Patent Application
20120277401
The present invention relates to a method for preparing heat-resistance polyimide resin. In particular, the present invention provides a method for preparing polyimide resin having enhanced heat-resistance and superior mechanical properties, especially high elongation at high temperature as compared to conventional polyimide resin. The polyimide resin prepared according to the method of the present invention can be used as a core heat-resistant material of semiconductor and aerospace fields where high heat-resistance is required.
Generally, the term “polyimide resin” refers to high heat-resistant resin which is prepared by reacting aromatic tetra carboxylic acid or a derivative thereof with aromatic diamine or aromatic diisocyanate, followed by imidization. The polyimide resin can have various types of a molecular structure depending on the kind of a monomer used. Representative aromatic tetracarboxylic acid derivatives may include pyromelitic dianhydride (PMDA) and 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA), and representative aromatic diamines may include oxydianiline (ODA) and para-phenylenediamine (p-PDA). The most representative polyimide resin has a structure represented by Formula 1 as a repeating unit.
The polyimide resin including the repeating unit of Formula 1 is ultra-high heat-resistant resin which is non-soluble/non-melting, has excellent heat resistance whose operating temperature for long term is 260° C. and operating temperature for short term is 480° C., and shows high electrochemical/mechanical properties, radiation resistance and low temperature properties, and chemical resistance. Therefore, the polyimide resin has been widely used as a core material in the various high-tech industries including electrics/electronics, automotives, semiconductor and aerospace industries.
However, in spite of its good heat-resistance and mechanical properties, its application is partially restricted to a certain temperature range, and especially, there is a problem in that cracks are generated on the surface when exposed to a high temperature for a long time. Therefore, there have been several attempts to improve heat-resistance of polyimide while maintaining its mechanical properties. For example, U.S. Pat. No. 5,162,492 discloses a method for preparing polyimide by reacting 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and meta-phenylenediamine (m-PDA) in an aprotic organic solvent such as dimethyl acetamide, N-methylpyrrolidinone and pyridine. When an imidization reaction is carried out in a liquid phase under the presence of an aprotic organic solvent according to conventional techniques, its heat-resistance can be improved, but there is a problem of lowering mechanical properties including tensile strength and elongation rate at high temperature due to extremely high crystallinity. Thus, in order to overcome such drawbacks, it has been suggested a method for preparing polyimide resin with good heat-resistance and mechanical properties by isolating polyamic acid and performing imidization in a solid phase.
The imidization method in a solid phase has several problems in that it is very difficult to regulate operation conditions for separating, transferring and drying due to high viscosity of polyamic acid, leading to the increase in unit production cost. In order to prevent the decrease in mechanical properties, especially tensile strength and elongation rate, U.S. Pat. No. 5,886,129 discloses a two-step polymerization method for preparing polyimide resin having improved heat-resistance and mechanical properties by polymerizing two kinds of aromatic diamins such as meta-phenylenediamine (m-PDA) and para-phenylenediamine (p-PDA) at a specific mixed ratio in an aprotic organic solvent such as 3,3′4,4′-biphenyltetracarboxylic dianhydride (BPDA), dimethyl acetamide, N-methylpyrrolidinone and pyridine to prepare a corresponding polyamic acid, transferring the thus prepared polyamic acid to a secondary reactor, and then performing imidization.
However, such a method for preparing polyimide resin under the presence of an aprotic organic solvent suffers from the problem in that it is difficult to regulate reaction conditions due to high viscosity of polyamic acid generated during the intermediate reaction, and the selection of monomers and combination thereof is subject to restriction. Further, water that may be included in a solvent used in the polymerization of polyimide or generated during the reaction is an obstacle to increase a molecular weight of polyimide. Since the aprotic organic solvents mentioned above are miscible with water, it is required to regulate a water content of a solvent used in the reaction to 100 ppm or lower or to use a separate method and apparatus for removing water generated during the reaction.
The present inventors have therefore endeavored to overcome the problems of the prior art described above, and found a monomer composition effective to prepare polyimide resin having improved heat-resistance and optimal mechanical properties and develop a new method for preparing the same which is easier and economical than conventional techniques.
Therefore, it is an object of the present invention to provide a method for preparing polyimide resin having higher heat-resistance and mechanical properties, especially having higher elongation rate at high temperature than conventional polyimide resin, which can be effectively used as a core heat-resistant material of semiconductor and aerospace fields where high heat-resistance is required.
