Information
-
Patent Grant
-
6645564
-
Patent Number
6,645,564
-
Date Filed
Wednesday, March 6, 200222 years ago
-
Date Issued
Tuesday, November 11, 200320 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
-
CPC
-
US Classifications
Field of Search
US
- 427 402
- 427 4071
- 427 560
- 427 600
- 427 162
- 427 3741
- 427 3742
- 427 3743
- 427 3831
- 427 3981
- 427 404
- 427 409
- 427 4301
- 427 327
- 427 318
- 427 309
-
International Classifications
-
Abstract
A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base is provided. The method includes the step of forming the basecoat layer and the metal plating layer on the surface of the base. The step is followed by subjecting the metal plating layer to a cold heat treatment or an ultrasonic wave treatment, thus forming a microcrack in the metal plating layer. Afterwards, the topcoat layer is formed on the surface of the metal plating layer.
Description
BACKGROUND OF THE INVENTION
The present invention relates to methods for fabricating a plated product that has a base on which a basecoat layer, a metal plating layer, and a topcoat layer are formed, and, more particularly, to methods for fabricating a plated product that has microcracks formed in a metal plating layer to suppress corrosion development in the metal plating layer, thus maintaining the appearance of the product.
For example, Japanese Laid-Open Patent Publication No. 10-309774 describes a method for fabricating a layered body with a silver plating layer. The layered body includes a base, an undercoat layer, the silver plating layer, and a topcoat layer. The undercoat layer is formed by drying an undercoat agent, or a varinish that contains alkoxy-titanium-ester and at least either a silane coupling agent with epoxy radicals or epoxy resin.
To form the layered body, the undercoat agent is applied to the surface of the base and is dried to obtain the undercoat layer. Subsequently, an aqueous solution of silver is applied to the surface of the undercoat layer and is dried to form the silver plating layer. The topcoat layer is then formed on the surface of the silver plating layer. The method of the aforementioned patent publication is applicable to layered products with various bases such as insulating or conductive bases. Further, as fabricated by this method, the layered body has the silver plating layer and the undercoat layer that are securely bonded together, and the durability of the layered body is improved. That is, the method makes it possible to efficiently and easily fabricate a layered body that has a silver plating layer with an improved property.
However, the layered body does not include a structure for preventing the topcoat layer and the silver plating layer from being corroded. Thus, if a chloride ion (Cl
−
) from the exterior of the layered body enters the silver plating layer through the topcoat layer, the material of the silver plating layer, or silver, is corroded. Once the corrosion occurs, the corrosion develops to the entire silver plating layer, thus forming visible whitish lines in the silver plating layer. This significantly hampers the appearance of the layered body. The layered body is thus highly unlikely to pass a salt water spraying test or CASS(Cupric chloride, acetic Acid, Salt Spray) Test for estimating anti-corrosion resistance and anti-weather resistance of a plated product used as an ornament.
SUMMARY OF THE INVENTION
Accordingly, to solve the aforementioned problem, it is an objective of the present invention to provide a method for fabricating a plated product that prevents the appearance of the product from being hampered by corrosion of a metal plating layer and passes an anti-corrosion resistance test.
To achieve the foregoing and other objectives and in accordance with the purpose of the present invention, the invention provides a method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base. The method includes the steps of forming the basecoat layer and the metal plating layer on the surface of the base, forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or a supersonic wave treatment after the formation of the basecoat layer and the metal plating layer, and forming the topcoat layer on a surface of the metal plating layer.
A further perspective of the present invention is a method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base formed of synthetic resin. The method includes the step of forming the basecoat layer on the surface of the base. The basecoat layer is obtained by applying a basecoat agent to the surface of the base or immersing the surface of the base in the basecoat agent and then drying the basecoat agent on the surface of the base. The method also includes the step of forming the metal plating layer on the basecoat layer. The metal plating layer is obtained by a chemical silver plating method. The method further includes the steps of forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or an ultrasonic wave treatment, and forming the topcoat layer on the surface of the metal plating layer.
Other aspects and advantages of the invention will become apparent from the following description, taken in conjunction with the accompanying drawings, illustrating by way of example the principles of the invention.
BRIEF DESCRIPTION OF THE DRAWINGS
The invention, together with objectives and advantages thereof, may best be understood by reference to the following description of the presently preferred embodiments together with the accompanying drawings in which:
FIG.
