The invention relates to the technical field of producing a thin film device by printing, specifically, to a method for surface treatment.
Ink jet printing technology is one of the main technologies used for printing in the modern office. In recent years, the researchers begin to attempt to use the ink jet printing technology in the production of plane functional materials, such as polymeric conductive films, color organic light emitting diode, thin film semiconductor devices, and the like.
Ink jet printing means that after spreading, drying and solidifying, an ink material printed on a substrate by spraying forms a film and eventually a thin film meeting special requirements for properties is obtained. The quality of the printed thin film includes the morphology of the thin film and the state of the thin film at the interface of the substrate, which are the critical factors determining the properties of the printed thin film device. On the one hand, the surface energy of the substrate affects the quality of the printed thin film, wherein the value of the surface energy is the sum of a dispersive component and a polar component. On the other hand, the quality of the printed thin film also depends on the printed ink. Due to the own characters of inks, different inks also have different requirements for the dispersive component and/or the polar component of the substrate.
In the prior ink-jet printing, the substrate patterns of different materials have been deposited on some regions on a base plate, and substrate patterns of different materials have different surface energies. Additionally, the different requirement for printing results in a different requirement for the surface energies of different substrate patterns. For example, in order to obtain a uniform morphology of a thin film, the difference between the surface energies of the various substrate patterns should be reduced to make the surface energies similar. However, in order to increase the precision of thin film printing, the difference between surface energies of the various substrate patterns is required to be increased. Thus, it is required to modify the surface energy of the substrate pattern according to the actual requirement, so as to make the difference between surface energies of the various substrate patterns larger or smaller.
The invention, in various embodiments, provides a method for surface treatment. By the method for surface treatment, the dispersive component and/or the polar component of a substrate pattern is modified, and furthermore, the surface energy of the substrate pattern is modified, so as to make the difference between the surface energies of different substrate patterns larger or smaller, in order to meet the requirement for printing.
In order to achieve the above-mentioned object, the examples of the invention make use of the following technical solutions.
The invention, in an exemplary embodiment, provides a method for surface treatment, comprising a step of subjecting a surface of a base plate having at least two kinds of substrate patterns formed thereon to a surface treatment for forming a self-assembled monomolecular layer for at least once and a surface treatment by ultraviolet-ozone cleaning, so as to make the difference between the surface energies of the different substrate patterns larger or smaller.
Optionally, the surface treatment for forming a self-assembled monomolecular layer specifically comprises:
Optionally, the method further comprises: before adding the material for forming a monomolecular layer or the solution containing the material for forming a monomolecular layer at the first position in the containment space, keeping charging an inert gas into the containment space to discharge the air in the containment space;
Optionally, the material for forming a monomolecular layer is a fluorine-containing hydrophobic silane, a fluorine-containing thiophenol, or a hydrophobic silane having an alkyl chain structure.
Optionally, the surface treatment for forming a self-assembled monomolecular layer specifically comprises:
Optionally, in an oxygen-free environment, at least the material for forming a monomolecular layer is mixed with the organic solvent to prepare a solution.
Optionally, the method further comprises:
Optionally, the material for forming a monomolecular layer is a fluorine-containing thiophenol, an alkyl thiol, or a hydrophobic silane having an alkyl chain structure.
Optionally, the surface treatment for forming a self-assembled monomolecular layer is conducted twice or more, wherein the materials for forming a monomolecular layer used in each time of the surface treatment for forming a self-assembled monomolecular layer conducted twice or more are different.
Optionally, in the surface treatment by ultraviolet-ozone cleaning, the time of the ultraviolet-ozone cleaning is adjusted correspondingly according to the requirement for the surface energies of the substrates.
