Patent Application
20250102905
The present disclosure relates to a method for preparing a pixel defining layer of a light emitting display device using a photosensitive resin composition.
As a flat panel display device, a liquid crystal display device (LCD), an organic light emitting display device (OLED), etc. are widely used. Among these, the organic light emitting display device has advantages such as low power consumption, a fast response speed, high color reproducibility, high luminance, and a wide viewing angle.
In the case of the organic light emitting display device, a polarizing film is used to block the light being reflected from the panel when external light is incident, and there is a disadvantage in that the polarizing film is not suitable for application to a flexible device due to a lack of bending properties.
As a method for solving the above problem, methods such as forming an inorganic film for blocking light on an upper substrate as well as a color filter and a black matrix have been proposed. However, these methods have limitations in obtaining a desired level of antireflection effect, and no specific methods for replacing the polarizing film have yet been suggested.
Meanwhile, colored light blocking layers, especially black light blocking layers, are used to prevent color interference between red, green, and blue color filters in liquid crystal display devices to improve image quality, and recently, the use of the colored light blocking layers has been studied even in organic light emitting displays for the same purpose and to improve image visibility with low reflectivity.
When producing the colored patterns, carbon black and inorganic pigments as well as various types of organic pigments are used as colorants, pigment dispersions in which these are dispersed are mixed with other compositions to form patterns.
Organic light emitting materials are deposited on the patterns formed in this way, and since the HTL layer, which is a common layer, is deposited over the entire areas of the organic light emitting displays, their adhesion to the colored patterns that distinguish the pixels is very important. Therefore, since the adhesion to the HTL material is low if the surface roughnesses of the colored patterns are low, there is a high probability that peeling will occur during the subsequent deposition process or that peeling will occur due to external impact after panel formation, resulting in defective pixels. However, since the colored patterns lack crosslinking during the development process, they contain moisture in a large amount, and the moisture is removed through the post-heat treatment process. In addition, if sufficient crosslinking is not achieved during the post-heat treatment process, rather external moisture may be absorbed. If there is much moisture, problems such as pixel shrinkage, dark spots, and electrode oxidation occur to reduce the lifespan and luminance of the organic light emitting displays.
In order to solve the problems of the above-mentioned related art, one embodiment of the present disclosure implements a colored pattern having a constant value of surface roughness on an electrode substrate so that there is no peeling phenomenon after deposition of a common layer (HTL), and reliability and lifespan of the display are increased.
That is, if the roughness value of the colored pattern after post-heat treatment is low, it may cause pixel off due to common layer peeling, so an object of the present disclosure is to minimize surface flow by leaving it at high temperatures during post-heat treatment.
In addition, one embodiment of the present disclosure is not only to ensure vivid colors but also to increase display reliability and lifespan by implementing a colored pattern with a small amount of moisture and a low moisture absorption rate on an electrode substrate.
In other words, since it may cause a decrease in luminance and a decrease in lifespan due to pixel shrinkage if the moisture content in the panel after post-heat treatment is 50 ppm or more, in order to minimize the moisture content after completing the post-heat treatment process, it is necessary to sufficiently remove moisture during the post-heat treatment step and block external moisture absorption to minimize moisture generation in the panel state.
Another embodiment is to provide an organic light emitting display device including a pixel defining layer prepared by the method.
Still another embodiment is to provide an electronic device including the organic light emitting display device.
A method for preparing a pixel defining layer according to the present disclosure is a method for preparing a pixel defining layer, the method including steps of: applying and coating a photosensitive resin composition; performing prebaking; performing exposure; performing development; and performing post-heat treatment, wherein it is preferable that the post-heat treatment step is performed at an oven temperature of 210° C. to 300° C. for 30 to 120 minutes, and a coating film after the post-heat treatment step has a moisture content of 50 ppm or less and a surface roughness value of 1.48 nm to 3.0 nm.
It is more preferable that the oven temperature of the post-heat treatment step is 230 to 270° C.
It is more preferable that the post-heat treatment step is performed for 60 to 120 minutes.
It is more preferable that the surface roughness after the post-heat treatment is 1.48 nm to 2.7 nm.
It is preferable that the photosensitive resin composition contains a colorant.
It is preferable that the colorant includes one or more of an inorganic dye, an organic dye, an inorganic pigment, and an organic pigment.
It is preferable that the colorant is contained in an amount of 1 to 40% by weight based on the total amount of the photosensitive resin composition.
It is preferable that the colorant is pretreated using: a dispersant; or a water-soluble inorganic salt and a wetting agent.
It is preferable that the colorant has an average particle diameter of 20 nm to 110 nm.
It is preferable that the photosensitive resin composition contains a patterning resin which includes an acrylic binder resin, a cardo-based binder resin, or a combination thereof.
It is preferable that the acrylic binder resin has a weight average molecular weight of 3,000 g/mol to 150,000 g/mol.
It is preferable that the cardo-based binder resin includes a repeating structure of Formula 1 below.
In Formula 1,
In Formula 2 and Formula 3,
In Formula 6 and Formula 7,
In Formula 4 and Formula 5,
It is preferable that the cardo-based resin has a weight average molecular weight of 1,000 to 100,000 g/mol.
It is preferable that the cardo-based resin is contained in an amount of 1 to 30% by weight based on the total amount of the photosensitive resin composition.
It is preferable that the photosensitive resin composition contains a reactive unsaturated compound in an amount of 1 to 40% by weight based on the total amount of the photosensitive resin composition.
It is preferable that the photosensitive resin composition contains a photoinitiator in an amount of 0.01 to 10% by weight based on the total amount of the photosensitive resin composition.
In still another embodiment, it is preferable that the present disclosure provides a pixel defining layer prepared by the preparation method.
In still another embodiment, it is preferable that the present disclosure provides an organic light emitting display device including the pixel defining layer.
In still another embodiment, it is preferable that the present disclosure provides an electronic device including the display device and a control unit for driving the display device.
The present disclosure is not only to reduce peeling in a post-process of a common layer (HTL) but also to increase display reliability and lifespan by implementing a colored pattern having a constant roughness value on an electrode substrate. In other words, since it may cause a decrease in the lifespan due to peeling of the common layer and pixel off if the roughness of the pattern after post-heat treatment is low, it is possible to have a constant roughness by minimizing the flow of the surface by leaving it at high temperatures during post-heat treatment according to the present disclosure.
In addition, the present disclosure can be not only to ensure vivid colors but also to increase display reliability and lifespan by implementing a colored pattern with low moisture content on an electrode substrate. In other words, the present disclosure can minimize the reduction in lifespan due to moisture in the panel state by minimizing the content of moisture after completing the post-heat treatment process by including a colorant according to the present disclosure.
Hereinafter, some embodiments of the present disclosure will be described in detail with reference to exemplary drawings. In adding reference numerals to components of each drawing, the same components may have the same reference numerals as far as possible even though they are indicated in different drawings.
When it is determined that a detailed description of a related known constitution or function may obscure the gist of the present disclosure in describing the present disclosure, the detailed description thereof may be omitted. When the expressions “includes”, “has”, “consisting of”, etc. mentioned in this specification are used, other parts may be added unless “only” is used. When a component is expressed in the singular form, it may include a case in which the plural form is included unless otherwise explicitly stated.
