Mercury-containing copper oxide superconductor and method of producing same

Abstract

A superconductor having at least one Hg-M-Cu—O (M=Ba, Sr and/or Ca) superconducting film provided on a substrate and having a thickness of between 300 Å to 950 Å. The superconductor may be prepared by forming, on a substrate, a precursor laminate composed of a first, M-Cu—O film and a second, Hg—O film. The precursor laminate film-bearing substrate is placed in a closed vacuum chamber together with a first pellet of HgO, MO and CuO and a second pellet of MO and CuO. The contents in the chamber are heated to form, on the substrate, a superconducting Hg-M-Cu—O film. The thickness of the first M-Cu—O film of the precursor is controlled so that the thickness of the superconducting Hg-M-Cu—O film is in the range of between 300 Å to 950 Å.

Description

BACKGROUND OF THE INVENTION

[0001] This invention relates to a mercury-containing copper oxide superconductor having a high superconducting transition temperature.

[0002] Because superconductors have unique characteristics that (1) the electrical resistivity is zero, (2) they show perfect diamagnetism and (3) they show Josephson effect, superconductors are anticipated for utilization in various applications such as electric power transmission, electric generators, nuclear fusion plasma containment, magnetic levitation trains, magnetic shield and high speed computers.

[0003] An oxide superconductor (La1-xBax)2CuO4 having a high superconducting transition temperature Tc of about 30 K was found by Bendonorz and Müller in 1986. Since then, reports have been successively made on superconducting transition at high temperatures in connection with YBa2Cu3Ox (Tc=90 K), Bi2Sr2Ca2Cu3Oy (Tc=110 K), Tl2Ba2Ca2Cu3Oz (Tc=125 K) and HgBa2Ca2Cu3Oz (Tc=135 K). A number of studies are now being made on the method of preparation, physical properties and application of these substances. In particular, mercury-containing copper oxide superconductors are considered to be promising because of their high superconducting transition temperature.

[0004] In order to practically use a copper oxide superconductor, it is important that the superconductor have a shape suitable for its utilization. For the utilization in electronic devices, for example, development of film forming techniques for superconductors is essential. Studies on the formation of mercury-containing copper oxide superconductor films have been extensively made all over the world since 1993 in which a mercury-containing copper oxide superconductor was first found.

[0005] A process for the preparation of a mercury-containing copper oxide superconductor film having Tc of 100K or more is known in which a precursor film composed of constituent elements is first prepared and then heat treated in the presence of mercury (Y. Q. Wang et al., Appl. Phys. Lett. 63 (1993) 3084).

[0006] A physical vacuum deposition method such as RF sputtering or pulsed laser ablation (PLD) is generally adopted for the production of the precursor film. When the precursor film is exposed to air, Ba contained therein reacts with moisture and carbon dioxide, which considerably adversely affect the formation of a desired mercury-containing copper oxide superconductor film. To prevent such a reaction, a mercury oxide film is generally provided over the precursor film (C. C. Tsuei et al., Science 263 (1994) 1259).

[0007] In the heat treatment, the precursor film is placed in a vacuum quartz tube together with pellets of Hg—Ba—Ca—Cu—O for the purpose of controlling the mercury vapor pressure. The heat treatment is performed at about 800° C. under vacuum to obtain a mercury-containing copper oxide superconductor film having Tc of 130K or more (W. N. Kang et al., Appl. Phys. Lett. 73 (1998) 381).

[0008] A mercury-containing copper oxide superconductor film having a critical current density Jc of about 106 A/cm2 or more at 77K is also reported (S. L. Yan et al., Appl. Phys. Lett. 73 (1998) 2989).

[0009] As an application to an electronic device, a superconducting quantum interference device (SQUID) using a mercury-containing copper oxide superconductor film having a thickness of 2000 Å is reported (A. Tsukamoto et al., Appl. Phys. Lett. 73 (1988) 990). The junction is reported to have Jc of 4×103 to 6×104 A/cm2 at 77K and IcRn of 450 μV which is greater than IcRn values of currently most widely studied Y123 type superconductors (200 to 300 μV) . Further, the SQUID is reported as operable at 111K. These characteristics suggest high potential of mercury-containing copper oxide superconductors.

