Patent Application
20170258563
This patent application claims the benefit of and priority to German Patent Application No. 10 2015 122 861.0, filed on Dec. 28, 2015, which is herein incorporated by reference for all purposes.
The invention relates, inter alia, to a method for the preparation of a blank of a ceramic material, in particular a blank to be used for the preparation of a dental restoration, wherein a first ceramic material and then a second ceramic material of different compositions are filled into a die and wherein the materials are pressed and after pressing are sintered.
The invention also relates to a pre-sintered or fully-sintered blank to be used for the preparation of a dental restoration, such as a dental framework, crown, partial crown, bridge, cap, veneer, abutment, pin construction, in particular a crown or partial crown, comprising a ceramic material which in particular contains zirconium dioxide and has regions of different compositions.
U.S. Pat. No. 8,936,848 B2 discloses a blank of zirconium dioxide that is used for the preparation of a tooth replacement and comprises a number of layers of different chemical compositions. The individual layers thereby have different percentages of yttrium oxide.
A body of zirconium dioxide exhibits a decrease or increase in chromacity along a straight line in the L*a*b* color space (US 2014/0328746 A1).
A blank of zirconium dioxide for the preparation of dental objects in accordance with WO 2014/062375 A1 has at least two material regions which have different percentages of tetragonal and cubic crystal phases, wherein in one of the regions the quotient is greater than 1 and in the other region the quotient is lower than 1.
EP 2 371 344 A1 relates to a ceramic body which is enriched with a stabilizing agent from the surface to a desired depth.
Zirconium dioxide is used as a ceramic material to produce dental restorations. A framework can be milled, for example, from a blank of zirconium dioxide and can then be sintered. In the following processing stages, a veneer is applied manually to the framework, wherein at least one incisor material is applied and fused. All of these process measures are time-consuming and moreover do not ensure that the dental restoration will meet the requirements.
It is an object of the present invention to develop a method of the aforementioned type in such a way that the disadvantages of the prior art are avoided and in particular that a dental restoration can be produced from a ceramic material without laborious finishing, which satisfies aesthetic requirements and moreover is of high strength in regions under severe loads.
To achieve this aim it is proposed, inter alia, that a layer of a first ceramic material is filled into the die and that a first open cavity is formed in the layer, that the second ceramic material is filled into the first open cavity and that the materials are pressed together and are then heat-treated.
According to the invention, a layer of pourable material is first filled into a die. This may, for example, be a colorless zirconium dioxide granular material that has a bulk density between 1 g/cm3 and 1.4 g/cm3, in particular in the region between 1.15 g/cm3 and 1.35 g/cm3. Following filling of the granular material, which has a grain size D50 between 40 μm and 70 μm, an open cavity is formed, for example by means of a press plunger. This is carried out, for example, by expelling parts of the first ceramic material and/or lightly compacting them. Thus, in the so-formed recess or cavity, which in particular has a substantially conus-like geometry, the second ceramic material is filled, if a crown or partial crown is to be produced from the blank, the conus-like shaped recess or cavity is aligned with the geometry of a tooth stump or an abutment, so that the materials are pressed together.
There is also the possibility of forming a further, second open cavity in the second ceramic material that fills the first open cavity. This step can accompany the concomitant pressing of all materials.
Compaction of the materials takes place independently thereof.
Compression is preferably carried out at a pressure preferably between 1000 bar and 2000 bar. A density of approximately 3 g/cm3 is attained. Debinding and pre-sintering at a temperature between 700° C. and 1100° C. are then carried out, in particular in a range between 800° C. and 1000° C., over a time between 100 minutes and 150 minutes.
The debinding and pre-sintering should be carried out in such a way that a breaking strength between 10 MPa and 60 MPa, in particular between 10 MPa and 40 MPa is achieved, measured in accordance with DIN-ISO 6872.
Where a second open cavity is formed in the second ceramic material and a third ceramic material is filled into it, then this composition should differ from that of the second ceramic material, in particular in having a lower translucence and/or a higher bending strength than the second/first material.
In particular, according to the invention a number of first open cavities are provided in the layer of the first ceramic material, and the second ceramic material is filled into these. This yields a number of distinct, separated blank sections, so-called nests, so that after the pre-sintering a number of dental restorations can be derived from the sections of such a blank, in particular through milling and/or grinding. Thereby it is possible for the dimensions of the blank sections to differ from one another to derive restorations of different geometries which can also differ in the geometric arrangement of the respective root-side/dentine-side material regions. It is therefore possible to obtain teeth of different shapes from one blank, according to the number of nests/blank sections and their geometries. As already mentioned, the dentine cores are formed from the second regions and the incisors from the first region.
