Measuring semiconductor doping using constant surface potential corona charging

Information

  • Patent Grant
  • 10969370
  • Patent Number
    10,969,370
  • Date Filed
    Friday, June 5, 2015
    9 years ago
  • Date Issued
    Tuesday, April 6, 2021
    3 years ago
Abstract
An example method of characterizing a semiconductor sample includes measuring an initial value, Vin, of a surface potential at a region of a surface of the semiconductor sample, biasing the semiconductor sample to have a target surface potential value (V0) of 2V or less, and depositing a monitored amount of corona charge (ΔQ1) on the region of the surface after adjusting the surface potential to the target value. The method also includes measuring a first value, V1, of the surface potential at the region after depositing the corona charge, determining the first change of surface potential (ΔV1=V1−V0), and determining the first capacitance value C1=ΔQ1/ΔV1, and characterizing the semiconductor sample based on V0, V1, ΔV1, ΔQ1 and C1.
Description
TECHNICAL FIELD

This disclosure relates to systems and methods for measuring a semiconductor doping concentration, in particular, using constant surface potential corona charging.


BACKGROUND

Doping a semiconductor with donor or acceptor impurities changes the semiconductor electrical conductivity. As electrical conductivity is generally an important characteristic of a semiconductor material, for quality control purposes, it can be beneficial to measure or monitor a semiconductor doping concentration (e.g., the concentration of doping atoms per volume of the semiconductor) during the production of semiconductor materials and devices. As examples, a manufacturing process can include steps for monitoring the doping concentration of semiconductor wafers sliced from semiconductor crystals, monitoring the doping concentration of thin epitaxial layers grown or deposited on bulk wafers, and monitoring the doping concentration of semiconductors after the performance of deliberate doping processes (e.g., after impurity diffusion or ion implantation processes).


SUMMARY

In general, in an aspect, a method of characterizing a semiconductor sample includes measuring an initial value, Vin, of a surface potential at a region of a surface of the semiconductor sample, biasing the semiconductor sample to have a target surface potential value (V0) of 2V or less, and depositing a monitored amount of corona charge (ΔQ1) on the region of the surface after adjusting the surface potential to the target value. The method also includes measuring a first value, V1, of the surface potential at the region after depositing the corona charge, determining the first change of surface potential (ΔV1=V1−V0), determining the first capacitance value C1=ΔQ1/ΔV1, and characterizing the semiconductor sample based on V0, V1, ΔV1, ΔQ1 and C1.


Implementations of this aspect may include or more of the following features.


In some implementations, the method can further include a series of consecutive monitored corona charge deposition steps with adjustment of the surface potential to the target value (V0) before each deposition step and measuring a surface potential value after each deposition step and using the results of each step to determine corresponding incremental values of surface potential (ΔVk), corona charge (ΔQk), capacitance (Ck), and cumulative values of surface voltage (Vk=ΣΔVk) and charge (Qk=ΣΔQk), where k refers to the kth step, and the semiconductor sample is characterized based on the values for V0, Vk, ΔVk, Qk and Ck. The corona charge ΔQk can be corrected by a calibration function F(V, I) to obtain a charge density (ΔQck) under a probe used for measuring the surface potential. ΔQck can be used to determine a corrected space charge capacitance, Cck=ΔQck/ΔVk. A corrected net corona charge density Qck=ΣΔQck and the corrected space charge capacitance Cck can be used to determine a doping density of the semiconductor sample from a slope of a 1/Cck2 vs. Vk plot, a slope of a Qck2 vs. Vk plot or from a CckQck capacitance charge factor. A quality of the calibration function can be determined using the capacitance charge factor CckQck. The method can further include performing a charge density calibration using a semiconductor calibrating sample with a known doping density over a distance W under a surface of the semiconductor calibrating sample. The corona charge deposition and surface potential adjustment steps can be repeated until a target doping monitoring depth is reached.


In some implementations, a polarity of the corona charging can be such that it creates a depletion surface space charge region in the semiconductor sample. The semiconductor sample can be an n-type semiconductor and the corona charge is deposited using a negative charging polarity. The semiconductor sample can be a p-type semiconductor and the corona charge is deposited using a positive charging polarity.


In some implementations, characterizing the semiconductor sample can include determining a doping density and/or a doping profile.


In some implementations, the semiconductor sample can include a wide bandgap semiconductor.


In some implementations, the semiconductor sample can include a semiconductor selected from the group consisting of SiC, GaN, ZnO, ZnS, and ZnSe.


In some implementations, the surface potential measurements can be performed using a non-contact vibrating probe.


In some implementations, surface potential measurements can be performed using a capacitive electrode.


In some implementations, V0 can be 0.5 V or less.


In some implementations, V0 can be approximately 0 V.


In some implementations, the deposited corona charge can be photo-neutralized and removed from the semiconductor surface using illumination with light of photon energy sufficient to generate excess carriers in the semiconductor sample. The method can further include repeating characterization of the semiconductor sample after photo-neutralizing the deposited corona charge prior to each repetition.


In general, in another aspect, a method includes repeatedly depositing a corona charge at a region of a surface of a sample after biasing a surface potential at the region to have the same target value.


