Method for processing a silver halide color photographic material

FIELD OF THE INVENTION
The present invention relates to a method for processing an exposed silver halide color photographic material (hereinafter referred to as a color light-sensitive material). More particularly, the present invention relates to an improved processing method which accelerates the bleaching function, thus shortening the processing time while conducting sufficient bleaching, and provides a color photographic image of excellent image quality.
BACKGROUND OF THE INVENTION
The fundamental steps of processing color light-sensitive materials generally include a color developing step and a silver removing step (e.g., bleaching step, bleach-fixing step, etc.). Thus, an imagewise exposed silver halide color photographic material undergoes a color developing step, where silver halide is reduced with a color developing agent to produce silver and the oxidized color developing agent in turn reacts with a color former to yield a dye image. Subsequently, the color photographic material undergoes a silver removing-step, where silver produced in the developing step is oxidized with an oxidizing agent (usually called a bleaching agent), and is dissolved away with a silver ion complexing agent, usually called a fixing agent. Therefore, only a dye image is formed in the thus processed photographic material. In addition to the above described two fundamental steps of color development and silver removal, actual development processing involves auxiliary steps for maintaining the photographic and physical quality of the resulting image or for improving the preservability of the image. Some examples of these auxiliary steps include a hardening bath for preventing a light-sensitive layer from being excessively softened during photographic processing, a stopping bath for effectively stopping the developing reaction, an image stabilizing bath for stabilizing the image, and a layer removing bath for removing the backing layer on the support.
The above described silver removal step may be conducted in two basic ways: one way uses two steps individually employing a bleaching bath and a fixing bath; and the other way is more simple and is conducted in one step employing a bleach-fixing bath containing both a bleaching agent and a fixing agent for the purpose of accelerating the processing and elimination of labor.
In recent years, bleach processing using a ferric ion complex salt (for example, aminopolycarboxylic acid ferric ion complex salt, particularly iron (III) ethylenediaminetetraacetate complex salt) as a major bleaching component has mainly been employed in processing color photographic light-sensitive materials in view of the acceleration and simplification of the bleaching provided and the need to prevent environmental pollution.
However, ferric ion complex salts have a comparatively low oxidizing power and, therefore, have generally insufficient bleaching power. A bleaching or bleach-fixing solution containing such a complex salt as a bleaching agent can attain some desirable objects when bleaching or bleach-fixing a low speed silver halide color photographic light-sensitive material containing, for example, a silver chlorobromide emulsion as a major component. However, such a solution provides insufficient desilveration due to insufficient bleaching power or requires a long time to bleach when processing a high speed, spectrally sensitized silver halide color photographic light-sensitive material containing a silver chlorobromoiodide emulsion or a silver iodobromide emulsion as a major component, particularly color reversal light-sensitive materials for photography or color negative light sensitive materials for photography comprising an emulsion containing a larger amount of silver.
In the color light-sensitive materials, sensitizing dyes are generally employed for the purpose of spectral sensitization. In particular, when a silver halide emulsion containing a large amount of silver or tabular grains having a high aspect ratio is employed in order to achieve high sensitivity, a problem occurs in that sensitizing dyes adsorbed on the surfaces of silver halide grains interfere with the bleaching of silver formed during the development step.
Known bleaching agents, other than ferric ion complex salts, include persulfates. Persulfates are usually used in a bleaching solution together with a chloride. However, this type of persulfate-containing bleaching solution has less bleaching ability than ferric ion complex salts, thus requiring a substantially long period of time for bleaching.
As described above, bleaching agents which do not cause environmental pollution or corrode vessels and apparatus usually have only a weak bleaching power. Hence, it is desired to enhance the bleaching power of a bleaching solution or a bleach-fixing solution containing a weak bleaching agent, particularly a ferric ion complex salt or a persulfate.
In order to increase the bleaching power of a bleaching solution or a bleach-fixing solution containing a ferric ion complex salt such as iron (III) ethylene-diaminetetraacetate as a bleaching agent, it has been heretofore proposed to add various bleach accelerating agents to the processing bath.
Examples of such bleach accelerating agents include various mercapto compounds as described, for example, in U.S. Pat. No. 3,893,858, British Patent 1,138,842 and JP-A-53-141623 (the term "JP-A" as used herein means an "unexamined published Japanese patent application"), compounds having a disulfide bond as described, for example, in JP-A-53-95630, thiazolidine derivatives as described, for examples, in JP-B-53-9854 (the term "JP-B" as used herein means an "examined Japanese patent publication), isothiourea derivatives as described, for example, in JP-B-53-94927, thiourea derivatives as described, for example, in JP B-45-8506 and JP-B-49-26506, thioamide compounds as described, for example, in JP-A-49-42349, and dithiocarbamates as described, for example, in JP-A-55-26506.
Among these bleach accelerating agents, although some compounds certainly exhibit a bleach accelerating function, their effects are not always sufficient. Further, these compounds are extremely unstable in a processing solution, particularly in a bleach-fixing solution and lose their effects in a short period of time. Therefore, they are not always suitable for practical use.
Other bleach accelerating agents, for example, onium compounds as described, for example, in U.S. Pat. No. 3,748,136, phenylene linking ammonium salts as described, for example, in JP-B-54-12056, and amine compounds as described, for example, in U.S. Patent 4,552,834 are also known. However, these compounds have only weak bleach accelerating effects and they are not always suitable for practical use, although they are stable in a bleaching solution or a bleach-fixing solution.
Moreover, the compounds as described in JP-B-60-24936 do not always show a satisfactory bleach accelerating effect, although they do exhibit a certain degree of bleach accelerating effect. Further, they often form stains in the case of continuous processing.
As described above, many of these bleach accelerating agents do not always show a satisfactory bleach accelerating effect, and some of them lack stability in the processing solution although they exhibit an excellent bleach accelerating effect. Therefore, they provide a processing solution having only a short effective life or which cannot be stored for a long time.
The above-mentioned compounds as described in JP -B-60-24936 show a certain degree of bleach accelerating effect and are capable of being stored for a relatively long period of time. However, such compounds, as noted, still have a problem in that they often form stains on the photographic material thus-processed.
SUMMARY OF THE INVENTION
An object of the present invention is, therefore, to provide a method for processing a color photographic light-sensitive material which does not release environmentally harmful materials, which meets the requirement of preventing environmental pollution and which has excellent bleaching speed.
Another object of the present invention is to provide a processing method involving a bleaching or bleach-fixing step in which enhanced bleaching power is attained without deteriorating other photographic properties, using a bleaching agent having a weak bleaching power, in particular, a ferric ion complex salt or a persulfate.
A further object of the present invention is to provide a bleaching process for a color photographic light-sensitive material which uses a bleaching or bleach-fixing solution showing increased bleaching speed and having excellent stability.
A still further object of the present invention is to provide a processing method which can rapidly bleach or bleach-fix a color photographic light-sensitive material having photographing speed.
Yet another object of the present invention is to provide a method which can rapidly bleach or bleach-fix a color photographic light-sensitive material without the formation of stains on the photographic material thus-processed.
Other objects and advantages of the present invention will become apparent from the following description and examples.
These and often objects and advantages of the present invention are attained by a method for processing a silver halide color photographic material comprising after development, bleaching or bleach-fixing an imagewise exposed silver halide color photographic material in the presence of at least one compound represented by formula (I): ##STR2## wherein R.sup.1 and R.sup.2, which may be the same or different, each represents a hydrogen atom or an alkyl group, or R.sup.1 and R.sup.2 may combine with each other to form a heterocyclic ring; A.sup.1 and A.sup.2, which may be the same or different, each represents an alkylene group having from 2 to 5 carbon atoms which may be substituted; and n represents an integer from 2 to 6.
DETAILED DESCRIPTION OF THE INVENTION
The method according to the present invention comprises subjecting an imagewise exposed silver halide color photographic material to color development, then to bleaching and fixing or, alternatively, to bleach-fixing.
The compounds represented by formula (I) are described in detail below.
In formula (I), R.sub.1 and R.sub.2, which may be the same or different, each represents a hydrogen atom or an alkyl group. The alkyl group is preferably an unsubstituted alkyl group having preferably from 1 to 10 carbon atoms, particularly preferably from 1 to 5 carbon atoms. Alternatively, R.sub.1 and R.sub.2 may combine with each other to form a heterocyclic ring. The heterocyclic group thus-formed includes, for example, a piperidyl group, a pyrrolidinyl group, a morpholino group, a imidazolinyl group, a pyrazolinyl group, and an indolinyl group. These heterocyclic groups have preferably from 1 to 10 carbon atoms and more preferably from 1 to 5 carbon atoms.
A.sup.1 and A.sup.2, which may be the same or different, each represents an alkylene group having generally from 2 to 5 carbon atoms and preferably from 2 to 4 carbon atoms, which may be substitued. Suitable examples of the substituent for the alkylene group include a hydroxyl group, an amino group and a carboxyl group. Specific examples of the alkylene group represented by A.sup.1 or A.sup.2 include ethylene, propylene, trimethylene, tetramethylene, pentamethy lene, 2 -hydroxytrimethyle ne, a nd aminotrimethylene. Ethylene and trimethylene are preferred.
n represents an integer from 2 to 6 and preferably is 2 or 3 in view of prevention of deposition of the compound at room temperature. When n is 7 or more, a problem of decrease in solubility may occur and it is not preferred to use such compounds in practice. On the other hand, when n is 1 or less, such compounds are not preferred in view of their poorer bleach accelerating ability. The (S--A.sup.2) moiety in formula (I) represents a repeating unit and the groups represented by A.sup.2 in this repeating unit may be the same or different in the same compound.
The compound represented by formula (I) used in the present invention as a bleach accelerating agent can be incorporated only into either a bleaching solution, a bleach-fixing solution (including replenishers thereof) or a prebath thereof. Alternatively, the compound can be previously incorporated into the color light-sensitive material and then introduced into a bleaching solution or a bleach-fixing solution. The amount of the compound added to the bleaching solution, bleach-fixing solution or prebath thereof is preferably from 1.times.10.sup.-5 to 1.times.10.sup.1 mol, more preferably from 1.times.10.sup.-3 to 2.times.10.sup.2 mol, and most preferably from 2.times.10.sup.-3 to 1.times.10.sup.-2 mol, per liter of the processing solution. When the compound is incorporated into the color light-sensitive material, the amount thereof is preferably from 1.times.10.sup.-4 to 1.times.10.sup.-2 mol, and more preferably from 2.times.10.sup.-4 to 5.times.10.sup.-3 mol, per m.sup.2 of the color light-sensitive material.
The compound represented by formula (I) can be employed individually or as a combination of two or more thereof as the bleach accelerating agent.
An attempt of employing a thioether compound similar to the compound of the formula (I) used in the present invention as a bleach accelerating agent has been hitherto made as described in JP-B-60-24936. In JP-B-60-24986, although compounds having 2 to 3 thioether bonds are disclosed, the amino compounds described which, on superficial examination appear similar to the compounds according to the present invention, have only two thioether bonds.
On the contrary, the amino compounds according to the present invention are characterized by containing many (i.e., 3 to 7) thioether bonds and have distinctly superior bleach accelerating effect in comparison with the compounds as described in JP-B-60-24936. Further, the examples of amino compounds described in JP-B-60-24936 having two thioether bonds show a certain degree of bleach accelerating effect, but often form stains on the color photographic material when continuously processed. In contrast, the compounds according to the present invention have a very large bleach accelerating effect and do not cause stain on the photographic material processed.
The compounds according to the present invention exhibit an extraordinarily large bleach accelerating ability and are stable in the bleaching solution or the bleach-fixing solution. Therefore, they are satisfactorily applicable to continuous processing for a long period of time using an automatic developing machine as conventionally practiced.
Specific examples of the compounds represented by formula (I) used in the present invention are set forth below but the present invention should not be construed as being limited thereto. ##STR3##
The compounds according to the present invention can be easily synthesized with reference to methods generally well known. Specific methods for synthesis of the compounds are illustrated below. The percentage of solution is by weight.
SYNTHESIS OF COMPOUND (1)
To 150 ml of ethanol were added 11.8 g of bismercaptoethylsulfide and 17.8 g of 2-chloroethylamine hydrochloride, to the mixture was added 59.2 g of a 28% methanol solution of sodium methoxide under a nitrogen atmosphere and then the mixture was refluxed by heating for 3 hours. After removing the resulting inorganic salt by filtration, to the filtrate were added 25 ml of a 25% ethanol solution of hydrogen chloride and then 200 ml of ethyl acetate. The crystals thus-deposited were collected by filtration and recrystallized from a mixture of 300 ml of methanol and 200 ml of ethyl acetate to obtain compound (1) as dihydrochloride. Yield 17.5 g (73%).
SYNTHESIS OF COMPOUND (11)
To 150 ml of an ethanol solution containing 5 g of 1, 4, 8, 11-tetrathiaundecane which was synthesized by the method as described in J. Am. Chem. Soc., Vol. 91, page 4694(1969) and 6.3 g of dimethylaminoethyl chloride hydrochloride, was added 17 g of a 28% methanol solution of sodium methoxide under a nitrogen atmosphere and the mixture was refluxed by heating for 3 hours. After removing the resulting inorganic salt by filtration, to the filtrate were added 15 ml of a 25% ethanol solution of hydrogen chloride and then added 200 ml of ethyl acetate. The crystals thus-deposited were collected by filtration and recrystallized from a mixture of 100 ml of ethanol and 250 ml of ethyl acetate to obtain compound (11) as dihydrochloride. Yield: 5.5 g(55%).
