Claims
- 1. A magnetizable recording medium for magnetic inspection of an object comprising a pad of a rubber-like resilient matrix formed of a polymer having dispersed therein Fe.sub.2 O.sub.3 magnetic oxide particles having a high magnetic remanent flux density of at least about 1,850 gauss and a high magnetic coercive force of at least about 280 oersteds, and wherein said Fe.sub.2 O.sub.3 particles are non-migrating in said rubber-like resilient material, employing about 4 to about 50% of said magnetic oxide particles by weight of said matrix, said Fe.sub.2 O.sub.3 magnetic oxide particles permitting obtaining multiple magnetic recordings of cracks at an angle to each other or essentially parallel to each other in the recording medium without erasing the initial crack recording.
- 2. The magnetizable recording medium of claim 1, said magnetic oxide particles also having a magnetic maximum flux density saturation of at least about 3,450 gauss.
- 3. The magnetizable recording medium of claim 1, said magnetic oxide particles being in the form of gamma Fe.sub.2 O.sub.3 particles, by weight of said polymer, said magnetic oxide particles having a magnetic remanent flux density ranging from about 1,850 to about 2,000 gauss, and a high magnetic coercive force ranging from about 280 to about 340 oersteds, and of a fine size ranging from about 40 to about 5 microns.
- 4. The magnetizable recording medium as defined in claim 3, said magnetic oxide particles also having a magnetic maximum flux density saturation ranging from about 3,450 to about 3,600 gauss.
- 5. The magnetizable recording medium as defined in claim 3, said rubber-like matrix polymer being a silicone polymer.
- 6. The magnetizable recording medium as defined in claim 3, employing about 4 to about 40% of said magnetic oxide particles by weight of said polymer.
- 7. The magnetizable recording medium as defined in claim 3, employing about 5 to about 15% of said magnetic oxide particles by weight of said polymer.
- 8. The magnetizable recording medium as defined in claim 1, said rubber-like matrix polymer being selected from the group consisting of a silicone polymer, natural rubber and a neoprene-type polymer.
- 9. A magnetizable recording medium for magnetic inspection of an object comprising a pad of a rubber-like resilient matrix formed of a polymer having dispersed therein Fe.sub.2 O.sub.3 magnetic oxide particles having a high magnetic remanent flux density of at least about 1,850 gauss and a high magnetic coercive force of at least about 280 oersteds, and wherein said Fe.sub.2 O.sub.3 particles are non-magrating in said rubber-like resilient material, and having an open mesh reinforcing fabric embedded in said rubber-like matrix.
- 10. The magnetizable recording medium as defined in claim 9, said open mesh reinforcing fabric being selected from the group consisting of silk, nylon, acrylics, and cellulose acetate.
- 11. The magnetizable recording medium as defined in claim 9, in which said open mesh fabric reinforcing layer is sandwiched between two layers of said rubber-like matrix.
- 12. The magnetizable recording medium as defined in claim 9, said rubber-like matrix polymer being selected from the group consisting of a silicone polymer, natural rubber and a neoprene-type polymer.
- 13. A magnetizable recording medium for magnetic inspection of an object comprising a pad of a rubber-like resilient matrix formed of a polymer having dispersed therein Fe.sub.2 O.sub.3 magnetic oxide particles having a high magnetic remanent flux density of at least about 1,850 gauss and a high magnetic coercive force of at least about 280 oersteds, and wherein said Fe.sub.2 O.sub.3 particles are non-migrating in said rubber-like resilient material, and having an open mesh reinforcing fabric embedded in said rubber-like matrix, said matrix containing about 4 to about 50% of said magnetic oxide particles in the form of gamma Fe.sub.2 O.sub.3 particles, by weight of said polymer, said magnetic oxide particles having a magnetic remanent flux density ranging from about 1,850 to about 2,000 gauss, and a high magnetic coercive force ranging from about 280 to about 340 oersteds, and of a fine size ranging from about 40 to about 5 microns.
- 14. The magnetizable recording medium as defined in claim 13, said rubber-like matrix polymer being a silicone polymer.
- 15. A magnetizable recording medium for magnetic inspection of an object comprisng a pad of a rubber-like resilient matrix formed of a polymer having dispersed therein Fe.sub.2 O.sub.3 magnetic oxide particles having a high magnetic remanent flux density of at least about 1,850 gauss and a high magnetic coercive force of at least about 280 oersteds, and wherein said Fe.sub.2 O.sub.3 particles are non-migrating in said rubber-like resilient material, and a silk reinforcing fabric embedded in said rubber-like matrix polymer.
- 16. The magnetizable recording medium of claim 15, said matrix containing about 4 to about 50% of said magnetic oxide particles in the form of gamma Fe.sub.2 O.sub.3 particles, by weight of said polymer, said magnetic oxide particles having a magnetic remanent flux density ranging from about 1,850 to about 2,000 gauss, and a high magnetic coercive force ranging from about 280 to about 340 oersteds, and of a fine size ranging from about 40 to about 5 microns, said rubber-like matrix polymer being a silicone polymer.
Parent Case Info
This application is a continuation-in-part of copending application Ser. No. 932,893, filed Aug. 11, 1978 now abandoned, which was a continuation-in-part of Ser. No. 678,279 filed Apr. 19, 1976, now U.S. Pat. No. 4,110,236.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4098935 |
Knudsen |
Jul 1978 |
|
4146671 |
Fujiyama et al. |
Mar 1979 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
932893 |
Aug 1978 |
|