Patent Application
20060068096
Not Applicable
Not Applicable
Not Applicable
1. Field of the Invention
The invention relates to a method of synthesising carbon nano tubes (CNTs) on a catalyst layer formed on a support member, by catalytic deposition of carbon from a gaseous phase.
2. Background of the Invention
Carbon nano tubes are known for their conductive or semiconductive properties due to the elongated tubulous structure. They are used especially in the field of industrial technology. The plurality of industrial applications of CNTs shows the need for improving the production process to obtain higher specific quality at increased quantities.
A number of methods synthesising vertically aligned CNTs are known from prior art. The majority of synthesis comprise a formation of a catalyst layer on which CNTs are developed. Popular methods obtaining such catalyst layer are sputtering, deposition processes, such as electron beam deposition, thermal deposition and the like. Preferred processes for growing CNT thereon include arc discharge, laser vaporisation, gas phase synthesis, CVD (Chemical vapor deposition) method, which include thermal CVD method, plasma CVD and the like.
Recent ambitions show that CNTs are developed on defined local areas on the catalyst layer to obtain vertically aligned nano tubes, by reasons of which a formation of such local areas has to be performed prior to the development of the carbon nano tubes.
The EP 1 059 266 A1 describes a method of synthesising carbon nano tubes where a catalyst layer comprising the catalytic metal particles is obtained by thermal deposition, sputtering or electron beam deposition. Local isolated catalytic metal particles from the metal catalyst layer are subsequently formed by etching the catalyst layer. Another possibility for obtaining isolated particles is the use of photolithography. Thereby, the catalyst layer is coated with photoresist and subjected to exposure and development processing to form a nanosized photoresist pattern which is used as an etching mask to form the isolated catalytic particles. The size and the density of particles can be controlled by controlling the size and density of the photoresist pattern. Growing the nano tubes is performed by thermal chemical vapor deposition in which a carbon source gas is supplied to a thermal CVD apparatus to form carbon nano tubes.
When electron beam deposition is used for obtaining a catalyst layer the actual deposition does not take place on the support member on which the electrons are impacting. The electron beams are used to evaporate particles from the surface of metal catalyst which are then deposited as catalytically active particles on the support member. The formation of a catalyst layer can not be performed directly on the support member.
Preparing an existing catalyst layer by the use of electron beams, in particular in relation to photolithographical methods, especially the exposure, results in high impact depths on the surface of the catalyst layer. This does not often give a favourable result because the impact of electrons might easily damage the catalyst and additional procedural steps are necessary. This clearly is a significant economic disadvantage when mass production is required.
Etching methods which are preferably used in industrial mass production in the field of nano technology are time consuming processes since a number of procedural steps are needed for the preparation of a catalyst layer. Furthermore, additional substances and/or materials are required in order to perform such preparations. This can easily cause detriments to the catalytic particles and a proper synthesis of a CNT subsequent to the preparation of a catalyst layer is not satisfying. It might even result in hindering the entire process of synthesising CNTs. These factors, in particular the time consuming and cost factor, play an important role in industrial production.
Therefore, it is an object of the present invention to provide an improved method of synthesising carbon nano tubes which limits or avoids the above mentioned problems and simplifies the entire process. A main object of the present invention is to gain the controlled synthesis of CNT by reducing and even omitting procedural, i.e. preparatory steps. Moreover, it is an object of the present invention to obtain a method which provides the control and the influence of the CNT during and/or after the synthesis without additional means or apparatuses.