SYNTHESIS OF COMPOUND (36)
1, 4, 7, 10, 13, 16 hexathiahexadecane was synthesized with reference to the method as described in J. Am. Chem. Soc., Vol. 91, page 4694(1969). To a mixture of 10 g of the above-described compound, 75 ml of ethyl acetate and 75 ml of ethanol were added 23.3 g of a 28% methanol solution of sodium methoxide and then added 8.6 g of dimethylaminoethyl chloride hydrochloride under a nitrogen atmosphere and the mixture was refluxed by heating for 3 hours. 200 ml of water was added to the reaction mixture, extracted twice with chloroform, and the extract was concentrated under a reduced pressure. To the residue were added 100 g of methanol and 15 ml of a 25% ethanol solution of hydrogen chloride to obtain Compound (36) as dihydrochloride. Yield: 5.1 g(30%).
Other compounds can be synthesized in a similar manner.
The present invention exhibits its effects in any processing method wherein a bleaching bath, a bleach-fixing bath and a fixing bath are employed in combination as a desilvering step. Suitable examples of the desilvering steps are set forth below, but the present invention is not to be construed as being limited thereto.
No. 1 Bleaching--Fixing
No. 2 Bleaching--Washing with water--Fixing
No. 3 Bleaching--Bleach-fixing
No. 4 Bleaching--Bleach-fixing--Fixing
No. 5 Fixing--Bleach-fixing
No. 6 Bleach-fixing
Of the above-described types of desilvering steps, No. 6 is most preferred.
Further, the desilvering step is ordinarily conducted after the development step, and a bath for washing with water or bleach acceleration may be provided between developing step and the desilvering step. It is preferred in view of a rapid processing that the desilvering step is carried out after immediately the development step.
Moreover, each processing step is preferably performed in an co-current or counter-current multistage processing system. Particularly, a two-stage or three-stage counter-current system is preferred.
Any known bleaching agent can be employed as a bleaching agent in the bleaching solution or bleach-fixing solution of the present invention. In particular, an aminopolycarboxylic acid-ferric complex salt or a persulfate is preferably employed in the bleaching solution, and an aminopolycarboxylic acid-ferric complex salt is preferably employed in the bleach-fixing bath. The aminopolycarboxylic acid-ferric complex salt is a complex of ferric ion and an aminopolycarboxylic acid or a salt thereof.
Representative examples of the aminopolycarboxylic acids are set forth below, but the present invention should not be construed as being limited thereto.
A-1 : Ethylenediaminetetraacetic acid
A-2 : Diethylenetriaminepentaacetic acid
A-3 : 1,3-Diaminopropanetetraacetic acid
A-4 : 1,2-Diaminopropanetetraacetic acid
A-5 : Ethylenediamine-N-(.beta.-oxyethyl)-N,N',N'-triacetic acid
A-6 : Nitrilotriacetic acid
A-7 : 1,2-Cyclohexanediaminetetraacetic acid
A-8 : Iminodiacetic acid
A-9 : Dihydroxyethylglycine
A-10: Ethyl ether diaminetetraacetic acid
A-11: Glycol ether diaminetetraacetic acid
A-12: Ethylenediaminetetrapropionic acid
Of these compounds, A-1 to A-3, A-7, A-8 and A-11 are particularly preferred.
The aminopolycarboxylic acid-ferric complex salt may be used in the form of a complex salt or may be formed in a solution by using an aminopolycarboxylic acid together with a ferric salt such as a ferric sulfate, ferric nitrate, ferric chloride, ferric ammonium sulfate and ferric phosphate. When the complex salt is used in the form of a complex salt, one, or two or more of the complex salts may be employed. On the other hand, when a complex salt is formed in the solution by using a ferric salt and an aminopolycarboxylic acid, one, or two or more ferric salts may be used. Further, one, or two or more aminopolycarboxylic acids may also be employed. In any case, it is preferred that an aminopolycarboxylic acid is used in an excess amount of what is necessary to form a ferric ion complex salt.
The aminopolycarboxylic acid and ferric complex salt thereof is preferably employed usually in the form of an alkali metal salt or an ammonium salt. Particularly, an ammonium salt thereof is preferred in view of the solubility.
Further, the bleaching solution or bleach-fixing solution containing the ferric ion complex according to the present invention may further contain metal ion complex salts other than iron ion complex salt, such as cobalt ion complex salt and copper ion complex salt.
Suitable examples of the persulfates used in the present invention include an ammonium salt, a potassium salt and a sodium salt thereof.
Furthermore, a compound conventionally known as a bleach accelerating agent can also be added to the bleaching solution, bleach-fixing solution or prebath thereof in addition to the bleach accelerating agent according to compounds represented by formula (I) of the present invention. Suitable examples of such bleach accelerating agents include compounds having a mercapto group or a disulfide bond as described, for example, in U.S. Pat. No. 3,893,858, German Patent 1,290,812, British Patent 1,138,842, JP-A-53-95630 and Research Disclosure, No. 17129 (July, 1978); thiazolidine derivatives as described in JP-A-50-140129; thiourea derivatives as described in U.S. Pat. No. 3,706,561, iodides as describe in JP-A-58-16235; polyethylene oxides as described in German Patent 2,748,430; and polyamine compounds as described in JP-B-45-8836. The mercapto compounds as described in British Patent 1,138,842 are particularly preferred.
These bleach accelerating agents can also be added to a bath preceding the processing solution having a bleaching ability according to the present invention.
In addition to the bleaching agent and the bleach accelerating compounds described above, the bleaching solution according to the present invention can contain rehalogenating agents, for example, bromides such as potassium bromide, sodium bromide and ammonium bromide and chlorides such as potassium chloride, sodium chloride and ammonium chloride. The amount of the rehalogenating agent is generally from 0.1 to 5 mol, preferably from 0.5 to 3 mol per liter of the bleaching solution.
Further, other additives that have a pH buffering ability and are known to be used generally in a bleaching solution can be employed. For example, one or more inorganic acids, organic acids and their salts such as nitrates (e.g., sodium nitrate and ammonium nitrate), boric acid, borax, sodium metaborate, acetic acid, sodium acetate, sodium carbonate, potassium carbonate, phosphorous acid, phosphoric acid, sodium phosphate, citric acid, sodium citrate and tartaric acid can be added to the solution.
In the present invention, when a bleaching solution is used, the amount of the bleaching agent is from 0.05 to 1 mol and preferably from 0.1 to 0.5 mol, per liter of the bleaching solution.
The pH of the bleaching solution is generally from 4.0 to 8.0 and preferably from 5.0 to 6.5 in case of using an aminopolycarboxylic acid-ferric complex salt and is generally from 0.5 to 8.0 and preferably from 2.0 to 4.0 in case of using a persulfate. The temperature of the bleaching solution is usually from 10 to 60.degree. C., preferably from 30 to 50.degree. C., and more preferably from 35 to 45.degree. C. The amount of replenishment for the bleaching solution is generally from 50 to 2,000 ml and preferably from 100 to 500 ml, per m.sup.2 of the color light-sensitive material.
In the present invention, when a bleach-fixing solution is used, the amount of the bleaching agent in the bleach-fixing solution is generally from 0.05 to 0.5 mol and preferably from 0.1 to 0.4 mol, per liter of the solution.
Further, in the bleach-fixing solution, thiosulfates such as sodium thiosulfate, ammonium thiosulfate, sodium ammonium thiosulfate and potassium thiosulfate; thiocyanates such as sodium thiocyanate, ammonium thiocyanate and potassium thiocyanate; thiourea; and thioethers are employed as fixing agents. The amount of the fixing agents used is generally from 0.3 to 3 mol and preferably from 0.5 to 2 mol, per liter of the bleach-fixing solution.
The bleach-fixing solution further may contain compounds which are added to the above bleaching solution in addition to the bleaching agents and the fixing agents as described above. The bleach-fixing solution can contain preservatives such as sulfites (e.g., sodium sulfite, potassium sulfite and ammonium sulfite), hydroxylamines, hydrazines and aldehyde compound-bisulfite adducts (e.g., acetaldehyde-sodium bisulfite adduct). Further, various fluorescent brightening agents, deforming agents, surface active agents, polyvinyl pyrrolidone, and organic solvents (e.g. methanol) may be added to the bleach-fixing solution.
The pH of the bleach-fixing solution is generally from 4.0 to 9.0, preferably from 5.0 to 8.0, and more preferably from 6.0 to 7.5. The preferred temperature of the bleach-fixing solution is the same as that described for the above bleaching solution.
The amount of replenishment for the bleach-fixing solution is preferably from 300 to 3,000 ml and more preferably from 300 to 1,000 ml, per m2 of the color light-sensitive material.
The compound represented by formula (I) according to the present invention can also be used in a method employing a bleaching-bleach fixing step as described in JP-A-61-75352. In such a case, the bleach accelerating compound may be added either to a bleaching solution, a bleach-fixing solution or to both.
In the processing method of the present invention, the fixing solution may contain any of compounds which are described above for the bleach-fixing solution.
The pH of the fixing solution is generally from 3.0 to 9.0 and preferably from 5.0 to 8.0, and the processing time is preferably from 20 sec. to 10 min. and more preferably from 30 sec. to 4 min. The amount of the fixing agent used and the preferred temperature of the fixing solution are same as those described for the above bleach-fixing solution.
When the bleaching, bleach-fixing or fixing step is directly followed by a water washing or stabilizing step, a part or all of over-flow solution therefrom is preferably introduced into the bleaching, bleach-fixing or fixing solution.
The color developing solution used in the present invention contains a known aromatic primary amine color developing agent. Preferred examples thereof are p-phenylenediamine derivatives. Typical examples of the p-phenylenediamine derivative used are set forth below, but the present invention should not be construed as being limited thereto.
D-1: N,N-Diethyl-p-phenylenediamine
D-2: 2-Amino-5-diethylaminotoluene
D-3: 2-Amino-5-(N-ethyl-N-laurylamino)toluene
D-4: 4-[N-Ethyl-N-(.alpha.-hydroxyethyl)amino]aniline
D-5: 2-Methyl-4-[N-ethyl]N-(.beta.-hydroxyethyl)amino]aniline
D-6: 4-Amino-3-methyl-N-ethyl-N-[.beta.-(methanesulfonamido)ethyl]aniline
D-7: N-(2-Amino-5-diethylaminophenylethyl)methanesulfonamide
D-8: N,N-Dimethyl-p-phenylenediamine
D-9: 4 Amino-3-methyl-N-ethyl-N-methoxyethylaniline
D-10: 4-Amino-3-methyl-N-ethyl-N-.beta.-ethoxyethylaniline
D-11: 4-Amino-3-methyl-N-ethyl-N-.beta.butoxyethylaniline
Of these p-phenylenediamine derivatives, D-5 is particularly preferred.
These p-phenylenediamine derivatives may be in the form of salts such as sulfates, hydrochlorides, sulfites, or p-toluenesulfonates.
The aromatic primary amine developing agent is preferably used in an amount of generally from about 0.1 g to about 20 g and more preferably from about 0.5 g to about 10 g per liter of the developing solution.
Also, the color developing solution used in the present invention may contain, if desired, sulfites such as sodium sulfite, potassium sulfite, sodium bisulfite, potassium bisulfite, sodium metasulfite, and potassium metasulfite, or carbonyl-sulfite adducts, as preservatives.
However, in order to increase the color forming property of the color developing solution, it is preferred that the color developing solution substantially does not contain sulfite ion. The term "substantially not contain" means that the color developing solution contains sulfite ion in an amount of 0.5 g or less and preferably 0.2 g or less calculated as sodium sulfite per liter of the solution. It is more preferred that the color developing solution does not contain sulfite ion at all.
Further, it is preferred to add, as compounds capable of directly preservating the color developing agent, various hydroxylamines, hydroxamic acids as described in JP-A-63-43138, hydrazines and hydrazides as described in European Patent 170,756, phenols as described in JP-A-63-44657 and JP-A-63-58443, .alpha.-hydroxyketones and .alpha.-aminoketones as described in JP-A-63-44656, and/or various saccharides as described in JP-A-63-36244 to the color developing solution. Moreover, together with the above described compounds, monoamines as described in JP-A-63-4235, JP-A-63-24254, JP-A-63-21647, JP-A-63-146040, JP-A-63-27841 and JP-A-63-25654; diamine as described in JP-A-63-30845, JP-A-63-146040 and JP-A-63-43139; polyamines as described in JP-A-63-21647 and JP-A-63-26655; polyamines as described in JP-A-63-44655, nitroxy radicals as described in JP-A-63-53551; alcohols as described in JP-A-63-43140 and JP-A-63-53549; oximes as described in JP-A-63-56654; and tertiary amines as described in European Patent 266,797 are preferably employed.
Other preservatives such as various metals as described in JP-A-57-44148 and JP-A-57-53749, salicylic acids as described in JP-A-59-180588, alkanolamines as described in JP-A-54-3532, polyethyleneimines as described in JP-A-56-94349, aromatic polyhydroxyl compounds as described in U.S. Pat. No. 3,746,544, etc. may be incorporated into the color developing solution, if desired. Particularly, the addition of aromatic polyhydroxy compounds is preferred.
The color developing solution used in the present invention has a pH which ranges preferably from 9 to 12 and more preferably from 9 to 11.0. The color developing solution may also contain any of the compounds that are known to be usable as components of conventional developing solutions.
