I. Field of the Invention
The present invention relates to a method of applying a material, preferably a pattern of material on a substrate.
II. Discussion of the Background
During the past decade, soft lithography has developed to a versatile technique for fabricating chemically micro- and nanostructured surfaces [1,2]. Among several techniques known collectively as soft lithography, micro contact printing (μCP) has become the most commonly used method [1]. The technique was initially developed for the transfer of organic molecules [3], but later on also widely used for the transfer of biomolecules such as proteins [4].
Initially polydimethylsiloxane (PDMS) was used as stamp materials in μCP. As a result of the small Young's Modulus conformal contact between the stamp and the target substrate, a prerequisite for the successful pattern transfer, are easily achieved. The drawbacks of soft materials, however, are deformations known as pairing, buckling, sagging or a complete collapse of patterns [5]. PDMS has a Young's modulus of approximately 1 MPa and hence, does not allow to transfer patterns with dimensions below 200 nm. Other PDMS mixtures were investigated to make it harder and thus increase the resolution [6]. The so-called h-PDMS has got a Young's modulus around 8 MPa, enabling the transfer of quadratic patterns with feature sizes down to 80 nm. Line structures with these critical dimensions could not be demonstrated. In addition, even harder materials such as polyolefines, e.g. Affinity [7] or block copolymers SBS (poly(sterene-block-butadiene-block-styrene) or SEBS (poly(styrene-block-ethylene-co-butylene-block-styrene)) [8] were investigated. Their Young's modulus is around 45 MPa and allows the transfer of 100 nm lines. However, the quality of the transfer patterns suffers from sagging effects.
Another field of transfer methods used for the transfer of metals and other solids such as CNTs is nanotransfer printing (nTP) [9,10]. There a thin layer of metal is evaporated onto a patterned elastomeric stamp, which has been fabricated by drop casting of polydimethylsiloxane (PDMS) onto a patterned Si wafer. The evaporated metal layer is brought in conformal contact with an organic layer on a substrate. As a result of the chemical bond formation at the metal-organic interface, the metal-organic adhesion is stronger than the metal-PDMS adhesion and the metal layer is transferred from the PDMS stamp onto the organic layer. The transfer of metal by nanotransfer printing suffers from the same drawbacks of soft stamps as microcontact printing.
The preparation of polymer stamps and subsequent micrcontact printing technique of organic and inorganic structures have been developed. Critical for a good pattern transfer is the conformal contact between the substrate and the stamp. Polymers with different Young's modulus have been used to transfer patterns of organic molecules (proteins and alkanethiols) and inorganic materials with critical dimensions down to ˜75 nm over small areas. For the transfer of patterns with critical dimensions below 100 nm hard substrate and hard stamp materials, at least as far as their contacting surfaces are concerned, are required.
U.S. Pat. No. 6,482,742 [1] and Tan et al. [12], disclose a method of imprint lithography involving the use of fluid pressure to press a mould into a substrate-supported film. According to this method, the mould and/or substrate are sufficiently flexible to provide wide area contact under the fluid pressure. It is emphasized that both substrates and moulds need to have sufficient flexibility and pliability to be used in this method.
However, none of the prior art processes allows and ensures the achievement of a conformal contact between hard surfaces. Accordingly, it was an object of the present invention to provide for a method that can be adapted to the use of hard surfaces within printing processes. Moreover, it was an object of the present invention to provide for a method which allows the usage of hard surfaces so as to enable a transfer of materials, preferably patterned materials with dimensions ≦30 nm. It has also been an object of the present invention to provide for a method that ensures uniform printing over large areas.
The objects of the present invention are solved by a method of applying a material, preferably a pattern of material, on a substrate, comprising the steps:
In a preferred embodiment, it is said second surface which has a Young's modulus ≧100 MPa.
Preferably, the method according to the present invention, further comprises the steps:
Preferably, said second surface is a patterned surface having a pattern of protrusions and/or recesses.
In one embodiment said second pressure conditions are applied on said assembly by means of a chamber capable of being evacuated and/or pressurized, wherein, for application of said second pressure conditions, said chamber is pressurized, whilst said assembly is located in said chamber.
In one embodiment said first pressure conditions are atmospheric or ambient pressure or a pressure below atmospheric or ambient pressure, preferably 0.1 mbar to 900 mbar, more preferably 100 mbar to 500 mbar.
Preferably, said third pressure conditions are atmospheric or ambient pressure or a pressure below atmospheric or ambient pressure.
