Claims
- 1. A method for the preparation of paper products having improved water and solvent resistance which comprises
- (a) preparing a paper base formulation prior to the formation of the paper base sheet, said formulation comprising paper making proportions of paper making ingredients including filler,
- an amount of the filler being nonfilm-forming plastic particles soluble in a solvent having an average particle size in the range of from 0.01 to 20 microns and selected from the group consisting of polymerizable hard resin monomers which can be polymerized and copolymerized with each other including styrene, alpha-methyl styrene, ar-(tert.-buty)styrene, ar-methyl styrene, ar, ar-dimethyl styrene, ar-chlorostyrene, ar-(tert.-amyl) styrene, ar-bromo styrene, ar-fluorostyrene, ar-cyanostyrene, ar-methoxy styrene, ar-ethyl styrene, ar-hydroxymethyl styrene, ethoxy styrene, ar-chloro-ar-methyl styrene, ar, ar-dichlorostyrene, ar, ar-difluorostyrene, vinyl naphthalene; acrylates and copolymers thereof, methyl methacrylate, chloroethyl methacrylate, 2-butyl methacrylate, 3,3-dimethyl butyl methacrylate, 3,3-dimethyl-2-butyl methacrylate, ethyl methacrylate, isobutyl methacrylate, isopropyl methacrylate, phenyl methacrylate, butyl chloroacrylate, isobutyl chloroacrylate, cyclohexyl chloroacrylate, methyl chloroacrylate, ethyl chloroacrylate, isopropyl chloroacrylate; vinyl acetate and copolymers thereof, vinyl benzoate, vinyl-ar-toluate, vinyl ar-ethylbenzoate, vinyl propionate, allyl acetate, allyl ar-ethylbenzoate, vinyl trimethylacetate, vinyl trichloroacetate, acrylonitrile, methacrylonitrile, fumaronitrile, vinyl chloride, vinyl bromide; vinyl butyral and copolymers thereof, vinyl butyl ether, mixtures of styrene and acrylonitrile, vinyl coumarones, vinyl carbazole, styrene/acrylic acid copolymers, styrene/acrylic acid/itaconic acid copolymers, styrene/methacrylic acid copolymers, t-butyl styrene/acrylonitrile/acrylic acid copolymers, vinyl chloride/acrylic acid copolymers, vinyl benzoate/acrylic acid copolymers, styrene/maleic copolymers, ethylene terephthalate, propylene terephthalate, ethylene-1,5-naphthalate, ethylene-isophthalate, ethylene-4,4-(2,2-butylidene)dibenzoate, 4,4'-butylidene diphenylene carbonate, 4,4'-isopropylidene diphenylene carbonate, 4,4'-methylene benzoic anhydride, isophthalic anhydride, hexamethylene pimelamide, hexamethylene azeloamide, hexamethylene adipamide, 7-aminoenanthic acid, 3-cyclohexyl-1-propene, vinyl cyclohexane, hexafluoropropylene, 3-o-methyl-phenylpropene, ethylene, propylene, 1-butene, 5,5-dimethyl-1-hexene, 3-methyl-1-butene, vinylidene chloride, 1,2-difluoro-ethylene, cellulose acetate-butyrate, cellulose triacetate, and mixtures of any of the above,
- (b) formming said paper base formulation into a paper base sheet;
- (c) drying the formed paper base sheet, the plastic particles being in an essentially noncoalesced state at time of formation of the paper base sheet and nonfilm-forming under the conditions of formation of the paper base sheet and drying of the sheet;
- (d) thereafter wetting the formed paper base sheet from step (c) with said solvent in which the plastic particles are soluble for a time sufficient to solubilize the plastic particles; and
- (e) drying the formed sheet; the amount of plastic particles and solubility being sufficient to form a plastic film which is sufficiently continuous to materially increase water and solvent resistance of the paper base sheet.
- 2. The method of claim 1 wherein said plastic particles are thermoplastic organic resinous polymers.
Parent Case Info
This is a division of application Ser. No. 827,127, filed Aug. 24, 1977, now abandoned.
US Referenced Citations (27)
Foreign Referenced Citations (2)
Number |
Date |
Country |
456887 |
Aug 1944 |
BEX |
166805 |
Apr 1934 |
CHX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
827127 |
Aug 1977 |
|