The present application claims priority 35 U.S.C. §119 to European Patent Publication No. EP 13198868.5 (filed on Dec. 20, 2013), which is hereby incorporated by reference in its entirety.
Embodiments relate to a method for producing a vehicle body or a vehicle body module, such vehicle body module to be in particular a subassembly of a vehicle.
For the production of vehicle bodies or vehicle body modules, it is known to use sandwich components. The sandwich components may use pre-impregnated semifinished products, in particular what are termed “prepregs”, the matrix of the semifinished products being cured in a furnace, in particular in an autoclave, before the sandwich components are used further. The cured sandwich components are then joined to further vehicle body parts by known joining methods, such as spot welding, clinching, etc. The finished vehicle body or the vehicle body module is then coated, for example, by way of cathodic dip coating.
European Patent Publication No. EP 2529920 A2 discloses a method for producing a hybrid component for a motor vehicle, in which a metallic base profile is provided with a reinforcing element made of fibre composite material, these being pressed together in a pressing tool. In this process, the pressing tool is heated in order to achieve curing of the fibre composite material.
German Patent Publication No. DE 10 2011 113 319 A1 describes a method for producing a vehicle body component having a metallic main body and an areally connected reinforcement made of fibre-reinforced plastic (FRP), the reinforcement being sprayed onto the main body. After the FRP has been applied, the curing of the resin takes place.
In accordance with embodiments, a method for producing a vehicle body or a vehicle body module is provided which may be carried out easily and cost-effectively.
In accordance with embodiments, a method for producing a vehicle body or a vehicle body module, may include at least one of: producing at least one sandwich component, comprising a first metal sheet layer, a semifinished product layer formed by a non-cured semifinished product pre-impregnated with a matrix, and a second metal sheet layer; joining the sandwich component into a vehicle body part to form a vehicle body or a vehicle body module, the matrix of the semifinished product layer of the sandwich component not being cured; and dip coating and drying the vehicle body or the vehicle body module, the matrix of the semifinished product layer of the sandwich component being cured.
In accordance with embodiments, a vehicle body module, such as a subassembly of a vehicle, or equally substantially an entire vehicle body of a vehicle is produced with at least one sandwich component, the fibre composite matrix of which has not yet been cured. The time-consuming and costly curing of the sandwich component or of the individual sandwich components is therefore dispensed with. Embodiments are based here on the concept that it is possible to handle the sandwich component comprising a middle pre-impregnated, non-cured semifinished product layer and outer metal sheet layers even if the semifinished product has not yet been cured, and therefore, the dip coating and drying method carried out for the vehicle body module may be utilized for the curing. This is promoted in particular by the viscosity of the matrix used.
Developments of embodiments are specified in the dependent claims, the description and also the accompanying drawings.
In accordance with embodiments, the vehicle body module is a subassembly. By way of example, the subassembly of a vehicle or else equally an entire vehicle body of a vehicle is therefore produced and coated.
In accordance with embodiments, the sandwich component is produced preferably by pressing the semifinished product layer onto the first metal sheet layer and by pressing the second metal sheet layer onto the semifinished product layer. It is also possible for a plurality of semifinished product layers to be stacked one on top of another and to be arranged between the metal sheets.
In accordance with embodiments, the matrix of the semifinished product layer may be exclusively used as an adhesive for producing the sandwich component. It is then possible to dispense with the use of an additional adhesive for joining the layers of the sandwich component.
In accordance with embodiments, before the sandwich component is produced, the metal sheet for the first and the second metal sheet layers is cut to size, cleaned and dried. The surface treatment of the metal sheet layers is important in particular for securely joining the layers by way of the matrix of the semifinished product.
In accordance with embodiments, at least one of the metal sheet layers of the sandwich component may comprise a plurality of separate metal sheets. It is also the case that the semifinished product layer of the sandwich component may comprise a plurality of separate semifinished products, which may be arranged on a common metal sheet layer.
In accordance with embodiments, after the sandwich component has been produced and before the sandwich component is joined into a vehicle body part, the sandwich component is formed, in particular at temperatures of below 70° C., particularly preferably without heating or at approximately 60° C., such that the matrix has not yet been cured. The forming may be effected in particular by deep drawing.
In accordance with embodiments, the first and second metal sheet layers of the sandwich component are joined to one another at least in marginal regions of the sandwich component, if appropriate also in core regions. This may be effected in particular by way of spot welding, friction stir welding, riveting, clinching and/or adhesive bonding.
In accordance with embodiments, the sandwich component is joined into a vehicle body part to form a vehicle body or a vehicle body module by welding, riveting, clinching, screwing and/or adhesive bonding.
In accordance with embodiments, the dip coating and drying of the vehicle body module or of the vehicle body comprises a drying phase at temperatures of above 100° C., preferably above 120° C., for at least 10 minutes, the matrix of the semifinished product layers of the sandwich components being cured substantially in the drying phase. Here, “substantially” waythat the curing is effected to an extent of at least 80%, better to an extent of at least 90%, during this drying phase.
In accordance with embodiments, the drying phase takes place at temperatures of 155° C. to 185° C. for at least 15 minutes. The drying phase may be followed by topcoat application at temperatures of at least 140° C., such that the matrix of the semifinished product layers of the sandwich components is cured further. It is preferable, however, that complete curing is effected, i.e. to an extent of approximately 100%, already in the drying phase.
