Patent Grant
11713498
This application claims priority to and the benefit of Korean Patent Application No. 10-2019-0059872, filed on May 22, 2019, the disclosure of which is incorporated herein by reference in its entirety.
The present disclosure relates to a method of manufacturing a uranium target (particularly, a high-density and low-enriched uranium target) to be soluble in a basic solution and a method of extracting radioactive Mo-99 using the same.
Tc-99m, which is an element that accounts for about 80% of the demand for medical diagnostic radioisotopes, is an important medical radioisotope for nuclear medical disease diagnosis. Tc-99m is an artificial element that does not exist in nature and is a daughter nuclide produced by radiation decay of Mo-99. Currently, as a method of preparing Mo-99 that is the only parent nuclide of Tc-99m in the world, a method of extracting Mo-99 from a product produced by nuclear fission of uranium powder in a plate-type dispersion target is widely used. However, since Mo-99 has a very short half-life of 66 hours, a highly enriched uranium target with a concentration of 90% or higher has been used to increase productivity.
Recently, the United States and the International Atomic Energy Agency (IAEA) has focused on the nuclear non-proliferation policy of reducing the concentration of an irradiated target material, uranium, from a high concentration of about 90% to 20% or less so as to produce a medical radioisotope, Mo-99. This policy has been promoted worldwide since 1996. Accordingly, major Mo-99 producers are converting their Mo-99 production facilities using highly enriched uranium to low-enriched uranium facilities. Currently, in South Africa's SAFARI reactor and Australia's OPAL reactor, Mo-99 is being produced using dispersion targets with 20% or less of low-enriched uranium. However, since the concentration of uranium in an irradiated target material is lowered from about 90% to 20% or less, the amount of U-235 actually contained in the target is reduced by one third, compared to the case of using high-enriched uranium, which causes a decrease in a production amount of Mo-99. Thereby, research into increasing a total content of uranium in a target, rather than reducing the concentration of U-235 from 90% to a low concentration of 20%, is underway.
The Korea Atomic Energy Research Institute has manufactured a high-density dispersion target with a uranium density of 6 gU/cc using a uranium centrifugal atomization powder. However, this target consists of a metal U phase that is not dissolved in a basic solution used to produce isotopes, such as NaOH. Since such a metal U phase can only be dissolved using nitric acid, and a solution obtained after separating Mo-99 from a uranium solution, dissolved in the nitric acid, by ion adsorption, contains uranium, the solution should be classified and treated as liquid radioactive waste. Here, since the liquid radioactive waste, in which uranium is dissolved, has a small fission critical mass, it occupies a large space and causes corrosion of nearby devices and facilities due to acid fumes.
Therefore, the present disclosure has been made in view of the above problems, and it is one object of the present disclosure to manufacture a high-density and low-enriched uranium target soluble in a basic solution so as to extract radioactive Mo-99 and, accordingly, provide a method of manufacturing a uranium target, the method including (a) a step of preparing a conjugate including a matrix and a uranium target green compact formed in the matrix; and (b) a step of performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate.
It will be understood that technical problems of the present disclosure are not limited to the aforementioned problem and other technical problems not referred to herein will be clearly understood by those skilled in the art from the disclosure below.
In accordance with an aspect of the present disclosure, the above and other objects can be accomplished by the provision of a method of manufacturing a uranium target, the method including: preparing a conjugate including a matrix and a uranium target green compact formed in the matrix; and performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate.
In accordance with another aspect of the present disclosure, there is provided a method of extracting radioactive Mo-99, the method including: manufacturing the uranium target, and then dissolving the uranium target in a basic solution; and extracting radioactive Mo-99 from the basic solution containing the uranium target dissolved therein.
The above and other objects, features and other advantages of the present disclosure will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
First, the term “uranium target” used in the present specification refers to a uranium target that has undergone fission through irradiation of a uranium-containing material with neutrons and includes a fission product including radioactive Mo-99. The uranium target may be plate-shaped or annular.
Existing low-enriched uranium targets are manufactured by dispersing uranium aluminide in an aluminum matrix. Such low-enriched uranium targets have low uranium densities of about 2.6 to 2.7 gU/cm3, thus having low production yields and generating more waste, compared to high-enriched uranium targets.