Among other advantages, embodiments may be used to measure the doping concentration of a semiconductor sample without fabricating any permanent or temporary metal-semiconductor diodes and without any invasive electrical contacts. Thus, in some cases, measurements can be obtained relatively quickly, and the semiconductor wafer can be further processed or used after the doping measurement is performed. Further, in some implementations, electrical charges can be deposited onto a surface of a semiconductor sample incrementally and according to a constant compensated surface potential value (e.g., biased to zero or some other constant value), such that the effects of electrostatic charge repulsion are reduced, or in some cases, practically eliminated. Further still, in general, implementations of these techniques can be performed without the use of mercury, a hazardous material that is often subject to environment regulation or other usage restrictions.


The details of one or more embodiments are set forth in the accompanying drawings and the description below. Other features and advantages will be apparent from the description and drawings, and from the claims.





DESCRIPTION OF DRAWINGS


FIG. 1A is a schematic diagram of an example system for measuring doping concentrations of semiconductor samples in a first configuration.



FIG. 1B is a schematic diagram of the example system shown in FIG. 1A in a second configuration.



FIG. 1C is a schematic diagram of the example system shown in FIG. 1A in a third configuration.



FIG. 2 is an example 1/C2 vs. V plot with and without corona charge areal density correction for a very uniformly doped p-type epitaxial SiC semiconductor sample with N=2.37×1017 cm−3.



FIG. 3 is an example CQ vs. V plot for very uniformly doped p-type epitaxial SiC with N=2.37×1017 cm−3 with and without corona charge correction.



FIG. 4 is a dopant depth profile for an example p-type epitaxial SiC semiconductor sample with constant doping density N=2.37×1017 cm−3 determined using the CQ factor with and without corona charge correction.



FIG. 5 shows example charge profiles for a semiconductor wafer after an initial deposition of charge, after a sequence of ten depositions of charge, and after a sequence of twenty depositions of charge.



FIG. 6 shows an example method of characterizing a semiconductor sample.



FIG. 7 shows an example method of depositing a corona charge at a region of a surface of a sample.





Like reference symbols in the various drawings indicate like elements.


DETAILED DESCRIPTION

The present disclosure pertains to measuring doping concentrations of a semiconductor using accurate, fast-feedback, non-invasive, and non-contact techniques. Implementations of these techniques include measuring the surface potential at a test site of a semiconductor, applying a bias voltage to the semiconductor in order to obtain a particular surface potential at the test site (e.g., zero, substantially zero, or some other constant value), and depositing a charge on the test site of the semiconductor surface (e.g., using corona discharge in air). This sequence of surface potential measurement, surface potential compensation, and charge deposition can be repeated multiple times in order to create a precisely controlled depletion surface space charge layer, similar to that of a Schottky barrier in metal contact diodes. The semiconductor depletion space charge capacitance C can then be measured to determine the doping concentration of the semiconductor in the depletion space charge layer, and to obtain doping depth profiles beneath the semiconductor surface. In some implementations, the product of the semiconductor depletion space charge capacitance and the total charge deposited at the test site, CQ, can be used as a measurement quality factor for precise doping depth profiling.


As the surface potential of the semiconductor is compensated after each incremental deposition of charge, the effects of electrostatic charge repulsion are reduced, or in some cases, practically eliminated. Further, as the depletion space charge layer can be formed without fabrication of any permanent or temporary metal-semiconductor diodes and without any invasive electrical contacts, measurements can be obtained relatively quickly, and the semiconductor wafer can be further processed or used after the doping measurement is performed. Further, in general, implementations of these techniques can be performed without the use of mercury, a hazardous material that is often subject to environment regulation or other usage restrictions.


Implementations of these techniques can be used to measure doping concentrations of semiconductor materials capable of retaining corona deposited charge. This can include, for example, wide bandgap semiconductors (e.g., SiC, GaN, or ZnO semiconductors that are not exposed to short wavelength illumination). This can also include, for example, semiconductors that have been coated with dielectric films that prevent corona charge neutralization (e.g., SiO2, or Si3N4 films).


Further, implementations of these techniques can be used to improve the manufacturing of semiconductor wafers used for a variety of applications. For example, these techniques can extend the range of corona-induced depletion voltages to relatively high voltages (e.g., hundreds of volts), which can be advantageous for conducting doping profiling in SiC and GaN semiconductor wafers for high voltage power devices. As another example, these technique can be used to improve the manufacturing of semiconductor wafers that are used for optoelectronic applications.


In some cases, the described techniques also can be applied to other corona charge-based characterization processes, including the measurement of dielectrics and interface on wafers and micro-test sites.


An example system 100 for measuring the doping concentration of a semiconductor sample is shown in FIG. 1A. The system 100 includes a stage assembly 110, a Kelvin probe 120, a corona charging station 130, a voltage compensation assembly 140, and a processing module 150.


In an example operation of the system 100, a semiconductor sample 160 is placed on the stage assembly 110 and is positioned for examination by the Kelvin probe 120. The Kelvin probe 120 measures the surface potential of a test site 162 on the front surface of the semiconductor sample 160. The voltage assembly 140 then applies a bias voltage to the semiconductor sample 160 (e.g., at the back surface 164 of semiconductor sample 160) to compensate the surface potential of the test site to a particular value (e.g., zero volts, 0.5V or less, or some other value). The semiconductor sample 160 is then repositioned beneath the corona charging station 130, which deposits a charge on the test site 162 of the semiconductor sample 160. After the charge is deposited, surface potential measurement, surface potential compensation, and charge deposition are repeated one or more times in order to create a depletion space charge layer that is induced beneath the surface on the semiconductor sample 160 by the deposited charge. After each of these repetitions, the semiconductor depletion space charge capacitance is determined, and based on these determinations, the processing module 150 determines the doping concentration of the semiconductor and/or doping depth profiles beneath the semiconductor surface. During this process, the semiconductor sample 160 can be shielded from stray illumination (e.g., by enclosing all or part of the system 100 in a light-shielded housing or facility).