It is another object of the present invention to provide a method for preparing a polyimide molded article using the polyimide resin prepared according to the above method.
In accordance with an aspect thereof, the present invention provides polyimide resin through direct polymerization in the presence of a polar organic solvent using two kinds of aromatic tetracarboxylic dianhydrides and aromatic diamine at a specific ratio, wherein the aromatic tetracarboxylic dianhydrides are 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and pyromelitic dianhydride (PMDA) and whose mixed ratio is properly regulated. According to the method of the present invention, it is possible to prepare polyimide resin having improved heat-resistance and high tensile properties, especially high elongation rate at high temperature as compared to conventional polyimide.
The polyimide resin with high heat-resistance prepared through imidization in a liquid phase according to the present invention has a structure represented by following Formula 2.
In Formula 2, R is to prepare using two kinds of tetracarboxylic dianhydrides whose mixed ratio is properly regulated, and R′ is to prepare using one or more than two aromatic diamine derivatives.
Further, the present invention provides a method for preparing a polyimide molded article by compression molding the polyamide resin prepared according to the above method at a pressure of 50,000 to 100,000 psi and sintering it.
According to the present invention, it is possible to prepare polyimide resin and a molded article with improved heat-resistance as compared to conventional polyimides through an easy and economic method. Further, the polyimide of the present invention overcomes the drawback of conventional polyimides whose elongation rate is decreased at high temperature of 260° C. or higher, leading to the lowering of durability.
Therefore, the polyimide of the present invention exhibits superior heat-resistance, ware-resistance and mechanical properties to the conventional polyimide materials, and thus can be effectively used as a core heat-resistant material of the high-tech industry including electric/electronics, semiconductor, flat panel display, automotive and aerospace fields.
Hereinafter, the present invention will be described in more detail.
In order to prepare a wholly aromatic polyimide resin with improved heat-resistance as compared to conventional polyimide resins, aromatic tetracarboxylic dianhydride and diamine have to exhibit aromaticity and not contain any functional group such as —O—, —S— or —CO— that is structurally fragile.
Further, for maintaining high mechanical properties through imidization in a liquid phase, the thus prepared polyimide must have a linear molecular structure.
Therefore, the present invention employs two kinds of aromatic tetracarboxylic dianhydride, in which the mixed ratio of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and pyromelitic dianhydride (PMDA) is regulated, and employs para-phenylenediamine (p-PDA) and meta-phenylenediamine (m-PDA) as an aromatic diamine at a specific ratio. Since the present invention employs one step direct polymerization in the presence of a phenolic polar organic solvent having a high boiling point, it is possible to prepare polyamide resin with improved heat-resistance as compared to conventional polyimides, and high tensile properties and elongation rate at high temperature.
The polyimide resin with high heat-resistance prepared by liquid phase imidization according to the present invention has a structure represented by the following Formula 3.
In Formula 3, R is to prepare using two kinds of tetracarboxylic dianhydrides whose mixed ratio is properly regulated. The mixed ratio is 40˜80 mole % of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and 20˜60 mole % of pyromelitic dianhydride (PMDA). Preferably, the mixed ratio is 65˜75 mole % of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and 25˜35 mole % of pyromelitic dianhydride (PMDA).
R′ is to prepare using one or more than two aromatic diamine derivatives. Preferably, R′ is prepared using 15˜60 mole % of para-phenylenediamine (p-PDA) and 40˜85 mole % of meta-phenylenediamine (m-PDA), and more preferably 50˜60 mole % of para-phenylenediamine (p-PDA) and 40˜50 mole % of meta-phenylenediamine (m-PDA).
The polyimide resin described above can be prepared according to the following method.
Para-phenylenediamine (p-PDA) and meta-phenylenediamine (m-PDA) as aromatic diamines are dissolved in a phenolic polar organic solvent having a high boiling point at a desired mole %. Here, it is preferable that after 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) and pyromelitic dianhydride (PMDA) are uniformly mixed at a desired mole %, the resulting mixture was divided into three equal parts, and then, each of solid parts is added to the solvent solution while heating to a temperature of 80˜120° C. for 1˜2 hours.
