The present invention relates to arts of a method for manufacturing a glass film laminate, a glass film laminate, and a method for manufacturing an electronic device.
From a point of view of space-saving, instead of a CRT type display which had spread conventionally, a flat panel display such as a liquid crystal display, a plasma display, and an organic EL display spreads in recent.
There is a need of making the flat panel display thinner.
In recent, concerning a substrate and cover glass used for devices such as the flat panel display, a need of realizing further thinning and high flexibility is increased.
For providing flexibility to a glass substrate, thinning of the glass substrate is effective, and the Patent Literature 1 proposes a glass film whose thickness is not more than 200 μm.
Manufacturing relevant processes such as a machining process and a washing process is performed concerning the glass substrate used for an electronic device such as the flat panel display and a solar cell.
However, when the glass substrate used for the electronic device is thinned, since grass is a brittle material, some change of stress causes damage, whereby there is a problem in that treatment is very difficult at the time of performing the manufacturing relevant processes of the electronic device.
In addition, since the glass film whose thickness is not more than 200 μm has high flexibility, positioning at the time of performing the process is difficult and there is a problem in that a gap or the like occurs at the time of patterning.
For improving handling of the thinned glass film, the Patent Literature 1 proposes a glass film laminate in which the glass film is laminated on support glass.
According to the glass film laminate, even when the glass film which lacks intensity and rigidity alone is used, since rigidity of the support glass is high, positioning of the whole glass film laminate at the time of performing the process is easy.
After finishing the process, the glass film can be exfoliated from the support glass.
When a thickness of the glass film laminate is the same as a thickness of the conventional glass substrate, an electronic device can be manufactured with an electronic device manufacturing line for the conventional glass substrate.
Patent Literature 1: the Japanese Patent Laid Open Gazette 2011-183792
In the case of manufacturing the electronic device such as a liquid crystal panel with the glass film laminate shown in the Patent Literature 1, generally, a step in which resist liquid is applied to the glass film laminate (resist step) is provided. The resist liquid applied to the glass film laminate in the resist step is solidified by a method such as photosensitizing, heating or drying.
In the conventional glass film laminate 1 shown in the Patent Literature 1, as shown in FIG. 16, bubbles 14 may be formed in an interface 13 of the glass film 10 and a support glass 12 which is the support body 11. The bubbles 14 include a bubble communicated with atmosphere at an outer peripheral edge of the glass film 10. Hereinafter, such the bubble 14 is referred to as an open bubble 14a.
In the glass film laminate 1 in which the open bubble 14a exists in the interface 13, there is a problem in that the resist liquid applied in the resist step enters the open bubble 14a.
Since the resist liquid entering the open bubble 14a is then solidified, there is a problem in that the glass film 10 and the support glass 12 in a part in which the open bubble 14a exists are made adhere each other by the solidified resist liquid.
Furthermore, in the glass film laminate 1 adhered by the resist liquid, at the time of separating the support glass 12 and the glass film 10, there is a problem in that the adhered part is hard to be exfoliated so as to cause damage of the glass film 10, whereby a yield of the glass film 10 is worsened and a non-defective rate of the glass film 10 obtained from the glass film laminate 1 is worsened.
Accordingly, it is desired that occurrence of damage at the time of exfoliating the glass film is suppressed by preventing the adhesion of the support glass and the glass film by the resist liquid so as to improve the yield and the non-defective rate of the glass film.
The present invention is provided in consideration of the conditions as mentioned above, and the purpose of the invention is to provide a glass film laminate a method for manufacturing the glass film laminate in which generation of an open bubble in a laminating interface of the glass film laminate is prevented while improving handling of a glass film so as to improve a yield and a non-defective rate of the glass film.
The problems to be solved by the present invention have been described above, and subsequently, the means of solving the problems will be described below.