The stage assembly 110 supports and positions the semiconductor sample 160 during examination by the system 100. The stage assembly 110 includes a chuck 112 capable of conducting electric charge to and from the semiconductor sample (e.g., a semiconductor wafer). In some cases, the chuck 112 can be composed of one or more electrically conductive materials. For example, the chuck 112 can be composed of aluminum, and coated with titanium nitride. In practice, other conductive materials are also possible, depending on the implementation.


The semiconductor sample 160 (e.g., semiconductor wafer) is secured to the chuck 112 such that electrical contact is provided between the semiconductor sample 160 (e.g., the back surface 164) and the chuck 112. The semiconductor sample 160 can be non-invasively secured to the chuck 112. For example, in some cases, the semiconductor sample 160 can be secured to the chuck 112 through suction applied by a vacuum 114. Although a vacuum 114 is shown in FIG. 1A, in practice, other securing mechanisms (e.g., pins, brackets, and/or ties) are also possible, depending on the implementation.


The stage assembly 110 can move along one or more axes, such that the semiconductor sample 160 can be translated in relation to the Kelvin probe 120 and the charging station 130. For example, in some cases, the chuck 112 can move along the x, y, and/or z axes of a Cartesian coordinate system in order to move the semiconductor sample 160 along any of three dimensions in relation to the other components of the system 100.


As shown in FIG. 1A, the stage assembly 110 initially positions the semiconductor sample 160 beneath the Kelvin probe 120, such that the Kelvin probe 120 can measure the surface potential of the test site 162. Measurements obtained by the Kelvin probe 120 are transmitted to the processing module 150 for analysis.


The Kelvin probe 120 can measure the surface potential of the test site 162 without contacting the semiconductor sample 160. The surface potential can be obtained by measuring the constant potential difference (CPD) between a reference probe having a known work function, and the semiconductor surface having an unknown work function. Typically, the probe is placed above the surface of the semiconductor test site and is vibrated, which causes a periodic variation in capacitance between the probe and the semiconductor test site and causes a time-varying current into the probe. This current may be measured and nullified by applying an opposite voltage on the probe or semiconductor surface. This voltage, known as the backing potential, results in zero current when it is equal to the CPD between the probe and the semiconductor surface. This voltage can be determined, for example, using a measuring system 122.


Although a vibrating Kelvin probe 120 is shown in FIG. 1A, in practice, other non-contact vibrating probes or measurement systems also can be used, depending on the implementation. For example, in some cases, a Monroe probe can be used instead of a Kelvin probe


In some implementations, the vibrating probe 120 can have a particular diameter (e.g., 1 mm, 2 mm, or some other diameter). In some cases, the Kelvin probe 120 can move with respect to the semiconductor sample (e.g., move laterally across the semiconductor sample) in order to measure the surface potential of several test sites on the semiconductor sample.


During measurement of the surface potential of the test site 162, the voltage compensation assembly 140 is configured to electrically ground the back surface 164 of the semiconductor sample 160. For example, as shown in FIG. 1A, the voltage compensation assembly 140 includes a direct current (DC) voltage source 142 coupled to the chuck 112 through a switch 148a, and an input capacitor 146 coupled the chuck 112 through a switch 148b. During measurement of the surface potential of the test site 162, the switch 148a is open, and the switch 148b is in position A. As a result, the chuck 112 and the back surface 164 of the semiconductor sample 160 are both electrically grounded.


The system 100 compensates the test site surface potential by applying a bias voltage to the back surface 164 of the semiconductor sample 160. As shown in FIG. 1A, in some implementations, this bias voltage is applied by electrically coupling the input capacitor 146 to the back surface 164 of the semiconductor sample 160, and charging the input capacitor 146 until a particular bias voltage is obtained across it. As shown in FIG. 1B, this can be performed by closing the switch 148a and toggling the switch 148b to position B. When the switches 148a-148b are in these positions, the DC voltage source 142 and the input capacitor 146 are each electrically coupled together and to the chuck 112. Thus, the DC voltage sources 142 electrically charges the input capacitor 146. Further, as the input capacitor 146 is electrically coupled to the chuck 112 and the back surface 164 of the semiconductor sample 160, the voltage across the input capacitor 146 biases the test site surface potential.


The bias voltage of the input capacitor 146 can be monitored using a measuring system 170 in parallel with the input capacitor 146. Measurements obtained by the measuring system 170 can be transmitted to the processing module 150 for analysis.