The invention in particular provides for the thermal expansion coefficient of the second ceramic material to be 0.2 μm/m*K to 0.8 μm/m*K higher than the thermal expansion coefficient of the first ceramic material. As a result of the different thermal expansion coefficients of the materials, a compressive stress is created in the first material i.e. in the incisor material which leads to an increase in strength of the dental restoration derived from the blank.
Furthermore, there is the possibility of coloring the ceramic materials to the desired extent, in particular such that for the first region an incisor material is used which is more translucent and less colored compared to the second ceramic material.
If a dental restoration or other molded body is preferably derived from the pre-sintered blank, then there is naturally also the possibility that the blank is first fully-sintered to then produce the molded body, in particular by milling or grinding.
Independently of when the blank is sintered through, it is provided in particular for the complete sintering to be carried out over a period of between 10 minutes and 250 minutes at a temperature in the range between 1300° C. and 1600° C. Sintering may also be carried out at a slightly higher temperature.
If sintering is performed at a temperature which, for example, is 100° C. above the temperature given by the manufacturer of the starting material, and above the time recommended by the manufacturer for the complete sintering, this is referred to as over-sintering.
The present values apply in particular when the starting material substantially contains zirconium dioxide, in particular more than 80 wt %.
Yttrium oxide is in particular added to the zirconium dioxide, but calcium oxide, magnesium oxide and/or ceroxide may also be added.
If the ceramic material is colored, then in particular a color-imparting oxide from elements of the group Pr, Er, Tb, Fe, Co, Ni, Ti, V, Cr, Cu, Mn, preferably Fe2O3, Er2O3 or Co3O4 is used.
The invention is therefore also characterized by the fact that the ceramic materials used contain zirconium dioxide to which is added yttrium oxide (Y2O3), calcium oxide (CaO), magnesium oxide (MgO) and/or cerium oxide (CeO2), in particular yttrium oxide, wherein the first ceramic material differs from the material of the second ceramic material in terms of color and/or crystal forms stabilized at room temperature.
Further, it is provided for the first and/or second ceramic material to be such that the percentage of yttrium oxide in the second material is in the range 4.5 wt % to 7.0 wt % and/or the percentage in the first material is in the range 7.0 wt % to 9.5 wt %, wherein the percentage of yttrium oxide in the first ceramic material is higher than that in the second material.
The materials of the first and also the second region should thereby be selected such that the quotient of the tetragonal crystal phase to the cubic crystal phase of zirconium dioxide of both regions after pre-sintering is ≧1.
The following composition in wt % is preferred as the basic material for the first and second ceramic material:
It is also possible for additional binding agents to be added. This is not taken into account in the above statement of percentage by weight.
According to the teaching of the invention, after full sintering a monolithic dental restoration is obtained, which in principle does not have to be veneered, but if so then there is no departure from the invention.
A pre-sintered or fully sintered blank for use in producing a dental restoration such as a dental framework, crown, partial crown, bridge, cap, veneer, abutment, pin construction, in particular crown or partial crown, consisting of a ceramic material, which in particular contains zirconium dioxide and regions of different compositions, wherein a first region is of a first ceramic material and at least one second region is of a second ceramic material and the regions are adjacent to each other, is characterized by the fact that at least one second region extends within the first region and has an outer geometry that tapers from a basal region. Thereby, the basal region should extend in the region of an outer surface of the first region, and preferably merge with it.
It is also possible for the second region extending from the basal region to have a cavity.
Independently of this, the second region in its outer geometry has a conus-like extending geometry.
There is also the possibility that a third region extends within the second region, said third region consisting of a third ceramic material of a composition which deviates from that of the second ceramic material.
It is to be emphasized and in accordance with this invention that a number of second regions are surrounded by the first region, in particular some of the plurality of second regions differ in their external geometries.
Thus, for example, crowns or artificial teeth of different geometries can be produced, which have a higher strength in the dentine than in the incisal region. For this purpose upon derivation of the dental restoration from the blank, the dentine is formed in the region of sections of the second region and the incisal region is formed from sections of the first region of the blank.
The invention is further characterized in that the blank contains zirconium dioxide to which yttrium oxide has been added, that the percentage of yttrium oxide in the second or third ceramic material lies between 4.5 wt % and 7.0 wt % and in the first ceramic material lies between 7.0 wt % and 9.5 wt %, wherein the percentage of yttrium oxide in the first ceramic material is greater than in the second ceramic material.
The lower yttrium content in the material of the second region results in a higher strength in comparison to that of the first region.
Furthermore, there is the possibility that the ceramic material of the second region is colored and that of the first region is colored to a lesser degree or not at all, so that a higher translucency than in the second region results.
A dental restoration, in particular tooth, crown or partial crown, is characterized by comprising a first layer of a first material which extends on the incisial side and a root side-extending second layer consisting of a second ceramic material, in that the first layer has a higher translucency and/or a lower strength than the second layer and that the first layer has a thermal expansion coefficient of about 0.2 μm/m*K to 0.8 μm/m*K lower than that of the second layer.
