The present invention relates to a stamper used during the manufacture of an information medium such as an optical disc or a magnetic disc comprising an uneven pattern such as grooves and prepits, a method of manufacturing the stamper using a photoresist master, a photoresist master, and an information medium manufactured using the stamper.
Optical discs, which represent one type of information media, are currently available in two different varieties: optical recording discs which enable writing or rewriting of information, and read-only discs in which the information has been pre-recorded onto the disc.
A groove (guide channel) that is used for tracking and the like is formed in the disc substrate of an optical recording disc, and a recording layer comprising a phase change material or an organic dye material is laminated on top of the disc substrate. When the laser beam is irradiated onto the recording layer, the recording layer undergoes a chemical or physical change, thus forming a recording mark. In contrast, in the case of a read-only disc, recording marks (information pits) are formed in advance as part of an uneven pattern on the disc substrate. When a reading laser beam is irradiated onto these recording marks, the quantity of reflected light varies, and by detecting these variations, the information is able to be read (played back).
In order to manufacture a disc substrate with an uneven pattern of grooves, information pits, and the like, a stamper is used in which the negative pattern (which is itself a type of uneven pattern) of the desired uneven pattern has been formed. For example, a method of manufacturing a disc substrate by conducting injection molding using a mold with the above stamper secured inside the cavity, thereby transferring the negative pattern to the resin used to fill the cavity, is common.
A stamper with an uneven pattern is usually formed from a metal stamper containing Ni or the like. In the steps required for manufacturing this stamper, first a photoresist master with the negative pattern of the uneven pattern of the stamper is prepared, and a metal film is then formed on this photoresist master by plating. Subsequently, the metal film is separated from the photoresist master, and then subjected to a series of predetermined treatments such as surface washing to form the stamper.
As follows is a description of the manufacturing process for a photoresist master 1, with reference to the conventional photoresist master 1 shown in
In order to use this photoresist master 1 to prepare a stamper 20 by plating, first, as shown in
Subsequently, electroplating is conducted with the thin metal film 8 as a backing, thereby forming a metal film 10 containing Ni or the like. By removing the thin metal film 8 and the metal film 10 from the photoresist master 1, a stamper 20 containing the transferred uneven pattern 6 can be obtained.
In recent years, as the capacity of optical recording media has increased, uneven patterns such as grooves have become much finer, meaning errors in the pattern shape have a large effect on the recording and reading accuracy. Accordingly, it is desirable to form a sharp uneven pattern on the disc substrate, but in order to achieve this sharp pattern, the uneven pattern of the photoresist layer 4, which is the basis for the pattern, must be formed with a high level of precision (sharpness).
The minimum width of the latent image pattern formed on the photoresist layer 4 is limited by the spot diameter of the laser beam when it reaches the photoresist layer 4. When λ is the laser wavelength, and NA is the numerical aperture of the objective lens of the irradiating optical system, then the spot diameter w is represented by the formula w=k·λ/NA. k is a constant that is determined by the aperture shape of the objective lens and the intensity distribution of the incident light beam.
However, even in the case of patterns with widths that theoretically do not exceed the spot diameter limit, if the photoresist layer 4 is thin, then problems of inadequate sharpness can arise due to factors such as shallowness of the uneven pattern transferred to the stamper, or rounding of the shape of the uneven pattern (this is known as pattern sag). It is thought that these problems are caused by fluctuations occurring in the thickness of the photoresist layer 4 (this is known as film thinning) during typical exposure and developing operations. It is thought that these thickness fluctuations are caused by laser beam reflection between the photoresist layer 4 and the glass substrate 2, with this reflection causing excessive exposure of the photoresist layer 4.
The inventor of the present invention has clarified that forming a light absorption layer between the glass substrate 2 and the photoresist layer 4 is an effective way of resolving these problems. By so doing, the light absorption layer can absorb the laser beam and suppress any light reflection, and consequently a sharper exposure and development can be achieved than in a conventional process.
