The present invention pertains to the field of hydraulic cement materials.
Hydraulic Portland cements are calcium silicate cements made with a combination of compounds containing elements of calcium, silicon, aluminum, and iron bearing shale, clay and limestone. A series of oxidization reactions cause the materials to fuse and so create cement clinker. Very high temperatures are required in the conventional production of cements. Finely ground powder produced by the above process sets after mixing with water and preliminary hardening in the air, the powder continues to cure and increase in strength in water. Portland cements are used for binding sand and gravel together to form concrete.
In particular, the following chemical reactions occur in the production of hydraulic lime cements. Limestone (lime) CaCO3 is roasted to produce quicklime CaCO. Quicklime, CaCO, is then slaked (water added) to produce slaked lime Ca(OH)2. Slaked lime, Ca(OH)2 is then converted, by way of the action of atmospheric carbon dioxide, CO2, back into lime CaCO3, which hardens cement as a result of crystallization of the CaCO3 (the formation of elongated crystalline needles). It is this crystallization, which gives lime cement its strength.
Portland cement concrete is the most popular and widely used building materials today as a result of the global availability of raw materials for its production, its ease for preparing with water and its ease of fabrication into a plurality of different shapes. Further, to the above, so far as strength of materials is concerned, it was the discovery in 1757 by Smeaton, using scientific methods, of the lost art of cement making (lost in the Middle Ages), that it was the presence of clay ‘impurities’ in limestone, CaCO3, that gave Portland cement (so named because of the similarity of clay impurities used to those found in the Portland area of England) its great strength.
The production of Portland cement is an extremely resource and energy intensive process. There are major drawbacks with respect to sustainability of Portland cement production including:
About 1.5 tons of raw materials are needed to produce every ton of Portland cement.
Cement and lime manufacture is reported to produce from 8% to 10% of global carbon dioxide emissions annually. In particular, about one ton of carbon dioxide (CO2) is released into the atmosphere for every ton of Portland cement produced.
Co-grinding of cement clinker and limestone, with CO2 capture in the cement powder, can be used to make Portland cement. However, this process has an adverse effect on the concrete's workability.
Concrete made of Portland cement deteriorates when exposed to severe environments, and is eroded by weak acids. Portland cement has limited autogenous healing behavior. Cracking and corrosion have significant influence on Portland cement's service behavior, design life and safety.
Further to the above, Portland cement repels cellulose and cannot incorporate organic silicate fibers such as bamboo, hemp or rice husks into the cement matrix. When organic silicate fibers are use as reinforcing natural fibers, notably lignin and hemicellulose, then the cement produced is typically susceptible to degradation.
An alternative to hydraulic cements like Portland cement, are the alkali-activated cements. Alkali activated cement can be made from ground granulated blast furnace slag (metallurgical slag and fly ash) and is not hydraulic (not solidifying without alkali activation and in particular under water) but rather must be “activated” by addition of caustic alkalis such as caustic soda, NaOH, or lime (an economical choice) so that the cement will set. These alkali-activated cements use common industrial by-products and cure at room temperature into compact well-cemented composites, with similar workability to Portland cement. Alkali activated cements have the advantages of low energy costs, high strength and good durability compared to Portland cement.
Geopolymer cement, being alkali-activated aluminum silicate cement, can include aluminosilicate minerals from thermally activated clays and ground granulated blast-furnace slag or fly ash. The mortar formed from geopolymer cement sets hard with the addition of a highly alkaline silicate solution. Geopolymers have favorable properties such as being made from abundant raw resource, little CO2 emission, less energy consumption, low production cost, high early strength and fast setting.
However, disadvantages of geopolymers and other alkali-activated cements include:
Magnesium Phosphate Cements are chemical cements that rely on the precipitation of insoluble magnesium phosphate from a mix of magnesium oxide and a soluble phosphate. The oxides such as magnesium, aluminum or zirconium, will react with phosphoric acid at room temperature forming a coherent mass, setting quickly and giving high early strength. Magnesium oxide cement has much lower associated energy consumption and CO2 emissions compared to Portland cement. These cements develop considerably greater compressive and tensile strengths. Magnesium-based cements also have a natural affinity for cellulose materials, such as vegetable fiber reinforcement. Further, magnesium phosphate cements can incorporate a higher proportion of non-toxic industrial waste.
