Material having a damping property and masterbatch pellets therefor

BACKGROUND OF THE INVENTION
The present invention relates to a material having a damping property and masterbatch pellets used for production thereof. More particularly, the present invention relates to a material having a damping property which shows a high internal loss at around room temperature and has a sufficient strength and hardness. The material having a damping property (hereinafter referred to as "damping material") of the present invention is mainly used as structural materials of electrical or electronic equipments, casings or bodices of household electric appliances of office automation equipments, parts of various kinds of machines and apparatus, interior parts of vehicles and ships, building materials and the like. It finds particularly useful application to a cartridge half and a cassette half.
As is well known, a damping material is widely used in many fields of industry for the purpose of damping vibration or noise generated from various sources and occasions, for example, vibration or noise which is generated incidental to operation of engine or motor mounted in various kinds of machines and apparatus, for instance, office automation equipments, household electric appliances such as washing machines, dryer, etc., a cartridge half and cassette half of data cartridge tapes, video tapes, audio tapes, etc., disk shells of optical discs, magneto-optical discs, magnetic discs, acoustic optical discs, etc., acoustic equipments, precision machine tools, works plant equipments, and various kinds of vehicles and ships; vibration or noise generated from piping such as water and gas pipes in buildings, ducts of air conditioning systems, etc.; and vibration or noise generated from running of vehicles on road or railway tracks.
The damping material is usually offered as a sheet-like material or block-like material produced by kneading and molding a binder resin and filler material such as mica, iron oxide or the like by a suitable molding method such as extrusion molding, calender molding, compression molding, injection molding or cast molding, or it is provided directly as a structural material of electrical or electronic equipments, casings of household electric appliances, office automation equipments, a cartridge half and a cassette half, etc. Namely, as for the using mode of the damping material, it may be used so that a molded sheet-like material or block-like material is stuck to or put between pertinent section(s) of an objective apparatus, etc., or it may be directly applied as a structural material of electrical or electronic equipments, casings of household electric appliances, office automation equipments, a cartridge half, a cassette half, etc.
Recently, there is seen a remarkable trend toward the miniaturization and lightweight of handy apparatus such as office automation equipments and acoustic equipments, and a damping material used in such machines, equipments, appliances and tools has been strongly required to miniaturize and reduce the weight. To meet this requirements, the damping material is demanded to have a high damping property, that is, a high internal loss. However, if it is simply tried to increase the amount of inorganic filler material used in the damping material for the only purpose of improving damping property, it invites a reduction of strength and hardness of rigid resin used as binder resin, and moldability of the material is impaired. Further, since specific gravity of the produced damping material elevates, this runs counter to the requirements of the miniaturization and lightweight. It is thus strongly required of damping material to have an excellent damping property while maintaining an intrinsic strength (e.g. bending strength) and hardness of a rigid resin. This fact is referred to in, for instance, Japanese Patent Application Laid-open (KOKAI) No. 4-45142 which states: "As thermoplastic resin composition having damping properties, there are known compositions obtained by blending a large amount of filler material such as calcium carbonate with polypropylene. These compositions, however, had the disadvantages in that the intrinsic priorities of resin (such as good moldability and high impact strength) are deteriorated because of blending of a large amount of filler material. Development of a damping materiel capable of retaining the intrinsic properties of resin has, therefore, been desired."
Recently, large numbers of the movable parts such as motors, relays, transforms, gears, cums, gear boxes and the like, and the electrical, electronic or machine parts which generate vibration and/or noise are used in the household electric appliances or the office automation equipments. The vibration generated from such parts is transferred to other parts and/or casings, and as a result, the intended performances of the product can not be exhibited. According to circumstances, it may be invite to malfunction and/or generate unpleasant vibration. So, the damping material used as a structural material of the electrical, electronic or machine parts, and the casings of the household electric appliances or the office automation equipments is strongly required to have a sufficiently high strength and hardness, and excellent internal loss at around room temperature (e. g., 20 to 28.degree. C.).
Also, in recording media such as optical disks or magnetic disks used in computers, word processors and the like, data-cartridge tapes, video and audio optical disks, cassette tapes, etc., higher reliability, tone quality and picture quality of the recording media are strongly demanded.
These recording media are set in a recorder and driven to run by a motor or other motive force to make recording or reading-out. Vibration generated in the inside of the cartridge half or cassette half (for example, vibration caused by "play" around a shaft such as hub for taking up the magnetic tape) or vibration from a source outside the cartridge half or cassette half (for example, vibration caused by operation of motor) exerts baneful influence on recording and reading-out, so that it is difficult to have accurate recording and reading-out of information. Therefore, the damping material used as a structural material for cartridge half or cassette half is strongly required to satisfy the above requirement, i.e., to have an excellent internal loss at around room temperature while maintaining high strength and hardness.
As binder resin for damping material, there are usually used thermoplastic resins (rigid resins) such as polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers, modified polyphenylene ethers and the like. These rigid resins are preferably used because of relatively low cost and excellent molding workability.
These rigid resins, however, are not satisfactorily excellent in internal loss at around room temperature.
Many attempts have been made for improving a damping property of these rigid resins. For instance, Japanese Patent Application Laid-open (KOKAI) No. 2-3-00250 proposes a polypropylene composition improved in a damping property obtained by incorporating a styrene-isoprene-styrene block copolymer in polypropylene resin. Japanese Patent Application Laid-open (KOKAI) No. 3-45646 proposes an ABS resin composition having improved damping property, obtained by incorporating a styrene-isoprene-styrene copolymer to an acrylonitrile-butadiene-styrene copolymer. Japanese Patent Application Laid-open (KOKAI) No. 3-181552 proposes a polyphenylene ether resin composition having excellent damping properties, comprising a polyphenylene ether and a styrene-isoprene-styrene block copolymer. Japanese Patent Application Laid-open (KOKAI).No. 5-70699 proposes a thermoplastic resin composition with improved damping property, obtained by incorporating a styrene-isoprene-styrene block copolymer in a thermoplastic resin. Also, in Japanese Patent Application Laid-open (KOKAI) No. 5-59234 is proposed a damping material resin composed of polypropylene and a styrene-isoprene-styrene block copolymer.
