The present invention relates to a method for treating biological tissue and to the biological tissue, and more specifically to a method for treating biological tissue so as to suppress the degeneration and strength reduction of the tissue due to sterilization, and a biological tissue obtained by the treatment method.
The present applicants have already proposed a method for acellularizing an animal tissue, such as pericardium or tendon, harvested from an animal, such as a cow or a pig, in order to transplant the animal tissue into a human body (see Patent Literature 1 and the like). Here, the biological tissue harvested from an animal and acellularized (hereinafter referred to as “acellularized tissue”) may not be used immediately after the acellularization but sterilized for storage for the time being. In order to put such an animal-derived acellularized tissue to practical use, treatment for sterilizing the acellularized tissue is essential.
However, the application of sterilization to a tissue consisting of biological components (hereinafter referred to as “biological tissue”) and the like leads to the significant damage of the biological tissue and reduces the strength of the tissue compared to that before the treatment. As a result of intensive experimental works, the present inventors have found that the lyophilization and sterilization of biological tissue followed by rehydration causes tissue degeneration in which the tissue has a lower moisture content and becomes harder than the biological tissue before the treatment. Accordingly, the present inventors have impregnated biological tissue with a trehalose solution before the sterilization of the biological tissue. As a result, it has been found that the impregnation can suppress strength reduction and tissue degeneration in the sterilized biological tissue.
The present invention has been worked out based on these findings, and an object thereof is to provide a method for treating biological tissue which can suppress strength reduction and tissue degeneration in the sterilized tissue comprising biological components and the like, and a biological tissue obtained by the treatment method.
In the present invention, a tissue consisting of biological components and the like (hereinafter referred to as “biological tissue”) is immersed in a trehalose solution and shaken for about 24 hours to impregnate the biological tissue with the trehalose solution. The trehalose solution used here is one obtained by dissolving trehalose in a phosphate buffered saline, the concentration of trehalose being preferably in the range of 20 wt % to 35 wt %.
Thereafter, the biological tissue is dried to remove moisture in the biological tissue. The drying here is not particularly limited; however, it is carried out at a temperature of about −45° C. for about 24 hours.
Then, the tissue is sterilized with ethylene oxide gas. The conditions of the sterilization here are not particularly limited, and are set to a temperature of about 30° C. for suppressing collagen degeneration, an exposure time of about 12 hours, and an aeration of about 20 hours. It is also possible to adopt other sterilization methods, such as hydrogen peroxide low-temperature plasma sterilization. In the present invention, another oligosaccharide of disaccharide, such as sucrose, lactose, or maltose can be used in place of trehalose. In other words, various embodiments can be adopted as long as drying and sterilization are carried out after impregnating biological tissue with an oligosaccharide solution of a disaccharide as described above.
According to the present invention, tissue degeneration and strength reduction can be suppressed in sterilized biological tissues.
In addition, when the trehalose concentration in the trehalose solution can be set to 20 wt % to 35 wt %, tissue structure and strength in biological tissue before the treatment can be maintained to almost the same extent.
First, a harvested bovine pericardium was made into the form of a 5-cm-by-7-cm rectangular sheet about 300 μm in thickness and 1.5 g in mass and washed with a phosphate buffered saline (PBS) containing an antibiotic.
Then, the washed bovine pericardium was subjected to acellularization by a method as already proposed by the present inventors (see Japanese Patent Laid-Open No. 2011-05043).
Next, 40 ml of a trehalose solution obtained by adding trehalose to PBS was provided, and the bovine pericardium after the acellularization (acellularized tissue) was placed together with the trehalose solution in a 50-ml centrifuge tube, the tube is shaken with the bovine pericardium impregnated with the trehalose solution. In this Example, the concentration of trehalose in the trehalose solution was set to 1 wt %. The shaking treatment was carried out at a revolution of 180 rpm for 24 hours using a bioshaker warmed at 37° C.
Thereafter, using a lyophilizer, the bovine pericardium was allowed to stand at about −45° C. for about 24 hours to remove the moisture of the bovine pericardium.
Then, in an ethylene oxide gas sterilizer, the bovine pericardium was sterilized with ethylene oxide gas to provide a sterilized dried tissue of the bovine pericardium. Here, the exposure temperature was set to 30° C.; the exposure time, to 12 hours; and aeration, to 20 hours.
A sterilized dried tissue of bovine pericardium was obtained as in Example 1 except that the concentration of trehalose in a solution thereof was changed. Specifically, the bovine pericardium acellularized as described above was placed in a trehalose solution whose trehalose concentration was set to each of 5, 10, 20, 25, 30, 35, 40, and 50 wt %, subjected to the above-described shaking treatment, and then dried and sterilized as described above to provide a sterilized dried tissue of the bovine pericardium according to each of Examples 2 to 9.
Also, the maximum concentration of trehalose was set to 50% because the concentration of trehalose dissolved in PBS at 37° C. was about 50%.
A sterilized dried tissue of bovine pericardium was obtained under the same conditions as in Examples 1 to 9 except that the acellularization was not conducted.
A sterilized dried tissue of bovine tendon was obtained under the same conditions as in Examples 1 to 18 except that a tissue to be treated was changed from bovine pericardium to bovine tendon.
Here, the bovine tendon used was in the order of 10 cm long and 10 mm thick.
A sterilized dried tissue of bovine pericardium was obtained following a different procedure from that in Example 1, where the acellularized bovine pericardium was not impregnated with a trehalose solution, but dried and sterilized as described above.
A sterilized dried tissue of bovine pericardium was obtained under the same conditions as in Comparative Example 1 without impregnation with a trehalose solution, except that the acellularization was not conducted.
