Method for modifying polycarbonate blends

Abstract
Provided is a method of modifying a blend of polycarbonate and acrylonitrile/butadiene/styrene copolymer comprising adding composite particles to the blend, wherein the composite particles comprise (I) a partially crosslinked polyolefin core and(II) a full or partial shell comprising polymerized units of one or more vinyl monomer, and the resulting modified blend.
Description

Particles that contain polyolefin are useful for a variety of purposes. For example, composite particles may be formed in which a full or partial shell of (meth)acrylic polymer resides on a polyolefin core. Such composite particles may be used as additives to blends of polycarbonate with acrylonitrile/butadiene/styrene copolymers (ABS), to improve one or more of the impact resistance or the melt flow rate, without harming other critical properties, such as, for example, one or more of tensile properties, chemical resistance, or heat resistance.


US 2016/0177077 describes composite polymer compositions comprising the emulsion polymerization product of an aqueous polyolefin dispersion and one or more (meth)acrylic monomers. It is desired to provide improved polyolefin particles and to provide a process for making improved polyolefin particles, so that when a shell of (meth)acrylate polymer is formed on the improved polyolefin particles, and the resulting composite particles are added to matrix polymer such as a blend of polycarbonate with ABS to form compounded matrix polymer, one or more of the following benefits is obtained: the impact resistance of the matrix polymer is improved; and/or the compounded matrix polymer has melt flow characteristics better than the original matrix polymer, as measured by the melt flow rate.


The following is a statement of the invention.


A first aspect of the present invention is a method of modifying a blend of polycarbonate and acrylonitrile/butadiene/styrene copolymer comprising adding composite particles to the blend, wherein the composite particles comprise

    • (I) a partially crosslinked polyolefin core and
    • (II) a full or partial shell comprising polymerized units of one or more vinyl monomer.


A second aspect of the present invention is a compounded composition comprising polycarbonate, acrylonitrile/butadiene/styrene copolymer, and composite particles, wherein the composite particles comprise

    • (I) a partially crosslinked polyolefin core and
    • (II) a full or partial shell comprising polymerized units of one or more vinyl monomer.


The following is a detailed description of the invention.


As used herein, the following terms have the designated definitions, unless the context clearly indicates otherwise.


A hydrocarbon is a compound containing only atoms of hydrogen and carbon. An atom other than carbon and hydrogen is a “hetero” atom. A chemical group that contains one or more hetero atom is a “hetero” group.


A “polymer,” as used herein is a relatively large molecule made up of the reaction products of smaller chemical repeat units. Polymers may have structures that are linear, branched, star shaped, looped, hyperbranched, crosslinked, or a combination thereof; polymers may have a single type of repeat unit (“homopolymers”) or they may have more than one type of repeat unit (“copolymers”). Copolymers may have the various types of repeat units arranged randomly, in sequence, in blocks, in other arrangements, or in any mixture or combination thereof. Polymers have weight-average molecular weight of 1,000 daltons or higher. Polymers are considered fully crosslinked when the polymer chains are sufficiently crosslinked that they become insoluble in any solvent. Fully crosslinked polymers are considered to have infinite molecular weight. A sample of polymer may be a mixture that contains some polymer chains that are fully crosslinked and contains other polymer chains that are not fully crosslinked and that are soluble in an appropriate solvent. Such a mixture is herein referred to as “partially crosslinked.”


Molecules that can react with each other to form the repeat units of a polymer are known herein as “monomers.” The repeat units so formed are known herein as “polymerized units” of the monomer.


Vinyl monomers have the structure




embedded image



where each of R1, R2, R3, and R4 is, independently, a hydrogen, a halogen, an aliphatic group (such as, for example, an alkyl group), a substituted aliphatic group, an aryl group, a substituted aryl group, another substituted or unsubstituted organic group, or any combination thereof. Vinyl monomers are capable of free radical polymerization to form polymers. Some vinyl monomers have one or more polymerizable carbon-carbon double bonds incorporated into one or more of R1, R2, R3, and R4; such vinyl monomers are known herein as multifunctional vinyl monomers. Vinyl monomers with exactly one polymerizable carbon-carbon double bond are known herein as monofunctional vinyl monomers.


An olefin monomer is a monomer that is a hydrocarbon having one or more carbon-carbon double bond and having no aromatic rings.


Vinyl monomers that are hydrocarbons are olefin monomers. A polymer having more than 50% by weight polymerized units of olefin monomers is a polyolefin. Vinyl aromatic monomers are vinyl monomers in which one or more of IV, R2, R3, and R4 contains one or more aromatic rings. (Meth)acrylate means acrylate or methacrylate. (Meth)acrylic means acrylic or methacrylate. (Meth)acrylic monomers are monomers selected from acrylic acid, methacrylic acid, alkyl esters thereof, substituted-alkyl esters thereof, amides thereof, N-substituted amides thereof, acrylonitrile, methacrylonitrile, and mixtures thereof. Substituents may be, for example, hydroxyl groups, alkyl groups, aromatic groups, groups containing non-aromatic carbon-carbon double bonds, or other groups, or combinations thereof. A (meth)acrylic polymer is a polymer having more than 50% by weight polymerized units of (meth)acrylic monomers.


An alpha-olefin is a hydrocarbon having 3 or more carbon atoms and having exactly one carbon-carbon double bond, which is located at a terminal carbon atom. That is, in an alpha-olefin, at least one of the two carbon atoms in the carbon-carbon double bond also has two hydrogen atoms attached. A diene is a hydrocarbon having exactly two carbon-carbon double bonds. A diene may be conjugated or non-conjugated.


A polyolefin that is made exclusively of hydrocarbon monomers is considered to be a hydrocarbon, even if a small number of hetero groups is attached to the polyolefin, as fragments from an initiator and/or chain transfer agent. In hydrocarbon polyolefins, the mole ratio of hetero atoms to polymerized units of all monomers is 0.001:1 or lower. A polyolefin that is not a hydrocarbon is a non-hydrocarbon polyolefin.


As used herein, a crosslinking agent is a compound having two or more carbon-carbon double bonds.


A dispersion is a collection of particles that are distributed throughout a continuous liquid medium. A continuous liquid medium is an aqueous medium if the liquid medium is 50% or more water by weight based on the weight of the liquid medium. A dispersion has “solids” content that is determined by weighing the dispersion (WDISP), then drying the dispersion in an infrared moisture balance at 150° C. until the weight is stable, then determining the weight of the dry residue (WDRY), and then solids=100*WDRY/WDISP.