The DC voltage source 142 can be configured to charge the input capacitor 146 to a particular bias voltage in order to compensate the surface potential at the test site 162. In some cases, the DC voltage source 142 can be configured to achieve a zero, or substantially zero surface potential at the test site 162. For instance, the DC voltage source 142 can charge the input capacitor 146 such that the bias voltage across the input capacitor 146 is the opposite of the surface voltage that was measured by the Kelvin probe 120. That is, if the Kelvin probe 120 measured a surface voltage of V0 while the back surface 164 was electrically grounded (e.g., while the switch 148a was open and the switch 148b was in position A), while the switch 148b is closed and the switch 148b is in position B, the DC voltage source 142 can apply a voltage of −V0 across the input capacitor 146. Thus, the surface potential at the test site 162 is compensated to zero once the input capacitor 146 is charged and a bias voltage of −V0 is obtained across it.


After the input capacitor 146 is charged, an electrical charge is deposited onto the test site 162 according to the biased surface potential condition. As shown in FIG. 1C, the semiconductor sample 160 is repositioned by the stage assembly 110, such that the test site 162 is positioned beneath the corona charging station 130. The corona charging station 130 then deposits a charge on the test site 162. During charge deposition, the switch 148a is in an open position, and the switch 148b is in position B. Thus, the input capacitor 146 continues to bias the test site's surface potential during charge deposition.


In some cases, the corona charging station 130 deposits charge onto the test site 162 through corona discharge in air. For example, as shown in FIG. 1C, the corona charging station 130 includes a high voltage source 132, and a corona charging gun 134 with a discharge needle electrode. High voltage creates corona discharge and the ions generated by the corona discharge are directed from the charging gun 134 towards the test site 162, and are deposited on the surface of the test site 162. As a result of the charge deposition, a slight change of voltage is induced across the input capacitor 146. This voltage change, δV, can be used as an in situ measure of the deposited charge Qin=CinδV, where Cin is the capacitance of the input capacitor 146 and Qin is the deposited charge. This change in voltage can be measured using the measuring system 170 in parallel with the input capacitor 146. Measurements obtained by the measuring system 170 can be transmitted to the processing module 150 for analysis.


In some implementations, the corona charging station 130 is configured to deposit charge within a particular region (e.g., a circular region having, e.g., a diameter of approximately 8-10 mm), and the Kelvin probe 120 can be configured to measure the surface potential of a smaller sub-region within the charge deposition region (e.g., a circular sub-region having a diameter of approximately 2 mm). This can be beneficial, for example, to ensure that charge is being uniformly deposited across the entirety of the region being measured by the Kelvin probe 120.


After charge is deposited onto the semiconductor sample 160, the sequence of surface potential measurement, surface potential compensation, and charge deposition shown in FIGS. 1A-1C can be repeated one or more times in order to vary, in a precisely controlled manner, the surface depletion space charge layer at the test site 162. For example, the system 100 can be returned to the configuration shown in FIG. 1A, and a new surface voltage measurement V1 can be determined for the test site 162. Likewise, the system 100 can again be switched to the configuration shown in FIG. 1B, in order to bias the surface potential of the test site 162 according to the new voltage measurement V1 (e.g., by charging the input capacitor 146 to a bias voltage of −V1 and coupling the input capacitor 146 to the back surface 164 of the semiconductor sample 160). Further, the system 100 can again be switched to the configuration shown in FIG. 1C, such that charge can again be deposited onto the test site 162 according to the biased surface potential condition. In this manner, charge can be incrementally deposited onto the test site 162 according to a consistent or substantially consistent surface potential. Further still, the voltage change that is induced during each charge deposition step can be observed and used as an in situ measure of the deposited charge.


The processing module 150 determines the doping concentration of the semiconductor and/or doping depth profiles beneath the semiconductor surface based on the semiconductor depletion space charge capacitance. For example, the voltage difference caused by charging, ΔV=V1−V0, and the density of deposited charge, ΔQ per cm2, can be used to determine the semiconductor space charge capacitance, C=ΔQ/ΔV. As described in greater detail below, this relationship can be used to estimate the doping concentration of the semiconductor sample.


In some implementations, the processing module 150 can be implemented using digital electronic circuitry, or in computer software, firmware, or hardware, or in combinations of one or more of them. For example, in some cases, the processing module 150 can be implemented, at least in part, as one or more computer programs (e.g., one or more modules of computer program instructions, encoded on computer storage medium for execution by, or to control the operation of, a data processing apparatus). A computer storage medium can be, or can be included in, a computer-readable storage device, a computer-readable storage substrate, a random or serial access memory array or device, or a combination of one or more of them. The term “processing apparatus” encompasses all kinds of apparatus, devices, and machines for processing data, including by way of example a programmable processor, a computer, a system on a chip, or multiple ones, or combinations, of the foregoing. The apparatus can include special purpose logic circuitry, e.g., an FPGA (field programmable gate array) or an ASIC (application specific integrated circuit). The apparatus can also include, in addition to hardware, code that creates an execution environment for the computer program in question, e.g., code that constitutes processor firmware, a protocol stack, a database management system, an operating system, a cross-platform runtime environment, a virtual machine, or a combination of one or more of them. The apparatus and execution environment can realize various different computing model infrastructures, such as web services, distributed computing and grid computing infrastructures.


In some implementations, the processing module 150 can also control the operation one or more of the other components of the system 100. For example, in some implementations, the processing module 150 can be communicatively coupled to the stage assembly 110, the Kelvin probe 120, the corona charging station 130, and/or the voltage compensation assembly 140 in order to control each of these components.