A sterilized dried tissue of bovine tendon was obtained under the same conditions as in Comparative Examples 1 and 2 without impregnation with a trehalose solution, except that a tissue to be treated was changed from bovine pericardium to bovine tendon as in Example 19 and others.
Then, experiments for demonstrating the effect of the present invention were carried out.
As a first experiment, an experiment for demonstrating the effect of suppressing tissue degeneration according to the present invention was carried out using the sterilized dried tissue obtained in each of the above Examples and Comparative Examples.
Specifically, 40 ml of antibiotic-containing PBS is added to a 50-ml centrifuge tube, in which each sterilized dried tissue is placed. Then, it is shaken at a revolution of 180 rpm for 24 hours using a bioshaker warmed at 37° C., and the mass of the sterilized dried tissue thereby rehydrated is measured using an electronic balance. Then, the rate of increase in the mass of the sterilized dried tissue of each Example relative to that of the sterilized dried tissue of the corresponding Comparative Example without impregnation with a trehalose solution was calculated. The corresponding Comparative Example is Comparative Example 1 for Examples 1 to 9; the corresponding Comparative Example is Comparative Example 2 for Examples 10 to 18; the corresponding Comparative Example is Comparative Example 3 for Examples 19 to 27; and the corresponding Comparative Example is Comparative Example 4 for Examples 28 to 36.
As a second experiment, a tension test for demonstrating the effect of suppressing the strength reduction of tissue according to the present invention was carried out using the sterilized dried tissue obtained in each of the above Examples and Comparative Examples.
The experiment was carried out under the following conditions for each of Examples 1 to 18 and Comparative Examples 1 and 2 in which a bovine pericardium was used as a tissue to be treated.
After rehydrating each sterilized dried tissue of the bovine pericardium under the same conditions as those in the first experiment, a strip specimen of 3 mm wide was prepared, and a tension test was carried out by setting the initial chuck distance to 7 mm. The tension test was conducted under the conditions of an initial tension load of 0.5 N, a specimen elongation of 20%, a tensile speed of 120 mm/min, and a cycle number of 3,000. Then, for each specimen, the rate of stress relaxation over time was determined which was calculated by subtracting the load after 3,000 cycles from the initial load and dividing the balance by the initial load, and the rate of increase from the stress relaxation rate for the sterilized dried tissue of each of the corresponding Comparative Examples was calculated. The stress relaxation rate here is a measure of a viscoelastic characteristic (flexibility), and a larger stress relaxation rate means higher flexibility. The sterilization of biological tissue has been found to decrease the rate of stress relaxation compared to that before the treatment.
For each of Examples 19 to 36 and Comparative Examples 3 and 4 in which a bovine tendon was used as a tissue to be treated, the experiment was carried out under the following conditions.
Each specimen in the above-described shape was rehydrated under the same conditions as those in the first experiment, followed by performing a tension test by setting the width of the specimen to 4 mm and the initial chuck distance to 45 mm. The tension test was conducted under the conditions of an initial tension load of 66.7 N for 15 minutes and then the 10,000 cycles of a tension load of 100 N at a tensile speed of 300 mm/min. Then, for each specimen, the point was determined at which the percentage of increase in strain in every 100 cycles became less than 0.15%, and the influence of the crimp structure of collagen or the like constituting the tissue was eliminated as much as possible by subtracting a value of strain at the point where the percentage of increase in strain in every 100 cycles reached less than 0.15% from a value of strain until 10,000 cycles to calculate the rate of change in the strain of the tissue structure itself. The rate of change in strain here is similarly a measure of a viscoelastic characteristic. Then, for each specimen, the rate of increase in rate of change in strain relative to that of the sterilized dried tissue of corresponding Comparative Example was calculated.
The results of the experiments are shown in tables below.
The biological tissue treated by the conventional method (hereinafter referred to as “conventional treated tissue”) has a decreased mass compared to that of the untreated tissue; however, according to the above experimental results, the biological tissue subjected to the treatment of the present invention (hereinafter referred to as “the treated tissue of the present invention”) was enabled to have an increased mass compared to that of the conventional treated tissue. In addition, the trehalose concentration can be set to within the range of 20 wt % to 35 wt % to provide a peak of the highest mass among the treated tissues of the present invention, enabling the mass of the resultant tissue to be made at almost the same level as the mass of the untreated tissue. As a result, the present invention can be estimated to have the effect of suppressing the phenomenon of destroying the fine structure of tissue before treatment and was demonstrated to suppress the degeneration of biological tissue after treatment compared to the conventional method.
The conventional treated tissue has reduced strength compared to that of the untreated tissue due to reduced flexibility; however, according to the above experimental results, the treated tissue of the present invention was enabled to have increased flexibility and strength compared to those of the conventional treated tissue. In addition, the trehalose concentration can be set to within the range of 20 wt % to 35 wt % to provide a peak of the highest flexibility among the treated tissues of the present invention, enabling the flexibility thereof to be made at almost the same level as the flexibility of the untreated tissue. As a result, the present invention was demonstrated to suppress the strength reduction of biological tissue after treatment to a greater extent than the conventional method.
Further, according to the present invention, even when biological tissue was acellularized, tissue degeneration or strength reduction was demonstrated to be suppressed in the dried and sterilized tissue.
The present invention can be similarly applied, without being limited to the tissues of the above Examples, to any tissue provided that it is a tissue consisting of biological components and the like.
The present invention can be used for treatment for industrially processing or preserving a tissue harvested from an animal as a tissue for transplantation into a human body.
Number | Date | Country | Kind |
---|---|---|---|
2012-083367 | Mar 2012 | JP | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/JP2013/059842 | 4/1/2013 | WO | 00 |