In order to maintain the pH within the above-described range, various kinds of buffers are preferably employed. Specific examples of these buffers include sodium carbonate, potassium carbonate, sodium bicarbonate, potassium bicarbonate, trisodium phosphate, tripotassium phosphate, disodium phosphate, dipotassium phosphate, sodium borate, potassium borate, sodium tetraborate (borax), potassium tetraborate, sodium o-hydroxybenzoate (sodium salicylate), potassium o-hydroxybenzoate, sodium 5-sulfo-2-hydroxybenzoate (sodium 5-sulfosalicylate), and potassium 5-sulfo-2-hydroxybenzoate (potassium 5-sulfosalicylate). The present invention should not be construed as being limited to these compounds.
The amount of the buffer to be added to the color developing solution is preferably 0.1 mol or more and more preferably from 0.1 mol to 0.4 mol per liter of the developing solution.
In addition, various chelating agents can be used in the color developing solution according to the present invention for the purpose of preventing calcium or magnesium precipitation or increasing the stability of the color developing solution.
As the chelating agents, organic acid compounds are preferred and include aminopolycarboxylic acids, organic phosphoric acids and phosphonocarboxylic acids.
Specific examples of useful chelating agents are set forth below, but the present invention should not be construed as being limited thereto.
Nitrilotriacetic acid
Diethylenetriaminepentaacetic acid
Ethylenediaminetetraacetic acid
N,N,N-Trimethylenephosphonic acid
Ethylenediamine-N,N,N',N'-tetramethylenephosphonoic acid
Trans-cyclohexanediaminetetraacetic acid
1,2-Diaminopropanetetraacetic acid
Hydroxyethyliminodiacetic acid
Glycol ether diaminetetraacetic acid
Ethylenediamine-o-hydroxyphenylacetic acid
2-Phosphonobutane-1,2,4-tricarboxylic acid
1-Hydroxyethylidene-1,1-diphosphonic acid
N,N'-Bis(2-hydroxybenzyl)ethylenediamine-N,N'-diacetic acid
Two or more kinds of such chelating agents may be employed together, if desired.
The chelating agent is added to the color developing solution in an amount sufficient to block metal ions being present therein. For example, a range of from about 0.1 g to about 10 g per liter of the color developing solution may be employed.
The color developing solution may contain appropriate development accelerators, if desired. However, it is preferred that the color developing solution used in the present invention does not substantially contain benzyl alcohol in view of prevention of environmental pollution, the easy preparation of the solution and prevention of color stain. The term "substantially not contain" means that the color developing solution contains benzyl alcohol in an amount of 2 ml or less per liter of the solution, and preferably does not contain benzyl alcohol at all.
Examples of suitable development accelerators include thioether type compounds as described in JP-B-37-16088, JP-B-37-5987, JP-B-38-7826, JP-B-44-12380, JP-B-45-9019 and U.S. Pat. No. 3,813,247; p-phenylenediamine type compounds as described in JP-A-52-49829 and JP-A-50-15554; quaternary ammonium salts as described in JP-A-50-137726, JP-B-44-30074, JP-A-56-156826 and JP-A-52-43429; amine type compounds as described in U.S. Pat. Nos. 2,494,903, 3,128,182, 4,230,796, 3,253,919, 2,482,546, 2,596,926, and 3,582,346 and JP-B-41-11431; polyalkylene oxides as described in JP-B-37-16088, JP-B-42-25201, JP-B-41-11431, JP-B-42-23883 and U.S. Patents 3,128,183 and 3,532,501; 1-phenyl-3-pyrazolidones; and imidazoles.
The color developing solution used in the present invention may contain appropriate antifoggants, if desired. Alkali metal halides such as sodium chloride, potassium bromide, and potassium iodide as well as organic antifoggants may be employed as antifoggants. Representative examples of organic antifoggants include nitrogen-containing heterocyclic compounds such as benzotriazole, 6-nitrobenzimidazole, 5-nitroisoindazole, 5-methylbenzotriazole, 5-nitrobenzotriazole, 5-chlorobenzotriazole, 2-thiazolylbenzimi dazole, 2-thiazolylmethyl-benzimidazole, indazole, hydroxyazaindolizine and adenine, etc.
It is preferred that the color developing solution used in the present invention contains a fluorescent brightening agent. As fluorescent brightening agents, 4,4'-diamino-2,2'-disulfostilbene type compounds are preferred. The amount of the fluorescent brightening agent added is from 0 to 5 g and preferably from 0.1 g to 4 g, per liter of the color developing solution.
Furthermore, the color developing solution according to the present invention may contain various surface active agents such as alkylsulfonic acids, arylphosphonic acids, aliphatic carboxylic acids, and aromatic carboxylic acids, etc., if desired.
The processing temperature of the color developing solution used in the present invention is usually from 20.degree. C. to 50.degree. C. and preferably from 30.degree. C. to 45.degree. C. The processing time is usually from 20 sec. to 5 min. and preferably from 30 sec. to 3 min. Further, the amount of replenishment for the color developing solution is preferably as small as feasible, and is usually from 100 ml to 1,500 ml, preferably from 100 ml to 800 ml, and more preferably from 100 ml to 400 ml, per square meter of the color light-sensitive material.
If required, the color developing bath may be divided into two or more baths, so that a color developing replenisher may be supplied from the first bath or the last bath to shorten the developing time or to reduce the amount of the replenisher.
The processing method according to the present invention can be used in a color reversal process. A suitable black-and-white developing solution used in this case includes a black-and-white first developing solution (used in reversal process of color photographic light-sensitive materials), or one that can be used in processing black-and-white photographic light-sensitive materials. Further, known various additives that are generally added to a black-and-white developing solution can be contained in the solution.
Representative additives include developing agents such as 1-phenyl-3-pyrazolidone, Metol (HOC.sub.6 H.sub.4 NHCH.sub.3. 1/2H.sub.2 SO.sub.4) and hydroquinone; preservatives such as sulfites; accelerators comprising an alkali such as sodium hydroxide, sodium carbonate and potassium carbonate; inorganic or organic restrainers such as potassium bromide, 2-methylbenzimidazole and methylbenzothiazole; hard water softening agents such as polyphosphates; and development restrainers comprising trace amounts of iodides or mercapto compounds.
The processing method according to the present invention comprises processing steps including color development, bleaching, bleach-fixing, etc., as mentioned above. After the bleach-fixing step, although processing steps that include water washing and stabilizing are generally carried out, a simple processing method is also possible wherein after bleach-fixing, a stabilizing process is carried out without performing substantial water washing.
The washing water used in the water washing step can contain, if desired, known additives. For example, hard water softening agents such as inorganic phosphoric acid, amino-polycarboxylic acids and organic phosphoric acids, antibacterial and antifungal agents for preventing various bacteria and algae from proliferating (e.g., isothiazolone, organic chlorine type disinfectants and benzotriazole) and surface active agents for lowering drying load or for preventing uneven drying can be used. Compounds described, for example, in L. E. West, "Water Quality Criteria", Phot. Sci. and Eng., Vol. 9, No. 6, pages 344 to 359 (1965) can also be used.
A suitable stabilizing solution used in the stabilizing step includes a processing solution for stabilizing dye images. For example, a solution having a pH of from 3 to 6 and a buffering ability and a solution containing an aldehyde (e.g., formalin) can be used. The stabilizing solution can contain, if desired, ammonium compounds, compounds containing metals such as Bi and Al, fluorescent brightening agents, chelating agents (e.g., 1-hydroxy-ethylidene-1,1-diphosphonic acid), antibacterial, antifungal agents, hardening agents, surface active agents, etc.
It is preferred to employ a multistage countercurrent system in the water washing step or stabilizing step. Two to four stages are preferably used. The amount of replenishment is from 1 to 50 times, preferably from 2 to 30 times and more preferably from 2 to 15 times the amount of processing solution carried over from the preceding bath per a unit area of the color light-sensitive material.
Water suitable for use in the water washing step or the stabilizing step includes city (tap) water, water that has been deionized, for example, by ion exchange resins to reduce Ca and Mg concentrations to 5 mg/liter or below, or water that has been sterilized, for example, by a halogen lamp or a bactericidal ultraviolet lamp.
When continuous processing is performed using an automatic developing machine, concentration of the processing solution tends to occur by evaporation in each step of the processing of color light-sensitive materials. This phenomenon particularly occurs in a case wherein a small amount of color light-sensitive materials is processed or wherein an open area of the processing solution is large. In order to compensate for such concentration of processing solution, it is preferred to replenish them with an appropriate amount of water or a correcting solution.
The present invention can be applied to various color photographic light-sensitive materials, and typical examples thereof include color negative films for general use or cinematography, color reversal films for slides or television, color papers, color positive films, color reversal papers, and direct positive color light-sensitive materials.
Suitable silver halide emulsions used in the color light-sensitive materials to be processed in accordance with the present invention can be prepared by using the method as described in Research Disclosure, Vol. 176, No. 17643, Item [I].
In the color light-sensitive materials processed in accordance with the present invention, any of silver bromide, silver iodobromide, silver iodochlorobromide, silver chlorobromide and silver chloride can be employed as silver halide. Silver halide containing at least 1 mol % of silver iodide is preferably employed.
The silver halide grains in the photographic emulsion may be so-called regular grains having a regular crystal form such as a cubic, octahedral or tetradecahedral structure, or may have an irregular crystal form such as a spherical crystal, a crystal defect such as a twin plane, or composite structure thereof.
The silver halide may be fine grains having a grain diameter of up to about 0.1 microns or coarse grains wherein the diameter of the projected area is up to about 10 microns, and a monodispersed emulsion having a narrow distribution or a polydispersed emulsion having a wide distribution can be used.
A typical monodispersed emulsion is one wherein the average grain diameter of the silver halide grains is greater than about 0.1 micron and at least about 95 wt % of the silver halide grains are within .+-.40% of the average grain diameter. In the present invention, an emulsion can be used wherein the average grain diameter is about 0.25 to 2 microns, and at least about 95% by weight or at least about 95% by number of the silver halide grains are within .+-.20% of the average particle diameter.
The crystal structure of the grains may be uniform, or the outer portion of the halogen composition may be different from the inner portion thereof, or may have a stratified structure. These types of emulsion grains are disclosed, for example, in British Patent 1,027,146, U.S. Pat. No. 3,505,068 and 4,44,877 and JP-A-60-143331. Silver halide grains having different compositions joined upon epitaxial conjunction may also be employed.
When tabular grains are used in the silver halide photographic emulsions used in the present invention, improvement in sensitivity (including improvement in color sensitizing effect by sensitizing dyes), improvement in the relationship between sensitivity and graininess, improvement in sharpness, improvement in development proceeding, improvement in covering power and improvement in crossover, can be attained. The term "tabular silver halide grains" used herein refers to tabular silver halide grains whose diameter/thickness ratio is about 5 or higher, and, includes for example, tabular silver halide grains having a diameter/thickness ratio of more than 8 and tabular silver halide grains having a diameter/thickness ratio of from 5 to 8.
Preferably, the tabular grain halogen composition includes silver bromide, silver bromoiodide, silver bromochloride, silver bromochloroiodide, silver chloroiodide or silver chloride. For highly sensitive photographic materials, silver iodobromide is particularly preferably used. In the case of using silver iodobromide, the content of silver iodide is generally from not more than 40 mol %, preferably not more than 20 mol %, and more preferably not more than 15 mol %. For photographic materials used for printing, silver chloride and silver bromide are particularly preferred.
Tabular grains may comprise a uniform halogen composition or may be composed of two or more phases having different halogen compositions. For example, when silver iodobromide is used, the silver iodobromide tabular grains may have a structure with plural layers different in their iodide content. Preferred examples of the halogen composition of tabular silver halide grains and the distribution of the halogens in the grains are described, for example, in JP-A-58-113928 and JP-A-59-99433.
Preferred methods of using tabular silver halide grains according to the present invention are described in detail, for example, in Research Disclosure, No. 22534 (January, 1983) and Research Disclosure, No. 25330 (May, 1985), in which, for example, a method of using tabular silver halide grains based on the relationship between the thickness of the tabular silver halide grains and the optical properties thereof is disclosed.
To facilitate ripening of the formation of silver halide grains, it is useful to employ a silver halide solvent. For example, to facilitate ripening, it is known to allow an excess of halogen ions to be present in the reactor. Ripening agents other than halogen ions that can be used are ammonia, amine compounds, and thiocyanates such as alkali metal thiocyanates, particularly sodium thiocyanate, potassium thiocyanates and ammonium thiocyanate. The use of thiocyanate ripening agents is described in U.S. Pat. Nos. 2,222,264, 2,448,534 and 3,320,069. Commonly used thioether ripening agents as described in U.S. Pat. Nos. 3,271,157, 3,574,628 and 3,737,313 can also be used. Further, thione compounds as described in JP-A-53-82408 and JP-A-53-144319 can be employed.
Generally, the silver halide emulsions are chemically sensitized. Chemical sensitization is performed suitably in the presence of a gold compound and a thiocyanate compound or in the presence of a sulfur-containing compound as described in U.S. Pat. Nos. 3,857,711, 4,266,018 and 4,054,457, or in the presence of a sulfur-containing compound such as hypo (sodium thiosulfate), a thiourea type compound and a rhodanine type compound.
The silver halide photographic emulsion used in the present invention may be spectrally sensitized with a methine dye or other dyes. Sensitizing dyes particularly useful are cyanine dyes, merocyanine dyes and complex merocyanine dyes.
These sensitizing dyes may be used alone or in combination, and when they are used in combination, they are often used for the purpose of supersensitization. In addition to a sensitizing dye, the emulsion may contain a dye that does not have a spectral sensitizing effect itself, but exhibits a supersensitizing effect, or a material that does not absorb substantially visible light, but exhibits a supersensitizing effect.
Examples of these types of sensitizing dyes are described in Research Disclosure, Vol. 176, No. 17643, Item IV (December, 1978).
