Claims
- 1. Method for producing a hard metal body having increased wear resistance, the hard metal body containing at least one of the binder metals iron, cobalt and nickel and at least one of the carbides of the elements titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten, and being produced by way of sintering and having a nitrogen containing surface, comprising: directly after a final sintering at a temperature between 1400.degree. C. and 1500.degree. C. of a hard metal body containing the binder metal and carbide, subjecting the body to a cooling cycle to cool the body to a temperature of 800.degree. C. to 1450.degree. C., and at any time after the body has been cooled by at least 50.degree. C. from its final sintering temperature of 1400.degree. C. to 1500.degree. C. and during said cooling cycle, subjecting the body to a pressure between 50 bar and 5000 bar in a sintering autoclave at a temperature between 800.degree. and 1450.degree. C. and in an atmosphere comprising nitrogen, to enrich the hard metal body with nitrogen and to nitride the surface.
- 2. Method as defined in claim 1 wherein the pressure of the nitrogen atmosphere is between 50 and 2000 bar.
- 3. Method as defined in claim 1 wherein the enrichment treatment lasts for at least 15 minutes.
- 4. Method as defined in claim 3 wherein the enrichment treatment duration is between 1 and 10 hours.
- 5. Method as defined in claim 1 wherein the enrichment treatment of the hard metal body is effected in the presence of nitrogen, or a nitrogen-noble gas mixture, or a nitrogen-noble gas-carbon monoxide mixture, or a nitrogen-noble gas-C.sub.n H.sub.m mixture, or a nitrogen-C.sub.n H.sub.m mixture.
Priority Claims (1)
Number |
Date |
Country |
Kind |
2717842 |
Apr 1977 |
DEX |
|
CROSS REFERENCE TO RELATED APPLICATION
This application is a continuation of Applicants' copending United States Application Ser. No. 887,812, filed Mar. 17th, 1978 abandoned.
US Referenced Citations (5)
Foreign Referenced Citations (4)
Number |
Date |
Country |
314212 |
Mar 1974 |
ATX |
331049 |
Jul 1976 |
ATX |
1304291 |
Jan 1973 |
GBX |
1437069 |
May 1976 |
GBX |
Non-Patent Literature Citations (3)
Entry |
Metals Handbook 8th ed. vol. a, Heat Treating, Cleaning and Finishing, American Society for Metals 1964, pp. 161-162. |
Rudiger et al., "Verschleiss-Schutzschichten auf Hartmetablen" pp. 267-282, May 1977, Wear. |
VDI-Z 99, No. 36, Dec. 21st (1957). |
Continuations (1)
|
Number |
Date |
Country |
Parent |
887812 |
Mar 1978 |
|