The present invention pertains to a method for converting a composition into thermoplastic polyurethane, said composition comprising polyurethane resin. The invention particularly concerns articles obtained by shaping the thermoplastic polyurethane obtained by this method. These articles are used as eyewear lenses such as sunwear, ophthalmic lenses, safety glasses, shields and goggles.
The material used to produce eyewear lenses must be optically clear. In addition, the finished product must meet specifications with regards to the color of the product. In particular, the color must remain stable during the life of the product. Certain materials, among them thermoplastic polyurethanes, are not suitable for use in eyewear applications due to a high initial Yellowness Index (YI) and/or due to an increasing YI because of its instability when exposed to UV radiation (e.g. from sunlight).
The rigid thermoplastic polyurethane resin ISOPLAST was first introduced and manufactured by Dow Chemical Company. In the ISOPLAST resin family, the commercially available thermoplastic polyurethane ISOPLAST® 301 produced by Lubrizol Advanced Materials is an injection molded transparent polyurethane derived from 4,4′-methylene diphenyldiisocyanate (MDI) and a mixture of 3 diols which are 1,6-hexanediol, 1,4-bis(hydroxymethyl)cyclohexane and polytetramethylene glycol. As the raw material MDI is pale yellow, the ISOPLAST® 301 resin is tinted with yellow with a measured Yellowness Index of 6 for a 3.2 mm thick injection molded sample based on ASTM D 1925. Thus ISOPLAST® 301 has both a high initial YI and an increasing YI as a function of time.
Nevertheless, in view of its high toughness and its chemical resistance, this material ISOPLAST® 301 material would be of interest for use in eyewear applications, if it were transparent.
There is therefore a need for a method for producing thermoplastic polyurethane such as ISOPLAST® 301, which can be used in eyewear applications, overcoming the limitations of the known thermoplastic polyurethanes, without compromising its other optical and mechanical properties. Advantageously the present invention discloses a method that addresses the issues discussed above. These and other advantages are achieved in accordance with the present invention as described below.
The invention provides a method for converting a composition into thermoplastic polyurethane, said composition comprising polyurethane resin, said method comprising the step of combining the composition with a chemical compound, and the step of converting said mixture into thermoplastic polyurethane, said method being characterized in that said chemical compound is 1,4-Di(2,6-dibromo-4-methylphenylamino)anthracene-9,10-dione.
The polyurethane resin of the composition according to the invention is usually either a polymerizable composition comprising precursors of thermoplastic polyurethane, or pellets and/or powder made of thermoplastic polyurethane which is not light-stabilized (i.e. which does not include any additive—such as colorant or stabilizer—in order to improve the YI).
When the thermoplastic polyurethane is a thermoplastic aromatic based polyurethane, the precursors of said thermoplastic polyurethane are usually: at least one polyol, at least one chain extender, and at least one aromatic isocyanate
The compound “1,4-Di(2,6-dibromo-4-methylphenylamino) anthracene-9,10-dione” is represented by the molecular formula C28H18Br4N2O2. It can be the commercial product sold by Pylam. This compound is a colorant of CAS No.: 68239-76-9. It can be found under the commercial names Pylakrome Blue Violet LX-10330, Solvent Violet 38 and Morplas Violet 3B.
Advantageously according to the invention, this colorant neutralizes the initial Yellowness Index of the thermoplastic polyurethane, that is to say that it lowers the initial Yellowness Index of the thermoplastic resin, in particular when said resin is of the ISOPLAST family, with or without any additive in it. Furthermore, this colorant is surprisingly thermally stable during the converting step into the thermoplastic polyurethane.
According to the invention, said composition can further comprise at least one additive. Said additive is preferably selected from the group of antioxidants and light stabilizers.
The additive(s) and the other components according to the invention can be incorporated in any combination or sequence with the composition, e.g. individually or together, or incorporated during any one of the combination step and the conversion step, or during both steps.
