveling of the tip array.
Also provided are instruments including printing and patterning instruments, as well as nanolithography instruments. Instruments can be used which provide both imaging and patterning capability. While the methods and devices herein can be used with scanning probe and AFM instrumentation, the instruments are not so limited. Dispensing instruments and tools for delivering small scale amounts of materials to surfaces are known. See for example U.S. Pat. Nos. 6,024,925; 6,087,274; 5,981,733;
A preferred example of an instrument for lithography including microlithography and nanolithography is the NScriptor™ from Nanoink (Chicago, Ill.). Commercial AFM instruments can be used.
An instrument is described in U.S. Pat. No. 7,008,769 to Henderson et al.
DPN patterning is describe in the references noted above in the Introduction Section and other references cited herein.
Substrates can be made with massive numbers of micron-scale or nanometer-scale structures, or nanostructures, formed at massively fast rates. For example, one important parameter is the rate at which structures can be formed. Using methods described herein, structures can be formed at a rate of at least 100,000 per minute, or at least 1,000,000 structures per minute, and even further at least 2,000,000 structures per minute, and even further at least 3,000,000 structures per minute, and even further at least 4,000,000 structures per minute, and even further at least 5,000,000 structures per minute, and even further at least 10,000,000 structures per minute. For example, structures formed at fast rates can be dot features having a diameter of for example about 25 nm to about 500 nm, or about 50 nm to about 200 nm. The structures can be dots and circles, wherein the tip is not moved in the X-Y direction during deposition of the patterning compound.
Other rate parameters can be used. For example, direct-writing can be carried out at a rate of at least 1.0 meter/min, or at least 3.3 meters/min (for example, if the tips are moved at appropriate rates such as for example a rate of 1 um/s). Patterning can be executed at 10,000,000 square microns per hour. Rates can be in some cases determined by the rate of diffusion spreading for one pen with multiplication by the number of pens.
A preferred embodiment comprises a method for direct-write nanolithography comprising: directly writing nanostructures at a rate of at least 100,000 per minute, wherein the directly writing comprises contacting a tip having a patterning compound thereon with a substrate. The rate can be at least 1,000,000 per minute, or at least 4,000,000 per minute. The nanostructures can comprise dots, lines, or substantially complete circles. The nanostructures can comprise dots having diameter about 50 nm to about 1,000 nm. The nanostructures can be separated by a distance between about 50 nm and about 1,000 nm, or about 100 nm to about 750 nm.
Substrates can be coated and patterned with for example at least 25,000,000 structures, or at least 50,000,000 structures, or at least 75,000,000 structures, or at least 1,000,000 structures, or at least 500,000,000 million structures, or at least 1,000,000,000 structures.
An important aspect is that the pattern formed on the substrate substantially matches either (1) a pattern generated with software and made with tip motion, or (2) the pattern of the array when the tips are not moved over the surface.
An important embodiment comprises the elimination of a feedback system. This embodiment, having this eliminated, is a basic and novel feature.
The substrates for patterning can be single layer or multilayer. They can be solids including polymers, glasses, composites, silicon, mica, diamond, ceramics, metals, and various oxides and complex mixtures.
The ink-substrate combination can be selected to provide stable structures. Stability can be enhanced by use of covalent bonding or chemisorption, or electrostatic attraction.
Arrays can be formed of inorganic, organic, or biological materials including nanostructures such as viruses, proteins, carbon nanotubes, nanowires, dendrimers, fullerenes, and the like. Combinatorial arrays can be formed. Each spot in the array can provide the same composition or a different composition compared to the next spot.
Vibration isolation tables can be used. Environmental chambers can be used including nebulizer, real-time sensors for temperature and humidity control, and heating and cooling fans. High resolution optics can be used. Independent three motor leveling can be used. Tip biasing can be used.
If AFM-like instrumentation is used, the mode can be contact mode, non-contact mode, or intermittent contact mode.
Another example of a use can be found in Lenhert et al, “Massively Parallel Dip-Pen Nanolithography of Heterogeneous Supported Phospholipid Multilayer Patterns,” Small, 2007, 3, No. 1, 71-75, which is hereby incorporated by reference including
The various embodiments are further illustrated by the following non-limiting examples.