The spectral sensitization of the silver halide emulsion used in the present invention can be carried out during any stage of preparation of the emulsion. In particular, U.S. Pat. Nos. 4,183,756 and 4,225,666 disclose that it is advantageous to add a spectral sensitizing dye to an emulsion after the formation of stable nuclei for the formation of silver halide grains, since the adsorption of the photographic sensitizing dye onto the silver halide grains is enhanced.
For the purpose of increasing the sensitivity and the contrast or to facilitate development, the photographic emulsion layer of the photographic light-sensitive material according to the present invention may contain, for example, polyalkylene oxides or their derivatives such as their ethers, esters and amines, thioether compounds, thiomorpholines, quaternary ammonium salt compounds, urethane derivatives, urea derivatives, imidazole derivatives and 3-pyrazolidones.
The silver halide photographic emulsion used in the present invention may also contain various compounds for the purpose of preventing the photographic materials from fogging in the process of the preparation thereof or during the storage thereof, or during photographic processing, or for the purpose of stabilizing the photographic performance. Specifically, various compounds known as stabilizers or antifoggants can be added, for example, azoles such as benzothiazoliums, nitroimidazoles, nitrobenzimidazoles, chlorobenzimidazoles, bromobenzimidazoles, mercaptothiazoles, mercaptobenzothiazoles, mercaptobenzimidazoles, mercaptothiadiazoles, aminotriazoles, benzotriazoles, nitrobenzotriazoles and mercaptotetrazoles (particularly, 1-phenyl-5-mercaptotetrazole); mercaptopyrimidines; mercaptotriazines; thioketo compounds such as oxazolinethione; azaindenes such as triazaindenes, tetraazaindenes (particularly, 4-hydroxy substituted (1,3,3a,7)tetraazaindenes) and pentaazaindenes; benzenethiosulfonic acid, benzenesulfinic acid; and benzenesulfonic acid amide.
In the photographic material to be processed in accordance with the present invention, various types of couplers can be used, and specific examples thereof are described in the patents cited in Research Disclosure, No. 17643, Items VII-C to VII-G. Important dye forming couplers include couplers that give rise to the three primary colors (that is, yellow, magenta and cyan) of the subtractive color process by color development, and suitable examples of diffusion resistant 4-equivalent or 2-equivalent couplers include those described in the patents cited in Research Disclosure, No. 17643, Items VII-C and D. Also, the couplers described below can be preferably used.
Typical yellow couplers useful in the present invention include oil protected acylacetamide type couplers. Specific examples thereof are described, for example, in U.S. Pat. Nos. 2,407,210, 2,875,057 and 3,265,506. In the present invention, 2-equivalent yellow couplers are preferably employed and typical examples thereof include yellow couplers of oxygen atom releasing type as described, for example, in U.S. Pat. Nos. 3,408,194, 3,447,928, 3,933,501 and 4,022,620, and yellow couplers of nitrogen atom releasing type as described, for example, in JP-B-55-10739, U.S. Pat. Nos. 4,401,752 and 4,326,024, Research Disclosure, No. 18053 (April, 1979), British Patent 1,425,020 and West German Patent Application (OLS) Nos. 2,219,917, 2,261,361, 2,329,587 and 2,433,812. .alpha.-Pivaloylacetanilide type couplers are characterized by fastness, particularly light fastness, of the dyes formed, and .alpha.-benzoylacetanilide type couplers are characterized by providing a high color density.
Magenta couplers useful in the present invention include oil protected indazolone type couplers, cyanoacetyl type couplers, and preferably 5-pyrazolone type couplers and pyrazoloazole type couplers such as pyrazolotriazoles. Of 5-pyrazolone type couplers, those substituted with an arylamino group or an acylamino group at the 3-position thereof are preferred in view of hue and color density of images formed. Typical examples thereof are described, for example, in U.S. Pat. Nos. 2,311,082, 2,343,703, 2,600,788, 2,908,573, 3,062,653, 3,152,896 and 3,936,015. 2-Equivalent 5-pyrazolone type couplers are preferably used. Particularly, nitrogen atom releasing groups as described in U.S. Pat. No. 4,310,619 and arylthio groups as described in U.S. Pat. No. 4,351,897 and preferred as releasing groups. Further, 5-pyrazalone type couplers having a ballast group described in European Patent 73,636 are advantageous because they provide a high color density.
Examples of pyrazoloazole type couplers include pyrazolobenzimidazoles as described in U.S. Pat. No. 3,369,879, and preferably pyrazolo[5,1-c][1,2,4]-triazoles as described in U.S. Pat. No. 3,725,067, pyrazolotetrazoles as described in Research Disclosure, No. 24220 (June, 1984) and pyrazolopyrazoles as described in Research Disclosure, No. 24230 (June, 1984). Imidazo[1,2-b]pyrazoles as described in European Patent 119,741 are preferred and pyrazolo[1,5-b][1,2,4]-triazoles as described in European Patent 119,860 are particularly preferred, in view of less yellow subsidiary absorption and light fastness of dyes formed.
As cyan couplers useful in the present invention, oil protected naphthol type and phenol type couplers are exemplified. Typical examples thereof include naphthol type couplers as described in U.S. Pat. No. 2,474,293 and preferably oxygen atom releasing type 2-equivalent naphthol type couplers as described, for example, in U.S. Pat. Nos. 4,052,212, 4,146,396, 4,228,233 and 4,296,200, and phenol type couplers as described, for example, in U.S. Pat. Nos. 2,369,929, 2,801,171, 2,772,162 and 2,895,826.
Cyan couplers fast to humidity and temperature are preferably used in the present invention. Typical examples thereof include phenol type cyan couplers having an alkyl group having two or more carbon atoms at the meta-position of the phenol nucleus as described in U.S. Pat. No. 3,772,002, 2,5-diacylamino-substituted phenol type couplers as described, for example, in U.S. Pat. Nos. 2,772,162, 3,758,308, 4,126,396, 4,334,011 and 4,327,173, West German Patent Application (OLS) No. 3,329,729 and JP-A-59-166956, and phenol type couplers having a phenylureido group at the 2-position thereof and an acylamino group at the 5-position thereof as described, for example, in U.S. Pat. Nos. 3,446,622, 4,333,999, 4,451,559 and 4,427,767.
Couplers capable of forming appropriately diffusible dyes can be used in combination in order to improve graininess. Specific examples of such couplers include the magenta couplers as described, for example, in U.S. Pat. No. 4,366,237 and the low, magenta and cyan couplers as described, for example, in European Patent 96,570.
Dye forming couplers and the special couplers as described above may be in the form of polymers including dimers or more. Typical examples of dye forming couplers that are polymerized are described, for example, in U.S. Pat. No. 3,451,820. Specific examples of polymerized magenta couplers are described, for example, in U.S. Pat. No. 4,367,282.
Couplers capable of releasing a photographically useful group upon the coupling reaction can also preferably be used in the present invention. Useful DIR couplers which release a development inhibitor include the couplers described in the patents cited in Research Disclosure, No. 17643, Item VII-F.
In the color light-sensitive materials according to the present invention, couplers can be used which as capable of releasing imagewise a nucleating agent, a development accelerator or a precursor thereof when developed. Specific examples of such compounds are described, for example, in British Patents 2,097,140 and 2,131,188. Also, for example, DIR redox compound-releasing couplers as described, for example, in JP-A-60-185950 and couplers which can release a dye that will restore color after being released as described, for example, in European Patent 173,302A, can be used.
Couplers which can be used in the present invention are incorporated into the color light-sensitive material by any one of various known dispersion methods. Examples of organic solvents having a high boiling point used in the oil-in-water droplet dispersion method are described, for example, in U.S. Pat. No. 2,322,027. Further, the latex dispersion method, the effects thereof, and specific examples of latexes for impregnation are described, for example, in U.S. Pat. No. 4,199,363 and West German Patent Application (OLS) Nos. 2,541,274 and 2,541,230.
The color light-sensitive materials used in the present invention may contain, as color fog preventing agents or color mixing preventing agents, hydroquinone derivatives, aminophenol derivatives, amines, gallic acid derivatives, catechol derivatives, ascorbic acid derivatives, non-color-forming couplers and sulfonamidophenol derivatives.
The color light-sensitive materials used in the present invention can also contain known color fading preventing agents. Typical examples of known color fading preventing agents include hindered phenols such as hydroquinones, 6-hydroxycoumarones 5-hydroxycoumarans, p-alkoxyphenols, spirochromans or bisphenols; gallic acid derivatives, methylenedioxybenzenes, aminophenols, hindered amines and also ether or ester derivatives thereof wherein the phenolic hydroxyl group of these compounds is silylated or alkylated.
In the color light-sensitive materials used in the present invention, an ultraviolet light absorbing agent can be added into a hydrophilic colloid layer thereof. Typical examples of ultraviolet light absorbing agents are described, for example, in Research Disclosure, No. 24239 (June, 1984).
The color light-sensitive materials used in the present invention may contain one or more surface active agents as coating assistants, as antistatic agents, or for the purposes of improving the slipping characteristics, the emulsification/dispersion ability and the photographic characteristics (e.g., acceleration of development, increase in contract and sensitization), for the purpose of preventing adhesion and for other purposes.
Examples of useful surface active agents include nonionic surface active agents, such as saponin (steroid type), alkylene oxide derivatives (e.g., polyethylene glycol, polyethylene glycol/polypropylene glycol condensates, polyethylene glycol alkyl ethers or alkylaryl ethers, polyethylene glycol esters, polyethylene glycol sorbitan esters, polyalkylene glycol alkylamines or alkylamides, polyethylene oxide adducts of silicone, etc.), glycidol derivatives (e.g., alkenylsuccinic acid polyglycerides, alkylphenol polyglycerides, etc.), fatty acid esters of polyhydric alcohols, alkyl esters of sugars, etc.; anionic surface active agents containing an acid group (e.g., carboxyl group, a sulfo group, a phospho group, a sulfate group, a phosphate group, etc.), such as alkylcarboxylates, alkylsulfonates, alkylbenzenesulfonates, alkylnaphthalenesulfonates, alkylsulfates, alkylphosphates, N-acyl-N-alkyltaurines, sulfosuccinates, sulfoalkylpolyoxyethylene alkyl phenyl ethers, polyoxyethylene alkylphosphates, etc.; amphoteric suface active agents, such as amino acids, aminoalkylsulfonic acids, aminoalkyl sulfates or phosphates, alkylbetaines, amine oxides, etc.; and cationic surface active agents, such as alkylamine salts, aliphatic or aromatic quaternary ammonium salts, heterocyclic quaternary ammonium salts, e.g., pyridinium, imidazolium, etc., aliphatic or heterocyclic phosphonium or sulfonium salts, and the like.
The color light-sensitive materials used in the present invention may contain water-soluble dyes in a hydrophilic colloid layer as filter dyes or for the purpose of preventing irradiation or halation, or for other purposes. Preferred examples of such dyes include oxonol dyes, hemioxonol dyes, styryl dyes, merocyanine dyes, anthraquinone dyes and azo dyes, and cyanine dyes, azomethine dyes, triarylmethane dyes and phthalocyanine dyes can also be used. Oil-soluble dyes can be emulsified by the oil-in-water-droplet dispersion method to be added to the hydrophilic colloid layer.
In the color light-sensitive materials used in the present invention, in order to introduce oleophilic compounds (such as photographic couplers) into a hydrophilic organic colloid layer, various methods can be used, such as the oil-in-water-droplet dispersion method, the latex dispersion method, the solid dispersion method and the alkali dispersion method. A preferred method can be suitably selected depending on the chemical structure and the physicochemical properties of the compound to be incorporated therein.

EXAMPLE
The present invention will now be explained in greater detail with reference to the following examples, but the present invention should not be construed as being limited thereto.
In the following examples, the bleach accelerating compounds of formula (I) according to the present invention will be indicated using the numbers which are affixed to the specific compounds set forth hereinbefore. Comparative compounds used in the following examples are shown below. ##STR4##
EXAMPLE 1
On a cellulose triacetate film support having a subbing layer was coated layers having the composition set forth below to prepare a multilayer color light-sensitive material which was designated Light-sensitive material A.
Composition of the light-sensitive material
With respect to the compositions of the layers, coated amounts of silver halide and colloidal silver are shown by g/m.sup.2 units of silver, the coated amounts of couplers, additives and gelatin are shown by g/m.sup.2 units, and the coated amounts of sensitizing dyes are shown by mol number per mol of silver halide being present in the same layer.