In addition, when a uranium target is manufactured by dispersing a uranium alloy or uranium metal having a high density in an aluminum matrix, the uranium alloy or uranium metal is not easily dissolved in a basic solution. Accordingly, a basic solution could not be used in a process of extracting radioactive Mo-99.
Accordingly, the uranium target according to the present disclosure is a high-density and low-enriched uranium target and may be dissolved in a basic solution.
In particular, the uranium target is a low-enriched uranium target and may include 20% by weight or less of U-235, which is prone to fission, of uranium isotopes. Uranium exists in the form of isotopes of U-238 and U-235. In nature, there is about 99.3% of U-238, which is not prone to fission, and about 0.7% of U-235 which is prone to fission. Here, low-enriched uranium is suitable for preventing nuclear proliferation due to a low content of U-235, compared to high-enriched uranium with a U-235 content of 90% or more.
In addition, the uranium target is characterized by having a high density. In particular, the density of the uranium target may be 3.0 gU/cm3 to 10.0 gU/cm3, preferably 3.0 gU/cm3 to 8.0 gU/cm3, but the present disclosure is not limited thereto. Due to the increased density of uranium, an extraction yield of radioactive Mo-99 may be increased.
According to a conventional method, a uranium target conjugate is subjected to hot rolling; a blister test; cold rolling and plate correction; and phase transformation heat treatment, thereby manufacturing a uranium target. When phase transformation heat treatment is separately carried out after hot rolling in such a manner, deformation and breakage of the shape of a finally produced uranium target are inevitable due to volume expansion of a uranium-aluminum alloy powder occurring during the phase transformation.
Accordingly, the present inventors have performed thermo-mechanical treatment, a blister test, cold rolling, and plate correction (that is, additional heat treatment has been performed during a hot rolling pass in a hot rolling process and separate phase transformation heat treatment has been omitted) for a uranium target conjugate, instead of the conventional method, to manufacture a uranium target, and have confirmed that a uranium target soluble in a basic solution can be manufactured without shape deformation and breakage, thus completing the present disclosure.
Hereinafter, the present disclosure is described in detail.
Method of Manufacturing Uranium Target
The present disclosure provides a method of manufacturing a uranium target, the method including (a) a step of preparing a conjugate including a matrix and a uranium target green compact formed in the matrix; and (b) a step of performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate.
First, the method of manufacturing a uranium target according to the present disclosure includes a step [step (a)] of preparing a conjugate including a matrix and a uranium target green compact formed in the matrix.
In particular, the conjugate includes a matrix and a uranium target green compact formed in the matrix.
The matrix serves to disperse uranium aluminide and may include aluminum.
In addition, the high-density and low-enriched uranium target green compact may be prepared by mixing and compacting a uranium-aluminum alloy powder and an aluminum powder. The content of the aluminum in the uranium-aluminum alloy powder may be 20% by weight or less. In other words, the high-density and low-enriched uranium target green compact may be manufactured by mixing and compacting a uranium-aluminum alloy powder and an aluminum powder. In particular, the uranium-aluminum alloy powder may be mixed in a content of 60% by volume or less, preferably 10% by volume to 50% by volume, with respect to the sum of the uranium-aluminum alloy powder and the aluminum powder. Here, the mixing may be performed at 10 rpm to 100 rpm for 1 hour to 10 hours, and the compacting may be performed for a compression time of 60 seconds to 180 seconds and a decompression time of 30 seconds to 120 seconds under a pressure of 50 ton to 200 ton.
Meanwhile, the matrix and the high-density and low-enriched uranium target green compact may be joined to form a conjugate by welding. Here, the welding may be performed at a current of 100 A to 200 A and a voltage of 5 V to 20 V.
Next, the method of manufacturing a uranium target according to the present disclosure includes a step [step (b)] of performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate.
In particular, the thermo-mechanical treatment refers to additional heat treatment performed during a hot rolling pass in a process of hot rolling.
The hot rolling through the hot rolling pass is a conventional method. Here, a surface temperature of the hot roll may be 80° C. to 100° C.
Before performing the hot rolling pass, preheating may be performed at 480° C. to 520° C. for 10 minutes to 1 hour. In addition, the number of hot rolling passes is preferably 5 to 10, and a reduction ratio per pass is preferably 10% to 30%, but the present disclosure is not limited thereto. Here, between the hot rolling passes, a step of reheating at 480° C. to 520° C. for 1 minute to 20 minutes may be additionally included.