More specifically, Japanese KOKAI No. 2-300250 discloses a polypropylene composition comprising (a) 97-50 parts by weight of polypropylene and (b) 3-50 parts by weight of a block copolymer having a number-average molecular weight of 30,000-300,000 or a hydrogenation product thereof, the said block copolymer composed of blocks (A) comprising an aromatic vinyl monomer having a number-average molecular weight of 2,500-40,000 and blocks (B) comprising isoprene or an isoprene-butadiene mixture, whose number-average molecular weight is 10,000-200,000 and 3,4 bond and 1,2 bond content is 40% or more, and which shows a peak of main dispersion of tan .delta. at 0.degree. C. or more.
The problem to be solved by Japanese KOKAI No. 2-300250 is to reduce vibration and noise at around room temperature in the range where various kinds of the equipments and appliances are practically used.
Japanese KOKAI No. 3-45646 discloses an ABS resin composition comprising (a) 97-50 parts by weight of an ABS resin and (b) 3-50 parts by weight of a block copolymer having a number-average molecular weight of 30,000-300,000 or a hydrogenation product thereof, the said block copolymer composed of blocks (A) comprising an aromatic vinyl monomer having a number-average molecular weight of 2,500-40,000 and blocks (B) comprising isoprene or an isoprene-butadiene mixture, having a number-average molecular weight of 10,000-200,000 and a 3,4 bond and 1,2 bond content of 40% or more and showing a peak of main dispersion of tan .delta. at 0.degree. C. or more.
The object of Japanese KOKAI No. 3-45646 is to improve a damping property at around room temperature in the widely used ABS resin for damping material in various kinds of the equipments and appliances.
Japanese KOKAI No. 3-181552 discloses a polyphenylene ether resin composition comprising (a) 97-50 parts by weight of polyphenylene ether and (b) 3-50 parts by weight of a block copolymer having a number-average molecular weight of 30,000-300,000 or a hydrogenation product thereof, the said block copolymer composed of blocks (A) comprising an aromatic vinyl monomer having a number-average molecular weight of 2,500-40,000 and blocks (B)comprising isoprene or an isoprene-butadiene mixture, having a number-average molecular weight of 10,000-200,000 and a 3,4-bond and 1,2-bond content of 40% or more and showing a peak of main dispersion of tan .delta. at 0.degree. C. or more.
Japanese KOKAI No. 5-70699 discloses a thermoplastic resin composition comprising (a) 97-50 parts by weight of a thermoplastic resin and (b) 3-50 parts by weight of a block copolymer having a number-average molecular weight of 30,000-300,000 or a hydrogenation product thereof, said block copolymer composed of blocks (A) comprising an aromatic vinyl monomer having a number-average molecular weight is 2,500-40,000 and blocks (B) comprising isoprene or an isoprene-butadiene mixture, whose number-average molecular weight is 10,000-200,000 and Tg is 0 to 40.degree. C., wherein said blocks A and B are coupled together in the form of A(BA).sub.n or (AB).sub.n (n:an integer of 1 or more).
The object of Japanese KOKAI No. 5-70699 is to improve impact resistance in the low temperature region.
The thermoplastic resins proposed in Japanese KOKAI No. 5-70669 include polyolefins such as polyethylene and polypropylene, polyester such as polyethylene terephthalate and polybutylene terephthalate, styrene resins such as ABS and AS resins, polyamides, polyphenylene ethers, polyacetals and polycarbonates.
Japanese KOKAI No. 5-59234 discloses a damping material resin comprising a polypropylene resin composition composed of a mixture of 50-95% by weight of a polypropylene and 5-50% by weight of a thermoplastic elastomer and an inorganic filler, said inorganic filler being blended in an amount of 10-150 parts by weight based on 100 parts by weight of said resin mixture, wherein said thermoplastic elastomer is composed of a block polymer of a styrene-isoprene-styrene structure having polyisoprene blocks of vinyl structure.
A damping material composition obtained by adding iron oxide particles as an inorganic filler for improving a damping property is proposed in Japanese Patent Application Laid-open (KOKAI) No. 3-287652. The composition of this KOKAI comprises 100 parts by weight of a block copolymer having a number-average molecular weight of 30,000 to 300,000 and composed of blocks (A) comprising an aromatic vinyl monomer having a number-average molecular weight of 2,500 to 40,000, and blocks (B) comprising isoprene or an isoprene-butadiene mixture, having a number-average molecular weight of 10,000 to 200,000 and a 3,4-bond and 1,2-bond content of 40% or more and showing a peak of main dispersion of tan .delta. at 0.degree. C. or more, and 30 to 1000 parts by weight of iron oxide particles.
In production of damping materials mainly composed of thermoplastic resins, it has been common practice in the art to add an inorganic filler material directly to a base resin. However, for better handling and easier preparation of the composition, there is proposed a process using masterbatch pellets in which masterbatch pellets are prepared by dispersing an inorganic filler material in a base resin at a higher concentration than the desired one and these masterbatch pellets are mixed and dispersed in the base resin to adjust the concentration of inorganic filler to the purposed level thereof.
Accordingly, the masterbatch pellets for the damping material, which are easy to handle in producing the damping material and capable of affording a satisfactory damping effect with a moderate amount of addition thereof, are also required.
A damping material having an excellent internal loss in the commonly used temperature range, particularly at around room temperature (for example, 20 to 28.degree. C.), while maintaining a satisfactorily high strength and hardness of a rigid resin, is most strongly required at present, but none of the damping materials of the prior art mentioned above is unable to well satisfy the said requirements.
Any of the damping materials disclosed in the above-mentioned Japanese KOKAIs No. 2-300250, No. 3-45646, No. 3-181552, No. 5-70699 and No. 5-59234 is unsatisfactory in a damping property because of non-use of iron oxide particles as inorganic filler and also incapable of maintaining an intrinsic strength and hardness of a rigid resin because of high content of an inorganic filler.
The damping material disclosed in Japanese KOKAI No. 3-287652 mentioned above has an excellent damping property in the practical temperature range from room temperature to high temperature but is low in strength, that is, this damping material is low in bending modulus.
The problem to be solved by the present invention is to provide a damping material having an excellent internal loss in the practical temperature range, particularly at around room temperature, while maintaining the intrinsic strength and hardness of rigid resin.