In addition, in describing the components of the present disclosure, terms such as first, second, A, B, (a), (b), etc. may be used. Such terms are only for distinguishing the components from other components, and the essence, order, sequence, number, or etc. of the relevant components are not limited by the terms.
In the description of the positional relationship of the components, when two or more components are described as being “connected”, “linked”, or “fused”, etc., the two or more components may be directly “connected”, “linked”, or “fused”, but it should be understood that the two or more components may also be “connected”, “linked”, or “fused” by way of a further “interposition” of a different component. Here, the different component may be included in any one or more of the two or more components that are to be “connected”, “linked”, or “fused” to each other.
In addition, when a component such as a layer, a film, a region, a plate, or etc. is described to be “on top” or “on” of another component, it should be understood that this may not only include a case where the component is “immediately on top of” another component, but also include a case where another component is disposed therebetween. In contrast, it should be understood that when a component is described to be “immediately on top of” another part, this may mean that there is not another part disposed therebetween.
In the description of the temporal flow relationship relating to the components, the operation method, or the preparation method, for example, when the temporal precedence or flow precedence is described by way of “after”, “subsequently”, “thereafter”, “before”, etc., it may also include cases where the flow is not continuous unless terms such as “immediately” or “directly” are used.
Meanwhile, when the reference is made to numerical values or corresponding information for components, numerical values or corresponding information may be interpreted as including an error range that may occur due to various factors (e.g., process factors, internal or external shocks, noise, etc.) even if a separate explicit description is not present.
The terms used in this specification and the appended claims are as follows unless otherwise stated without departing from the spirit of the present disclosure.
The term used in this application “halo” or “halogen” includes fluorine (F), chlorine (Cl), bromine (Br), and iodine (I) unless otherwise specified.
The term used in this application “alkyl” or “alkyl group” refers to a radical of saturated aliphatic functional groups having 1 to 60 carbons linked by a single bond unless otherwise specified, and including a linear chain alkyl group, a branched chain alkyl group, a cycloalkyl (alicyclic) group, an alkyl-substituted cycloalkyl group, and a cycloalkyl-substituted alkyl group.
The term used in this application “haloalkyl group” or “halogenalkyl group” refers to an alkyl group in which a halogen is substituted unless otherwise specified.
The term used in this application “alkenyl” or “alkynyl”, unless otherwise specified, has a double bond or triple bond, respectively, includes a linear or branched chain group, and has 2 to 60 carbon atoms, but is not limited thereto.
The term used in this application “cycloalkyl” refers to alkyl which forms a ring having 3 to 60 carbon atoms unless otherwise specified, but is not limited thereto.
The term used in this application “alkoxy group” or “alkyloxy group” refers to an alkyl group to which an oxygen radical is bonded, and has 1 to 60 carbon atoms unless otherwise specified, but is not limited thereto.
The term used in this application “alkenoxyl group”, “alkenoxy group”, “alkenyloxyl group”, or “alkenyloxy group” refers to an alkenyl group to which an oxygen radical is attached, and has 2 to 60 carbon atoms unless otherwise specified, but is not limited thereto.
The term used in this application “aryl group” and “arylene group” each have 6 to 60 carbon atoms unless otherwise specified, but are not limited thereto. The aryl group or arylene group in this application includes monocyclic compounds, ring assemblies, multiple fused cyclic compounds, etc. For example, the aryl group may include a phenyl group, a monovalent functional group of biphenyl, a monovalent functional group of naphthalene, a fluorenyl group, and a substituted fluorenyl group, and the arylene group may include a fluorenylene group and a substituted fluorenylene group.
The term used in this application “ring assemblies” means that two or more ring systems (monocyclic or fused ring systems) are directly connected to each other through a single bond or double bond, and the number of direct links between such rings is one less than the total number of ring systems contained in the compound. In the ring assemblies, the same or different ring systems may be directly connected to each other through a single bond or double bond.
Since the aryl group in this application includes ring assemblies, the aryl group includes biphenyl and terphenyl in which a benzene ring, which is a single aromatic ring, is connected by a single bond. In addition, since the aryl group also includes a compound in which an aromatic ring system fused to an aromatic single ring is connected by a single bond, it also includes, for example, a compound in which a benzene ring, which is an aromatic single ring, and fluorine, which is a fused aromatic ring system, are linked by a single bond.
The term used in this application “multiple fused ring systems” refers to a fused ring form in which at least two atoms are shared, and it includes a form in which ring systems of two or more hydrocarbons are fused, a form in which at least one heterocyclic system including at least one heteroatom is fused, etc. Such multiple fused ring systems may be an aromatic ring, a heteroaromatic ring, an aliphatic ring, or a combination of these rings. For example, in the case of an aryl group, it may be a naphthalenyl group, a phenanthrenyl group, a fluorenyl group, etc., but is not limited thereto.
The term used in this application “a spiro compound” has “a spiro union”, and the spiro union refers to a linkage in which two rings are formed by sharing only one atom. At this time, the atom shared by the two rings is called a “spiro atom”, and they are each called “monospiro-”, “dispiro-”, and “trispiro-” compounds depending on the number of spiro atoms included in a compound.
The terms used in this application “fluorenyl group”, “fluorenylene group”, and “fluorenetriyl group” refer to a monovalent, divalent, or trivalent functional group in which R, R′, R″, and R′″ are all hydrogen in the following structures, respectively, unless otherwise specified, “substituted fluorenyl group”, “substituted fluorenylene group”, or “substituted fluorenetriyl group” means that at least one of the substituents R, R′, R″, and R′″ is a substituent other than hydrogen, and cases where R and R′ are bound to each other to form a spiro compound together with carbon to which they are linked are included. In this specification, all of the fluorenyl group, the fluorenylene group, and the fluorenetriyl group may also be referred to as a fluorene group regardless of valences such as monovalent, divalent, trivalent, etc.
In addition, R, R′, R″, and R′″ may each independently be an alkyl group having 1 to 20 carbon atoms, an alkenyl group having 1 to 20 carbon atoms, an aryl group having 6 to 30 carbon atoms, and a heterocyclic group having 2 to 30 carbon atoms and, for example, the aryl group may be phenyl, biphenyl, naphthalene, anthracene, or phenanthrene, and the heterocyclic group may be pyrrole, furan, thiophene, pyrazole, imidazole, triazole, pyridine, pyrimidine, pyridazine, pyrazine, triazine, indole, benzofuran, quinazoline, or quinoxaline. For example, the substituted fluorenyl group and the fluorenylene group may each be a monovalent functional group or divalent functional group of 9,9-dimethylfluorene, 9,9-diphenylfluorene, and 9,9′-spirobi[9H-fluorene].
The term used in this application “heterocyclic group” includes not only an aromatic ring such as “heteroaryl group” or “heteroarylene group”, but also a non-aromatic ring, and refers to a ring having 2 to 60 carbon atoms each including one or more heteroatoms unless otherwise specified, but is not limited thereto. The term used in this application “heteroatom” refers to N, O, S, P, or Si unless otherwise specified, and the heterocyclic group refers to a monocyclic group including a heteroatom, ring assemblies, multiple fused ring systems, spiro compounds, etc.
For example, the “heterocyclic group” may also include a compound including a heteroatom group such as SO2, P═O, etc. such as the compound shown below, instead of carbon that forms a ring.
The term used in this application “ring” includes monocyclic and polycyclic rings, includes heterocycles containing at least one heteroatom as well as hydrocarbon rings, and includes aromatic and non-aromatic rings.