According to a particularly preferred embodiment, the composition further comprises benzenepropanoic acid, 3(1,1-dimethylethyl)-4-hydroxy-5-methyl-1,1′-[1,2-ethanediylbis(oxy-2,1-ethanediyl)]ester; bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-[[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl]methyl]butylmalonate; together with at least one component selected from the group of phenol, 2-(5-chloro-2H-benzotriazol-2-yl)-6-(1,1-dimethylethyl)-4-methyl and 2,2′-methylenebis(6-(2H-benzotriazol-2-yl)-4-1,1,3,3-tetramethylbutyl)phenol), wherein phenol, 2-(5-chloro-2H-benzotriazol-2-yl)-6-(1,1-dimethylethyl)-4-methyl is preferably present.
Advantageously according to the invention, the combination of these specific stabilizing additives (that is to say an antioxidant and two light stabilizers), for example at the level of approximately 0.33% by weight of each additive, and of 1,4-Di(2,6-dibromo-4-methylphenylamino)anthracene-9,10-dione, neutralizes the initial Yellowness Index of the thermoplastic polyurethane surprisingly even in the presence of these, additive(s) which have a rather high Yellowness Index by themselves.
The compound “benzenepropanoic acid, 3(1,1-dimethylethyl)-4-hydroxy-5-methyl-1,1′-[1,2-ethanediylbis(oxy-2,1-ethanediyl)]ester” can be the commercial product sold by the Ciba subsidiary of BASF, Irganox® 245. Irganox® 245 is a hindered phenolic antioxidant with a CAS No of 36443-68-2.
The compound “bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-[[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl]methyl]butylmalonate” can be the commercial product sold by the Ciba subsidiary of BASF, Tinuvin® 144. This compound has the CAS No 63843-89-0. It is a Hindered Amine Light Stabilizer (or HALS).
The compound “phenol, 2-(5-chloro-2H-benzotriazol-2-yl)-6-(1,1-dimethylethyl)-4-methyl” can be the commercial product sold by the Ciba subsidiary of BASF, Tinuvin® 326. This compound has the CAS No 3896-11-5. It is an Ultraviolet Absorbent (or UVA).
The compound “2,2′-methylenebis(6-(2H-benzotriazol-2-yl)-4-1,1,3,3-tetramethylbutyl)phenol)” can be the commercial product sold by the Ciba subsidiary of BASF, Tinuvine 360. This compound has the CAS No 103597-45-1. It is an Ultraviolet Absorbent (or UVA).
According to an embodiment of the invention, the content of 1,4-Di(2,6-dibromo-4-methylphenylamino)anthracene-9,10-dione lies in the range from 1 to 20 ppm, preferably from 5 to 10 ppm (by weight). The amount of the colorant depends generally on whether at least another additive such as UV absorber, antioxidant, and/or HALS has been added to the resin.
Preferably, the combining step is carried out according to a dry blending method or a master batch method, but any other method known to the one skilled in the art can be used.
Preferably, the converting step is carried out according to an injection molding method or an extrusion method, and the converting step is more preferably carried out according to an injection molding method, as known to the one skilled in the art.
When the converting step is carried out according to an extrusion method, the converting step is usually followed by the step of forming an article, preferably a lens, from the thermoplastic polyurethane.
The lens is generally transformed into an ophthalmic lens by suitable shaping, as known by the one skilled in the art. The shaping comprises usually steps of grinding, fining and polishing.
The polyurethane resin is preferably a commercially available product. Alternatively it can be manufactured just before or during the converting step. It is usually in the form of pellets and/or powder.
According to the invention, the polyurethane resin is preferably one of the commercial products sold by Lubrizol Advanced Materials preferably from the ISOPLAST® family such as ISOPLAST® 301, ISOPLAST® 2530 and ISOPLAST® 2531, and the polyurethane resin is more preferably ISOPLAST® 301.
The invention also relates to the thermoplastic polyurethane obtained according to this method. Said thermoplastic polyurethane is “light-stabilized”.
The invention also concerns any article, preferably an ophthalmic lens, formed by the step of shaping the thermoplastic polyurethane obtained according to the method for the invention.