The object of the invention is achieved by a method of synthesising CNT on a catalyst layer formed on a support member, by catalytic deposition of carbon from a gaseous phase, whereby an ion beam is used prior to, during and/or after formation of said carbon nano tubes for modifying the physical, chemical and/or conductive properties of said carbon nano tubes. Synthesising CNTs by performing this method is advantageous due to its high procedural flexibility. The use of ion beam shows a variety of applications which also comprises the formation of the catalyst layer on a support member, as well as a further preparation thereof. Thus, the subsequent in-situ growth of nano tubes on the catalyst is provided in a highly controlled manner. When forming the catalyst, it is preferable, that ion beam is used with regard to catalytically active particles. This is advantageous, since a deposition may be performed directly on the support member without the need of any additional means. In relation to preparatory purposes of a catalyst layer, irrespective of its formation, the application of ion beam is advantageous since the impact of ions on the surface of the catalyst layer does not cause high impact depths thereon and, thus, no detriments to the surface and/or the catalytical particles thereof. Further, preparing a catalyst layer prior to the development of CNTs by the use of ion beam may comprise forming defined (isolated) local areas of catalytical active particles on said layer or even single catalytical active particles, thus providing control of the subsequent growth of CNTs, in particular in relation to their vertical alignment. Such a control may also be obtained when ion beam is used during the growth of CNTs, thus physical, chemical and/or conductive properties of said CNTs may be modified. After formation of carbon nano tubes the application of ion beam is preferable, because already developed CNTs may be easily altered according to need. Thus, physical, chemical and/or conductive properties of said carbon nano tubes can be enhanced in a very simple and rapid manner.
In the following the term “carbon nano tubes” is understood to refer to variants of carbon nano tubes which encompass nanofibres. Since the mechanism of growth is the same, the variants include variants showing single walls or poly walls or may be of a fishbone type.
When preparing an existing catalyst layer by the use of ion beam, irrespective to its formation, it is advantageous that it has a thickness in the range of 0.1 nm to 500 nm, preferably 0.5 nm to 30 nm.
A preferred feature of the invention is that the ion beam is guided by a diverting member and/or a focussing member. Hence, a control of the beam is provided, first of all ensuring the precise direction of the beam pointing to the support member and secondly defining the exact position of bombardment. For such a proper guidance of the ion beam, it is advantageous that said members are located at various positions apart from the support member. It may well be that the guiding members are able to be inclined or declined during the use of the ion beam. It should be mentioned here that the general position of said diverting member and/or the focusing member is in a certain distance to the support member on which CNTs subsequently are grown.
When controlling the beam it is advantageous that a stencil mask is used. It is preferable that the mask has a defined pattern of structure openings through which the beams are able to pass. The presence of such a mask has the advantage of obtaining the defined pattern on the support member, whether or not the catalyst layer is to be formed or the support member is already coated with a catalyst layer. Thus, desired isolated catalytically active particles or areas may be defined on the surface of said layer where the CNTs are subsequently grown. It is favourable that the stencil mask is situated between the beam source emitting the ion beam and said support member, preferably in a certain distance of both. Further, is most advantageous when such mask is replaceable by another mask having a different pattern of structure openings. It may well be that stencil masks having various patterns of structure openings are provided. Consequently, guiding the ion beam, especially in relation to possible variations of forming patterns of defined areas of catalytically active particles or even single catalytically active particles, can be performed more easily and rapidly by use of a stencil mask.
When a stencil mask is used, it is advantageous that a demagnifying ion optical system with a demagnification factor between 4 and 400, preferably 8 to 100 is used. Preferably, the stencil mask is located within said system, above the support member, thus being able to create an image on the support member or on the catalyst layer. Further, the image can be projected precisely within sub nanometers, which is most advantageous when forming single isolated catalytically active particles. For that purpose, the demagnifying ion optical system may comprise a system known in the art.
It is advantageous that the ion beam comprises a plurality of said beams, the plurality of sub-beams being controlled by a multi-beam ion optical system. An application of said system is preferred in combination with the use of a stencil mask, mentioned above, and the use of already described demagnifying ion optical system. By an application of said features favourable results of defined nanosized catalytic metal particles can be gained. It may comprise a lithographical process.
According to another feature of the invention with regard to a controller an electronically controlled beam source emitting said ion beam is used. For such beam source common electronic controllers may be used. A beam source of such a kind provides a simple way of guiding the ion beam since no additional means or members, such as a diverting member or a focussing member, for instance a stencil mask or the like, are needed in the apparatus, in which the method according to the invention is performed. It may well be that a combination of the above mentioned features of the invention are applied, especially in relation to the multi-beam ion optical system. Hence, a pattern, i.e. an ion image, can be projected on the support member in a simple and exact way.
