TREA

Method for marking steel and aluminum alloys

Follow

Information

  • Patent Grant
  • 6497985
  • Patent Number
    6,497,985
  • Date Filed
    Wednesday, June 9, 1999
    25 years ago
  • Date Issued
    Tuesday, December 24, 2002
    22 years ago
Information
Abstract
The present invention relates to a method for marking metallic alloys using laser alloying. Specifically, the present invention is directed toward the use of laser alloying steel or aluminum alloys with a mark that provides protection against wear and corrosion and greater permanency.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to a method for marking metallic alloys using laser alloying. Specifically, the present invention is directed toward the use of laser alloying steel or aluminum alloys with a mark that provides protection against wear and corrosion and greater permanency.




2 . Description of the Prior Art




Items made of steel or aluminum have been marked for a variety of reasons including identifying one or more characteristics of the item. One method of marking employs the use of a visible marking substance, such as ink or paint. Such marking substances are subject to fading and/or wear, particularly in abrasive environmental conditions such as wind, rain, and/or direct sunlight. In many cases it is desirable to mark a component prior to the completion of the manufacturing process. It is desirable to have a mark that will not deteriorate during the manufacturing process, which may include heating, bending, abrasion machining and/or welding.




Other methods of marking involve imprinting a visible mark into the surface of an item, such as by etching, engraving, or punching. Methods such as etching or engraving result in some loss of material from the substance to be marked. Methods such as punching result in compression of material, sometimes resulting in a change in the mechanical properties of the material.




The present invention overcomes the drawbacks of the prior art by providing a method of marking steel or aluminum alloys which is far more resistant to wear, abrasion, and fading, and which does not result in a loss of material or in compression of the material to be marked.




SUMMARY OF THE INVENTION




The present invention is directed toward a method for laser marking of metallic alloys. This method comprises applying a layer of precursor comprising a binder and metallic or ceramic powder to a steel or aluminum substrate. The layer has a thickness in the range of 50-250 microns. The method further comprises irradiating the surface of the substrate with a laser beam at a sufficient energy level and for a sufficient time to produce a corrosion and/or wear resistant alloyed apron on the substrate. The laser beam used to perform this step of producing an alloyed apron is referred to herein as the “alloying laser beam.” The irradiation is performed while the substrate and the laser beam are moved relative to each other. The method further comprises marking on the apron with the laser beam to produce a pre-selected marking on the apron. The laser beam used to perform the step of marking the apron is referred to herein as the “marking the laser beam.”











DESCRIPTION OF THE FIGURES





FIG. 1

is a block diagram of a first embodiment of the present invention.





FIG. 2

is a block diagram of the second embodiment of the present invention.





FIG. 3

is a top view of a substrate being marked by the method of the present invention.





FIG. 4

is an enlarged top view of a laser beam cross section for use in the present invention.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




A first embodiment of the present invention is shown in FIG.


1


. This method embodiment for laser marking of metallic alloys comprises applying a layer of precursor comprising a binder and metallic or ceramic powder to a metallic substrate, as described in Block


10


of FIG.


1


. In a preferred embodiment, the metallic substrate is made from steel or aluminum. The layer has a thickness in the range of 50-250 microns. In a preferred embodiment, the powder comprises chromium. In another preferred embodiment, the powder comprises silicon carbide.




The invention further comprises irradiating the surface of the substrate with an alloying laser beam at a sufficient energy level and for a sufficient time to produce a corrosion resistant alloyed apron on the substrate, as shown in Block


12


of FIG.


1


. The irradiation takes place while the substrate


20


undergoes relative movement with respect to the laser beam


22


as shown in FIG.


3


.




In a preferred embodiment, the substrate


20


is moved relative to the alloying laser beam


22


at a translation rate in the range of 500-9000 millimeters per minute. The direction of movement of the laser beam relative to the substrate is known as the “translation axis”


24


, as shown in FIG.


3


.




In a preferred embodiment, the irradiating by the alloying laser beam is performed at a laser power density in the range of 45-55 kilowatts/cm


2


where the powder comprises chromium and the metallic substrate comprises steel. In another preferred embodiment, where the binder comprises chromium and the substrate comprises steel, the alloying laser beam power density is 50 kilowatts/cm


2


. In another preferred embodiment, the irradiating is performed with a pulsed laser.




In a preferred embodiment, the alloying laser beam


22


has a rectangular cross sectional area comprising two shorter sides


25


and two longer sides


23


, as shown in FIG.