However, based on further research, the inventor of the present invention noticed that a photoresist master 1 with a light absorption layer displayed some problems relating to the formation of the thin metal film 8 by electroless plating. Specifically, it was surmised that a photoresist master 1 in which the light absorption layer was partially exposed was prone to increases in fine irregularities (fine defects) during the electroless plating process. In other words, it was discovered that even though the same method was used to form the thin metal film, on some occasions when the stamper was removed, for some reason or other fine irregularities (fine defects) had been formed on the surface of the uneven pattern of the stamper. During playback these fine irregularities manifest as noise, meaning that despite the attempt to improve the recording capacity by effectively utilizing a light absorption layer, in reality a decrease occurs in the recording and playback performance.
If this problem can be resolved, then the manufacture of a stamper with a sharp uneven pattern should be possible using a photoresist master with a light absorption layer. In other words, it became clear that a sharp uneven pattern that had been formed on the master through the effects of the light absorption layer, could be transferred faithfully to a stamper.
The present invention is directed to a solution to the above described disadvantage, and it is an object of the present invention to provide a method of manufacturing a stamper in which shape errors are suppressed during the electroless plating process, as well as a stamper manufactured using such a method.
As a result of intensive research on methods of manufacturing information media such as optical discs and magnetic discs (discrete media), the inventor of the present invention discovered a method of forming a sharp uneven pattern on a stamper. In other words, the above object can be achieved by the present invention described below.
(1) A method of manufacturing a stamper for manufacturing an information medium, comprising the steps of: manufacturing a photoresist master by forming a light absorption layer with a film thickness T that satisfies T>180 (nm) and a photoresist layer, in that order, on top of a substrate, irradiating light onto said photoresist layer to form a latent image from an opposite surface to that which contacts said light absorption layer, and then developing said latent image to form an uneven pattern; forming a thin metal film on top of said uneven pattern of said photoresist master; forming a metal film on top of said thin metal film; and forming a stamper by separating said thin metal film and said metal film from said photoresist master.
(2) The method of manufacturing a stamper according to (1), wherein the film thickness T of said light absorption layer satisfies T>200 (nm).
(3) A stamper for manufacturing an information medium, in a surface of the stamper an uneven pattern being formed in advance, the stamper being manufactured by the steps of: manufacturing a photoresist master by forming a light absorption layer with a film thickness T that satisfies T>180 (nm) and a photoresist layer, in that order, on top of a substrate, irradiating light onto said photoresist layer to form a latent image from an opposite surface to that which contacts said light absorption layer, and then developing said latent image to form an uneven pattern; forming a thin metal film on top of said uneven pattern of said photoresist master; forming a metal film on top of said thin metal film; and forming the stamper by separating said thin metal film and said metal film from said photoresist master.
(4) A stamper according to (3), wherein the film thickness T of said light absorption layer satisfies T>200 (nm).
(5) A photoresist master comprising a substrate, a light absorption layer laminated on top of said substrate, and a photoresist layer which is laminated on top of said light absorption layer and is capable of having an uneven pattern formed therein by forming and subsequently developing of a latent image, wherein a film thickness T of said light absorption layer satisfies T>180 (nm) and preferably T>200 (nm).
(6) An information medium, in which a final uneven pattern is formed by using, as a negative pattern, an uneven pattern of a stamper manufactured by the steps of: manufacturing a photoresist master by forming a light absorption layer with a film thickness T that satisfies T>180 (nm) and a photoresist layer, in that order, on top of a substrate, irradiating light onto said photoresist layer to form a latent image from an opposite surface to that which contacts said light absorption layer, and then developing said latent image to form an uneven pattern; forming a thin metal film on top of said uneven pattern of said photoresist master; forming a metal film on top of said thin metal film; and forming the stamper by separating said thin metal film and said metal film from said photoresist master.
(7) The information medium according to (6), wherein said final uneven pattern is formed by direct transfer of said uneven pattern from said stamper.
(8) The information medium according to (6), wherein said final uneven pattern is formed by transfer of an uneven pattern from a mother stamper, and said uneven pattern of said mother stamper is formed by transfer of said uneven pattern using said stamper as a master stamper.
(9) The information medium according to (6), wherein said final uneven pattern is formed by transfer of an uneven pattern from a child stamper, and said uneven pattern of said child stamper is formed by transfer of an uneven pattern from a mother stamper, which has been formed by transfer of said uneven pattern using said stamper as a master stamper.