The invention, in an exemplary embodiment, provides a method for surface treatment, wherein the dispersive component and/or the polar component of one substrate pattern is modified by conducting the surface treatment for forming a self-assembled monomolecular layer once, and furthermore, the surface energy of the substrate pattern is modified; by the surface treatment by ultraviolet-ozone cleaning, the dispersive component and/or the polar component of the same substrate patterns is modified, and furthermore, the surface energy of the substrate pattern is modified, or, the dispersive components and/or the polar components of different substrate patterns are modified, and furthermore, the surface energies of the substrate patterns are modified, so as to make the difference between the surface energies of the different substrate patterns larger or smaller, in order to meet various requirements for printing.
In order to describe the technical solutions in the invention or in the prior art more clearly, the drawings used for describing the examples or the prior art are briefly described now. It is obvious that the drawings in the description below are only some examples of the invention. Those skilled in the art can, without inventive labor, further attain other drawings, according to these drawings.
1—a gold substrate pattern; 2—a silica substrate pattern.
The technical solutions in the invention will be described clearly and completely in combination with the drawings in the invention. Obviously, the examples described are only a part of, but not all of the examples of the invention.
The invention is described in detail by using an ink-jet printed bottom-contact OTFT (organic thin film transistor) as an example. The printed bottom-contact organic thin film transistor indicates that in the organic thin film transistor, a metal electrode is located under the semiconductor.
An organic thin film transistor comprises a source electrode, a drain electrode, a gate electrode, and a semiconductor layer and an insulator layer. In the invention, a top-gate organic thin film transistor is used as an example. Exemplarily, during the production of an organic thin film transistor, on a silicon base sheet (i.e. the base plate), a silica layer is grown as a second substrate pattern (hereafter referred to as a silica substrate pattern), which generally covers the entire base plate; and then a source electrode and a drain electrode are produced as a first substrate pattern (hereafter referred to as a gold substrate pattern) on the silica by using gold (Au); and then a semiconductor layer is formed between the source electrode and the drain electrode by printing a poly(3-hexylthiophene) (P3HT, an organic polymer semiconductor) ink solution (concentration: 0.25-0.75 wt %), in which the solvent is o-dichlorobenzene; and at last a gate electrode is formed on the semiconductor layer, so as to produce an organic thin film transistor.
Generally, before the poly(3-hexylthiophene) ink solution is printed, it is necessary to treat the base plate having the silica substrate pattern and the gold substrate pattern formed thereon. The methods for surface treatment provided below in the invention can be used for this, and the effect of the methods provided in the invention on the surface energy of the substrate patterns will be analyzed in detail with regard to the materials of the two substrate patterns. Of course, a substrate pattern formed on the base plate is not limited to these two kinds of substrate pattern and can be a substrate formed of other materials. Furthermore, the number of substrate patterns is not limited to 2 and can be 3 or more, wherein the substrate patterns are formed of different materials. In the examples of the invention, the detailed explanation is made by using a base plate having a silica substrate pattern and a gold substrate pattern formed thereon as an example.
The invention, in an exemplary embodiment, provides a method for surface treatment, comprising a step of subjecting a surface of a base plate having at least two kinds of substrate patterns formed thereon to a surface treatment for forming a self-assembled monomolecular layer for at least once and a surface treatment by ultraviolet-ozone cleaning, so as to make the difference between the surface energies of the different substrate patterns larger or smaller.
Here, a substrate pattern generally indicates a pattern formed of one material and located in the same layer. The substrate pattern can be an entire connected pattern, e.g. the silica substrate pattern mentioned above, or can be several disconnected patterns, e.g. the gold substrate pattern mentioned above (including a source electrode and a drain electrode).
The principles for modifying the surface energy of substrate pattern in different surface treatments may be different, and the different surface treatments can affect each other, thus if the order of various treatments is different, the modification to the surface energy of the substrate pattern is also different. Specifically, in the surface treatment for forming a self-assembled monomolecular layer, the surface energy of the substrate pattern is modified because a chemical reaction occurs between the material for forming a monomolecular layer and the hydroxy groups located in the surface of the substrate pattern and thus a monomolecular layer is formed on the surface of the substrate pattern; in the surface treatment by ultraviolet-ozone cleaning, the essential principle is that eliminating the organic molecules on the surface of the substrate pattern will increase the amount of hydroxy groups on the substrate surface, and thus the polar component of the surface energy of the substrate pattern increases significantly, and at the same time, the uniformity of the surface of the substrate pattern is also improved, furthermore, in a certain range of the duration of the surface treatment, the surface energy of the substrate pattern can be controlled in a relatively wide range by controlling the duration of the ultraviolet-ozone cleaning.