1
(
a
) is a cross-sectional view schematically showing a portion of a plated product of an embodiment according to the present invention;
FIG.
1
(
b
) is a perspective view corresponding to FIG.
1
(
a
); and
FIG. 2
is a flowchart showing a method for fabricating the plated product of the embodiment.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
An embodiment of the present invention will now be described with reference to the drawings.
As shown in FIG.
1
(
a
), a plated product
11
includes a base
12
formed of synthetic resin. A basecoat (BC) layer
13
, a silver plating layer
14
, and a topcoat (TC) layer
15
are applied in this order to a surface (a design surface) of the base
12
. The silver plating layer
14
is formed by a chemical plating method (electroless deposition) that uses a silver mirror reaction.
The base
12
is formed of acrylonitrile-butadiene-styrene copolymer (ABS), polycarbonate-ABS (PC-ABS) alloy, polypropylene (PP), olefin type thermoplastic elastomer (TPO), polymethyl methacrylate (PMMA), or thermoplastic elastomer (TPE) by a known injection molding method.
To form the basecoat layer
13
, a basecoat agent is applied to the surface of the base
12
or the surface of the base
12
is immersed in the basecoat agent. The basecoat agent is then dried to complete the basecoat layer
13
. The basecoat agent includes polyester resin, alkyd resin, and acrylic resin. However, since a double-liquid hardened type polyurethane resin is easy to apply, it is preferred that the resin be used as the basecoat agent.
To form the silver plating layer
14
, a solution of ammoniacal silver nitrate ([Ag(NH
3
)
2
]
+
OH
−
) (Tollens reagent) and a reducer solution are applied to a surface of the basecoat layer
13
such that the two solutions are mixed on the surface. This causes an oxidization-reduction reaction, and silver (Ag) is deposited on the surface of the basecoat layer
13
to form the silver plating layer
14
. It is preferred that an organic compound with an aldehyde group including glyoxal (R—CHO), sodium sulfite, or sodium thiosulfate be used as the reducer solution. The silver mirror reaction between the ammoniacal silver nitrate solution and the organic compound with the aldehyde group is indicated by the following formula (1):
2[Ag(NH
3
)
2
]
+
OH
−
+R—CHO→2Ag+R—CO
2
NH
4
+H
2
O+3NH
3
(1)
Although the silver plating layer
14
is visible as a metal layer, numerous microcracks are formed in the silver plating layer
14
. Thus, as microscopically observed, the silver plating layer
14
forms a continuous structure in which numerous fine metal particles
16
with hexagonal or scale-like shapes are put together tightly, as schematically shown in FIG.
1
(
b
). In this structure, one side of each metal particle
16
is in contact with or is located close to the corresponding side of the adjacent metal particle
16
. The boundary between these sides of the metal particles
16
form a crystalline interface
17
.
To form the topcoat layer
15
, a topcoat agent is applied to a surface of the silver plating layer
14
or the surface of the silver plating layer
14
is immersed in the topcoat agent. The topcoat agent is then dried to complete the topcoat layer
15
. The topcoat agent includes polyester resin and acrylic resin. However, since the double-liquid hardened type polyurethane resin or acrylic modified silicone resin is easy to apply, it is preferred that these resins be used as the topcoat agent. It is further preferred that the topcoat agent contain a chlorine type trapping agent such as an epoxy type additive. The trapping agent traps a chloride ion that enters the topcoat agent
15
from the exterior of the plated product
11
and stops the chloride ion from reaching the silver plating layer
14
. This prevents the silver plating layer
14
from being corroded. Further, if the chloride ion is located on the surface of the silver plating layer
14
, the trapping agent traps the chloride ion, thus suppressing development of corrosion.
A method for fabricating the plated product
11
will now be described.
First, as shown in
FIG. 2
, the base
12
is formed in a predetermined shape through injection molding in step S
20
. A basecoat forming step (a BC forming step) S
30
is then conducted.
In the step S
30
, the basecoat layer
13
is formed on the surface of the complete base
12
using the basecoat agent. More specifically, in a pretreatment substep S
31
, the surface (the design surface) of the base
12
is sufficiently washed with a cleaning agent such as isopropanol. Subsequently, in a basecoat agent applying substep S
32
, the design surface of the base
12
is uniformly coated with the basecoat agent. The coating may be conducted by applying the basecoat agent on the design surface of the base
12
or immersing the design surface of the base
12
in the basecoat agent. However, since the design surface of the base
12
is easily coated by spraying the basecoat agent on the design surface, it is preferred that the coating be conducted through spraying. Afterwards, in a drying substep S
33
, the basecoat agent on the design surface of the base
12
is dried at approximately 80 degrees Celsius for about 60 minutes. The method then moves on to a plating step S
40
.