After that, the resulting reaction solution is stirred at a temperature of 80˜120° C. for 2 hours and heated to a temperature of 160˜200° C. over 1˜2 hours, followed by keeping it to that temperature for 2 hours. Since the phenolic polar organic solvent used in the above reaction is immiscible with water, water generated during the reaction is evaporated, condensed in a condenser and subjected to layer separation. Therefore, water can be easily removed, and thus it is possible to obtain polyimide resin with a high molecular weight. After the thus generated polyimide slurry solution is cooled down to a temperature of 60˜80° C., 30˜60 volume % of methylalcohol based on 100 volume % of the phenolic polar organic solvent used is added thereto to dilute it. The diluted polyimide slurry is washed with an organic solution with a low boiling point such as acetone or methylalcohol and dried at a temperature of 100˜250° C. and 10−1 Torr or lower of vacuum and under nitrogen atmosphere for 18 fours. Here, it is preferable to dry at a temperature of 160˜220° C., and more preferably at a temperature of 190˜200° C.
The resulting polyimide resin generated above has a proper crystallinity of 5˜20% or lower and a high specific surface area, and thereby, it can be effectively subjected to compression molding.
The phenolic polar organic solvent having a high boiling point used in the above reaction may include meta-cresol or a mixed cresol in which ortho-, meta- and para-isomers are nonuniformly mixed. Further, the concentration of a solid is preferably in the range of 6˜16 wt %, and more preferably in the range of 8˜12 wt %.
The thus prepared polyimide resin powder according to the present invention has an inherent viscosity of 0.7˜2.5 dl/g, a crystallinity of 5˜10%, a specific surface area of 50˜200 m2/g, and an imidization degree of 98˜99%.
The polyimide resin of the present invention can be prepared into a polyimide molded article having high heat-resistance and excellent mechanical strength through compression molding at room temperature and high temperature under the pressure of 50,000˜100,000 psi (345˜690 Mpa), and then sintered at a temperature of 350˜400° C. and under nitrogen atmosphere for 2˜3 hours, or through compression molding to which high temperature and high pressure are simultaneously applied.
The polyimide molded article prepared using the polyimide resin of the present invention shows improved heat-resistance as compared to conventional polyimide. In addition, under the same condition, while the conventional polyimide exhibits a weight loss of 5.0 wt % or more, the polyimide of the present invention exhibits a weight loss of 2.0˜1.5 wt % or lower, which suggests that the polyimide of the present invention show significantly improved heat-resistance.
Further, the conventional polyimide shows elongation rate properties in which an elongation rate measured at high temperature of 260° C. is lower than that measured at room temperature, which results in the generation of cracks while using it at high temperature or in the remarkable decrease in mechanical strength. Due to these properties, the use of the conventional polyimide is extremely restricted to the fields of semiconductor and aerospace fields where high heat-resistance is required. However, when tensile properties are measured at high temperature, the polyimide prepared according to the present invention shows rather higher elongation rate than the conventional polyimide whose elongation rate is decreased. Therefore, the polyimide having high heat-resistance according to the present invention can be effectively used as a core heat-resistant material of semiconductor and aerospace fields.
The present invention is further illustrated by the following examples. However, it shall be understood that these examples are only used to specifically set forth the present invention, rather than being understood that they are used to limit the present invention in any form.
A 2-L reactor equipped with a stirrer, a temperature regulator and a nitrogen injector was added with 37.85 g of meta-phenylenediamine (m-PDA), and the resulting mixture was dissolved in mixed cresol, and then passed through nitrogen gas at room temperature.
While increasing the temperature of the mixture up to 110° C. lasting 2 hours, 72.08 g of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA, 70 mole %) and 22.90 g of pyromelitic dianhydride (PMDA, 30 mole %) were added thereto in a solid phase. Here, the addition was carried out three times with the equal amount each time, and the concentration of the solid was fixed to 8 wt %. After allowing the mixture to react at 110° C. for 2 hours, the temperature of the reaction solution was increased up to 175° C. lasting 2 hours and stirred for 2 hours to induce imidization. Upon completion of the reaction, the reaction solution was cooled down to 40° C., and methylalcohol was added thereto at an amount of 40 volume % as compared with 100 volume % of cresol used in the reaction. The resulting mixture was further stirred for 30 minutes and dried under vacuum (10−1 Torr) and nitrogen atmosphere for 16 hours.
Inherent viscosity of the thus prepared polyimide resin was measured at a concentration of 0.5 g/dl using concentrated sulfuric acid as a solvent at 30° C.. As a result, the polyimide resin had an inherent viscosity of 1.20 dl/g, and its imidization degree was 99%.