As a result of the present inventors' earnest studies for solving the above-mentioned problem, it has been found that by preparing masterbatch pellets from 100 parts by weight of a binder resin composed of not more than 70% by weight of at least one base resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers, and not less than 30% of styrene-isoprene-styrene block copolymer, and 50 to 300 parts by weight of iron compound particles, adding 70 to 99% by weight of at least one base resin selected from polypropylenes, polystyrenes, acryl onitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers to 1 to 30% by weight of said masterbatch pellets, and after kneading, molding the resultant mixture, the obtained damping material composed of 100 parts by weight of a binder resin composed of 85 to 99% by weight of at least one base resin selected from polypropylenes,. polystyrenes, acrylonitrile-butadiene-styrene copolymer, polycarbonates, polyphenylene ethers and modified polyphenylene ethers and 1 to 15% by weight of styrene-isoprene-styrene block copolymers, and 1 to 20 parts by weight of iron compound particles, has an excellent internal loss at around room temperature, and high strength and hardness. The present invention has been attained on the basis of this finding.
SUMMARY OF THE INVENTION
The object of the present invention is to provide a damping material having an excellent internal loss at around room temperature, and satisfactory strength and hardness
To attain the aim, in the first aspect of the present invention, there is provided a damping material comprising 100 parts by weight of binder resin composed of 85 to 99% by weight of at least one base resin selected from polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers and 1 to 15% by weight of styrene-isoprene-styrene block copolymer, and 1 to 20 parts by weight of iron compound particles.
DETAILED DESCRIPTION OF THE INVENTION
The damping material according to the present invention has a loss factor of not less than 0.015, preferably not less than 0.020 at a temperature of 24.degree. C. and a relative bending modulus of not less than 70%, preferably not less than 75% based on a bending modulus of a damping material consisting of the base resin, which show that the internal loss at around room temperature is excellent and the intrinsic strength and hardness of rigid resin is fully maintained.
As base resin used in the present invention, one or more of the resins selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers can be used. The amount of the base resin used is 85 to 99% by weight, preferably 88 to 98% by weight based on the binder resin. When the amount of the base resin exceeds 99% by weight, there can not be obtained the desired effect of improving the damping property because of too small content of styrene-isoprene-styrene block copolymer in the binder resin. When the amount of the base resin is less than 85% by weight, the strength and hardness of the base resin, specifically the bending modulus thereof is lowered because of too large content of styrene-isoprene-styrene block copolymer in the binder resin, and thus it is impossible to maintain the intrinsic strength of the base resin and to provide the damping material of the desired bending modulus and hardness.
As polypropylenes usable in the present invention, homopolypropylenes, propylene copolymers such as propylene-ethylene random copolymer (ethylene content being not more than 20% by weight) and propylene-ethylene block copolymer (ethylene content being not more than 20% by weight), and polypropylenes modified with an unsaturated carboxylic acid or derivatives thereof may be exemplified.
Acrylonitrile-butadiene-styrene copolymers used in the present invention are of a composition of 20 to 30 wt % of acrylonitrile, 10 to 30 wt % of butadiene and 40 to 70 wt % of styrene.
As polystyrenes used in the present invention, available polystyrenes including homopolystyrenes and copolymers such as polystyrene-butadiene copolymers, etc. can be cited. As the polystyrene-butadiene copolymers, a high-impact polystyrene (HI-PS) obtained by graft-polymerizing styrene to butadiene rubber may be exemplified.
Polycarbonates used in the present invention are preferably one having a viscosity-average molecular weight of 1.8.times.10.sup.4 to 3.3.times.10.sup.4. Such polycarbonates are commercially available under the trade names of Novalex (produced by Mitsubishi Chemical Co., Ltd.), Panlight (produced by Teiji Chemical Co., Ltd.), Yupiron (Produced by Mitsubishi Gas Chemical Co., Ltd.), Taflon (produced by Idemitsu Petrochemical Co., Ltd.), Rexan (produced by General Electric Corp.), Macron (Produced by Bayer Corp.), etc.
Examples of polyphenylene ethers usable in the present invention are poly(2,6-dimethyl-1,4-phenylene) ether, poly(2,6-diethyl-1,4-phenylene) ether, poly(2-methyl-6-ethyl-1,4-phenylene) ether, poly(2-methyl-6-propyl-1,4-phenylene) ether, poly(2,6-dipropyl-1,4-phenylene) ether, and poly(2-ethyl-6-propyl-1,4-phenylene) ether.
Modified polyphenylene ethers usable in the present invention is a polymer alloy of polyphenylene ether and styrene-based resin (Noryl resin, produced by General Electric Corp.) and a polymer alloy of polyphenylene ether and polyamide resin (Noryl GTYX resin, produced by General Electric Corp.).
As a base resin, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers are preferably used in the present invention.
Styrene blocks in the styrene-isoprene-styrene block copolymer used in the present invention are constituted by an aromatic vinyl monomer capable of anionic polymerization, such as styrene, 1-vinylnaphthalene, 2-vinylnaphthalene, 3-methylstyrene, 4-propylstyrene, 4-cyclohexylstyrene, 4-dodecylstyrene, 2-ethyl-4-benzylstyrene, 4-phenylbutylstyrene and the like. Among them, styrene is especially preferred.
Isoprene blocks in the said styrene-isoprene-styrene block copolymer are preferably constituted by isoprene or isoprene-butadiene. In case other monomers are used, for instance, if butadiene alone is used, the temperature at which a damping effect is produced is below 0.degree. C. even if the content of vinyl bonds is increased, and the desired damping property cannot be obtained in the practical temperature range. In this case, therefore, the damping material can be applied to a wide scope of use and has a very high practical significance. When isoprene-butadiene is used, the desired damping property can be obtained in the temperature range not less than 0.degree. C. in case of isoprene being not less than 40%. As the isoprene-butadiene copolymers, random, block or tapered copolymers are usable.
Number-average molecular weight of the obtained styrene-isoprene-styrene block copolymer is in the range of 30,000 to 300,000. When the molecular weight is less than 30,000, the mechanical properties such as strength and elongation at breaking of the block copolymer itself are deteriorated, resulting in a reduced strength of the damping material. When the molecular weight exceeds 300,000, the workability thereof worsened. Thus, the preferred range of the molecular weight (Mn) of the said block copolymers is from 80,000 to 250,000.
The block formation in the said styrene-isoprene-styrene block copolymers is A(BA).sub.n or (AB).sub.n, wherein A represents styrene block, B represents isoprene block, and n is an integer of 1 or more. The formation of A(BA).sub.n is preferred.
The content of the styrene-isoprene-styrene block copolymers in the binder resin is in the range of 1 to 15% by weight, preferably 2 to 12 % by weight. When the content is less than 1% by weight, the desired improvement of damping properties can not be obtained due to diffusion of the said block copolymers in the base resin. When the content exceeds 15% by weight, the strength and hardness of the base resin is lowered, thereby making it unable to maintain the intrinsic strength and hardness of the base resin.