The inventor of the present invention applied a metal catalyst to a photoresist master comprising a light absorption layer, and discovered that the synergistic effect of the advantages offered by the light absorption layer and the provision of the metal catalyst enabled the formation of an uneven pattern with better sharpness than that obtainable by conventional processes. In addition, noticing the fact that a photoresist master in which the light absorption layer is partially exposed can be prone to increases in fine irregularities (fine defects) during the electroless plating process, the inventor of the present invention investigated in further detail, and discovered that by ensuring that the film thickness T of the light absorption layer satisfies T>180 (nm), the quantity of fine defects on the surface of the uneven pattern of the stamper can be reduced.
The reason for this observation is thought to be as follows, although this is only conjecture.
Following application of the metal catalyst, during removal of Sn using an accelerator, the accelerator penetrates into the partially exposed light absorption layer, reaching as far as the glass substrate surface. At this point, the coupling agent layer that is normally applied to the surface of the glass substrate undergoes some form of reaction with the accelerator, generating a gas and causing the formation of fine irregularities. In the present invention, the thickness of the light absorption layer is thickened to at least 180 nm to ensure that the accelerator cannot reach as far as the glass substrate surface, and consequently fine irregularities do not develop. As a result, the synergistic effect of this thicker layer, in combination with the fact that a sharp uneven pattern is formed due to the advantages offered by the light absorption layer, enables the formation of a stamper in which, compared with conventional processes, an even sharper uneven pattern has been transferred faithfully to the stamper.
As a result, the grooves, information pits, and the like of an information medium can also be formed with good sharpness, and this makes it possible to improve the recording and playback characteristics. Furthermore, because the invention is compatible with future ongoing miniaturization of uneven patterns, it also enables increases in the information memory (recording) capacity of information media.
As follows is a detailed description of an embodiment of the present invention, based on the drawings.
The numeral 107 in
As described below, the aforementioned uneven pattern 106 becomes the pattern surface 206 of a stamper 120. Furthermore, the area in which the uneven pattern has not been formed becomes the mirror surface 207 of the stamper 120.
During exposure, the patterning laser beam is absorbed by the light absorption layer 103, thereby suppressing light reflection and enabling the formation of fine unevennesses with good sharpness.
Pd (106A) is then provided on the surface of the uneven pattern 106 of the photoresist master 100. Specifically, a catalyst (a Pd-Sn compound) is adsorbed onto the surface of the uneven pattern 106, and an accelerator is used to remove only the Sn from the catalyst, leaving the Pd deposited on the surface of the uneven pattern 106. The surface of the uneven pattern 106 on which the Pd has been provided may then be washed with a liquid. For example, by washing the surface of the uneven pattern 106 using water (and preferably ultra pure water), the generation of fine irregularities can be even better suppressed.
In
In this formation process, first electroless plating is used to form a Ni thin film 108 on the surface of the uneven pattern 106 on which the Pd has been deposited.
During this formation, a reducing agent in the plating solution is oxidized at the Pd surface, which possesses catalytic activity, and emits an electron, and this electron reduces a Ni ion in the solution, enabling the Ni thin film 108 to effectively conform to, and follow the uneven pattern 106.
Subsequently, a current is passed through the surface, using the Ni thin film 108 as a backing, and electroplating is used to form a Ni film 110. If the Ni thin film 108 and the Ni film 110 are then removed from the photoresist master 100, then as shown in
In this stamper 120, the pattern surface 206 is formed in the area corresponding with the uneven pattern 106, and the mirror surface 207 is formed in the area corresponding with the non-uneven area 107.
Although not specifically shown in the drawings, the stamper 120 can then be installed in a mold, and injection molding or the like is used to manufacture an optical disc substrate having a final uneven pattern created by transferring the uneven pattern as a negative pattern. In addition to using the stamper 120 to manufacture optical disc substrates, the stamper 120 can also be used as a master stamper for preparing a mother stamper by an electroforming process, and this mother stamper can then be used to manufacture optical discs.
In addition, this mother stamper could also be used as a master for preparing a child stamper, and this child stamper can then be used to manufacture the optical discs. In other words, the stamper 120 of the present invention need not necessarily be used directly for the manufacture of optical discs, but may also be used indirectly for such optical disc manufacture, as the master stamper used in the preparation of a mother stamper or the like.