A compound is said herein to be water soluble if the amount of the compound that may be dissolved in 100 g of water at 23° C. is 5 grams or more.


An initiator is a compound that, when exposed to initiation conditions, produces radical moieties that are capable of initiating free-radical polymerization. The nature of the initiation condition varies among initiators. Some examples: thermal initiators produce radical moieties when heated to a sufficiently high temperature; and photoinitiators produce radical moieties when exposed to radiation of sufficiently short wavelength and sufficiently high intensity. As another example, a redox initiator is a pair of molecules that react together in an oxidation/reduction reaction to produce radical moieties; initiation conditions obtain when both members of the pair are present and can react with each other.


Emulsion polymerization is a process in which monomer emulsion droplets, water-soluble initiator, and optional seed particles are present in an aqueous medium. During emulsion polymerization, monomer molecules transfer from the monomer emulsion droplets to the particles where polymerization takes place, which may be separate particles formed during polymerization or may be the seed particles, or a combination thereof.


Polymers may be characterized by their glass transition temperature (Tg), which is measured by differential scanning calorimetry (DSC), at a scan rate of 10° C./min, using the inflection point method.


A collection of particles may be characterized by the volume mean diameter.


Ratios are characterized herein as follows. For example, if a ratio is said to be 5:1 or higher, it is meant that the ratio may be 5:1 or 6:1 or 100:1 but may not be 4:1. To state this characterization in a general way, if a ratio is said to be X:1 or higher, then the ratio is Y:1, where Y is greater than or equal to X. Similarly, for example, if a ratio is said to be 2:1 or lower, it is meant that the ratio may be 2:1 or 1:1 or 0.001:1 but may not be 3:1. To state this characterization in a general way, if a ratio is said to be Z:1 or lower, then the ratio is W:1, where W is less than or equal to Z.


The present invention involves the use of a dispersion of “initial” polyolefin particles. The label “initial” distinguishes the polyolefin particles from various polyolefin particles that are formed as a result of operations performed on the initial polyolefin particles. Preferably, the solids of the dispersion of initial polyolefin particles is 70% or less; more preferably 60% or less. Preferably, the solids of the dispersion of initial polyolefin particles is 40% or more; more preferably 50% or more.


Preferably, the amount of water in the aqueous medium, by weight based on the weight of the aqueous medium, is 60% or more; more preferably 70% or more; more preferably 80% or more; more preferably 90% or more.


Preferably, the volume average particle diameter of the dispersion of initial polyolefin particles is 100 nm or larger; more preferably 150 nm or larger; more preferably 200 nm or larger; more preferably 250 nm or larger. Preferably, the volume average particle diameter of the dispersion of initial polyolefin particles is 2000 nm or smaller; more preferably 1000 nm or smaller; more preferably 750 nm or smaller; more preferably 500 nm or smaller.


The amount of total polyolefin in the initial polyolefin particles is, by weight based on the total solid weight of the dispersion, preferably 50% or more; more preferably 60% or more; more preferably 70% or more; more preferably 80% or more. The amount of total polyolefin polymer in the initial polyolefin particles is, by weight based on the total solid weight of the dispersion, preferably 98% or less; more preferably 96% or less. Initial polyolefin particles preferably contain one or more non-hydrocarbon polyolefin. More preferably the initial polyolefin particles contain one or more non-hydrocarbon polyolefin and one or more hydrocarbon polyolefin.


The initial polyolefin particles preferably have Tg of 50° C. or lower; more preferably 30° C. or lower; more preferably 15° C. or lower; more preferably 0° C. or lower; more preferably −15° C. or lower.


Examples of hydrocarbon polyolefins include, but are not limited to, homopolymers and copolymers (including elastomers) of monomers chosen from ethylene and one or more alpha-olefins. Examples of alpha-olefins include propylene, 1-butene, 3-methyl-1-butene, 4-methyl-1-pentene, 3-methyl-1-pentene, 1-heptene, 1-hexene, 1-octene, 1-decene, and 1-dodecene. Further examples of hydrocarbon polyolefins include copolymers (including elastomers) of one or more dienes with ethylene, with one or more alpha-olefins, or with a combination thereof. Examples of dienes include butadiene; dicyclopentadiene; 1,5-hexadiene; ethylidene norbornene, and vinyl norbornene.


Preferred hydrocarbon polyolefins are copolymers of two or more alpha-olefins and copolymers of ethylene with one or more alpha-olefins. More preferred are copolymers of ethylene with one or more alpha-olefins. Among copolymers of ethylene with one or more alpha-olefins, preferably an alpha-olefin is used that has 5 or more carbon atoms, more preferably 6 or more carbon atoms; more preferably 7 or more carbon atoms; more preferably 8 or more carbon atoms. Among copolymers of ethylene with one or more alpha-olefins, preferably an alpha-olefin is used that has 12 or fewer carbon atoms; more preferably 10 or fewer carbon atoms; more preferably 9 or fewer carbon atoms; more preferably 8 or fewer carbon atoms.


Polyolefins that are copolymers may be statistical copolymers, block copolymers, graft copolymers, copolymers having other structure, or mixtures thereof. Preferred are statistical copolymers.


Some suitable hydrocarbon polyolefins are commercially available from The Dow Chemical Company, under the tradename AFFINITY™, VERSIFY™, or ENGAGE™; or from ExxonMobil Chemical Company, under the tradename VISTAMAXX™, VISTALON™, or EXACT™; or from Eastman Chemicals under the trade name EASTOFLEX™.


Some suitable hydrocarbon polyolefins are copolymers of one or more olefin monomers with one or more vinyl aromatic monomers. Among such copolymers are, for example, copolymers of ethylene and styrene and block copolymers of styrene-olefin monomer(s)-styrene, including, for example, styrene-butadiene-styrene, styrene-isoprene-styrene, styrene-isoprene-butadiene-styrene, and the hydrogenated versions of these block copolymers, including styrene-ethylene-butylene-styrene, styrene-ethylene-propylene-styrene, and styrene-ethylene-ethylene-propylene-styrene.


The amount of hydrocarbon polyolefin in the initial polyolefin particles is, by weight based on the total solid weight of the dispersion of initial polyolefin particles, preferably 95% or less; more preferably 90% or less; more preferably 85% or less. In some embodiments, the amount of hydrocarbon polyolefin may be zero.


