This disclosure relates to a method and system of conformal coating and, more particularly, to a system and method of providing an amorphous fluorinated polymer conformal coating to at least one side of an RF circuit board.
Unlike most circuit board assemblies, which have a protective conformal coating, radiofrequency (“RF”) board assemblies are normally exposed directly to air during use without any coating, for fear of degrading their electrical performance. However, damaging incidents can occur due to this lack of coating, and these incidents could cause a manufacturer and/or user to incur long troubleshooting times and, potentially, performance problems that are difficult to remedy. These incidents could have a potentially large negative impact on RF projects and manufacturer/user costs and schedules. For example, splattering of solder on the finished but uncoated high reliability RF board assemblies during the sealing of a package housing with a cover selectively plated with solder can occur and cause undesirable short-circuits on the RF board assemblies. If such splattering occurred onto a conformal coating, the resulting short-circuit effects could be greatly reduced or even eliminated. This hydrophobic coating can also reduce undesirable corrosion effects upon the electric/electronic circuitry of the RF board assemblies.
GVD Corporation, of Cambridge, Mass., currently uses vapor phase processes to deposit a coating of Teflon™ brand polytetrafluoroethylene (available from The Chemours Company, of Wilmington, Del.) onto MEMS chips or wafer-type circuit boards in a thin enough layer that the RF performance of these items is not adversely affected. However, the coating chamber size for GVD's process is very small (a maximum of about 4″ diameter circular board assemblies can be accommodated), and the coating cannot cover the solder balls of ball grid array components, so this process is not practical for most RF board assemblies, which are substantially larger.
Generally, Teflon™ is known as being able to be applied as a conformal or corrosion protective coating as a film along even a large circuit board or part, but this film-coating application process results in a conformal coating that is thicker than desired for desired high precision and reliability performance of any RF circuit board assembly. Currently known brush- or dip-coating processes are not able to coat a consistently thin enough layer of Teflon™ on an RF circuit board assembly to achieve the desired conformal coating performance results.
In an embodiment, a method of providing an amorphous fluorinated polymer conformal coating to an RF circuit board is described. A coating solution including the amorphous fluorinated polymer dissolved in a fluorinated solvent is provided. The coating solution is applied to the RF circuit board via a mechanically controlled fluid spray application device to produce a coated board. A predetermined time period is waited for substantial evaporation of the fluorinated solvent from the coated board, thus leaving behind a conformal coating of the amorphous fluorinated polymer on a board surface area.
In an embodiment, a system for providing an amorphous fluorinated polymer conformal coating to an RF circuit board is described. A supply of a coating solution includes a solution of the amorphous fluorinated polymer with a fluorinated solvent. A mechanically controlled fluid spray application device is provided for applying the coating solution to the RF circuit board to produce a coated board. The amorphous plastic achieves a conformal coating on a board surface area responsive to the fluorinated solvent being selectively evaporated from the coated board.
For a better understanding, reference may be made to the accompanying drawings, in which:
This technology comprises, consists of, or consists essentially of the following features, in any combination.
Teflon™ AF is a family of amorphous fluoropolymers based on copolymers of 2,2-bistrifluouomethyl-4,5-difluoro-1,3-dioxole (PDD) and tetrafluoroethylene (TFE). Teflon™ AF has the chemical structure shown below.
The glass transition temperature (Tg) of Teflon™ AF is a function of PDD content in mol %. When the PDD content is about 40 mol %, the Tg is 90° C. Another example of a fluorinated polymer resin 206 that can be used is Cytop® 809M, available from AGC Chemicals Europe of Amsterdam, the Netherlands and having a formula Poly 1,1,2,4,4,5,5,6,7,7-decafluor-3-oxa-1,6-heptadiene.
Vertrel™ XF is a fluorinated-hydrocarbon solvent and will be generally referenced herein as a fluorinated solvent 208. Another example of a suitable fluorinated solvent 208 is the perfluoronated solvents known as 3M™ Fluorinert™ Electronic Liquids FC-72, FC-75, and/or FC-40, available from 3M Corporation of St. Paul, Minn. (“Per” means higher content of fluorine atoms than normally used fluorinated solvents.)
The system 202 also includes a mechanically controlled fluid spray application device 210 for applying the coating solution 204 to a board surface area (e.g., a top side, a bottom side, and/or another desirably-coated surface) of the RF circuit board assembly 100 to produce a coated board assembly 212. For example, the mechanically controlled fluid spray application device 210 can be a spray nozzle coating device. The coating solution 204 could be applied to one or both sides of a substantially flat RF circuit board assembly. The fluid spray application device 210 is able to be tilted and angled with respect to the RF circuit board assembly 100 to achieve desired fluid-coating thicknesses even on cavities or discontinuities on the board surface. One example of a suitable fluid spray application device 210 is the Select Coat SC-280N/SC-280C Film Coater Applicator, available from Nordson Corporation of Westlake, Ohio.