In the step S
40
, the silver plating layer
14
is formed on the basecoat layer
13
. First, in a silver mirror reaction pretreatment substep S
41
, a 2-3 weight percent solution of stannic chloride (SnCl
2
) is applied to the surface of the basecoat layer
13
or the surface of the basecoat layer
13
is immersed in the solution. Tin is thus adsorbed to the surface of the basecoat layer
13
. Subsequently, in a washing substep S
42
, the surface of the basecoat layer
13
is washed with ion exchange water (ion exchange water with electric conductivity of 3 μS/cm or lower is preferred) or distilled water. Excessive stannic chloride, which remains non-adsorbed, is thus removed. In these substeps S
41
and S
42
, palladium (Pd) may be used instead of tin.
Next, in a silver mirror reaction coating substep S
43
, an ammoniacal silver nitrate solution and a reducer solution are applied together to the washed surface of the basecoat layer
13
. This causes a silver mirror reaction between the solutions such that silver is deposited on the surface of the basecoat layer
13
. The solutions may be easily applied to the basecoat layer
13
with a double-headed spray gun or a concentric spray gun. The deposited silver replaces the tin on the surface of the basecoat layer
13
and is adsorbed to and accumulated on the surface of the basecoat layer
13
, thus forming the silver plating layer
14
. In a subsequent washing step S
44
, the surface of the silver plating layer
14
is washed with ion exchange water or distilled water to remove excessive solution and tin. The method then moves on to a silver mirror reaction posttreatment substep S
45
.
Even after the washing substep S
44
, a trace quantity of impurities may remain adsorbed to the surface of the silver plating layer
14
. Particularly, organic byproducts from the silver mirror reaction indicated by the formula (1) such as NH
3
or R—CO
2
NH
4
may remain unwashed on the surface of the silver plating layer
14
.
These impurities are modified through natural oxidization by oxygen in the ambient air, thus discoloring the surface of the silver plating layer
14
to an yellowish tone. This significantly hampers the appearance of the plated product
11
. Thus, in the substep S
45
, an appropriate posttreatment is conducted to prevent the impurities from discoloring the silver plating layer
14
. The posttreatment may be performed as an impurity disintegrating stage, an impurity adsorbing stage, or an antioxidant film forming stage. In the impurity disintegrating stage, the impurities are disintegrated to be removed from the surface of the silver plating layer
14
. In the impurity adsorbing stage, the impurities are adsorbed to be removed from the surface of the silver plating layer
14
. In the antioxidant film forming stage, a thin antioxidant film is formed on the surface of the silver plating layer
14
.
More specifically, in the impurity disintegrating stage, a low concentration acid is applied to the surface of the silver plating layer
14
or the surface of the silver plating layer
14
is immersed in the acid, thus disintegrating the impurities to remove the impurities from the surface of the silver plating layer
14
. It is preferred that the acid be acetic acid or dilute sulfuric acid. It is further preferred that the acid strength of the acid be 1.0×10
5
to 1.0×10
7
in terms of acid constant Ka, or −7 to 5 in terms of pKa. Also, it is preferred that 3 to 10 weight percent acetic acid or 2 to 6 weight percent dilute sulfuric acid be used. In the subsequent impurity adsorbing stage, a protein dispersed solution is applied to the surface of the silver plating layer
14
or the surface of the silver plating layer
14
is immersed in the solution, thus enabling the protein to adsorb the impurities and remove the impurities from the surface of the silver plating layer
14
. The protein dispersed solution includes mammalian milk such as cow milk and powdered milk. However, it is preferred that casein dispersed in water or a low-concentration aqueous alcohol solution as solvent be used as the protein dispersed solution.
In the antioxidant film forming stage, a metal surface treatment agent is applied to the surface of the silver plating layer
14
or the surface of the silver plating layer
14
is immersed in the agent, thus forming a thin antioxidant film on the surface of the silver plating layer
14
.