[0010] A mercury-containing copper oxide superconductor is a layer compound. The crystal grain has a plate-like shape as illustrated in FIG. 3. A desired superconductor film is composed of c-axis oriented plate-like crystals 11A continuously arranged on a substrate 10. However, it has been found that known mercury-containing copper oxide superconductor film has a number of defects. Thus, as shown in FIGS. 4(a)-4(c), there are steps 13, holes 14 and gaps 15 in known films. The defects also include outgrowths whose crystal orientations are not uniform (see FIG. 6). These defects cause a reduction of Jc as well as variation of superconductive characteristics at different locations of the film and interfere the fabrication of electronic devices.

SUMMARY OF THE INVENTION

[0011] It is an object of the present invention to provide a mercury-containing copper oxide superconductor film free of the above-described defects.

[0012] Another object of the present invention is to provide a superconductor film of the above-mentioned type which has a desired thickness.

[0013] It is a further object of the present invention is to provide a superconductor film of the above-mentioned type which has two or more mercury-containing copper oxide superconductor layers having different compositions so that the superconductive characteristics of the film is modulated.

[0014] It is a further object of the present invention to provide a method which can prepare the above mercury-containing copper oxide superconductor film.

[0015] In accomplishing the foregoing object, the present invention provides a superconductor having a substrate, and a superconducting film provided on the substrate and having a thickness in the range of between 300 Å to 950 Å, wherein the superconducting film contains Hg, M which is Ba, Sr or Ca, Cu and O.

[0016] The present invention also provides a method of producing a superconductor, which includes the steps of:

[0017] (a) forming, on a substrate, a precursor laminate film having a first film containing M which is Ba, Sr or Ca, Cu and O and a second, mercury oxide film provided on the first film;

[0018] (b) placing the precursor laminate film-bearing substrate in a closed vacuum chamber together with a first pellet containing Hg, M which is as defined above, Cu and O and a second pellet containing M which is as defined above, Cu and O; and

[0019] (c) heating the precursor laminate film-bearing substrate, the first and second pellets in the vacuum chamber to form, on the substrate, a superconducting film having a thickness in the range of between 300 Å to 950 Å and containing Hg, M, Cu and O.

[0020] The mechanism by which the known mercury-containing copper oxide superconductor film is formed is considered to be as follows.

[0021] As shown in FIG. 5(a), a substrate 10 on which a precursor film consisting of a M-Cu—O layer and a Hg—O layer is provided is placed in a vacuum chamber together with pellets. Then, the contents in the chamber are heated so that a mercury-containing copper oxide superconductor film having a thickness of 1000 Å or more is formed on the substrate. As shown in FIG. 5(b), a liquid phase 12 composed of Hg, M, Cu and O is formed during the heat treatment. Seed crystals are formed in the liquid phase 12 and grow gradually. In the region adjacent to the surface of the substrate 10 where the surface tension of the liquid phase 12 effectively acts on the growing crystal grains, the c-axis thereof orient in the direction normal to the substrate. However, crystal grains 11A growing in the region remote from the surface of the substrate 10 orient at random. As a consequence, as shown in FIG. 6, there are formed steps 13, holes 14, gaps 15 and outgrowths 16.

[0022] In contrast, the superconductor film according to the present invention is considered to be produced as follows.