4


. In another preferred embodiment, the longer sides of the rectangular cross sectional area have a length of at least four millimeters and the shorter sides of the rectangular cross sectional area have a length of at least 0.6 millimeters. A rectangular beam profile having the dimensions described above can be achieved by aligning a spherical lens closest to the beam, a second cylindrical lens closest to the substrate and a first cylindrical lens between the spherical lens and the second cylindrical lens. The spherical lens should have a focal length of 101.6 millimeters and the first cylindrical lens should have a focal length of 203.2 millimeters. The second cylindrical lens should have a focal length of 152.4 millimeters. The spherical lens and the first cylindrical lens should be spaced apart by five millimeters. The first cylindrical lens and second cylindrical lens should be spaced apart 15 millimeters.




The invention further comprises marking the aprona marking laser beam to produce a preselected marking on the apron, as shown in Block


14


of FIG.


1


. In a preferred embodiment, the marking comprises laser etching, as shown in FIG.


3


. The present invention encompasses both positive and negative marking. The term “positive marking,” as used herein, refers to the laser alloyed region constituting the preselected mark. The term “negative marking,” as used herein refers to the unalloyed region constituting the mark. In either case, the pattern traced out by the laser on the substrate defines the preselected pattern of the mark.




In a preferred embodiment, the invention further comprises directing a shielding gas at the region of the substrate being irradiated by the alloying laser beam, as shown in Block


15


of FIG.


1


. In a preferred embodiment, the shielding gas is nitrogen or argon.




Another embodiment of the present invention is depicted in FIG.


2


. This embodiment comprises applying a layer of precursor comprising a binder in metallic or ceramic powder to a steel or aluminum or substrate, as shown in Block


16


of FIG.


2


. The precursor layer has a thickness in the range of 50-75 microns.




This embodiment further comprises irradiating the surface of the substrate with a laser beam in a preselected pattern at a sufficient energy level and for a sufficient time to produce a preselected alloyed marking on the substrate, as described in Block


18


of FIG.


2


and as shown in FIG.


3


. The laser alloyed region of the substrate will have increased corrosion and/or wear resistance. In a preferred embodiment, the irradiating is performed with a laser beam having a rectangular cross sectional area comprising two shorter sides and two longer sides, as shown in FIG.


4


.




The foregoing disclosure and description of the invention are illustrative and explanatory. Various changes in the size, shape, and materials, as well as in the details of the illustrative construction may be made without departing from the spirit of the invention.