It is advantageous that the ion beam comprises particles or molecules selected from the group consisting of catalytically active particles, preferably Co, Ni, Fe; gases, preferably He, H, Ar, Xe, Kr, O or doping agents As, P, B, Ag, Au, Pt, Pd, as well as mixtures thereof. Generally, it is well known that catalytic activity for the synthesis of carbon nano tubes is best provided by metals, such as Co, Ni, Fe or mixtures thereof. Due to the different properties of molecules, such as size and density, they may be selected depending on the way of performing the method according to the invention. Additionally, whether the ion beam is used prior to, during and/or after formation of said carbon nano tubes, different molecules and/or gases may be selected. For instance, when depositing catalytically active particles directly on the support member, the selection of molecules and/or gases may be distinct from the choice for developing catalytically active centres on an existing catalyst layer. Most preferably, the ion beam comprises any of the above mentioned elements or mixtures thereof and a gaseous phase of the above mentioned gases is present. Above mentioned features, such as the stencil mask, multi-beam optical system and the like, may well be applied in order to achieve a proper control of the ion beam comprising said elements. When ion beam is used during the formation of CNTs or after their growth, selected elements, such as As, P, B, Xe, Au, Pt, Pd, as well as mixtures thereof are preferably used, irrespective of their way of transport onto the catalytically active particles. Such elements may, preferably, be present in a gaseous phase or any other form, and the use of ion beam induces chemical reactions for their transport. When such elements are present and ion beam is applied, a modification and/or alteration of the properties of an already existing catalyst layer may easily be achieved in order to provide an influence of the subsequent in situ growth of carbon nano tubes and even to their further development. The application of P, for instance, is known in the art, as having a limiting effect of the catalytic activity. It may hinder or even block the catalytical activity in relation to the synthesis of CNTs. Said elements therefore are causing contaminations in/on the catalyst. It is also advantageous that such contaminating elements are used when carbon nano tubes are already developed in order to obtain a modification of said nano tubes, in particular to influence the electrical properties of particular nano tubes. A different example is Pd, which is able to enhance the surface energy of areas on a catalyst layer constituted by the presence of uneven surfaces, such as rims or ridges, thus improving development of carbon nano tubes.
Another preferred feature of the invention is that the catalyst layer comprises a metal catalyst layer. In relation to this it is most preferable that ion beam is used prior to the formation of the CNT. It is desirable that the catalytic activity is then developed out of the metal catalyst by the use of ion beam. Thus, a definition of isolated catalytically active particles may be performed in a rapid manner, irrespective what particular kind of element, mentioned above, is applied. Again, it may well be that for this purpose control guiding means, as already described, are applied.
A further advantageous feature according to the invention is that prior to the formation of said CNTs the catalyst layer is deposited on the support member by ion beam deposition. For that purpose, it is preferable that ion beam or a plurality of sub-beams, comprise catalytic material, such as Co, Ni, Fe or mixtures thereof. Thus, the ion beam is simply used as a transport medium for said particles, in order to be deposited directly on the support member. When the particles reach the surface of the support member, Van der Waals forces are coming into effect resulting in adhasion of said particles on the support member. It is advantageous, for the purpose of ion beam deposition, that a guiding member, such as a stencil mask having a predetermined pattern of structure openings is supplied. Further, it is preferable that demagnifying ion optical system is provided to obtain precise deposition of the metal particles onto the support member. Optionally, the beam comprising the catalytic material may be guided by an electronically controlled beam source. Ion beam deposition according to the invention therefore provides the possibility of direct and precise formation of catalytically active particles on the support member on which the CNTs can then be grown. The formation of catalytically active particles include the formation of isolated catalytically active particles, areas of catalytically active particles, and an entire catalyst layer comprising said particles. The direct deposition on the surface of the support member provides an immediate subsequent growth of the CNTs and additional preparations to obtain said CNTs can be omitted.