[0023] As shown in FIG. 1(a), a substrate 10 on which a precursor film 11B having a thickness smaller than the above and consisting of a M-Cu—O layer and a Hg—O layer is provided is used. The precursor film-bearing substrate is placed in a vacuum chamber together with pellets. Then, the contents in the chamber are heated. As shown in FIG. 1(b), a liquid phase 12 composed of Hg, M, Cu and O is formed during the heat treatment. Seed crystals are formed in the liquid phase 12 and grow gradually. Since a the precursor film 11B is thin, most of crystal grains grow in the region adjacent to the surface of the substrate 10. Thus, the orientation of the crystal grains receives a strong influence of the crystal orientation of the substrate 10. Accordingly, the c-axis thereof orient in the direction normal to the surface of the substrate, with the a-axis thereof being oriented in the direction corresponding to the crystal orientation of the substrate 10. Moreover, since the liquid phase 12 can effectively wet both the surface of substrate and the crystal grains in contact therewith, the crystal grains grow in the lateral direction in an enhanced manner. Thus, as shown in FIG. 1(c), the mercury-containing copper oxide superconductor film 11 is free of steps, holes, gaps and outgrowths and is flat and uniform. Further, the crystal grains are tightly connected with each other.

BRIEF DESCRIPTION OF THE DRAWINGS

[0024] Other objects, features and advantages of the present invention will become apparent from the detailed description of the preferred embodiments of the invention which follows, when considered in the light of the accompanying drawings, in which:

[0025] FIGS. 1(a) through 1(c) are sectional views schematically illustrating a process of growing a mercury-containing copper oxide superconductor film on a substrate according to the present invention;

[0026] FIGS. 2(a) and 2(b) are sectional views similar to FIGS. 1(a) and 1(c), respectively, schematically illustrating a process of growing a mercury-containing copper oxide superconductor film by repeating procedures according to the present invention;

[0027] FIG. 3 is a perspective view schematically illustrating a crystal grain of a mercury-containing copper oxide superconductor;

[0028] FIGS. 4(a) through 4(c) are SEM photographs of sections of known mercury-containing copper oxide superconductor films;

[0029] FIGS. 5(a) and 5(b) are sectional views similar to FIGS. 1(a) and 1(b), respectively, schematically illustrating a process of growing a known mercury-containing copper oxide superconductor film;

[0030] FIG. 6 is a sectional view similar to FIG. 1(c) schematically illustrating a known mercury-containing copper oxide superconductor film.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

[0031] Referring to FIG. 1(c), a superconductor according to the present invention includes a substrate 10, and a mercury-containing copper oxide superconductor film 11 provided thereon.

[0032] Any customarily employed substrate may be used for the purpose of the present invention. Examples of suitable substrate include SrTiO3, LaAlO3, (LaAlO3)0.3.(Sr2AlTaO6)0.7, NdGaO3, YAlO3, Y-stabilized ZrO2 and MgO. The mercury-containing copper oxide superconductor film contains Hg, M (=Ba, Sr and/or Ca), Cu and O. Examples of mercury-containing copper oxide superconductors include HgM3Cu2Oy (y=6.10-6.31) and HgM4Cu3Oz (z=8.17-8.30) where M is as defined above.

[0033] It is important that the mercury-containing copper oxide superconductor film should have a thickness in the range of between 300 Å to 950 Å.

[0034] Because the superconductor according to the present invention is free of surface defects, the critical current density Jc thereof is high. Preferably, the superconductor according to the present invention has a critical current density Jc at 77K of at least 8×106 A/cm2.

[0035] The superconductor may be produced as follows.

[0036] First, as shown in FIG. 1(a), a precursor laminate film 11B having a first film containing M, Cu and O and a second, mercury oxide film covering thereon is formed on a substrate 10 (step (a)). The precursor laminate film-bearing substrate is then placed in a closed vacuum chamber together with a first pellet containing Hg, M, Cu and O and a second pellet containing M, Cu and O (step (b)). The contents in the vacuum chamber are heated to form, on the substrate 10, a superconducting film 11 containing Hg, M, Cu and O (step (c)).

[0037] In the above process, it is important that the thickness of the first film containing M, Cu and O of the precursor film 11B should be controlled so that the superconducting film 11 has a thickness in the range of between 300 Å to 950 Å.