If the surface treatment for forming a self-assembled monomolecular layer is conducted twice or more, it is preferred that different materials for forming a monomolecular layer, are respectively used in each time of the surface treatment for forming a self-assembled monomolecular layer conducted twice or more, so that monomolecular layers formed of different organic molecules are formed on the surfaces of the substrate patterns.
The surface treatment for forming a self-assembled monomolecular layer, which includes a wet liquid phase surface treatment for forming a self-assembled monomolecular layer and a dry gas phase surface treatment for forming a self-assembled monomolecular layer, is an efficient method to modify the surface energy of the substrate pattern. Here, the dry gas phase surface treatment for forming a self-assembled monomolecular layer includes that a material for forming a monomolecular layer or a solution containing the material for forming a monomolecular layer and a base plate having at least two substrate patterns formed thereon are placed in the same containment space, and the material for forming a monomolecular layer or the solution containing the material for forming a monomolecular layer undergoes a surface chemical reaction with the substrate pattern via diffusion, so as to form a monomolecular layer on the surface of the substrate pattern. The wet liquid phase surface treatment for forming a self-assembled monomolecular layer includes that the base plate having at least two substrate patterns formed thereon is soaked into a solution containing the material for forming a monomolecular layer, and the material for forming a monomolecular layer undergoes a surface chemical reaction with the substrate pattern, so as to form a monomolecular layer on the surface of the substrate pattern. The materials generally used for the dry gas phase surface treatment for forming a self-assembled monomolecular layer are fluorine-containing hydrophobic silanes, fluorine-containing thiophenols, or hydrophobic silanes having an alkyl chain structure; and the materials generally used for the wet liquid phase surface treatment for forming a self-assembled monomolecular layer are fluorine-containing thiophenols, alkyl thiols, or hydrophobic silanes having an alkyl chain structure. In the invention, the hydrophobic silanes having an alkyl chain structure are silanes having better hydrophobic properties and longer alkyl chain structure, e.g. octadecyltrichlorosilane (OTS).
Here, the fluorine-containing hydrophobic silanes include perfluorododecyltrichlorosilane (FDTS) or the like; the fluorine-containing thiophenols include pentafluorothiophenol (PFTP) or the like; and the hydrophobic silanes having an alkyl chain structure include octadecyltrichlorosilane or the like. The material for forming a monomolecular layer can be in solid state or in liquid state, and the solution containing the material for forming a monomolecular layer can be a mixed solution of the material for forming a monomolecular layer and an organic solvent or the like. The invention is described in detail by using a liquid material for forming a monomolecular layer as an example.
A material for forming a monomolecular layer generally has a remarkable selectivity for different substrate patterns, and thus also differently modifies the surface energies of different substrate patterns. For example, perfluorododecyltrichlorosilane can selectively form a monomolecular layer by self-assembling on the surface of the silica substrate pattern, so that the dispersive component and the polar component of the silica substrate pattern are can be remarkably reduced and ink droplets are not enable to spread or they trend to roll on the surface; pentafluorothiophenol can selectively form a monomolecular layer by self-assembling on the surface of the gold substrate pattern, so that the dispersive component of the gold substrate pattern can be efficiently reduced; octadecyltrichlorosilane can selectively form a monomolecular layer by self-assembling on the surface of the silica substrate pattern, so that the polar component of the silica substrate pattern can be efficiently reduced while the dispersive component of the silica substrate pattern is still relatively large. Therefore, it is possible to select different materials, which will form monomolecular layer, to treat the base plate having at least two substrate patterns formed thereon, according to the different requirements for printing.