Claims
  • 1. A method for laser marking of metallic alloys, comprising:a. applying a layer of precursor comprising a binder and metallic or ceramic powder to a metallic substrate, said layer having a thickness in the range of 50-250 microns; b. irradiating the surface of the substrate with an alloying nonpulsed laser beam at a laser power density of 45-55 kilowatts/cm2 while said substrate is moved relative to said laser beam at a translation rate in the range of 500-9000 millimeters per minute to produce a corrosion resistant alloyed apron on the substrate; and c. marking the apron with a marking laser beam to produce a pre-selected marking on said apron.
  • 2. The method of claim 1 further comprising directing a shielding gas at the region of the substrate being irradiated by the alloying laser beam used for irradiating said surface.
  • 3. The method of claim 2 wherein said shielding gas is nitrogen or argon.
  • 4. The method of claim 1 wherein said powder comprises chromium or silicon carbide.
  • 5. The method of claim 4 wherein said metallic alloy comprises steel or aluminum.
  • 6. The method of claim 1 wherein the longer sides of the rectangular cross sectional area have a length of at least four millimeters and the shorter sides of said rectangular cross sectional area have a length of at least 0.6 millimeters.
  • 7. The method of claim 1 wherein said marking comprises laser etching.
  • 8. A method for laser marking of metallic alloys, comprising:a. applying a layer of precursor comprising a binder and metallic or ceramic powder to a metallic substrate, said layer having a thickness in the range of 50-75 microns; and b. aligning a laser with two cylindrical optical elements and one spherical optical element to permit a nonrectangular beam emitted by the laser to be shaped by the optical elements such that a rectangular beam is emitted from the optical element farthest from the laser; c. transmitted said nonrectangular laser beam from the laser through the spherical and cylindrical optical elements to produce said laser beam having a rectangular cross-sectional area; d. irradiating the surface of the substrate with said rectangular laser beam in a preselected pattern at a sufficient energy level and for a sufficient time to produce a preselected alloyed marking on the substrate having enhanced wear or corrosion resistance.
  • 9. The method of claim 8 further comprising directing a shielding gas at the region of the substrate being irradiated by the laser beam.
  • 10. The method of claim 8 wherein said powder comprises chromium or silicon carbide.
  • 11. The method of claim 8 wherein said metallic alloy comprises steel or aluminum.
  • 12. A method far laser marking of steel or aluminum alloys, comprising:a. applying a layer of precursor comprising a binder and metallic or ceramic powder to a steel or aluminum substrate, said layer having a thickness in the range of 50-250 microns; b. aligning a nonpulsed laser with two cylindrical optical elements and one spherical optical element to permit a nonrectangular beam emitted by the laser to be shaped by the optical elements such that a rectangular beam is emitted from the optical element farthest from the laser; c. transmnitted said nonrectangular laser beam from the laser through the spherical and cylindrical optical elements to produce said laser beam having a rectangular cross sectional area; d. irradiating the surface of the substrate with said laser beam having a rectangular cross sectional area at a sufficient energy level and for a sufficient time to produce a corrosion resistant alloyed apron on said substrate while said substrate is moved relative to said laser beam; e. directing a shielding gas at the region of the substrate being irradiated by the laser beam; and f. marking the apron with a marking laser beam to produce a preselected marking on said apron.
  • 13. The method of claim 12 wherein the aligning is accomplished by placing a spherical lens closest to the laser, a second cylindrical lens closest to the subtrate, and a first cylindrical lens between the spherical lens and the second spherical lens.
  • 14. The method of claim 13 wherein said irradiating is performed at a laser powered density in the range of 45-55 kilowatts/cm2.
  • 15. The method of claim 14 wherein said subtrate is moved relative to said laser beam at a translation rate in the range of 500-9000 millimeters per minute.
US Referenced Citations (73)
Number Name Date Kind
3705758 Haskal Dec 1972 A
3848104 Locke Nov 1974 A
3986767 Rexer et al. Oct 1976 A
