Patent Grant
10457790
This present application is a national stage filing under 35 U.S.C § 371 of PCT application number PCT/KR2016/003562 filed on Apr. 6, 2016. The disclosures of the above-listed applications are hereby incorporated by reference herein in their entirety.
The present disclosure relates to a method of manufacturing a polishing pad, and more particularly, to a method of manufacturing a polishing pad configured to collect a slurry of a predetermined size.
The chemical mechanical planarization/chemical mechanical polishing (hereinafter, “CMP”) process has been introduced to planarize semiconductor devices. With the tendency of increasing the wafer size, high density integration, further downsizing of the linewidth, and multilayer wiring structure, the CMP process is getting more attention in the semiconductor manufacturing process.
Polishing speed and degree of planarization are key parameters in the CMP process, which can be determined by process condition of a polishing apparatus and expendable members used in the apparatus, such as polishing slurry and polishing pad. In particular, the polishing pad evenly spreads the slurry on the wafer while being in contact with the surface of the wafer, and causes a physical removal operation by polishing particles in the slurry and surface undulation of the polishing pad.
When polishing the wafer, the surface of the polishing pad having direct contact with the wafer should cause the slurry to smoothly circulate while maintaining saturated state of the slurry on the surface thereof. To this end, techniques for forming minute holes (e.g., pores) on the surface of the polishing pad have been proposed in, for example, U.S. Pat. No. 5,578,362, Korean Patent Application Laid-Open No. 10-2001-2696, and Korean Patent Application Laid-Open No. 10-2001-55971.
In order to improve function and performance of the polishing pad in the CMP process, it matters to maintain the saturated state of the slurry on the polishing pad, and hence various grooves are formed to make a flow of the slurry on the polishing pad, and above and beyond that, the minute holes are formed on the surface of the polishing pad by opening fine porous material.
Regarding the formation of the groove, the technique has been developed with attempts of employing various patterns; however, the porous pore technique for forming the minute holes is practically limited to restricted usage of a specific pore forming method.
That is, as there are merits and demerits in the conventional pore forming method, the practical CMP process adjusts necessary process based on such merits and demerits of the pore forming method.
With demand of more minuteness and delicacy in the semiconductor process, however, the CMP process needs to develop a new porous pore forming method to support the state-of-the-art semiconductor process.
In particular, the failure to form the pore on the polishing pad with minute and constant size range cannot provide an appropriate CMP process in a technical field in which the delicacy and the minuteness are required.
For example, there is a technique for forming pores using inert gas only. However, the recent sophisticated CMP process requires the average size of pores in the polishing pad to be 31 μm or smaller and a fluctuation range thereof to be minimized. From this point of view, the above-mentioned technique of forming the pore using the inert gas only provides the average size of the pores that cannot meet such a condition.
Further, another technique for forming pores using chemical blowing agent produces pores having various sizes from several tens of micrometers to several thousands of micrometers, which is far from pores having a uniform size.
According to some embodiments of the present invention, a method of manufacturing a polishing pad includes producing an urethane prepolymer having a viscosity of 20,000 cps (at 25° C.) to 40,000 cps (at 25° C.) by mixing a plurality of polymers, mixing the urethane prepolymer with an inert gas and a low-boiling blowing agent having a boiling point of 60° C. to 150° C., and manufacturing a polishing layer including porous pores by causing a mixture produced at the mixing to be subjected to gelation and curing in a predetermined cast.
In some embodiments of the present invention, with reference to the total volume of the produced composite, 5% to 40% of the inert gas and 0.1% to 10% of low-boiling blowing agent are mixed to the urethane prepolymer.
Further, in some embodiments of the present invention, the method further includes producing the urethane prepolymer by mixing polypropylene glycol having tetravalent or more functional group and forming polyurethane of three-dimensional bonding structure by mixing the produced urethane prepolymer and curing agent.
Moreover, in some embodiments of the present invention, polishing layer is processed to spread pores by opening the porous pores on the surface thereof.