In accordance with embodiments, a method for producing a vehicle body may include at least one of: producing at least one sandwich component having a first metal sheet layer, a semifinished product layer formed by a non-cured semifinished product pre-impregnated with a matrix, and a second metal sheet layer; forming the vehicle body by joining the sandwich component into a vehicle body part, the matrix of the semifinished product layer of the sandwich component being uncured; and dip coating and drying the vehicle body, the matrix of the semifinished product layer of the sandwich component being cured during the dip coating and drying of the vehicle body.
In accordance with embodiments, a method for producing a vehicle body module may include at least one of: producing at least one sandwich component having a first metal sheet layer, a semifinished product layer formed by a non-cured semifinished product pre-impregnated with a matrix, and a second metal sheet layer; joining the sandwich component into a vehicle body part to thereby form the vehicle body in which the matrix of the semifinished product layer of the sandwich component is uncured; and dip coating and drying the vehicle body, the matrix of the semifinished product layer of the sandwich component being cured during the dip coating and drying of the vehicle body.
Embodiments will be illustrated by way of example in the drawings and explained in the description below.
Embodiments are not restricted to CFRP fabric layers. It is also possible to use other materials, such as GFRP, aramid fibres, basalt fibres, cellulose fibres, etc. Furthermore, it is also possible for various materials to be mixed, and in addition the fibre orientation or the thickness of the layers may vary.
The prepregs which are used have a tacky state and retain this up to a later process step for the coating. The viscosity of the resin permits further processing.
As illustrated in
As illustrated in
As illustrated in
The preparation of the semifinished product 3 will be described in more detail hereinbelow.
The prepreg semifinished product 3 may comprise one or a plurality of fabric layers 7, as illustrated in
Optionally, it is also possible for individual fabric layers 7 alone to be cut. Individually cut fabric layers 7 have to be stacked to the desired number by hand or using a robot. The individual fabric layers 7 may have the same fibre orientation (unidirectional, anisotropic) or different fibre directions (multidirectional, quasi-isotropic). The previously cut metal sheets 2, 5 have to be cleaned and degreased by hand or by way of a spraying system since they are usually supplied covered in oil. Then, the metal sheets are dried. A flawless surface is important for the subsequent joining process so that the resin adheres.
The production of the sandwich component 1 will be described on the basis of
As illustrated in
As illustrated in
As illustrated in
As illustrated in
Optionally, it is possible to use a plurality of semifinished products 3 of differing type (resin, fibre type, direction, etc.) and dimension (length, width, height). The metal sheet layers 2, 5 bond to the semifinished product layer 3 by way of the matrix of the semifinished product 3. Optionally, an additional adhesive may also be used.
As illustrated in
A preliminary pressing and forming process may subsequently be effected. The sandwich 1 is removed from the apparatus for forming the sandwich stack and inserted into a press 11.
As illustrated in
As illustrated in
Further steps such as further forming, perforating or the pressing in of sleeves or bushings are optionally effected. For the pressing in of bushings, the sandwich component 1 has to be held down by way of holding-down devices 15.
As illustrated in
As illustrated in
As illustrated in
This is followed by a coating process (not illustrated) for the vehicle body or the vehicle body module and the curing of the sandwich. The vehicle body or the module undergoes a conventional coating process. The coating process may comprise the following process steps, for example in a bodywasher and pretreatment system: degreasing, activation, phosphating, passivation.
This is followed by the actual cathodic dip coating (CDC): the vehicle body passes through one or more dipping basins for CDC coating and cleaning. The prevailing temperatures of up to 60° C. initially are not sufficient to cure the component. After these baths, the CDC coating is burned into the vehicle body by way of drying at 155-185° C. for at least 15 minutes. In this process, the vehicle body passes through a dryer with heat retention and cooling phases.
The available time and temperature window, without heating and cooling times, of at least 15 minutes at 155-185° C. is sufficient for curing the resin at least to an extent of 95%. Up to the end of the coating process, high temperatures are again applied during topcoat application, at least 140° C. for 10 minutes, at which the component is cured further.
As illustrated in
The term “coupled” or “connected” may be used herein to refer to any type of relationship, direct or indirect, between the components in question, and may apply to electrical, mechanical, fluid, optical, electromagnetic, electromechanical or other connections. In addition, the terms “first,” “second,” etc. are used herein only to facilitate discussion, and carry no particular temporal or chronological significance unless otherwise indicated.
Those skilled in the art will appreciate from the foregoing description that the broad techniques of the embodiments may be implemented in a variety of forms. Therefore, while the embodiments have been described in connection with particular examples thereof, the true scope of the embodiments should not be so limited since other modifications will become apparent to the skilled practitioner upon a study of the drawings, specification, and following claims.
Number | Date | Country | Kind |
---|---|---|---|
13198868 | Dec 2013 | EP | regional |
Number | Name | Date | Kind |
---|---|---|---|
20060134395 | Sigler et al. | Jun 2006 | A1 |
20100098910 | Naritomi | Apr 2010 | A1 |
Number | Date | Country |
---|---|---|
102186666 | Sep 2011 | CN |
102806621 | Dec 2012 | CN |
103619578 | Mar 2014 | CN |
1557342 | Feb 1972 | DE |
102011015071 | Sep 2012 | DE |
102011113319 | Mar 2013 | DE |
2529920 | Dec 2012 | EP |
1181688 | Feb 1970 | GB |
2011100734 | Aug 2011 | WO |
Number | Date | Country | |
---|---|---|---|
20150174642 A1 | Jun 2015 | US |