The first invention of the application is a method for manufacturing a glass film laminate produced by laminating a glass film on a support body including an ultrasonic wave application step in which an ultrasonic wave is applied to at least peripheral parts of the glass film and the support body, a washing step in which the glass film and the support body passing through the ultrasonic wave application step are washed, and a laminating step in which the glass film and the support body passing through the washing step are laminated so as to produce the glass film laminate.
According to the second invention of the application, the support body is support glass.
According to the third invention of the application, in the ultrasonic wave application step, the ultrasonic wave is applied by a horn-type ultrasonic wave generator.
According to the fourth invention of the application, in the ultrasonic wave application step, the ultrasonic wave is applied to only the peripheral parts of the glass film and the support glass.
According to the fifth invention of the application, in an ultrasonic wave washing step, the glass film and the support body are dipped in liquid in an ultrasonic wave washing tub and the whole of the glass film and the support glass are ultrasonic-washed by the ultrasonic wave washing tub.
The sixth invention of the application further includes an open bubble inspection step inspecting existence of an open bubble which is a bubble existing in an interface of the glass film and the support body and contacting an edge side of the glass film.
According to the seventh invention of the application, in the open bubble inspection step, existence of a bubble except for the open bubble in a peripheral part of the glass film laminate corresponding to the peripheral part of the glass film is inspected further.
According to the eighth invention of the application, the peripheral part of the glass film laminate is within a width of not less than 10 mm from the edge side of the glass film.
According to the ninth invention of the application, a number of bubbles in the glass film laminate except for the peripheral part is not less than 0.1/m2 and not more than 10000/m2.
The tenth invention of the application is a glass film laminate produced by laminating directly a glass film and support glass, wherein all the edge sides of the glass film contact tightly the support glass.
According to the eleventh invention of the application, the glass film contacts tightly the support glass with a width not less than 10 mm from all the edge sides of the glass film.
According to the twelfth invention of the application, a number of bubbles in a part of the glass film laminate except for the part in which the glass film contacts tightly the support glass is not less than 0.1/m2 and not more than 10000/m2.
According to the thirteenth invention of the application, a thin film layer is provided in the support glass.
The fourteenth invention of the application is a method for manufacturing an electronic device including a laminating step in which a glass film is laminated on a support body so as to produce the glass film laminate before a manufacturing relevant process of the electronic device, a step in which the manufacturing relevant process of the electronic device is performed to the glass film of the glass film laminate so as to form an element on the glass film of the glass film laminate and the element is closed by a closing substrate, thereby producing the electronic device with the support body, and a step in which the glass film of the electronic device with the support body after the manufacturing relevant process of the electronic device is exfoliated from the support body so as to manufacture the electronic device. In the laminating step, the glass film laminate is produced by the method for manufacturing the glass film laminate according to one of claims 1 to 8.
The present invention brings the following effects.
According to the first invention of the application, generation of the open bubble in the peripheral part of the glass film laminate can be prevented.
Accordingly, penetration of the resist liquid to the interface of the glass film and the support body in the resist step can be prevented, and as a result, adhesion of the glass film and the support body can be prevented, thereby preventing damage of the glass film at the time of exfoliation.
According to the second invention of the application, at the time of using the support grass as the support body, generation of the open bubble in the peripheral part of the glass film laminate can be prevented.
According to the third invention of the application, foreign matters causing the normal open bubble can be removed certainly from the peripheral part of the glass film and the support body.
According to the fourth invention of the application, time required for removing the foreign matters causing the normal open bubble can be shortened.
According to the fifth invention of the application, the foreign matters causing the open bubble can be removed certainly from the peripheral parts of the glass film and the support body.
By removing foreign matters in parts of the glass film and the support body except for the peripheral parts, a non-defective rate of the glass film can be improved.
According to the sixth invention of the application, the glass film laminate in which the open bubble exists can be eliminated.
Accordingly, a yield of the glass film after a manufacturing relevant process can be improved.
According to the seventh invention of the application, generation of the open bubble after inspecting existence of the open bubble can be prevented.
Accordingly, the yield of the glass film after a manufacturing relevant process can be improved certainly.