The metal surface treatment agent includes known metal surface treatment agents that are applicable to other metals than silver. The metal surface treatment agent forms a highly water-repellent antioxidant film, as applied to the surface of the silver plating layer
14
or other metal surfaces or metal plated surfaces. If the antioxidant film is formed on the surface of the silver plating layer
14
, the film physically inhibits the exposure of the surface of the silver plating layer
14
to the ambient air. The film thus functions as an antioxidant film that prevents the impurities on the surface of the silver plating layer
14
from being naturally oxidized by oxygen in the ambient air. Also, the film prevents the impurities from being nitrided by nitrogen in the ambient air.
It is most preferred that Top Rinse (brand name) of OKUNO SEIYAKU KOGYO KABUSHIKI KAISHA be used as the metal surface treatment agent. More specifically, it is preferred that the product be used as an aqueous solution of 1 to 50 weight percent. If the concentration of the product is less than one weight percent, the antioxidant effect on the surface of the silver plating layer
14
becomes insufficient. In contrast, if the concentration of the product exceeds
50
weight percent, the color of the surface of the silver plating layer
14
turns opaque.
After the silver mirror reaction posttreatment substep S
45
is completed, a washing substep S
46
is conducted. In S
46
, the surface of the silver plating layer
14
is washed with ion exchange water or distilled water. Subsequently, in a water blowing substep S
47
, water is blown by air and is removed from the surface of the silver plating layer
14
. Next, a microcrack forming substep (an MC forming substep) S
48
is conducted to form microcracks in the silver plating layer
14
. In the MC forming substep S
48
, a cold heat treatment or an ultrasonic wave treatment is performed.
In the cold heat treatment, a treatment cycle is defined by rapid cooling of the silver plating layer
14
followed by rapid heating of the silver plating layer
14
. The treatment cycle is repeated a plurality of times to form the microcracks in the silver plating layer
14
. In this treatment, it is preferred that the silver plating layer
14
be cooled to −20 degrees Celsius or lower and then be heated to 60 degrees Celsius or higher. Further, it is more preferred that the silver plating layer
14
be heated to 80 degrees Celsius or higher. The cooling of each treatment cycle is performed by, for example, maintaining the silver plating layer
14
, together with the base
12
, in a cold insulator at −20 degrees Celsius or lower for approximately 20 minutes or exposing the entire surface of the silver plating layer
14
to cold air at −20 degrees Celsius or lower for approximately 20 minutes. In addition, it is preferred that about three treatment cycles be performed to obtain an appropriate number of microcracks efficiently.
During the cold heat treatment, the silver plating layer
14
is repeatedly exposed to a temperature change between −20 degrees Celsius or lower and 60 degrees Celsius or higher. This forms numerous crystalline interfaces
17
in the silver plating layer
14
, as observed microscopically, without causing a visible change in the silver plating layer
14
. On the other hand, if the ultrasonic wave treatment is performed in S
48
, the surface of the silver plating layer
14
is exposed to ultrasonic waves for approximately ten minutes. Like the cold heat treatment, the ultrasonic wave treatment forms numerous crystalline interfaces
17
in the silver plating layer
14
, as observed microscopically, without causing a visible change in the silver plating layer
14
.
After the MC forming substep S
48
is completed, a topcoat forming step (a TC forming step) S
50
may follow immediately. However, it is preferred that a microcrack posttreatment substep (an MC posttreatment substep) S
49
be performed after the substep S
48
. It is preferred that an ultra-fine particle applying stage or a corrosion proof film forming stage be performed in the MC posttreatment substep S
49
. In the ultra-fine particle applying stage, a solution in which ultra-fine particles of an inorganic oxide are dispersed is applied to the surface of the silver plating layer
14
. In the corrosion proof film forming stage, a corrosion proof film is formed on the surface of the silver plating layer
14
. Alternatively, the ultra-fine particle applying stage and the corrosion proof film forming stage may be combined and performed in a certain order. This further improves the corrosion proof effect on the silver plating layer
14
.
More specifically, the ultra-fine particle dispersed solution used in the ultra-fine particle applying stage contains ultra-fine particles of an inorganic oxide with a particle size of nanometer order. Further, it is preferred that the solvent of the ultra-fine particle dispersed solution be removed from the surface of the silver plating surface
14
to dry the surface. Accordingly, the surface of the silver plating layer
14
is coated with the ultra-fine particles, and each of the crystalline interfaces
17
is filled with the particles. The inorganic oxide includes aluminum oxide (Al
2
O
3
), titanium oxide (TiO
2
), zirconium oxide (ZrO
2
), silicium oxide (SiO
2
), iron oxide (Fe
2
O
3
), zinc oxide (ZnO), cerium oxide (CeO
2
), and yttrium oxide (Y
2
O
3
). However, since aluminum oxide is easily available and is inexpensive, it is preferred that the substance be used as the inorganic oxide. Further, the ultra-fine particles of the inorganic oxide need to have an average particle size of nanometer order such that the particles are sufficiently dispersed in water. It is preferred that commercially available particles with an average particle size of 10 to 40 nanometers be used as the ultra-fine particles of the inorganic oxide.
