Claims
- 1. A chemical vapor deposition method for the preparation of high temperature stable thin film resistors having a predetermined temperature coefficient of resistance (TCR) and bulk resistivity comprising:
- placing a substrate having an electrically insulative surface in a reactor;
- flowing a reducing carrier gas through the reactor at a pressure of about 0.1 to 10 Torr to remove the ambient gas;
- heating the substrate to a controlled temperature between 500.degree. C. and 900.degree. C.;
- introducing a reactant gas into the flowing carrier gas, the reactant gas comprising a mixture of at least one decomposable compound of tungsten and at least one decomposable compound of silicon in a controlled ratio; and
- contacting the flowing reactor and carrier gases with the heated surface of the substrate to decompose the reactant gas to deposit a thin film of tungsten silicide on the substrate, the controlled ratio of tungsten to silicon in the reactant gas being in part determinative of the tungsten to silicon ratio in the thin film which is determinative of the bulk resistivity and TCR of the film, and the controlled temperature of the substrate being determinative of the crystallinity of the film which is determinative of the TCR of the film, whereby for a tungsten to silicon ratio in the range of 1:3 to 3:1 a low substrate temperature will produce an essentially amorphous film having a TCR nearly equal to 0 ppm/.degree.C. and increasing the substrate temperature will produce a more crystalline film having a more positive TCR, and whereby for tungsten to silicon ratios outside the limits of 1:3 to 3:1 the tungsten to silicon ratio will also affect the value of the TCR.
- 2. The method of claim 1 wherein the ratio of tungsten to silicon in the thin film is controlled within the range of 3:1 to 1:3 whereby as the ratio approaches 3:1 the bulk resistivity approaches about 100.times.10.sup.-6 .OMEGA. cm and the TCR approaches about +200 ppm/.degree.C., and as the ratio approaches 1:3 the bulk resistivity approaches about 0.5.OMEGA. cm and the TCR approaches about -200 ppm/.degree.C.
- 3. The method of claim 1 wherein the ratio of tungsten to silicon in the thin film is maintained above 3:1 whereby as the ratio increases the bulk resistivity will approach a lower limit of about 7.5.times.10.sup.-6 .OMEGA. cm and the TCR will approach a positive limit of about +3000 ppm/.degree.C.
- 4. The method of claim 1 wherein the ratio of tungsten to silicon in the thin film is maintained below 1:3 whereby as the ratio decreases the bulk resistivty will exponentially approach an upper limit of about 10.sup.6 .OMEGA. cm and the TCR will approach a negative limit of about -4000 ppm/.degree.C.
- 5. The method of claim 2 wherein tungsten to silicon ratio is about 1:1 and the deposition temperature is between 600.degree. C. and 800.degree. C. whereby the TCR of the thin film is about 0 ppm/.degree.C.
- 6. The method of claim 1 wherein the decomposable gaseous compounds of tungsten are selected from the group consisting of tungsten hexafluoride and tungsten pentachloride and the decomposable compounds of silicon are selected from the group consisting of silane, silicon tetrachloride, and dichlorosilane.
- 7. The method of claim 6 wherein the substrate is selected from the group consisting of silicon, sapphire, quartz and passivated molybdenum.
- 8. The method of claim 7 wherein the reducing carrier gas is selected from the group consisting of helium containing at least 10% hydrogen, argon containing at least 10% hydrogen, and hydrogen, and the ratio of carrier gas to reactant gas is from 100:1 to 1000:1.
- 9. The method of claim 8 wherein the deposition time is from about 3 to about 12 minutes.
Parent Case Info
This application is a continuation-in-part of U.S. patent application Ser. No. 27,439 filed Apr. 5, 1979, now abandoned.
CONTRACTUAL ORIGIN OF THE INVENTION
The U.S. Government has rights in this invention pursuant to Contract No. EY-76-S-02-4081 between the U.S. Department of Energy and University of Arizona.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3540920 |
Wakefield |
Nov 1970 |
|
3563873 |
Beyer |
Feb 1971 |
|
Foreign Referenced Citations (2)
Number |
Date |
Country |
45-13782 |
Apr 1970 |
JPX |
481945 |
Jun 1975 |
SUX |
Non-Patent Literature Citations (1)
Entry |
Vapor Deposition, Powell, 1966, pp. 322-325, 403, 596-597. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
27439 |
Apr 1979 |
|