The initial polyolefin particles preferably contain one or more non-hydrocarbon polyolefin. Non-hydrocarbon polyolefins contain one or more hetero group (as defined above). The hetero group may have been attached to a comonomer prior to polymerization or may have been added to the polyolefin by grafting after polymerization.


Examples of non-hydrocarbon polyolefins are copolymers of one or more alpha-olefin with one or more non-hydrocarbon vinyl monomer. Examples of non-hydrocarbon vinyl monomers are vinyl acetate, ethyl acrylate, vinyl alcohol, vinyl chloride, and (meth)acrylic monomers.


Among non-hydrocarbon polyolefins, preferred hetero groups are carboxyl groups, ester groups, anhydride groups, alkoxysilane groups, and combinations thereof. More preferred are anhydride groups; more preferred is the product of grafting maleic anhydride onto a hydrocarbon polyolefin. Preferred hydrocarbon polyolefins onto which hetero groups may be grafted are polyethylene and copolymers of ethylene with one or more alpha-olefin monomers. An unsaturated compound containing a hetero atom may be grafted to a hydrocarbon polyolefin by any effective method, for example by a free radical method, for example in the presence of a free radical initiator or in the presence of ionizing radiation.


Some suitable non-hydrocarbon polyolefins include, for example, the AMPLIFY™ polymers, PARALOID™ functionalized ethylene-octene copolymers, PRIMACOR™ ethylene acrylic acid copolymers, and RETAIN′ polymers (available from The Dow Chemical Company). Additional examples include FUSABOND™ polymers, ELVAX™ copolymers, and NUCREL™ polymers (available from E.I. DuPont de Nemours), EXXELOR™ polymers (available from ExxonMobil Chemical Company), POLYBOND™ polymers (available from Chemtura Corporation), A-C™ wax additives (available from Honeywell), and LICOCENE™ polymers (available from Clariant International Ltd.).


Preferably, each of the hydrocarbon polyolefins and non-hydrocarbon polyolefins has relatively low molecular weight, as characterized by the melt flow rate (MFR, measured as described below in the Examples, using 2.16 kg load at 190° C.). Preferably has melt flow rate of 20 grams per 10 minutes or higher; more preferably 50 grams per 10 minutes or higher; more preferably 100 grams per 10 minutes or higher.


The dispersion of initial polyolefin particles additionally contains a crosslinking agent. Preferred crosslinking agents are chosen from polyolefins having carbon-carbon double bonds (“polyolefin crosslinking agents”) and compounds having molecular weight of 500 or less and having two or more carbon-carbon double bonds (“monomer crosslinking agents”). Among polyolefin crosslinking agents, preferred are homopolymers and copolymers that contain polymerized units of one or more diene (for example, EPDM rubber and polybutadiene). Among monomer crosslinking agents, preferred are those with two or more carbon-carbon double bonds; more preferably 3 or more carbon-carbon double bonds. Suitable monomer crosslinking agents include, for example, triallyl isocyanurate and 1,3,5,7-tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane.


The amount of crosslinking agent is, by weight based on the total solid weight of the dispersion of initial polyolefin particles, preferably 0.5% or more; more preferably 1% or more; more preferably 1.5% or more. The amount of crosslinking agent is, by weight based on the total solid weight of the dispersion of initial polyolefin particles, preferably 20% or less; more preferably 15% or less.


The dispersion of initial polyolefin particles preferably contains one or more surfactant. Preferred surfactants are anionic surfactants, which have a hydrocarbon group of 8 or more carbon atoms and an anionic group. The hydrocarbon group may be linear, branched, aromatic, or a combination thereof; preferred are linear hydrocarbon groups. An anionic group is a chemical group that, in water at pH of 7, carries a negative charge. Preferred anionic groups are phosphate groups, phosphonate groups, carboxylate groups, sulfate groups, and sulfonate groups; more preferred are sulfate groups. Preferred anionic surfactants also contain the group —(CH2CH2O)n—. When the group —(CH2CH2O)n— is present, it is preferably bonded to the sulfate group. The index n is 1 or more, preferably 2 or more. The index n is preferably 20 or less; more preferably 15 or less; more preferably 10 or less; more preferably 6 or less; more preferably 4 or less; more preferably 3 or less.


The amount of surfactant in the initial polyolefin particles is, by weight based on the total solid weight of the dispersion, preferably 0.5% or more; more preferably 1% or more; more preferably 2% or more; more preferably 3% or more. The amount of surfactant in the initial polyolefin particles is, by weight based on the total solid weight of the dispersion, preferably 10% or less; more preferably 8% or less; more preferably 6% or less; more preferably 4% or less.


The initial polyolefin particles optionally contain one or more oil, one or more silicon-containing polymer (such as, for example, polydimethylsiloxane), or a mixture thereof.


Preferably, the total amount of the sum of hydrocarbon polyolefins, nonhydrocarbon polyolefins, crosslinking agents, and surfactants, by weight based on the total solids weight of the dispersion of initial polyolefin particles, is 40% or more; more preferably 50% or more; more preferably 60% or more; more preferably 70% or more; more preferably 80% or more; more preferably 90% or more; more preferably 95% or more.


The dispersion of initial particles in an aqueous medium may be formed by any method. One example of a suitable method is as follows. A hydrocarbon polyolefin and a non-hydrocarbon polyolefin are fed via a feed throat into an extruder. The hydrocarbon polyolefin and the non-hydrocarbon polyolefin may be added separately to the extruder; may be mixed together and then added to the extruder as a mixture; or may be compounded together by melt mixing prior to addition to the extruder. If a crosslinking agent is used that is solid at 25° C., then that crosslinking agent is also fed via the feed throat along with hydrocarbon polyolefin and non-hydrocarbon polyolefin. If a crosslinking agent is used that is liquid at 25° C., then that crosslinking agent is injected via a pump into the melt zone of the extruder. The polyolefins, including the crosslinking agent, are mixed together in the melt state in the extruder and then emulsified in the extruder by the addition of water and surfactant via pumps. The emulsion thus formed has solids level of 70% or higher. One method of making such an emulsion is taught in US 2016/0177077. Then further water is added to the extruder, and the final dispersion exiting the extruder has solids level of less than 70%.


One suitable method making the dispersion of initial particles is to form an emulsion of particles of the hydrocarbons as described above and then add crosslinking agent to the emulsion, preferably while the emulsion is held at a temperature above the melting point of one or more of the polyolefins.