As iron compound particles in the present invention, there can be used hematite particles, maghemite particles, magnetite particles, Berthollide compounds particles and hard ferrite particles such as strontium ferrite particles and barium ferrite particles, and hydrous iron oxide particles such as goethite (.alpha.-FeOOH) particles, akaganeite (.beta.-FeOOH) particles, lepidocrosite (.gamma.-FeOOH) particles and the like. Among them, magnetite particles, strontium ferrite particles and barium ferrite particles are preferred. The preferred BET specific surface of the magnetite particles is 3 to 40 m.sup.2 /g and the BET specific surface the barium ferrite particles or strontium ferrite particles is 0-3 to 20 m.sup.2 /g. The shape thereof is not limited, and it may be, for instance, granular, spindle, acicular, plate-like or the like. The granular shape is preferred. The average particle size of the iron compound particles usable in the present invention is in the range of 0.05 to 10 .mu.m. It is preferable in the range of 0.1 to 5 .mu.m due to advantageous in terms of properties of the damping material and economy.
The amount of iron compound particles used in the present invention is 1 to 20 parts by weight based on 100 parts by weight of the binder resin. When the amount is less than 1 part by weight, the desired excellent internal loss can not be obtained. When the amount exceeds 20 parts by weight, the bending modulus which is an index of strength of rigid resin, lowers to make it unable to obtain a satisfactory strength of the damping material. Also, specific gravity of the damping material increases, thereby vitiating the advantage of the resin of being lightweight The preferred content of iron compound particles is 3 to 20 parts by weight based on 100 parts by weight of the binder resin.
The damping material according to the present invention comprises the base resin, the styrene-isoprene-styrene block copolymer and the iron compound particles as essential components, but if necessary, other polymer(s), compatilizing agent, oxidation stabilizer, etc., may be blended within the range which does not impair the purpose of the present invention. For instance, polymers such as natural rubbers (NR), isoprene rubbers (IR), butadiene rubbers (BR), styrene-butadiene rubbers (SBR), ethylene-propylene-diene terpolymars (EPDM), ethylene-propylene rubbers (EPR), styrene-conjugated diene block copolymers and hydrogenation product thereof may be blended. The amount of the polymer is not more than 30 parts by weight, preferably in the range of 5 to 25 parts by weight based on 100 parts by weight of the binder resin.
For producing the damping material according to the present invention, masterbatch pellets for damping material described later and the base resin composed of at least one resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers are mixed by a suitable mixer such as Ribbon blender, Nauta mixer, Henschel mixer or Supermixer, and the resultant mixture is molded into the objective product by a suitable molding machine such as injection molding machine.
The masterbatch pellets for the damping material according to the present invention have a grain size of 1 to 10 mm, preferably 3 to 7 mm. When the grain size of pellets is less than 1 mm, the workability is bad in the production of pellets, while when the grain size exceeds 10 mm, it becomes difficult to disperse the pellets in base resin.
The grain shape is not specified, but it may be, for instance, indeterminate, columnar, spherical, flaky and the like.
As the base resin of the said masterbatch pellets, at least one resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers is used in an amount of not more than 70% by weight, preferably in the range of not more than 65% by weight based on the binder resin. When the amount of the base resin exceeds 70% by weight, it is difficult to obtain the desired concentration of styrene-isoprene-styrene block copolymer resin in production of damping material because of small content of styrene-isoprene-styrene block copolymer.
The composition of base resin in the masterbatch pellets may be the same combination of resins as base resin to be mixed with masterbatch pellets, or may be a different combination of the resins.
As styrene-isoprene-styrene block copolymer resin in the masterbatch pellets, there can be used the resins mentioned above and the amount thereof added is 30 to 100% by weight, preferably 35 to 100% by weight based on the binder resin of the masterbatch pellets. If the amount of this resin is less than 30% by weight, it is undesirable since the amount of masterbatch pellets necessary for producing the damping material increases.
As iron compound particles of the masterbatch pellets, those mentioned above can be used and the amount of the iron compound particles is 50 to 300 parts by weight, preferably 60 to 250 parts by weight based on 100 parts by weight of the binder resin. If the amount of the iron compound particles is less than 50 parts by weight, the amount of the masterbatch pellets necessary for producing the damping material increases. If the amount of the iron compound particles exceeds 300 parts by weight, it becomes difficult to adjust the content of the iron compound particles to a desired level since their content in the damping material is varied greatly by a slight change of the amount of the masterbatch pellets added. This is also causative of extensive mechanical abrasion.
The masterbatch pellets for the damping material according to the present invention are produced by mixing styrene-isoprene-styrene block copolymers and iron compound particles with base resin selected from polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymer, polycarbonates, polyphenylene ethers and modified polyphenylene ethers by a suitable mixing machine such as Ribbon blender, Nauta mixer, Henschel mixer, Supermixer or the like, and kneading and molding the resultant mixture by a known single-screw or twin-screw extruder, and cutting the molded product, or pulverizing and molding the resultant mixture kneaded by a Banbury mixer, press kneader or the like and cutting the molded product, thereby obtaining the desired granular material.
The damping material according to the present invention is produced by adding 1 to 30% by weight of the said masterbatch pellets to 70 to 99% by weight, preferably 75 to 95% by weight of the base resin comprising at least one resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers, and kneading and molding the resultant mixture. The preferable amount of the masterbatch pellets added 5 to 25% by weight, more preferably 5 to 20% by weight. When the amount of the masterbatch pellets added is less than 1% by weight, the effect of addition thereof is too small. When the amount of the masterbatch pellets exceeds of 30% by weight, the intrinsic strength and hardness of base resin may be adversely affected.
The structural materials of electrical or electronic equipments, casings or bodies of household electric appliances, office automation equipments, etc., a cartridge half, a cassette half and the like according to the present invention are produced from the damping material of the present invention, and the above-described production process can be employed for the production of the structural materials of electrical or electronic equipments, casings or bodies of household electric appliances, office automation equipments, etc., a cartridge half, a cassette half and the like.
The structural materials of electrical or electronic equipments, casings or bodies of household electric appliances, office automation equipments, etc., a cartridge half, a cassette half and the like according to the present invention have a loss factor of not less than 0.015, preferably not less than 0.020 at an-ordinary temperature (24.degree. C.), and a relative bending modulus of not less than 70%, preferably not less than 75% based on a bending modulus of structural materials, casings, a cartridge half, a cassette half made of only the base resin.