According to the eighth invention of the application, generation of the open bubble in the peripheral part of the glass film laminate can be prevented certainly.
According to the ninth invention of the application, generation of the close bubble at an inner side from the peripheral part of the glass film laminate can be prevented certainly while suppressing time and cost.
According to the tenth invention of the application, penetration of the resist liquid to the interface of the glass film and the support body in the resist step can be prevented, and as a result, adhesion of the glass film and the support body can be prevented, thereby preventing damage of the glass film at the time of exfoliation.
According to the eleventh invention of the application, the yield of the glass film can be improved.
According to the twelfth invention of the application, generation of the close bubble at an inner side from the peripheral part of the glass film laminate can be prevented certainly while suppressing time and cost.
According to the thirteenth invention of the application, the glass film can be exfoliated easily, whereby the yield of the glass film can be improved.
According to the fourteenth invention of the application, a yield of the electronic device can be improved.
A suitable embodiment of a glass film laminate according to the present invention is explained referring to drawings.
Firstly, a method for manufacturing a glass film laminate 1 according to the present invention is explained.
In the method for manufacturing the glass film laminate 1 according to the present invention, as shown in
Silicate glass and silica glass, preferably borosilicate, the most preferably non-alkali glass are used for the glass film 10.
When the glass film 10 includes alkali components, positive ions fall off from a surface of the film and so-called sodium blowing phenomenon occurs, whereby the structure becomes rough. In this case, when the glass film 10 is used while being bent, the part which becomes rough by deterioration with time may be broken.
Herein, the non-alkali glass is glass which does not include alkali components (alkali metal oxides) substantially, and is concretely glass whose alkali components are not more than 3000 ppm.
A content of the alkali components of the non-alkali glass used for the present invention is preferably not more than 1000 ppm, more preferably not more than 500 ppm, further more preferably not more than 300 ppm.
A thickness of the glass film 10 is preferably not more than 300 μm, more preferably 5 to 200 μm, and the most preferably 5 to 100 μm.
Accordingly, the glass film 10 can be made thinner so as to obtain suitably flexibility.
The thinner glass film 10 is difficult to be handled and problems such as miss of positioning and bending at the time of patterning tend to occur. However, by using the support body 11 discussed later, manufacturing relevant processes such as patterning can be performed easily.
When the thickness of the glass film 10 is less than 5 μm, strength of the glass film 10 is needy and the glass film 10 may be hard to be exfoliated from the support body 11.
A material of the support body 11 is not limited if it can support the glass film 10, and a platy body such as a synthetic resin plate, a natural resin plate, a wood plate, a metal plate, a grass plate, a ceramic plate, a crystallized glass plate and the like can be used. A thickness of the support body 11 is not limited and may be selected suitably corresponding to rigidity of a material selected as the support body. For improving the handling of the glass film 10, a resin film such as a PET film may be used. The support body 11 may be configured by providing suitably a resin layer discussed later on a surface of the platy body so as to control property of adhering to and exfoliating from the glass film 10.
Preferably, a support glass 12 is used for the support body 11. Accordingly, characteristics and shapes of the glass film 10 and the support glass 12 are stable concerning heat treatment, chemical liquid treatment, exposure treatment and the like in the manufacturing relevant processes of an electronic device, whereby stable laminated state of the glass film laminate 1 can be maintained.
Similarly to the glass film 10, silicate glass and silica glass, borosilicate or non-alkali glass is used for the support glass 12.
As the support glass 12, preferably, glass that a difference of thermal expansion coefficients with the glass film 10 at 30 to 380° C. is within 5×10−7/° C. is used.
For suppressing the difference thermal expansion rates, the most preferably, glass of the same composition is used for both the glass film 10 and the support glass 12.
A thickness of the support glass 12 is preferably not less than 400 μm. When the thickness of the support glass 12 is less than 400 μm, problems may be caused by strength when the support glass 12 is dealt with alone. The thickness of the support glass 12 is preferably 400 to 700 μm, and the most preferably 500 to 700 μm.