The additional heat treatment is performed at 530° C. to 600° C., preferably 540° C. to 600° C., during the hot rolling pass, but the present disclosure is not limited thereto. Here, when the temperature of the additional heat treatment is too low, a U or UAl2 phase of the conjugate may not be changed to a UAl3 or UAl4 phase. When the temperature of the additional heat treatment is too high, Al (melting point: 658° C.) may be melted, whereby damage to the uranium target is inevitable.
In addition, the additional heat treatment may be performed for a total of 5 hours to 20 hours. To sufficiently change a U or UAl2 phase to a UAl3 or UAl4 phase, the additional heat treatment is preferably performed for a total of 7 hours to 20 hours, but the present disclosure is not limited thereto.
Meanwhile, the additional heat treatment may be performed for a single hot rolling pass or over multiple hot rolling passes. When the additional heat treatment is slowly performed over multiple hot rolling passes, deformation, etc. due to the additional heat treatment may be prevented.
In other words, when the thermo-mechanical treatment is performed through additional heat treatment during a hot rolling pass in a process of hot rolling, a U or UAl2 phase in the conjugate may be changed to a UAl3 or UAl4 phase.
Meanwhile, when hot rolling is performed without additional heat treatment as in a conventional method, a U or UAl2 phase becomes present in a finally produced uranium target, so that dissolution in a basic solution is not accomplished. When phase transformation heat treatment is performed after hot rolling so as to address the problems, the volume of a uranium-aluminum alloy powder expands during phase transformation, resulting in deformation and breakage of the shape of a finally produced uranium target.
After the thermo-mechanical treatment, a blister test and cold rolling may be additionally performed. On the other hand, after the thermo-mechanical treatment, a separate phase transformation heat treatment may be omitted.
Method of Extracting Radioactive Mo-99
The present disclosure provides a method of extracting radioactive Mo-99, the method including a step of manufacturing a uranium target, and then dissolving the same in a basic solution; and a step of extracting radioactive Mo-99 from the basic solution containing the uranium target dissolved therein.
First, in the method of extracting radioactive Mo-99 according to the present disclosure, the uranium target is dissolved in a basic solution, thereby preparing a basic solution including uranium aluminide and a fission product.
Since there is no U or UAl2 phase in the uranium target, the uranium target has an advantage of being easily dissolved in a basic solution. When such a basic solution is used, solid waste is generated, and thus the amount of waste is small, unlike the case in which an acidic solution is used. Since the solid waste may be immediately stored, there is an advantage of easy handling.
The basic solution may be any known basic solution and is preferably a sodium hydroxide (NaOH) solution, but the present disclosure is not limited thereto.
Next, in the method of extracting radioactive Mo-99 according to the present disclosure, radioactive Mo-99 is extracted from the basic solution in which the uranium target has been dissolved. Here, since the density of uranium is increased, an extraction yield of radioactive Mo-99 may also be increased. In addition, a nuclear proliferation problem may be prevented due to use of the low-enriched uranium.
The extraction may be performed using various known methods such as adsorption, chromatography, precipitation separation, and ion exchange.
As described above, the method of manufacturing a uranium target according to the present disclosure includes (a) the step of preparing a conjugate including a matrix and a uranium target green compact formed in the matrix; and (b) the step of performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate. Accordingly, a U or UAl2 phase in the conjugate may be changed to a UAl3 or UAl4 phase through the thermo-mechanical treatment.
Therefore, the uranium target manufactured according to the method is a high-density and low-enriched uranium target and may be dissolved in a basic solution without shape deformation and breakage, so that radioactive Mo-99 may be efficiently extracted.
Now, the present disclosure will be described in more detail with reference to the following preferred examples. These examples are provided for illustrative purposes only and should not be construed as limiting the scope and spirit of the present disclosure.
Experimental Methods
(1) Preparation of Atomized U—Al Powder
The Korea Atomic Energy Research Institute manufactured U-xAl (x=0, 5, 10, 15, 20 and 25% by weight) alloy powders using the centrifugal atomization technology. First, U and Al ingots were prepared, and arc-melted together in an Ar atmosphere to avoid thermal shock. Next, a U—Al master alloy was fed into a ZrO2 crucible, followed by heating at a temperature of 300° C. higher than a melting point of the intermetallic compound to increase the fluidity of the molten metal. Finally, the molten metal was fed onto a rotating graphite disk. Through the rotating graphite disk, numerous small droplets were produced. The droplets were dispersed toward a chamber and cooled very quickly. The microstructures and constituent phases of produced powders were confirmed using SEM/EDS and XRD.