In the corrosion proof film forming stage, a metal surface treatment agent is applied to the surface of the silver plating layer
14
or the surface of the silver plating layer
14
is immersed in the agent, thus forming a thin corrosion proof film on the surface of the silver plating layer
14
. It is preferred that the treated surface of the silver plating layer
14
be washed with ion exchange water or distilled water and then be dried. The metal surface treatment agent is the same as the one used in the antioxidant film forming stage of the silver mirror reaction posttreatment substep S
45
. That is, as in the antioxidant film forming stage, the treatment agent forms a highly water-repellent antioxidant film on the surface of the silver plating layer
14
. This physically inhibits the exposure of the surface of the silver plating layer
14
to chloride ions. The antioxidant film thus functions as a corrosion proof film that prevents the surface of the silver plating layer
14
from being corroded by the chloride ions.
Afterward, the TC forming step S
50
is performed to form the topcoat layer
15
on the surface of the silver plating layer
14
using a topcoat agent. The step S
50
includes a topcoat agent applying substep S
51
followed by a drying substep S
52
. In the substep S
51
, the topcoat agent is applied uniformly to the surface of the silver plating layer
14
. The surface of the silver plating layer
14
is then dried at approximately 70 degrees Celsius for about 60 minutes in the drying substep S
52
. The topcoat layer
15
is thus completed.
As fabricated by the above-described method, the plated product
11
includes the basecoat layer
13
, the silver plating layer
14
, and the topcoat layer
15
that are formed on the design surface of the base
12
in this order. As described, although the numerous crystalline interfaces
17
are formed in the silver plating layer
14
, as observed microscopically, the crystalline interfaces
17
are invisible. Thus, the surface of the plated product
11
is visible as an optimally shining silver mirror surface. Further, no impurities are caught between the silver plating layer
14
and the topcoat layer
15
or the impurities are physically prevented from being naturally oxidized. This suppresses yellowish discoloration of the design surface of the plated product
11
. Accordingly, a white reflected light is visible on the design surface of the plated product
11
, and the appearance of the product
11
is improved.
If a chloride ion enters the silver plating layer
14
via the topcoat layer
15
, one or more metal particles
16
may be corroded as observed microscopically. However, the corrosion of these metal particles
16
remains invisible, thus maintaining the appearance of the plated product
11
. Further, the crystalline interfaces
17
, which are formed along the sides of each of the metal particles
16
, significantly suppress further corrosion of the metal particles
16
, thus delaying development of the corrosion. In addition, even if the corrosion of the metal particles
16
is developed, the corrosion forms only a microscopic mark and remains invisible. This prevents the appearance of the silver plate product
11
from being hampered by the corrosion.
Thus, if the plated product
11
is exposed to salt water for a relatively long time, the appearance of the product
11
is hardly hampered. Also, the visible appearance of the plated product
11
is maintained when subjected to anti-corrosion resistance tests or anti-weather resistance tests, such as various salt water spray tests and CASS Test as defined by JIS. The plated product
11
thus easily passes these tests. In addition, the plated product
11
maintains its visible appearance even if the product
11
is exposed to ultraviolet rays for a relatively long time or if the base
12
is deformed.
The illustrated embodiment of the present invention has the following effects.
In the method for fabricating the plated product
11
according to the present invention, the basecoat layer
13
and the silver plating layer
14
are first formed on the surface of the base
12
. Subsequently, the silver plating layer
14
is subjected to the cold heat treatment or the ultrasonic wave treatment to form the microcracks in the silver plating layer
14
. Afterwards, the topcoat layer
15
is formed on the treated surface of the silver plating layer
14
. Accordingly, the crystalline interfaces
17
, which are formed around each of the microcracks, efficiently suppress development of corrosion in the silver plating layer
14
. This prevents the appearance of the silver plating product
11
from being hampered by the corrosion. Also, the plated product
11
easily passes various anti-corrosion resistance tests.