Accordingly, the glass film 10 can be supported certainly by the support glass 12, and breakage of the glass film 10 occurring at the time of exfoliating the glass film 10 from the support glass 12 can be suppressed efficiently.
At the time of applying resist liquid discussed later (third step), when the glass film laminate 1 is mounted on a setter (not shown), the thickness of the support glass 12 may be less than 400 μm (the same thickness as the glass film 10, for example 300 μm).
The glass film 10 and the support glass 12 used for the present invention are made preferably by a down draw method, and more preferably by an overflow down draw method.
Especially, the overflow down draw method shown in
In the overflow down draw method shown in
An embodiment in which the support glass 12 is adopted as the support body 11 is explained. In the parts except for characteristic explanations resulting from a material of the support glass 12, the support glass 12 can be suitably read as the support body 11.
As shown in
The contact surface 10a faces and contacts the support glass 12 at the time of being laminated with the support glass 12.
The effective surface 10b is opposite to the contact surface 10a and the manufacturing relevant processes such as forming of elements are performed therein.
A contact surface 12a and a conveyance surface 12b are set in the support glass 12.
The contact surface 12a faces and contacts the glass film 10 at the time of being laminated with the glass film 10.
The conveyance surface 12b is opposite to the contact surface 12a and contacts conveyance rollers when the glass film laminate 1 is conveyed on the conveyance rollers.
Though the glass film 10 having substantially the same area as the support glass 12 is laminated on the support glass 12 in
In this case, an overflow amount of the support glass 12 from the glass film 10 is preferably 0.5 to 10 mm, and more preferably 0.5 to 1 mm.
By making the overflow amount of the support glass 12 small, an area of the effective surface 10b of the glass film 10 can be secured more widely.
The step laminating the glass film 10 on the support glass 12 may be performed under decompression. Accordingly, bubbles generated between the glass film 10 and the support glass 12 when the glass film 10 and the support glass 12 are laminated can be reduced.
A surface roughness Ra of each of the contact surface 10a of the glass film 10 and the contact surface 12a of the support glass 12 is preferably not more than 2.0 nm. Accordingly, the glass film contacts the support glass with smooth surfaces so as to improve the adhesion, whereby the glass film and the support glass can be laminated firmly stably without any bonding agent.
For laminating firmly stably the glass film 10 and the support glass 12 without any bonding agent, the surface roughness Ra of each of the contact surfaces 10a and 12a of the glass film 10 and the support glass 12 used in the present invention is preferably not more than 1.0 nm, more preferably not more than 0.5 nm, and the most preferably not more than 0.2 nm.
In this embodiment, the surface roughness Ra of each of the surfaces of the glass film 10 and the support glass 12 contacting each other is not more than 2.0 nm, and in the first step, the glass film 10 and the support glass 12 each of whose surfaces contacting each other is not more than 2.0 nm are laminated and the glass film 10 is fixed firmly to the support glass 12, whereby the glass film laminate 1 is produced.
By smoothing the contact surfaces 10a and 12a of the glass film 10 and the support glass 12 so as to make the surface roughness Ra thereof not more than 2.0 nm, when the two smooth glass plates contact tightly each other, the glass plates are made adhere detachably without any bonding agent, whereby the glass film laminate 1 is configured. It is guessed that this phenomenon is based on following mechanism.
As shown in
Though the glass film 10 is laminated directly on the support glass 12 in this embodiment, it may be configured that a thin film layer 15 is formed on the support glass 12 and then the glass film 10 is laminated as shown in
On the other hand, a surface roughness of the effective surface 10b of the glass film 10 is not limited especially. However, since a forming step of elements and the like are performed in a third step discussed later, the surface roughness Ra of the effective surface 10b is preferably not more than 2.0 nm, more preferably not more than 1.0 nm, further more preferably not more than 0.5 nm, and the most preferably not more than 0.2 nm. A surface roughness of the conveyance surface 12b of the support glass 12 is not limited especially.