The fact that a damping material having an excellent internal loss in the practical temperature range, especially at around room temperature, while maintaining the intrinsic strength and hardness of rigid resin can be obtained according to the present invention may be accounted for by the followings.
It is considered that in the damping material according to the present invention, styrene-isoprene-styrene block copolymer is dispersed, in the form of fine lumps, in the base resin comprising at least one resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers, and a damping effect is produced by friction at the interface between the dispersed fine lumps of styrene-isoprene-styrene block copolymer and the base resin. The fact is particularly notable that the smaller the size of the said dispersed fine lumps, the greater becomes the contact area between the dispersed fine lumps of styrene-isoprene-styrene block copolymer and the base resin, resulting in a better damping property, that is, higher internal loss.
However, when the content of styrene-isoprene-styrene copolymer is increased, although the loss factor elevates, the intrinsic strength and hardness of the rigid resin, specifically its bending modulus, is reduced.
As a result of the present inventors' studies on the subject problem, it has been found that by using iron compound particles, it is possible to elevate the loss factor more than that of using conventional inorganic fillers such as mica other than iron compound, and by adding a small amount of styrene-isoprene-styrene block copolymer resin, the efficient enhancement of loss factor can be effected, while suppressing the lowering the strength and hardness of the base resin.
This effect may be attributed to the followings. The lumps of styrene-isoprene-styrene block copolymer dispersed in base resin can be made fine in size due to the iron compound particles, and consequently the dispersed state of the lumps thereof becomes finer, thereby elevating the damping effect by friction with the base resin, resulting in an increased loss factor.
By the way, as seen from Comparative Examples 13 and 14 described later, the damping property of the damping material comprising the base resin and iron compound particles dispersed in the base resin without blending styrene-isoprene-styrene block copolymer do not improved.
Further, a smaller amount of the iron compound particles than that of mica or other conventional filler is required for obtaining a same level of loss factor, and the amount of styrene-isoprene-styrene block copolymer to be added can be minimized. As a result, it is considered that a damping material showing an excellent internal loss in the practical temperature range, particularly at around room temperature, while maintaining the intrinsic strength and hardness of the rigid resin, can be obtained.
Thus, according to the present invention, by the synergistic effect of the combination and the said specific mixing ratios of (1) base resin comprising at least one resin selected from the group consisting of polypropylenes, polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers, preferably at least one resin selected from the group consisting of polystyrenes, acrylonitrile-butadiene-styrene copolymers, polycarbonates, polyphenylene ethers and modified polyphenylene ethers (2) styrene-isoprene-styrene block copolymer, and (3) iron compound particles, such damping material has a loss factor of not less than 0.015, preferably not less than 0.020 at an ordinary temperature (24.degree. C.), a relative bending modulus of not less than 70%, preferably not less than 75% based on a bending modulus of a damping material consisting of the base resin, and a specific gravity of 0..95 to 1.30.
The damping material according to the present invention, as described particularly in the Examples given below, has a high internal loss at around room temperature, while maintaining the intrinsic strength and hardness of rigid resin, so that it is capable of significant miniaturization, lightweight and thinning, and can be effectively applied to structural materials of electrical or electronic equipments, casings or bodies of office automation equipments or household electric appliances, parts of various kinds of machines and apparatus, internal parts of vehicles and ships, building materials, etc., particularly useful to cartridge half and cassette half of data cartridge tapes, video tapes, audio tapes etc., disk shell of optical discs, magneto-optical discs, magnetic discs, acoustic optical disc, etc.

EXAMPLES
The present invention will be explained in more detail hereinafter with reference to the following examples and comparative examples.
Loss factor .eta. used as an index of damping property, i.e., loss factor of the damping material was determined by injection molding a 200 mm.times.12.5 mm.times.3 mm test piece and measuring loss factor .eta. of this test piece by cantilever beam-type resonance method under the conditions of 24.degree. C. and 1 kHz.
Loss factor .eta. of casing of cassette half, household electric appliances or office automation equipments was determined in the followings. The casing was suspended from two points with a kite string. Then a metal hall (1.05 g in weight and 6 mm in diameter) suspended with a kite string (250 mm in length) was pulled up to an angle of 60.degree. from the vertical plane with its fulcrum taken vertically above the casing and dropped down to the casing to give vibrations to the central part of the casing. Transmission of vibrations was detected by a vibration pickup set at the bottom of the casing and data processing was made by FFT Analyzer 3550 (manufactured by B & K Corp.) under the condition of 24.degree. C. to determine loss factor .eta..
Bending modulus which is an index of strength of damping material was determined by injection molding a 80 mm.times.12.5 mm.times.3 mm test piece and measuring bending modulus of this test piece according to ASTM D-790.
Specific gravity was measured by a specific gravity hydrometer (manufactured by EW-120SG, Mirage Trading Co., Ltd.).
<Production of masterbatch pellets for damping material>
EXAMPLE 1
100 parts by weight of binder resin composed of 50 parts by weight of high-impact polystyrene resin (Sumibright M-574, produced by Sumitomo Chemical Co., Ltd.) and 50 parts by weight of styrene-isoprene-styrene block copolymer (VS-1, produced by Kuraray Co., Ltd.), and 100 parts by weight of granular magnetite (VD-803C, produced by Toda Kogyo Corporation; average particle size: 0.27 .mu.m and BET specific surface area: 4.5 m.sup.2 /g) were kneaded at 160.degree. C. by a twin-screw kneader and extruded from a 3 mm.phi. die, and the extrudate was cut to the approximately 3 mm units to obtain masterbatch pellets A.
EXAMPLES 2-9 AND COMPARATIVE EXAMPLES 1-2
The kind and amount of base resin, styrene-isoprene-styrene block copolymer and iron oxide particles in the masterbatch pellets were selected as shown in Table 1 to prepare masterbatch pellets for damping material B-K.
<Production of damping material>
EXAMPLE 10
90 parts of high-impact polystyrene resin (Sumibright M-574, produced by Sumitomo Chemical Co., Ltd.) used as base resin and 10 parts by weight of masterbatch pellets A were uniformly blended by a Henschel mixer and injection-molded into a strip-shaped test piece. The loss factor .eta. of this test piece at an ordinary temperature (24.degree. C.) was 0.021, its bending modulus was 25,400 kgf/cm.sup.2 (relative bending modulus: 95%) and its specific gravity was 1.09.