Magnesium phosphate cements have the following disadvantages:
Problems with background art including (as recited above and as identified by the inventor):
To ameliorate some of the effects of the general problems and the specific problems as recited above and in particular to provide, at least in part, a cement having improved physical properties that can include: reduced porosity, improved strength and improved durability.
Technical Solution: dissolving organic binders that bind silicates in organic matter, including cellulose, so as to free up the silicates for reaction with other cement constituents including metal oxides and in particular calcium derived from lime. The process can be undertaken using a vast array of disparate organic chemicals in the form of solutions, colloids, suspensions and mixtures, the chemicals including: acids, chelates, alkali solutions and in some cases chemicals that are arguably amphoteric in nature. Central to the inventor's discovery is the realization that a “physical process”, be it chemical, electrical or mechanical in nature that is sufficient to remove synthetic silicates (silicates in natural organic material as opposed to those found in natural rock formations) bound in organic matter from their binders so as to enable the silicates to react with other cement components can improve the properties of cements. Preferably also the process of removing the silicate will damage the silicate by a plurality of processes, some including silicate etching, so as to serve as centers for crystal growth. Preferably also the “physical” processes involved in the removal, or at the least exposure of the silicates to other cement reactants, will reduce particle size of reactants so as to improve the effectiveness of reactions taking place during cement production. The above processes can also be applied to natural silicates (rocks, sea shells, chalks and Pozzolanic compounds) where the silicate is otherwise bound and its reactions with other cement constituents impeded without attempts being made to further expose the silicates to other cement reactants by means including at least one of chemical, mechanical, thermal or electrical.
Increasing the concentration of nucleation sites for metal silicate crystals by using a plurality of organic additives solves the problem of porosity.
Accordingly, a class of hydraulic, organic chemical, activated cements are formed by reacting powdered metal oxides, alkali silicates and silica bearing minerals which set at near neutral pH and ambient conditions under the influence of an organic chemical activating agent when mixed with water to form a monolithic cement (the cement can contain fillers, aggregates or natural organic silica fibers).
In one aspect of invention a cement is recited including:
The description in the body of the specification pertains to ‘preferred’ modes of invention. Accordingly, features recited in the body should not be construed to be essential features of the invention unless explicitly indicated. Further, any reference in the body to the expression ‘invention’ should be construed to imply a reference to preferred embodiments only.
The recitation of problems recited in the Background Art section above, does not constitute an admission against interest that persons, other than the present inventor, identified the problems in the prior art.
Gesser H D, “Applied Chemistry”, Springer, 2002, provides a reference source for basic technical terminology used in relation to cements.
Reactants according to one mode of the present invention include:
Secondary metal oxides are preferably Titanium dioxide TiO2 (Titanium White) due to its self-cleaning effect and due to its role in the creation of crystal nucleation sites.
Transition metal oxides that form colored pigmentation are preferable, most notably:
Pozzolanic compounds that are a source of silica bearing minerals or metal silicates (containing SiO2,Al2O3, Fe2O3 and CaO). Synthetic compounds having properties similar to Pozzolanic silicates include (hereinafter referred to as synthetic Pozzolanic substitutes):
Alkaline silicates are preferably Potassium silicate K2SiO3 and preferably:
Preferred organic silica include:
Water-soluble activators, including in some cases chelates, include:
One embodiment of the present invention uses an alternative aqueous-based solution-colloid processes for manufacturing of modern functional inorganic materials such as concrete, cements, mortars, concrete bricks, stoneware and trowel-able plasters, water-resistant plasterboards, silicate paints.
In one embodiment, according to a hydraulic chelate-activated cement the following properties include (approximately in order of importance):
Other applications include kitchen counter tops, flotation devices, stucco, decking, fireplace mantles, cinder block, structural insulated panels, blasting grit, recycled plastic lumber, utility poles, railway sleepers, highway sound barriers, marine pilings, door and window frames, sign posts, paving stones, park benches, landscape timbers, planters, pallet blocks, bowling balls and artificial reefs.
Tentative qualitative explanations of some of the processes in preferred embodiments, in use, follow. In the following embodiments, some activators can include chelates, some reactions can by catalytic in nature and some products of reactions can take on the appearance of a mineral polymer.