The sequence of surface potential measurement, surface potential compensation, and charge deposition can be repeated any number of times in order to create a particular surface depletion layer. For instance, in some cases, the sequence can be repeated for a prescribed number repetitions (e.g., 10 repetitions, 20 repetitions, 30 repetitions, or any other number of repetitions) or until a desired width of the surface depletion layer W is obtained. In some cases, a larger number of incremental charging steps (e.g., 10 or more, 20 or more) can be used for doping depth profiling and for corona charge calibration.


By incrementally depositing charge in this manner, the capacitance C becomes a differential depletion space charge capacitance CD related to the width of the surface depletion layer W as CDsεo/W, where εs is the dielectric constant of the semiconductor and εo is the permittivity of free space εo=8.854×10−14 F/cm. As an example, an initial surface potential value V0 is determined for a test site on the front surface of semiconductor sample, and the surface potential of the test site is compensated by applying a bias voltage (e.g., −VO) to the back surface of a semiconductor sample. A dose of charge having a charge density ΔQ1 is then deposited at the test site. After charge deposition, the bias voltage is removed, and the surface potential value V1 is determined for the test site. The differential surface space charge capacitance C1 of the semiconductor sample is then calculated using the relationship C1=ΔQ1/(V1−V0). The surface potential of the test site is then compensated by applying a new bias voltage (e.g., −V1) to the semiconductor sample. A second dose of charge having a charge density ΔQ2 is then deposited at the test site. After charge deposition, the bias voltage is removed, and the surface potential value V2 is determined for the test site. The differential surface space charge capacitance C2 of the semiconductor sample is then calculated using the relationship C2=ΔQ2/(V2−V1).


This sequence can be repeated k number of times (e.g., k=20 repetitions) or until achieving a desired doping monitoring depth W=εsεo/Ck. For example, in some cases, a series of consecutive monitored corona charge deposition steps can be performed, and the surface potential at the test site can be adjusted to a particular target value (e.g., zero volts, 0.5 V or less, or some other value) before each deposition step. The surface potential value can be measured after each deposition step, and the measurement results of each step can be used to determine corresponding incremental values of surface potential (ΔVk), corona charge (ΔQk), capacitance (Ck), cumulative values of surface voltage (Vk=ΣΔVk) and charge (Qk=ΣΔQk), where k refers to the kth step or repetition. The semiconductor sample can be characterized based on the values for V0, Vk, ΔVk, Qk and Ck.


In some cases, the deposited charge density doses can be the same for each repetition of charge deposition (e.g., ΔQ1=ΔQ2=ΔQ3= . . . =ΔQk).


In some implementations, the deposited charge can be removed after the doping concentration of the semiconductor is determined. For example, in some cases, corona deposited charge can be photo-neutralized and removed from the semiconductor surface using illumination with photon light energy sufficient to generate excess carriers in a semiconductor sample (e.g., blue light having photon energy above 3.3 eV for SiC, GaN or ZnO semiconductors). In some cases, the doping concentration of a test site can be measured multiple times by removing deposited charges between each measurement, and repeating the deposition of charge.


Measuring the doping concentration of a semiconductor often requires a particular depletion barrier voltage (e.g., 10V, 20V, 50V, 100V, 200V or more). Without compensation, high surface potentials can often hinder corona charge deposition due to the electrostatic forces that exist between the deposited and incoming corona ions. For example, in some cases, electrostatic repulsion between the deposited and incoming corona ions can limit the density of charge deposition. In addition, in many cases, the forces acting on corona ions can direct incoming ions away from the center of the charging site, causing non-uniform lateral distribution of charge density. This potentially can cause errors in the quantification of deposited charge dose density at the test site, and can cause corresponding errors in capacitance and doping density calculations. These limitations and errors can be mitigated or, in some cases, entirely eliminated by incrementally depositing charge onto a semiconductor surface having a constant or substantially constant surface potential at the deposition site (e.g., in the manner described above).


When measuring semiconductor doping concentration using corona charge-based techniques, the surface depletion layer is created due to net electrical neutrality of the semiconductor surface and the underlying surface space charge region. Accordingly, an electric charge placed on the semiconductor surface is mirrored by the opposite charge in the surface space charge region. To create depletion-type space charge, negative corona charge is deposited on an n-type semiconductor and positive corona charge is deposited on a p-type semiconductor.


For semiconductor doping concentration N, the depletion layer space charge per unit area can be expressed as QD=qNW, where W is the depletion layer width and q is the elemental charge. The depletion layer forms a capacitor with the capacitance CD per unit area:







C
D

=




ɛ
S



ɛ
o


W

=

q




ɛ
S



ɛ
o



Q
D



N






Based on the above relation, a doping measurement can be obtained based on the capacitance times charge factor CQ. This can used for two purposes: i) for calibration of corona deposited charge density Q, and ii) for determination of the doping concentration N.


Corona charge calibration can be used to precisely determine the incremental charge density ΔQ deposited per unit surface area at the test site. By compensating the surface potential of a semiconductor test site and depositing charge at the test site according to constant compensated surface potential, the surface of the semiconductor can be charged more precisely and/or more uniformly.