The term used in this application “polycyclic” includes ring assemblies such as biphenyl, terphenyl, etc., multiple fused ring systems, and spiro compounds, includes non-aromatic as well as aromatic compounds, and includes heterocycles containing at least one heteroatom as well as hydrocarbon rings.
The term used in this application “alicyclic group” refers to cyclic hydrocarbons other than aromatic hydrocarbons, includes monocyclic compounds, ring assemblies, multiple fused ring systems, spiro compounds, etc., and refers to a ring having 3 to 60 carbon atoms unless otherwise specified, but is not limited thereto. For example, even when benzene, which is an aromatic ring, and cyclohexane, which is a non-aromatic ring, are fused, the alicyclic group corresponds to an aliphatic ring.
In addition, when prefixes are named consecutively, it means that the substituents are listed in the order they are described. For example, in the case of an arylalkoxy group, it means an alkoxy group substituted with an aryl group, in the case of an alkoxycarbonyl group, it means a carbonyl group substituted with an alkoxy group, and further in the case of an arylcarbonyl alkenyl group, it means an alkenyl group substituted with an arylcarbonyl group, wherein the arylcarbonyl group is a carbonyl group substituted with an aryl group.
In addition, unless otherwise explicitly specified, “substituted” in the term used in this application “substituted or unsubstituted” refers to a substitution with one or more substituents selected from the group consisting of deuterium, a halogen, an amino group, a nitrile group, a nitro group, a C1-C30 alkyl group, a C1-C30 alkoxy group, a C1-C30 alkylamine group, a C1-C30 alkylthiophene group, a C6-C30 arylthiophene group, a C2-C30 alkenyl group, a C2-C30 alkynyl group, a C3-C30 cycloalkyl group, a C6-C30 aryl group, a C6-C30 aryl group substituted with deuterium, a C8-C30 arylalkenyl group, a silane group, a boron group, a germanium group, and a C2-C20 heterocyclic group containing at least one heteroatom selected from the group consisting of O, N, S, Si, and P, but is not limited to these substituents.
Although the “names of functional groups” corresponding to the aryl group, arylene group, heterocyclic group, etc. exemplified as examples of each symbol and a substituent thereof in this application may be described as “names of the functional groups reflecting their valences”, they may also be described as the “names of their parent compounds”. For example, in the case of “phenanthrene”, which is a type of an aryl group, the names of the groups may also be described such that the monovalent “group” is divided and described as “phenanthryl (group)”, and the divalent “group” is divided and described as “phenanthrylene (group)”, etc., but may also be described as “phenanthrene”, which is the name of its parent compound regardless of its valence.
Similarly, in the case of pyrimidine as well, it may be described as “pyrimidine” regardless of its valence, or it may also be described as the “name of the group” of the relevant valence such as pyrimidinyl (group) in the case of monovalent and pyrimidinylene (group) in the case of divalent. Therefore, when the type of a substituent in this application is described as the name of its parent compound, it may refer to an n-valent “group” formed by detachment of a hydrogen atom bonded to a carbon atom and/or hetero atom of its parent compound.
In addition, in describing the names of the compounds or the substituents in this specification, the numbers, alphabets, etc. indicating positions may be omitted. For example, pyrido[4,3-d]pyrimidine may be described as pyridopyrimidine, benzofuro [2,3-d]pyrimidine may be described as benzofuropyrimidine, and 9,9-dimethyl-9H-fluorene may be described as dimethylfluorene. Therefore, both benzo[g]quinoxaline and benzo[f]quinoxaline may be described as benzoquinoxaline.
In addition, unless there is an explicit description, the formulas used in this application are applied in the same manner as in the definition of substituents by the exponent definition of the formula below.
Here, when a is an integer of 0, it means that the substituent R1 is not present, that is, when a is 0, it means that hydrogen is bonded to all carbons that form a benzene ring, and at this time, the indication of hydrogen bonded to carbons may be omitted, and the formula or compound may be described. In addition, when a is an integer of 1, one substituent R1 may be bonded to any one of carbons forming a benzene ring, when a is an integer of 2 or 3, it may be bonded, for example, as shown below, even when a is an integer of 4 to 6, it may be bonded to carbons of a benzene ring in a similar manner, and when a is an integer of 2 or more, R1 may be the same as or different from each other.
Unless otherwise specified in the present application, forming a ring means that adjacent groups bind to one another to form a single ring or multiple fused rings, and the single ring and the formed multiple fused rings may include a heterocycle containing at least one heteroatom as well as a hydrocarbon ring, and include aromatic and non-aromatic rings.
In addition, unless otherwise specified in this specification, when indicating a condensed ring, the number in “number-condensed ring” indicates the number of rings to be condensed. For example, a form in which three rings such as anthracene, phenanthrene, benzoquinazoline, etc. are condensed with one another may be marked as a 3-condensed ring.
Meanwhile, the term used in this application “bridged bicyclic compound” refers to a compound in which two rings share 3 or more atoms to form a ring unless otherwise specified. At this time, the shared atoms may include carbon or a hetero atom.
An organic electric device in this application may refer to a component(s) between a positive electrode and a negative electrode, or may refer to an organic light emitting diode which includes a positive electrode, a negative electrode, and a component(s) positioned therebetween.
In addition, in some cases, the display device in this application may refer to an organic electric device, an organic light emitting diode, and a panel including the same, or may refer to an electronic device including a panel and a circuit. Here, for example, the electronic device may include all of a lighting device, a solar cell, a portable or mobile terminal (e.g., a smart phone, a tablet, a PDA, an electronic dictionary, a PMP, etc.), a navigation terminal, a game machine, various TV sets, various computer monitors, etc., but is not limited thereto, and may be any type of device as long as it includes the component(s).
Hereinafter, embodiments of the present disclosure will be described in detail. However, these embodiments are presented as examples, and the present disclosure is not limited thereby, and the present disclosure is only defined by the scope of the claims to be described later.
The composition containing a colorant according to one embodiment of the present disclosure may be used to prepare a pixel defining layer (PDL) with a red pattern, a green pattern, a blue pattern, or a black matrix.
A black pixel defining layer (PDL) according to one embodiment of the present disclosure may further contain an organic black pigment or black dye as an additional coloring material other than a coloring material included in the colorant described above. For example, an organic pigment may be used alone, or a mixture of an organic pigment and a coloring pigment may be used. At this time, there is an advantage in that the strength of the film (layer) or the adhesion to the substrate is not reduced even when the amount of the coloring material is relatively increased since a coloring pigment that is lack in light blocking properties is mixed. The negative pixel defining layer (PDL) according to one embodiment of the present disclosure may contain a black pigment or black dye as an additional coloring material instead of a coloring material included in the colorant described above.
Hereinafter, each component will be described in detail.
A photosensitive resin composition is a low-viscosity liquid sample, and a spin coater or slit coater is used in order to coat the photosensitive resin composition to a certain thickness after applying the photosensitive resin composition onto a substrate. The spin coater has an advantage in that the flatness deviation in the area decreases although the thickness is decreased as the number of revolutions increases, and a slit coater is preferable to a spin coater in order to coat the photosensitive resin composition on a large area substrate. Due to the solvent remaining after coating, the surface may have fluidity, and there is a disadvantage in that flatness deteriorates due to this, and in order to overcome the disadvantage, the fluidity on the surface is lowered by removing a portion of the solvent using vacuum chamber dry (VCD).