It is advantageous that prior to formation of said CNTs the catalyst layer is formed from a gaseous phase comprising catalyst particles, preferably an organometallic gas jet, and deposited on the support member by controlled ion beam induction, and CNTs are then grown on said catalyst layer. Ion beam induction according to the invention may be understood as ion beam, in particular ion beamlets, coming into contact with catalytic particles being present in the gaseous phase thereby inducing the chemical reaction wich results in the decomposition of the gas followed by the deposition of the residuals (the catalytically active particles) on the support member. Hence, the subsequent growth of carbon nano tubes is controlled. This may be obtained by the use metals such as Fe, Co, Ni or mixtures thereof. Likewise, it is desirable that the ion beam comprise gases selected from the group of gases mentioned above, most preferable Ar+. Further, the control may be achieved by the additional use of a focussing member, diverting member, such as a stencil mask, a demagnifying ion optical system and a multi-beam ion optical system, or a controller being an electronically controlled beam source emitting said beam.
According to another feature of the invention it is advantageous that prior to the formation of said CNTs the catalytic activity of the catalyst layer is at least partially enhanced by an ion beam and CNTs are then grown on the active centers of the catalytic layer. The active centers are to be understood of having catalytic active properties for the synthesis of CNTs. They may be in form of local areas of catalytic active particles as well as in form of individual, separate metal particles. Thus, the the CNT immediately grown on said active centers may be controlled, in particular their physical and/or conductive properties. For such a purpose, again already described features according to the invention, such as a stencil mask with a demagnifying ion optical system, a multi-beam ion optical system or in the alternative a controller being an electronically controlled beam source emitting said beam, may be used.
Similarly, prior to the formation of said carbon nano tubes it is advantageous that the catalytic activity of a catalyst layer is at least partially decreased by an ion beam. By the way of this, local active centres of said layer may be defined resulting in an isolation of local areas showing minor catalytical activity. A negative image or pattern of ions enhancing or depleting the catalyst may be created. Thus, CNTs then grown thereon may be controlled, in particular in relation to their vertical aligned growth. As already mentioned above, according to the distribution of structure openings of the stencil mask—when such feature is applied—the pattern or image is projected onto the catalyst layer.
Likewise, an image may be projected on a catalyst with the difference that the bombarded areas are at least partially activated by an ion beam and CNTs are then grown on the active centres of the catalyst layer in a controlled manner. When activating catalytical particles of the catalyst layer by the use of ion beam it is favourable that said layer comprises a metal catalyst layer.
In relation to this it is favourable that the catalyst layer comprises an oxidised metal catalyst, which is at least partially reduced and activated by a beam comprising H+-ions, and carbon nano tubes are then grown on the defined active centres of the catalyst layer. H+-ions being subject of beam bombardment induces reduction of the irradiated areas within the layer thus creating the active centres required to form the nano tubes. Such catalytic oxidised layer may comprise metal oxides of elements, such as Fe, Ni, Co or combinations thereof. When irradiation of ion beams takes place on the layer by applying the features mentioned above, namely the guiding member such as a stencil mask having a specified pattern of the structure openings, the pattern of said guiding member is preferably projected to the layer.
In an alternative feature of the invention the catalyst is coated with catalytically non-active materials, in particular a polymer, which is, prior to the formation of said CNTs, at least partially removed by an ion beam and carbon nano tubes are then grown on said active centres of the catalyst. According to this feature of the invention a bombardment by ions may cause partial activation or complete activation. The local active centres or patterns may again be defined by use of guiding members and the demagnification optical system. Due to different properties of the chemical elements, such as size, mass and energy,—which may be selected—different impacts on the catalyst layer are caused, thus, resulting in different ranges of catalytical activity. Thus, even with a coating of the catalyst layer by a layer comprising non-active materials, such as a polymer layer, the use of ion beams comprising elements of a particular size and energy causes accurant activation of the catalyst. It may well be that, in such a case, the polymer layer is subjected to exposure for the defining a negative image on said layer and postexposure development of nano tubes is performed. Thereby, the remnants of the treated layer are removed in order to be able to perform the synthesis of CNTs. Such a removal may be performed in various ways. It may be that ion beam is used or etching methods, for instance using alcohol or an alcalic medium, are applied. Other, similar methods may be performed which provide a simple and rapid removal of the catalytically non-active layer. Hence, postexposure development of nano tubes may be understood in a development of the negative tone.