In the photoresist layer 104 of this embodiment, the provision of the light absorption layer 103 enables a well defined latent image to be projected, thus enabling a sharp uneven pattern 106 to be produced. As a result, sagging of the uneven pattern formed on the stamper 120 is suppressed. In addition, by ensuring that the film thickness T of the light absorption layer 103 satisfies T>180 (nm), and preferably T>200 (nm), the number of fine irregularities (fine defects) on the surface of the uneven pattern transferred to the stamper 120 can be reduced markedly. Accordingly, the sharp uneven pattern 106 can be transferred to the stamper 120 with good retention of this sharpness, and by using this stamper 120, optical recording media with suppressed noise levels and good levels of recording and reading (playback) accuracy can be produced.
Furthermore, even in those cases where exposure is stopped prior to exposure of the light absorption layer, that is, partway through the thickness of the photoresist layer, a synergistic effect is still obtained due to the applied Pd and the light absorption layer, and consequently the sharp uneven pattern is able to be transferred to the stamper with good retention of this sharpness, in a similar manner to that described above.
In addition, in the present embodiment only the case involving a Ni plating treatment was described, but the present invention is not limited to this case, and other metal plating can also be used.
Furthermore, the stamper described above is applicable not only to optical discs, but can also be applied generally to the manufacture of information media, including magnetic discs (discrete media).
Following formation of a layer of a coupling agent on top of a polished glass substrate, a light absorption layer was formed by spin coating. The application liquid used was SWK-T5D60 (manufactured by Tokyo Ohka Kogyo Co., Ltd.) containing 4,4′-bis(diethylamino)benzophenone as a light absorption agent. The applied layer was baked at 200° C. for 15 minutes to cure the layer and remove residual solvent, thus forming a light absorption layer of 200 nm in thickness. Subsequently, a photoresist (DVR100, manufactured by Zeon Corporation) was spin coated onto the light absorption layer, and residual solvent was vaporized by baking, thus forming a photoresist layer of 25 nm in thickness.
Subsequently, using a cutting machine manufactured by Sony Corporation, and targeting the formation of a groove pattern with a track pitch of 320 nm and a groove width of 150 nm, the photoresist layer was exposed with a Kr laser (wavelength=351 nm) and subsequently developed to form an uneven pattern, thus producing a photoresist master.
Following activation of the surface of the photoresist layer of this photoresist master using a surfactant, a catalyst (a Pd, Sn colloid) was applied as a preliminary treatment to electroless plating. An accelerator (HBF4 solution) was then used to remove the Sn and achieve deposition of the Pd onto the surface of the photoresist master, thus completing the preparation for electroless plating.
The photoresist master was then immersed in a NiCl2 solution, and a Ni thin film was formed by electroless plating. Electroplating was then conducted with this Ni thin film as a backing, thus forming a Ni film. The laminate formed from this Ni thin film and the Ni film was separated from the master, the rear surface was polished, and the surface was washed, thus completing production of a stamper No. 1.
With the exception of altering the film thickness of the light absorption layer to 140 nm, a stamper No. 2 was prepared in the same manner as the preparation of the stamper No. 1.
With the exception of not providing a light absorption layer, a stamper No. 3 was prepared in the same manner as the preparation of the stamper No. 1.
(Evaluation Results 1)
The shape of the uneven pattern formed on each stamper was confirmed by inspection using an AFM (atomic force microscope). A silicon nitride (SiN) probe tip was used for the AFM probe. Measurement was conducted using a non-contact mode, and the variations in atomic force between the sample and the probe were converted to an image.
As is evident from comparing
(Evaluation Results 2)
The uneven states of the stamper No. 1 and the stamper No. 2, as measured by a scanning electron microscope (10,000× magnification), are shown in
In the present invention, the light absorption layer contacting the photoresist layer enables the formation of a sharp uneven pattern on the photoresist master, and adjustment of the film thickness of the light absorption layer enables the production of a stamper that is faithful to this uneven pattern.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-1776 | Jan 2002 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP03/00019 | 1/6/2003 | WO |