In one embodiment said second pressure conditions involve a higher pressure than said first and third pressure conditions, wherein, preferably, said first and third pressure conditions are the same and involve atmospheric or ambient pressure or a pressure below atmospheric or ambient pressure.
In another embodiment said first and third pressure conditions are not the same and said third pressure conditions involve a higher pressure than said first pressure conditions, wherein said third pressure conditions involve atmospheric or ambient pressure and said first pressure conditions involve a pressure below atmospheric or ambient pressure.
In one embodiment said first pressure conditions involve a pressure below atmospheric or ambient pressure, and wherein said first pressure conditions are applied on said assembly by means of a chamber capable of being evacuated and/or pressurized, wherein, for application of said first pressure conditions, said chamber is evacuated, whilst said assembly is located in said chamber, wherein, preferably, said chamber is the chamber used for application of said second pressure conditions.
In one embodiment said third pressure conditions involve atmospheric or ambient pressure and wherein said third pressure conditions are applied on said assembly by means of a chamber capable of being evacuated and/or pressurized, wherein, for application of said third pressure conditions, said chamber is evacuated to atmospheric or ambient pressure, whilst said assembly is located in said chamber, wherein, preferably, said chamber is the chamber used for application of said second and/or said first pressure conditions.
In one embodiment said second pressure conditions involve the application of a pressure higher than atmospheric pressure, wherein, preferably, said second pressure conditions involve the application of a pressure in the range of from 2 bar to 100 bar, more preferably from 2 bar to 42 bar.
In one embodiment, said second pressure conditions are applied over a period of from 5 s to 60 min.
In one embodiment said second pressure conditions involve the increase of pressure up to a maximum pressure in the range of from 2 bar to 100 bar, more preferably from 2 bar to 42 bar.
In one embodiment, said maximum pressure is maintained over a period of from 10 s to 59 min.
In one embodiment said second substrate is made of a material having a Young's modulus ≧100 MPa which material is selected from the group comprising polymers, metals, semiconductors, crystals, amorphous solids and composites thereof, wherein, preferably, said polymer is selected from the group comprising polyolefines, ionomers, polymethylmethacrylates, polycarbonates, cellulose acetate, polyamide, polyimide, polystyrene, polytetrafluoroethylene, polyoxymethylene and copolymers.
In one embodiment said first substrate is made of a material having a Young's modulus≧100 MPa which material is selected from the group comprising polymers, metals, semiconductors, crystals and composites thereof, wherein, preferably said polymer is selected from the group of thermosetting plastics comprising polyolefines, ionomers, polyethylene-methacrylate-copolymers, polymethylmethacrylate, polycarbonates, cellulose acetate, polyamide, polyimide, polystyrene, polytetrafluoroethylene, polyoxymethylene and copolymers.
In one embodiment said sealing occurs by applying a sealing material to said assembly of said first substrate and said second substrate, to enclose said volume between said first and said second substrate and to isolate said volume from the surroundings of said assembly, wherein, preferably, said sealing material is a sealing ring or a foil enclosing said assembly, or two foils enclosing said assembly.
In one embodiment said second pressure conditions are applied at a temperature in the range of from 0° C. to 200° C., more preferably in the range of from 0° C. to 95° C.
Preferably, steps a) and b) occur in the order ab or ba, or they occur concomitantly.
In one embodiment said material, to be applied, preferably patterned on said first surface, is selected from the group comprising molecules, such as organic molecules, metal complex compounds, proteins; thin films of inorganic solids, nanoparticles, wherein, preferably, said inorganic solids are selected from the group comprising metals, metal oxides, semiconductors; and objects such as viruses.
In one embodiment said material, to be applied, preferably patterned on said first surface, is applied on said second surface by a process selected from contact inking and wet inking.