Another feature according to the invention is the partial deactivation performed by ion beam. In particular, prior to the formation of carbon nano tubes the catalyst layer is partially deactivated by an ion beam and carbon nano tubes are then grown on the remaining active centres of said catalyst layer. When CNTs are subsequently grown on the remaining centres, their pattern according to which they grow resembles a “negative” image of pattern created by ion beam bombardment in said catalyst layer. That means that ion beam is used for the definition of inactivated areas on said layer. The residuals of the layer are not affected by the ion beam which means that they still show catalytical activity and carbon nano tubes are able to grow thereon. Partial deactivation may be possible depending on the selection of the kind of ion beam, which is the selection of a particular element with its particular characteristics, such as mass, size and energy, as already pointed out above.
In relation to this it is advantageous that the catalyst layer comprises active metal catalyst which is partially oxidised and deactivated by a beam comprising O2+-ions. The application of O2+-ions is performed in a similar way as the application of H+-ions described above. An oxidation, in particular an oxidation of an active metal catalyst layer leads to the effect of an at least partial deactivation of the catalytic activities of the respective areas.
According to the invention the ion beam may be used during the formation of carbon nano tubes whereby the direction of growth of said CNTs is influenced by partial polarisation of the surrounding surface by an ion beam. Due to such polarisation carbon nano tubes may be influenced in such a way that the subsequent growth of the particular carbon nano tubes is changing towards a direction different from the direction of initial growth. This alternative feature according to the invention may be performed when the direction of growth of CNTs is not satisfying and a modification of their growth is desired. In correspondence with other features of the invention, as already pointed out, the beams and subsequently the development of carbon nano tubes may be controlled by the use of a stencil mask with a demagnifying ion optical system or, alternatively, by a direct control of said ion beam, such as the use of an electronically controlled beam source. In addition, a multi-beam ion optical system—when ion beam is comprising a plurality of sub-beams—may be supplied.
In order to exploit semiconductive properties of carbon nano tubes, it is advantageous that said CNTs are doped by an ion beam. Doping particles include ions which are able to influence electric conductivity. Preferably, such elements comprise As, B, Ag, Au, Pt, Pd, P or mixtures thereof. Dotation may be performed by the application of one of the features according to the invention already described, for instance ion beam deposition or ion beam induced deposition. This comprises either a direct transport and implantation of the foreign ion by the ion beam, or altenatively, a gaseous phase comprising said foreign particles which desposition is induced by the beam. When selecting one of these options according to the invention it has to be understood that a control, i.e. guidance of ion beams in order to modify the conductive properties of developed carbon nano tubes may be performed in correspondence to the features according the invention. It may be that a stencil mask and a demagnifying ion optical system is applied. Alternatively, an electronically controlled beam source is used. Desirably, the ion beam comprises sub-beams being controlled by multi-beam ion optical system. Thus, precise positioning, i.e. placement of the foreign ion with regard to depletion or even destruction of a CNT is obtained. Moreover, it is possible that a nano tube transistor is developed by such application of ion beam.
Another preferred feature according to the invention comprises milling of carbon nano tubes by the use of an ion beam. This feature is advantageous when controlling the thickness of the walls of said carbon nano tubes is desired. In relation to this purpose it is preferable that the ion beam is controlled in an exact manner by applying a controller according to the features of the invention, since undesired detriment to adjacent carbon nano tubes which are not to be milled, may be omitted.
It is advantageous that after formation of carbon nano tubes said tubes are decapped by an ion beam for removing the bucky-ends of said carbon nano tubes. This may comprise a removal, i.e. cut-off, of the bucky-end of a particular nano tube and it may also comprise a zapping of a particular nano tube performed by ion beam bombardment of the respective nano tube. In these cases, the ion beamlet is to be applied very precisely, which is, most desirably, be performed by use of a control of the beams according to the features according to the invention.