4015100 Gnanamuthu et al. Mar 1977 A
4017708 Engel et al. Apr 1977 A
4157923 Yen et al. Jun 1979 A
4212900 Serlin Jul 1980 A
4322601 Serlin Mar 1982 A
4323755 Nierenberg Apr 1982 A
4434189 Zaplatynsky Feb 1984 A
4475027 Pressley Oct 1984 A
4480169 Macken et al. Oct 1984 A
4495255 Draper et al. Jan 1985 A
4535218 Krause et al. Aug 1985 A
4617070 Amende et al. Oct 1986 A
4638163 Braunlich et al. Jan 1987 A
4644127 La Rocca Feb 1987 A
4720312 Fukuizumi et al. Jan 1988 A
4724299 Hammeke Feb 1988 A
4746540 Kawasaki et al. May 1988 A
4750947 Yoshiwara et al. Jun 1988 A
4801352 Piwczyk Jan 1989 A
4839518 Braunlich et al. Jun 1989 A
4847112 Halleux Jul 1989 A
4898650 Wu et al. Feb 1990 A
4904498 Wu Feb 1990 A
4964967 Hashimoto et al. Oct 1990 A
4981716 Sundstrom Jan 1991 A
4998005 Rathi et al. Mar 1991 A
5059013 Jain Oct 1991 A
5095386 Scheibengraber Mar 1992 A
5124993 Braunlich et al. Jun 1992 A
5130172 Hicks et al. Jul 1992 A
5147999 Dekumbis et al. Sep 1992 A
5196672 Matsuyama et al. Mar 1993 A
5208431 Uchiyama et al. May 1993 A
5230755 Pierantoni et al. Jul 1993 A
5247155 Steen et al. Sep 1993 A
5257274 Barrett et al. Oct 1993 A
5265114 Sun et al. Nov 1993 A
5267013 Spence Nov 1993 A
5290368 Gavigan et al. Mar 1994 A
5308431 Maher et al. May 1994 A
5314003 Mackay May 1994 A
5319195 Jones et al. Jun 1994 A
5322436 Horng et al. Jun 1994 A
5331466 Van Saarloos Jul 1994 A
5352538 Takeda et al. Oct 1994 A
5387292 Morishige et al. Feb 1995 A
5406042 Engelfriet et al. Apr 1995 A
5409741 Laude Apr 1995 A
5409742 Arfsten et al. Apr 1995 A
5411770 Tsai et al. May 1995 A
5430270 Findlan et al. Jul 1995 A
5446258 Mordike Aug 1995 A
5449536 Funkhouser et al. Sep 1995 A
5466906 McCune, Jr. et al. Nov 1995 A
5484980 Pratt et al. Jan 1996 A
5486677 Maischner et al. Jan 1996 A
5491317 Pirl Feb 1996 A
5514849 Findlan et al. May 1996 A
5530221 Benda et al. Jun 1996 A
5546214 Black et al. Aug 1996 A
5558788 Mashburn Sep 1996 A
5563095 Frey Oct 1996 A
5599590 Hayashi et al. Feb 1997 A
5614114 Owen Mar 1997 A
5643641 Turchan et al. Jul 1997 A
5659479 Duley et al. Aug 1997 A
5874011 Ehrlich Feb 1999 A
6051448 Hayama et al. Apr 2000 A
6075223 Harrison Jun 2000 A
6284067 Schwartz et al. Sep 2001 B1
Foreign Referenced Citations (19)
Number Date Country
2129926 Jun 1971 DE
876870 Apr 1998 EP
49-41084 Nov 1974 JP
59-033094 Feb 1984 JP
60-172590 Sep 1985 JP
61-195893 Aug 1986 JP
61-210189 Sep 1986 JP
63-278692 Nov 1988 JP
401083676 Mar 1989 JP
381082 Apr 1991 JP
3115587 May 1991 JP
403115531 May 1991 JP
05-285686 Nov 1993 JP
06-173031 Jun 1994 JP
398706 Mar 1974 SU
1557193 Apr 1990 SU
1743770 Jun 1992 SU
WO 9521720 Aug 1995 WO
WO 9747397 Dec 1997 WO
Non-Patent Literature Citations (48)
Entry
ASM Handbook, vol. 6, Welding, Brazing, and Soldering, 1993.
Ayers, et al.; “A Laser Processing Technique for Improving the Wear Resistance of Metals,” Journal of Metals, Aug. 1981, 19-23.
Belvaux, et al.; “A Method for Obtaining a Uniform Non-Gaussian Laser Illumination,” Optics Communications, vol. 15, No. 2, Oct. 1975, 193-195.
Bett, et al.; “Binary phase zone-plate arrays for laser-beam spatial-intensity distribution conversion,” Applied Optics, vol. 34, No. 20, Jul. 10, 1995, 4025-4036.
Bewsher, et al.; “Design of single-element laser-beam shape projectors,” Applied Optics, vol. 35, No. 10, Apr. 1, 1996, 1654-1658.
Breinan, et al.; “Processing material with lasers,” Physics Today, Nov. 1976, 44-50.
Bruno, et al.; “Laserbeam Shaping for Maximum Uniformity and Maximum Loss, A Novel Mirror Arrangement Folds the Lobes of a Multimode Laserbeam Back onto its Center,” Lasers & Applications, Apr. 1987, 91-94.
Chen, et al.; “The Use of a Kaleidoscope to Obtain Uniform Flux Over a Large Area in a Solar or Arc Imaging Furnace,” Applied Optics, vol. 2, No. 3, Mar. 1963, 265-571.
Christodoulou, et al.; “Laser surface melting of some alloy steels,” Metals Technology, Jun. 1983, vol. 10, 215-222.
Cullis, et al.; “A device for laser beam diffusion and homogenisation,” J. Phys.E:Sci. Instrum., vol. 12, 1979, 668-689.
Dahotre, et al., “Development of microstructure in laser surface alloying of steel with chromium,” Journal of Materials Science, vol. 25, 1990, 445-454.
Dahotre, et al., “Laser Surface Melting and Alloying of Steel with Chromium,” Laser Material Processing III, 1989, 3-19.
Fernelius, et al.; “Design and Testing of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4042), Sep. 1984, 46 pages.
Frieden; “Lossless Conversion of a Plane Laser Wave to a Plane Wave of Uniform Irradiance,” Applied Optics, vol. 4, No. 11, Nov. 1965, 1400-1403.