(2) Manufacture of High-Density Dispersion Targets
High-density dispersion targets having a uranium density of 3.2 gU/cm3 were manufactured using atomized U-xAl (x=0, 5, 10, 15 and 20% by weight) powders. To limit a U—Al powder volume percentage in a target, U-25Al was excluded based on Table 1. Next, targets were manufactured using typical plate fuel manufacturing procedures including mixing with a Al powder, compaction, TIG welding, hot rolling, a blister test, and cold rolling. Here, heat treatment was performed at 550° C. during a hot rolling pass in a process of hot rolling a conjugate to change U and UAl2 phases to UAl3 and UAl4 phases. Constituent phases were confirmed using XRD.
Atomized U—Al powders were successfully prepared.
Previous studies have shown that a U—Al powder consists of complex intermetallic phases.
Manufacture of Hot-Rolled Targets
Some conventional targets have been manufactured using U-15Al and U-10Al powders and subjected to phase transformation heat treatment (phase transformation heat treatment condition: at 550° C. for 20 hours in an air atmosphere) after hot rolling. The phase transformation caused significant volume expansion due to great deformation. To prevent such deformation, a heat treatment process was included in the hot rolling process. Table 3 shows the modified heat treatment conditions. As a result, a target was successfully manufactured without any deformation as shown in
Meanwhile, as shown in
The Korea Atomic Energy Research Institute manufactured a high-density LEU target having a uranium density of 3.2 gU/cm3 using an atomized uranium-aluminum powder. The characteristics of the atomized powder depended upon the content of Al: the contents of Al in α-U and UAl2 phases were less than 15% by weight; and the contents of Al in UAl2 and UAl3 phases were 20 to 25% by weight. The target was subjected to heat treatment to remove a UAl2 phase. The heat treatment was performed during hot rolling so as to prevent deformation of the target. It was confirmed that heat treatment should be performed at 550° C. for 7 hours so as to cause the entire phase transformation of a UAl2 phase.
As apparent from the above description, the present disclosure provides a method of manufacturing a uranium target, the method including (a) a step of preparing a conjugate including a matrix and a uranium target green compact formed in the matrix; and (b) a step of performing thermo-mechanical treatment through additional heat treatment at 530° C. to 600° C. during a hot rolling pass in a process of hot-rolling the conjugate. Accordingly, a U or UAl2 phase in the conjugate can be changed to a UAl3 or UAl4 phase through the thermo-mechanical treatment.
Therefore, the uranium target manufactured according to the method is a high-density and low-enriched uranium target and can be dissolved in a basic solution without shape deformation and breakage, so that radioactive Mo-99 can be efficiently extracted.
The aforementioned description of the present disclosure is provided by way of example and those skilled in the art will understand that the present disclosure can be easily changed or modified into other specified forms without change or modification of the technical spirit or essential characteristics of the present disclosure. Therefore, it should be understood that the aforementioned examples are only provided by way of example and not provided to limit the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2019-0059872 | May 2019 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2917383 | Saller et al. | Dec 1959 | A |
| 4705577 | Ondracek et al. | Nov 1987 | A |
| 5694799 | Wolpert | Dec 1997 | A |
| 20150340110 | Stepnik | Nov 2015 | A1 |
| 20200234836 | Park et al. | Jul 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 2014280928 | Feb 2016 | AU |
| 2681744 | Jan 2016 | EP |
| 2994574 | Feb 2014 | FR |
| 10-0764902 | Oct 2007 | KR |
| 10-1138445 | Apr 2012 | KR |
| 10-1460690 | Nov 2014 | KR |
| 101460690 | Nov 2014 | KR |
| 10-1640237 | Jul 2016 | KR |
| WO 2012121466 | Sep 2012 | WO |
| Entry |
|---|
| Espacenet machine translation of KR-101460690-B1 retrieved on May 3, 2022 (Year: 2014). |
| Number | Date | Country | |
|---|---|---|---|
| 20200368820 A1 | Nov 2020 | US |