The polyimide resin was subjected to compression molding at a pressure of 100,000 psi, and then sintered at 400° C. for 3 hours under nitrogen atmosphere.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The polyimide resin was prepared using 37.85 g of m-PDA, 61.79 g of BPDA (60 mole %) and 30.54 g of PMDA (40 mole %) according to the same method as described in Example 1. The thus prepared polyimide resin had an inherent viscosity of 1.02 dl/g and an imidization degree of 99%.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The polyimide resin was prepared using 37.85 g of m-PDA, 51.49 g of BPDA (50 mole %) and 38.17 g of PMDA (50 mole %) according to the same method as described in Example 1. The thus prepared polyimide resin had an inherent viscosity of 0.96 dl/g and an imidization degree of 99%.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The polyimide resin was prepared using 37.85 g of m-PDA, 30.89 g of BPDA (30 mole %) and 53.44 g of PMDA (70 mole %) according to the same method as described in Example 1. The thus prepared polyimide resin had an inherent viscosity of 0.92 dl/g and an imidization degree of 99%.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The polyimide resin was prepared using 15.14 g of m-PDA (40 mole %), 22.17 g of p-PDA (60 mole %), 72.08 g of BPDA (70 mole %) and 22.90 g of PMDA (30 mole %) according to the same method as described in Example 1. The thus prepared polyimide resin had an inherent viscosity of 0.92 dl/g and an imidization degree of 99%.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The polyimide resin was prepared using 26.49 g of m-PDA (70 mole %), 11.35 g of p-PDA (30 mole %), 72.08 g of BPDA (70 mole %) and 22.90 g of PMDA (30 mole %) according to the same method as described in Example 1. The thus prepared polyimide resin had an inherent viscosity of 0.92 dl/g and an imidization degree of 99%.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
A 2-L reactor equipped with a stirrer, a temperature regulator and a nitrogen injector was added 36.11 g of 4,4-oxydianiline (ODA) and dissolved in mixed cresol, the resulting mixture was passed through nitrogen gas at room temperature.
While increasing the temperature of the mixture up to 60˜80 ° C. lasting 1˜2 hours, 39.45 g of pyromelitic dianhydride (PMDA) was added thereto in a solid phase. Here, the addition was carried out three times with the equal amount each time, and the concentration of the solid was fixed to 12 wt %. After the mixture was reacted for 1˜2 hours, the temperature of the reaction solution was gradually increased up to 165° C. and stirred for 1˜2 hours to induce imidization. Upon completion of the reaction, the reaction solution was cooled down to 80° C., filtered and washed with methylalcohol.
The thus prepared polyimide resin was dried at 190° C. under vacuum, nitrogen atmosphere for 16 hours.
Inherent viscosity of the thus prepared polyimide resin was measured at a concentration of 0.5 g/dl using concentrated sulfuric acid as a solvent at 30° C.. As a result, the polyimide resin had an inherent viscosity of 0.98 dl/g, and its imidization degree was 99%.
The polyimide resin was subjected to compression molding at a pressure of 100,000 psi, and then sintered at 400° C. for 3 hours under nitrogen atmosphere.
Tensile strength, elongation rate and heat-resistance of the thus prepared polyimide molded article were measured according to the following method for assessing performance, and the results are shown in Table 1.
The tensile strength and elongation rate of the polyimide molded articles prepared above were measured according to ASTM D 1708 Standard Test.
The polyimide molded article was kept at 400° C. for 25 hours at a pressure of 0.61 Mpa, and then weight loss was measured.
% Weight loss=(initial weigh−weight after exposure)/initial weight×100
As shown in Table 1, since the polyimide molded articles of the present invention were prepared using PMDA and BPDA in a properly mixed form, and preferably along with using m-PDA and p-PDA, they showed higher heat-resistance than those prepared according to conventional methods using PMDA or ODA alone, and had superior mechanical properties including tensile strength and elongation rate, especially at high temperature (260° C.).
Therefore, the polyimide molded articles prepared according to the present invention can be used as a core heat-resistant material of semiconductor and aerospace fields where high heat-resistance, tensile strength and elongation rate at high temperature are required.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2009-0134767 | Dec 2009 | KR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/KR10/08741 | 12/8/2010 | WO | 00 | 6/29/2012 |