Claims
- 1. A method of making a composite, neutron absorbing article which is of a thickness in the range of 1 to 7 mm. and of a B.sup.10 loading from 0.001 to 0.1 g./sq. cm. which comprises coating a side of a fiberglass cloth backing member with a curable liquid phenolic resin, applying boron carbide particles to the liquid resin and solidifying the resin to cross-linked permanently set form.
- 2. A method according to claim 1 wherein the article made is of a thickness of 1 to 3 mm., the B.sup.10 loading applied is from 0.005 to 0.03 g./sq. cm., the weight of the article is in the range of 0.5 to 3 kg./sq. m., phenolic resin and boron carbide particles are applied to both sides of the backing member and the boron carbide particles are distributed so that 3 to 25% of the B.sup.10 is on one side of the backing member and the balance is on the other side.
- 3. A method according to claim 2 wherein the B.sup.10 applied to one side of the article is from 10 to 20% of the total B.sup.10 of the article and the balance is applied to the other side, such balance being of finely divided boron carbide particles mixed in with the resin and larger boron carbide particles adhered to said resin.
- 4. A method of making a composite neutron absorbing article which comprises coating a side of a fiberglass backing member with a mixture of liquid synthetic organic polymeric material and finely divided boron carbide particles, partially curing the polymeric material, coating the other side of the backing member with a liquid synthetic organic polymeric material, applying boron carbide particles to such polymeric mateial, with the amount of boron carbide particles being sufficient to bring the B.sup.10 loading of the neutron absorbing article to within the range of 0.001 to 0.1 g./sq. cm., and solidifying the polymer(s) to cross-linked permanently set form.
- 5. A method according to claim 4 wherein the backing member is of woven fiberglass cloth.
- 6. A method according to claim 5 wherein the normally liquid synthetic organic polymeric material is a thermosettable phenolic resin in resol stage when applied, which is converted to solid form when partially cured.
- 7. A method according to claim 6 wherein the fiberglass cloth is of a thickness in the range of 0.1 to 2 mm., the weight thereof is from 50 to 2,000 g./sq. m., boron carbide particles which are of particle sizes in the No. 170 to 400 U.S. Sieve series range are mixed with the resin applied to the first side of the fiberglass cloth backing member, boron carbide particles which are of particle sizes in the No. 170 to 400 U.S. Sieve series range are mixed with the resin applied to the other side of the backing member, larger size boron carbide particles which are of particle sizes in the No. 60 to 170 U.S. Sieve series range, are applied to the other side of the backing member, the proportion of boron carbide particles, by weight, on the first side of the backing member is from 3 to 25% of the total boron carbide in the article, the proportion applied to the other side of the backing member mixed with the phenolic resin is from 10 to 35%, the proportion of larger size boron carbide particles applied to said other side of the backing member is 40 to 80%, and the B.sup.10 concentration in the finished article is in the range of 0.005 to 0.03 g./sq. cm.
- 8. A method according to claim 4 which includes coating a first side of the fiberglass backing member with a mixture of thermosettable normally liquid synthetic organic polymeric material and finely divided boron carbide particles mixed therein, partially curing said thermosettable polymeric material, coating the other side of the backing member with a thermosettable, normally liquid synthetic organic polymeric material, applying boron carbide particles of generally larger particle size than those applied to the first side to the polymeric material on said other side of the backing member and curing the polymer to cross-linked permanently set form.
- 9. A method according to claim 8 wherein the backing member is of fiberglass cloth and before application of the coating to the first side of the backing member said cloth is filled on both sides thereof with thermosettable normally liquid synthetic organic polymeric material and such material is partially cured.
- 10. A method according to claim 9 wherein there are mixed with the thermosettable normally liquid synthetic organic polymeric material applied to the other side of the backing member finely divided boron carbide particles of particle sizes in the same range as those particles applied to the first side of the backing member.
- 11. A method according to claim 10 wherein after application of boron carbide particles to the other side of the backing member and before curing of the polymer to cross-linked permanently set form the side of the article having the coarser boron carbide particles thereon is coated with thermosettable normally liquid synthetic organic polymeric material and such material, together with the other polymeric material in the article, is subsequently cross-linked to permanently set form.
- 12. A method according to claim 11 wherein the thermosettable normally liquid synthetic organic polymeric material is a phenolic resin in resole stage when applied and is converted to solid form when partially cured.
- 13. A method according to claim 12 wherein the backing member is of woven fiberglass cloth.
- 14. A method according to claim 13 wherein the cloth is of a thickness in the range of 0.1 to 2 mm., the weight thereof is from 50 to 2,000 g./sq. m., the boron carbide particles mixed with the resin applied to the first side of the backing member are of particle sizes in the No. 170 to 400 sieve range, the boron carbide particles mixed with the resin applied to the other side of the backing member are of particle sizes in the No. 170 to 400 range, the larger size boron carbide particles applied to the other side of the backing member are of particle sizes in the No. 60 to 170 sieve range, the proportion of boron carbide particles, by weight, on the first side of the backing member is from 3 to 25% of the total boron carbide in the article, the proportion applied to the other side of the backing member mixed with the phenolic resin is from 10 to 35% and the proportion of larger size boron carbide particles applied to said other side of the backing member is 40 to 80%.
- 15. A method according to claim 14 wherein the partial cures are effected over periods of about 20 minutes to three hours at temperatures in the range of 95.degree. to 125.degree. C. and the final cure is effected at temperatures within the range of 95.degree. to 180.degree. C. over a period of time from 2 to 50 hours, while holding the article flat or in desired final shape.
- 16. A method according to claim 15 wherein the generally larger particle size boron carbide particles are applied to the other side of the backing member by passing such backing member, in substantially horizontal position, other side upward and coated with curable resin of a molecular weight in the range of about 200 to 1,000, under falling boron carbide particles and removing unadhered particles after pressing the deposited particles into the resin.
Parent Case Info
This is a division of copending application Ser. No. 870,237, filed Jan. 17, 1978 now U.S. Pat. No. 4,218,622.
US Referenced Citations (20)
Foreign Referenced Citations (3)
Number |
Date |
Country |
2037514 |
Feb 1972 |
DEX |
2263676 |
Jul 1973 |
DEX |
1007977 |
Oct 1965 |
GBX |
Non-Patent Literature Citations (1)
Entry |
The Merck Index, Ninth Edition, Merck and Co. Inc., Rahway, N.J., pp. 1351 and 1352. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
870237 |
Jan 1978 |
|