[0038] In another embodiment shown in FIG. 2(b), the superconductor according to the present invention includes a substrate 10, and a superconducting laminate film provided on the substrate. The laminate film includes at least two superconducting layers 11 each having a thickness in the range of between 300 Å to 950 Å. Each of the superconducting layers 11 contains Hg, M (Ba, Sr and/or Ca), Cu and O. The compositions of the layers 11 may be the same or different. Examples of mercury-containing copper oxide superconductors include HgM3Cu2Oy and HgM4Cu3Oz where M, y and z are as defined previously.

[0039] The superconductor having the superconducting laminate film may be prepared by repeating a cycle of the above steps (a) through (c). Thus, the product obtained in step (c) of the first cycle is used as the substrate for step (a) of the second cycle, as shown in FIG. 2(a). Steps (b) and (c) are then performed to form two superconducting layers 11 on the substrate 10 as shown in FIG. 2(b). The cycle including the steps (a)-(c) is repeated until a laminate superconducting film has a desired thickness.

[0040] When the precursor laminate film and the first and second pellets used in respective cycles are the same, the superconducting layers have the same composition. If desired, different the precursor laminate film and the first and second pellets may be used in respective cycles. In this case, the superconducting layers have different compositions.

[0041] The following examples will further illustrate the present invention.

EXAMPLE 1

[0042] On a SrTiO3 (100) substrate, a Ba2CaCu2Oy film and a HgO film were formed by PLD to obtain a precursor laminate film-bearing substrate. The thicknesses of the Ba2CaCu2Oy and HgO films were 1000 Å and 500 Å, respectively. This was then placed in a quartz tube together with a first pellet composed of a mixture of HgO powder, BaO powder, CaO powder and CuO powder with a molar ratio of 1:2:1:2 and a second pellet composed of a mixture of BaO powder, CaO powder and CuO powder with a molar ratio of 2:1:2. After the quartz tube had been made vacuum and closed, the contents in the quartz tube were heated at 700-800° C., thereby obtaining a superconductor having a HgBa2CaCu2Oy film on the substrate. The X-ray diffraction analysis revealed that the film was biaxially oriented film with its c-axis and a-axis being uniformly oriented. The film was also measured for its temperature dependency of the resistance, revealing that the resistance became zero at 116K or lower. A scanning secondary electron microscope (SEM) of a surface and a cross section of the film did no reveal any steps, holes, gaps or outgrowths. The thickness of the film was found to be 750 Å. The superconductor had a Jc at 77K of 1.02×107 A/cm2. Variation of Jc of the superconductor at different positions was about 10%. The AFM (atomic force microscope) observation revealed that the average roughness Ra of the superconducting film in an area of 10 μm×8 μm was 29.0 Å and that the maximum surface roughness was 100.2 Å (13% of the thickness).

EXAMPLES 2-12 AND COMPARATIVE EXAMPLES 1-4

[0043] Example 1 was repeated in the same manner as described except that the thicknesses of the films were changed as shown in Table 1. The thickness, results of SEM observation, Tc and Jc of each of the superconducting films thus obtained are summarized in Table 1 together with those of Example 1.

TABLE 1
		Thickness			Jc at
	Thickness	of super-			77 K
Example	Ba2CaCu2Oy/	conducting	SEM	Tc	(×106
No.	HgO (Å)	Film (Å)	Analysis	(K)	A/cm2)
Comp. 1	100/500	—	islands	—	—
Comp. 2	200/500	—	islands	—	—
2	400/500	300	no defects	118	9.12
3	600/500	450	no defects	117	9.56
4	800/500	600	no defects	117	10.00
1	1000/500	750	no defects	116	10.20
5	1200/500	900	no defects	118	8.99
Comp. 3	1400/500	1050	holes,	119	5.99
			outgrowths
Comp. 4	1600/500	1200	holes,	119	5.85
			outgrowths
6	900/200	700	no defects	118	9.56
7	900/400	700	no defects	116	8.67
8	900/600	700	no defects	117	9.88
9	900/800	700	no defects	116	9.12
10	900/1000	700	no defects	117	9.46
11	900/1200	700	no defects	119	10.00
12	900/1400	700	no defects	118	9.34

