1. Field of Invention
The present invention relates to a manufacture method for a semiconductor device. More particularly, the present invention relates to a fabrication method for a semiconductor device with a locally strained channel.
2. Description of Related Art
The metal-oxide-semiconductor (MOS) transistor is an important device applied in very-large-integrated-circuits such as microprocessors and semiconductor memories. In addition to a gate oxide layer and a conductive gate structure, the MOSFET transistor further includes a source/drain region having a conductivity type opposite to that of the substrate.
To enhance the device performances, a silicon layer, which has received a tensile strain, is sometimes used as a channel. Strained silicon layer is the result of biaxial tensile stress induced in silicon grown on a substrate formed with a material whose lattice constant is greater than that of silicon, for example a silicon germanium layer. Strained silicon is shown to modify the electron or hole mobility of the silicon layer, which in turns affect the performance of a device. Larger enhancements of electron or hole mobility require a higher amount of strain.
Moreover, to increase the number of components per IC chip, the device dimensions must be scaled down. As the device dimension continues to shrink, the source/drain regions also become smaller. The smaller the source/drain region is, the higher is the resistance, thus reducing the current of the device and inducing over loading. However, if the junction depth of the source/drain region is increased to improve the aforementioned problems, new issues, including short channel effects and junction leakage, can arise. On the other hand, if heavy dosage implantation is used to reduce the resistance, solid solubility limitation may hamper application of heavy dosage implantation for forming shallow junction for the source/drain regions. In the prior art, the shallow junction source/drain region is coupled with shrunk spacers for preventing short channel effects. However, the resulted silicided shallow junction may lead to unacceptable junction leakage and further increase the junction resistance.
The invention provides a manufacturing method for a semiconductor device, wherein the channel is locally strained to modify the carrier transport properties.
The invention further provides a manufacturing method for a semiconductor device for decreasing the resistance of the source/drain region.
Accordingly, the present invention provides a manufacturing method for a semiconductor device, which is applicable for forming a strained channel. Because the gate structure is under a compressive stress, tensile strain is introduced to the channel.
The invention further provides a manufacturing method for a semiconductor device, which is applicable for forming shallow junction source/drain regions. Because the conductivity of the source/drain region is increased, the source/drain region can adopt shallow junctions to prevent short channel effect and junction leakage.
As embodied and broadly described herein, the invention provides a method for forming a semiconductor device structure, which includes forming a silicon germanium (SiGe) layer on a substrate and a strained silicon layer on the SiGe layer. A gate oxide layer is further formed on the strained silicon layer and a gate structure is formed on the gate oxide layer. A doping step is then performed to form a lightly doped source/drain region in the strained silicon layer at both sides of the gate structure. Subsequent to forming a spacer on a sidewall of the gate structure, the gate structure and the strained silicon layer are heavily doped with n-type dopants to form an n-type gate structure and a heavily doped drain region in the strained silicon layer. Alternatively, the heavily doped drain region is formed in the strained silicon layer and the SiGe layer at both sides of the gate structure. A cap layer is further formed over the substrate. Subsequent to a cap annealing process, the cap layer is removed.
By growing a silicon layer on a SiGe layer, the channel at the strained silicon layer is under biaxial tensile strain. Further with the cap-annealing process, a compressive stress is generated on the n-type gate structure, which in turns introduces tensile strain to the strained silicon layer. The tensile strain of the strained silicon layer enhances the horizontal mobility of electrons in the channel. As a result, the operating speed of a device can also be increased.
For the manufacturing method of a semiconductor device of the present invention, because the source/drain region is located either in the strained silicon layer or in both the strained silicon layer and the SiGe layer with higher conductivity, the resistance of the source/drain region is effectively reduced.
Further, since the resistance of the source/drain region is effectively reduced, the source/drain region can be formed as shallow junctions, thus avoiding short channel effect and junction leakage.
For the semiconductor device of the present invention and the manufacturing method thereof, both the performance and the reliability of the device are improved.
It is to be understood that both the foregoing general description and the following detailed description are exemplary, and are intended to provide further explanation of the invention as claimed.