As shown in
The ultrasonic wave application step (STEP-1-1) and the washing step (STEP-1-2) prevent generation of an open bubble in the interface 13 of the glass film laminate 1.
As shown in
Namely, by removing certainly the foreign matters on the contact surface 10a of the glass film 10 and the contact surface 12a of the support glass 12, generation of the bubbles 14 in the interface 13 can be prevented.
As shown in
Among the bubbles 14 existing in the interface 13 of the glass film 10 and the support glass 12, the open bubble 14a contacts the edge side 10c of the glass film 10 and is communicated with the outside. The close bubble 14b does not contact the edge side 10c of the glass film 10 and is not communicated with the outside.
In the method for manufacturing the glass film laminate 1 according to the present invention, as shown in
As shown in
As shown in
The peripheral part 10d of the glass film 10 does not need to be completely in agreement with the peripheral part 12d of the support glass 12. The peripheral part 10d of the glass film 10 may overflow the peripheral part 12d of the support glass 12, and on the contrary, the peripheral part 12d of the support glass 12 may overflow the peripheral part 10d of the glass film 10.
There is an especially high possibility that the foreign matters existing in the peripheral part 1d become a factor of the open bubble 14a. There is a high possibility that the close bubble 14b owing to the foreign matters existing in the peripheral parts 10d and 12d changes to the open bubble 14a by shifting its position by stress from the outside or change with time.
Namely, for preventing the open bubble 14a certainly, forming of the close bubble 14b in the peripheral part 1d must be prevented.
Accordingly, in the method for manufacturing the glass film laminate 1 according to the present invention, the foreign matters in the peripheral parts 10d and 12d are certainly removed by the ultrasonic wave application step (STEP-1-1) and the washing step (STEP-1-2), whereby no foreign matter exists in the peripheral part 1d. The glass film laminate 1 according to the present invention is produced so that the open bubble 14a does not exist in the peripheral part 1d, and as shown in
A number of the close bubbles 14b except for the peripheral part 10d is preferably small.
Concretely, the number of the close bubbles 14b whose diameter converted to a circle is not less than 5 mm is preferably not more than 10000/m2, more preferably not more than 1000/m2, further more preferably not more than 100/m2, and the most preferably not more than 10/m2.
That is because since smoothness is required at the time of performing the manufacturing relevant processes of the element (electronic device), the number of the close bubble 14b except for the peripheral part 10d is preferably small.
The number of the close bubbles 14b except for the peripheral part 10d is preferably not less than 0.1/m2.
That is because time for washing and the like is required for lessening the number of the close bubbles 14b except for the peripheral part 10d as much as possible and cost for producing the glass film laminate may be increased. The number of the close bubbles 14b except for the peripheral part 10d is preferably not less than 0.5/m2, more preferably not less than 1/m2, further more preferably not less than 2/m2.
The predetermined width N of the peripheral part 1d of the glass film laminate 1 according to this embodiment is 10 mm, and the predetermined width N of the glass film laminate according to the present invention is preferably not less than 10 mm.
That is because there is an especially high possibility that the bubble 14 generated at a position whose distance from the edge side 10c of the glass film 10 is less than 10 mm becomes the open bubble 14a, and there is a possibility that the close bubble 14b generated in this range changes to the open bubble 14a by shifting its position by stress from the outside or change with time.
Furthermore, that is because the foreign matters existing 10 mm or more inner side from the edge side 10c is hardly become the factor of the open bubble 14a.
The range to which the ultrasonic wave US is applied in the ultrasonic wave application step (STEP-1-1) may include a part at an inner side from the peripheral parts 10d and 12d (the range of the predetermined widths L and M shown in
That is because by removing the foreign matters existing at the inner side from the peripheral parts 10d and 12d, a non-defective rate of the glass film 10 can be improved.
As shown in
In comparison with a tub-type ultrasonic wave generator, the horn-type ultrasonic wave generator 30 can apply partially the stronger ultrasonic wave US, thereby being suitable for removing foreign matters adhering the surfaces of the glass film 10 and the support glass 12. Especially, by using the horn-type ultrasonic wave generator 30, grass powder adhering to the surfaces which cannot be removed by normal scrubbing can be removed.