A preferred method of making partially crosslinked particles contains a step of contacting the dispersion of initial polyolefin particles with a peroxide initiator. Peroxide initiators have the structure R1—O—O—R2, where IV and R2 are each independently H or an organic group. Preferably R1 and R2 are each independently H or an alkyl group. Preferably R1 and R2 are not both H. Preferably R1 is H. Preferably R2 is an alkyl group with 2 or more carbon atoms; more preferably 3 or more carbon atoms, more preferably 4 or more carbon atoms. Preferably R2 is an alkyl group with 12 or fewer carbon atoms; more preferably 10 or fewer carbon atoms; more preferably 8 or fewer carbon atoms; more preferably 6 or fewer carbon atoms; more preferably 4 or fewer carbon atoms.


Preferred peroxide initiators are water soluble. Preferred peroxide initiators are hydrogen peroxide and alkyl hydroperoxides; more preferred is t-butyl hydroperoxide.


Preferably, a reducing agent is also included to form a redox initiator with the peroxide. Preferred reducing agents are water soluble. Preferred reducing agents are ascorbic acid, isoascorbic acid, sodium formaldehyde sulfoxylate, tetramethyl ethylene diamine, sodium metabisulfites, and mixtures thereof; more preferred is isoascorbic acid. Preferably a catalyst for the oxidation/reduction reaction between the peroxide and the reducing agent is also included. Preferred catalyst is a salt of iron (II); more preferred is FeSO4. Preferably the mole ratio of peroxide to reducing agent is 0.7:1 or higher; more preferably 0.8:1 or higher; more preferably 0.9:1 or higher. Preferably the mole ratio of peroxide to reducing agent is 1.3:1 or lower; more preferably 1.2:1 or lower; more preferably 1.1:1 or lower.


The amount of peroxide is preferably, by weight based on the total solid weight of the dispersion of initial polyolefin particles, 0.02% or more; more preferably 0.05% or more; more preferably 0.1% or more. The amount of peroxide is preferably, by weight based on the total solid weight of the dispersion of initial polyolefin particles, 2% or less; more preferably 1% or less; more preferably 0.5% or less. The mole ratio of reducing agent to peroxide is preferably 0.2:1 or higher; more preferably 0.5:1 or higher; more preferably 0.8:1 or higher. The mole ratio of reducing agent to peroxide is preferably 2:1 or lower; more preferably 1.5:1 or lower; more preferably 1.2:1 or lower. The amount of catalyst is, by weight based on the solid weight of the dispersion of initial polyolefin particles, preferably 1 ppm or more; more preferably 2 ppm or more; more preferably 4 ppm or more. The amount of catalyst is, by weight based on the solid weight of the dispersion of initial polyolefin particles, preferably 50 ppm or less; more preferably 20 ppm or less; more preferably 10 ppm or less.


While the invention is not limited to any specific mechanism, it is contemplated that the initiator generates free radical moieties that interact with the double bonds in the crosslinking agent and cause them to attach to polymer chains in the hydrocarbon polyolefin, thus creating crosslinks between polymer chains in the hydrocarbon polyolefin. This interaction is known herein as the crosslinking reaction. If a thermal initiator is used, it is expected that the dispersion will be heated to a temperature sufficiently high that the initiator will generate radicals for the crosslinking reaction. If a photoinitiator is used, it is expected that the dispersion will be exposed to radiation of sufficiently short wavelength and of sufficient intensity that the initiator will generate radicals for the crosslinking radicals. If a redox initiator is used, it is expected that the oxidation/reduction reaction will generate radicals for the crosslinking radicals. Redox initiators are preferred.


After the crosslinking reaction is complete, the particles in the dispersion are now referred to as partially crosslinked polyolefin particles. Preferably, the partially crosslinked polyolefin particles remain as a dispersion in the aqueous medium.


The partially crosslinked polyolefin particles preferably have Tg of 50° C. or lower; more preferably 30° C. or lower; more preferably 15° C. or lower; more preferably 0° C. or lower; more preferably −15° C. or lower.


Preferably, the volume average particle diameter of the partially crosslinked polyolefin particles is 100 nm or larger; more preferably 150 nm or larger; more preferably 200 nm or larger; more preferably 250 nm or larger. Preferably, the volume average particle diameter of the partially crosslinked polyolefin particles is 2000 nm or smaller; more preferably 1000 nm or smaller; more preferably 750 nm or smaller; more preferably 500 nm or smaller.


In the dispersion of partially crosslinked polyolefin particles, preferably the amount of water, by weight based on the weight of the aqueous medium, is 60% or more; more preferably 70% or more; more preferably 80% or more; more preferably 90% or more.


Preferably, the solids of the dispersion of partially crosslinked polyolefin particles is 20% or more; more preferably 25% or more; more preferably 30% or more; more preferably 35% or more. Preferably, the solids of the dispersion of partially crosslinked polyolefin particles is 60% or less; more preferably 55% or less; more preferably 50% or less; more preferably 45% or less.


The extent of crosslinking is assessed by measuring the gel fraction of the particles. The gel fraction is measured by drying the dispersion to remove the water, weighing the dry residue (weight=WTOT), then mixing the dry residue with toluene at 90° C. for 1 hour, then filtering the hot toluene through porous metal column fits of 75 μm pore size, as explained in detail in “method B” in the Examples below. The residual solid material not dissolved in the toluene is considered “gel” or crosslinked polymer. The gel fraction is the weight of dry gel (after removal of residual toluene) (weight=WGEL) divided by the weight of the total solid portion of the dispersion, expressed as a percentage. That is,

gel fraction=100*WGEL/WTOT.


Preferably, the gel fraction is 5% or higher; more preferably 10% or higher; more preferably 15% or higher. Because the polyolefin particles are partially crosslinked and not fully crosslinked, the gel fraction is less than 100%; more preferably 80% or less; more preferably 60% or less; more preferably 50% or less.


The dispersion of partially crosslinked polyolefin particles may be used for any purpose. A preferred purpose is as an ingredient in a process for making a dispersion of composite particles in an aqueous medium. A preferred process for making a dispersion of composite particles in an aqueous medium is to perform emulsion polymerization on one or more vinyl monomers in the presence of the dispersion of partially crosslinked polyolefin particles.


Preferably, one or more vinyl monomers are mixed with water and one or more surfactant to form an emulsion of droplets in an aqueous medium, where the droplets contain (meth)acrylic monomer. Preferably, a mixture is formed that contains a dispersion of partially crosslinked polyolefin particles in an aqueous medium, the emulsion of vinyl monomer droplets, and one or more water soluble initiator. The mixture is subjected to conditions that cause the initiator to produce radicals. Those conditions may be established at the same time the ingredients are mixed together, or those conditions may be established after some or all of the ingredients have been mixed together.