Exemplary embodiments of the present disclosure are described in detail below with reference to the accompanying drawings. In the following descriptions, like reference numerals designate like elements although the elements are shown in different drawings. Further, detailed descriptions of known functions and configurations incorporated herein are omitted for the purpose of clarity and for brevity.
As shown in
As shown in
Therefore, the support layer 110 includes a nonporous solid-state uniformly-elastic material having a hardness higher than the polishing layer 120.
Further, at least a part of the support layer 110 is transparent or translucent to allow a light beam for detecting surface flatness of a surface of the polishing target to pass therethrough.
Although the wafer 7 having a film to be polished including metal, insulating layer, and the like is instantiated as a polishing target in
Further, although it is shown that the shape of the polishing pad 100 is circular to fit to the rotating-type polishing apparatus 1 in
As shown in
In some embodiments, the polymer matrix 130 is formed with a material that is insoluble in a polishing slurry 13 that is a chemical solution for performing the surface flatness. For example, the polymer matrix 130 can be formed with a material that is not penetrable by the polishing slurry 13 supplied through a nozzle 11 of the polishing apparatus 1 as shown in
The polymer matrix 130 can be formed by chemically bonding or physically mixing materials for forming the polymer matrix.
The material for the polymer matrix include any one selected from the group consisting of polyurethane, polyether, polyester, polysulfone, polyacrylic, polycarbonate, polyethylene, polymethyl methacrylate, polyvinyl acetate, polyvinyl chloride, polyethyleneimine, polyethersulfone, polyetherimides, polyketone, melamine, nylon, fluorohydrocarbon, and any combination thereof.
A polyalkylene glycol compound can be any one selected from the group consisting of compounds obtained by doping alkylene oxide into a compound including water or active hydrogen and any combination thereof.
In some embodiments of the present invention, the polymer matrix 130 can be formed by mixing polymer (such as polypropylene glycol) having tetravalent or more functional group such as hydroxyl group. In this case, compared to the conventional case in which only polypropylene glycol having divalent or trivalent functional group is mixed, the performance of the polishing pad 100 can be enhanced in an excellent cost effective manner.
For example, when the polishing layer 120 is formed with the polyurethane, the structure of the polyurethane produced by the conventional method includes many repetitive two-dimensional bonding of ˜C—O molecules as shown in
However, when the polyurethane is formed by mixing the polypropylene glycol having tetravalent or more functional group as in the case of the present invention (see
In some embodiments, the polymer having tetravalent or more hydroxyl group is contained by the content of 1% to 30% with respect to the weight of produced urethane prepolymer.
For example, when the urethane prepolymer is formed by mixing a polymer having divalent hydroxyl group, a polymer having trivalent hydroxyl group, and a polymer having tetravalent or more hydroxyl group, the polymer having tetravalent or more hydroxyl group is mixed with the weight ratio of 1% to 30% of the urethane prepolymer.
When the weight ratio of the polymer having tetravalent or more hydroxyl group is smaller than 1% of the whole urethane prepolymer, the three-dimensional bonding by the polymer having the tetravalent or more hydroxyl group is unlikely to be generated, and as a result, not much contribution is given to the enhancement of the degree of cross-linkage. On the other hand, when the weight ratio of the polymer having tetravalent or more hydroxyl group is larger than 30% of the whole urethane prepolymer, the physical property of the tetravalent flexible polishing member is considerably decreased, causing the corresponding urethane prepolymer to be hardly controlled physically in the process of producing the polishing layer.
Therefore, in some embodiments, the polymer having the tetravalent or more hydroxyl group is mixed by the amount of 1% to 30% of the weight of the whole urethane prepolymer produced.
A glazing phenomenon (phenomenon in which surroundings of a pore is worn due to high pressure and friction, and the pore is blocked by the urethane and smudged) is generated while the CMP process is under progress in a pore 141′ area on the surface of the polishing pad 100; however, in the case of the polyurethane having the mesh structure as the present invention, the shape of the pore is constantly maintained for the lifetime of the polishing pad 100 while the CMP process is under progress.