EXAMPLES 11-23 AND COMPARATIVE EXAMPLES 3-9
Samples of damping material were produced by the same procedure as Example 10 except that the kind of masterbatch pellets, the kind of base resin mixed with masterbatch pellets and the mixing ratios of said base resin and masterbatch pellets were changed as shown in Table 2. The characteristics of the samples of Examples 11-23 are shown in Table 4, and the characteristics of the samples of Comparative Examples 3-9 are shown in Table 5.
COMPARATIVE EXAMPLES 10-14
Samples of damping material were produced by blending and kneading base resin, styrene-isoprene-styrene block copolymer and flaky mica without using masterbatch pellets, at the ratios shown in Table 3, and molding the mixtures. The characteristics of these samples are shown in Table 5.
EXAMPLE 24
90 parts by weight of high-impact polystyrene resin (Sumibright M-574, produced by Sumitomo Chemical Co., Ltd.) used as base resin and 10 parts by weight of masterbatch pellets A were uniformly blended by a Henschel mixer and injection molded into a cassette half casing (structural materials) The loss factor .eta. of this casing at an ordinary temperature (24.degree. C.) was 0.031.
REFERENCE EXAMPLE 1
Cassette half of a commercial available cassette tape was taken as reference example and its loss factor at an ordinary temperature (24.degree. C.) was determined. It was 0.015.
EXAMPLE 2
93 parts by weight of polycarbonate (Novalex 7025A, produced by Mitsubishi Chemical Corporation) used as base resin and 7 parts by weight of masterbatch pellets F were uniformly blended by a Henschel mixer and injection molded into a gear. The loss factor .eta. of this gear at ordinary temperature (24.degree. C.) was 0.021.
REFERENCE EXAMPLE 2
A gear was produced by the same procedure as Example 25 except for not using masterbatch pellets. The loss factor .eta. of this gear at an ordinary temperature (24.degree. C.) was 0.008.
EXAMPLE 26
90 parts by weight of modified polyphenylene ether resin (Noryl 731, Japan G.E. Plastic Co., Ltd.) used as base resin and 10 parts by weight of masterbatch pellets G were uniformly blended by a Henschel mixer and injection molded into a dot printer casing (exterior part). The loss factor .eta. of this casing at an ordinary temperature (24.degree. C.) was 0.035.
REFERENCE EXAMPLE 3
A dot printer casing was produced by following the procedure of Example 26 without using masterbatch pellets. The loss factor .eta. of this casing at an ordinary temperature (24.degree. C.) was 0.010.
TABLE 1__________________________________________________________________________Production of masterbatch pellets for vibration damper__________________________________________________________________________ Binder resin (100 parts by weight) Base resin Content Content Content ABS resin (% by weight) HIPS resin (% by weight) PC resin (% by__________________________________________________________________________ weight) Ex. 1 -- -- Sumibright M574 50 -- -- (Sumitomo Chem.) Ex. 2 -- -- -- -- -- -- Ex. 3 ABS 15 (JSR*1)) 40 -- -- -- -- Ex. 4 ABS 15 (JSR*1)) 40 -- -- -- -- Ex. 5 -- -- -- -- Novalex 7025A 50 (*2) Ex. 6 -- -- -- -- Novalex 7025A 50 Ex. 7 -- -- -- -- -- -- Ex. 8 -- -- -- -- -- -- Ex. 9 -- -- -- -- -- -- Comp. Ex. 1 -- -- Sumibright M574 100 -- -- (Sumitomo Chem.) Comp. Ex. 2 ABS 15 (JSR) 40 -- -- -- --__________________________________________________________________________Binder resin (100 parts by weight) Inorganic fillerBase resin SIS resin Iron compound particles Content Content Content Content Pellets PPE resin (% by weight) PP resin (% by weight) Kind (% by weight) Kind (wt parts)__________________________________________________________________________ No. Ex. 1 -- -- -- -- VS-1 50 Granular magnetite 100 A (Kuraray) (average particle size: 0.27 .mu.m) Ex. 2 -- -- -- -- VS-1 100 Strontium ferrite plates 233 B (Kuraray) (average plate diameter: 1.2 .mu.m) Ex. 3 -- -- -- -- VS-1 60 Strontium ferrite plates 60 C (Kuraray) (average plate diameter: 1.2 .mu.m) Ex. 4 -- -- -- -- VS-1 60 Magnetite granular (averge 100 D (Kuraray) particle diameter: 0.27 .mu.m) Ex. 5 -- -- -- -- VS-1 50 Magnetite granular (averge 100 E (Kuraray) particle diameter: 0.27 .mu.m) Ex. 6 -- -- -- -- VS-1 50 Magnetite granular (averge 233 F (Kuraray) particle diameter: 0.27 .mu.m) Ex. 7 Noryl 731 50 -- -- VS-1 50 Magnetite plates (averge 100 G (*3) (Kuraray) particle diameter: 0.27 .mu.m) Ex. 8 Noryl 731 50 -- -- VS-1 50 Magnetite granular (averge 233 H (Kuraray) particle diameter: 0.27 .mu.m) Ex. 9 -- -- K6014 50 VS-1 50 Granular magnetite (averge 100 I (Chisso) (Kuraray) particle diameter: 0.27 .mu.m) Comp. -- -- -- -- -- -- Magnetite granular (averge 100 J Ex. 1 particle diameter: 0.27 .mu.m) Comp. -- -- -- -- VS-1 60 Magnetite granular 400 K Ex. 2 (Kuraray) (particle diameter: 0.27 .mu.m)__________________________________________________________________________ *1) Produced by Japan Synthetic Rubber Co., Ltd. *2) Produced by Mitsubishi Chemical Co., Ltd. *3) Produced by Japan G. E. Plastic Co., Ltd.