The ultraviolet-ozone cleaning can modify the dispersive component and/or the polar component of a substrate pattern and further modify the surface energy of the substrate pattern. Here, the adjusting effects of the ultraviolet-ozone cleaning on the surface energies of different substrate patterns also have remarkable selectivity. For example, compared with the case of a gold substrate pattern, the ultraviolet-ozone cleaning improves the polar component of a silica substrate pattern more easily, and thus improves the surface energy of the silica substrate pattern. Additionally, in a certain range of the duration of the surface treatment, the longer the duration of the ultraviolet-ozone cleaning is, the larger is the surface energy of the silica substrate pattern. Therefore, it is possible to adjust the duration of the ultraviolet-ozone cleaning correspondingly, according to the requirement for printing, in order to meet different requirements for printing.
In the method for surface treatment provided in an exemplary embodiment of the invention, if the surface of the base plate having at least two substrate patterns formed thereon is subjected to the surface treatment for forming a self-assembled monomolecular layer once, it is possible to modify the dispersive component and/or the polar component of one substrate pattern, and furthermore, the surface energy of the substrate pattern; if the surface of base plate is subjected to the surface treatment for forming a self-assembled monomolecular layer twice or more and in each time a different material for forming a monomolecular layer is used, then in each time of the surface treatment for forming a self-assembled monomolecular layer, it is possible to modify the dispersive component and/or the polar component of the same substrate pattern, and furthermore, the surface energy of the substrate pattern, or, to modify the dispersive components and/or the polar components of the different substrate patterns, and furthermore, the surface energies of the different substrate patterns; if the surface of the base plate is subjected to the ultraviolet-ozone cleaning surface treatment, it is possible to modify the dispersive component and/or the polar component of the same substrate pattern, and furthermore, the surface energy of the substrate pattern, or, to modify the dispersive components and/or the polar components of the different substrate patterns, and furthermore, the surface energies of the substrate patterns. Thus, the difference between the surface energies of the substrate patterns becomes larger or smaller to meet the different requirements for printing.
The invention, in an exemplary embodiment, provides a method for surface treatment, comprising a step of subjecting a surface of a base plate having at least two kinds of substrate patterns formed thereon to a surface treatment for forming a self-assembled monomolecular layer for once and a surface treatment by ultraviolet-ozone cleaning, so as to make the difference between the surface energies of the different substrate patterns larger or smaller. Here, in the exemplary embodiment of the invention, the detailed explanation is made by using the base plate having two substrate patterns, i.e. the silica substrate pattern and the gold substrate pattern, as an example.
Here, the surface treatment for forming a self-assembled monomolecular layer for the base plate having at least two substrate patterns formed thereon can be: subjecting the surface of the base plate having at least two substrate patterns formed thereon to a dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane; or subjecting the surface of the base plate having at least two substrate patterns formed thereon to a wet liquid phase surface treatment for forming a self-assembled monomolecular layer by using pentafluorothiophenol; or subjecting the surface of the base plate having at least two substrate patterns formed thereon to a wet liquid phase surface treatment for forming a self-assembled monomolecular layer by using octadecyltrichlorosilane. All of the above are subjecting the surface of the base plate having at least two substrate patterns formed thereon to a surface treatment for forming a self-assembled monomolecular layer, however, the materials for forming a monomolecular layer are different and the monomolecular layers formed on the surfaces of the substrate patterns are different, so that the surface energies of the substrate patterns are also different.
Specifically, subjecting the surface of the base plate having at least two substrate patterns formed thereon to a wet liquid phase surface treatment for forming a self-assembled monomolecular layer using pentafluorothiophenol specifically comprises: adding a solution at a concentration into a reaction vessel, wherein the solution contains a material for forming a monomolecular layer and an organic solvent; placing the base plate having at least two substrate patterns formed thereon into the above-mentioned solution containing the material for forming a monomolecular layer and soaking the base plate for some time, so as to make the material form a monomolecular layer on the surfaces of the substrate patterns.
Since an oxidation reaction may occur while octadecyltrichlorosilane being in contact with air, the solution may optionally be prepared from the material for forming a monomolecular layer and the organic solvent in an oxygen-free environment.