The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
FIG. 3B and
Referring to
Due to the lattice mismatch with the SiGe layer 202, the strained silicon layer 204 is under biaxial tensile strain. The band structure is modified and the carrier transport is enhanced. The tensile strain of the strained silicon layer 204 on the relaxed SiGe layer 202 also improves the so-called surface roughness scattering.
Referring to
It is noted that the underlying strained silicon layer 204 will be consumed and become thinner during the formation process of the gate oxide layer 206. The gate oxide layer 206 formed on the strained silicon layer 204 has a uniform thickness and the interface between the gate oxide layer 206 and the strained silicon layer 204 is smooth.
Afterwards, a gate structure 208 is formed on the gate oxide layer 206. The material for forming the gate structure 208 is, for example, polysilicon or silicon germanium. The process to form the gate structure 208 includes depositing a polysilicon layer or a silicon germanium layer (not shown) on the gate oxide layer 206 and patterning the polysilicon layer or the silicon germanium layer to form the gate structure 208, for example.
Referring to
Referring to
Since the LDD region 210 is configured in the strained silicon layer 204 at both sides of the gate structure 208, a channel region 212 is defined in the strained silicon layer 204 between the LDD region 210.
Continuing to
Still referring to
Continuing to
Referring to
Due to lattice mismatch with the SiGe layer 202, the strained silicon layer 204 is under biaxial tensile strain when it is being epitaxially grown on a SiGe layer. During the cap annealing process, a compressive stress is generated on the n-type gate structure 208bs due to the expansion of the arsenic ions implanted in the gate structure 208. A tensile strain is thereby further introduced to the strained-channel 212. The induced tensile strain modifies the band structure and enhances the carrier transport. Thus, if a field effect transistor is formed by using the strained silicon layer 204 as the channel, the horizontal mobility of electrons increases in the channel, and the operating speed of the transistor also increases. A higher amount of strain can be induced from generating tensile stress in the n-type gate.
The tensile strain of the strained silicon layer 204 on the relaxed SiGe layer 202 improves the so-called surface roughness scattering and the phonon scattering. Due to the improved surface roughness scattering-limited mobility and the phonon scattering-limited mobility of strained silicon, the electron mobility increases. Further, the current drive characteristics of a strained silicon device also exhibit improvement.
In accordance to the present invention, the source/drain region is formed in the strained silicon layer, the channel region is thus also located in the strained silicon layer. Because the conductivity of the SiGe layer is higher and the electron mobility in the strained silicon layer is faster compared with the conventional silicon substrate, resistance of the source/drain region can be efficiently reduced. Therefore, the source/drain region of the present invention can adopt shallow junctions, thus avoiding short channel effect and junction leakage. As a result, not only the device performance but also reliability of the device can be improved. Accordingly, the strained Si MOSFET of the present invention is promising in high performance deep sub-100 nm (sub-0.1 micron) CMOS technology.
In conclusion, in accordance to the manufacturing method of a semiconductor device of the present invention, a compressive stress is generated on the N-type gate. A tensile strain is also further being introduced to the channel disposed in the strained silicon layer underneath the N-type gate. The horizontal mobility of electrons thus increases in the channel.
Further, the source/drain region is located either in the strained silicon layer or in both the strained silicon layer and the SiGe layer with higher conductivity, the resistance of the source/drain region is effectively reduced.
Since the resistance of the source/drain region is effectively reduced, the source/drain region can be formed as shallow junctions, thus avoiding short channel effect and junction leakage.
For the manufacture method of a semiconductor device of the present invention, both the performance and the reliability of the device are improved.
Although in the above, the present invention has been described with respect to a NMOS device, the present invention is also applicable to devices, such as, high/low voltage transistors in the peripheral device region or other types of transistors.
It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the present invention without departing from the scope or spirit of the invention. In view of the foregoing, it is intended that the present invention cover modifications and variations of this invention provided they fall within the scope of the following claims and their equivalents.
This application is a continuation-in-part of a prior application Ser. No. 10/064,705, filed Aug. 8, 2002 now abandoned, which is incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
6071783 | Liang et al. | Jun 2000 | A |
6600170 | Xiang | Jul 2003 | B1 |
Number | Date | Country | |
---|---|---|---|
20040115888 A1 | Jun 2004 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 10064705 | Aug 2002 | US |
Child | 10605122 | US |