______________________________________First Layer: Antihalation LayerBlack colloidal silver 0.2Gelatin 1.3ExM-9 0.06UV-1 0.03UV-2 0.06UV-3 0.06Solv-1 0.15Solv-2 0.15Solv-3 0.05Second Layer: IntelayerGelatin 1.0UV-1 0.03ExC-4 0.02ExF-1 0.004Solv-1 0.1Solv-2 0.1Third Layer: Low-Sensitive Red-Sensitive Emulsion LayerSilver iodobromide emulsion 1.2 g(AgI: 4 mol %, uniform AgI type, (as silver)diameter corresponding to sphere:0.5 .mu.m, coefficient of variationof diameter corresponding to sphere:20%, tabular grain, diameter/thickness ratio: 3.0)Silver iodobromide emulsion 0.6(AgI: 3 mol %, uniform AgI type, (as silver)diameter corresponding to sphere:0.3 .mu.m, coefficient of variationof diameter corresponding to sphere:15%, spherical grain, diameter/thickness ratio: 1.0)Gelatin 1.0ExS-1 4 .times. 10.sup.-4ExS-2 5 .times. 10.sup.-4ExC-1 0.05ExC-2 0.50ExC-3 0.03ExC-4 0.12ExC-5 0.01Fourth Layer: High-Sensitive Red-sensitive Emulsion LayerSilver iodobromide emulsion 0.7(AgI: 6 mol %, internal high AgI (as silver)type, with core/shell ratio of1/1, diameter corresponding to sphere:0.7 .mu.m, coefficient of variationof diameter corresponding to sphere:15%, tabular grain, diameter/thickness ratio: 5.0)Gelatin 1.0ExS-1 3 .times. 10.sup.-4ExS-2 2.3 .times. 10.sup.-5ExC-6 0.11ExC-7 0.05ExC-4 0.05Solv-1 0.05Solv-3 0.05Fifth Layer: IntelayerGelatin 0.5Cpd-1 0.1Solv-1 0.05Sixth Layer: Low-Sensitive Green-Sensitive Emulsion LayerSilver iodobromide emulsion 0.35(AgI: 4 mol %, surface high AgI (as silver)type, with core/shell ratio of1/1, diameter corresponding to sphere:0.5 .mu.m, coefficient of variationof diameter corresponding to sphere:15%, tabular grain, diameter/thickness ratio: 4.0)Silver iodobromide emulsion 0.20(AgI: 3 mol %, uniform AgI type, (as silver)diameter corresponding to sphere:0.3 .mu.m, coefficient of variationof diameter corresponding to sphere:25%, spherical grain, diameter/thickness ratio: 1.0)Gelatin 1.0ExS-3 5 .times. 10.sup.-4ExS-4 3 .times. 10.sup.-4ExS-5 1 .times. 10.sup.-4ExM-8 0.4ExM-9 0.07ExM-10 0.02ExY-11 0.03Solv-1 0.3Solv-4 0.05 Seventh Layer: High-Sensitive Green-Sensitive EmulsionLayerSilver iodobromide emulsion 0.8(AgI: 4 mol %, internal high AgI (as silver)type, with core/shell ratio of1/3, diameter corresponding to sphere:0.7 .mu.m, coefficient of variationof diameter corresponding to sphere:20%, tabular grain, diameter/thickness ratio: 5.0)Gelatin 0.5ExS-3 5 .times. 10.sup.-4ExS-4 3 .times. 10.sup.-4ExS-5 1 .times. 10.sup.-4ExM-8 0.1ExM-9 0.02ExY-11 0.03ExC-2 0.03ExM-14 0.01Solv-1 0.2Solv-4 0.01Eighth Layer: InterlayerGelatin 0.5Cpd-1 0.05Solv-1 0.02 Ninth Layer: Donor Layer of Interlayer Effect to Red-Sensitive LayerSilver iodobromide emulsion 0.35(AgI: 2 mol %, internal high AgI (as silver)type, with core/shell ratio of2/1, diameter corresponding to sphere:1.0 .mu.m, coefficient of variationof diameter corresponding to sphere:15%, tabular grain, diameter/thickness ratio: 6.0)Silver iodobromide emulsion 0.20(AgI: 2 mol %, internal high AgI (as silver)type, diameter corresponding to sphere:0.4 .mu.m, coefficient of variationof diameter corresponding to sphere:20%, tabular grain, diameter/thickness ratio: 6.0)Gelatin 0.5ExS-3 8 .times. 10.sup.-4ExY-13 0.11ExM-12 0.03ExM-14 0.10Solv-1 0.20Tenth Layer: Yellow Filter LayerYellow Colloidal Silver 0.05Gelatin 0.5Cpd-2 0.13Solv-1 0.13Cpd-1 0.10 Eleventh Layer: Low-Sensitive Blue-Sensitive EmulsionLayerSilver iodobromide emulsion 0.3(AgI: 4.5 mol %, uniform high AgI type, (as silver)diameter corresponding to sphere:0.7 .mu.m, coefficient of variationof diameter corresponding to sphere:15%, tabular grain, diameter/thickness ratio: 7.0)Silver iodobromide emulsion 0.15(AgI: 3 mol %, uniform AgI type, (as silver)diameter corresponding to sphere:0.3 .mu.m, coefficient of variationof diameter corresponding to sphere:25%, tabular grain, diameter/thickness ratio: 7.0)Gelatin 0.5ExS-6 2 .times. 10.sup.-4ExC-16 0.05ExC-2 0.10ExC-3 0.02ExY-13 0.07ExY-15 1.0Solv-1 0.20 Twelfth Layer: High-Sensitive Blue-Sensitive EmulsionLayerSilver iodobromide emulsion 0.5(AgI: 10 mol %, internal high AgI (as silver)type, diameter corresponding to sphere:1.0 .mu.m, coefficient of variationof diameter corresponding to sphere:25%, multiple twin tabular grain,diameter/thickness ratio: 2.0)Gelatin 0.5ExS-6 1 .times. 10.sup.-4ExY-15 0.20ExY-13 0.01Solv-1 0.10Thirteenth Layer: First Protective LayerGelatin 0.8UV-4 0.1UV-5 0.15Solv-1 0.01Solv-2 0.01Fourteenth Layer: Second Protective LayerFine grain silver iodobromide 0.5emulsion (AgI: 2 mol %, uniform AgI (as silver)type, diameter corresponding tosphere: 0.07 .mu.m)Gelatin 0.45Polymethyl methacrylate particle 0.2(diameter: 1.5 .mu.m)H-1 0.4Cpd-5 0.5Cpd-6 0.5______________________________________
Each layer described above further contained a stabilizer for emulsions (Cpd-3: 0.04 g/m.sup.2) and a surface active agent (Cpd-4: 0.02 g/m.sup.2) as a coating aid in addition to the above described compounds.
The compounds used for the preparation of Sample A are illustrated below. ##STR5## Solv-1: Tricresyl phosphate Solv-2: Dibutyl phthalate ##STR6##
The light-sensitive material thus-prepared was exposed to light in an exposure amount of 10 CMS using a light source of 4800.degree. K. (color temperature) and then subjected to development processing according to the following processing steps. In the bleaching step, bleaching solutions containing a bleach accelerating agent as shown in Table 1 below and a bleaching solution which did not contain a bleach accelerating agent were employed, respectively.
______________________________________Processing Processing ProcessingStep Time Temperature______________________________________Color Development 2 min. 30 sec. 40.degree. C.Bleaching 1 min. 30 sec. 40.degree. C.Fixing 2 min. 30 sec. 40.degree. C.Washing with Water 1 min. 30 sec. 40.degree. C.Stabilizing 30 sec. 40.degree. C.Drying 1 min. --______________________________________
The composition of each processing solution used is illustrated below.
Color Developing Solution
______________________________________Diethylenetriaminepenta- 1.0 gacetic Acid1-Hydroxyethylidene-1,1- 2.0 gdiphosphonic AcidSodium Sulfite 4.0 gPotassium Carbonate 30.0 gPotassium Bromide 1.4 gPotassium Iodide 1.3 mgHydroxylamine Sulfate 2.4 g4-(N-Ethyl-N-.beta.-hydroxy- 5.0 gethylamino)-2-methyl-aniline SulfateWater to make 1.0 lpH 10.20______________________________________
Bleaching Solution
______________________________________Ammonium Iron (III) 120 gEthylenediaminetetra-acetate DihydrateDisodium Ethylenediamine- 10.0 gtetraacetateAqueous Ammonia 7 mlAmmonium Nitrate 10.0 gAmmonium Bromide 100.0 gBleach Accelerating Agent (shown in Table 1 below)Water to make 1.0 lpH 6.0______________________________________
Fixing Solution
______________________________________Disodium Ethylenediamine- 2.0 gtetraacetateSodium Sulfite 4.0 gAmmonium Thiosulfate 175.0 ml(700 g/l aq. soln.)Sodium Bisulfite 4.6 gWater to make 1.0 lpH 6.6______________________________________
Stabilizing Solution
______________________________________Formalin (37 wt %) 0.2 mlPolyoxyethylene- 0.3 gp-monononylphenylether(average degree ofpolymerization: 10)Water to make 1.0 l______________________________________
To the bleaching solution were added the compounds shown in Table 1 respectively and their bleach accelerating abilities were compared based on the amount of remaining silver. The amount of remaining silver was determined by X-ray fluorometric analysis. Further, the presenced stains on the photographic material after processing was visually observed. The results thus-obtained are shown in Table 1 below.
TABLE 1______________________________________ Amount of Bleach* RemainingRun Accelerat- Silver Stains AfterNo. ing Agent (.mu.g/cm.sup.2) Processing Remark______________________________________1 -- 21.3 not observed Comparison2 (A) 6.2 observed "3 (B) 7.3 observed "4 (C) 8.5 slightly observed "5 (1) 5.2 not observed Present Invention6 (2) 5.0 not observed Present Invention7 (5) 4.9 not observed Present Invention8 (7) 4.7 not observed Present Invention9 (11) 4.5 not observed Present Invention10 (12) 4.2 not observed Present Invention11 (16) 4.8 not observed Present Invention12 (27) 3.2 not observed Present Invention13 (29) 3.4 not observed Present Invention14 (31) 3.5 not observed Present Invention15 (35) 3.6 not observed Present Invention16 (37) 3.8 not observed Present Invention17 (41) 3.7 not observed Present Invention18 (44) 3.3 not observed Present Invention______________________________________ *Amount added: 5 .times. 10.sup.-3 mol per liter of the bleaching solution.
As is apparent from the results shown in Table 1, a rapid desilvering process is realized using the compounds according to the present invention as the bleach accelerating agent.
EXAMPLE 2
The same procedure as described in Example 1 was repeated except that the bleaching solution was substituted with the one set forth below, and similar results to those in Example 1 were obtained.
Bleaching Solution
______________________________________Ammonium Iron (III) 1,3-diaminopropane- 30 gtetraacetateAmmonium Iron (III) Ethylenediaminetetra- 90 gacetate DihydrateDisodium Ethylenediaminetetraacetate 10.0 gAqueous Ammonia (27% weight/weight) 7.0 mlAmmonium Nitrate 10.0 gAmmonium Bromide 100.0 gBleach Accelerating Agent (shown in Table 1 above)Water to make 1.0 lpH 5.5______________________________________
EXAMPLE 3
Light-sensitive material A as prepared in Example 1 was exposed to light in the same manner as described in Example 1 and then subjected to development processing according to the following processing steps. In the bleaching step, a bleaching solution containing a bleach accelerating agent as shown in Table 2 below and a bleaching solution which did not contain a bleach accelerating agent were employed, respectively.
______________________________________Processing Processing ProcessingStep Time Temperature______________________________________Color Development 2 min. 30 sec. 40.degree. C.Bleach-Fixing 2 min. 40.degree. C.Washing with Water 1 min. 30 sec. 40.degree. C.Drying 1 min. 60.degree. C.______________________________________
The composition of each processing solution used is illustrated below.
Color Developing Solution
Same composition as described in Example 1.
Bleach-Fixing Solution
______________________________________Ammonium Iron (III) Ethylenediaminetetra- 60.0 gacetate DihydrateDisodium Ethylenediaminetetraacetate 9.0 gSodium Sulfite 12.0 gAmmonium Thiosulfate 240 ml(700 g/l aq. soln.)Bleach Accelerating Agent (shown in Table 2 above)Water to make 1.0 lpH 6.5______________________________________
Washing Water
______________________________________Polyoxyethylene-p-monononylphenylether 0.3 g(average degree of polymerization: 10)Distilled Water to make 1.0 l______________________________________
After the processing, the amount of remaining silver was determined by X-ray fluorometric analysis. Further, the presence of stains on the photographic material after processing was visually observed. The results thus-obtained are shown in Table 2 below.
TABLE 2______________________________________ Amount of Bleach* RemainingRun Accelerat- Silver Stains AfterNo. ing Agent (.mu.m/cm.sup.2) Processing Remark______________________________________19 -- 22.4 not observed Comparison20 (A) 10.3 observed "21 (B) 11.2 observed "22 (C) 13.3 slightly observed "23 (1) 4.8 not observed Present Invention24 (2) 4.5 not observed Present Invention25 (5) 4.6 not observed Present Invention26 (7) 4.5 not observed Present Invention27 (11) 3.9 not observed Present Invention28 (12) 3.8 not observed Present Invention29 (16) 4.2 not observed Present Invention30 (27) 2.8 not observed Present Invention31 (29) 2.5 not observed Present Invention32 (31) 2.7 not observed Present Invention33 (35) 2.9 not observed Present Invention34 (37) 3.0 not observed Present Invention35 (41) 2.9 not observed Present Invention36 (44) 2.8 not observed Present Invention______________________________________ *Amount added: 5 .times. 10.sup.-3 mol per liter of the bleach fixing solution.
As is apparent from the results shown in Table 2, desilveration in the bleach-fixing step is remarkably accelerated using the compound according to the present invention.
Further, it can be seen from the comparison of the results shown in Table 2 with those shown in Table 1 of Example 1 that the bleach accelerating effect (the decrease in the amount of remaining silver compared with the case wherein the bleach accelerating agent was not added) of the compounds according to the present invention are significantly attained when they are used in a bleach-fixing solution in comparison with the cases wherein they are used in a bleaching solution.
EXAMPLE 4
The same procedure as described in Example 3 was repeated except that the bleach-fixing solution was changed to one set forth below, and similar results to those in Example 3 were obtained.
Bleach-Fixing Solution
______________________________________Ammonium Iron (III) Diethylenediamine- 60.0 gpentaacetateDiethylenetriaminepentaacetic Acid 5.0 gSodium Sulfite 12.0 gAmmonium Thiosulfate 240 ml(700 g/l aq. soln.)Bleach Accelerating Agent (shown in Table 2 above)Water to make 1.0 lpH 7.5______________________________________
The pH was adjusted with aqueous ammonia (27% weight/weight).