Specifically, before the above steps are carried out, subjecting the base plate having at least two substrate patterns formed thereon to a wet liquid phase surface treatment for forming a self-assembled monomolecular layer by using octadecyltrichlorosilane further comprises: before adding the solution at a concentration into a reaction vessel, keeping charging an inert gas into the reaction vessel, so as to discharge the air in the reaction vessel; and after placing the base plate having the at least two kinds of substrate patterns into the above solution comprising the material for forming a monomolecular layer, sealing the reaction vessel.
The air in the reaction vessel has been discharged with the inert gas. If the reaction space is sealed at this time, there is no air in the reaction vessel. Therefore after the reaction vessel is sealed, the charging of the inert gas can go on or stop, so far as that there is no air in the reaction space. In the invention, the explanation is made by using a method including sealing the reaction space as an example.
Specifically, referring to
S101. cleaning the base plate having the silica substrate pattern and the gold substrate pattern formed thereon;
S102. drying the cleaned base plate having the silica substrate pattern and the gold substrate pattern formed thereon in vacuum;
S103. keeping charging argon gas into the reaction vessel to discharge the air in a reaction vessel;
S104. preparing a solution by mixing octadecyltrichlorosilane and anhydrous toluene in a certain proportion in a reaction vessel full of argon;
S105. placing the base plate having the silica substrate pattern and the gold substrate pattern formed thereon into the above-mentioned solution containing the material for forming a monomolecular layer, and sealing the reaction space;
S106. after reaction for a time period, taking out the base plate having the silica substrate pattern and the gold substrate pattern formed thereon, placing it in ethanol and washing it ultrasonically, blowing nitrogen on it until it is dry, and carrying out a drying treatment in an oven at 120° C. for half an hour.
Of course, the specific steps of the surface treatment mentioned above are not limited to the steps mentioned above. For example, step S104 can also be: preparing a solution at a concentration by mixing octadecyltrichlorosilane and anhydrous toluene in a certain proportion in an oxygen-free environment, and then adding it to a reaction vessel full of argon;
Specifically, referring to
S201. diluting pentafluorothiophenol with ethanol to prepare a solution at a concentration of 1 mM, which is added into a reaction vessel;
S202. placing the base plate surface having the silica substrate pattern and the gold substrate pattern formed thereon into the above-mentioned solution and soaking it for some time;
S203. taking out the base plate having the silica substrate pattern and the gold substrate pattern fowled thereon, washing it with ethanol, and then blowing nitrogen on it until it is dry.
In the exemplary embodiment of the invention, the detailed explanation is made by using the following as an example: subjecting the base plate having the silica substrate pattern and the gold substrate pattern formed thereon to a dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane and to a ultraviolet-ozone cleaning surface treatment.
Specifically, referring to
S301. subjecting the base plate having the silica substrate pattern and the gold substrate pattern formed thereon to a dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane;
S302. subjecting the base plate having the silica substrate pattern and the gold substrate pattern formed thereon to a surface treatment by ultraviolet-ozone cleaning.
Of course, it is possible to carry out the step S302 firstly and then carry out the step S301. However, the value of the surface energy of the substrate pattern treated like this is not the same as that of the substrate pattern undergoing firstly the step S301 and then the step S302. Specifically, the step S301 is essentially a surface chemical reaction, which happens between perfluorododecyltrichlorosilane and the hydroxy groups located in the surface of the substrate pattern and forms a monomolecular layer, which can reduce the surface energy of the substrate pattern; the step S302 increases the polar component of the surface energy of the substrate pattern, increases the surface energy of the substrate pattern, and improves the uniformity of the surface of the substrate pattern. Accordingly, the surface energy of the substrate pattern treated by the step S301 and the step S302 in turn can be controlled in a relatively large range and the surface of the substrate pattern is more uniform; whereas the surface of the substrate pattern treated by the step S302 and the step S301 in turn is more uniform, but the surface energy of the substrate pattern is smaller.