For example, the emulsion polymerization could be performed as a “batch” process. In a batch process, all of the desired dispersion of partially crosslinked polyolefin particles and all of the desired vinyl monomer(s) are mixed together. Then conditions are established to cause initiator to create radicals, for example by having a water-soluble thermal initiator present in the mixture and then heating the mixture, or by adding a redox initiator combination to the mixture. The radicals then initiate polymerization of the vinyl monomer in the presence of the partially crosslinked polyolefin particles.


A preferred emulsion polymerization method is “gradual addition.” In a gradual addition process, all of the desired dispersion of partially crosslinked polyolefin particles are placed in a vessel. Then, one or more emulsion of vinyl monomer(s) are gradually added to the vessel, under conditions in which an initiator is producing radicals. In a preferred version of gradual addition, at the same time the one or more emulsion of vinyl monomers is being added, one or more water soluble initiators are also being added. If the water soluble initiator is a thermal initiator, the mixture in the vessel is preferably at a temperature sufficiently high to make the initiator produce radicals. If the water-soluble initiator is a redox initiator, preferably the various compounds of the redox initiator are simultaneously fed to the reactor gradually, preferably separately. In a gradual addition process, preferably the time from the addition of the first amount of monomer until the cessation of the addition of monomer is preferably 10 minutes or more; more preferably 20 minutes or more; more preferably 30 minutes or more; more preferably 40 minutes or more; more preferably 50 minutes or more.


Preferred vinyl monomers are (meth)acrylic monomers, vinyl aromatic monomers, and mixtures thereof; more preferred are (meth)acrylic monomers. Among (meth)acrylic monomers, preferred are (meth)acrylic acid, unsubstituted alkyl esters thereof, substituted-alkyl esters thereof, and mixtures thereof; more preferred are (meth)acrylic acid, unsubstituted alkyl esters thereof, and mixtures thereof; more preferred are unsubstituted alkyl esters of (meth)acrylic acid. Among unsubstituted alkyl esters of acrylic acid, preferred are those in which the alkyl group has 2 or more carbon atoms, more preferably 3 or more carbon atoms, more preferably 4 or more carbon atoms. Among unsubstituted alkyl esters of acrylic acid, preferred are those in which the alkyl group has 18 or fewer carbon atoms; more preferably 12 or fewer carbon atoms; more preferably 8 or fewer carbon atoms. Among unsubstituted alkyl esters of methacrylic acid, preferred are those in which the alkyl group has 4 or fewer carbon atoms; more preferably 3 or fewer carbon atoms; more preferably 2 or fewer carbon atoms; more preferably 1 carbon atom.


Optionally the vinyl monomers used in the emulsion polymerization contain one or more monofunctional monomer and one or more multifunctional monomer.


Preferably, the emulsion polymerization of vinyl monomer(s) forms a vinyl polymer that has a glass transition that is distinct from the glass transition of the partially crosslinked polyolefin particles. Preferably, the Tg of the vinyl polymer is higher than 50° C.; more preferably higher than 75° C.


Preferably, the vinyl polymer forms on the surfaces of the particles of partially crosslinked polyolefin. It is contemplated that the vinyl polymer forms a full or partial shell around particles of partially crosslinked polyolefin. The partially crosslinked polyolefin particle with a full or partial shell of vinyl polymer is called herein a composite particle. Preferably, at the conclusion of the emulsion polymerization process, the composite particles are dispersed in an aqueous medium. The partially crosslinked polyolefin particle is then referred to herein as the “core.” The vinyl polymer formed during the emulsion polymerization is referred to herein as the “shell.”


Preferably, the volume average particle diameter of the composite particles is 100 nm or larger; more preferably 150 nm or larger; more preferably 200 nm or larger; more preferably 250 nm or larger. Preferably, the volume average particle diameter of the composite particles is 2000 nm or smaller; more preferably 1000 nm or smaller; more preferably 750 nm or smaller; more preferably 500 nm or smaller.


In the dispersion of composite particles, preferably the amount of water, by weight based on the weight of the aqueous medium, is 60% or more; more preferably 70% or more; more preferably 80% or more; more preferably 90% or more.


Preferably, the solids of the dispersion of composite particles is 20% or more; more preferably 25% or more; more preferably 30% or more; more preferably 35% or more. Preferably, the solids of the dispersion of composite particles is 60% or less; more preferably 55% or less; more preferably 50% or less; more preferably 45% or less.


Preferably, the composite particles show two separate Tg's. It is expected that one Tg is a characteristic of the polyolefin core while the other Tg is a characteristic of the vinyl polymer shell. Preferably, the Tg of the polyolefin core is 50° C. or lower; more preferably 30° C. or lower; more preferably 15° C. or lower; more preferably 0° C. or lower; more preferably −15° C. or lower. Preferably, the Tg of the vinyl polymer shell is higher than 50° C.; more preferably 60° C. or higher; more preferably 70° C. or higher.


Preferably some of the vinyl polymer of the shell is grafted to the polyolefin core. That is, preferably, some of the polymer chains of the vinyl polymer shell are covalently attached to one or more of the polymer chains in the polyolefin core. The extent of grafting may be assessed using the method described below in the Examples. Preferably the amount of shell that is grafted to the core, by weight based on the total amount of the shell, is 40% or more; more preferably 50% or more; more preferably 60% or more; more preferably 70% or more; more preferably 80% or more; more preferably 90% or more.


The relative amounts of polyolefin core and vinyl polymer shell may be characterized by the weight of core, expressed as a percentage based on the sum of the weights of the core and the shell. The weight of the shell is deduced from the weight of all (meth)acrylic polymers added to the reaction vessel during emulsion polymerization. Preferably the amount of core is 95% or less; more preferably 92% or less; more preferably 87% or less. Preferably the amount of core is 60% or more; more preferably 70% or more; more preferably 77% or more.


Optionally, one or more buffer may be added to the dispersion of composite particles in order to adjust the pH of the dispersion.


A dispersion of composite particles according to the present invention may be used for any purpose. For some purposes, it is desirable to remove water from the dispersion and create a powder that contains the composite particles. Suitable methods for removing water from the dispersion of composite particles include, for example, spray drying and coagulation. When coagulation is used, it is preferably followed by subsequent drying methods including, for example, filtration, fluid bed drying, and combinations thereof. Preferably the process of removing water results in a powder in which the powder particles contain composite particles. It is expected that each particle in the powder will contain many composite particles. A powder particle will often contain 1000 or more composite particles.