The present inventors have surprisingly found that subjecting an assembly of two surfaces between which material is to be transferred, to pressures ≧2 bar enables the usage of hard surfaces, i.e. substrates which are used as stamps and/or target substrates. This, in turn, allows the transfer of patterns with dimensions ≦30 nm. The idea underlying the method according to the present invention is that after bringing substrates into contact with each other, with the material to be transferred in between, a volume is enclosed between the substrate and the stamp for which, in a first step, first pressure conditions are established. In a preferred embodiment, such first pressure conditions are below atmospheric pressure, such as 100 mbar. These first pressure conditions are conserved by sealing and thereby isolating and delimiting the volume between the stamp and the substrate from the surroundings. In a subsequent step, second pressure conditions are established which are higher than said first pressure conditions and which involve pressures up to 100 bar. Such second pressure conditions thereby create a difference to the reference pressure, i.e. said first pressure conditions, which are established and still exist within the volume enclosed by the stamp and the substrate and the seal around it. The second pressure conditions, i.e. the high pressure, is maintained for a defined period of time. It is clear to someone skilled in the art that such second pressure conditions may involve variable pressures and may also involve defined pressure profiles. Typically, second pressure conditions are applied for a period of time in the range of from 5 s to 60 min. Thereafter, the pressure is lowered again, which may be atmospheric pressure or may be the same pressure as those pressure conditions that had been applied and established as reference pressure. These pressure conditions after the high-pressure-step are herein also sometimes referred to as “third pressure conditions”. Without wishing to be bound by any theory, the inventors presently believe that by applying high pressure conditions, a uniform printing process is ensured, because, essentially, the pressure conditions act on the assembly of stamp and substrate in a uniform manner. Preferably, the high pressure conditions are applied on the assembly by means of a chamber capable of being evacuated and/or pressurized. Such a chamber is a chamber wherein pressure may be applied by means of the gas or liquid within the chamber. Likewise, a vacuum may be applied by evacuating said chamber of said gas or liquid. Again, the pressure, namely the negative pressure thus created, is uniformly applied on the object within the chamber, e.g. an assembly of a substrate and a stamp. The method according to the present invention ensures that the stamp cannot move with respect to the target substrate. Moreover, the method can be carried out with different printing pressures which may be precisely adjusted. Additionally, even pressure profiles may be performed which may include pressure ramps, i.e. pressure increases as well as pressure declines. The method according to the present invention allows the usage of very hard substrates and/or stamps which, in turn allows the transfer of patterns with dimensions≦30 nm. If, as a stamp, a polymeric material is used, such polymeric stamp may be made in a single step and is simple to fabricate. Moreover, the entire process is defect-tolerant. A dust grain which may, for example, have ended up between the stamp and the substrate only causes a minor area of affected transfer and printing. If a three dimensional stamp pattern is to be printed, the process does not pose high requirements on the uniformity of such three dimensional stamp patterns, as fluctuations in the height may be compensated.
The term “a first substrate”, as used herein, usually refers to the target substrate, onto which material is to be applied or printed or patterned. Although the method according to the invention allows for the application of material in general, which does not necessarily need to have a pattern, a preferred embodiment of the method according to the present invention is directed at applying a pattern of material on such first substrate or target substrate. Such first substrate has a first surface which is the surface onto which the material is to be applied, preferably patterned.
The term “a second substrate”, as used herein, usually refers to the stamp which is used in the method according to the present invention. In its simplest form, this stamp may have a smooth surface, but preferably it has a patterned surface which is the pattern that is to be applied ultimately to the target substrate. The patterning of said second surface of said second substrate, i.e. of the surface of said stamp can be performed by a number of processes known to the person skilled in the art, such as lithographic methods, etching methods, as disclosed in Nishi [13] and Levinson [14].
The term “an assembly of said first substrate and said second substrate”, as used herein, is meant to refer to an arrangement wherein the first substrate, i.e. the target substrate, and the second substrate, i.e. the stamp, have been brought together; and their respective surfaces, i.e. the first surface and the second surface, which are involved in the transfer process have been brought into contact with each other, such that the material that is to be transferred from the stamp to the target substrate is sandwiched between the stamp and the target substrate. The material that is to be applied, preferably patterned on the target substrate is first brought onto the stamp by any process useful for that purpose, such as contact inking or wet inking, or by evaporating the material, e.g. metal, to be applied onto the stamp, or via a shuttle process. Usually, in the inking processes, a stamp, preferably a patterned stamp is covered with an ink of molecules to be applied, preferably patterned on the target substrate. In contact inking, the solvent of the ink is reduced to the dry state while the molecules self assemble on an ink pad. The molecules are transferred onto the stamp under ambient conditions by bringing the stamp and the ink pad into conformal contact. In wet inking, the ink is poured over the stamp and then reduced under a stream of gas, e.g. nitrogen, to a dry state. In both cases, the molecules have been placed onto a stamp prior to the subsequent transfer onto the target substrate. In the assembly of the target substrate and the stamp, a volume is enclosed between the stamp and the target substrate which comprises the material to be applied to said target substrate and, if present, a pattern of protrusions and/or recesses on which the material to be applied on the target substrate, is arranged.