Since an operator can select and scan a position to which the ultrasonic wave US is applied simultaneously by the horn-type ultrasonic wave generator 30, a part of the glass film 10 and the support glass 12 in which the foreign matters become the factor of the open bubble 14a (that is, the range of the predetermined widths L and M) can be selected preferentially and the ultrasonic wave US can be applied thereto.
According to the configuration in which the ultrasonic wave US is applied to only the range of the predetermined widths L and M by the horn-type ultrasonic wave generator 30, time required for a work applying the ultrasonic wave US can be shortened, whereby generation of the open bubble 14a can be prevented efficiently.
In the method for manufacturing the glass film laminate 1 according to the present invention, when the ultrasonic wave US is applied to the glass film 10 and the support glass 12 in the ultrasonic wave application step (STEP-1-1), the glass film 10 and the support glass 12 are arranged in a tub 32 filled with liquid 31 and the ultrasonic wave US is applied to the glass film 10 and the support glass 12 while being dipped in the liquid 31.
In this embodiment, pure water is used as the liquid 31 in which the glass film 10 and the support glass 12 are dipped. Liquid except for the pure water such as ethanol may be used as the liquid 31 in which the glass film 10 and the support glass 12 are dipped.
In the method for manufacturing the glass film laminate 1 according to the present invention, it may be configured that an ultrasonic wave washing tub is used as the tub 32 and an ultrasonic wave washing process is provided further. Namely, the ultrasonic wave may be applied to the whole of the glass film 10 and the support glass 12 by the tub (ultrasonic wave washing tub) 32 before, after or midst applying the ultrasonic wave US to the glass film 10 and the support glass 12 by the horn-type ultrasonic wave generator 30.
According to the configuration in which the ultrasonic wave is applied to the range of the predetermined widths L and M by the horn-type ultrasonic wave generator 30 while the ultrasonic wave is applied to the whole of the glass film 10 and the support glass 12, the foreign matters adhering the whole range of the whole of the glass film 10 and the support glass 12 can be removed in addition to preventing generation of the open bubble 14a in the peripheral part 1d, whereby the non-defective rate of the glass film 10 can be improved.
As shown in
In the open bubble inspection step (STEP-2), the glass film laminate 1 in which the open bubble 14a exists in the peripheral part 1d as shown in
As the open bubble inspection step (STEP-2), in addition to visual inspection, optical inspection using suitably an edge light, a microscope, a line camera or the like can be used.
Namely, the method for manufacturing the glass film laminate 1 according to the present invention includes further the open bubble inspection step (STEP-2) inspecting existence of the open bubble 14a contacting the edge side 10c of the glass film 10 among the bubbles 14 existing in the interface 13 of the glass film 10 and the support glass 12.
According to the configuration, the glass film laminate 1 in which the open bubble 14a can be eliminated, whereby a yield of the glass film 10 can be improved.
In the method for manufacturing the glass film laminate 1 according to the present invention, it may be configured that existence of not only the open bubble 14a in the peripheral part 1d but also the close bubble 14b in the peripheral part 1d is inspected in the open bubble inspection step (STEP-2).
The close bubble 14b does not contact the edge side 10c of the glass film 10 and has a possibility to move to a position contacting the edge side 10c by change with time or external force at the time of the inspection, and has a possibility to change to the open bubble 14a after the inspection.
Accordingly, in the method for manufacturing the glass film laminate 1 according to the present invention, in (STEP-2), the glass film laminate 1 in which the close bubble 14b exists in the peripheral part 1d as shown in
On the other hand, in the open bubble inspection step (STEP-2), the glass film laminate 1 in which the bubble 14 (the close bubble 14b) exists at an inner side from the peripheral part 1d as shown in
The glass film laminate 1 which is judged to be a defective product in the open bubble inspection step (STEP-2) is separated into the glass film 10 and the support glass 12 and returned to the first step so as to be reused.