Particularly, the appearance maintaining effect of the plated product
11
is pronounced when the product
11
is plated with silver. More specifically, if a plated product with a metal plating layer formed of poorly corrosion-resistant material, such as silver, is fabricated by a conventional method, the product may not pass an anti-corrosion resistance test, and the appearance of the product may be significantly hampered over time. This makes it difficult to fabricate a plated product using the poorly corrosion-resistant metal, or silver. However, since the plated product
11
of the present invention includes the microcracks formed in the silver plating layer
14
, the visible appearance of the plated product
11
is maintained even when corrosion is microscopically observed in the silver plating layer
14
. Accordingly, the method of the present invention makes it possible to fabricate a high-quality plated product using a desired metal, regardless of the level of anti-corrosion resistance.
The MC forming substep S
48
is easily completed by repeating the treatment cycle of the rapid cooling of the silver plating layer 14 to −20 degrees Celsius or lower followed by the rapid heating of the silver plating layer
14
to 60 degrees Celsius or higher. That is, the substep S
48
makes it possible to readily form an appropriate number of microcracks with appropriate dimensions that are regularly aligned in the silver plating layer
14
.
As described, if the ultra-fine particle applying stage is performed in the MC posttreatment substep S
49
, the ultra-fine particles of the inorganic oxide in water is applied to the surface of the silver plating layer
14
. This efficiently suppresses corrosion of the silver plating layer
14
and, in case the corrosion occurs, efficiently stops development of the corrosion in the silver plating layer
14
. Further, if the corrosion proof film forming stage is performed in the substep S
49
, the corrosion proof film is formed on the surface of the silver plating layer
14
. This efficiently suppresses corrosion of the silver plating layer
14
and, in case the corrosion occurs, efficiently stops development of the corrosion in the silver plating layer
14
. In addition, a general type may be used as the metal surface treatment agent in the corrosion proof film forming stage. That is, the metal surface treatment agent is readily available and inexpensive. Also, since the ultra-fine particle applying stage and the corrosion proof film forming stage are easy to conduct, work efficiency is maintained.
As described, the topcoat layer
15
is applied to the surface of the silver plating layer
14
using the topcoat agent that contains the chlorine type trapping agent for trapping chloride ions. This improves the effect of suppressing corrosion of the silver plating layer
14
and development of the corrosion in the silver plating layer
14
.
The following is examples of the illustrated embodiment and their comparative examples.
EXAMPLE 1
First, the base
12
with a square plate shape was formed of ABS through injection molding. The pretreatment substep S
31
was then completed by spraying isopropanol on the surface (the design surface) of the base
12
. Subsequently, in the basecoat agent applying substep S
32
, B-3 (brand name, acrylic urethane coating materials) of OHASHI KAGAKU KOGYO KABUSHIKI KAISHA was sprayed on the design surface of the base
12
as a basecoat agent. The drying substep S
33
was then performed in a drying furnace at 80 degrees Celsius for 60 minutes. The basecoat layer
13
with a uniform thickness of approximately 20 micrometers was thus formed on the design surface of the base
12
. Afterwards, an undercoat agent (U-1 (brand name) of OHASHI KAGAKU KOGYO KABUSHIKI KAISHA) was sprayed on the surface of the basecoat layer
13
and was then dried to form an undercoat layer.
Further, a solution that contained three weight percent of stannic chloride and one weight percent of hydrochloric acid was sprayed on the surface of the undercoat layer, thus completing the silver mirror reaction pretreatment substep S
41
. The surface of the undercoat layer was then washed by spraying ion exchange water with electric conductivity of 3 μS/cm or lower on the surface of the undercoat layer to complete the washing substep S
42
. Subsequently, in the silver mirror reaction coating substep S
43
, Tollens reagent and glyoxal were sprayed on the surface of the undercoat layer using a double-headed spray gun (RG-2 (brand name) of ANESUTO IWATA KABUSHIKI KAISHA). The silver plating layer
14
with a uniform thickness of approximately 1000 Angstrom was then formed on the surface of the undercoat layer. Afterwards, the surface of the silver plating layer
14
was washed by spraying ion exchange water on the surface of the silver plating layer
14
, thus completing the washing substep S
44
.
