This application claims the priority benefit of Chinese application serial no. 201510030433.6, filed on Jan. 21, 2015, the content of which is hereby incorporated by reference herein and made a part of this specification.
This invention relates to a method for preparing a cube textured nickel-tungsten alloy composite substrate used for high-temperature coated superconductor, and it belongs to the field of high-temperature coated superconducting substrate preparation technology.
Coated superconducting material is one of the high-temperature superconducting materials with broad application prospects and great potential commercial value. In a textured metal substrate used for coated conductors, since the core of the composite substrate is made of high-strength, non-ferromagnetic alloy material, the mechanical and magnetic properties of the entire composite substrate with high cube textured surface are further improved, so that the composite substrate is one of the new metal alloy substrates with high performance and high potential application value. Element diffusion composite substrate has been proven to be a high performance textured metal substrate used for coated conductor, which has the capability to obtain sharp cube texture and has a good interface binding force between the inner layer and the outer layer.
Currently, Ni—W alloy substrate is one of the most widely studied substrate materials in scientific research. Compared to smelting method, it is easier for powder metallurgy method for preparing a composite substrate to achieve interlayer element diffusion. In addition, the recrystallization temperature in the powder metallurgy method is much higher than that in the smelting method, and thus the powder metallurgy method has more pronounced diffusion effect than the smelting method. Hot isostatic pressing technique is more suitable for preparing large billets to achieve large scale industrial production of composite substrates. But exorbitant annealing temperature will deepen the depth and width of thermal erosion grooves, which is unfavorable to further coating a transit layer on the surface of the composite substrate. In view of this, powder metallurgy method is taken in the present invention for preparing element diffusion composite Ni—W alloy substrate. By using electric pulse technology, a high-frequency and low-voltage large pulse current is passed through a substrate being annealed in the furnace in the process of dynamic annealing, which thereby greatly enhances the interdiffusion of interlayer elements in the composite substrate and reduces the recrystallization temperature of the substrate to some extent.
In the aspect of liquid metal solidification, the pulse current treatment leads to increase in metal solidification temperature, decrease in solidification time and temperature gradient, solidification structure refinement and mechanical property improvement; in the aspect of solid metal element diffusion, electric pulse technology can enhance diffusion coefficient and reduce diffusion annealing temperature. Reduced energy consumption-during high temperature annealing can reduce costs. In addition to enhancing the interdiffusion effect of interlayer elements of the composite substrate, the main effect of high-energy electric pulse is due to the interaction between electrons and dislocations, which can greatly enhance the process of recrystallization of the alloy, but it just promotes recrystallization nucleation in the deformed tissue and has no significant effect on the mechanisms of nucleation in deformed band and the final texture of composite substrate.
In summary, sandwich-like Ni—W alloy composite substrate prepared with the powder metallurgic method is more favorable to interdiffusion of interlayer elements, by which higher concentration W sufficiently diffuses from the inner layer to the outer layer, leading to the ferromagnetic character of the entire composite substrate being weakened. Electric pulse accelerates element diffusion effect of the composite substrate, meanwhile improves the surface roughness of the composite substrate indirectly, so that the general application performance of the composite substrate is further improved.
The method according to the present invention can be applied to large-scale production of high-performance composite substrate by a vertical dynamic annealing device.
This invention is to provide a method for preparing element diffusion type composite Ni—W alloy substrate in powder metallurgy method, characterized in following specific steps:
The key to the present invention is to develop a technology for preparing special nickel-tungsten alloy composite substrate used for coated conductor, to obtain an alloy substrate with excellent properties; compared to traditional single-layer nickel-tungsten alloy substrate, cube texture content, ferromagnetic properties and strength of the entire substrate in this invention are improved; nickel tungsten alloy composite substrate prepared with the combination of powder metallurgy and electric pulse annealing technology is easier to achieve mutual diffusion of interlayer elements. The present invention can be applied to large-scale industrial production of composite substrate.