In a third step shown in
At this time, if the open bubble 14a exists in the interface 13 of the glass film laminate 1 as shown in
The element 41 is closed by cover glass 43, and if the device is a liquid crystal panel, liquid crystal is injected (not shown), whereby the electronic device 40 with the support glass is formed.
Though the cover glass 43 and the glass film 10 are made adhere directly each other in the mode shown in
As a closing substrate closing the element 41, the cover glass 43 made by silicate glass and silica glass, borosilicate or non-alkali glass similarly to the glass film 10 is used.
As the cover glass 43, preferably, glass with a coefficient of linear thermal expansion whose difference with the glass film 10 at 30 to 380° C. is within 5×10−7/° C.
Accordingly, when temperature of a surrounding environment of a produced electronic device 50 is changed, warp by heat and breakage of the glass film 10 and the cover glass 43 caused by the difference of the coefficient of linear thermal expansion hardly occur, whereby the electronic device 50 is hard to be damaged.
For suppressing the difference of the coefficient of linear thermal expansion, the most preferably, glass of the same composition is used for both the cover glass 43 and the glass film 10.
A thickness of the cover glass 43 is preferably not more than 300 μm, more preferably 5 to 200 μm, and the most preferably 5 to 100 μm. Accordingly, the cover glass 43 can be made thinner so as to obtain suitably flexibility. When the thickness of the cover glass 43 is less than 5 strength of the cover glass 43 is needy.
Next, in a fourth step, in the electronic device 40 with the support glass, the glass film 10 is exfoliated from the support glass 12, whereby the electronic device 50 which is the glass film 10 in which the element 41 is formed is produced.
As shown in
When the electronic device 50 is exfoliated from the support glass 12, an edge of the glass film 10 is pulled so as to be separated from the support glass 12 while a wedge (not shown) is inserted into the interface 13 of the glass film 10 and the support glass 12, whereby the electronic device 50 (the glass film 10) is exfoliated.
Supposing, in the glass film laminate 1 in which the glass film 10 and the support glass 12 are made adhere each other as shown in
On the other hand, in the mode in which generation of the open bubble 14a at the peripheral part 1d is prevented as the glass film laminate 1 according to the present invention (see
As shown in
According to the configuration of suppressing damage of the glass film 10 as the method for manufacturing the glass film laminate 1 according to the present invention, a reuse rate of the support glass 12 can be improved, thereby reducing a cost of the glass film laminate 1.
As explained above, the method for manufacturing the glass film laminate 1 according to the present invention is the method for manufacturing the glass film laminate 1 which is produced by laminating the glass film 10 and the support glass 12, and includes the ultrasonic wave application step (STEP-1-1) in which the ultrasonic wave US is applied to at least the peripheral parts 10d and 12d of the glass film 10 and the support glass 12, the washing step (STEP-1-2) in which the glass film 10 and the support glass 12 passing through the ultrasonic wave application step (STEP-1-1) are washed, and the laminating step (STEP-1-3) in which the glass film 10 and the support glass 12 passing through the washing step (STEP-1-2) are laminated so as to produce the glass film laminate 1.
According to the configuration, generation of the open bubble 14a in the peripheral part 1d of the glass film laminate 1 can be prevented.
Accordingly, penetration of the resist liquid 42 to the interface 13 of the glass film 10 and the support glass 12 in the resist step (third step) can be prevented, and as a result, adhesion of the glass film 10 and the support glass 12 can be prevented, thereby preventing damage of the glass film 10 at the time of exfoliation.
Next, results of an experiment confirming effect the method for manufacturing the glass film laminate 1 according to the present invention are explained.
In this experiment, a thin plate glass made by Nippon Electric Glass Company, Limited (product name: OA-10G) is used. A plate glass of 350 mm×450 mm×0.2 mm is used as the glass film, and a plate glass of 360 mm×460 mm×0.5 mm is used as the support glass. Using the glass film and the support glass of the above specifications, the 100 glass film laminates are produced respectively concerning total four kinds including the glass film laminates 1 according to examples 1 to 3 and the glass film laminate 1 according to a comparative example 1 intermingled at an optional rate.