Further, in some cases, in situ measured charge increments ΔQink (e.g., ΔQin1, ΔQin2, or any other value ΔQink, as described above) can be converted into calibrated charge increments at the test site ΔQck=QinF(V, I), where F(V, I) is a calibration function dependent on the surface potential V and I is the corona charging current. The calibrated charge increments ΔQck can be used to determine a corrected space charge capacitance Cck=ΔQck/ΔVk, which in turn can be used to determine a corrected doping concentration. In some cases, the calibration function F(V, I) can be determined empirically. For example, a charge density calibration can be performed using a semiconductor calibrating sample having a known doping density with a constant doping depth profile over a known distance W under the surface. The function F(V, I) can be determined by determining a corrective function needed to satisfy the relationship ΔQck=ΔQinF(V, I). This function can then be used to correct doping density determinations for samples having unknown doping densities.


A number of different techniques can be used to calculate the doping density using the corrected corona charge increments ΔQck, the measured change in surface voltage, ΔVk, and the corrected space charge capacitance Cck=ΔQck/ΔVk. As an example, in some cases, a 1/C2−V technique can be used. By analogy to a Schottky diode C−V measurement, the calculation of doping density N can be made using a plot of 1/Cck2 versus the surface voltage Vk based on the follow relationship, where the corrected space charge capacitance Cck can be used in place of C:







1

C
ck
2


=


2


(


V
k

-

V
o


)



q






ɛ
S



ɛ
o


N






If the doping density is constant through the depletion region, the plot is a straight line and the doping density is determined from the slope of the line as:






N
=


2


ɛ
S



ɛ
o





(

slope

-
1


)







FIG. 2 illustrates an example 1/C2 vs. V plot with and without corona charge areal density correction for a very uniformly doped p-type epitaxial SiC semiconductor sample with N=2.37×1017 cm−3. In this example, without the correction, erroneous bending of the line is observed. In some cases, a very large overestimation of N up to 50% can be made in higher voltage range by using uncorrected corona charge. For example, in some cases, a need for charge correction can be apparent for surface voltages exceeding about 8V. This effect demonstrates the importance of electrostatic force effects in corona-charging, even for relatively low surface potentials.


As another example, another technique that can be used to assess the doping concentration N is the Q2−V technique. For example, the doping density N can be determined based on the total charge Qk, the total surface voltage Vk, and the depletion layer relationship, where the corrected corona charge increments ΔQck can be used to determine the total charge Qck=ΣQck:

Qck2=2sεoN|Vk−Vo|


If N is constant, this Q2−V equation gives a straight line, and the slope of this straight line gives the doping concentration N:






N
=


1

2

q






ɛ
S



ɛ
o



·



(
slope
)








In some cases, the cumulative total charge used in the Q2−V technique can be more sensitive to charge dose errors and to corresponding corona charge neutralization by leakage current, compared to a single charge increment ΔQck used in the capacitance measurement and the 1/C2−V technique. In cases of negligible leakage and proper correction of charge dose for electrostatic force effect, both techniques can provide similar results.


The capacitance-charge product, CQ, of a semiconductor (or CckQck if expressed according to the corrected space charge capacitance and the corrected corona charge increment) also can be used to determine the doping concentration N. FIG. 3 illustrates this CQ factor (where CQ is proportional to N) as a function of surface voltage with and without corona charge correction for an example constant doping density p-type epitaxial SiC semiconductor sample with N=2.37×1017 cm−3. In this example, at 40V, the error in N is about 35% by not using corrected corona charge. The CQ factor can be a constant for a sample with a uniform dopant depth profile (e.g., as illustrated in FIG. 3), and in these cases, can be used as a self-consistent charge dose verification metric. For example, semiconductors having non-uniform dopant depth profile can be distinguished by identifying semiconductors exhibiting a varying or non-constant CQ profile.


As another example, FIG. 4 illustrates the dopant depth profile for an example p-type epitaxial SiC semiconductor sample with constant doping density N=2.37×1017 cm−3 determined using the CQ factor with and without corona charge correction. As shown in FIG. 4, due to the uniform dopant depth profile of the sample, the corrected CQ factor is substantially constant.


Depositing charge following a surface potential adjustment to constant value can eliminate or otherwise reduce undesirable charge deposition patterns that tend to occur over multiple charging steps at the same site, such as the presence of craters, gradients, or other non-uniform charge deposition patterns. As a comparative example, FIG. 5 shows charge profiles for a semiconductor wafer after an initial deposition of charge (profile 510) nominally at a center location on a surface, after a sequence of ten depositions of charge (profile 520) at the same location, and after a sequence of twenty depositions of charge (profile 530) at the same location. In this example, the surface potential of the semiconductor wafer was not adjusted to a constant target value prior to each deposition of charge. As a result, electrostatic repulsion causes a decrease of the charge magnitude at the center and a spreading of the charge profile is observed at the deposition site after successive charge depositions. In contrast, by adjusting (biasing) the surface potential prior to each charge step, the spread of the charge profile can be lessened and the space-charge profile remains similar from one charging to the next. Accordingly, the accuracy of charge deposition and corona charge monitoring can be improved.


Although an example system 100 is shown and described, this is merely an illustrative example. In practice, the system 100 can have other arrangements, depending on the implementation.


For example, in some cases, the stage assembly 110 does not move during doping concentration measurement. Instead, one or more of the other components of the system 100 (e.g., the Kelvin probe 120 and/or the corona charging station 130) can move with respect to the semiconductor sample 160 in order to perform doping concentration measurements.