EXAMPLES 13-17 AND COMPARATIVE EXAMPLES 5-8

[0044] Example 1 was repeated in the same manner as described except that the PLD was replaced by RF sputtering for the formation of precursor films and that the thicknesses of the films were changed as shown in Table 2. The thickness, results of SEM observation, Tc and Jc of each of the superconducting films thus obtained are summarized in Table 2.

TABLE 2
		Thickness			Jc at
	Thickness	of super-			77 K
Example	Ba2CaCu2Oy/	conducting	SEM	Tc	(×106
No.	HgO (Å)	Film (Å)	Analysis	(K)	A/cm2)
Comp. 5	200/500	—	islands	—	—
Comp. 6	400/500	—	islands	—	—
13	600/500	400	no defects	115	9.85
14	800/500	550	no defects	113	10.10
15	1000/500	700	no defects	114	10.00
16	1200/500	850	no defects	116	9.95
17	1400/500	950	no defects	114	8.56
Comp. 7	1600/500	1100	outgrowths	117	5.98
Comp. 8	1800/500	1250	holes,	118	4.86
			outgrowths

[0045] From the results shown in Tables 1 and 2, it will be appreciated that superconducting films having no defects and a high Jc are obtained when the thickness thereof is between 300-950 Å. C-axis oriented HgBa2CaCu2Oy films having flat surfaces were obtained in Examples 1-17. When the thickness of the Ba2CaCu2Oy film of the precursor laminate film was too thin to obtain a HgBa2CaCu2Oy film with a thickness of 300 Å or more (Comparative Examples 1, 2, 5 and 6), crystal grains on the substrate failed to provide a film but only formed islands. Thus, no Tc and Jc were measurable. On the other hand, when the thickness of the Ba2CaCu2Oy film of the precursor laminate film was too thick to obtain a HgBa2CaCu2Oy film with a thickness of 950 Å or less (Comparative Examples 3, 4, 7 and 8), surface defects were produced so that Jc was below 6×106 A/cm2. The results shown in Tables 1 and 2 also indicate that the thickness of HgO film of the precursor laminate does not give any significant influence upon the superconducting films.

EXAMPLE 18

[0046] On the superconductor obtained in Example 1, a HgBa2CaCu2Oy film (second layer) was additionally formed. Thus, on the HgBa2CaCu2Oy film (first layer) prepared on the substrate in Example 1, a Ba2CaCu2Oy film and a HgO film were formed by PLD to obtain a precursor laminate film-bearing substrate. The thicknesses of the Ba2CaCu2Oy and HgO films were 1000 Å and 500 Å, respectively. This was then placed in a quartz tube together with a first pellet composed of a mixture of HgO powder, BaO powder, CaO powder and CuO powder with a molar ratio of 1:2:1:2 and a second pellet composed of a mixture of BaO powder, CaO powder and CuO powder with a molar ratio of 2:1:2. After the quartz tube had been made vacuum and closed, the contents in the quartz tube were heated at 700-800° C., thereby obtaining a superconductor having a laminate HgBa2CaCu2Oy film on the substrate. The X-ray diffraction analysis revealed that the film was biaxially oriented film with its c-axis and a-axis being uniformly oriented. The film was found to have Tc of 120K. No steps, holes, gaps or outgrowths were observed by SEM. The thickness of the film was found to be 1450 Å. No boundary was determinable between the first and second layers of the film because they were closely united and integrated into a unitary film. The superconductor had a Jc at 77K of 6.54×106 A/cm2.