EXAMPLE 5
The same procedure as described in Example 3 was repeated except that the bleach accelerating agent and the amount thereof used in the bleach-fixing solution were changed as shown in Table 3 below. The amount of remaining silver thus-obtained are shown in Table 3 below.
TABLE 3______________________________________ Amount of Bleach Solubility* Bleach Accelerating of Bleach Amount ofRun Accelerat- Agent Added Accelerating RemainingNo. ing Agent (mol/l) Agent Silver______________________________________19 -- -- -- 22.437 (12) 5 .times. 10.sup.-6 A 21.038 " 1.5 .times. 10.sup.-5 A 17.039 " 5 .times. 10.sup.-5 A 15.040 " 1.5 .times. 10.sup.-4 A 12.841 " 5 .times. 10.sup.-4 A 9.842 " 1.5 .times. 10.sup.-3 A 5.543 " 5 .times. 10.sup.-3 A 3.844 " 1.5 .times. 10.sup.-2 A 5.245 " 5 .times. 10.sup.-2 B 9.846 " 1.5 .times. 10.sup.-1 C 15.547 (31) 5 .times. 10.sup.-6 A 20.048 " 1.5 .times. 10.sup.-5 A 16.049 " 5 .times. 10.sup.- 5 A 14.850 " 1.5 .times. 10.sup.-4 A 14.051 " 5 .times. 10.sup.-4 A 10.552 " 1.5 .times. 10.sup.-3 A 4.553 " 5 .times. 10.sup.-3 A 2.754 " 1.5 .times. 10.sup.-2 B 2.555 " 5 .times. 10.sup.-2 C 5.056 " 1.5 .times. 10.sup.-1 9.8______________________________________ *A: Completely Soluble in the bleachfixing solution (at 40.degree. C.) B: Small amount of insoluble compound was observed C: Large amount of insoluble compound was observed
From the results shown in Table 3 above it is apparent that the compounds according to the present invention exhibit the smallest amounts of remaining silver when they are added to the bleach-fixing solution in the amount from 1.5.times.10.sup.-3 to 1.5.times.10.sup.-2 mol per liter of the solution, and the desilvering effect decreases when they are employed in amounts larger or smaller amount than the above range.
EXAMPLE 6
On a cellulose triacetate film support having a subbing layer was coated layers having the composition set forth below to prepare a multilayer color light-sensitive material, which was designated light-sensitive material B.
Composition of the light-sensitive material
With respect to the compositions of the layers, coated amounts are shown in units of g/m.sup.2, coated amounts of silver halide and colloidal silver are shown by a silver coated amount in units of g/m.sup.2, those of sensitizing dyes are shown as a molar amount per mol of silver halide being present in the same layer.
______________________________________First Layer: Antihalation LayerBlack colloidal silver 0.18 (as silver)Gelatin 0.40Second Layer: Interlayer2,5-Di-tert-pentadecylhydro- 0.18quinoneEX-1 0.07EX-3 0.02EX-12 0.002U-1 0.06U-2 0.08U-3 0.10HBS-1 0.10HBS-2 0.02Gelatin 1.04Third Layer: First Red-Sensitive Emulsion LayerMonodispersed Silver Iodobromide 0.55 (as silver)Emulsion (silver iodide: 6 mol %,average particle diameter: 0.6 .mu.m,coefficient of variation onparticle diameter: 0.15)Sensitizing Dye I 6.9 .times. 10.sup.-5Sensitizing Dye II 1.8 .times. 10.sup.-5Sensitizing Dye III 3.1 .times. 10.sup.-4Sensitizing Dye IV 4.0 .times. 10.sup.-5EX-2 0.350HBS-1 0.005EX-10 0.020Gelatin 1.20Fourth Layer: Second Red-Sensitive Emulsion LayerTabular Silver Iodobromide 1.00 (as silver)Emulsion (silver iodide: 10 mol %,average particle diameter: 0.7 .mu.m,average aspect ratio: 5.5,average thickness: 0.2 .mu.m)Sensitizing Dye I 5.1 .times. 10.sup.-5Sensitizing Dye II 1.4 .times. 10.sup.-5Sensitizing Dye III 2.3 .times. 10.sup.-4Sensitizing Dye IV 3.0 .times. 10.sup.-5EX-2 0.400EX-3 0.050EX-10 0.015Gelatin 1.30Fifth Layer: Third Red-Sensitive Emulsion LayerSilver Iodobromide Emulsion 1.60 (as silver)(silver iodide: 16 mol %,average particle diameter: 1.1 .mu.m)Sensitizing Dye IX 5.4 .times. 10.sup.-5Sensitizing Dye II 1.4 .times. 10.sup.-5Sensitizing Dye lII 2.4 .times. 10.sup.-4Sensitizing Dye IV 3.1 .times. 10.sup.-5EX-3 0.240EX-4 0.120HBS-1 0.22HBS-2 0.10Gelatin 1.63Sixth Layer: InterlayerEX-5 0.040HBS-1 0.020EX-12 0.004Gelatin 0.80Seventh Layer: First Green-Sensitive Emulsion LayerTabular Silver Iodobromide 0.40 (as silver)Emulsion (silver iodide: 6 mol %,average particle diameter: 0.6 .mu.m,average aspect ratio: 6.0,average thickness: 0.15 .mu.m)Sensitizing Dye V 3.0 .times. 10.sup.-5Sensitizing Dye VI 1.0 .times. 10.sup.-4Sensitizing Dye VII 3.8 .times. 10.sup.-4EX-6 0.260EX-1 0.021EX-7 0.030EX-8 0.025HBS-1 0.100HBS-4 0.010Gelatin 1.75Eighth Layer: Second Green-Sensitive Emulsion LayerMonodispersed Silver Iodobromide 0.80 (as silver)Emulsion (silver iodide: 9 mol %,average particle diameter: 0.7 .mu.m,coefficient of variation onparticle diameter: 0.18)Sensitizing Dye V 2.1 .times. 10.sup.-5Sensitizing Dye VI 7.0 .times. 10.sup.-5Sensitizing Dye VII 2.6 .times. 10.sup.-4EX-6 0.180EX-8 0.010EX-1 0.008EX-7 0.012HBS-1 0.160HBS-4 0.008Gelatin 1.10Ninth Layer: Third Green-Sensitive Emulsion LayerSilver Iodobromide Emulsion 1.2 (as silver)(silver iodide: 12 mol %,average particle diameter: 1.0 .mu.m)Sensitizing Dye V 3.5 .times. 10.sup.-5Sensitizing Dye VI 8.0 .times. 10.sup.-5Sensitizing Dye VII 3.0 .times. 10.sup.-4EX-6 0.065EX-11 0.030EX-1 0.025HBS-1 0.25HBS-2 0.10Gelatin 1.74Tenth Layer: Yellow Filter LayerYellow Colloidal Silver 0.05 (as silver)EX-5 0.08HBS-3 0.03Gelatin 0.95Eleventh Layer: First Blue-Sensitive Emulsion LayerTabular Silver Iodobromide 0.24 (as silver)Emulsion (silver iodide: 6 mol %,average particle diameter: 0.6 .mu.m,average aspect ratio: 5.7,average thickness: 0.15 .mu.m)Sensitizing Dye VIII 3.5 .times. 10.sup.-4EX-9 0.85EX-8 0.12HBS-1 0.28Gelatin 1.28Twelfth Layer: Second Blue-Sensitive Emulsion LayerMonodispersed Silver Iodobromide 0.45 (as silver)Emulsion (silver iodide: 10 mol %,average particle diameter: 0.8 .mu.m,coefficient of variation onparticle diameter: 0.16)Sensitizing Dye VIII 2.1 .times. 10.sup.-4EX-9 0.20EX-10 0.015HBS-1 0.03Gelatin 0.46Thirteenth Layer: Third Blue-Sensitive Emulsion LayerSilver Iodobromide Emulsion 0.77 (as silver)(silver iodide: 14 mol %,average particle diameter: 1.3 .mu.m)Sensitizing Dye VIII 2.2 .times. 10.sup.-4EX-9 0.20HBS-1 0.07Gelatin 0.69Fourteenth Layer: First Protective LayerSilver Iodobromide Emulsion 0.5 (as silver)(silver iodide: 1 mol %,average particle diameter: 0.07 .mu.m)U-4 0.11U-5 0.17HBS-1 0.90Gelatin 1.00Fifteenth Layer: Second Protective LayerPolymethyl methacrylate 0.54particle (diameter: about1.5 .mu.m)S-1 0.15S-2 0.05Gelatin 0.72______________________________________
Gelatin Hardener H-1 and a surface active agent were added to each of the layers in addition to the above described components.
The compounds employed for the preparation of light-sensitive material B are shown below.
U-1: Same as UV-1 used in Example 1
U-2: Same as UV-2 used in Example 1
U-3: Same as UV-3 used in Example 1
U-4: Same as UV-4 used in Example 1
U-5: Same as UV-5 used in Example 1
EX-1: Same as ExM-9 used in Example 1
EX-2: Same as ExC-2 used in Example 1
EX-3: Same as ExC-4 used in Example 1
EX-4: Same as ExC-7 used in Example 1
EX-5: Same as Cpd-1 used in Example 1
EX-6: Same as ExM-8 used in Example 1, except that the average molecular weight was 30,000
EX-7: Same as ExM-12 used in Example 1
EX-8: Same as ExY-13 used in Example 1
EX-9: Same as ExY-15 used in Example 1
EX-10: Same as ExC-16 used in Example 1, except that R was ##STR7## EX-11: Same as ExM-9 used in Example 1, except that R was H. EX-12: ##STR8## S-1: Same as Cpd-5 used in Example 1 S-2: Same as Cpd-6 used in Example 1
HBS-1: Tricresyl phosphate
HBS-2: Dibutyl phthalate
HBS-3: Bis(2-ethylhexyl) phthalate
HBS-4: Same as Solv-4 used in Example 1
H-1: Same as H-1 used in Example 1 ##STR9##
Light-sensitive material B thus-prepared was exposed in an exposure amount of 2.5 CMS using a light source having color temperature of 4800.degree. K. and then subjected to development processing according to the processing steps shown below. To the bleaching solution and the bleach-fixing solution were added the bleach accelerating agent as shown in Table 2 above in an amount of 5.times.10.sup.-3 mol per liter of the solution, respectively. The same test of desilveration as in Example 3 was carried out. The results was similar to those obtained in Example 3.
______________________________________Processing Processing ProcessingStep Time Temperature______________________________________Color Development 2 min. 30 sec. 40.degree. C.Bleaching 30 sec. 38.degree. C.Bleach-Fixing 1 min. 38.degree. C.Washing with Water 1 min. 38.degree. C.Stabilizing 30 sec. 38.degree. C.Drying 1 min. 60.degree. C.______________________________________
The composition of each processing solution used is illustrated below.
Color Developing Solution
Same as described in Example 1.
Bleaching Solution
______________________________________Ammonium Iron (III) Ethylenediaminetetra- 120 gacetate DihydrateDisodium Ethylenediaminetetraacetate 10.0 gAmmonium Bromide 100.0 gAmmonium Nitrate 10.0 gAqueous Ammonia (27% weight/weight) 15.0 mlWater to make 1.0 lpH 6.3______________________________________
Bleach-Fixing Solution
______________________________________Ammonium Iron (III) Ethylenediaminetetra- 50.0 gacetate DihydrateDisodium Ethylenediaminetetraacetate 5.0 gSodium Sulfite 12.0 gAqueous Solution of Ammonium Thiosulfate 240.0 mlAqueous Ammonia (27% weight/weight) 6.0 mlWater to make 1.0 lpH 7.2______________________________________
Washing Water
City water was passed through a mixed bed type column filled with an H type strong acidic cation exchange resin (Amberlite IR-l20B manufactured by Rohm & Haas Co.) and an OH type anion exchange resin (Amberlite IR-400 manufactured by Rohm & Haas Co.) to prepare water containing not more than 3 mg/l of calcium ion and magnesium ion. To the water thus-treated were added sodium dichloroisocyanulate in an amount of 20 mg/l and sodium sulfate in an amount of 0.15 g/l. The pH of the solution was in a range from 6.5 to 7.5.
Stabilizing Solution
______________________________________Formalin (37 wt %) 0.2 mlPolyoxyethylene-p-monononylphenylether 0.3 g(average degree of polymerization: 10)Disodium ethylenediaminetetraacetate 0.05 gWater to make 1.0 lpH 5.0 to 8.0______________________________________
EXAMPLE 7
On a cellulose triacetate film support having a subbing layer, layers having the composition shown below were coated to prepare a multilayer color light-sensitive material which was designated light-sensitive material C.