Galletti, et al.; “Transverse-mode selection in apertured super-Gaussian resonators: an experimental and numerical investigation for a pulsed CO2 Doppler lidar transmitter,” Applied Optics, vol. 36, No. 6, Feb. 20, 1997, 1269-1277.
Gori, et al.; “Shape-invariance range of a light beam,” Optics Letters, vol. 21, No. 16, Aug. 15, 1996, 1205-1207.
Grojean, et al.; “Production of flat top beam profiles for high energy lasers,” Rev. Sci. Instrum. 51(3), Mar. 1980, 375-376.
Hella, “Material Processing with High Power Lasers,” Optical Engineering, vol. 17, No. 3, May-Jun. 1978, 198-201.
Ignatiev, et al.; “Real-time pyrometry in laser machining,” Measurement and Science Technology, vol. 5, No. 5, 563-573.
“Laser Removing of Lead-Based Paint” Illinois Department of Transportation, Jun. 1992, 26 pages.
Charschan, “Lasers in industry,” Laser Processing Fundamentals, (Van Nostrand Reinhold Company), Chapter 3, Sec. 3-1, 139-145.
Fernelius, et al; “Calculations Used in the Design of a Refractive Laser Beam Homogenizer,” Airforce Writing Aeronautical Laboratories Report, (AFWAL-TR-84-4047), Aug. 1984, 18 pages.
Jain, et al.; “Laser Induced Surface Alloy Formation and Diffusion of Antimony in Aluminum,” Nuclear Instruments and Method, vol. 168, 275-282, 1980.
Molian; “Estimation of cooling rates in laser surface alloying processes,” Journal of Materials Science Letters, vol. 4, 1985, 265-267.
“High Power CW Nd:YAG Laser Transformation Hardening,” Hobart Laser Products, 2 pages.
Molian; Structure and hardness of laser-processed Fe-0.2%C-5%Cr and Fe-0.2%C-10%Cr alloys; Journal of Materials Science, vol. 20, 1985, 2903-2912.
“Line-Focussing Optics for Multiple-Pass Laser Welding,” NASA Tech Briefs MFS-29976, date unknown.
“Cylindrical Lenses,” Newport Technical Guide, date unknown, N-65.
“Fused Silica Cylindrical Lenses,” Newport Technical Guide,, date unknown, N-68.
Oswald, et al.; “Measurement and modeling of primary beam shape in an ion microprobe mass analyser,” IOP Publishing Ltd., 1990, 255-259.
Renaud, et al., “Surface Alloying of Mild Steel by Laser Melting of an Electroless Nickel Deposit Containing Chromium Carbides,” Materials & Manufacturing Processes, 6(2), 1991, 315-330.
Smurov, et al.; “Peculiarities of pulse laser alloying: Influence of spatial distribution of the beam,” J. Appl. Phys. 71(7), Apr. 1, 1992, 3147-3158.
“Spawr Integrator,” Spawr Optical Research, Inc., Data Sheet No. 512, Jun. 1986.
Veldkamp, et al.; “Beam profile shaping for laser radars that use detector arrays,” Applied Optics, vol. 21, No. 2, Jan. 15, 1982, 345-358.
Veldkamp; “Laser Beam Profile Shaping with Binary Diffraction Gratings,” Optics communications, vol. 38, No. 5,6, Sep. 1, 1981, 381-386.
Veldkamp; “Laser beam profile shpaing with interlaced binary diffraction gratings,” Applied Optics, vol. 21, No. 17, Sep. 1, 1982, 3209-3212.
Veldkamp; “Technique for generating focal-plane flattop laser-beam profiles,” Rev. Sci. Instru., vol. 53, No. 3, Mar. 1982, 294-297.
Walker, et al.; “Laser surface alloying of iron and 1C-1·4Cr steel with carbon,” Metals Technology, vol. 11, Sep. 1984, 5 pages.
Walker, et al.; “The laser surface-alloying of iron with carbon,” Journal of Material Science vol. 20, 1985, 989-995.
Wei, et al.; “Investigation of High-Intensity Beam Characteristics on Welding Cavity Shape and Temperature Distribution,” Journal of Heat Transfer, vol. 112, Feb. 1990, 163-169.
Jones, et al.; “Laser-beam analysis pinpoints critical parameters,” Laser Focus World, Jan. 1993, 123-130.
Khanna, et al.; “The Effect of Stainless Steel Plasma Coating and Laser Treatment on the Oxidation Resistance of Mild Steel,” Corrosion Science, vol. 33, No. 6, 1992, 949-958.
“New Products” Laser Focus World, Aug. 1996, 173.
Lugscheider, et al.;“A Comparison of the Properties of Coatings Produced by Laser Cladding and Conventional Methods,” Surface Modification Technologies V, The Institute of Materials, 1992, 383-400.
Manna, et al.; “A One-dimensional Heat Transfer Model for Laser Surface Alloying of Chromium on Copper Substrate,” Department of Metallurgical & Materials Engineering, Indian Institute of Technology, vol. 86, N. 5, May 1995, 362-364.
Mazille, et al.; “Surface Alloying of Mild Steel by Laser Melting of Nickel and Nickel/Chromium Precoatings,” Materials Performance Maintenance, Aug. 1991, 71-83.
Molian; “Characterization of Fusion Zone Defects in Laser Surface Alloying Applications,” Scripta Metallurgica, vol. 17, 1983, 1311-1314.
Molian; “Effect of Fusion Zone Shape on the Composition Uniformity of Laser Surface Alloyed Iron,” Scripta Metallurgica, vol. 16, 1982, 65-68.