FIG. 6 shows an example method 600 of characterizing a semiconductor sample.



FIG. 7 shows an example method 700 of depositing a corona charge at a region of a surface of a sample.


A number of embodiments have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the disclosure. Accordingly, other embodiments are within the scope of the following claims.

Claims
  • 1. A method of characterizing a semiconductor sample, the method comprising: (i) measuring an initial value of a surface potential at a region of the semiconductor sample;(ii) applying a bias voltage to the semiconductor sample via a voltage source electrically coupled to a surface of the semiconductor sample so that the semiconductor sample has a target surface potential value of two volts or less;(iii) depositing a dose of corona charge on the region of the surface while applying the bias voltage to the semiconductor sample, wherein the amount of corona charge is monitored during the deposition;(iv) measuring a further value of the surface potential at the region after depositing the dose of corona charge and removing the bias voltage from the semiconductor sample;(v) determining an incremental value of surface potential equal to a difference between the values of the surface potential, without the bias voltage applied to the semiconductor sample, measured before and after depositing the dose of corona charge;(vi) determining a surface space charge capacitance value of the semiconductor sample equal to a ratio of the dose of corona charge to the incremental value of the surface potential;(vii) repeating steps (ii) through (vi) k times to provide k corona charge values, k incremental values of surface potential, and k surface space charge capacitance values, wherein k is an integer greater than 1 and sufficient to achieve a target doping monitoring depth of the semiconductor sample; and(viii) characterizing the semiconductor sample based on the initial value of the surface potential, the k further values of the surface potential, the k corona charge doses, the k incremental values of the surface potential, and the k surface space charge capacitance values.
  • 2. The method of claim 1, wherein the k corona charge doses are corrected by a calibration function F(V, I) to obtain k corresponding charge density values under a probe used for measuring the surface potential.
  • 3. The method of claim 2, where each of the k charge density values are used to determine a corresponding corrected space charge capacitance equal to a ratio of the corresponding charge density value to the corresponding incremental value of the surface potential.
  • 4. The method of claim 3, where a corrected net corona charge density equal to a sum of the k charge density values and the corrected space charge capacitances are used to determine a doping density of the semiconductor sample.
  • 5. The method of claim 4, wherein a quality of the calibration function is determined using a capacitance charge factor equal to a product of the corrected space charge capacitance and the corresponding corrected net charge density value.
  • 6. The method of claim 1, further comprising performing a charge density calibration using a semiconductor calibrating sample with a known doping density over a distance W under a surface of the semiconductor calibrating sample.
  • 7. The method of claim 1, wherein a polarity of the corona charging is such that it creates a depletion surface space charge region in the semiconductor sample.
  • 8. The method of claim 7, wherein the semiconductor sample is an n-type semiconductor and the corona charge is deposited using a negative charging polarity.
  • 9. The method of claim 7, wherein the semiconductor sample is a p-type semiconductor and the corona charge is deposited using a positive charging polarity.
  • 10. The method of claim 1, wherein characterizing the semiconductor sample comprises determining a doping density and/or a doping profile.
  • 11. The method of claim 1, wherein the semiconductor sample comprises a wide bandgap semiconductor.
  • 12. The method of claim 1, wherein the semiconductor sample comprises a semiconductor selected from the group consisting of SiC, GaN, ZnO, ZnS, and ZnSe.
  • 13. The method of claim 1, wherein the surface potential measurements are performed using a non-contact vibrating probe.
  • 14. The method of claim 1, wherein the surface potential measurements are performed using a capacitive electrode.
  • 15. The method of claim 1, wherein the target surface potential is 0.5 volts or less.
  • 16. The method of claim 1, wherein the target surface potential is approximately zero volts.
  • 17. The method of claim 1, wherein the deposited corona charge is photo-neutralized and removed from the semiconductor surface using illumination with light of photon energy sufficient to generate excess carriers in the semiconductor sample.