This is a process of removing a portion of the solvent contained in the coating film by heating the coated substrate with a hot plate or an oven at a predetermined temperature and time. When the surface or core part of the coating film is not dried, photomask contamination occurs during exposure in the next process, and when irradiated with ultraviolet light, the exposed portion does not cure well, and the pattern is not formed and removed in the development process due to non-curing.
This is a process of curing a formed film by irradiating active rays (ultraviolet rays) using a photomask in which a pattern is formed when the prebaking process is finished. Types of lamps that generate active rays include LED lamps or metal (mercury) lamps, and wavelengths include g-line (436 nm), h-line (405 nm), i-line (365 nm), and deep UV (<260 nm), which can be used individually or in a mixed form.
When irradiating active rays in the exposure step, the formed film is divided into an exposed portion and a non-exposed portion by the photo mask, and in the case of the positive type, the exposed portion is melted by a developer, and the non-exposed portion withstands the developer and the pattern remains. In the case of the negative type, the exposed portion is cured and has resistance to the developer, and the non-exposed portion is developed. The black pixel defining layer (PDL), which is prepared from a composition containing a colorant of the present disclosure, is a negative type and divided into the exposed portion (curing) and the non-exposed portion (development) to form a pattern.
This is a process of removing the solvent and moisture remaining on it by heating the developed substrate at a high temperature of 230° C. or higher. If the solvent and moisture are not completely removed in the relevant process, the device will be affected by the solvent and moisture remaining in the process after the post-heat treatment process, and dark spots, pixel shrinkage, or the like will affect the lifespan of the device due to this.
In the present disclosure, the post-heat treatment step is performed at an oven temperature of 210 to 300° C., more preferably 230 to 270° C. In addition, the post-heat treatment step is performed for 30 to 120 minutes, more preferably 60 to 120 minutes.
It is preferable that the surface roughness after the post-heat treatment step has a value of 1.48 nm to 3.0 nm, more preferably 1.48 nm to 2.7 nm.
In the present disclosure, it is desirable that the substrate should be treated so that the content of moisture generated after the post-heat treatment step is 50 ppm or less, preferably 40 ppm or less, and more preferably 30 ppm or less.
The patterning resin according to one embodiment of the present disclosure may include a cardo-based binder resin.
The acrylic binder resin is a copolymer of a first ethylenically unsaturated monomer and a second ethylenically unsaturated monomer copolymerizable therewith, and is a resin including one or more acrylic repeating units.
The first ethylenically unsaturated monomer is an ethylenically unsaturated monomer containing one or more carboxyl groups, and specific examples thereof may include acrylic acid, methacrylic acid, maleic acid, itaconic acid, fumaric acid, or combinations thereof. The first ethylenically unsaturated monomer may be contained in an amount of 5 to 50% by weight, for example, 10 to 40% by weight based on the total amount of the acrylic binder resin.
The second ethylenically unsaturated monomer may include aromatic vinyl compounds such as styrene, α-methylstyrene, vinyltoluene, vinylbenzyl methyl ether, etc.; unsaturated carboxylic acid ester compounds such as methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxy butyl (meth)acrylate, benzyl (meth)acrylate, cyclohexyl (meth)acrylate, phenyl (meth)acrylate, etc.; unsaturated carboxylic acid amino alkyl ester compounds such as 2-aminoethyl (meth)acrylate, 2-dimethylaminoethyl (meth)acrylate, etc.; carboxylic acid vinyl ester compounds such as vinyl acetate, etc.; unsaturated carboxylic acid glycidyl ester compounds such as glycidyl (meth)acrylate, etc.; vinyl cyanide compounds such as (meth)acrylonitrile, etc.; and unsaturated amide compounds such as (meth)acrylamide, etc., and these may be used alone or in mixtures of two or more.
Specific examples of the acrylic binder resin may include a (meth)acrylic acid/benzyl methacrylate copolymer, a (meth)acrylic acid/benzyl methacrylate/styrene copolymer, a (meth)acrylic acid/benzyl methacrylate/2-hydroxyethyl methacrylate copolymer, a (meth)acrylic acid/benzyl methacrylate/styrene/2-hydroxyethyl methacrylate copolymer, etc., but are not limited thereto. These may be used alone or in a mixture of two or more. The acrylic binder resin may have a weight average molecular weight of 3,000 g/mol to 150,000 g/mol, for example, 5,000 g/mol to 50,000 g/mol, for example, 20,000 g/mol to 30,000 g/mol.
The cardo-based resin includes a repeating structure such as Formula 1 below.
In Formula 1,
In Formula 2 and Formula 3,
In Formula 6 and Formula 7,
In Formula 4 and Formula 5,
When R′, R″, X2, L1 to L3, R1 to R8, and Rio to R13 are an aryl group, they may preferably be a C6-C30 aryl group, and more preferably a C6-C18 aryl group, for example, phenyl, biphenyl, naphthyl, terphenyl, etc.
When R′, R″, X2, L1 to L3, R1 to R8, and Rio to R13 are a heterocyclic group, they may preferably be a C2-C30 heterocyclic group, and more preferably a C2-C18 heterocyclic group, for example, dibenzofuran, dibenzothiophene, naphthobenzothiophene, naphthobenzofuran, etc.
When R′, R″, R1 to R8, and Rio to R13 are a fluorenyl group, they may preferably be 9,9-dimethyl-9H-fluorene, 9,9-diphenyl-9H-fluorenyl group, 9,9′-spirobifluorene, etc.
When L1 to L3 are an arylene group, they may preferably be a C6-C30 arylene group, and more preferably a C6-C18 arylene group, for example, phenyl, biphenyl, naphthyl, terphenyl, etc.
When R′, R″, X2, R1 to R8, and Rio to R13 are an alkyl group, they may preferably be a C1-C10 alkyl group, for example, methyl, t-butyl, etc.
When R′, R″, X2, R1 to R8, and Rio to R13 are an alkoxyl group, they may preferably be a C1-C20 alkoxyl group, and more preferably a C1-C10 alkoxyl group, for example, methoxy, t-butoxy, etc.
Rings formed by binding between neighboring groups of R′, R″, X2, L1 to L3, R1 to R8, and R10 to R13 may be a C6-C30 aromatic ring; a fluorenyl group; a C2-C60 heterocyclic group containing at least one heteroatom of O, N, S, Si, and P; or a C3-C60 alicyclic group, and for example, when the neighboring groups bind with each other to form an aromatic ring, preferably, a C6-C20 aromatic ring, and more preferably a C6-14 aromatic ring, for example, benzene, naphthalene, phenanthrene, etc. may be formed.
The cardo-based resin may be prepared by mixing two or more of, for example, fluorene-containing compounds such as 9,9-bis(4-oxiranylmethoxyphenyl)fluorene, etc.; anhydride compounds such as a benzene tetracarboxylic acid dianhydride, a naphthalene tetracarboxylic acid dianhydride, a biphenyltetracarboxylic acid dianhydride, a benzophenonetetracarboxylic acid dianhydride, a pyromellitic acid dianhydride, a cyclobutanetetracarboxylic acid dianhydride, a perylenetetracarboxylic acid dianhydride, a tetrahydrofurantetracarboxylic acid dianhydride, a tetrahydrophthalic acid anhydride, etc.; glycol compounds such as ethylene glycol, propylene glycol, polyethylene glycol, etc.; alcohol compounds such as methanol, ethanol, propanol, n-butanol, cyclohexanol, benzyl alcohol, etc.; solvent compounds such as propylene glycol methylethyl acetate, N-methylpyrrolidone, etc.; phosphorus compounds such as triphenylphosphine, etc.; and amine or ammonium salt compounds such as tetramethylammonium chloride, tetraethylammonium bromide, benzyldiethylamine, triethylamine, tributylamine, benzyltriethylammonium chloride, etc.