It is advantageous that the ion beam irradiates from a direction which is substantially not parallel to the respective nano tube. Further, it is preferable that carbon nano tubes are opened by an ion beam in longitudinal direction after the synthesis of said CNTs when further processing of said CNTs is desired. In this regard, it is advantageous that similar conditions to the conditions applied when performing decapping of carbon nano tube according to the invention are applied. Opening of nano tubes may be understood by using the ion beam as cutting means in order to provide separation of carbon nano tubes. In this regard, it has again to be pointed out that a precise guidance, i.e. control, is important in order to achieve the desired results. Further processing of said nano tubes may comprise modifying or altering the physical structure of the respective nano tube including their physical, chemical and/or conductive properties.
Another preferred feature of the invention comprises an elongation of already grown carbon nano tubes. This is performed by fusion of one CNT with another carbon nano tube by the use of ion beam. The ion beam causes a defined point of a nano tube to be made available in order provide a subsequent connection, i.e. fusion, with a further nano tube.
In correspondence to this it is advantageous that the elongation is carried out by heating the catalytically active particles in the fusion area between two carbon nano tubes by an ion beam. Here again, the performance of such fusion may be carried out very precisely, preferably be the use of guiding means and a demagnifying ion optical system with a determined demagnication factor, according to the invention.
In addition, it is advantageous when elongation is carried out by depositing catalytically active particles in the fusion area between two CNTs by an ion beam. The deposition of catalytically active particles will provide the growing together of carbon nano tubes resulting in an elongated nano tube. A deposition of said catalytically active particle may be performed by an alternative feature according to the invention which may include the application of a stencil mask.
A further preferable feature according to the invention is providing an analysis of carbon nano tubes performed by ion beam. It provides the control of the size and direction of growth of CNTs. Generally, it is known that carbon nano tubes are growing in an arbitrary manner. This characteristic shows the need of providing a control of already grown carbon nano tubes. The results given by the analysis of CNTs by the use of ion beam provides the possibility that even subsequent modifications may be carried out according to one of the above mentioned features according to the invention. Such a modification may include a polarisation by an ion beam or a decapping performed by an ion beam, or even zapping by an ion beam, or fusion of nano tubes by an ion beam, or the like.
When analysis of grown carbon nano tubes is carried out it is advantageous that secondary ions which are re- and/or deflected by said nano tubes, are detected. For this purpose it is preferable that analysis is performed with the presence of noble gas. Further, it is favourable that a control means, preferably in form of a stencil mask and a demgnifying ion optical system is applied.
In order to gain a favourable result according to the aspects of the present invention, it is advantageous that ion beams are generally used with an energy from 10 keV to 300 keV, preferably from 40 keV to 100 keV. Depending on the way in which carbon nano tubes are to be synthesised according to the invention corresponding energy ranges are to be applied. It has to be understood that the application of each energy range has to be carried out in correspondence of the kind of ions constituting the ion beam are used.
Similarly, it is advantageous that the methods are performed at a temperature range of 200° C. to 1000° C., preferably 400° C. to 700° C.
In the following the method according to the invention is described in more detail in the enclosed drawings, whereby
a and 1b show the formation of carbon nano tubes, whereby ion beam induces deposition of a metal catalyst;
a and 2b show the formation of carbon nano tubes whereby ion beam is used for direct deposition of the catalyst;
a and 3b illustrate the formation of carbon nano tubes whereby ion beam is used for inducing activation of a catalyst layer;
a and 4b show the formation of carbon nano tubes whereby ion beam is used for inducing inactivation of a catalyst;
a and 5b illustrate the formation of carbon nano tubes whereby ion beam is used for inducing enhancement of a catalyst layer;
a and 6b show the formation of carbon nano tubes whereby ion beam is used for inducing modification of a catalytically non-active layer coating a catalyst;
a and 7b show grown carbon nano tubes whereby ion beam is used for modification;
a and 8b illustrate carbon nano tubes whereby ion beam is used to induce elongation;
a and 9b show carbon nano tubes whereby ion beam is used to induce horizontal growth.
a and 10b is a sectional view of a nano tube transistor whereby ion beam is used to induce doping or destruction thereof.
a and 1b show a first preferred embodiment according to the invention in which prior to the formation of carbon nano tubes a catalyst layer is formed from a gaseous phase comprising catalysts and deposited on the support member by the use of ion beam. In particular, in
The CNTs 4 may generally be synthesised in various manners, preferably by vapor deposition of carbon from a gaseous phase immediately after deposition of the catalytically active particle 3 by the ion beams.