In the present invention, the rolled composite nickel-tungsten alloy substrate is heated and kept at certain temperature, meanwhile, a low voltage and high current density pulse current is applied to two ends of the rolled substrate. High-performance nickel-tungsten alloy composite substrate is obtained with the method in the present invention and the sandwich-like composite substrate has low ferromagnetic property and high strength due to diffusion of the higher concentration solute from the inner layer to the outer layer, yet which does not affect the formation of sharp cube texture on the surface of the substrate. On the one hand, the adoption of electric pulse technology accelerates interdiffusion effect of interlayer elements, on the other hand, it promotes the recrystallization nucleation and reduces the recrystallization annealing temperature of the substrate, thus energy saving effect is achieved and the negative effects of annealing thermal erosion grooves among crystal boundary to subsequent coating are effectively reduced. The alloy composite substrate prepared in this invention has the characteristics of high cube texture content, low magnetism, high strength, and can be applied to large-scale industrial production.
The invention is further illustrated in conjunction with the figures and the embodiments below.
This invention is further illustrated by the embodiments, but is not limited to by the following embodiments.
Ni powder and W powder with a purity of greater than 99.95% are provided in the proportion of 8% and 12% atomic percentage of W, respectively; each of the two differently proportioned raw materials is mixed evenly by high-energy ball milling and then three layers of the mixed powders with the volume ratio of 1:2:1 are sequentially and hierarchically loaded into a vacuum thin-wall wrap for hot isostatic pressing, wherein, Ni, W mixed powder with higher W content is loaded into the middle layer, the hot isostatic pressing is carried out under a temperature of 1200° C., a pressure of 150 MPa and the time of 25 min; after the hot isostatic pressing treatment, the billet is subjected to a heat treatment for homogenization and to hot rolling cogging, the billet is then cold rolled into a 80 μm thick composite substrate, the total deformation is 99%; the composite substrate is subjected to dynamic recrystallization annealing heat treatment in a vertical heat treatment furnace ventilating hydrogen argon protective atmosphere; at a moving rate of 10 mm/min, the total time of the composite substrate-moving at constant temperature area 1150° C. for 1 h; at the same time, a pulse current is applied to the annealing composite substrate in the heat treatment furnace with a gap of 900 mm between electrodes, a pulse frequency of 250 Hz, a current density of 530 A/mm2, a DC voltage of 3V; the composite substrate is eventually moved slowly out of the heat treatment furnace with a coil take-up system, which gives rise to an air cooling effect; a section of the composite substrate that has passed through the constant temperature area is cut and measured to get an element distribution curve along the ND direction by EDS line scanning, as shown in
Ni powder and W powder with a purity of greater than 99.95% are provided in the proportion of 8% and 12% atomic percentage of W, respectively; each of the two differently proportioned raw materials is mixed evenly by high-energy ball milling and then three layers of the mixed powders with the volume ratio of 1:2:1 are sequentially and hierarchically loaded into a vacuum thin-wall wrap for hot isostatic pressing, wherein, Ni, W mixed powder with higher W content is loaded into the middle layer, the hot isostatic pressing is carried out under a temperature of 1200° C., a pressure of 150 MPa and the time of 25 min; after the hot isostatic pressing treatment, the billet is subjected to a heat treatment for homogenization and to hot rolling cogging, the billet is then cold rolled into a 80 μm thick composite substrate, the total deformation is 99%; the composite substrate is subjected to dynamic recrystallization annealing heat treatment in a vertical heat treatment furnace ventilating hydrogen argon protective atmosphere; at a moving rate of 5 mm/min, the total time of the composite substrate-moving at constant temperature area 1150° C. for 2 h; at the same time, a pulse current is applied to the annealing composite substrate in the heat treatment furnace with a gap of 900 mm between electrodes, a pulse frequency of 250 Hz, a current density of 530 A/mm2, a DC voltage of 3V; the composite substrate is eventually moved slowly out of the heat treatment furnace with a coil take-up system, which gives rise to an air cooling effect; a section of the composite substrate that has passed through the constant temperature area is cut and measured to get an element distribution curve along the ND direction by EDS line scanning, as shown in