  • 18. The method of claim 17, further comprising repeating characterization of the semiconductor sample after photo-neutralizing the deposited corona charge prior to each repetition.
US Referenced Citations (102)
Number Name Date Kind
4812756 Curtis Mar 1989 A
5216362 Verkuil Jun 1993 A
5485091 Verkuil Jan 1996 A
5498974 Verkuil Mar 1996 A
5639357 Xu Jun 1997 A
5644223 Verkuil Jul 1997 A
5773989 Edelman Jun 1998 A
5807467 Givens Sep 1998 A
5963783 Lowell Oct 1999 A
6011404 Ma Jan 2000 A
6034535 Liberman Mar 2000 A
6037797 Lagowski Mar 2000 A
6051121 Givens Apr 2000 A
6097196 Verkuil Aug 2000 A
6097205 Liberman Aug 2000 A
6127289 Debusk Oct 2000 A
6191605 Miller Feb 2001 B1
6267852 Givens Jul 2001 B1
6335630 Miller Jan 2002 B2
6395437 Wollesen May 2002 B1
6448804 Miller Sep 2002 B2
6538462 Lagowski Mar 2003 B1
6569691 Jastrzebski May 2003 B1
6679976 Baldwin Jan 2004 B2
6723209 Baldwin Apr 2004 B2
6734696 Horner May 2004 B2
6937050 Fung Aug 2005 B1
7012438 Miller Mar 2006 B1
7103848 Barsness Sep 2006 B2
7110238 Xu Sep 2006 B1
7202691 Lagowski Apr 2007 B2
7230443 Fung Jun 2007 B1
7316764 Baldwin Jan 2008 B2
7335315 Matsuda Feb 2008 B2
7358748 Miller et al. Apr 2008 B1
7405580 Marinskiy Jul 2008 B2
7491953 Horsky Feb 2009 B2
7521946 Janik Apr 2009 B1
7538333 Samsavar May 2009 B1
7663385 Kamieniecki Feb 2010 B2
7772866 Patterson Aug 2010 B2
7893703 Rzepiela Feb 2011 B2
7960709 Horsky Jun 2011 B2
8004290 Zhang Aug 2011 B1
8071958 Horsky Dec 2011 B2
8163571 Jaeger Apr 2012 B2
8232817 Kamieniecki Jul 2012 B2
8410459 Horsky Apr 2013 B2
8585877 Jaeger Nov 2013 B2
8618514 Horsky Dec 2013 B2
8909365 Valcore, Jr. Dec 2014 B2
9084334 Gefter Jul 2015 B1
20010000651 Miller May 2001 A1
20010014520 Usui Aug 2001 A1
20020006740 Kamieniecki Jan 2002 A1
20020008536 Miller Jan 2002 A1
20020125900 Savtchouk Sep 2002 A1
20020130674 Lagowski Sep 2002 A1
20020189938 Baldwin Dec 2002 A1
20030024807 Baldwin Feb 2003 A1
20040019442 Kitajima Jan 2004 A1
20040112764 Stokes Jun 2004 A1
20040191936 Tsidilkovski Sep 2004 A1
20040241890 Steele Dec 2004 A1
20050006226 Baldwin Jan 2005 A1
20050059174 Steele Mar 2005 A1
20050174135 Matsuda Aug 2005 A1
20050196882 Steeples Sep 2005 A1
20050239224 Kitajima Oct 2005 A1
20060097193 Horsky May 2006 A1
20060267622 Lagowski Nov 2006 A1
20070018674 Cho Jan 2007 A1
20070069759 Rzepiela Mar 2007 A1
20070148795 Kitajima Jun 2007 A1
20070181830 Horsky Aug 2007 A1
20070194252 Horsky Aug 2007 A1
20070273400 Kamieniecki Nov 2007 A1
20080174918 Kim Jul 2008 A1
20080260398 Itoh Oct 2008 A1
20080297189 Everaert Dec 2008 A1
20080299681 Jaeger Dec 2008 A1
20080305598 Horsky Dec 2008 A1
20090090872 Horsky Apr 2009 A1
20100008015 Booth Jan 2010 A1
20100032587 Hosch Feb 2010 A1
20100060307 Kamieniecki Mar 2010 A1
20110226969 Horsky Sep 2011 A1
20120076475 Horsky Mar 2012 A1
20120160415 Jaeger Jun 2012 A1
20120176146 Oborina Jul 2012 A1
20120283973 Samara Nov 2012 A1
20120321335 Fujiwara Dec 2012 A1
20130068963 Kireeff Covo Mar 2013 A1
20130082241 Kub Apr 2013 A1
20130164665 Ishii Jun 2013 A1
20130257472 Kamieniecki Oct 2013 A1
20140061816 Horsky Mar 2014 A1
20140132286 Oborina May 2014 A1
20140147134 Verheijen May 2014 A1
20150020972 Jensen Jan 2015 A1
20150061714 Kelly-Morgan Mar 2015 A1
20150098161 Horowy Apr 2015 A1
Foreign Referenced Citations (3)
Number Date Country
S64-69024 Mar 1989 JP
H05-206243 Aug 1993 JP
H08-236591 Sep 1996 JP
Non-Patent Literature Citations (9)
Entry
Wikipedia Entry for Capacitance (Year: 2019).
“www.keithly.com applications guide: C-V Testing for Components and Semiconductor Devices” (Year: 2014).
Czett, A. et al., Non-contact High Precision Alternative to Hg Probe for Dopant Profiling in SiC, Phys. Status Solidi C 11, pp. 1601-1605 (2013), DOI: 10, 1002/pssc201400057.
Marinskiy, D., et al., “A Novel Approach to Measuring Doping in SiC by Micro Spot Corona—Kelvin Method”, Materials Science Forum, vols. 821-823, pp. 273-276 (2015).
Savtchouk, S. et al., “Non-contact Doping Profiling in Epitaxial SiC”, Materials Science Forum, vols. 457-460, pp. 755-758 (2004).
Schroeder, D.K., “Charge-Based and Probe Characterization”, Semiconductor Material and Device Characterization, (2006), Ch. 9, pp. 523-527.
Verkuil, R.I. et al., “Contactless Silicon Doping Measurements by Means of a Corona-Oxide-Semiconductor (COS) Technique”, Extended Abstracts, vol. 88-2, Abstract No. 438, Electrochemical Society Meeting, Chicago, IL (1988), pp. 643-644.
EP Extended European Search Report Issued in European Application No. 16804449.3, dated Feb. 18, 2019, 8 pages.
JP Office Action in Japanese Appln. No. 2018-515182, dated May 19, 2020, 11 pages (with English translation).
Related Publications (1)
Number Date Country
20160356750 A1 Dec 2016 US