Using conventional photolithographic techniques, a 55,000 pen two-dimensional array was fabricated (pen yield >98%; pen spacing 90×20 μm,
First, arrays of Si3N4 (or silicon rich nitride material) cantilevers with pyramidal tips were fabricated such that the tips are about three times larger than conventional silicon nitride AFM tips (the apex of each tip was 7.6±0.2 μm taller than its cantilever base).
Second, the cantilevers were bent at a ˜20° angle from their base by coating them with 25 nm of Au (and 5 nm Ti adhesion layer) and then annealing at 300° C. This curvature is a result of the different thermal expansion coefficients of Si3N4 and Au (see, for example, Wenzler, et al. T. P. Rev. Sci. Instrum. 67, 4191-4197 (1996)). This array architecture leads to greater tolerance to the substrate morphology and inherent tip misalignment within the array (±10 μm misalignment can be compensated).
Third, gravity (˜20 nN/tip), instead of a complex set of feedback systems, was used to bring all of the tips in contact with a sacrificial substrate prior to use.
Finally, the tip array was locked into position with respect to the piezo scanner head by taking advantage of the malleability of a rapidly curing epoxy resin (see supplementary information). This alignment procedure was useful so all of the tips within the array could be engaged and disengaged in a deliberate and controlled fashion without a feedback system. Once engaged, the pen array can be used to directly write virtually any pattern of molecules on the underlying substrate and simultaneously generate ˜55,000 duplicates.
To test the writing capabilities of the pen array, its cantilevers were uniformly coated with 1-octadecanethiol (ODT) by vapor deposition and subsequently used to pattern a 25 nm film of polycrystalline gold on an oxidized silicon substrate with a 5 nm Ti adhesion layer. Using ODT as a chemical etch resist, the molecular patterns were developed into gold nanostructures, allowing the use of an optical or scanning electron microscope to characterize the patterns over large areas. In an initial experiment, the 55,000 pen array was used to generate ˜88 million dot features (each tip generating 1,600 100±20 nm dots in a 40×40 array) in less than 20 min (
Materials. Gold substrates were prepared according to literature procedures. (Weinberger et al., Advanced Materials, 12, 1600 (2000); Zhang et al., Langmuir, 20, 962-968 (2004). 1-octadecanethiol (ODT) (98%) and 1-octanol (99%) were purchased from Aldrich Chemical Co. Fe(NO3)39H2O (99%) was purchased from Acros Chemicals, thiourea (ACS grade) was purchased from Fisher Scientific, and ethanol (ACS/USP grade) was purchased from Pharmco Products Inc. 5-min epoxy gel was purchased from Devcon and used as specified by the manufacturer. All chemicals were used as received.
Fabrication of 55,000 Cantilever Arrays: The Microfabrication process used to generate the tips was designed to be simple and robust, which affords high yields and is amenable for future modifications (
Separately, a Pyrex wafer was coated with a 200 nm thick chromium layer and lithographically patterned to form 100 micron rectangular trenches. The Pyrex was etched in a reactive ion etcher, forming 8 micron recesses to allow the cantilevers free movement, and the chromium was then removed. The nitrided silicon wafer and the Pyrex wafer were then electrostatically bonded, and the back of the Pyrex wafer was scribed into 1 cm2 substrates by a diamond saw. Finally, the silicon wafer was etched, leaving the nitrided tip arrays attached to the Pyrex. The resulting cantilever structures were characterized by optical and electron microscopy (
The force constant (k) of a fixed-free cantilever beam with a length, width, and thickness of l, w, and t is given by k=Ewt3/413 (1), under a small displacement assumption. The term E denotes the modulus of elasticity of the probe material. The approximate modulus of elasticity is 145 GPa for the thin film of low-stress deposited layer of Si3N4. The cantilevers had measured dimensions of l=45 microns, w=14.5 microns, and t=400 nm, which correspond to a force constant k=0.40±0.10 N/m. Annealing of pen arrays. To induce tip curling away from the cantilever base, the tip-side of the cantilevers were first coated with a 5 nm Ti adhesion layer and 25 nm Au using a BOC 306 Edwards vacuum evaporator operated at a base pressure below 5×10−7 mbar. Subsequently, the pen arrays were placed in an oven, held at 300° C. for 2 hr, and then slowly cooled to room temperature at a rate <5° C./min. The degree of cantilever bending was inspected by optical microscopy and quantitatively measured by SEM. Although annealing the pen arrays at 400° C. induced a larger degree of cantilever bending, the high temperature also resulted in coarsening of the gold grains due to enhanced Au diffusion. Therefore, 300° C. was chosen as the annealing temperature. Cantilever bending is caused by the different thermal expansion of gold (αAu=13.8×106° C.−1) and Si3N4 (αSi
where D is the thickness (D1=DAu=25 nm; D2=DSi
Heating the tips to 300° C. would produce the expected deflection or curling of 14 microns. However, the experimentally determined value is about 20-30 microns, which is most likely a result of deviations in the thickness of Au and the Si3N4 layers across the entire tip arrays. (Wenzler et al., Review of Scientific Instruments, 67, 4191-4197 (1996).
