Patent Application
20200157691
Embodiments of the present disclosure relate to the field of surface treatments of mechanical parts against corrosion. The embodiments relate, in particular, to a method of compacting an anti-corrosive paint covering a part, for example a turbine engine part.
Mechanical parts, in particular those used in aircraft turbine engines, are exposed to environments which are constraining in terms of temperatures, corrosive elements, and oxidation reactions. Parts, such as the compressor and low-pressure turbine shafts, are made, for example, of steel or a steel alloy with a reduced cobalt content, so as to have an increased mechanical resistance. These steels have a high sensitivity to corrosion phenomena which are mainly manifested by the development of corrosion pits consisting of localized and deep attacks. These parts are also subjected to heavy mechanical stresses during the functioning of the turbine engine, which can lead to development of the corrosion. The constraint/corrosion synergy effect leads to a notable increase in corrosion phenomena.
Certain parts have been covered by a paint which is resistant to increased temperatures and to different corrosive and oxidative elements (kerosene, oil, etc.), such that these resist the environment, in which they occur, and in particular protect them from corrosion. This paint being partially composed of chromium trioxide, has been classed as CMR, which is the acronym for Carcinogenic, Mutagenic, Reprotoxic, and is governed by the REACH regulation, on the Registration, Evaluation, Authorisation and Restriction of Chemical substances.
In order to avoid constraints linked to this regulation, a solution consisting in making the paint anodic has been developed. Examples of this solution are described in documents FR-A1-2991216 and FR-A1-3040013. In particular, this solution consists in spraying on the surface of the part, a liquid paint having a mineral binder and loaded with metal particles, such as aluminium. This paint is sprayed via a gun handled by an operator. The paint-coated part is heated in a furnace to polymerise the sprayed paint. The polymerised paint then undergoes a mechanical action such as compacting, in order to put the metal particles in contact, without damaging the cosmetic and physical appearance of the paint. This action makes it possible to achieve electrical continuity of the metal particles with the metal parts to be treated. The paint layer is thus made dense and electrically conductive, to make this a sacrificial layer which will preferably be corroded, instead of the metal of the part to be protected. Thus, the term “anodic paint” is used to describe the sacrificial layer that has been rendered conductive.
The compacting consists of sandblasting or grit blasting the painted portions after polymerisation with white corundum particles, glass balls, or plastic particles. The compacting makes it possible to densify the paint and give it sacrificial properties, responsible for the efficient anti-corrosive properties thereof. Alternatively, it is also known to produce the anodic paint by buffing. The buffing is a manual punching of the part with sandpaper which takes a long time to implement.
The step consisting in making the paint anodic is optional when the paint contains chromium trioxide. It is, however, essential for paints which do not contain it.
However, the particles used for the compacting can be embedded in the paint and on the surface thereof. In operation, a discharge or release of these particles can occur and can damage other members of the turbine engine which are in the path of these particles. Certain particles like corundum, which is a mineral element, has an increased hardness of around 9.5 on the Mohs scale. For parts, like the turbine shafts and the compressor shafts, the compacting step is therefore not carried out to avoid the release of these very hard particles at an increased speed, which leads to a decrease of the anti-corrosive properties thereof. Indeed, the paint layer not being conductive without the compacting, it plays a very low anti-corrosive protective role, only by forming a barrier on the surface of the part. The anti-corrosive effect brought by this layer forming a barrier depends largely on the porosity rate thereof.
In addition, as soon as the part is scuffed or scratched, the protection stops and the part becomes sensitive to corrosion. Furthermore, for these parts of which the coating is not compacted, the paint is applied manually in at least two layers to limit, to a minimum, its porosity. This extends the duration for producing the part without counting the different steps necessary for preparing the front part, during and after the application of the paint. Controlling the thicknesses of the different layers of paint is difficult, and in particular on parts having a complex configuration.
Embodiments of the present disclosure aim to provide a simple and effective solution, making it possible to ensure densification of an anti-corrosive paint to increase protection against corrosion, without embedding of hard particles, and by avoiding damaging the anti-corrosive paint.
This aim is achieved, for example, due to a method of compacting an anti-corrosive paint comprising metal particles and covering a mechanical part such as a turbine engine part. The method in some embodiments comprises a step of at least one spraying of solid ice particles on the part so as to densify and to make the paint electrically conductive.