Next, in the silver mirror reaction posttreatment substep S
45
, a metal surface treatment agent (a 10 weight percent aqueous solution of Top Rinse (band name) of OKUNO SEIYAKU KOGYO KABUSHIKI KAISHA) was sprayed on the surface of the silver plating layer
14
. The surface of the silver plating layer
14
was then washed by spraying ion exchange water on the surface of the silver plating layer
14
, thus completing the washing substep S
46
. Subsequently, in the water blowing substep S
47
, compressed air was blown (an air blow was produced) to the surface of the silver plating layer
14
. At this stage, the plated product
11
had the base
12
, the basecoat layer
13
, the undercoat layer, and the silver plating layer
14
. The MC forming substep S
48
was then conducted by repeating three cycles of cold heat treatment. Each treatment cycle included cooling of the plated product
11
in a cold insulator at −20 degrees Celsius for 10 minutes followed by heating of the plated product
11
in a drying (heating) furnace at 80 degrees Celsius for 20 minutes.
Finally, a topcoat agent (T-1 (brand name) of OHASHI KAGAKU KOGYO KABUSHIKI KAISHA) was sprayed on the surface of the silver plating layer
14
, thus completing the topcoat agent applying substep S
51
. The plated product
11
was then subjected to the drying substep S
52
in a drying furnace at 70 degrees Celsius for 60 minutes. The topcoat layer
15
with a uniform thickness of approximately 20 micrometers was thus formed on the surface of the silver plating layer
14
. The obtained plated product
11
had the base
12
on which the basecoat layer
13
, the undercoat layer, the silver plating layer
14
, and the topcoat layer
15
were formed.
COMPARATIVE EXAMPLE 1
Comparative Example 1 was produced in the same manner as Example 1, except that the MC forming substep S
48
was not performed and the product
11
was dried in a drying furnace at 50 degrees Celsius for 30 minutes after the water blowing substep S
47
. The obtained plated product had the base
12
on which the basecoat layer
13
, the undercoat layer, the silver plating layer
14
, and the topcoat layer
15
were formed.
EXAMPLE 2
In Example 2, U-2 (brand name, bisphenol type epoxy coating materials) of OHASHI KAGAKU KOGYO KABUSHIKI KAISHA was used as the undercoat agent, and PTC-02 (brand name, silicone acrylic coating materials) of FUJIKURA KASEI KABUSHIKI KAISHA was used as the topcoat agent. Further, the MC posttreatment substep S
49
was performed between the MC forming substep S
48
and the topcoat agent applying substep S
51
. In the MC posttreatment substep S
49
, ultra-fine particles of aluminum oxide (Nanomaterial (brand name) of NANOTECH KABUSHIKI KAISHA) dispersed in acescent water was first sprayed on the surface of the silver plating layer
14
. The product
11
was then dried in a drying furnace at 50 degrees Celsius for 30 minutes. The remainder of Example 2 was performed in the same manner as Example 1. The obtained plated product
11
had the base
12
on which the basecoat layer
13
, the undercoat layer, the silver plating layer
14
, and the topcoat layer
15
were formed.
COMPARATIVE EXAMPLE 2
Comparative Example 2 was performed in the same manner as Example 2, except that the MC forming substep S
48
and the MC posttreatment substep S
49
were omitted. The obtained plated product had the base
12
on which the basecoat layer
13
, the undercoat layer, the silver plating layer
14
, and the topcoat layer
15
were formed.
Anti-Corrosion Resistance Acceleration Tests
Anti-corrosion resistance acceleration tests were performed on the plated products
11
of Examples 1, 2 and the plated products of Comparative Examples 1, 2 in accordance with a method of CASS Test. More specifically, a 5 weight percent aqueous solution of sodium chloride that contained a small quantity of acetic acid and cupric chloride were sprayed in a test apparatus while maintaining the temperature of the solution at 49 degrees Celsius. Each plated product was placed still in the test apparatus to visually evaluate development of corrosion and opaque discoloration of the silver mirror surface. As a result, the corrosion development and the discoloration of the silver mirror surface were both observed in the plated product of each comparative example, as time elapsed. However, neither corrosion nor discoloration was visually observed in the plated products
11
of Examples 1, 2. Further, this difference between Examples and Comparative Examples gradually became more pronounced as time elapsed.
It should be apparent to those skilled in the art that the present invention may be embodied in many other specific forms without departing from the sprit or scope of the invention. Particularly, it should be understood that the invention may be embodied in the following forms.
The silver mirror reaction posttreatment substep S
45
may be omitted.