Ni powder and W powder with a purity of greater than 99.95% are provided in the proportion of 8% and 12% atomic percentage of W, respectively; each of the two differently proportioned raw materials is mixed evenly by high-energy ball milling and then three layers of the mixed powders with the volume ratio of 1:2:1 are sequentially and hierarchically loaded into a vacuum thin-wall wrap for hot isostatic pressing, wherein, Ni, W mixed powder with higher W content is loaded into the middle layer, the hot isostatic pressing is carried out under a temperature of 1200° C., a pressure of 150 MPa and the time of 25 min; after the hot isostatic pressing treatment, the billet is subjected to a heat treatment for homogenization and to hot rolling cogging, the billet is then cold rolled into a 80 μm thick composite substrate, the total deformation is 99%; the composite substrate is subjected to dynamic recrystallization annealing heat treatment in a vertical heat treatment furnace ventilating hydrogen argon protective atmosphere; at a moving rate of 10 mm/min, the total time of the composite substrate-moving at constant temperature area 1250° C. for 1 h; at the same time, a pulse current is applied to the annealing composite substrate in the heat treatment furnace with a gap of 900 mm between electrodes, a pulse frequency of 280 Hz, a current density of 610 A/mm2, a DC voltage of 3V; the composite substrate is eventually moved slowly out of the heat treatment furnace with a coil take-up system, which gives rise to an air cooling effect; a section of the composite substrate that has passed through the constant temperature area is cut and measured to get an element distribution curve along the ND direction by EDS line scanning, as shown in
Ni powder and W powder with a purity of greater than 99.95% are provided in the proportion of 8% and 12% atomic percentage of W, respectively; each of the two differently proportioned raw materials is mixed evenly by high-energy ball milling and then three layers of the mixed powders with the volume ratio of 1:2:1 are sequentially and hierarchically loaded into a vacuum thin-wall wrap for hot isostatic pressing, wherein, Ni, W mixed powder with higher W content is loaded into the middle layer, the hot isostatic pressing is carried out under a temperature of 1200° C., a pressure of 150 MPa and the time of 25 min; after the hot isostatic pressing treatment, the billet is subjected to a heat treatment for homogenization and to hot rolling cogging, the billet is then cold rolled into a 80 μm thick composite substrate, the total deformation is 99%; the composite substrate is subjected to dynamic recrystallization annealing heat treatment in a vertical heat treatment furnace ventilating hydrogen argon protective atmosphere; at a moving rate of 5 mm/min, the total time of the composite substrate-moving at constant temperature area 1250° C. for 1 h; at the same time, a pulse current is applied to the annealing composite substrate in the heat treatment furnace with a gap of 900 mm between electrodes, a pulse frequency of 280 Hz, a current density of 610 A/mm2, a DC voltage of 3V; the composite substrate is eventually moved slowly out of the heat treatment furnace with a coil take-up system, which gives rise to an air cooling effect; a section of the composite substrate that has passed through the constant temperature area is cut and measured to get an element distribution curve along the ND direction by EDS line scanning, as shown in
Number | Date | Country | Kind |
---|---|---|---|
2015 1 0030433 | Jan 2015 | CN | national |
Number | Name | Date | Kind |
---|---|---|---|
1765955 | Von Maltitz | Jun 1930 | A |
3805571 | Toda | Apr 1974 | A |
20090269605 | Warke | Oct 2009 | A1 |
Entry |
---|
Suo et al., “Development of cube textured Ni-W alloy substrates used for coated conductors,” presented at the 11th European Conference on Applied Superconductivity, Genova, Italy, Sep. 2013. |
Zhao et al., “Highly reinforced, low magnetic and biaxially textured Ni-7 at.%W/Ni-12 at.%W multi-layer substrates developed for coated conductors,” Superconductor Science and Technology 21 075003, Apr. 2008. |
Gao et al., “Characterization and properties of an advanced composite substrate for YBCO-coated conductors,” Acta Materialia 58(4), pp. 1299-1308, Feb. 2010. |
Bhattacharjee et al., “Nickel base substrate tapes for coated superconductor applications,” Journal of Materials Science 42(6), pp. 1984-2001, Mar. 2007. |
Conrad et al., “Effect of electric current pulses on the recrystallization of copper,” Scripta Metallurgica 17(3), pp. 411-416, Mar. 1983. |
Liu et al., “Fabrication of textured Ni-9.3at.%W substrate by electropulsing intermediate annealing method,” Physica C: Superconductivity and its Applications 497, pp. 119-122, Dec. 2013. |
Zhang, “Effect of electropulsing treatment on microstructure and machinability in ultra-precision machining of Mg-9AI-1Zn alloy,” thesis, Hong Kong Polytechnic University, Nov. 2010, http://hdl.handle.net/10397/5341. |
Number | Date | Country | |
---|---|---|---|
20160211437 A1 | Jul 2016 | US |