Washing of the contact surfaces 10a and 12a are performed by rubbing the glass film 10 and the support glass 12 with sponge made from urethane while applying washing liquid to which alkaline detergent is added.
The ultrasonic wave (frequency 25 kHz) is applied to only the peripheral parts 10d and 12d of the glass film 10 and the support glass 12 for 30 seconds by the horn-type ultrasonic wave generator (tip area 20×80 mm), and then the contact surfaces 10a and 12a are washed and subsequently laminated directly, whereby the glass film laminate 1 according to the example 1 is produced.
Quality judging of the glass film laminate 1 according to the example 1 is performed only by the number of the bubbles 14 in the interface 13.
In the inspection by the number of the bubbles 14 in the interface 13, the product in which the number of the bubbles 14 is not more than 100/m2 is judged to be a non-defective product (the same applies to the following).
The ultrasonic wave (frequency 25 kHz) is applied to contact surfaces 10a and 12a (whole surfaces) of the glass film 10 and the support glass 12 for 30 seconds by the horn-type ultrasonic wave generator (the same as the above), and then the contact surfaces 10a and 12a are washed and subsequently laminated directly, whereby the glass film laminate 1 according to the example 2 is produced.
Quality judging of the glass film laminate 1 according to the example 2 is performed only by the number of the bubbles 14 in the interface 13.
The ultrasonic wave (frequency 25 kHz) is applied to the contact surfaces 10a and 12a (whole surfaces) of the glass film 10 and the support glass 12 for 30 seconds by the horn-type ultrasonic wave generator (the same as the above), and then the contact surfaces 10a and 12a are washed and subsequently laminated directly, whereby the glass film laminate 1 according to the example 3 is produced.
Quality judging of the glass film laminate 1 according to the example 3 is performed firstly by counting the number of the bubbles 14 in the interface 13, and the quality judging is performed further by inspecting existence of the open bubble 14a and the close bubble 14b in the peripheral part 1d (L=10 mm).
On the other hand, the glass film laminate 1 according to the comparative example 1 is produced by washing of the contact surfaces 10a and 12a and subsequent direct lamination without application of the ultrasonic.
Quality judging of the glass film laminate 1 according to the comparative example 1 is performed only by the number of the bubbles 14 in the interface 13.
In the case of the glass film laminate 1 according to the example 1, as a result of the judgement only by existence of the bubbles 14 in the interface 13, one defective product exists in the final panels and a final panel non-defective rate is 99%.
In the case of the glass film laminate 1 according to the example 2, as a result of the judgement only by existence of the bubbles 14 in the interface 13, two defective products exist in the final panels and the final panel non-defective rate is 98%.
In the case of the glass film laminate 1 according to the example 3, as a result of the judgement by existence of the bubbles 14 in the interface 13 and existence of the open bubble 14a and the close bubble 14b in the peripheral part 1d, no defective product exists in the final panels and a final panel non-defective rate is 100%.
On the other hand, in the case of the glass film laminate 1 according to the comparative example 1, as a result of the judgement only by existence of the bubbles 14 in the interface 13, ten defective products exist in the final panels and the final panel non-defective rate is 89%.
According to the results of the experiment shown in
According to the results of the experiment, as the glass film laminate 1 according to the example 3, by confirming that the open bubble 14a and the close bubble 14b do not exist in the peripheral part 1d, a yield of the final product can be improved further.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-215398 | Oct 2013 | JP | national |
This is the U.S. national stage of application No. PCT/JP2014/076790, filed on Oct. 7, 2014. Priority under 35 U.S.C. §119(a) and 35 U.S.C. §365(b) is claimed from Japanese Application No. 2013-215398, filed Oct. 16, 2013, the disclosure of which is also incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/076790 | 10/7/2014 | WO | 00 |