TABLE 2______________________________________Formulations for producing vibration damperMasterbatch pellets Base resin Content Content (parts by (part by Kind weight) Kind weight)______________________________________Ex. 10 A 10 HIPS resin 90 (Sumibright M574) Ex. 11 A 20 HIPS resin 80 (Sumibright M574) Ex. 12 A 10 ABS resin 90 (ABS 15) Ex. 13 B 10 ABS resin 90 (ABS 15) Ex. 14 C 25 ABS resin 75 (ABS 15) Ex. 15 D 7 ABS resin 93 (ABS 15) Ex. 16 D 10 ABS resin 90 (AB5 15) Ex. 17 E 12.5 PC resin 87.5 (Novalex 7025A) Ex. 18 F 7 PC resin 93 (Novalex 7025A) Ex. 19 F 12.5 PC resin 87.5 (Novalex 7025A) Ex. 20 G 10 PPE resin 90 (Noryl 731) Ex. 21 H 7 PPE resin 93 (Noryl 731) Ex. 22 H 10 PPE resin 90 (Noryl 731) Ex. 23 I 10 PP resin 90 (K 6014) Comp. -- -- HIPS resin 100 Ex. 3 (Sumibright M574) Comp. -- -- ABS resin 100 Ex. 4 (ABS 15) Comp. -- -- PC resin 100 Ex. 5 (Novalex 7025A) Comp. -- -- PPE resin 100 Ex. 6 (Noryl 731) Comp. -- -- PP resin 100 Ex. 7 (K 6014) Comp. J 10 ABS resin 90 Ex. 8 (ABS 15) Comp. K 35 ABS resin 65 Ex. 9 (ABS 15)______________________________________
TABLE 3______________________________________Formulations for producing vibration damper bydirect kneading Binder resin (100 parts by weight) HIPS resin PC resin Content Content Kind (wt %) Kind (wt %)______________________________________ Comp. Sumibright M574 97.4 -- -- Ex. 10 (Sumitomo Chem.) Comp. Sumibright M574 98.7 -- -- Ex. 11 (Sumitomo Chem.) Comp Sumibright M574 98.7 -- -- Ex. 12 (Sumitomo Chem.) Comp. Sumibright M574 100 -- -- Ex. 13 (Sumitomo Chem.) Comp. -- -- PC resin 100 Ex. 14 (Novalex 7025A)______________________________________Formulations for producing vibration damper by direct kneading Binder resin (100 parts by weight)PPE resin SIS resin Content Content Kind (wt %) Kind (wt %)______________________________________ Comp. -- -- VS-1 2.6 Ex. 10 (Kuraray) Comp. -- -- VS-1 1.3 Ex. 11 (Kuraray) Comp. -- -- VS-1 1.3 Ex. 12 (Kuraray) Comp. -- -- -- -- Ex. 13 Comp. -- -- -- -- Ex. 14______________________________________Formulations for producing vibration damper by direct kneading Inorganic fillerIron compound Mica Content Content Kind (wt parts) Kind (wt parts)______________________________________ Comp. -- -- -- -- Ex. 10 Comp. -- -- Flaky mica 5.3 Ex. 11 (plate diameter: 150 .mu.m) Comp. -- -- Flaky mica 11.1 Ex. 12 (plate diameter: 150 .mu.m) Comp. Granular 4.0 -- -- Ex. 13 magnetite (average particle diameter: 0.27 .mu.m) Comp. Strontium 11.1 -- -- Ex. 14 ferrite plates (average particle diameter: 1.2 .mu.m)______________________________________
TABLE 4______________________________________Composition of vibration damper Binder resin (100 parts by weight)HIPS resin ABS resin Content Content Kind (parts) Kind (wt %)______________________________________ Ex. 10 Sumibright M574 97.4 -- -- (Sumitomo Chem.) Ex. 11 Sumibright M574 94.4 -- -- (Sumitomo Chem.) Ex. 12 Sumibright M574 2.6 ABS 15 94.8 (Sumitomo Chem.) (JSR*2)) Ex. 13 -- -- ABS 15 96.8 (JSR) Ex. 14 -- -- ABS 15 89.7 (JSR) Ex. 15 -- -- ABS 15 97.8 (JSR) Ex. 16 -- -- ABS 15 96.8 (JSR) Ex. 17 -- -- -- -- Ex. 18 -- -- -- -- Ex. 19 -- -- -- -- Ex. 20 -- -- -- -- Ex. 21 -- -- -- -- Ex. 22 -- -- -- -- Ex. 23 -- -- -- --______________________________________Composition of vibration damper Binder resin (100 parts by weight)PC resin PPE resin PP resin Content Content Content Kind (wt %) Kind (wt %) Kind (wt %)______________________________________ Ex. 10 -- -- -- -- -- -- Ex. 11 -- -- -- -- -- -- Ex. 12 -- -- -- -- -- -- Ex. 13 -- -- -- -- -- -- Ex. 14 -- -- -- -- -- -- Ex. 15 -- -- -- -- -- -- Ex. 16 -- -- -- -- -- -- Ex. 17 Novalex 96.7 -- -- -- -- 7025A Ex. 18 Novalex 98.9 -- -- -- -- 7025A Ex. 19 Novalex 97.9 -- -- -- -- 7025A Ex. 20 -- -- Noryl 97.4 -- -- 731 *4) Ex. 21 -- -- Noryl 98.9 -- -- 731 Ex. 22 -- -- Noryl 98.4 -- -- 731 Ex. 23 -- -- -- -- K-6014 97.4 (Chisso)______________________________________Composition of vibration damper Binder resin (100 parts by weight) Inorganic filler SIS resin Iron compound particles Content Content Kind (wt %) Kind (wt %)______________________________________ Ex. 10 VS-1 2.6 Granular magnetite 5.3 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 11 VS-1 5.6 Granular magnetite 11.1 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 12 VS-1 2.6 Granular magnetite 5.3 (Kurarav) (particle diameter: 0.27 .mu.m) Ex. 13 VS-1 3.2 Strontium ferrite plates 7.5 (Kuraray) (plate diameter: 1.2 .mu.m) Ex. 14 VS-1 10.3 Strontium ferrite plates 10.3 (Kuraray) (plate diameter: 1.2 .mu.m) Ex. 15 VS-1 2.2 Granular magnetite 3.6 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 16 VS-1 3.2 Granular magnetite 5.3 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 17 VS-1 3.3 Granular magnetite 6.5 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 18 VS-1 1.1 Granular magnetite 5.2 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 19 VS-1 2.1 Granular magnetite 9.6 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 20 VS-1 2.6 Granular magnetite 5.3 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 21 VS-1 1.1 Granular magnetite 5.2 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 22 VS-1 1.6 Granular magnetite 7.5 (Kuraray) (particle diameter: 0.27 .mu.m) Ex. 23 VS-1 2.6 Granular magnetite 5.3 (Kuraray) (particle diameter: 0.27 .mu.m)______________________________________Composition of vibration damper Properties of vibration damperInorganic Bending filler modulus of Mica elasticity Content Loss Measured Relative (part by factor values values Specific Kind weight) *1) (kgf/cd) (%) gravity______________________________________ Ex. 10 -- -- 0.021 25400 95 1.09 Ex. 11 -- -- 0.039 23500 88 1.13 Ex. 12 -- -- 0.028 23700 95 1.09 Ex. 13 -- -- 0.027 22800 91 1.11 Ex. 14 -- -- 0.059 19500 78 1.12 Ex. 15 -- -- 0.020 24200 97 1.07 Ex. 16 -- -- 0.031 23800 95 1.09 Ex. 17 -- -- 0.024 20600 94 1.23 Ex. 18 -- -- 0.021 21100 97 1.23 Ex. 19 -- -- 0.025 20200 93 1.27 Ex. 20 -- -- 0.023 23800 95 1.10 Ex. 21 -- -- 0.020 24500 98 1.10 Ex. 22 -- -- 0.028 23200 93 1.14 Ex. 23 -- -- 0.026 11600 93 0.96______________________________________ *1) Measuring conditions: 24.degree. C., 1 kHz *2) JSR: Produced by Japan Synthetic Rubber Co., Ltd. *3) Produced by Mitsubishi Chemical Co., Ltd. *4) Produced by Japan G.E. Plastic Co., Ltd.
