Method of producing an hydraulic hose

Abstract

An apparatus and method for producing an hydraulic hose having ends of different internal diameters. An uncured hose is produced by conventional extrusion. The uncured hose is placed upon a mandrel having a reduced diameter end. That end of the uncured hose proximate the reduced diameter of the mandrel is covered by a heat responsive shrink tube. The shrink tube is heated to mold the end of the hose about the mandrel. Thereafter, the hose is vulcanized.

Description

BACKGROUND OF THE INVENTION

This invention relates to the production of elastomeric pressurized fluid conveying system hoses and more particularly to a method of producing a pressurized fluid conveying system hose having ends of different diameter. Such hoses are commonly used in automotive vehicles for carrying hydraulic fluid between a pump, a reservoir and an hydraulic device such as a power steering unit. These hoses, commonly called hydraulic hoses, are customarily of uniform internal diameter and are clamped or coupled at each end to a nipple having an external diameter substantially equal to the internal diameter of the hose. This creates a design constraint for the equipment being serviced by the hose. Oftentimes it is desirable to present the hose ends to nipples of different external diameter. This requires an hydraulic hose having ends of different internal diameter. Heretofore there has been no economical way of producing a hose having a reduced diameter on at least one end.

It is known in the prior art to build a hose upon a mandrel in such a way as to produce an end of slightly reduced diameter, as shown, for example, in Greacen U.S. Pat. No. 165,324. However, the Greacen method proceeds by a complicated series of steps involving placement and positioning on the mandrel of a rubber core, a helically coiled, tempered and untempered steel wire and a suitable covering material. It is also known to place a hose upon a mandrel for curing and to wrap the hose with shrink film to compress it against the mandrel, as taught by Borden U.S. Pat. No. 3,752,719. Other prior art, such as Badberg et. al. U.S. Pat. No. 4,171,118, reshapes a cylindrical hose into a hose of complex configuration by vulcanization upon a specially shaped mandrel having at least one end enlarged.

SUMMARY OF THE INVENTION

This invention provides a method of producing an hydraulic hose adapted to carry hydraulic fluid between nipples of different diameter. The method involves producing of an uncured hose of uniform diameter and placing the uncured hose over a mandrel of non-uniform crossection. The mandrel has a diameter at one end which is substantially the same as the internal diameter of the uncured hose and a diameter at the other end which is substantially less. The uncured hose is placed on the mandrel in such a manner as to span the length of the mandrel between the crossections of different diameter. After the hose has been seated on the mandrel, the end of the hose is fitted with a heat responsive shrink tube. The shrink tube is heated to mold the uncured hose about the mandrel. Thereafter, the hose is vulcanized, preferably with the tube still in place. Following vulcanization, the shrink tube may be stripped from the hose. Preferably the mandrel is coated with a suitable lubricant for reception of the uncured hose. Also, the end of the uncured hose preferably is covered by a lubricant so as to facilitate removal of the shrink tube following vulcanization.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a flow chart illustrating the method of this invention.

FIG. 2 is a schematic illustration of an uncured hose being placed upon a mandrel.

FIG. 3 is an illustration of an uncured hose in position upon a mandrel.

FIG. 4 is a schematic illustration of a shrink tube in place about an end of an uncured hydraulic hose.

FIG. 5 illustrates an uncured hose having a shrink tube reduced to snugly fit the O.D. of the uncured hose.

FIG. 6 illustrates a cured hose following molding by vulcanization with the shrink tube.

FIG. 7 illustrates an hydraulic hose produced in accordance with this invention.

FIG. 8 illustrates a mandrel for use in this invention having multiple size reductions.

FIG. 9 illustrates an uncured hose mounted upon the mandrel of FIG. 8.

FIG. 10 illustrates a cured hose following simultaneous molding by vulcanization on the mandrel of FIG. 8.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Production of an hydraulic hose in accordance with this invention proceeds as illustrated by the flow chart of FIG. 1 and commences at block 10 with formation of an uncured elastomeric hose of substantially uniform internal diameter. The hose may be of rubber or synthetic rubber and may be produced by a conventional extrusion process. Suitable methods for extruding such an uncured hose are taught in Miller et al, U.S. Pat. No. 3,824,141 and in Derderian et al U.S. Pat. No. 3,972,757. A typically resulting uncured hose may have an internal diameter of about 0.75 inches and an external diameter of about 1.09 inches. Such an uncured hydraulic hose may appear as indicated by reference numeral 30 of FIGS. 2-6.