EXAMPLE 19

[0047] On the superconductor obtained in Example 18, a HgBa2CaCu2Oy film (third layer) was additionally formed. Thus, on the HgBa2CaCu2Oy film (second layer) prepared in Example 18, a precursor laminate was formed. This was treated in the same manner as that in Example 1 to form a HgBa2CaCu2Oy laminate film on the substrate. The X-ray diffraction analysis revealed that the film was biaxially oriented film with its c-axis and a-axis being uniformly oriented. The film was found to have Tc of 122K. No steps, holes, gaps or outgrowths were observed by SEM. The thickness of the film was found to be 2100 Å. No boundary was determinable between the second and third layers of the film. The superconductor had a Jc at 77K of 5.68×106 A/cm2.

EXAMPLE 20

[0048] On the superconductor obtained in Example 1, a HgBa2Ca2Cu3Oz film (second layer) was additionally formed. Thus, on the HgBa2CaCu2Oy film (first layer) prepared on the substrate in Example 1, a Ba2Ca2Cu3Oz film and a HgO film were formed by PLD to obtain a precursor laminate film-bearing substrate. The thicknesses of the Ba2CaCu2Oy and HgO films were 1000 Å and 500 Å, respectively. This was then placed in a quartz tube together with a first pellet composed of a mixture of HgO powder, BaO powder, CaO powder and CuO powder with a molar ratio of 1:2:2:3 and a second pellet composed of a mixture of BaO powder, CaO powder and CuO powder with a molar ratio of 2:2:3. After the quartz tube had been made vacuum and closed, the contents in the quartz tube were heated at 770-840° C., thereby obtaining a superconductor having a c-axis oriented laminate film composed of first, HgBa2CaCu2Oy layer and second, HgBa2Ca2Cu3Oz layer provided the substrate. The film was found to have Tc of 131K. No steps, holes, gaps or outgrowths were observed by SEM. The thickness of the film was found to be 1260 Å. No boundary was determinable between the first and second layers of the film because they were closely united and integrated into a unitary film.

[0049] The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all the changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.

[0050] The teachings of Japanese Patent Application No. H11-242418, filed Aug. 30, 1999, inclusive of the specification, claims and drawings, are hereby incorporated by reference herein.

Claims

1. A superconductor comprising a substrate, and a superconducting film provided on said substrate and having a thickness in the range of between 300 Å to 950 Å, said superconducting film containing Hg, M which is at least one element selected from the group consisting of Ba, Sr and Ca, Cu and O.

2. A superconductor as claimed in claim 1, and having a critical current density Jc at 77K of at least 6×106 A/cm2.

3. A superconductor as claimed in claim 1, wherein said superconducting film is represented by the following formula:

4. A superconductor comprising a substrate, and a superconducting laminate film provided on said substrate and including at least two superconducting layers each having a thickness in the range of between 300 Å to 950 Å, said superconducting layer containing Hg, M which is at least one element selected from the group consisting of Ba, Sr and Ca, Cu and O.

5. A superconductor as claimed in claim 4, wherein at least one of said layers is represented by the following formula:

6. A superconductor as claimed in claim 5, wherein at least one of the other layers is represented by the following formula:

7. A method of producing a superconductor, comprising the steps of: (a) forming, on a substrate, a precursor laminate film having a first film containing M which is at least one element selected from the group consisting of Ba, Sr and Ca, Cu and O and a second, mercury oxide film provided on said first film; (b) placing said precursor laminate film-bearing substrate in a closed vacuum chamber together with a first pellet containing Hg, M which is as defined above, Cu and O and a second pellet containing M which is as defined above, Cu and O; and (c) heating said precursor laminate film-bearing substrate, said first and second pellets in said vacuum chamber to form, on said substrate, a superconducting film having a thickness in the range of between 300 Å to 950 Å and containing Hg, M, Cu and O.

8. A method as claimed in claim 7, further comprising repeating steps (a) through (c) using the product obtained in step (c) as said substrate in step (a) until laminated superconducting films have a desired thickness.

9. A method as claimed in claim 8, wherein said first and second films and said first and second pellets used in respective repetition are the same so that the laminated superconducting films have the same composition.