The cardo-based resin may have a weight average molecular weight of 1,000 g/mol to 100,000 g/mol, preferably 1,000 to 50,000 g/mol, and more preferably 1,000 g/mol to 30,000 g/mol. When the weight average molecular weight of the resin is within the above-described range, the pattern formation is well performed without residue during the preparation of a light blocking layer, there is no loss of film thickness during development, and a good pattern may be obtained. The resin may be contained in an amount of 1 to 30% by weight, and more preferably 3 to 20% by weight based on the total amount of the photosensitive resin composition. When the resin is contained within the above-described range, excellent sensitivity, developing properties, and adhesiveness (adhesion) can be obtained.
A reactive unsaturated compound that is absolutely necessary for negative patterns may form a pattern having excellent heat resistance, light resistance, and chemical resistance by causing sufficient polymerization during exposure in the pattern forming process by having an ethylenically unsaturated double bond.
Specific examples of the reactive unsaturated compound may include ethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol diacrylate, triethylene glycol diacrylate, triethylene glycol dimethacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, pentaerythritol triacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, bisphenol A epoxy acrylate, ethylene glycol monomethyl ether acrylate, trimethylolpropane triacrylate, tripentaerythritol octaacrylate, etc.
Examples of commercially available products of the reactive unsaturated compound are as follows.
Examples of a bifunctional ester of (meth)acrylic acid may include Aronix M-210, M-240, M-6200, etc. of Toa Kosei Kagaku Kogyo Co., Ltd, KAYARAD HDDA, HX-220, R-604, etc. of Nippon Kayaku Co., Ltd, and V-260, V-312, V-335 HP, etc. of Osaka Yuki Kagaku Kogyo Co., Ltd.
Examples of a trifunctional ester of (meth)acrylic acid may include Aronix M-309, M-400, M-405, M-450, M-7100, M-8030, M-8060, etc. of Toa Kosei Kagaku Kogyo Co., Ltd, KAYARAD TMPTA, DPCA-20, DPCA-60, DPCA-120, etc. of Nippon Kayaku Co., Ltd, and V-295, V-300, V-360, etc. of Osaka Yuki Kagaku Kogyo Co., Ltd.
The above products may be used alone or used together in combinations of two or more.
The reactive unsaturated compound may be used after being treated with an acid anhydride so as to impart more excellent developing properties. The reactive unsaturated compound may be contained in an amount of 1 to 40% by weight, for example, 1 to 20% by weight based on the total amount of the photosensitive resin composition. When the reactive unsaturated compound is contained within the above-described range, sufficient curing occurs during exposure in the pattern forming process so that reliability is excellent, heat resistance, light resistance, and chemical resistance of the pattern are excellent, and resolution and adhesion are also excellent.
A photoradical initiator should be used in order to implement a negative pattern with photolithography. The photoinitiator is a photoinitiator which has a molar absorption coefficient of 10,000 L/mol·cm or more in the region of 330 to 380 nm and of which a 5% by weight loss occurs at 200° C. or lower. Here, the molar extinction coefficient may be calculated by Beer-Lambert Law. In addition, the weight loss was measured while raising the temperature to 300° C. at a rate of 5° C. per minute under a nitrogen atmosphere using TGA.
The photoinitiator is an initiator generally used in photosensitive resin compositions, and examples thereof may include an acetophenone-based compound, a benzophenone-based compound, a thioxanthone-based compound, a benzoin-based compound, a triazine-based compound, etc.
Examples of the acetophenone-based compound may include 2,2′-diethoxy acetophenone, 2,2′-dibutoxy acetophenone, 2-hydroxy-2-methylpropiophenone, p-t-butyltrichloro acetophenone, p-t-butyldichloro acetophenone, 4-chloro acetophenone, 2,2′-dichloro-4-phenoxy acetophenone, 2-methyl-1-(4-(methylthio) phenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butan-1-one, etc.
Examples of the benzophenone-based compound may include benzophenone, benzoyl benzoate, methyl benzoyl benzoate, 4-phenyl benzophenone, hydroxy benzophenone, acrylated benzophenone, 4,4′-bis(dimethylamino) benzophenone, 4,4′-bis(diethylamino) benzophenone, 4,4′-dimethylaminobenzophenone, 4,4′-dichlorobenzophenone, 3,3′-dimethyl-2-methoxybenzophenone, etc.
Examples of the thioxanthone-based compound may include thioxanthone, 2-chlorothioxanthone, 2-methylthioxanthone, isopropyl thioxanthone, 2,4-diethyl thioxanthone, 2,4-diisopropyl thioxanthone, 2-chlorothioxanthone, etc.
Examples of the benzoin-based compound may include benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, benzyldimethyl ketal, etc.
Examples of the triazine-based compound may include 2,4,6-trichloro-s-triazine, 2-phenyl 4,6-bis(trichloromethyl)-s-triazine, 2-(3′,4′-dimethoxystyryl)-4,6-bis (trichloromethyl)-s-triazine, 2-(4′-methoxynaphthyl)-4,6-bis(trichloromethyl)-s-triazine, 2-(p-methoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine, 2-(p-tolyl)-4,6-bis(trichloromethyl)-s-triazine, 2-biphenyl 4,6-bis(trichloromethyl)-s-triazine, bis(trichloromethyl)-6-styryl-s-triazine, 2-(naphtho-1-yl)-4,6-bis(trichloromethyl)-s-triazine, 2-(4-methoxy-naphtho-1-yl)-4,6-bis(trichloromethyl)-s-triazine, 2-4-trichloromethyl (piperonyl)-6-triazine, 2-4-trichloromethyl (4′-methoxystyryl)-6-triazine, etc.
The photoinitiator may include carbazole-based compounds, diketone-based compounds, sulfonium borate-based compounds, diazo-based compounds, imidazole-based compounds, non-imidazole-based compounds, etc. in addition to the above compounds.
The photoinitiator may include a peroxide-based compound, an azobis-based compound, etc. as radical polymerization initiators.
Examples of the peroxide-based compound may include ketone peroxides such as methyl ethyl ketone peroxide, methyl isobutyl ketone peroxide, cyclohexanone peroxide, methylcyclohexanone peroxide, acetylacetone peroxide, etc.; diacyl peroxides such as isobutyryl peroxide, 2,4-dichlorobenzoyl peroxide, o-methylbenzoyl peroxide, bis-3,5,5-trimethylhexanoyl peroxide, etc.; hydroperoxides such as 2,4,4,-trimethylpentyl-2-hydroperoxide, diisopropylbenzene hydroperoxide, cumene hydroperoxide, t-butyl hydroperoxide, etc.; dialkyl peroxides such as dicumyl peroxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, 1,3-bis(t-butyloxyisopropyl)benzene, t-butylperoxyvalerate n-butyl ester, etc.; alkyl peresters such as 2,4,4-trimethylpentyl peroxyphenoxyacetate, a-cumyl peroxyneodecanoate, t-butyl peroxybenzoate, di-t-butyl peroxytrimethyl adipate, etc.; and percarbonates such as di-3-methoxybutyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, bis-4-t-butylcyclohexyl peroxydicarbonate, diisopropyl peroxydicarbonate, acetylcyclohexylsulfonyl peroxide, t-butyl peroxyaryl carbonate, etc.