Upper image of
Upper image of
Comparing lower images of
The polishing performance should be maintained in a constant manner for the lifetime of the polishing pad 100 in the CMP process. When the pore on the polishing pad 100 is blocked and the glazing is generated, the polishing performance is gradually degraded, and eventually, the lifetime of the polishing pad 100 is limited. However, if the shape of the pore is constantly maintained as in the case of the present invention, the polishing performance of the polishing pad 100 is constantly maintained without being degraded, and eventually, the lifetime of the polishing pad 100 is ensured and the cost for replacing the polishing pad 100 can be saved accordingly.
The prepolymer is produced in the middle stage of producing the polymer matrix 130. In some embodiments of the present invention, the viscosity of such a prepolymer is 20,000 cps (at 25° C.) to 40,000 cps (at 25° C.).
The viscosity of the prepolymer determines the size of the pore together with the inert gas and the low-boiling blowing agent for producing the porous pore in the polishing layer 120, which will be described in detail later.
The polishing layer 120 includes the porous pore. The porous pore is produced by mixing the inert gas and the low-boiling blowing agent, as is described in detail later, and if the other conditions are the same, the size of the pore is controlled by a ratio of the inert gas and the low-boiling blowing agent in the mixture.
In this manner, the polishing layer 120 includes the porous pore, and on the surface of the polishing layer 120, which comes in direct contact with the wafer 7, a plurality of opened minute pores 141′ defined by such porous pores 141 is arranged.
The pore 141′ being opened and defined by the porous pore 141 means that the porous pore from the inert gas and the low-boiling blowing agent in the polishing layer 120 is exposed to the outside so that a corresponding pore area is left as the pore 141′ being capable of capturing a predetermined material from the outside.
With the polishing pad 100 worn in the polishing process, the embedded porous pores 141 are continuously exposed to the surface of the polishing layer 120 to form the pores 141′, which are replaced by the polishing slurry 13. Therefore, as the polymer matrix 130 that is the material of the polishing layer 120 exists only on the surface, the polishing pad 100 is prevented from being nonuniformly worn and the silicon wafer 7 that is a polishing target can be uniformly polished.
In some embodiments of the present invention, the porous pores included in the polishing pad 100 are produced from the inert gas and the low-boiling blowing agent as described above.
The inert gas means a chemically stable gas with the atomic valence of zero, including helium (He), neon (Ne), argon (Ar), krypton (Kr), xenon (Xe), radon (Rn), and the like. Further, the inert gas includes all gases that does not react with the polymer matrix 130, e.g., not contributing to the urethane reaction, such as N2 gas, as well as group 8 elements on the periodic table.
The blowing agent generates considerable amount of foams from thermal vaporization or reaction when mixed with a predetermined base material, which can be roughly divided into chemical blowing agent and a physical blowing agent.
The chemical blowing agent foams with carbon dioxide generated by a reaction with water or the like by using activation of isocyanate group, and hence the water is used as the foaming agent. The physical blowing agent forms bubbles by generating a reaction heat by mixing a gas or using a decomposing or vaporizing foaming agent, and hence it does not contribute to a polymer reaction. Types and features of such blowing agents are already known, and hence a further explanation thereof is omitted.
In some embodiments of the present invention, among such blowing agents, a low-boiling blowing agent having a boiling point of 60° C. to 150° C. is employed, and a further explanation thereof is given later.
It is preferred that the size of the pores be uniform in the polishing pad 100. In addition, in order to support the latest micro process in the semiconductor field, pores having minute size in the order of micrometers (particularly, 31 μm or smaller) needs to be produced.
That is, the conventional technique or a general method cannot satisfy such requirements. However, the present invention meets such requirements with the above-mentioned structure.
An example of the method of manufacturing the polishing pad 100 according to some embodiments of the present invention and an effect thereof are described below.