TABLE 5______________________________________Composition of vibration damper Binder resin (100 parts by weight)HIPS resin ABS resin Content Content (% by (% by Kind weight) Kind weight)______________________________________ Comp. Sumibright M574 100 -- -- Ex. 3 (Sumitomo Chem.) Comp. -- -- ABS 15 100 Ex. 4 (JSR*2)) Comp. -- -- -- -- Ex. 5 Comp. -- -- -- -- Ex. 6 Comp. -- -- -- -- Ex. 7 Comp. Sumibright M574 5.3 ABS 15 94.7 Ex. 8 (Sumitomo Chem.) (JSR) Comp. -- -- ABS 15 94.2 Ex. 9 (JSR) Comp. Sumibright M574 97.4 -- -- Ex. 10 (Sumitomo Chem.) Comp. Sumibright M574 98.7 -- -- Ex. 11 (Sumitomo Chem.) Comp. Sumibright M574 98.7 -- -- Ex. 12 (Sumitomo Chem.) Comp. Sumibright M574 100 -- -- Ex. 13 (Sumitomo Chem.) Comp. -- -- -- -- Ex. 14______________________________________Composition of vibration damper Binder resin (100 parts by weight)PC resin PPE resin PP resin Content Content Content (% by (% by (% by Kind weight) Kind weight) Kind weight)______________________________________ Comp. -- -- -- -- -- -- Ex. 3 Comp. -- -- -- -- -- -- Ex. 4 Comp Novalex 100 -- -- -- -- Ex. 5 7025A Comp -- -- Noryl 100 -- -- Ex. 6 731 *4) Comp. -- -- -- -- K6014 100 Ex. 7 (Chisso) Comp. -- -- -- -- -- -- Ex. 8 Comp. -- -- -- -- -- -- Ex. 9 Comp. -- -- -- -- -- -- Ex. 10 Comp. -- -- -- -- -- -- Ex. 11 Comp. -- -- -- -- -- -- Ex. 12 Comp. -- -- -- -- -- -- Ex. 13 Comp. Novalex 100 -- -- -- -- Ex. 14 7025A______________________________________Composition of vibration damper Binder resin Inorganic filler (100 parts by weight) Iron compound particlesSIS resin Content Content (part by Kind (wt %) Kind weight)______________________________________ Comp. -- -- -- -- Ex. 3 Comp. -- -- -- -- Ex. 4 Comp. -- -- -- -- Ex. 5 Comp. -- -- -- -- Ex. 6 Comp. -- -- -- Ex. 7 Comp. -- -- Granular magnetite 5.3 Ex. 8 (particle diameter: 0.27 .mu.m) Comp. VS-1 5.8 Granular magnetite 38.9 Ex. 9 (Kuraray) (particle diameter: 0.27 .mu.m) Comp. VS-1 2.6 -- -- Ex. 10 (Kuraray) Comp. VS-1 1.3 -- -- Ex. 11 (Kuraray) Comp. VS-1 1.3 -- -- Ex. 12 (Kuraray) Comp. -- -- Granular magnetite 4.0 Ex. 13 (particle diameter: 0.29 .mu.m) Comp. -- -- Strontium ferrite plates 11.1 Ex. 14 (plate diameter: 1.2 .mu.m)______________________________________Composition of vibration damper Properties of vibration damperInorganic Bending filler modulus of Mica elasticity Content Loss Measured Relative (part by factor values values Specific Kind weight) *1) (kgf/cd) (%) gravity______________________________________ Comp. -- -- 0.009 26700 100 1.05 Ex. 3 Comp. -- -- 0.010 25000 100 1.05 Ex. 4 Comp. -- -- 0.008 21800 100 1.19 Ex. 5 Comp. -- -- 0.010 25000 100 1.06 Ex. 6 Comp. -- -- 0.012 12500 100 0.90 Ex. 7 Comp. -- -- 0.011 26100 98 1.09 Ex. 8 Comp. -- -- 0.050 15100 60 1.50 Ex. 9 Comp. -- -- 0.013 25300 95 1.05 Ex. 10 Comp. Flaky mica 5.3 0.012 26500 99 1.08 Ex. 11 (plate diameter: 150 .mu.m) Comp. Flaky mica 11.1 0.013 23500 88 1.11 Ex. 12 (plate diameter: 150 .mu.m) Comp. -- -- 0.010 26000 97 1.08 Ex. 13 Comp. -- -- 0.008 21500 99 1.29 Ex. 14______________________________________ *1) Measuring conditions: 24.degree. C., 1 kHz *2) JSR: Produced by Japan Synthetic Rubber Co., Ltd *3) Produced by Mitsubishi Chemical Co., Ltd. *4) Produced by Japan G.E. Plastic Co., Ltd.

Number	Date	Country
54845	Jun 1982	EPX
287652	Dec 1991	JPX
59233	Mar 1993	JPX

Material having a damping property and masterbatch pellets therefor

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Parent Case Info

US Referenced Citations (1)

Foreign Referenced Citations (3)

Non-Patent Literature Citations (3)

Continuations (1)

Entry
Database WPI, Section CH, Week 9206, Derwent Publications Ltd., London, GB, Dec. 18, 1991. See Abstract.
Database WPI, Section CH Week 8523, Derwent Publications Ltd., London, GB, Apr. 25, 195, see Abstract.
Matthews "Polymer Mixing Technology"; 1984 pp. 225-226.