The collection of powder particles optionally contains additional ingredients. Additional ingredients may be added to the dispersion and dried along with the composite particles, or additional ingredients may be added to the powder particles after the drying process. For example, one or more antioxidants or one or more process stabilizers or a combination thereof may be added to the collection of powder particles. Preferred process stabilizers contained in the collection of powder particles are phosphate salts; more preferred is sodium phosphate.


A powder that contains the composite particles of the present invention may be used for any purpose. One preferred use of such a powder is as an additive to a matrix polymer. Preferably, the powder that contains the composite particles of the present invention is mixed with powder or pellets of the matrix polymer, and the two ingredients, along with optional additional ingredients, are heated and mechanically blended, for example in an extruder. Preferably, the individual composite particles of the present invention become dispersed throughout a continuous phase of the matrix polymer.


The matrix polymer contains a blend of polycarbonate (PC) and an acrylonitrile/butadiene/styrene copolymer (ABS). The ABS copolymer typically contains polymerized units, by weight, of 5% to 35% acrylonitrile, 5 to 60% butadiene, and 20 to 60% styrene. Preferably, the amount of PC, by weight based on the sum of the weights of PC and ABS, is 40% or more; more preferably 50% or more; more preferably 60% or more; more preferably 70% or more. Preferably, the amount of PC, by weight based on the sum of the weights of PC and ABS, is 95% or less; more preferably 90% or less; more preferably 85% or less.


In a composition that contains composite particles of the present invention and matrix polymer, the amount of composite particles is characterized as a weight percentage, based on the sum of the weights of the composite particles and the matrix polymer. Preferably, the amount of composite particles is 1% or more; more preferably 2% or more; more preferably 5% or more. Preferably, the amount of composite particles is 40% or less; more preferably 30% or less; more preferably 20% or less; more preferably 15% or less.


A composition containing matrix polymer and composite particles of the present invention is known herein as compounded matrix polymer. Optionally, additional ingredients in addition to the matrix polymer and the composite particles may be present in the compounded matrix polymer. Such additional ingredients may be added at any point in the process of making the compounded matrix polymer. For example, the process stabilizers described above as present in the powder form of the composite particles are optionally present in the compounded matrix polymer. Other process additional ingredients may be added during compounding (that is, when the composite particles are mixed with the matrix polymer). Additional ingredients suitable for addition during compounding include, for example process stabilizers (such as, for example, organic phosphates) and antioxidants.


When process stabilizers are present, preferably the amount of process stabilizer, by weight based on the weight of the compounded matrix polymer, is 0.05% or more; more preferably 0.1% or more. When process stabilizers are present, preferably the amount of process stabilizer, by weight based on the weight of the compounded matrix polymer, is 0.5% or less; more preferably 0.3% or less.


The following are examples of the present invention.


The following materials were used:


Hydrocarbon Polyolefin:






    • E/OCT-1=AFFINITY™ GA1950 ethylene/octene copolymer from the Dow Chemical Company


      Non-Hydrocarbon Polyolefins:

    • PE/MAH-1=LICOCENE™ PE MA 4351 maleated polyethylene wax, 5% maleic anhydride, from Clariant

    • PE/MAH-2=RETAIN™ 3000 copolymer of ethylene/octene copolymer grafted with maleic anhydride groups, from the Dow Chemical Company


      Crosslinking Agent:

    • EPDM=NORDEL™ 4820 ethylene-propylene-diene copolymer, from the Dow Chemical Company


      Surfactant:

    • SLES=EMPICOL™ ESB 40 surfactant, sodium lauryl ether sulfate, from Huntsman.





In the samples described below, sample numbers beginning with “C” are comparative, and sample numbers beginning with “Ex” are working examples. Some working examples also serve as preparative examples of other embodiments.







PREPARATIVE EXAMPLE 1: MAKING AQUEOUS DISPERSION OF INITIAL POLYOLEFIN Particles

An aqueous polyolefin dispersion was prepared utilizing a twin screw extruder (25 mm screw diameter, 48 L/D rotating at 450 rpm) using the following procedure. The hydrocarbon polyolefin and the non-hydrocarbon polyolefin were supplied to the feed throat of the extruder via a Schenck Mechatron loss-in-weight feeder and a Schenck volumetric feeder, respectively. The liquid crosslinking agent was injected into the polymer melt zone using Isco dual syringe pumps (from Teledyne Isco, Inc. (Lincoln, Nebr., USA)). The polymers were then melt blended, and then emulsified in the presence of a first aqueous stream and surfactant. The emulsion phase was then conveyed forward to the dilution and cooling zone of the extruder where additional dilution water was added to form the aqueous dispersions having solid level contents in the range of from less than 70 weight percent. The initial aqueous stream, and the dilution water were all supplied by Isco dual syringe pumps. The barrel temperature of the extruder was set to 140° C. After the dispersion exited the extruder, it was further cooled and filtered via a 200 μm mesh size bag filter. Particle size analysis was done with the Beckman Coulter LS 13320 Laser Light Scattering Particle Sizer (Beckman Coulter Inc., Fullerton, Calif.) using the standard procedure. Volume average particle size was obtained.


PREPARATIVE EXAMPLE 2: MAKING A DISPERSION OF PARTIALLY CROSSLINKED POLYOLEFIN PARTICLES IN AN AQUEOUS MEDIUM

Partially crosslinked polyolefin particles were produced in a modified emulsion polymerization according to the following procedure. The polyolefin dispersion from Preparative Example 1 was diluted to 40 wt % solids with a pH of 4-7. Then 5 ppm FeSO4 dissolved in water (based on polyolefin dispersion weight) was added into the dispersion prior to reaction. The dispersion was then charged into a 250 mL three-neck flask fitted with a condenser and a mechanical stirrer. The flask was placed in an oil bath at 65-100° C. The stirring rod was inserted through the Teflon adaptor and glass sleeve and connected to the center of the flask. The stirrer rate was set at 200 rpm. Nitrogen was slowly purged through the reactor, and cooling water was turned on to flow through the condenser. Redox initiator was tert-Butyl hydroperoxide (t-BuOOH) and a reducing agent. The reducing agent was isoascorbic acid (IAA) unless otherwise specified. The t-BuOOH and the reducing agent were dissolved in deionized water respectively and then fed into the reactor slowly using separate syringe pumps. Finally, the hybrid emulsion was collected by filtration through a 190 micron filter.