Ink Coating: The pen arrays were placed inside a sealed metal container with ODT (the pen arrays were attached to the cover of the container with a piece of double-sticky tape). The container was heated to 70° C. and held for 30 minutes, and then allowed to slowly cool. This vapor coating process was repeated (typically 2-3 times) until the tips were sufficiently coated with ODT for DPN printing experiments. Importantly, the coated pen array could be used to pattern more than 25 samples over a period of three days without the need of recoating the tips with more ODT ink.
Pen Array Mounting: The pen array was gently placed onto a sacrificial Au-coated SiOx substrate, letting the weight of the tip array (about 100 mg, 20 nN/tip) bring all tips into contact with substrate. An epoxy coated magnetic tip holder (1 cm×0.2 cm) was then gently brought down in contact with the Pyrex support of the pen array using the z motors of the AFM (
Dip Pen Nanolithography: DPN experiments were performed with an Nscriptor™ (NanoInk, Inc., Chicago, Ill.) equipped with a 100-micron scanner and closed-loop scan control and commercial lithographic software (DPNWrite™, DPN System-1, NanoInk, Inc., Chicago, Ill.). All DPN patterning experiments were carried out under ambient laboratory conditions without the aid of a clean room (about 30% relative humidity, about 20° C.).
Selective Etching of Au: Etching was performed on DPN-patterned gold substrates by immersing in a bath of 13.3 mM Fe(NO3)39H2O, 20 mM thiourea, 0.3% HCl in octanol saturated nanopure water (15 mL of etch solution for a about 1 square cm substrate). (Xia et al., Chemistry of Materials, 7, 2332-2337 (1995); Geissler et al, Langmuir, 18, 2374-2377 (2002); Zhang et al., Nano Letters, 3, 43-45 (2003). The bath was gently stirred as the substrate was visually inspected for etching (rate about 6 nm/min). The color of the substrate changed from yellow to dark blue as the gold was dissolved.
Pattern Characterization. Patterned structures, post etching, were characterized by SEM (Leo Gemini 1525), and optical microscopy (Zeiss Axiovert 100A inverted microscope, Thornwood N.Y.) equipped with a Penguin 600CL digital camera and StreamPix software. These tools provide a relatively high throughput method for evaluating the quality of the patterned structures. Tapping mode AFM images were collected with a Nanoman AFM equipped with a Nanoscope IV controller from Veeco (Santa Barbara, Calif.) with silicon tips (NCH—W, Veeco, spring constant 40 N/m) scanned at a rate of 0.5 Hz and set to a pixel resolution of 512×512. Gold coated commercial AFM cantilevers (sharpened Si3N4, Type A, NanoInk, Inc.) with a spring constant of 0.05 N/m were used for contact mode imaging.
Additional Examples of 2D Parallel DPN: Shown below are three additional examples that demonstrate the rapid prototyping capability of 2D parallel DPN reported herein.
Apex height was measured for a pyramidal tip as shown in
All references cited herein are hereby incorporated by reference in their entirety.
This application claims the priority benefit of U.S. provisional application Ser. No. 60/792,950 filed Apr. 19, 2006 to Mirkin et al., which is hereby incorporated by reference.
The present invention was developed with use of federal funding from the following grant agencies and grant numbers: Air Force Office Scientific Research, AFOSR FA9550-05-1-0348; AFOSR 28065-3/W911NF-04-1-071; and National Institutes of Health NIH DPI 0D000285-02. The federal government reserves rights in the invention.
| Number | Date | Country | |
|---|---|---|---|
| 60792950 | Apr 2006 | US |