In the exemplary embodiment of the invention, the detailed explanation is made by using the following case as an example: carrying out the step S301 firstly and then carrying out the step S302.
Optionally, the step S301 specifically comprises: adding a material for forming a monomolecular layer or a solution containing a material for forming a monomolecular layer at a first position in a containment space, and placing the base plate having the at least two kinds of substrate patterns at a second position in the containment space, so that under the effect of molecular diffusion, the material for forming a monomolecular layer undergoes a surface chemical reaction with the substrate surface so as to form a monomolecular layer on the surface of the substrate pattern.
The material for forming a monomolecular layer can be in solid state or in liquid state, and the solution containing the material for forming a monomolecular layer can be a mixed solution of the material for forming a monomolecular layer and an organic solvent or the like. In the invention, the detailed explanation is made by using a liquid material for forming a monomolecular layer as an example.
Here, the containment space is enclosed by the device carrying out the above-mentioned dry gas phase surface treatment for forming a self-assembled monomolecular layer. The first position is the position at which the material for faulting a monomolecular layer is placed. The second position is the position at which the base plate having at least two substrate patterns formed thereon is placed. The specific positions of the first position and the second position are determined by the specific device.
With regard to some materials for forming a monomolecular layer, reactions occur while the materials are in contact with air. In this case, an oxygen-free environment is needed for carrying out the above-mentioned method for surface treatment. The oxygen-free environment may be either a vacuum environment or an environment full of an inert gas. In the invention, the detailed explanation is made by using following case as an example: placing the material for forming a monomolecular layer and the substrate in an environment full of an inert gas, and then performing the method while keeping vacuumizing.
Optionally, the method comprises: before adding the material for forming a monomolecular layer or the solution containing the material for forming a monomolecular layer at the first position in the containment space, keeping charging an inert gas into the containment space to discharge the air in the containment space; after placing the base plate having the at least two kinds of substrate patterns at the second position in the containment space, sealing the containment space and stopping charging the inert gas; carrying out air-exhausting for a time period so as to make the material undergo a surface chemical reaction with the substrate pattern and form a monomolecular layer on the surfaces of the substrate patterns; charging the inert gas slowly again to equilibrize the pressure in the containment space and the external pressure.
Specifically, referring to
S3011. charging argon gas into the device (flow rate 40-50 sccm, 30 min), so as to discharge the air in the containment space;
S3012. adding a certain amount of perfluorododecyltrichlorosilane at the first position in the containment space, while keeping charging argon;
S3013. placing the base plate having the silica substrate pattern and the gold substrate pattern formed thereon at the second position in the containment space, so as to make perfluorododecyltrichlorosilane form a monomolecular layer on the surfaces of the substrate patterns.
Preferably, it is possible to allow the surface having the silica substrate pattern and the gold substrate pattern formed thereon of the base plate having the silica substrate pattern and the gold substrate pattern formed thereon upwards, in order to completely expose the gold substrate pattern and the silica substrate pattern in the containment space. It is advantageous for the generation of the monomolecular layer on the surface having the gold substrate pattern and the silica substrate pattern formed thereon by contacting perfluorododecyltrichlorosilane with the gold substrate pattern and with the silica substrate pattern.
S3014. lidding the coping of the device, sealing the containment space and stopping charging argon;
S3015. keeping exhausting the gas for about 2 h, so as to make perfluorododecyltrichlorosilane form the monomolecular layer on the substrate pattern;
S3016. charging an inert gas slowly to equalize the internal and the external pressures, then opening the coping, taking out the base plate having the gold substrate pattern and the silica substrate pattern formed thereon;
S3017. ultrasonically washing the base plate having the gold substrate pattern and the silica substrate pattern formed thereon taken out with anhydrous ethanol, and then carrying out a drying treatment in an oven at 120° C. for half an hour.