The gel fractions of the resulting dispersions were measured. As defined above, in all methods, gel fraction=100*WGEL/WTOT. First, the dispersion was dried to remove water, and the weight of dried dispersion was WTOT. The dried sample of partially crosslinked polyolefin particles was extracted with xylene in a Soxhlet extractor for 18 hours under reflux. The dry weight of the material after extraction was WGEL.


The crosslinking reaction is characterized by reaction time (RXTIME) and reaction temperature (RXTEMP).


PREPARATIVE EXAMPLE 3: EMULSION POLYMERIZATION

Composite particles were prepared by a seeded emulsion polymerization process. Each of the above partially crosslinked polyolefin particle dispersions of Table 4 was placed into a reactor to be used as a seed for polymerization of acrylic monomers. The monomers were premixed to form a monomer emulsion and then injected into the reactor over 60 min at 65° C. At the same time, a redox catalyst pair was fed separately into the reactor as a free radical initiator over 90 min. The reaction was maintained at 60° C. for 90 min and then allowed to cool to 25° C. and filtered through a 190 μm filter. In all cases the acrylic monomers were a mixture of methyl methacrylate (MMA) and butyl acrylate (BA), in a weight ratio of MMA:BA of 98.0:2.0.


Grafting was assessed as follows. Samples (approximately 0.2 gram) were dissolved in 5 g of tetrahydrofuran (THF) for approximately 16 hours at room temperature (approximately 23° C.). Then 5 g of acetonitrile (ACN) was added to the solution, which then stood for approximately 16 hours at room temperature. The solution was centrifuged at 70,000 revolutions per minute for 15 min. The supernatant was filtered and tested in a size exclusion chromatograph (SEC) apparatus, using styrene-divinylbenzene copolymer beads, flowing THF at 1 mL/min, with column temperature of 40° C., and differential refractive index detection. The extracted polymer was assumed to be ungrafted acrylic copolymer p(MMA/BA). The SEC curves of detector response versus time for each sample were compared to SEC curves for p(MMA/BA) standard samples of known concentrations. The graph of peak area vs. concentration for the p(MMA/BA) standard samples was fit to a standard line by the linear least-squares method. Using that standard line, the SEC peak area for each sample was converted to a concentration, which was used to calculate the amount of extractable polymer from each sample.


The resulting composite particles (“POA”) are shown in Table 1 below. The amounts of ingredients used are characterized as “phr,” which is parts by weight based on 100 parts by weight of dry initial polyolefin particles. The symbol “˜” means “approximately.”









TABLE 1







Summary of POA samples













CC-1
POA-1
POA-2
POA-3
POA-4















E/OCT-1
82
13.5
67.5
13.5
13.5


PE/MAH-1
15
5
5
5
5


PE/MAH-2

10
10
10
10


EPDM

13.5
13.5
13.5
13.5


SLES
3
3
3
3
3


Peroxide (phr)

0.5
0.5
0.2
0.2


RXTIME (h)

2.5
2.5
2.5
2.5


RXTEMP (° C.)

95
95
95
95


Polyolefin diameter (nm)
420
373
373
373
373


Gel fraction (%)
0
~40
~40
~20
~20








Shell composition
MMA:BA (98:2)












Core-shell ratio
85/15
85/15
70/30
75/25
80/20


Shell grafting* (%)
31
nm
nm
nm
80









EXAMPLE 4: COMPOUNDING OF COMPOSITE PARTICLES WITH MATRIX POLYMER

The aqueous dispersions of composite particles were spray dried according to the following procedure. A two-fluid nozzle atomizer was equipped on a Mobile Minor spray dryer (GEA Process Engineering Inc. (Copenhagen, Denmark)). The nitrogen pressure to nozzle was fixed at 1 bar with 50% flow which is equivalent to 6.0 kg/hour of air flow. A glass jar was placed under the cyclone with the valve on the bottom of the cyclone open. Olefin-acrylic dispersion (approximately 40 wt % solid) was pumped into the heated chamber by an emulsion feed pump. The spray drying experiment was conducted in N2 environment with an inlet temperature fixed at 120° C., and the outlet temperature was controlled at 40° C. by tuning the feed rate of the dispersion. The volume mean particle diameter of the dry powder was measured to be in the range of 20-40 μm.


The polycarbonate (PC) used was MAKROLON™ 2405 resin from Covestro. The ABS was BLENDEX™ 338, a high-rubber ABS impact modifier from Galata Chemicals. Before compounding, the PC was thoroughly dried for 2-4 hours at 110° C. in an oven, and the ABS was dried at 23° C. under vacuum. The PC, the ABS, and the composite particles (“modifier”) were compounded with a JSW 28 corotating twin screw extruder (L/D=40). The resin and the modifier were supplied to the feed throat of the extruder via gravimetric K-Tron feeders and then melt blended. The extruded strand was cooled and then pelletized with a granulometer. The temperature profile of the extruder was 25-250-260-270-270-270-270-270-270-270-270° C. (from the hopper to the die) and the compounding was done with a screw speed of 200 rpm and an output of 10 kg/hr. The extruded strand was chopped into pellets.


To make the injection-molded pieces for the testing, the compounded pellets were dried 4 hours at 110° C. in a low pressure dryer and injection molded utilizing the Battenfield HM80/120 machine with the following temperature profile: 280-280-285-290° C. (from the hopper to the die). The holding pressure was set as 200 bars and the mold temperature was 80° C. The molds were ejected after a cooling time of 40 secs.


EXAMPLE 5: EXPERIMENTAL RESULTS WITH MODIFIER IN PC/ABS BLEND

Samples were compounded and molded as described above, with 90% by weight PC/ABS blend and 10% by weight various modifiers. The results of the melt flow rate (MFR) (ISO 1133), tensile, deflection temperature under load (DTUL, ISO 75), and Izod impact tests (ISO 180) at various temperatures were as shown in Table 6. The tensile tests recorded yield strength (ISO 527), break strength (ISO 528), and break strain (ISO 529). “nt” means not tested. The conditions for MFR were 260° C. with 5 kg load. The amount of modifier in each sample was 10% by weight based on the total weight of the compounded matrix polymer. Sample numbers starting with “C” are comparative.









TABLE 6A







Results with 10% modifier in PC/ABS.