Thus, this solution makes it possible to achieve the abovementioned aim or others. In some embodiments, such solid ice particles make it possible to densify the paint which covers the mechanical part in order to put the metal parts located in the paint in contact, which increases the resistance thereof to corrosion. The solid ice particles also make it possible, on the one hand, to remove the problems of embedding and discharge, when functioning, of foreign particles such as glass balls or corundum particles, since these will disappear by being sublimated following the impact thereof on the paint. In this manner, the physical integrity of the paint is preserved. Finally, embodiments of this method is easily automated, such that it makes it possible to reduce the manual operations consisting, among other things, of applying different layers of paint to overcome the embedding of foreign particles, and consequently, a gain in terms of the production timeframe and cost.
Embodiments of the method also comprise one or more of the following features or steps, taken individually or in combination:
The disclosure also relates to a method for producing an anodic coating. In an embodiment, the method comprises the following steps:
The disclosure also relates to the use of dry solid ice particles to achieve a compacting of anti-corrosive paint coating a metal part, and for example a turbine engine part.
The disclosure also relates to a mechanical part, in particular of a turbine engine, covered at least partially by a compacted anti-corrosive paint according to the abovementioned method.
The foregoing aspects and many of the attendant advantages of the claimed subject matter will become more readily appreciated as the same become better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:
The detailed description set forth below in connection with the appended drawings, where like numerals reference like elements, is intended as a description of various embodiments of the disclosed subject matter and is not intended to represent the only embodiments. Each embodiment described in this disclosure is provided merely as an example or illustration and should not be construed as preferred or advantageous over other embodiments. The illustrative examples provided herein are not intended to be exhaustive or to limit the claimed subject matter to the precise forms disclosed.
It should be noted that, prior to the compacting method, the part 2 is covered by an anti-corrosive paint. The paint is an inorganic paint or any paint comprising metal particles. In particular, a liquid paint loaded with metal particles is sprayed over the surface of the part. Advantageously, the metal particles are aluminium particles. Examples of anti-corrosive parts applied on the surface of the parts are those known under the brand Sermetel W® or Maberbind CF®.
After spraying the paint, the coated part is polymerised such that the paint hardens and forms the anti-corrosive paint intended to protect the part.
The anti-corrosive paint is then compacted. For this, the compacting is achieved by the compacting device 1. By the term “compacting”, this means, in the present disclosure, the action of spraying materials, possibly abrasive, at a high speed on the surface of the coated part to make the paint conductive. In this manner, the anti-corrosive paint is densified which puts the metal particles of the paint in contact and increases its strength against corrosion. The paint is made electrically conductive. Thus, an anodic coating is obtained.
The compacting device 1 comprises at least one nozzle 3 which is configured to spray a beam or a jet 4 of solid particles, making it possible to treat the surface of the turbine engine part. In the present example, the device 1 comprises a single nozzle 3 with an outlet orifice 5 placed at a distance from the part 2. The nozzle 3 is connected to a line 6 which is supplied with solid particles. The solid particles are kept in a reservoir (not shown). In some embodiments, the outlet orifice 5 of the nozzle is placed at a distance d from the surface of the part which is between about 20 mm and about 100 mm. Advantageously, but in a non-limiting manner, the predetermined distance d is between about 30 mm and about 60 mm. Preferably, the distance is 50 mm.
The nozzle 3 has a general direction which is inclined with respect to the surface of the part so as to avoid early wear of the solid particles. This inclination is between about 30° and about 85°. The minimum limit of about 30° makes it possible to avoid scraping of the paint. In some embodiments, the inclination of the nozzle with respect to the part is between about 45° and about 90°. It is arranged to achieve between one and two passages of the beam of solid particles on the surface of the part, in order to preserve the physical and cosmetic integrity of the paint.
To spray the particles, the nozzle 3 is moved along the height and the circumference of the part, preserving, at any time, the same geometry for the relative position of the nozzle and the surface of the part.
Of course, the disclosure is not limited to using this compacting device, which is only described as an example. The compacting device could, for example, comprise two nozzles, each sending a jet or beam of particles 3, and each oriented between about 30° and about 90° with respect to the surface of the part 1, the two beams being extended in one same plane. The general directions of the two nozzles are oriented at 90° from one another. The two beams join at one focalisation point 4 which is situated on the part 1, i.e. they both reach the same point to be treated. Given the solid angle characterising the divergence of the beams 3, the surface subjected at each moment to sandblasting has the shape of a circle of diameter “I”.
The compacting device 1 here is a high-pressure cryogenic cleaning system.
The compacting device 1 is advantageously installed in an enclosure 7 provided for this purpose. The enclosure 7 is closed by a door, through which the part is introduced. Advantageously, inside the enclosure, an ambient temperature and a controlled hygrometry prevail, in order to avoid the condensation of water on the part. Of course, it is not necessary for the enclosure to be closed.