The RF circuit board assembly 100 which is coated to become a coated board assembly 212 may have a (coated) board surface area of more than thirteen square inches on at least one of the top and bottom board sides. Teflon™ coating of panels having surface areas of less than about thirteen square inches (such as, for example, a four-inch diameter round wafer) is currently available commercially, but achieving desired coating of Teflon™ across larger surface areas is believed to be impossible. As another example, the RF circuit board assembly 100 which is coated to become a coated board assembly 212 may have a board surface with a length dimension of less than nineteen inches and a width dimension of less than seventeen inches, when the present system uses particularly configured known fluid spray application devices 210.
As, or shortly after, the fluid spray application device 210 applies the coating solution 204 to the RF circuit board, the fluorinated solvent 208 evaporates. Accordingly, only the amorphous fluorinated polymer resin amorphous fluorinated polymer resin 206 portion of the coating solution 204 will remain on the coated board assembly 212 following the passage of a predetermined time period from the initiation of fluid-spray application of the coating solution 204. For example, Vertrel™ XF has a boiling point of about 57° C., and will “dry” within about 5-10 minutes after application, depending upon factors such as the room temperature and any convective air currents. The fluorinated solvent 208 can also serve a “cleaning” function, to dissolve and carry away any residual contaminants on the coated board assembly 212.
Once sufficient fluorinated solvent 208 has evaporated from the coating solution 204 located on the coated board, the amorphous fluorinated polymer resin 206 remains on the board, and is adhered to the board by adhesion of the amorphous fluorinated polymer resin 206 molecules and building layers of those molecules on the board surface. That is, the amorphous fluorinated polymer resin 206 achieves a conformal coating on a board and/or component surface area responsive to the fluorinated solvent 208 being selectively evaporated from the coated board assembly 212. Because the fluorinated solvent 208 also serves as a cleaning agent and as a coolant during its evaporation, the deposition rate of the amorphous fluorinated polymer resin 206 molecules can be slowed down to enhance the adhesion to the assembly surfaces. The adhesion may be further enhanced by subjecting the coated board assembly 212 to vacuum baking at 70° C. to 80° C. and 25 to 100 mTorr for 1 to 2 hours to help reduce or even eliminate trapped solvent and pores.
As a result, the board surface area becomes protectively coated with a material (both type and amount) which avoids (and/or does not cause) undesirable interference with, or degradation of, the performance of the RF circuits on the coated board assembly 212. For example, the conformal coating could be in the range of 3-18 microns thick across the board surface area. As another example, due to its fluorine content and low dielectric constant, the thickness of the conformal coating varies by less than 15 microns across the board surface area to help reduce or avoid performance degradation while still protecting the circuit traces from accidental high heat exposure.
A method of providing an amorphous fluorinated polymer 206 conformal coating to an RF circuit board assembly 100 is schematically described in
In third action block 318 of
If an error is made during the coating process, or through some other mechanism the coating solution 204 is applied to a surface for which a conformal coating is not desired, then the amorphous fluorinated polymer 206 (remaining after the fluorinated solvent 208 evaporates) can simply be removed from the unwanted portion(s) of the RF circuit board assembly 100, such as via wiping with a fluorinated solvent-dipped rag.
It is contemplated that the process shown in
While aspects of this disclosure have been particularly shown and described with reference to the example embodiments above, it will be understood by those of ordinary skill in the art that various additional embodiments may be contemplated. For example, the specific methods described above for using the apparatus are merely illustrative; one of ordinary skill in the art could readily determine any number of tools, sequences of steps, or other means/options for placing the above-described apparatus, or components thereof, into positions substantively similar to those shown and described herein. Any of the described structures and components could be integrally formed as a single unitary or monolithic piece or made up of separate sub-components, with either of these formations involving any suitable stock or bespoke components and/or any suitable material or combinations of materials. While the coated board assembly 212 is described, by way of example, as an RF circuit board assembly 100, it is contemplated that any type of circuit board, or any other device which is desired to provide with a conformal coating, could be similarly coated using the system 202 described herein. Any of the described structures and components could be disposable or reusable as desired for a particular use environment. A “predetermined” status may be determined at any time before the structures being manipulated actually reach that status, the “predetermination” being made as late as immediately before the structure achieves the predetermined status. Though certain components described herein are shown as having specific geometric shapes, all structures of this disclosure may have any suitable shapes, sizes, configurations, relative relationships, cross-sectional areas, or any other physical characteristics as desirable for a particular application. Any structures or features described with reference to one embodiment or configuration could be provided, singly or in combination with other structures or features, to any other embodiment or configuration, as it would be impractical to describe each of the embodiments and configurations discussed herein as having all of the options discussed with respect to all of the other embodiments and configurations. A device or method incorporating any of these features should be understood to fall under the scope of this disclosure as determined based upon the claims below and any equivalents thereof.
Other aspects, objects, and advantages can be obtained from a study of the drawings, the disclosure, and the appended claims.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5175023 | Iwase | Dec 1992 | A |
| 8148830 | Bedinger | Apr 2012 | B2 |
| 20120153285 | James | Jun 2012 | A1 |
| 20170194171 | Peterson | Jul 2017 | A1 |