Examples of the azobis-based compound may include 1,1′-azobiscyclohexan-1-carbonitrile, 2,2′-azobis(2,4-dimethylvaleronitrile), 2,2,-azobis(methylisobutyrate), 2,2′-azobis(4-methoxy-2,4-dimethylvaleronitrile), α,α′-azobis(isobutylnitrile), 4,4′-azobis(4-cyanovaleric acid), etc.
The photoinitiator may be used together with a photosensitizer that causes a chemical reaction by absorbing light and thus becoming an excited state and then transferring the energy of light. Examples of the photosensitizer may include tetraethylene glycol bis-3-mercaptopropionate, pentaerythritol tetrakis-3-mercaptopropionate, dipentaerythritol tetrakis-3-mercaptopropionate, etc.
The photoinitiator may be contained in an amount of 0.01 to 10% by weight, for example, 0.1 to 5% by weight based on the total amount of the photosensitive resin composition. When the photoinitiator is contained within the above-described range, curing occurs sufficiently during exposure in the pattern forming process so that excellent reliability may be obtained, heat resistance, light resistance, and chemical resistance of the pattern are excellent, resolution and adhesion are also excellent, and a decrease in transmittance due to an unreacted initiator may be prevented.
All of organic and inorganic pigments and dyes can be used as the colorant.
The colorant may include a red pigment, a green pigment, a blue pigment, a yellow pigment, a black pigment, etc.
Examples of the red pigment may include C.I. Red Pigment 254, C.I. Red Pigment 255, C.I. Red Pigment 264, C.I. Red Pigment 270, C.I. Red Pigment 272, C.I. Red Pigment 177, C.I. Red Pigment 89, etc.
Examples of the green pigment may include halogen-substituted copper phthalocyanine pigments such as C.I. Green Pigment 36, C.I. Green Pigment 7, etc.
Examples of the blue pigment may include copper phthalocyanine pigments such as C.I. Blue Pigment 15:6, C.I. Blue Pigment 15, C.I. Blue Pigment 15:1, C.I. Blue Pigment 15:2, C.I. Blue Pigment 15:3, C.I. Blue Pigment 15:4, C.I. Blue Pigment 15:5, C.I. Blue Pigment 16, etc.
Examples of the yellow pigment may include isoindoline-based pigments such as C.I. Yellow Pigment 139, etc., quinophthalone-based pigments such as C.I. Yellow Pigment 138, etc., and nickel complex pigments such as C.I. Yellow Pigment 150, etc.
Examples of the black pigment may include, for example, lactam black, aniline black, perylene black, titanium black, carbon black, etc.
In addition, the colorant in the photosensitive resin composition according to the embodiment may include pigments, dyes, or combinations thereof. For example, the dyes may include phthalocyanine-based compounds.
The pigments and dyes may be used alone or in a mixture of two or more, but are not limited to examples thereof.
Among them, the black pigment may be used in order to effectively perform light blocking of the light blocking layer. When the black pigment is used, it may be used together with color correcting agents such as anthraquinone-based pigments, perylene-based pigments, phthalocyanine-based pigments, azo-based pigments, etc.
In order to disperse the pigment in the photosensitive resin composition, a dispersant may be used together. Specifically, the pigment may be surface-treated with a dispersant in advance and used, or a dispersant may be added together with the pigment and used during preparation of the photosensitive resin composition.
The dispersant may include a nonionic dispersant, an anionic dispersant, a cationic dispersant, etc. Specific examples of the dispersant may include polyalkylene glycol and an ester thereof, polyoxyalkylene, a polyhydric alcohol ester alkylene oxide adduct, an alcohol alkylene oxide adduct, a sulfonic acid ester, a sulfonic acid salt, a carboxylic acid ester, a carboxylic acid salt, an alkylamide alkylene oxide adduct, alkyl amine, etc., and these may be used alone or in mixtures of two or more.
Examples of commercially available products of the dispersant include DISPERBYK-101, DISPERBYK-130, DISPERBYK-140, DISPERBYK-160, DISPERBYK-161, DISPERBYK-162, DISPERBYK-163, DISPERBYK-164, DISPERBYK-165, DISPERBYK-166, DISPERBYK-170, DISPERBYK-171, DISPERBYK-182, DISPERBYK-2000, DISPERBYK-2001, etc. from BYK; EFKA-47, EFKA-47EA, EFKA-48, EFKA-49, EFKA-100, EFKA-400, EFKA-450, etc. from EFKA Chemical; Solsperse 5000, Solsperse 12000, Solsperse 13240, Solsperse 13940, Solsperse 17000, Solsperse 20000, Solsperse 24000GR, Solsperse 27000, Solsperse 28000, etc. from Zeneka; or PB711, PB821, etc. from Ajinomoto.
The dispersant may be contained in an amount of 0.1 to 15% by weight based on the total amount of the photosensitive resin composition. When the dispersant is contained within the above-described range, stability, developing properties, and patternability of the composition are excellent when preparing the light blocking layer due to excellent dispersibility of the composition.
The pigment may be pretreated using a water-soluble inorganic salt and a wetting agent and used. When the pigment is pretreated and used as described above, the mean particle diameter of the pigment may be refined.
The pretreatment may be performed through a step of kneading the pigment together with a water-soluble inorganic salt and a wetting agent, and a step of filtering and washing the pigment obtained in the kneading step.
The kneading may be performed at a temperature of 40° C. to 100° C., and the filtration and washing may be performed by washing the inorganic salt using water, etc. and then performing filtration.
Examples of the water-soluble inorganic salt may include sodium chloride, potassium chloride, etc., but are not limited thereto.
The wetting agent serves as a medium through which the pigment and the water-soluble inorganic salt may be uniformly mixed to pulverize the pigment easily, and examples of the wetting agent may include alkylene glycol monoalkyl ethers such as ethylene glycol monoethyl ether, propylene glycol monomethyl ether, diethylene glycol monomethyl ether, etc.; and alcohols such as ethanol, isopropanol, butanol, hexanol, cyclohexanol, ethylene glycol, diethylene glycol, polyethylene glycol, glycerin polyethylene glycol, etc., and these may be used alone or in mixtures of two or more.
The pigment that has gone through the kneading step may have a mean particle diameter of 100 nm or less. When the mean particle diameter of the pigment is within the above-described range, a fine pattern may be effectively formed while having excellent heat resistance and light resistance.
The pigment may be contained in an amount of 1 to 40% by weight, more specifically 17 to 35% by weight based on the total amount of the photosensitive resin composition. When the pigment is contained within the above-described range, the color reproduction rate is excellent, and the curability and adhesion of the pattern are excellent.
The solvent may include materials which are compatible with the cardo-based resin, the reactive unsaturated compound, the pigment, the cardo-based compound, and the initiator, but do not react therewith.
