Claims
- 1. A method of improving the wear resistance and adhesive wear properties of a polymeric composite in a dry, smooth contact sliding tribological wear system wherein a surface of said polymeric composite bears against another surface causing friction and adhesive wear of said polymeric composite, the method comprising the steps of:
- a) providing a blend of a polyamide and a polypropylene selected from the group consisting of homopolymers and copolymers of propylene;
- b) providing to the blend a maleic-anhydride modified polypropylene functionalized to graft with the polyamide in the blend and compatible with the polypropylene in the blend; and
- c) melt-mixing the maleic-anhydride modified polypropylene with the blend to form a polymeric composite consisting essentially of the blend and the maleic anhydride-modified polypropylene, wherein the maleic anhydride-modified polypropylene in the composite is grafted to the polyamide such that the wear resistance of the polymeric composite is greater than a wear resistance of the blend in the tribological system.
- 2. A method according to claim 1, wherein said polyamide is selected from the group consisting of nylon-4/6, nylon-6, nylon-6/6, nylon-6/10, nylon-6/12, nylon-11 and nylon-12.
- 3. A method according to claim 1, wherein the ratio of said polyamide to said polypropylene is about 5:95 to about 95:5.
- 4. A method according to claim 3, wherein the ratio of said polyamide to said polypropylene is about 25:75 to 75:25.
- 5. A method according to claim 1, wherein said maleic-anhydride modified polypropylene comprises about 2 to about 20 weight percent of said composite.
- 6. A method according to claim 1, wherein said maleic-anhydride modified polypropylene has a tensile modulus greater than about 50,000 p.s.i.
- 7. The method according to claim 1, wherein the wear factor of the polymeric composite is no greater than 110.6.times.10.sup.-16 m.sup.3 /Nm.
- 8. A dry, smooth contact sliding tribological wear system comprising a first surface and a second surface, said second surface being formed of a polymeric composite and positioned to bear against said first surface in said tribological system to cause friction and adhesive wear, said polymeric composite consisting essentially of (i) a blend of a polyamide and a polypropylene selected from the group consisting of homopolymers and copolymers of propylene, and (ii) a maleic-anhydride modified polypropylene functionalized to graft with said polyamide in said blend and compatible with said polypropylene in said blend, said maleic anhydride-modified polypropylene in said composite being grafted to said polyamide such that the wear resistance of said polymeric composite in said tribological system is greater than the wear resistance of said blend in a tribological system comprising said blend and said first surface.
- 9. The tribological system of claim 8, wherein the wear factor of said polymeric composite in said system is no greater than 110.6.times.10.sup.-16 m.sup.3 /Nm.
Parent Case Info
This is a continuation of U.S. patent application Ser. No. 08/056,727, filed May 4, 1993 now abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (5)
Number |
Date |
Country |
3804161 |
Aug 1989 |
DEX |
59-149940 |
Aug 1984 |
JPX |
62-158739 |
Jul 1987 |
JPX |
1403797 |
Aug 1975 |
GBX |
WO88-006174 |
Aug 1988 |
WOX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
56727 |
May 1993 |
|