______________________________________First Layer: Antihalation LayerBlack colloidal silver 0.25 g/m.sup.2Ultraviolet Ray Absorbing 0.1 g/m.sup.2Agent U-1Ultraviolet Ray Absorbing 0.1 g/m.sup.2Agent U-2High Boiling Point Organic 0.1 g/m.sup.2Solvent Oil-1Gelatin 1.9 g/m.sup.2Second Layer: Interlayer-1Cpd-D 10 mg/m.sup.2High Boiling Point Organic 40 mg/m.sup.2Solvent Oil-3Gelatin 0.4 g/m.sup.2Third Layer: Interlayer-2Surface-fogged fine grain silver 0.05 g/m.sup.2iodobromide emulsion (iodide content: (as silver)1 mol %, average particle diameter:0.06 .mu.m)Gelatin 0.4 g/m.sup.2Fourth Layer: First Red-Sensitive Emulsion LayerSilver iodobromide emulsion (a 1/1 0.4 g/m.sup.2mixture of a monodisporsed cubic (as silver)emulsion having iodide content of5 mol % and average particle diameterof 0.2 .mu.m and a monodispersed cubicemulsion having iodide content of5 mol % and average particle diameterof 0.1 .mu.m) spectrally sensitizedwith Sensitizing Dye S-1 andSensitizing Dye S-2Coupler C-1 0.2 g/m.sup.2Coupler C-2 0.05 g/m.sup.2High Boiling Point Organic Solvent Oil-1 0.1 mg/m.sup.2Gelatin 0.8 g/m.sup.2Fifth Layer: Second Red-Sensitive Emulsion LayerSilver iodobromide emulsion (monodispersed 0.4 g/m.sup.2cubic emulsion having iodide content of (as silver)4 mol % and average particle diameterof 0.3 .mu.m) spectrally sensitizedwith Sensitizing Dye S-1 andSensitizing Dye S-2Coupler C-1 0.2 g/m.sup.2Coupler C-3 0.2 g/m.sup.2Coupler C-2 0.05 g/m.sup.2High Boiling Point Organic Solvent Oil-1 0.1 mg/m.sup.2Gelatin 0.8 g/m.sup.2Sixth Layer: Third Red-Sensitive Emulsion LayerSilver iodobromide emulsion (monodisporsed 0.4 g/m.sup.2cubic emulsion having iodide content of (as silver)2 mol % and average particle diameterof 0.4 .mu.m) spectrally sensitizedwith Sensitizing Dye S-1 andSensitizing Dye S-2Coupler C-3 0.7 g/m.sup.2Gelatin 1.1 g/m.sup.2Seventh Layer: Interlayer-3Dye D-1 0.02 g/m.sup.2Gelatin 0.6 g/m.sup.2Eight Layer: Interlayer-4Surface-fogged, fine grain silver 0.05 g/m.sup.2iodobromide emulsion (iodide content: (as silver)1 mol %, average particle diameter:0.06 .mu.m)Cpd-A 0.2 g/m.sup.2Gelatin 1.0 g/m.sup.2Ninth Layer: First Green-Sensitive Emulsion LayerSilver iodobromide emulsion (a 1/1 0.5 g/m.sup.2mixture of a monodisporsed cubic (as silver)emulsion having iodide content of5 mol % and average particle diameterof 0.2 .mu.m and a monodispersed cubicemulsion having iodide content of5 mol % and average particle diameterof 0.1 .mu.m) spectrally sensitizedwith Sensitizing Dye S-3 andSensitizing Dye S-4Coupler C-4 0.3 g/m.sup.2Cpd-B 0.03 g/m.sup.2Gelatin 0.5 g/m.sup.2Tenth Layer: Second Green-Sensitive Emulsion LayerSilver iodobromide emulsion (monodispersed 0.4 g/m.sup.2cubic emulsion having iodide content of (as silver)5 mol % and average particle diameterof 0.4 .mu.m) spectrally sensitizedwith Sensitizing Dye S-3 andSensitizing Dye S-4Coupler C-4 0.3 g/m.sup.2Cpd-B 0.03 g/m.sup.2Gelatin 0.6 g/m.sup.2Eleventh Laver: Third Green-Sensitive Emulsion LayerSilver iodobromide emulsion (tabular 0.5 g/m.sup.2emulsion having iodide content of (as silver)2 mol %, average particle diameter of0.5 .mu.m and aspect ratio of 5)Coupler C-4 0.8 g/m.sup. 2Cpd-B 0.08 g/m.sup.2Gelatin 1.0 g/m.sup.2Twelfth Layer: Interlayer-5Dye D-2 0.05 g/m.sup.2Gelatin 0.6 g/m.sup.2Thirteenth Layer: Yellow Filter LayerYellow Colloidal Silver 0.1 g/m.sup.2Cpd-A 0.01 g/m.sup.2Gelatin 1.1 g/m.sup.2Fourteenth Layer: First Blue-Sensitive Emulsion LayerSilver iodobromide emulsion (a 1/1 0.6 g/m.sup.2mixture of a monodispersed cubic (as silver)emulsion having iodide content of3 mol % and average particle diameterof 0.2 .mu.m and a monodispersed cubicemulsion having iodide content of3 mol % and average particle diameter of0.1 .mu.m) spectrally sensitized withSensitizing Dye S-5 and Sensitizing Dye S-6Coupler C-5 0.6 g/m.sup.2Gelatin 0.8 g/m.sup.2Fifteen Layer: Second Blue-Sensitive Emulsion LayerSilver iodobromide emulsion (tabular 0.4 g/m.sup.2emulsion having iodide content of (as silver)2 mol %, average particle diameter of0.5 .mu.m and aspect ratio of 7) spectrallysensitized with Sensitizing Dye S-7 andSensitizing Dye S-8Coupler C-5 0.3 g/m.sup.2Coupler C-6 0.3 g/m.sup.2Gelatin 0.9 g/m.sup.2Sixteenth Layer: Third Blue-Sensitive Emulsion LayerSilver iodobromide emulsion (tabular 0.4 g/m.sup.2emulsion having iodide content of (as silver)2 mol %, average particle diameter of1.0 .mu.m and aspect ratio of 7) spectrallysensitized with Sensitizing Dye S-7 andSensitizing Dye S-8Coupler C-6 0.7 g/m.sup.2Gelatin 11.2 g/m.sup.2Seventeenth Layer: First Protective LayerUltraviolet Ray Absorbing Agent U-1 0.04 g/m.sup.2Ultraviolet Ray Absorbing Agent U-3 0.03 g/m.sup.2Ultraviolet Ray Absorbing Agent U-4 0.03 g/m.sup.2Ultraviolet Ray Absorbing Agent U-5 0.05 g/m.sup.2Ultraviolet Ray Absorbing Agent U-6 0.05 g/m.sup.2Cpd-B 0.8 g/m.sup.2Dye D-3 0.05 g/m.sup.2Gelatin 0.7 g/m.sup.2Eighteenth Layer: Second Protective LayerSurface-fogged, fine grain silver iodo- 0.1 g/m.sup.2bromide emulsion (iodide content: (as silver)1 mol %, average particle diameter0.06 .mu.m)Polymethyl methacrylate particles 0.1 g/m.sup.2(average particle diameter: 0.06 .mu.m)Copolymer of methyl methacrylate and 0.1 g/m.sup.2acrylic acid (molar ratio; 4/6) (averageparticle diameter: 1.5 .mu.m)Silicon Oil 0.03 g/m.sup.2Fluorine-containing Surface Active Agent 3 g/m.sup.2W-1Gelatin 0.8 g/m.sup.2______________________________________
Gelatin hardener H-1 and a surface active agent were added to each of the layers in addition to the above described components.
The compounds employed for the preparation of Light-sensitive material C are illustrated below. ##STR10## Cpd-C Same as Cpd-6 used in Example 1 ##STR11## U-3: Same as UV-1 used in Example 1 U-4: Same as UV-2 used in Example 1
U-5: Same as UV-5 used in Example 1, except that R was C.sub.12 H.sub.25
U-6: Same as UV-5 used in Example 1 ##STR12## H-1: Same as H-1 used in Example 1 ##STR13##
Light-sensitive material C thus-prepared was exposed in an exposure amount of 10 CMS using a light source having a color temperature of 4800.degree. K., and then subjected to development processing according to the processing steps shown below. To the bleach-fixing solution were added the bleach accelerating property of these compounds were compared.
______________________________________ Processing ProcessingProcessing Step Time Temperature______________________________________First Development 6 min. 38.degree. C.First Washing with Water 45 sec. 38.degree. C.Reversal 45 sec. 38.degree. C.Color Development 6 min. 38.degree. C.Bleach-Fixing 4 min. 38.degree. C.Second Washing with Water (1) 1 min. 38.degree. C.Second Washing with Water (2) 1 min. 38.degree. C.Stabilizing 1 min. 25.degree. C.Drying 2 min. 50.degree. C.______________________________________
The composition of each processing solution used is illustrated below.
First Developing Solution
______________________________________Pentasodium Nitrilo-N,N,N- 2.0 gtrimethylenephosphonateSodium Sulfite 30 gPotassium Hydroquinone Monosulfonate 20 gPotassium Carbonate 33 g1-Phenyl-4-methyl-4-hydroxy- 2.0 gmethyl-3-pyrazolidonePotassium Bromide 2.5 gPotassium Thiocyanate 1.2 gPotassium Iodide 2.0 mgWater to make 1.0 lpH 9.60______________________________________
The pH was adjusted with hydrochloric acid or potassium hydroxide.
First Water Washing Solution
______________________________________Ethylene diaminetetramethylenephosphoric Acid 2.0 gDisodium Phosphate 5.0 gWater to make 1.0 lpH 7.00______________________________________
The pH was adjusted with hydrochloric acid or sodium hydroxide.
Reversal Solution
______________________________________Pentasodium Nitrilo-N,N,N- 3.0 gtrimethylenephosphonateStannous Chloride (dihydrate) 1.0 gp-Aminophenol 0.1 gSodium Hydroxide 8 gGlacial Acetic Acid 15 mlWater to make 1.0 lpH 6.00______________________________________
The pH was adjusted with hydrochloric acid or sodium hydroxide.
Color Developing Solution
______________________________________Pentasodium Nitrilo-N,N,N- 2.0 gtrimethylenephosphonateSodium Sulfite 7.0 gSodium Tertiary Phosphate (12 hydrate) 36 gPotassium Bromide 1.0 gPotassium Iodide 90 mgSodium Hydroxide 3.0 gCitrazinic Acid 1.5 gE-Ethyl-N-(.beta.-methanesulfonamidoethyl)- 11 g3-methyl-4-aminoaniline Sulfate3,6-Dithiaoctan-1,8-diol 1.0 gWater to make 1.0 lpH 11.80______________________________________
The pH was adjusted with hydrochloric acid or sodium hydroxide.
Bleach-Fixing Solution
______________________________________Ammonium Iron (III) Ethylenediamine- 80 gtetraacetate DihydroateDisodium ethylenediaminetetraacetate 5.0 gDihydrateAmmonium Thiosulfate 240 ml(700 g/l aqueous solution)Sodium Sulfite 12.0 gBleach Accelerating Agent (as shownin Table 4 below)Water to make 1.0 lpH 6.60______________________________________
The pH was adjusted with hydrochloric acid or sodium hydroxide.
Second Water Washing Solution
City (tap) water was passed through a mixed bed type column filled with an H type strong acidic cation exchange resin (Amberlite IR-l20B manufactured by Rohm & Haas Co.) and an OH type anion exchange resin (Amberlite IR-400 manufactured by Rohm & Haas Co.) to prepare water containing not more than 3 mg/l of calcium ion and magnesium ion. To the water thus-treated were added sodium dichloroisocyanulate in an amount of 20 mg/l and sodium sulfate in an amount of 0.15 g/l. The pH of the solution was in a range from 6.5 to 7.5.
Stabilizing Solution
______________________________________Formalin (37 wt %) 5.0 mlPolyoxyethylene-p-monononylphenylether 0.5 g(average degree of polymerization: 10)Water to make 1.0 lpH 6.60______________________________________
The pH was not adjusted.
TABLE 4______________________________________ Amount of Bleach* Remaining Accelerat- SilverRun No. ing Agent (.mu.g/cm.sup.2) Remark______________________________________57 -- 52.0 Comparison58 (A) 15.0 "59 (B) 17.0 "60 (C) 19.8 "61 (3) 10.2 Present Invention62 (6) 9.8 "63 (19) 7.0 "64 (21) 8.0 "65 (32) 5.2 "66 (38) 5.5 "67 (40) 5.5 "68 (42) 5.3 "______________________________________ *Amount added: 5 .times. 10.sup.-3 mol per liter of the bleachfixing solution.
The amount of remaining silver after the above-described processing was determined by X-ray fluorometric analysis. The results thus-obtained are shown in Table 4 above. From these results, it is apparent that the compounds according to the present invention exhibit a very large bleach accelerating ability in the bleach-fixing of a reversal color film.
EXAMPLE 8
The same test as described in Example 7 was conducted except for using the following processing steps and processing solutions.
______________________________________ Processing ProcessingProcessing Step Time Temperature______________________________________First Development 6 min. 38.degree. C.First Washing with Water 45 sec. 38.degree. C.Reversal 45 sec. 38.degree. C.Color Development 6 min. 38.degree. C.Bleaching Accelerating 45 sec. 38.degree. C.Bleaching 1 min. 38.degree. C.Second Washing with Water 45 sec. 38.degree. C.Fixing 3 min. 38.degree. C.Third Washing with Water 2 min. 38.degree. C.Stabilizing 1 min. 38.degree. C.Drying 2 min. 50.degree. C.______________________________________
First Developing Solution: Same as described in Example 7
First Washing with Water Solution: Same as described in Example 7
Reversal Solution: Same as described in Example 7
Color Developing Solution: Same as described in Example 7
Fixing Solution: Same as described in Example 7
Stabilizing Solution: Same as described in Example 7
Second Washing with Water Solution: Same as Second Washing with Water Solution described in Example 7.
Third Washing with Water Solution: Same as SEcond Washing with Water Solution described in Example 7.