Examples of the solvent include alcohols such as methanol, ethanol, etc.; ethers such as dichloroethyl ether, n-butyl ether, diisoamyl ether, methylphenyl ether, tetrahydrofuran, etc.; glycol ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, etc.; cellosolve acetates such as methyl cellosolve acetate, ethyl cellosolve acetate, diethyl cellosolve acetate, etc.; carbitols such as methylethyl carbitol, diethyl carbitol, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol dimethyl ether, diethylene glycol methyl ethyl ether, diethylene glycol diethyl ether, etc.; propylene glycol alkyl ether acetates such as propylene glycol methyl ether acetate, propylene glycol propyl ether acetate, etc.; aromatic hydrocarbons such as toluene, xylene, etc.; ketones such as methyl ethyl ketone, cyclohexanone, 4-hydroxy-4-methyl-2-pentanone, methyl-n-propyl ketone, methyl-n-butyl ketone, methyl-n-amyl ketone, 2-heptanone, etc.; saturated aliphatic monocarboxylic acid alkyl esters such as ethyl acetate, n-butyl acetate, isobutyl acetate, etc.; lactic acid esters such as methyl lactate, ethyl lactate, etc.; oxyacetic acid alkyl esters such as methyl oxyacetate, ethyl oxyacetate, butyl oxyacetate, etc.; alkoxy acetate alkyl esters such as methoxy methyl acetate, methoxy ethyl acetate, methoxy butyl acetate, ethoxy methyl acetate, ethoxy ethyl acetate, etc.; 3-oxypropionic acid alkyl esters such as 3-oxy methyl propionate, 3-oxy ethyl propionate, etc.; 3-alkoxy propionic acid alkyl esters such as 3-methoxy methyl propionate, 3-methoxy ethyl propionate, 3-ethoxy ethyl propionate, 3-ethoxy methyl propionate, etc.; 2-oxypropionic acid alkyl esters such as methyl 2-oxypropionate, ethyl 2-oxypropionate, propyl 2-oxypropionate, etc.; 2-alkoxy propionic acid alkyl esters such as 2-methoxy methyl propionate, 2-methoxy ethyl propionate, 2-ethoxy ethyl propionate, 2-ethoxy methyl propionate, etc.; monooxy monocarboxylic acid alkyl esters of 2-oxy-2-methyl propionic acid esters such as 2-oxy-2-methyl methyl propionate, 2-oxy-2-methyl ethyl propionate, etc., and 2-alkoxy-2-methyl propionic acid alkyls such as 2-methoxy-2-methyl methyl propionate, 2-ethoxy-2-methyl ethyl propionate, etc.; esters such as 2-hydroxyethyl propionate, 2-hydroxy-2-methyl ethyl propionate, ethyl hydroxyacetate, 2-hydroxy-3-methyl methyl butanoate, etc.; and ketonic acid esters such as ethyl pyruvate, etc.
Further, high-boiling point solvents such as N-methylformamide, N,N-dimethylformamide, N-methylformanilide, N-methylacetamide, N,N-dimethylacetamide, N-methylpyrrolidone, dimethyl sulfoxide, benzyl ethyl ether, dihexyl ether, acetylacetone, isophorone, caproic acid, caprylic acid, 1-octanol, 1-nonanol, benzyl alcohol, benzyl acetate, ethyl benzoate, diethyl oxalate, diethyl maleate, γ-butyrolactone, ethylene carbonate, propylene carbonate, and phenyl cellosolve acetate may also be used.
Considering compatibility and reactivity, glycol ethers such as ethylene glycol monoethyl ether, etc.; ethylene glycol alkyl ether acetates such as ethyl cellosolve acetate, etc.; esters such as ethyl 2-hydroxypropionate, etc.; carbitols such as diethylene glycol monomethyl ether, etc.); and propylene glycol alkyl ether acetates such as propylene glycol methyl ether acetate, propylene glycol propyl ether acetate, etc. among the above solvents may be used.
The solvent may be contained as a balance amount based on the total amount of the photosensitive resin composition, and specifically in an amount of 40 to 90% by weight. When the solvent is contained within the above-described range, the processability when preparing the pattern layer is excellent as the photosensitive resin composition has an appropriate viscosity.
In order to prevent stains or spots during application, to improve leveling performance, and to prevent the generation of residues due to nondevelopment, the photosensitive resin composition may further include additives including: malonic acid; 3-amino-1,2-propanediol; a silane-based coupling agent containing a vinyl group or (meth)acryloxy group; a leveling agent; a fluorine-based surfactant; a radical polymerization initiator; etc.
For example, the photosensitive resin composition may further include a silane-based coupling agent having a reactive substituent such as a vinyl group, a carboxyl group, a methacryloxy group, an isocyanate group, an epoxy group, or the like in order to improve adhesion to a substrate, etc.
Examples of the silane-based coupling agent may include trimethoxysilyl benzoic acid, γ-methacryloxypropyl trimethoxysilane, vinyl triacetoxysilane, vinyl trimethoxysilane, γ-isocyanate propyl triethoxysilane, γ-glycidoxy propyl trimethoxy silane, β-epoxy cyclohexyl ethyl trimethoxy silane, etc., and these may be used alone or in mixtures of two or more.
The silane-based coupling agent may be contained in an amount of 0.01 part by weight to 10 parts by weight based on 100 parts by weight of the photosensitive resin composition. When the silane-based coupling agent is contained within the above-described range, adhesion, storability, etc. are excellent.
In addition, the photosensitive resin composition may further include a surfactant, for example, a fluorine-based surfactant for the effects of improving coating properties and preventing creation of defects, if necessary.
The fluorine-based surfactant may include fluorine-based surfactants commercially available under the names of: BM-1000®, BM-1100®, etc. from BM Chemie; Megaface F 142D®, Megaface F 172®, Megaface F 173®, Megaface F 183®, Megaface F 554®, etc. from Dainippon Ink Kagaku Kogyo; Fluorad FC-135®, Fluorad FC-170C®, Fluorad FC-430®, Fluorad FC-431®, etc. from Sumitomo 3M; Saffron S-112®, Saffron S-113®, Saffron S-131®, Saffron S-141®, Saffron S-145®, etc. from Asahi Grass; and SH-28PA®, SH-190®, SH-193®, SZ-6032®, SF-8428®, etc. from Toray Silicone.
The surfactant may be used in an amount of 0 001 to 5 parts by weight based on 100 parts by weight of the photosensitive resin composition. When the surfactant is contained within the above-described range, coating uniformity may be secured, stains may not occur, and wetting to the glass substrate is excellent. In addition, a certain amount of other additives such as antioxidants and stabilizers may be added to the photosensitive resin composition within a range that does not impair physical properties.
In another embodiment, patterning may be performed on the pixel separation part of the organic light emitting device electrode using the photosensitive resin composition described above.
Hereinafter, Synthesis Examples and Examples according to the present disclosure will be described in detail, but Synthesis Examples and Examples of the present disclosure are not limited thereto.
25 g of 9,9-bis [4-(glycidyloxy)phenyl] fluorene of Formula 8 below was obtained by adding 20 g of 9,9′-bisphenol fluorene (Sigma Aldrich), 8.67 g of glycidyl chloride (Sigma Aldrich), and 30 g of anhydrous potassium carbonate together with 100 mL of dimethylformamide into a 300 mL 3-neck round-bottom flask having a distillation tube installed thereon, raising the temperature to 80° C. to perform reaction for 4 hours, lowering the temperature to 25° C. to filter the reaction solution, adding the filtrate dropwise to 1,000 mL of water while performing stirring, filtering the precipitated powder, washing the filtered precipitated powder with water, and drying it under reduced pressure at 40° C. As a result of purity analysis of the obtained powder by HPLC, a purity of 98% was shown.