First, the urethane prepolymer having the viscosity of 20,000 cps (at 25° C.) to 40,000 cps (at 25° C.) is produced by mixing a plurality of polymers.
The process of producing the urethane prepolymer itself is a general technique; however, in the present embodiments, the viscosity of the produced urethane prepolymer falls within a range of 20,000 cps (at 25° C.) to 40,000 cps (at 25° C.).
In particular, by producing the urethane prepolymer by mixing the polypropylene glycol having tetravalent or more functional group, the urethane prepolymer having the three-dimensional bonding structure is produced by mixing the urethane prepolymer and the curing agent. The effect of the three-dimensional structure is as described earlier.
Thereafter, the inert gas and the low-boiling blowing agent having the boiling point of 60° C. to 150° C. is mixed with the urethane prepolymer.
At this time, the ratio of mixing the inert gas and the low-boiling blowing agent is 5% to 40% of the inert gas and 0.1% to 10% of the low-boiling blowing agent with reference to the total volume of the produced mixture.
Thereafter, gelation and curing processes are performed (Step S110). That is, the mixture is solidified by putting the mixture in a case having a predetermined shape and performing the gelation and curing processes. The gelation process is performed for 5 minutes to 30 minutes at the temperature of 80° C. to 90° C., and the curing process is performed for 20 hours to 24 hours at the temperature of 80° C. to 120° C. However, it is a matter of course that the specific process temperature and time can be modified as appropriate to find the optimum condition.
Lastly, an output product cured in a predetermined shape is processed (Step S120). The process includes removal from the case, cutting and treatment of the surface.
First, the cured product is removed from the cast and cut to have predetermined thickness and shape. In order to improve the productivity, the polishing layer 120 can be formed in a sheet shape by using a known method in the field of manufacturing a polymer sheet, such as casting and press molding. In addition, in some embodiments of the present invention grooves of various shapes are formed on the surface of the polishing layer 120 to uniformly supply the polishing slurry 13 to the surface of the polishing layer 120.
Although the polishing pad 100 can be completed with the polishing layer 120 only, the support layer 110 can be provided by using a known method in the field of manufacturing the polishing pad 100 and the support layer 110 can be coupled with the polishing layer 120 to complete the polishing pad 100 as appropriate.
The polishing layer 120 produced in the above manner includes pores having minute and uniform sizes that cannot be compared with the conventional case.
As shown in
That is, it has been found that the pores having sizes of 30 μm or smaller can be produced when the viscosity of the urethane prepolymer is 20,000 cps (at 25° C.) or higher.
Further, when the viscosity of the urethane prepolymer is 40,000 cps (at 25° C.) or higher, the urethane prepolymer is not practically controllable due to the excess viscosity. In order to control the urethane prepolymer having such an excess viscosity requires considerable increase of the cost in the equipment side, and hence it is preferred to maintain the viscosity of the urethane prepolymer to 40,000 cps (at 25° C.) or lower.
As shown in
That is, it has been found that the pores having sizes of 30 μm or smaller can be produced when the viscosity of the boiling point of the blowing agent is 60° C. or higher. When the boiling point of the blowing agent 150° C. or higher, the reaction time is considerably increased due to a decrease of the foaming speed and the number of pores produced by the foaming is decreased, which degrades the efficiency of collecting the slurry by the polishing pad.
Therefore, it is preferred to use the blowing agent having the boiling point of 150° C. or lower.
As shown in
The low-boiling blowing agent needs to be mixed with the volume ratio of at least 0.1% or higher. When the volume ratio of the low-boiling blowing agent is lower than 0.1%, uniform and minute pores cannot be produced as if there exists the inert gas only.
In this case, pores having the size exceeding 31 μm are mainly produced, and hence the mixing volume ratio of the low-boiling blowing agent needs to be at least 0.1% or higher.
Specific experimental examples of the present invention are described below with comparison. Contents not described here can be technically understood by people having ordinary skill in the pertinent art, and therefore the explanations thereof will be omitted. It is a matter of course that these experimental examples should not be construed to limit the scope of the present invention.