The solid particles used to achieve the compacting of the anti-corrosive paint, which here covers the turbine engine part, are dry ice particles. These solid ice particles are composed advantageously, but in a non-limiting manner, of carbon dioxide (CO2) in solid form. Solid carbon dioxide is also known by the name of dry ice.
The solid ice particles are sprayed in the direction of the surface of the part (which is coated with paint) with a sufficient energy to densify the paint covering it. Once the solid particles have impacted the anti-corrosive paint, these are sublimated. This is made possible, thanks to the ambient temperature of the enclosure 7. The solid carbon dioxide is transformed into gas, which makes it possible not to leave particles embedded (superimposed) in the anti-corrosive paint. The sublimation temperature of the ice particles after impact is between 75° C. and 80° C. Advantageously, but in a non-limiting manner, the sublimation temperature is of around −78.9° C.
Advantageously, but in a non-limiting manner, a drying step can be implemented after the compacting, so as to control the condensation which can form after the sublimation of the solid dry ice particles. This can occur before the opening of the enclosure.
The solid particles have dimensions of between about 1 mm and about 30 mm. Advantageously, but in a non-limiting manner, the dimensions of these particles are between about 1 and about 10 mm. In one embodiment, the dimensions of the solid particles are about 3 mm. The particles can have a spherical shape.
The solid ice particles are delivered at a pressure of between about 2 and about 8 bars, and between about 5 and about 8 bars in some embodiments. In an embodiment, the pressure at which the particles are delivered is between about 6 bars and about 8 bars. This makes it possible to densify the paint without damaging it. There is no stripping of the paint with such an operational range. Likewise, in order to preserve the physical and cosmetic integrity of the paint, the ice particles are sprayed with a mass flow of between about 0.8 kg/h and about 2 kg/h. In an embodiment, the mass flow is between about 1 and about 1.5 kg/h.
The beam (cluster) of particles is moved to the surface of the part at a speed of between about 40 mm/s and about 60 mm/s. In an embodiment, the speed of the nozzle is about 50 mm/s.
The spraying of the ice particles at a constant pressure is facilitated thanks to an air flow sprayed at the same time as the particles in the nozzle, so as to facilitate the spraying of the particles. The nozzle 3 is moved at a speed of between about 40 mm/s and about 60 mm/s to move the cluster of ice particles.
Alternatively, a suctioning grit blasting machine, with a spray featuring an adapted air pressure and mass flow, can be considered for spraying the solid ice particles. This machine is, for example, equipped with one or two round nozzles of about 10 to about 14 mm.
Salt-spray tests (according to standard ISO 9227) to evaluate the resistance to corrosion of the paint thus compacted, have made it possible to demonstrate that this ensures its anti-corrosive role for the substrate after 168 hours of ageing. The ice particles also have the advantage of being sublimated after having been in contact with the paint, which leaves no trace of superimposed elements, contrary to the particles used in the prior art.
Concerning the paint compacted with the ice particles represented in
In an embodiment with a paint layer having a thickness of about 50 μm, the dry ice particles have been sprayed according to an inclination with respect to the surface of the part of about 90°. The particles have been sprayed, as a maximum, twice over the surface of the part. With a salt-spray test after 168 hours of ageing, the test tube has no red corrosion, nor any attack of localised corrosion (corrosion pit).
The present application may reference quantities and numbers. Unless specifically stated, such quantities and numbers are not to be considered restrictive, but exemplary of the possible quantities or numbers associated with the present application. Also in this regard, the present application may use the term “plurality” to reference a quantity or number. In this regard, the term “plurality” is meant to be any number that is more than one, for example, two, three, four, five, etc. The terms “about,” “approximately,” “near,” etc., mean plus or minus 5% of the stated value. For the purposes of the present disclosure, the phrase “at least one of A, B, and C,” for example, means (A), (B), (C), (A and B), (A and C), (B and C), or (A, B, and C), including all further possible permutations when greater than three elements are listed.
The principles, representative embodiments, and modes of operation of the present disclosure have been described in the foregoing description. However, aspects of the present disclosure which are intended to be protected are not to be construed as limited to the particular embodiments disclosed. Further, the embodiments described herein are to be regarded as illustrative rather than restrictive. It will be appreciated that variations and changes may be made by others, and equivalents employed, without departing from the spirit of the present disclosure. Accordingly, it is expressly intended that all such variations, changes, and equivalents fall within the spirit and scope of the present disclosure, as claimed.