This article is generally used alone or as part of a product or a device, where light passes through the article, and the light passing through the article will be detected by eyes or by a device for detecting the quality or other properties of the light. More preferably, the article is used as eyewear lenses such as in sunwear, ophthalmic lenses, safety glasses, shields and goggles.
The article, in the sense of the present invention, should be understood to mean an uncoated article. The article may in particular be an optically transparent material having the shape of an optical article.
Said article can further comprise a coating over at least one portion of a surface of the article. Said article is advantageously coated with coatings conventionally used in the ophthalmic optics field, such as anti-abrasion coatings, scratch-resistant coatings or anti-reflection coatings.
The invention thus also relates to said article further comprising a coating over at least one portion of a surface of the article.
According to a preferred embodiment, the article has a Yellowness Index which does not increase by more than 4.0, preferably of more than 2.5, over 200 hours in Suntest
Thus the use of the colorant according to the invention surprisingly neutralizes the initial Yellowness Index of the thermoplastic polyurethane while keeping the stability of the thermoplastic polyurethane over 200 hours Suntest as if the thermoplastic polyurethane did not comprise said colorant.
The Suntest is a test as described. This test involves an exposure of a plano test sample with a thickness of 2.0 mm, for 200 hours, of a xenon lamp (60+/−6 Klux, by suitable adjustment of the equipment's irradiance, measured in units of Wcm−2). A hard coating (polysiloxane based anti-abrasion coating), is carried out on this sample just before the Suntest. Filters are providing full day light spectrum from 295 to 780 nm (coated quartz glass/special UV glass/reflecting mirror UV/light).
The Yellowness Index is measured according to ASTM D 1925.
According to the invention, the colorant has an excellent thermal stability during high temperature molding processes, which can be readily understood by considering the accompanying drawing:
The invention is further illustrated by the following non-limiting examples which are given for illustrative purposes only.
In all the examples, the polyurethane resin is the commercially available compound ISOPLAST® 301 provided by the company Lubrizol Advanced Materials and 1,4-Di(2,6-dibromo-4-methylphenylamino) anthracene-9,10-dione will be referred to as the “1,4” colorant.
ISOPLAST® 301 resin (in the form of pellets) was dried at 100° C. for 4 hours so that the moisture level is below 100 ppm.
No colorant or a predetermined amount of “1,4” colorant (2.5 ppm) of the invention was added to the warm ISOPLAST® 301 resin just after drying. The resin pellets were then mixed (combined) by dry blending.
The thus obtained two different mixtures (one with no colorant and the other containing the 1,4 colorant) were separately injection molded into 2 mm thick 6-base plano lenses using a 110-ton Cincinnati Roboshot molding machine equipped with a 2-cavity mold.
Key molding process parameters are as follows:
Melt temperature: 480° F. (248.9° C.)
Mold temperature: 230° F. (thermolater set temperature) (110.0° C.)
Injection speed: 1.2 ips (inch per second) (30.48 mm/s)—one step
Shot size: 1.75 inch (44.45 mm)
Hold pressure: 6,000 psi (41.37 MPa)—5 s; 4,000 psi (27.59 MPa)—3 s; 2,000 psi (13.79 MPa)—2 s; 1,000 psi (6.89 MPa)—2 s
Cool time: 80 sec
Inserts: 76 mm 6-base steel inserts.
Two plano lenses with a center thickness of 2 mm, were then produced and sent to measure Yellowness Index and luminous transmittance using Lambda 900. The Yellowness Index and luminous transmittance results of the injection molded lenses are shown in Table 1. It is seen that the “1,4” colorant gives a low Yellowness Index of approximately 1 while maintaining a high luminous transmittance of 88.02%.
ISOPLAST 301 resin was dried in the same way as in Example 1. In addition to a predetermined amount of the “1,4” colorant, 0.33 wt % antioxidant (Ciba Irganox® 245), 0.33 wt % UV absorber (Ciba Tinuvin® 326) and 0.33 wt % HALS (Ciba Tinuvin® 144) were added to the warm dried resin. The mixtures were mixed (combined) using the dry blending method before injection molding. The molding conditions and Yellowness Index measurement are all same as those in Example 1. The Yellowness Index and luminous transmittance measurement results are shown in Table 2.