a and 2b illustrate a second preferred embodiment according to the invention in which ion beams 2 are used prior to the synthesis of carbon nano tubes (not shown) and metal ion direct deposition of metal catalysts 3 is carried out. Ion beams 2 comprising metal catalytic material, preferably Co, Ni, and/or Fe-ions, are coming into contact with the surface of the support member 1 and are directly placed thereon. In this case the beam source is emitting said metal ion beams. A preferred guidance of such beams 2 in order to define an exact position of the placement of the particles 3 is preferably conducted by an electronic controller (not shown) controlling such beam source. The subsequent growth of CNTs 4 by the catalytical active particles is shown in
Carrying out metal ion direct deposition of metal catalysts onto the surface of the support member 1 by ion beam may also be performed in relation to already synthesised carbon nano tubes irrespective of the stage of synthesis.
In
Particularly,
b shows vapor grown isolated carbon nano tubes at the correspondent positions where the beams 3 induced reduction, i.e. activation, of the catalyst layer 5. As mentioned in the first and second preferred embodiment according to the invention, the beams are preferably controlled in order to define an exact position on the support member. For this purpose a controller may be selected either a mask and a demagnifying ion optical system may be applied or the use of an electronically controlled beam source emitting the beams. The ion beam also may comprise a plurality of sub-beams in which case the controller comprises a multi-beam ion optical system. Applying such conditions, desired final patterns of vertically aligned nano tubes may be obtained by ion beam induction.
a and 4b illustrate the use of ion beam for modifying a catalyst layer 5 in such a way that a negative image is obtained on which carbon nano tubes 4 are then grown. The present embodiment according to the invention relates to a partial inactivation of an existing catalyst layer by ion beams. In particular, the catalytic activity of the catalyst layer 5 is at least partially decreased by an ion beam 2 and carbon nano tubes 4 are then grown on the remaining catalytically active centres 3 of the catalyst layer 5.
In order to provide precise placement of the ion beamlet, conditions relating to a control, i.e. guidance, of the beams already mentioned with regard to the previous embodiments may be applied. This also comprise the application of defined energy and temperature ranges in accordance of the kind of ions used. Applying various conditions may provide different results of the modification of the catalytical activity and the subsequent growth of CNT; either a desired inactivation of bombarded zones of the catalyst or, if desired, even a destruction (see embodiment in
In
The definition of the affected areas 3 on the catalyst layer 5 in
Performing the method according to the present preferred embodiment means, in correspondence to the embodiments illustrated in FIGS. 1 to 4, the arbitrary growth of nano tubes may be avoided by the use of ion beam induction and controlled substantially vertically aligned carbon nano tubes can be synthesised.
A further preferred embodiment according to the present invention is illustrated in
The embodiment described in
Zapping of nano tubes may well be possible in the longitudinal direction of a nano tube which might also be desired for further processing. An Ar+-ion beam is applicable to induce zapping which leads to the division of the CNT. Thus, the two halves of the nano tube may be subjected to doping by a different ion beam for the purpose of inducing semi-conductive properties of the affected CNT. For instance phosphor is directly implanted by the ion beam, in which case an electronically controlled beam source emitting ion beams including P is a simple way of control and said ion may be positioned exactly, e.g. on the end of the zapped nano tube. Similar, direct deposition of such a contaminating foreign ions may be performed in relation to decapped nano tubes.
Another preferred embodiment according to the invention is explained in more detail in
a and 10b provide a preferred embodiment according to the invention which shows another application of the method using ion beams. Here, a transistor is realised by a carbon nano tube whereby ion beam induction is applied in order to perform doping of defined areas of said carbon nano tube. For this purpose any CNTs may be supplied as well as nano tubes which are grown in accordance to one of the embodiments described above. A carbon nano tube transistor is shown in sectional view. In particular, in
The ion beam 2 is guided, preferably by the use of a stencil mask (not shown) whereby a demagnifying ion optical system (not shown) with a demagnification factor between 4 to 400 is applied. Alternatively, an electronically controlled beam source may be used.
In