Example














C1
C2
Ex 1
Ex 2
Ex 3
Ex 4





Modifier:
none
CC-1
POA-1
POA-2
POA-3
POA-4


MFR (g/10 min)
6.3
14.9 
8.3
7.3
8.5
 8.5


Yield Strength
42.51
34.42
35.36
36.67
37.1 
36.3


(MPa)








Break Strength
46.07
22.84
30.07
42.03
40.11
35.6


(MPa)








Break Strain
94.03
13.21
46.75
93.92
85.39
69.6


(%)










C1 is comparative because it has no modifier. C2 is comparative because the modifier CC-1 is not crosslinked. C2 has poor MFR and Break Strain.









TABLE 6B







Further Results with 10% modifier in PC/ABS.


Izod results in units of J/cm (ft*lb/in).









Example












C1
C2
Ex 1
Ex 3





Modifier:
none
POA-1
POA-2
POA-3


DTUL (° C. (° F.))
 45 (113)
 40 (105)
 42 (107)
 41 (105)


Izod at 23° C.
3.2 (5.9)
3.5 (6.6)
3.6 (6.8)
3.6 (6.7)


Izod at −20° C.
3.1 (5.8)
3.7 (6.9)
3.7 (7.0)
3.5 (6.6)










C1 has no modifier and shows the worst Izod performance C2, in which the modifier particle has no crosslinking, has the lowest DTUL.

Claims
  • 1. A method of modifying a blend of polycarbonate and acrylonitrile/butadiene/styrene copolymer comprising adding composite particles to the blend, wherein the composite particles comprise (I) a partially crosslinked polyolefin core, wherein the partially crosslinked polyolefin core has a gel fraction of 10% or higher and less than 100%; and(II) a full or partial shell comprising polymerized units of one or more vinyl monomer.
  • 2. The method of claim 1 wherein the vinyl monomer comprises one or more (meth)acrylate monomer.
  • 3. The method of claim 1 wherein the vinyl monomer comprises one or more unsubstituted alkyl ester of (meth)acrylic acid.
  • 4. The method of claim 1, wherein the partially crosslinked polyolefin core has gel fraction of 15% or higher and 50% or less.
  • 5. The method of claim 1, wherein the partially crosslinked polyolefin core is made by a process that comprises performing a crosslinking reaction on an initial polyolefin particle, wherein the initial polyolefin particle comprises one or more polyolefins, and wherein each of the polyolefins in the initial polyolefin particle has melt flow rate at 2.16 kg load at 190° C. of 50 g per 10 minutes or higher.
  • 6. The method of claim 1, wherein the partially crosslinked polyolefin core is prepared with an ethylene-propylene-diene copolymer crosslinking agent.
  • 7. A compounded composition comprising polycarbonate, acrylonitrile/butadiene/styrene copolymer, and composite particles, wherein the composite particles comprise (I) a partially crosslinked polyolefin core, wherein the partially crosslinked polyolefin core has a gel fraction of 10% or higher and less than 100%; and(II) a full or partial shell comprising polymerized units of one or more vinyl monomer.
  • 8. The composition of claim 7, wherein the polycarbonate is present in an amount of 40 to 95% by weight, based on the sum of the weights of the polycarbonate and the acrylonitrile/butadiene/styrene copolymer,and wherein the composite particles are present in an amount of 1 to 40% by weight based on the total of sum of the weights of the composite particles, the polycarbonate, and the acrylonitrile/butadiene/styrene copolymer.
  • 9. The composition of claim 7, wherein the amount of the shell that is grafted to the core is 40% or more by weight based on the weight of the shell.
  • 10. The composition of claim 7, wherein the partially crosslinked polyolefin core is prepared with an ethylene-propylene-diene copolymer crosslinking agent.
Priority Claims (1)
Number Date Country Kind
17290173 Dec 2017 EP regional
PCT Information
Filing Document Filing Date Country Kind
PCT/US2018/063758 12/4/2018 WO
Publishing Document Publishing Date Country Kind
WO2019/133197 7/4/2019 WO A
US Referenced Citations (23)
Number Name Date Kind
4430476 Liu Feb 1984 A
4499237 Tacke et al. Feb 1985 A
4521562 Rosenquist Jun 1985 A
4923246 Takahashi et al. May 1990 A
5290859 Niessner et al. Mar 1994 A
6506848 Hoenig et al. Jan 2003 B2
6709742 Ladika et al. Mar 2004 B2
7112625 Nakayama et al. Sep 2006 B2
7521501 James et al. Apr 2009 B2
7553912 Ikuta et al. Jun 2009 B2
7592394 Yang et al. Sep 2009 B2
7666941 Shiba et al. Feb 2010 B2
8324311 Wasserman et al. Dec 2012 B2
8349423 Palmlof Jan 2013 B2
8889784 Endres et al. Nov 2014 B2
9132209 He et al. Sep 2015 B2
9862870 Kim et al. Jan 2018 B2
20060004154 DeRudder Jan 2006 A1
20120157628 Navarro et al. Jun 2012 A1
20150210849 Motegi Jul 2015 A1
20160168368 Chen et al. Jun 2016 A1
20160177077 Nelliappan Jun 2016 A1
20180223098 Inazawa Aug 2018 A1
Foreign Referenced Citations (4)
Number Date Country
102585469 Jul 2012 CN
2011041230 Apr 2011 WO
2015002858 Jan 2015 WO
2016132337 Aug 2016 WO
Non-Patent Literature Citations (5)
Entry
Cho, “Toughening of Polycarbonate: Effect of Particle Size and Rubber Phase Contents of the Core-Shell Impact Modifier,” Journal of Applied Polymer Science, 2005, p. 748-755, vol. 95, Wiley Periodicals, Inc.
Greco, “Polycarbonate/ABS Blends: A Literature Review,” Advances in Polymer Technology, 1994, p. 249-258, vol. 13, No. 4, John Wiley & Sons, Inc.
Hussain, “Evaluation of the Stability of Emulsified Ethylene-Propylene-Diene-Monomer Using Novel Technique ” Journal of Dispersion Science and Technology,2010,31:1278-1284.
Hussain, “High Performance Emulsified EPDM grafted with vinyl acetate as Compatibilizer for EPDM with Polar Rubber,” Nature and Science, 2010, p. 348-357, vol. 8.
Kangwansupamonkon, “Modification of Natural Rubber by Grafting with Hydrophilic Vinyl Monomers,” Macromol. Chem. Phys., 2005, p. 2450-2460, vol. 206.
Related Publications (1)
Number Date Country
20200369868 A1 Nov 2020 US