Polytetramethylene glycol (molecular weight 1000) 70 kg, polypropylene glycol (molecular weight 1000) 30 kg, toluene disocyanate 60 kg were put into a 200-kg reactor and allowed to react for 4 hours to 5 hours at the temperature of 70° C. to 80° C., from which isocyanate prepolymer having NCO content of the final product of 9.0% was produced.
The viscosity of the produced isocyanate prepolymer was 35,000 cps (at 25° C.).
Polytetramethylene glycol (liquid ratio of molecular eight 1000:800=8:2) 80 kg, polypropylene glycol (liquid ratio of molecular weight 1000:2000=5:5, functional group f=4) 20 kg, toluene disocyanate 67 kg were put into a 200-kg reactor and allowed to react for 4 hours to 5 hours at the temperature of 70° C. to 80° C., from which isocyanate prepolymer having NCO content of the final product of 9.0% was produced. The viscosity of the produced isocyanate prepolymer was 30,000 cps (at 25° C.).
The isocyanate prepolymer of the experimental example 1 100 kg and MOCA 29 kg were discharged through a mixing head by using a casting machine. At this time, N2 gas as the inert gas was supplied to the mixing head with the volume ratio of 30%.
Thereafter, the mixture was immediately injected into a square-shaped cast. The injected reaction solution was put in a gelation process for 30 minutes with 1 minute of tack free time (TFT), and cured in a 100° C. oven for 20 hours.
The cured product was removed from the cast, and the polishing layer 120 of the polishing pad 100 was produced by cutting the surface.
The average pore size of the surface of the polishing layer 120 was about 40 μm or larger. The pore image is as shown in
The isocyanate prepolymer of the experimental example 2 100 kg, MOCA 29 kg, the inert gas, and the low-boiling blowing agent were discharged through a 5,000-rpm mixing head by using a casting machine. At this time, N2 gas as the inert gas and the low-boiling blowing agent were supplied to the mixing head with the volume ratio of 10% and 8%, respectively.
Thereafter, the mixture was immediately injected into a square-shaped cast. The injected reaction solution was put in a gelation process for 30 minutes with 1 minute of TFT, and cured in a 100° C. oven for 20 hours. The cured product was removed from the cast, and the polishing layer 120 of the polishing pad 100 was produced by cutting the surface.
The average pore size of the surface of the polishing layer 120 was about 29 μm. The pore image is as shown in
Consequently, the average size of produced pores can be 31 μm or smaller and as uniform as possible only when the specific condition according to the present invention is met.
The isocyanate prepolymer of the experimental example 2 100 kg, MOCA 29 kg, the inert gas, and the low-boiling blowing agent were discharged through a 5,000-rpm mixing head by using a casting machine. At this time, N2 gas as the inert gas and the low-boiling blowing agent were supplied to the mixing head with the volume ratio of 15% and 6%, respectively.
Thereafter, the mixture was immediately injected into a square-shaped cast. The injected reaction solution was put in a gelation process for 30 minutes with 1 minute of TFT, and cured in a 100° C. oven for 20 hours. The cured product was removed from the cast, and the polishing layer 120 of the polishing pad 100 was produced by cutting the surface.
The average pore size of the surface of the polishing layer 120 was about 27 μm. The pore image is as shown in
The isocyanate prepolymer of the experimental example 2 100 kg, MOCA 29 kg, the inert gas, and the low-boiling blowing agent were discharged through a 5,000-rpm mixing head by using a casting machine. At this time, N2 gas as the inert gas and the low-boiling blowing agent were supplied to the mixing head with the volume ratio of 18% and 4%, respectively.
Thereafter, the mixture was immediately injected into a square-shaped cast. The injected reaction solution was put in a gelation process for 30 minutes with 1 minute of TFT, and cured in a 100° C. oven for 20 hours. The cured product was removed from the cast, and the polishing layer 120 of the polishing pad 100 was produced by cutting the surface.