It can be seen that the Yellowness Index of the molded lenses can be effectively lowered by addition of high concentration of “1,4” colorant, which, however, can impair the luminous transmittance as well. The optimal concentration of “1,4” colorant to be chosen by the one skilled in the art usually depends on the target product's specification as a result of the compromise between Yellowness Index and luminous transmittance.
ISOPLAST 301 resin was dried in the same way as in Example 1. A predetermined amount (8 ppm) of the “1,4” colorant was added to the warm dried resin. In addition to the “1,4” colorant, 0.33 wt % antioxidant (Ciba Irganox® 245), 0.33 wt % UV absorber (Ciba Tinuvin® 326) and 0.33 wt % HALS (Ciba Tinuvin® 144) were also added to the warm dried resin. The mixture was mixed (combined) using the dry blending method before injection molding. The molding conditions and Yellowness Index measurement are all same as those in Example 1. The Yellowness Index and luminous transmittance measurement results are shown in
In the molding process of the resin prepared in the above manner, ten consecutively-molded lenses were collected and labeled as L1, L2, L3, L4, L5, L6, L7, L8, L9 and L10.
It can be seen that the Yellowness Index approaches a stable value. This suggests the excellent stability of the “1,4” colorant during high temperature molding process.
A ISOPLAST 301 resin was custom-made in the commercial resin manufacturing process with addition of 0.33 wt % antioxidant (Ciba Irganox 245), 0.33 wt % UV absorber (Ciba Tinuvin 326) and 0.33 wt % HALS (Ciba Tinuvin 144). A predetermined amount of “1,4” colorant was mixed well with the dried resin. The mixture was molded in the same conditions as that in Example 1. The Yellowness Index and luminous transmittance measurement results are shown in Table 3.
Again, the optimal concentration of “1,4” colorant to be chosen by the one skilled in the art is subject to the target product's specification as a result of the compromise between Yellowness Index and luminous transmittance.
Two batches of ISOPLAST 301 resin were prepared in a manner similar to that in the previous example four (one without any colorant, and the other with 10 ppm of “1,4” colorant), and 2.00 mm thick plano lenses were injection molded from these two batches of resin separately. Four lenses (two for each batch) are measured for YI during the 200 hours Suntest.
The results of the measurements are given in Table 4 below, the comparative examples being given in the second and third column of this Table, and the examples according to the invention being given in the fourth and fifth columns of this Table.
The data clearly shows that the use of the colorant according to the invention give similar results in terms of low increase in YI over 200 hours Suntest (2.42 and 2.19 with respect to 2.40 and 2.28), while allowing the initial YI of the lenses with colorants to be low. The use of the colorant neutralizes the Yellowness Index of the thermoplastic polyurethane lenses while keeping the stability of the lenses over 200 hours Suntest.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US2010/001599 | 5/27/2010 | WO | 00 | 1/11/2013 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/149445 | 12/1/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4639502 | Muller et al. | Jan 1987 | A |
| 5627254 | Oriani | May 1997 | A |
| 5679756 | Zhu et al. | Oct 1997 | A |
| 5785916 | Huarng | Jul 1998 | A |
| 7247658 | Ragsdale et al. | Jul 2007 | B2 |
| 20050191941 | Radford et al. | Sep 2005 | A1 |
| 20080246187 | Chiu et al. | Oct 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 1217001 | May 1999 | CN |
| 101516945 | Aug 2009 | CN |
| 0769527 | Apr 1997 | EP |
| 0105577 | Jan 2001 | WO |
| 02051911 | Jul 2002 | WO |
| Entry |
|---|
| Morplas Dyes for Plastics and Fibers. http://www.sunbeltcolors.com/pdf/MorplasBrochure.pdf, 2004. |
| International Search Report and Written Opinion, PCT/US2010/001599, Dated Jan. 31, 2011. |
| Number | Date | Country | |
|---|---|---|---|
| 20130201441 A1 | Aug 2013 | US |