The term “to apply nth (i.e. 1st, 2nd, etc.) pressure conditions on said assembly”, as used herein, is meant to refer to the application of uniform pressure onto the assembly, such as is for example achieved by adjusting the pressure of the medium surrounding the assembly to a specified value or a range of values. The term may also refer to the performance of a specified pressure profile, in the sense that the pressure of the surrounding medium may be increased over a number of steps and/or decreased over a number of steps. Such pressure profiles may be defined according to the needs and requirements of the individual experiment. In its simplest form, however, the term “to apply pressure conditions on said assembly” is meant to refer to the attainment of a specified pressure value and the maintenance of this pressure value for a defined period of time. In the context of the present invention, the “first pressure conditions” that are applied on said assembly serve the purpose of establishing a reference pressure on and within the assembly, most notably in the volume that is enclosed by the stamp and the target substrate. Such reference pressure is preserved by subsequently sealing the volume and isolating it from the surroundings of the assembly. The “second pressure conditions” that are applied on said assembly are the high pressure conditions which serve the purpose of exerting pressure in a uniform manner onto said assembly and to thereby bring the second substrate, i.e. the stamp, and the first substrate, i.e. the target substrate, into conformal contact with each other. The term “to bring into conformal contact with”, as used herein, is meant to denote a contact between two entities, e.g. surfaces, allowing the transfer of molecules that were on one entity before the contact, to the other entity. In some embodiments according to the present invention, an exertion of pressure is needed for such transfer to occur, and in these instances, the term “to bring into conformal contact with” may also be equated with “to press on (to)”. The “third pressure conditions” which are applied on said assembly, as used herein, refer to the pressure conditions that follow after application of the second, i.e. high, pressure conditions. In its simplest form, such third pressure conditions may be atmospheric or ambient pressure, or they may be a pressure below atmospheric or ambient pressure. The term “to apply nth pressure conditions”, as used herein, refers to any process whereby such pressure conditions are applied and exerted on the assembly in a uniform manner, i.e. by adjusting the pressure that the medium surrounding the assembly exerts on said assembly. In a typical embodiment, such application of pressure conditions is achieved by a chamber that may be pressurized or evacuated.
The term “sealing said volume”, as used herein, is meant to refer to a process whereby the pressure conditions that have been established within the volume are conserved by isolating the volume from the surroundings. Likewise, the term “unsealing said volume”, as used herein is meant to refer to a process wherein such seal is removed, as a result of which the pressure conditions within the volume may equilibrate and attain the same value as the surroundings. The term “pressure conditions involve a certain pressure”, (e.g. higher pressure), as used herein, is meant to refer to the fact that such pressure condition may comprise a single pressure value that is maintained for a defined period of time or may comprise a number of pressure values that are attained subsequently. In any case, the term “pressure conditions”, as used herein, is meant to imply that whatever pressure value is prevalent at a specific point in time, such pressure value is applied uniformly to the assembly.
The term “Young's modulus” or tensile modulus is meant to define the hardness of a material. The Young's modulus is defined as the ratio of the linear stress to linear strain (in Nm−2 or Pa). It is e.g. measured using ASTM D638 or ISO 527.
Sometimes in this application, reference is made to a substrate having a Young's modulus of a specified value. It is preferred that such indication of a Young's modulus refers to those parts of such substrate that are actually involved in the transfer process/printing process, such as the respective surface (first surface, second surface).
In the method according to the present invention, a number of steps are performed which are initiated by a single letter. Unless otherwise indicated, the order in which these steps are performed is the order in which the respective letters appear in the alphabet, that is step “a” occurs before “b” which occurs before step “c” etc. In this respect, it is to be noted that steps “a” and step “b” according to the method of the present invention may occur in the order ab or ba or they occur concomitantly. In this context, the term “concomitantly” is meant to denote a scenario wherein both steps are performed at the same time, i.e. they have the same beginning and end, or there may be an overlap between the two steps. Moreover, it should be noted that steps h and “i” may occur in the order hi or ih or they may occur concomitantly.
In the following, a preferred embodiment of the process is described.
Process Description of a Preferred Embodiment
Process (See Also
The process steps of a preferred embodiment involve
As substrate any hard surface can be used having dimensions up to 12 in. They could be flat and even, have any other shape or be irregular. They could be pre-patterned with three-dimensional structures or other molecules.
As stamps any hard materials with a Young's modulus >100 MPa might be used. Ideal candidates are polymeric materials such as thermoplastic materials. But any other solid with the appropriate properties could be used as well.
Polymeric stamps could be prepared by hot embossing or casting. Other hard stamps could be prepared by means of any other method which is capable of forming three-dimensional patterns. Also unpatterned materials can be used for the transfer. The inking of the stamp could be done by any conventional method such as wet inking or contact inking, or by evaporation or a shuttle process. Any molecular ink could be used. The process can also be applied for the transfer of metals or any other solid material which has got the appropriate properties.
