The invention relates to a method for fabricating semiconductor device, and more particularly to a method of using a soak anneal process to increase an oxygen concentration of a seal layer to a saturation level.
In current semiconductor industry, polysilicon has been widely used as a gap-filling material for fabricating gate electrode of metal-oxide-semiconductor (MOS) transistors. However, the conventional polysilicon gate also faced problems such as inferior performance due to boron penetration and unavoidable depletion effect which increases equivalent thickness of gate dielectric layer, reduces gate capacitance, and worsens driving force of the devices. In replacing polysilicon gates, work function metals have been developed to serve as a control electrode working in conjunction with high-K gate dielectric layers.
However, in current fabrication of high-k metal transistor particularly when ion implantation processes were conducted to implant dopants into the substrate for forming lightly doped drains (LDDs), the concentration of implanted dopants is often disturbed due to various factors and resulting in issue such as Vt roll-off and affecting the performance of the device. Hence, how to resolve this issue has become an important task in this field.
According to an embodiment of the present invention, a method for fabricating a semiconductor device includes the steps of: providing a substrate having a NMOS region and a PMOS region; forming a first gate structure on the NMOS region and a second gate structure on the PMOS region; forming a seal layer on the first gate structure and the second gate structure; forming a first lightly doped drain (LDD) adjacent to the first gate structure; forming a second LDD adjacent to the second gate structure; and performing a soak anneal process to boost an oxygen concentration of the seal layer for reaching a saturation level.
These and other objectives of the present invention will no doubt become obvious to those of ordinary skill in the art after reading the following detailed description of the preferred embodiment that is illustrated in the various figures and drawings.
Referring to
According to an embodiment of the present invention, the fin-shaped structure 14 could be obtained by a sidewall image transfer (SIT) process. For instance, a layout pattern is first input into a computer system and is modified through suitable calculation. The modified layout is then defined in a mask and further transferred to a layer of sacrificial layer on a substrate through a photolithographic and an etching process. In this way, several sacrificial layers distributed with a same spacing and of a same width are formed on a substrate. Each of the sacrificial layers may be stripe-shaped. Subsequently, a deposition process and an etching process are carried out such that spacers are formed on the sidewalls of the patterned sacrificial layers. In a next step, sacrificial layers can be removed completely by performing an etching process. Through the etching process, the pattern defined by the spacers can be transferred into the substrate underneath, and through additional fin cut processes, desirable pattern structures, such as stripe patterned fin-shaped structures could be obtained.
Alternatively, the fin-shaped structure 14 could also be obtained by first forming a patterned mask (not shown) on the substrate, 12, and through an etching process, the pattern of the patterned mask is transferred to the substrate 12 to form the fin-shaped structure. Moreover, the formation of the fin-shaped structure could also be accomplished by first forming a patterned hard mask (not shown) on the substrate 12, and a semiconductor layer composed of silicon germanium is grown from the substrate 12 through exposed patterned hard mask via selective epitaxial growth process to form the corresponding fin-shaped structure. These approaches for forming fin-shaped structure are all within the scope of the present invention.
Next, gate structures 22, 24 or dummy gate are formed on the substrate 12. In this embodiment, the formation of the gate structures 22, 24 could be accomplished by a gate first process, a high-k first approach from gate last process, or a high-k last approach from gate last process. Since this embodiment pertains to a high-k last approach, a gate dielectric layer 26 or interfacial layer, a gate material layer 28, and a selective hard mask such as a hard mask made of hard mask 30 and hard mask 32 could be formed sequentially on the substrate 12, and a pattern transfer process is then conducted by using a patterned resist (not shown) as mask to remove part of the hard masks 32, 30, part of the gate material layer 28, and part of the gate dielectric layer 26 through single or multiple etching processes. After stripping the patterned resist, gate structures 22, 24 each made of a patterned gate dielectric layer 26, a patterned material layer 28, and patterned hard masks 30, 32 are formed on the NMOS region 16 and PMOS region 18 respectively.
Next, a seal layer 34 is formed on the gate structures 22, 24, on the NMOS region 16 and PMOS region 18 to cover the surface of the substrate 12 and even the STI 20. In this embodiment, the seal layer 34 is preferably made of nitrides such as silicon nitride (SiN) having low-k dielectric constant or most preferably silicon oxycarbonitride (SiOCN). If the seal layer 34 were made of SiOCN the composition thereof preferably includes 32% of silicon atoms, 40% of oxygen atoms, 8% of carbon atoms, and 20% of nitrogen atoms.
Next, as shown in
Next, as shown in
Next, as shown in
It should be noted that even though the soak anneal process 42 is conducted through the injection of oxygen gas without the addition of any other gases to boost the oxygen content within the seal layer 34, according to other embodiment of the present invention it would also be desirable to not only injection oxygen gas but also other gas or gases such as nitrogen gas to conduct the soak anneal process 42, which is also within the scope of the present invention. Preferably, duration of the soak anneal process is between 60 minutes to 80 minutes or most preferably 70 minutes and temperature of the soak anneal process is between 700° C. to 1000° C., but not limited thereto.
Next, as shown in
Next, elements such as contact etch stop layer (CESL) could be formed on the gate structures 22, 24 on NMOS region 16 and PMOS region 18, an interlayer dielectric (ILD) layer could be formed on the surface of the CESL, a replacement metal gate (RMG) process could be conducted to transform the gate structures on each transistor region into metal gates, and a contact plug formation could be conducted to form contact plugs in the ILD layer and CESL for electrically connecting the source/drain regions 48, 50. This completes the fabrication of a semiconductor device according to an embodiment of the present invention.
Typically in current FinFET fabrication particularly when ion implantation processes were conducted to implant dopants into the substrate for forming lightly doped drains (LDDs), the concentration of implanted dopants is often shifted during waiting time or Q-time between different fabrication steps and resulting in issue such as Vt roll-off. To resolve this issue the present invention preferably conducts a soak anneal process after forming the LDDs to boost the oxygen concentration within the seal layer for reaching a saturation level so that the seal layer made of SiOCN is eventually transformed into SiO2. Upon experimental verification this approach could improve the issue of Vt roll-off significantly thereby improving the performance of the device.
Those skilled in the art will readily observe that numerous modifications and alterations of the device and method may be made while retaining the teachings of the invention. Accordingly, the above disclosure should be construed as limited only by the metes and bounds of the appended claims.