After the uncured hose 30 has been produced, it is placed upon a mandrel 32, as illustrated in FIG. 2. Mandrel 32 may have an enlarged end 32a, a transition section 32b, and a reduced end 32c. The end 32a should have a diameter substantially equal to the internal diameter of the uncured hose 30, while end 32c may have a substantially smaller diameter. In a typical application where the uncured hose has an internal diameter of 0.75 inches, mandrel 32 may have a diameter of 0.75 inches at the end 32a and a diameter of about 0.61 inches at end 32c.

As illustrated in FIG. 2, uncured hose 30 is placed over the smaller end 32c of mandrel 32 and then worked up over transition section 32b onto the enlarged end 32a. This placement may be facilitated by applying a suitable lubricant to end 32a of mandrel 32. A wide variety of suitable lubricants are commercially available. One lubricant which has been tested and found to be satisfactory is sold commercially under the trademark "UCON." This lubricating step is indicated in FIG. 1 at block 12.

FIG. 3 indicates the position of the mandrel 32 following full insertion into uncured hose 30. It will be noted that uncured hose spans the length of the mandrel between ends 32a, 32c. Placement of uncured hose 30 upon mandrel 32 is indicated by block 14 of FIG. 1.

After the uncured hose has been mounted upon the mandrel, the method proceeds to the step of block 16 wherein a lubricant is placed upon the end of uncured hose 30 proximate reduced end 32c of mandrel 32. This lubricant facilitates removal of a shrink tube as hereinafter described. Again, UCON lubricating liquid or a similar product may be used.

As indicated by block 18 of FIG. 1, the next step in the process involves the mounting of a shrink tube on uncured hose 30. Such a shrink tube is indicated by reference numeral 34 of FIG. 4. The internal diameter of shrink tube 34 should be slightly greater than the external diameter of uncured hose 30, as illustrated in FIG. 4 by the reference numeral 35. In a typical case where the exterior diameter of uncured hose 30 is about 1.09 inches, shrink tube 34 may have an internal diameter of about 1.31 inches. A suitable shrink tube for the purpose is sold commercially by Raychem under the trademark "RNF-3000." This tubing is made from a proprietary radiation cross-linked polyolefin material and has a shrink ratio of 3:1 when heated to 120.degree. C. A satisfactory shrink tube of the above internal diameter has a wall thickness of about 1.15 millimeters.

Heat shrinking of the tube 34 is indicated by block 20 of FIG. 1. Heat application for this purpose may be accomplished by blowing hot air over shrink tube 34. Heating and shrinking proceeds until shrink tube 34 is snugly fitted against uncured hose 30, as illustrated in FIG. 5. After a snug fit has been achieved, uncured hose 30 is vulcanized with shrink tube 34 in place, as indicated by block 22 of FIG. 1. This step cures the hose while concomitantly causing further shrinking of shrink tube 34. Vulcanizing continues until hose 30 has been fully molded about reduced end 32C of mandrel 32 and cured. This is illustrated in FIG. 6.

Vulcanizing (or curing) is carried out in the conventional manner in a vulcanizing oven at a temperature of about 320.degree. F. for about 20 minutes. Thereafter shrink tube 34 may be stripped from hose 30, and hose 30 may be removed from mandrel 32, as indicated by blocks 24 and 26 of FIG. 1. FIG. 7 illustrates the finished product.

It will be appreciated that further processing steps may be performed upon the cured hose 30, either prior to or following removal from mandrel 32. Also, hose 30 may be removed from mandrel 32 with shrink tube 34 in place. These alternatives are indicated by dotted lines on FIG. 1.