Preferred Process Parameters:
The major process parameter is the pressure difference between the “high pressure conditions” (i.e. second pressure conditions) and the “low pressure conditions” (i.e. first pressure conditions) between substrate/stamp and chamber. Therefore it is necessary to seal the stamp to the substrate by any useful means.
Furthermore, in the following reference is made to the figures wherein
Moreover, reference is made to the following examples which are given to illustrate, not to limit the present invention.
For all examples, the transferred patterns shown in the Figures were investigated with scanning electron microscopy.
In these examples the following polymeric materials were used:
A Nanonex NX-2000 tool based on [11,12] was used to perform the process. Therefore a 1 cm by 1 cm silicon-chip covered with a gold layer was used as a substrate. Surlyn 1702 stamps having features with critical dimensions of 5 μm to 75 nm were inked with protein solution of cytochrome c for 2 h using the wet inking method. Afterwards the stamps were dry blown under a stream of nitrogen. The substrate was placed onto a silicone foil. Subsequently the stamp was placed onto the substrate and a second silicone foil mounted in a tenter was placed on top such that the two silicone foils did not touch each other. This assembly was put into the pressure chamber of the NX-2000. Over a time period of 10 s the chamber was evacuated and the residual pressure was 100 mbar. Subsequently the two silicone foils are brought into contact by bringing the tenter in contact with the lower foil. Thus substrate and stamp were sealed against the chamber. The vacuum step is necessary to guarantee a good sealing. A first pressure of 2 bar was filled into the chamber for 15 s. Because stamp and substrate are sealed this exerts a reference pressure onto stamp and substrate. Then the pressure was increased to 25 bar for 1 min. Afterwards the pressure was released and after separating the foils, master and stamp were separated. Due to the sealing of the silicone foils the stamp can not move relative to the substrate during the transfer process. The SEM image (
Like in Example 1 an experiment is performed with Surlyn 1702 applying a maximum pressure of 18 bar. The SEM image (
Like in Example 1 an experiment is performed with Surlyn 1702 applying a maximum pressure of 42 bar. The SEM image (
Like in Example 1 an experiment is performed with Surlyn 1702 applying a maximum pressure of 25 bar. Instead of using a cytochrome c solution an octadecanethiol (ODT) solution was used as ink. The SEM image (
Like in Example 1 an experiment is performed. Instead of using Surlyn 1702 as stamp material Plexiglas 99530 was used. The SEM image (
Like in Example 1 an experiment is performed. Instead of using Surlyn 1702 as stamp materialZeonex E48R was used. The SEM image (
Like in Example 1 an experiment is performed. Instead of using Surlyn 1702 as stamp material Topas 8007 was used. The SEM image (
Like in Example 7 an experiment is performed with Topas 8007 as stamp material. Instead of using patterns with 5 μm to 75 nm a design with patterns between 400 nm and 25 nm was used. The SEM image (
The above described process allows the printing of molecules down to critical dimension≦30 nm with different hard stamp materials.
The main advantages of this process are:
The features of the present invention disclosed in the specification, the claims and/or in the accompanying drawings, may, both separately, and in any combination thereof, be material for realizing the invention in various forms thereof.
Number | Date | Country | Kind |
---|---|---|---|
06016355 | Aug 2006 | EP | regional |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP2007/005310 | 6/15/2007 | WO | 00 | 11/17/2008 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2008/014845 | 2/7/2008 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
5816158 | Ross | Oct 1998 | A |
5947027 | Burgin et al. | Sep 1999 | A |
6458426 | Bulovic et al. | Oct 2002 | B1 |
20020101460 | Miyauchi et al. | Aug 2002 | A1 |
20030159608 | Heidari | Aug 2003 | A1 |
20050145119 | Tan et al. | Jul 2005 | A1 |
20050224452 | Spiess et al. | Oct 2005 | A1 |
20060065143 | Sakurai et al. | Mar 2006 | A1 |
Number | Date | Country |
---|---|---|
0 492 258 | Jul 1992 | EP |
1 229 387 | Aug 2002 | EP |
1 244 939 | Aug 2006 | EP |
6 89858 | Mar 1994 | JP |
03 087935 | Oct 2003 | WO |
2005 109095 | Nov 2005 | WO |
Number | Date | Country | |
---|---|---|---|
20090183831 A1 | Jul 2009 | US |