Here, the above-mentioned subjecting the base plate having the gold substrate pattern and the silica substrate pattern formed thereon to the dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane is not limited to the steps mentioned above. For example, the step S3012 can also be: placing the base plate having the gold substrate pattern and the silica substrate pattern formed thereon at the second position in the containment space and allowing the surface having the silica substrate pattern and the gold substrate pattern formed thereon of the base plate having the silica substrate pattern and the gold substrate pattern formed thereon upwards, so as to make perfluorododecyltrichlorosilane form the monomolecular layer on the surface having the silica substrate pattern and the gold substrate pattern formed thereon, and keeping charging argon; and accordingly, step S3013 is adding a certain amount of perfluorododecyltrichlorosilane at the first position in the containment space.
The above-mentioned step S302, that is, subjecting the base plate surface having the silica substrate pattern and the gold substrate pattern formed thereon to a surface treatment by ultraviolet-ozone cleaning specifically comprises the following step of:
Exemplarily, after the base plate having the silica substrate pattern and the gold substrate pattern formed thereon has been subjected to the dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane, the base plate having the silica substrate pattern and the gold substrate pattern formed thereon is placed into the ultraviolet-ozone cleaner, the temperature is set to 35° C., the time is set to 8 min, and the start button is pressed to perform the ultraviolet-ozone cleaning.
In order to show the effects of the above-mentioned method, explanation is made referring to
The invention, in an exemplary embodiment, provides a method for surface treatment, comprising a step of subjecting a surface of a base plate having at least two kinds of substrate patterns formed thereon to a surface treatment for forming a self-assembled monomolecular layer for twice and a surface treatment by ultraviolet-ozone cleaning, so as to make the difference between the surface energies of the different substrate patterns larger or smaller. Here, different materials for forming a monomolecular layer are used in each of the two times.
Specifically, referring to
S401. the surface of the base plate having the gold substrate pattern and the silica substrate pattern formed thereon is subjected to the dry gas phase surface treatment for forming a self-assembled monomolecular layer by using perfluorododecyltrichlorosilane;
S402. the surface of the base plate having the gold substrate pattern and the silica substrate pattern formed thereon is subjected to the wet liquid phase surface treatment for forming a self-assembled monomolecular layer by using pentafluorothiophenol;
S403. the surface of the base plate having the gold substrate pattern and the silica substrate pattern formed thereon is subjected to the ultraviolet-ozone cleaning surface treatment;
In order to show the effects of the above-mentioned method, explanation is made referring to
Additionally, if the duration of the ultraviolet-ozone cleaning in the above-mentioned step S403 is different, the modification of the surface energy of the substrate pattern is also different. For example, the duration of the ultraviolet-ozone cleaning was changed to 10 min, then after the base plate having the gold substrate pattern 1 and the silica substrate pattern 2 formed thereon was subjected to the treatment mentioned above, the optical photograph of the printed lattice on the gold substrate pattern and the silica substrate pattern is as that shown in
In the methods provided in the exemplary embodiments of invention disclosed herein, the surface energies of the substrate patterns subjected to various surface treatments can be measured by experiment. Therefore, different surface treatments can be selected to obtain quantitatively the surface energy of the substrate pattern suitable for the ink-jet printing, according to the requirements. Exemplarily,
What described above are only detailed embodiments of the invention. However, the protection scope of the invention is not limited thereto. Any modifications or replacements, which can be easily envisaged by those skilled in the art, should be included in the protection scope of the invention. Therefore, the protection scope of the invention should be determined by the protection of the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012 1 0472646 | Nov 2012 | CN | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20030011304 | Duineveld et al. | Jan 2003 | A1 |
| 20050196969 | Gunner et al. | Sep 2005 | A1 |
| 20060213441 | Kobrin | Sep 2006 | A1 |
| 20070194386 | Hahn | Aug 2007 | A1 |
| 20080075885 | Nie et al. | Mar 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 101238556 | Jun 2008 | CN |
| Entry |
|---|
| English translation of text portion of first Office Action in corresponding Chinese Application No. 2012104726460. |
| Number | Date | Country | |
|---|---|---|---|
| 20140141564 A1 | May 2014 | US |