Alternative aqueous-based solution processes for manufacturing of hard setting functional inorganic silica based materials can be formed from metal alkoxide solutions using embodiments of the present invention. The precursor used in a sol-gel process according to one embodiment of the present invention consists of a metaloid element, colloidal/amorphous silicate and any of a number of organic activators. Metal oxides, such as aluminates, calcium based reactants and titanates are preferred precursors because of their high reactivity towards water. The sol-gel process according to one embodiment of the present invention consists of a series of hydrolysis and condensation reactions of dissolved colloidal silicates.
According to one embodiment, the process consist of:
Through the sol-gel process, homogenous, high durability inorganic metal silicates can be made at ambient temperature and at neutral or weakly alkaline PH rather than the high temperature and alkalinity required in conventional approaches for hydraulic cement materials. It is observed from SEM test results that a 3-dimensional gel is formed throughout the sample on curing that has the appearance of a mineral polymer. This pore filling process that incorporates metal silicate crystals provides additional beneficial effects such as higher strength; better wear resistance, greater durability, lower porosity and chemical stability.
Arguably, calcium complexes are not spent as they form cement crystals, but rather continue to work on their substrate. Complex molecules can be argued to diffuse naturally in solution through pores and voids of cement, masonry and plaster materials. Both water and space must be present for the crystals to form. The space is often provided by cracks that form due to damage to the substrate caused by weathering, drying shrinkage, or other mechanisms such as chloride or acid attack.
Metal oxides in the form of mineral pigments are incorporated into the silica matrix rather than being present as an inert filler. Activators are also shown to form silica compounds with the most common pigments that are used as coloring oxides in cement. These pigment crystals are integral with the coating and less maintenance is required at the surface if there is chipping or cracking thus exposing the interior concrete. The pigments have been examined by SEM and reacted chemically to some extent in the cement crystal increasing process.
When titanium dioxide (TiO2) absorbs ultraviolet light, it becomes highly reactive and breaks down pollutants that come into contact with the concrete's surface. Several recent investigations have reported the ability of titanium dioxide and silica complexes (TiO2.SiO2), in combination with UV light, to kill various microbial and removed air pollution [J. S. Dalton, P. A. Janes, N. G. Jones, J. A. Nicholson, K. R. Hallam, G. C. Allen, “Photocatalytic oxidation of NOx gases using TiO2:a surface spectroscopic approach”, Environmental Pollution 120 (2002) pp. 415-422.]. Moreover, it was previously claimed by thermal analysis and SEM, that TiO2 cannot be reacted with Portland cement and water, instead forming a fine non-reactive filler to cement that modifies the hydration reaction primarily due to dilution [Thanongsak Nochaiya and Arnon Chaipanich, “The effect of nano-TiO2 addition on Portlandcement properties”, Cement and Concrete Research Laboratory, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, Thailand, 50200]. The addition of an activator, which can include a chelate according to one embodiment of the present invention, has shown that titanium dioxide and silica complexes have been formed under the influence of the activator (which can have a catalytic effect in one embodiment).
Scanning electron microscope (SEM) analysis of the coating confirms that in the case of a catalyst activator according to one embodiment, that a ligand, forms chelate complexes within the coating. Metal ions have formed insoluble precipitates with silica, a prominent example being calcium silicate hydrate, the primary product of the hydration of Portland cement that is primarily responsible for the strength in cement based materials. SEM images show that the secondary hydration products grow in the form of fibers on both C3S scaffold, Ca(OH)2 and CaCO3 crystals. SEMQuant microanalysis of the fibrous particles indicates calcium metasilicate CaOSiO2 as wollastonite.
In the influence of a Oxalic Acid C2H2O4 chelate the element spectra graph shows the presence of other metal silicates including: sodium metasilicate Na2SiO3.nH2O; Aluminium silicate Al2SiO3; Potassium Silicate K2SiO3; Titanium Silicate TiO2SiO2; and Iron Silicate Fe2SiO4.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013901015 | Mar 2013 | AU | national |
The present invention claims the benefit of priority from AU Provisional Patent Application Number 2013901015 entitled A Metal Oxide Activated Cement filed on Mar. 24, 2013 and U.S. Provisional Patent Application No. 61/810,010 entitled Metal Oxide Activated Cement filed on Apr. 9, 2013 the contents of which are incorporated herein by reference (as if recited below).
| Number | Date | Country | |
|---|---|---|---|
| 61810010 | Apr 2013 | US |