The silver plating layer
14
does not necessarily have to be formed by a chemical plating method (electroless deposition). However, the silver plating layer
14
may be formed by an electric plating method, a roll leaf hot stamping method, or a vacuum deposition method. If this is the case, a microcrack forming substep identical with the substep S
48
need be performed after the silver plating layer
14
is formed.
When forming a plated product using metal other than silver, or, particularly, a relatively poorly corrosion-resistant metal, a microcrack forming substep identical with the substep S
48
may be performed after a metal plating layer is formed.
The material of the base
12
includes molded bodies of rubber, glass, ceramics, wood, or paper with various shapes, as long as the basecoat layer
13
can be formed directly or indirectly on the surface of the base
12
. Further, the base
12
may be formed of thermoplastic resin other than the one used in the illustrated embodiment or thermally hardened resin. In addition, the base may be formed of hard or soft synthetic resin.
The present examples and embodiments are to be considered as illustrative and not restrictive and the invention is not to be limited to the details given herein, but may be modified within the scope and equivalence of the appended claims.
Claims
- 1. A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, the method comprising the steps of:forming the basecoat layer and the metal plating layeron the surface of the base; forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment after the formation of the basecoat layer and the metal plating layer, wherein the cold heat treatment is performed by repeating a plurality of treatment cycles, and each of the treatment cycles includes cooling the metal plating layer to −20 degrees Celsius or lower and then heating the metal plating layer to 60 degrees Celsius or higher; and forming the topcoat layer on a surface of the metal plating layer.
- 2. A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, the method comprising the steps of:forming the basecoat layer and the metal plating layer on the surface of the base; forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or a supersonic wave treatment after the formation of the basecoat layer and the metal plating layer; applying a solution in which ultra-fine particles of an inorganic oxide are dispersed on the surface of the metal plating layer after the formation of the microcrack in the metal plating layer; and forming the topcoat layer on a surface of the metal plating layer.
- 3. A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base, wherein the metal plating layer is a silver plating layer formed by a chemical plating method that uses silver mirror reaction, the method comprising the steps of:forming the basecoat layer and the metal plating layer on the surface of the base; forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or a supersonic wave treatment after the formation of the basecoat layer and the metal plating layer; and forming the topcoat layer on a surface of the metal plating layer.
- 4. The method according to claim 3, further comprising the step of forming a corrosion proof film on the surface of the metal plating layer after the formation of the microcrack in the metal plating layer.
- 5. The method according to claim 4, wherein the corrosion proof film forming step includes coating the surface of the metal plating layer with a metal surface treatment agent.
- 6. The method according to claim 3, wherein the topcoat layer is formed of a topcoat agent that contains a trapping agent for trapping a chloride ion.
- 7. The method according to claim 3, wherein the base is formed of synthetic resin.
- 8. A method for fabricating a plated product with a basecoat layer, a metal plating layer, and a topcoat layer that are formed on a surface of a base formed of synthetic resin, the method comprising the steps of:forming the basecoat layer on the surface of the base, wherein the basecoat layer is obtained by applying a basecoat agent to the surface of the base or immersing the surface of the base in the basecoat agent and then drying the basecoat agent on the surface of the base; forming the metal plating layer on the basecoat layer, wherein the metal plating layer is obtained by a chemical silver plating method; forming a microcrack in the metal plating layer by subjecting the metal plating layer to a cold heat treatment or an ultrasonic wave treatment; and forming the topcoat layer on the surface of the metal plating layer.
- 9. The method according to claim 8, wherein the cold heat treatment is performed by repeating a plurality of treatment cycles, and each of the treatment cycles includes cooling the metal plating layer to −20 degrees Celsius or lower and then heating the metal plating layer to 60 degrees Celsius or higher.
- 10. The method according to claim 8, further comprising the step of applying a solution in which ultra-fine particles of an inorganic oxide are dispersed to the surface of the metal plating layer after the formation of the microcrack in the metal plating layer.
- 11. The method according to claim 8, further comprising the step of forming a corrosion proof film on the surface of the metal plating layer after the formation of the microcrack in the metal plating layer.
- 12. The method a cording to claim 11, wherein the corrosion proof film forming step includes coating the surface of the metal plating layer with a metal surface treatment agent.
Priority Claims (1)
Number |
Date |
Country |
Kind |
2001-062243 |
Mar 2001 |
JP |
|
US Referenced Citations (2)
Foreign Referenced Citations (1)
Number |
Date |
Country |
10-309774 |
Nov 1998 |
JP |