The average pore size of the surface of the polishing layer 120 was about 24 μm. The pore image is as shown in
The isocyanate prepolymer of the experimental example 2 100 kg, MOCA 29 kg, the inert gas, and the low-boiling blowing agent were discharged through a 5,000-rpm mixing head by using a casting machine. At this time, N2 gas as the inert gas and the low-boiling blowing agent were supplied to the mixing head with the volume ratio of 20% and 2%, respectively.
Thereafter, the mixture was immediately injected into a square-shaped cast. The injected reaction solution was put in a gelation process for 30 minutes with 1 minute of TFT, and cured in a 100° C. oven for 20 hours. The cured product was removed from the cast, and the polishing layer 120 of the polishing pad 100 was produced by cutting the surface.
The average pore size of the surface of the polishing layer 120 was about 21 μm. The pore image is as shown in
From the result of evaluating the polishing performance and the lifetime performance for Ceria Slurry and W slurry processes shown in
Further, the pores can be produced in the polishing pad with smaller and more uniform size according to some embodiments of the present invention, which allows a distance between the pores to be shortened. As shown in
Such a lowered Rsm value allows the pad wear debris size generated during the CMP process to be decreased as shown in
In the above-mentioned experimental examples, the temperature of mixing the inert gas and the low-boiling blowing agent can be selected in a range from 60° C. to 150° C.
It is an object of the present invention to provide a method of manufacturing a polishing pad that can collect polishing slurry with a uniform and minute size and maximize the polishing performance and the flattening performance.
The present disclosure should not be limited to these embodiments but various changes and modifications are made by one ordinarily skilled in the art within the subject matter, the spirit and scope of the present disclosure as hereinafter claimed. Specific terms used in this disclosure and drawings are used for illustrative purposes and not to be considered as limitations of the present disclosure. Exemplary embodiments of the present disclosure have been described for the sake of brevity and clarity. Accordingly, one of ordinary skill would understand the scope of the claimed invention is not to be limited by the explicitly described above embodiments but by the claims and equivalents thereof.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2016/003562 | 4/6/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/175894 | 10/12/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5100926 | Kondo | Mar 1992 | A |
| 5578362 | Reinhardt et al. | Nov 1996 | A |
| 6331577 | Volkert | Dec 2001 | B1 |
| 8697239 | Kulp | Apr 2014 | B2 |
| 20020078632 | Hasegawa | Jun 2002 | A1 |
| 20040053007 | Huh | Mar 2004 | A1 |
| 20040166790 | Balijepalli | Aug 2004 | A1 |
| 20060014846 | Sparks | Jan 2006 | A1 |
| 20070232711 | Frei | Oct 2007 | A1 |
| 20090062414 | Huang et al. | Mar 2009 | A1 |
| 20130212951 | Ahn | Aug 2013 | A1 |
| 20130243986 | Girotti | Sep 2013 | A1 |
| 20150133039 | Ahn | May 2015 | A1 |
| 20150375362 | Qian | Dec 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 2004-330411 | Nov 2004 | JP |
| 2004330411 | Nov 2004 | JP |
| 2006-519115 | Aug 2006 | JP |
| 2008-506815 | Mar 2008 | JP |
| 2009-125894 | Jun 2009 | JP |
| 2009125894 | Jun 2009 | JP |
| 2010-082719 | Apr 2010 | JP |
| 20010002696 | Jan 2001 | KR |
| 20010055971 | Jul 2001 | KR |
| Entry |
|---|
| Japanese Office Action dated Aug. 7, 2018, in connection with the Japanese Patent Application No. 2017-529389. |
| Japanese Notice to Grant a Patent dated Nov. 6, 2018, issued in corresponding Japanese Patent Application No. 2017-529389. |
| Extended European Search Report dated Sep. 9, 2019, in connection with counterpart European Patent Application No. 16858489.4, citing the above reference. |
| Number | Date | Country | |
|---|---|---|---|
| 20180118908 A1 | May 2018 | US |