25 g (54 mmol) of Compound 1 obtained in Synthesis Example 1, 8 g of acrylic acid (Daejung Chemicals & Metals Co., Ltd.), 0.2 g of benzyltriethylammonium chloride (Daejung Chemicals & Metals Co., Ltd.), and 0.2 g of hydroquinone (Daejung Chemicals & Metals Co., Ltd.) together with 52 g of propylene glycol methyl ether acetate (Sigma Aldrich) were added into a 300 mL 3-neck round-bottom flask having a distillation tube installed thereon, and stirring was performed at 110° C. for 6 hours. After completion of the reaction, 8 g of biphenyltetracarboxylic dianhydride (Mitsubishi Gas) and 1.8 g of tetrahydrophthalic acid (Sigma Aldrich) were added thereto, and then stirring was performed again at 110° C. for 6 hours. After completion of the reaction, a cardo-based binder resin having a molecular weight of 4,580 and a solid content of 45% could be obtained as a result of recovering the reaction solution and performing analysis.
A dispersion could be obtained by dispersing 15 g of Irgaphor Black S 100 CF (black pigment/BASF), 8.5 g of Disperbyk 163 (BYK), and 6.5 g of SR-3613 (SMS) together with 70 g of propylene glycol methyl ether acetate for 10 hours using a paint shaker (Asada) of 100 g of zirconia beads with a diameter of 0.5 mm (Toray).
Photosensitive resin composition solutions were prepared with the compositions as shown in Table 1 below.
Specifically, after the initiator was dissolved in a solvent, and then stirring was performed at room temperature, and then a binder resin and a polymerizable compound were added thereto to perform stirring at room temperature. Subsequently, a colorant and other additives were added to the obtained reactants, and stirring was performed at room temperature. Subsequently, the reaction products were filtered three times to remove impurities, thereby preparing photosensitive resin compositions.
The method for preparing a negative pixel defining layer (PDL) using the photosensitive resin composition is as follows.
A coating film is formed by removing a portion of the solvent using vacuum chamber dry (VCD) after applying a photosensitive resin composition to a certain thickness onto a substrate on which a washed 10 cm×10 cm metal has been deposited using a spin coater. The photosensitive resin composition is coated to a thickness of 2.0 micrometers to 1.7 micrometers after VCD to form the film.
In order to remove the solvent contained in the obtained coating film, the film is heated on a hot plate at 80° C. to 120° C. for 50 seconds to 200 seconds. A certain amount of the solvent in the relevant process may be removed, thereby reducing contamination of a pixel-shaped mask and forming a clean type pattern during the exposure step of the relevant process.
After interposing a pixel-shaped mask to form a pattern required for the obtained coating film and obtain a constant thickness, a pattern may be formed by irradiating an active ray of 190 nm to 600 nm, preferably a light source of a metal or LED lamp having a ghi-line through an exposure machine. The exposure amount irradiated for pattern formation is 20 to 150 mJ/cm2, and it is a negative-type photoresist material to be formed.
Following the exposure step, when washing is performed using ultrapure water (DI water) after development is performed by a method of dipping the coating film with a 2.38 wt % TMAH (tetramethylammonium hydroxide) developer at 23±2° C. for a certain period of time (minutes), the non-exposed portion is dissolved and removed so that only the exposed portion remains to form an image pattern.
In order to obtain the image pattern obtained by the development, post-heat treatment (post-baking) is performed in an oven at 210 to 300° C. for 30 to 120 minutes to completely remove the solvent and ultrapure water (DI water, moisture) which is absorbed into the coating film during the development step, the pattern is cured to form a film, and then roughness and moisture content are measured.
As a sample for roughness measurement, an evaluation substrate including a negative pixel defining layer formed through coating, exposure, development, and post-heat treatment with a composition containing a colorant on a glass surface could be obtained. The physical properties of the relevant evaluation substrate were measured using an atomic force microscope (AFM, Park Systems/XE-100), and in non-contact mode, the measurement was performed at a scan rate of 0.3 (Hz), a set point of 11.26 nm, and an area of 2 μm×2 μm.
After forming a colored pattern through the preparation process, a common layer (HTL) was deposited to a thickness of 120 to 140 nm in a deposition machine. 100 cut surfaces were formed on the deposited specimen using cross-cut, and then NICHIBAN's release tape (CT-24) was attached on the cut surfaces without bubbles. Tape peeling was performed with a constant force of a speed of 300 mm/min after fixing a tape to a 90° jig using UTM (QM 100S) equipment that is a manufactured product of Coretech Korea Co., Ltd. The number of tearings on the cut surfaces after peeling was measured compared to before the peeling test to check the adhesion.
The surface roughness and the film peeling (adhesion) with the common layer (HTL) were compared using the substrates obtained in the process after the post-heat treatment step. Referring to Comparative Examples 1 to 6 in Table 2, it could be confirmed that the surface roughness was 1.48 nm or less as the post-heat treatment temperature was high and the time was increased. When the surface roughness after the post-heat treatment was lowered to 1.48 nm or less, the adhesion with the common layer (HTL) decreased as in the adhesion, and thus the number of peelings increases.
After forming a pattern on the substrate using the photosensitive resin composition of Example 1 through the steps (1), (2), (3), (4), and (5) above, the moisture content in an area of 10 cm×10 cm was measured. A film was formed to a coating thickness of 1.45 to 1.55 μm after post-heat treatment, and the weight after coating and post-heat treatment of the photosensitive resin composition on a 10 cm×10 cm substrate is 11 to 12 g. Moisture was collected from the relevant substrate at 120° C. for 5 minutes using Brookfield's Vapor Pro XL. The samples were samples in which the process conditions such as the development time and temperature in the development step and the heating temperature and heat treatment time in the post-heat treatment step were changed, and the measured amounts of moistures measured respectively were compared.
When comparing the detection amounts of outgas, the minimum and maximum outgas detection amounts were confirmed under each process condition, and in order to evaluate device reliability after forming a patterned substrate for a pixel defining layer (PDL) depending on the respective conditions, the organic material was deposited to confirm reliability verification factors such as high temperature operation, pixel shrinkage, dark spots, and lifespan.
As disclosed in
The moisture generation amounts were measured and compared using the substrates obtained in the process after the post-heat treatment step. Referring to Comparative Examples 7 to 12 in Table 3, it could be confirmed that the moisture contents after post-heat treatment were 50 ppm or more even though the post-heat treatment time was increased due to the low post-heat treatment temperature. It was confirmed that when the moisture contents after the post-heat treatment increased, dark spots appeared during device operation as shown in
The above description is merely illustrative of the present disclosure, and those skilled in the art to which the present disclosure pertains will be able to make various modifications without departing from the essential characteristics of the present disclosure.
Accordingly, the embodiments disclosed in this specification are for illustrative purposes only and are not intended to limit the present disclosure, and the spirit and scope of the present disclosure are not limited by these embodiments. The scope of protection of the present disclosure should be interpreted in accordance with the claims, and all technologies within the scope equivalent thereto should be interpreted as being included in the scope of rights of the present disclosure.