Further details, advantages and features of the invention result not only from the claims and the features disclosed therein alone and/or in combination but also from the following description of the example embodiments shown in the drawings.
In the drawings:
The teaching of the invention is illustrated by reference to the figures, in which the same elements are basically given the same reference numerals, wherein in particular dental restorations are produced from a ceramic material having a monolithic structure such that after complete sintering an immediately usable monolithic tooth replacement is available.
To this end, the invention provides for the preparation of a blank, which has regions of ceramic material with differing compositions and thus properties, has desired optical and mechanical properties according to the restoration to be produced, which, as mentioned, offer the possibility of immediate usage of the tooth replacement monolithically fabricated after full sintering without, for example, having to apply incisor material by hand.
Further, specifically desired strength values are attainable in the ranges in which high loads occur. Desired optical properties can be achieved.
With reference to
Thus a pourable granulate in the form of a first ceramic material 14 is filled into the die 10 of a pressing tool 12, which is in particular a zirconium dioxide stabilized with yttrium oxide, which can have the following composition in wt %:
A binding agent may also be added, but is not taken into consideration in the above percentage by weight values.
However, in particular it is provided for the composition to contain coloring oxides only in small amounts or not at all, for example ≦0.5 wt %, as the first ceramic material 14 is used as an incisor material, so that a high translucency is desired. As a result of the relatively high percentage of yttrium oxide, the tetragonal crystal phase is only 50 to 60% in the incisal region of the produced mold part, i.e., the dental restoration, and the remainder is the cubic and monoclinic crystal phase.
Then, by means of a press plunger 16 an open cavity 18 is formed in a material 14 or in a layer formed from this material. By means of the press plunger, the material 14 is displaced or slightly compacted. After the cavity 18 is formed (
Thereby, the coloring oxide or oxides should be present in an amount that results in a desired tooth color, since the dentine of the tooth to be produced is formed from the second ceramic material 20. The relatively low percentage of Y2O3 further ensures that the dentine of the fully-sintered tooth replacement has a high tetragonal phase content of at least 85%, preferably at least 90%, thus yielding a high strength.
After filling of the second ceramic material 20 into the cavity 18 (
With regard to the ceramic materials 14, 20 it should also be noted that they have a bulk density between 1 g/cm3 and 1.4 g/cm3. After pressing, the density is approximately 3 g/cm3.
As can be seen from
However, in accordance with
Irrespective of whether the second cavity 26 is present or not, a pre-sintering of the blank 28 is carried out after pressing at a temperature in particular in the range between 800° C. and 1000° C. over a time period between 100 minutes and 150 minutes. There is initially a debinding and then pre-sintering. The density of the blank 28 after the pre-sintering is approximately 3 g/cm3. The breaking strength of the pre-sintered blank 28 should be between 10 MPa and 60 MPa.
The blank 28 is provided with a holder 30, so that the blank 28 can be worked for example in a milling or grinding machine to derive a dental restoration such as a tooth from the blank 28, as explained with reference to
As
After removal of the so virtually positioned tooth 42 from the blank 28, a tooth replacement is available, which in principle can be used directly, in particular does not require any veneer. A monolithic tooth 42 is prepared on the basis of the teaching of the invention. In this case, the preparation from the blank 28 is made easier in that the second region 34 already has an open cavity 26, as described with reference to
The teaching of the invention introduces the possibility of forming a blank 48 that has a plurality of regions 52, 54, 56, that are made of the second and optionally the third ceramic material, and can have different geometries (
As can be seen in particular from
The base region 35/the base surface that limits it on the underside merges with the lower side of the base surface 33 of the first region 32.
To prepare the blank sections 52, 54, 56 also referred to as nests, it is necessary as described with reference to
With regard to the physical properties of the materials 14, 20 it is to be noted that in addition to a difference in translucency and strength they should also have different thermal expansion coefficients. In particular, the invention provides for the first ceramic material 14 after full sintering to have a thermal expansion coefficient that is 0.2 μm/m*K to 0.8 μm/m*K lower than the second region 38, 52, 54, 56 formed from the second ceramic material 20. As a result of this a compression stress is generated in the first region 50, i.e., in the incisor material, which leads to an increase in strength.
With regard to the blanks 28, 48 it is to be noted that these can have a cuboid shape, for example the dimensions 18×15×25 mm or a disk shape, for example with a diameter of 100 mm, without thereby affecting the teaching of the invention. This brings in particular as explained by reference to
Since the position of one or more second regions 52, 56, i.e., nests, optionally with different geometries is known, they can be stored in a data record. Then, the restorations to be produced, which are available as CAD data sets, are positioned relative to and in the blank sections so that the tooth replacement can be derived from the blank by milling and/or grinding.