The above method has been performed repeatedly with good results in reducing a rubber hose from an internal diameter of 0.75 inches to an internal diameter of 0.61 inches. Good results have also been obtained in achieving other diameter reductions. For a reduction from 0.75 inches to 0.49 inches (internal diameters) two shrink tubes are preferred. The first step involves the application of heat to shrink tube 34 until the shrink tube 34 is snugly fitted against the uncured hose 30 as described above. Then a second shrink tube (not illustrated) is placed over the first shrink tube and heated until a snug fit has been achieved. A vulcanizing step then produces the final desired shrink.

Even greater hose end reductions are possible through use of multiple tubes. Such a multiple reduction may be carried out with the aid of a mandrel 132, as illustrated in FIG. 8. Mandrel 132 may have a full diameter section 134, joined to a plurality of reduced diameter sections 136a, 136b and 136c by a plurality of transition sections 138a, 138b and 138c. In use an uncured hose 130 is placed over mandrel 132 and fitted with a first shrink tube 140 which spans the distance from the smallest end 136c beyond the first reduced diameter section 138a, as illustrated in FIG. 9A. Then hose 130 and shrink tube 140 are heated until shrink tube 140 is snugly fitted against the uncured hose 130. At this point a second shrink tube 150 is applied spanning the length from the smallest end 136c beyond the second reduced diameter section 138b, and a second heating step is performed shrinking the second tube snugly against the first tube. Following this step a third shrink tube 160 is applied, spanning the length from the end 136c beyond the final transition 138c. A third heating step shrinks the third tube snugly against the second tube. Thereafter, the vulcanizing step reduces the uncured hose conforming same to the mandrel. This arrangement has successfully reduced a hose end from an initial inside diameter of 0.75 inch to a final inside diameter of 0.25 inch.

Still other applications of the method of this invention are possible. For example, the mandrel may be provided with a section of elliptical, or slightly flattened crossection. The circumference of this portion of the mandrel may be reduced in the order of about 10 percent from the inside circumference of the uncured hose, thereby facilitating removal of the hose from the mandrel while still warm from vulcanization.

While the method herein described constitutes a preferred embodiment of this invention, it is to be understood that the invention is not limited to this precise method, and that changes may be made without departing from the scope of the invention, which is defined in the appended claims.

Claims

1. An elastomeric hydraulic hose comprising at least three sections of substantially cylindrical crossection, produced by the method of:

(a) extruding an elastomeric hose to produce an uncured hydraulic hose having a substantially uniform inside diameter;

(b) pushing said uncured hydraulic hose over a mandrel, said mandrel having a full diameter section substantially equal to said inside diameter, said full diameter section being followed by a plurality of progressively smaller, reduced diameter sections, each of said reduced diameter sections being preceded by a transition section, said pushing being continued until said uncured hydraulic hose spans all of said transition sections;

(c) successively placing a plurality of progressively shorter heat responsive shrink tubes around said uncured hydraulic hose, said heat responsive shrink tubes each bridging one of said transition sections and extending therefrom to the end of said hose remote from said full diameter section; and

(d) successively heating said heat responsive shrink tubes to mold said hose against said mandrel.

2. A method of producing an hydraulic hose comprising the steps of:

(1) extruding an elastomeric material to produce an uncured hydraulic hose having a substantially uniform inside diameter;

(2) pushing said hydraulic hose over a mandrel, said mandrel having a substantially cylindrical first end of a first predetermined diameter substantially equal to said substantially uniform inside diameter, a substantially cylindrical second end of a second predetermined diameter substantially less than said first predetermined diameter and a transition section therebetween, said pushing being continued until said hydraulic hose spans the length of said mandrel between said first end of said mandrel and said second end of said mandrel;

(3) placing a first heat responsive shrink tube around said hydraulic hose;

(4) applying heat to said first heat responsive shrink tube in sufficient amount to cause said first heat responsive shrink tube to shrink into snug engagement with said hydraulic hose;

(5) placing a second heat responsive shrink tube around said first heat responsive shrink tube;

(6) applying heat to said second heat responsive shrink tube in sufficient amount to cause said second heat responsive shrink tube to shrink into snug engagement with said first heat responsive shrink tube; and

(7) vulcanizing said hydraulic hose with said first and second heat responsive shrink tubes mounted thereon, said vulcanizing causing further shrinking of said first and second heat responsive shrink tubes, thereby molding said hydraulic hose about said mandrel and producing hose ends of substantially different internal diameter.