Bleach Accelerating Solution
______________________________________Disodium Ethylenediaminetetraacetate 3.0 gBleach Accelerating Agent (as shown inTable 5 below)Water to make 1.0 lpH 4.5______________________________________
Bleaching Solution
______________________________________Potassium Persulfate 33 gSodium Chloride 18 gMonosodium Phosphate 7.0 gPhosphoric Acid (85% weight/weight) 14.7 gWater to make 1.0 lpH______________________________________
The results obtained are shown in Table 5 below.
TABLE 5______________________________________ Amount of Bleach* Remaining Accelerat- SilverRun No. ing Agent (.mu.g/cm.sup.2) Remarks______________________________________69 -- 103.5 Comparison70 (A) 20.5 "71 (B) 22.5 "72 (C) 28.0 "73 (10) 9.9 Present Invention74 (18) 8.1 "75 (34) 6.0 "76 (37) 6.5 "______________________________________ *Amount added: 5 .times. 10.sup.-3 mol l/l
As is apparent from the results shown in Table 5, the compounds according to the present invention exhibit a very large bleach accelerating ability in processing using a persulfate type bleaching solution.
EXAMPLE 9
Light-sensitive material A prepared in Example 1 was cut into a 35 m/m width strip, imagewise exposed to light under the condition of ISO 100, and then subjected to running processing according to the processing steps shown below with the processing solutions described below. The bleach-fixing solutions used and the contained the bleach accelerating agents were described in Table 6 below respectively. Before the running processing, the desilvering property of the processing solution just after the preparation was evaluated according to the same method as described in Example 1.
______________________________________ Amount Process- of*Processing Processing ing Tem- Capacity Replen-Step Time perature of Tank ishment______________________________________Color 2 min. 40.degree. C. 8 l 45 mlDevelopment 30 sec. Bleach- Fixing (1) Bleach- Fixing (2) 1 min. 20 sec. 40 sec. 40.degree. C. 40.degree. C. 4 l 2 l ##STR14## 25 ml Washing with Water (1) Washing with Water (2) 40 sec 1 min. 00 sec. 40.degree. C. 35.degree. C. 2 l 4 l ##STR15## 20 mlStabilizing 40 sec. 35.degree. C. 2 l 20 ml______________________________________ *Amount of replenishment per 1 meter of 35 m/m width strip **The bleachfixing steps (1) and (2) and washing with water steps (1) and (2) were conducted using a twostage countercurrent system from (2) to (1) respectively.
The composition of each processing solution used is illustrated below.
Color Developing Solution
______________________________________ Mother Liquor Replenisher______________________________________Diethylenetriaminepentaacetic acid 1.0 g 1.1 g1-Hydroxyethylidene-1,1- 2.0 g 2.2 gdiphosphonic acidSodium sulfite 4.0 g 4.4 gPotassium carbonate 30.0 t 32.0 gPotassium bromide 1.4 g 0.7 gPotassium iodide 1.3 mg --Hydroxylamine sulfate 2.4 g 2.6 g4-(N-Ethyl-N-.beta.-hydroxyethylamino)- 4.5 g 5.0 g2-methylaniline sulfateWater to make 1.0 l 1.0 lpH 10.00 10.05______________________________________
Bleach-Fixing Solution
______________________________________ Mother Liquor Replenisher______________________________________Ammonium thiosulfate 240 ml 260 ml(700 g/l aqueous solution)Sodium sulfite 18 g 20 gAmmonium iron (III) ethylenedi- 90 g 100 gaminetetraacetate dihydrateDisodium ethylenediaminetetra- 9.0 g 10.0 gacetate dihydrateBleach accelerating agent (shown in table 7 below)Water to make 1.0 l 1.0 lpH 6.5 6.0______________________________________
Washing Water
City (tap) water was passed through a column filled with an ion exchange resin (Amberlite MB-3 manufactured by Organo Co.) to form water having water quality shown below. Then, 0.02 g/l of sodium dichloroisocyanulate was added thereto.
______________________________________Calcium not more than 1 mg/lMagnesium not more than 0.5 mg/lpH 6.5 to 7.3______________________________________
Stabilizing Solution
______________________________________ Mother Liquor Replenisher______________________________________Formalin (37 wt %) 2.0 ml 3.0 mlPolyoxyethylene-p-monononylphenyl- 0.3 g 0.45 gether (average degree ofpolymerization: 10)Water to make 1.0 l 1.0 l______________________________________
The amount of processing was 30 meters per day and the processing was conducted continuously for 6 days. After stopping processing for one day, the desilvering property of the processing solution was evaluated again according to the same method as described in Example 1. The results thus-obtained are shown in Table 6 below.
TABLE 6______________________________________ Amount of Remaining Silver Bleach* Before AfterRun Accelerat- Running RunningNo. ing Agent (.mu.g/cm.sup.2) (.mu.g/cm.sup.2) Remark______________________________________77 -- 25.8 24.6 Comparison78 (D) 7.2 24.2 "79 (E) 5.9 24.5 "80 (F) 6.7 15.9 "81 (G) 7.1 18.0 "82 (6) 4.5 3.9 Present Invention83 (11) 4.2 3.5 "84 (12) 4.1 3.5 "85 (31) 3.0 2.4 "86 (32) 3.1 2.5 "87 (35) 3.1 2.6 "______________________________________ *Amount added: 5 .times. 10.sup.-3 mol per liter of the bleachfixing solution (both mother liquor and replenisher).
As is apparent from the results shown in Table 6 above, the compounds according to the present invention continuously exhibit excellent desilveration accelerating effects in the bleach-fixing solution.
EXAMPLE 10
On a cellulose triacetate film support having a subbing layer were coated layers having the compositions shown below to prepare a multilayer color light-sensitive material, which was designated Light-sensitive material D.
Regarding the compositions of the layers, coated amounts are shown in units of g/cm.sup.2, coated amounts of silver halide and colloidal silver are shown by a silver coated amount in a unit of g/m.sup.2, and those of sensitizing dyes are shown using a molar amount per mol of silver halide present in the same layer.
In the following, the coefficient of variation described below is a coefficient of variation as to particle diameter. The dispersion solvent means an organic solvent having a high boiling point for dispersing hydrophobic diffusion-resistant compounds contained in the layer.
______________________________________First Layer: Antihalation LayerBlack colloidal silver 0.2Gelatin 1.0Ultraviolet Ray Absorbing Agent UV-1' 0.1Ultraviolet Ray Absorbing Agent UV-2' 0.1Ultraviolet Ray Absorbing Agent UV-3' 0.1Dispersion Solvent Oil-1' 0.02Second Layer: InterlayerFine grain silver bromide (average 0.15particle diameter: 0.07 .mu.m)Gelatin 1.0Third Layer: First Red-Sensitive Emulsion LayerMonodispersed silver iodobromide 1.5emulsion (silver iodide: 2 mol %,average particle diameter: 0.3 .mu.m,coefficient of variation: 19%)Gelatin 0.9Sensitizing Dye S-A' 2.0 .times. 10.sup.-4Sensitizing Dye S-B' 1.0 .times. 10.sup.-4Sensitizing Dye S-C' 0.3 .times. 10.sup.-4Coupler Cp-1' 0.5Coupler CC-1' 0.2Coupler DIR-1' 0.02Coupler DIR-2' 0.01Dispersion Solvent Oil-1' 0.1Dispersion Solvent Oil-2' 0.1Fourth Layer: Second Red-Sensitive Emulsion LayerMonodispersed silver iodobromide 1.2emulsion (silver iodide: 5 mol %,average particle diameter: 0.7 .mu.m,coefficient of variation: 18%)Gelatin 1.0Sensitizing Dye S-A' 3.0 .times. 10.sup.-4Sensitizing Dye S-B' 1.5 .times. 10.sup.-4Sensitizing Dye S-C' 0.45 .times. 10.sup.-4Coupler Cp-2' 0.15Coupler Cp-3' 0.05Coupler CC-1' 0.03Coupler DIR-1' 0.01Dispersion Solvent Oil-2' 0.1Fifth Layer: InterlayerGelatin 1.0Compound Cpd-A' 0.05Dispersion Solvent Oil-2' 0.01Sixth Layer: First Green-Sensitive Emulsion LayerMonodispersed silver iodobromide 0.4emulsion (silver iodide: 3 mol %,average particle diameter: 0.3 .mu.m,coefficient of variation: 19%)Monodispersed silver iodobromide 0.8emulsion (silver iodide: 6 mol %,average particle diameter: 0.5 .mu.m)Gelatin 1.0Sensitizing Dye S-D' 1 .times. 10.sup.-4Sensitizing Dye S-E' 4 .times. 10.sup.-4Sensitizing Dye S-F' 1 .times. 10.sup.-4Coupler Cp-4' 0.4Coupler Cp-5' 0.4Coupler CC-2' 0.1Coupler DIR-3' 0.05Coupler DIR-2' 0.01Coupler DIR-3' 0.05Dispersion Solvent, Oil-2' 0.05Seventh Layer: Second Green-Sensitive Emulsion LayerPolydispersed silver iodobromide 0.9emulsion (silver iodide: 7 mol %,average particle diameter: 0.8 .mu.m,coefficient of variation: 15%)Gelatin 0.9Sensitizing Dye S-D' 0.7 .times. 10.sup.-4Sensitizing Dye S-E' 2.8 .times. 10.sup.-4Sensitizing Dye S-F' 0.7 .times. 10.sup.-4Coupler Cp-5' 0.15Coupler CC-2' 0.05Coupler DIR-3' 0.01Dispersion Solvent Oil-1' 0.08Dispersion Solvent Oil-3' 0.03Eighth Layer: Yellow Filter Layer: Antihalation LayerYellow Colloidal Silver 0.2Gelatin 0.8Cpd-A' 0.2Dispersion Solvent Oil-1' 0.1Ninth Layer: First Blue-Sensitive Emulsion LayerMonodispersed silver iodobromide 0.4emulsion (silver iodide: 6 mol %,average particle diameter: 0.3 .mu.m,coefficient of variation: 20%)Monodispersed silver iodobromide 0.4emulsion (silver iodide: 5 mol %,average particle diameter: 0.6 .mu.m,coefficient of variation: 17%)Gelatin 2.0Sensitizing Dye S-G' 1 .times. 10.sup.-4Sensitizing Dye S-H' 1 .times. 10.sup.-4Coupler Cp-6' 0.9Coupler DIR-1' 0.05Dispersion Solvent Oil-3' 0.9Tenth Layer: Second Blue-Sensitive Emulsion LayerMonodispersed silver iodobromide 0.5emulsion (silver iodide: 8 mol %,average particle diameter: 1.5 .mu.m,coefficient of variation: 14%)Gelatin 0.5Sensitizing Dye S-G' 5 .times. 10.sup.-5Sensitizing Dye S-H' 1 .times. 10.sup.-5Coupler Cp-6' 0.2Coupler DIR-1' 0.02Dispersion Solvent Oil-3' 0.01Eleventh Layer: First Protective LayerGelatin 0.5Ultraviolet Ray Absorbing Agent UV-1' 0.1Ultraviolet Ray Absorbing Agent UV-2' 0.1Ultraviolet Ray Absorbing Agent UV-3' 0.1Ultraviolet Ray Absorbing Agent UV-4' 0.1Twelfth Layer: Second Protective LayerFine grain silver bromide (average 0.25particle diameter: 0.07 .mu.m)Gelatin 0.5Polymethyl methacrylate particles 0.2(diameter: 1.5 .mu.m)Formaldehyde deactivator Cpd-B' 0.5______________________________________
Surface active agent W-1' and Hardening agent H-1' was added to each of the layers in addition to the above described components.
The compounds employed for the preparation of Light-sensitive material D are illustrated below. ##STR16## S-B': Same as Sensitizing Dye III used in Example 6 S-C': Same as Sensitizing Dye II used in Example 6 ##STR17## Cp-1': Same as ExC-1 used in Example 1, except R.sub.1 was Cl and R.sub.2 was CN. ##STR18## Oil-1': Same as Solv-3 used in Example 1 Oil-2': Same as Solv-1 used in Example 1 ##STR19## UV-1': Same as UV-2 used in Example 1 ##STR20## UV-3': Same as UV-1 used in Example 1 ##STR21##
The same test as described in Example 3 was conducted using Light-sensitive material D thus-prepared in place of Light-sensitive material A, and similar results to those in Example 3 were obtained.
EXAMPLE 11
Using the processing solutions (Run Nos. 82 to 87) after conducting continuous processing according to the present invention described in Example 9, imagewise exposed light-sensitive materials shown below were processed. Desilveration was sufficiently performed and good photographic properties were obtained.
Super HR 100, Super HR 200, Super HR 400 and Super HR 1600 each manufactured by Fu]i Photo Film Co., Ltd.,
SRV 100, SR 200, SR 400, SR 1600, GX 100, GX 400 and GX 3200 each manufactured by Konishiroku Photographic Industries,
VRG 100, VR 200, VR 400, VR 1000 and VRG 400 each manufactured by Eastman Kodak Co.,
XRS 100, XR 200 and XR 400 each manufactured by Agfa Gevaert, and
HR 100, HR 200 and HR 400 each manufactured by 3M.
While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Number	Date	Country	Kind
62-274095	Oct 1987	JPX
62-277580	Nov 1987	JPX

Number	Name	Date
4596764	Ishimaru	Jun 1986
4745048	Kishimoto et al.	May 1988
4756918	Ueda et al.	Jul 1988
4804618	Ueda et al.	Feb 1989

Method for processing a silver halide color photographic material

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)

US Referenced Citations (4)

Foreign Referenced Citations (1)

Non-Patent Literature Citations (2)

Entry
English Abstract of Jap. Pat. No. 63-261362 Oct. 28, 1988.
Ueda et al., "Processing Method for Silver Halide Color Photographic Sensitive Material".