BRIEF DESCRIPTION OF THE DRAWINGS
Many aspects of the present method can be better understood with reference to the following drawings. The components in the drawings are not necessarily to scale, the emphasis instead being placed upon clearly illustrating the principles of the present method. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.
FIG. 1 is flow views showing successive stages in a method of synthesizing single-wall carbon nanotubes (SWNTs).
FIG. 2 is a Raman scattering spectrum of SWNTs synthesized by the present method.
FIG. 3 is a scanning electron microscope (SEM) photo of SWNTs synthesized by the present method.
FIG. 4 is a transmission electron microscope (TEM) photo of the SWNTs in FIG. 3.
The exemplifications set out herein illustrate at least one preferred embodiment of the present method, in one form, and such exemplifications are not to be construed as limiting the scope of such a method in any manner.
DETAILED DESCRIPTION
Reference will now be made to the drawings to describe the synthesis of single-wall carbon nanotubes (SWNTs) at a relatively low temperature according to the present method in detail.
Referring to FIG. 1, a method of synthesizing single-wall carbon nanotubes (SWNTs) is provided. The method includes the steps of:
- (i) providing a substrate 10 having an upper portion 110 and a lower portion 120, the upper portion 110 comprised of indium tin oxide and having a thickness in the range of about 5 nanometers to about 100 nanometers, the lower portion 120 advantageously comprised of one of silicon and silicon oxide, e.g., quartz or glass;
- (ii) forming an aluminum layer 30 on the upper portion 110 of the substrate 10 by, e.g., an evaporating method or a sputtering method, the aluminum layer 30 having a thickness in the range from about 5 nanometers to about 10 nanometers, advantageously, the thickness of the aluminum layer 30 being about 40 nanometers;
- (iii) depositing a catalyst layer 40 with a suited thickness on the aluminum layer 30 to form a treated substrate, the catalyst layer 40 comprised of a material selected from a group consisting of iron (Fe), cobalt (Co), nickel (Ni) and an alloy including by at least two such metals, the thickness of the catalyst layer 40 corresponding to the selective materials of the catalyst layer 40, e.g., the thickness of an Fe catalyst layer 40 being advantageously in the range from about 3 nanometers to about 10 nanometers and being preferably 5 nanometers;
- (iv) annealing the treated substrate 10 at a temperature of about 300° C. to about 500° C. for a sufficient period of time (e.g., about 10 minutes to about 12 hours), in order to oxidize the catalyst layer 40 to form oxidized catalyst particles; and
- (v) positioning the substrate 10 in a reactive device (not shown in the drawings), that is suited to performing a chemical vapor deposition (CVD) method, heating the substrate 10 up to a predetermined temperature in a flow of a protective gas, introducing a mixing gas of the protective gas and a carbon source gas, and heating at a sufficient temperature (e.g., about 630° C. to about 900° C.) for a period of time from about 30 minutes to about 60 minutes, thereby resulting in SWNTs being formed.
In step (i), the upper portion 110 of the substrate 10 could be an ITO electrode using, e.g., a photolithography method, a method combining an electron beam photolithography technology with a reactive ion etching technology, a dry-etching method or a wet-etching method.
The photolithography method of forming the ITO electrode generally includes the steps of:
- moving the substrate 10 into a vacuum chamber, sputtering a piezoelectric layer in a flow of a sputtering gas of a combination of argon (Ar) and oxygen (O2) by, e.g., a reactive direct current (DC) sputtering method or a reactive radio frequency (RF) sputtering method, a sputtering material selected from a group consisting of ZnOx, LiNbOx, LiTiOx, and LiTaOx, a thickness of the piezoelectricity layer being in the range from about 0.02 micrometers to about 5 micrometers;
- forming a photo-resist layer on a surface of the piezoelectric layer by, for example, a spin-coating method;
- placing a photomask on the photo-resist layer, the photomask having a given pattern corresponding to the ITO electrode;
- irradiating the photomask by a laser or an ultraviolet to result in an exposal portion of the photo-resist layer;
- removing the photomask, developing the photo-resist and removing the exposal portion of the photo-resist layer thereby exposing a portion of the piezoelectric layer;
- forming an ITO layer on the treated surface of the substrate 10, the ITO layer having a thickness in the range from about 5 nanometers to about 100 nanometers; and
- removing a remaining portion of the photo-resist with a portion of the ITO layer formed thereon and, the remaining ITO layer forming the ITO electrode.
The web-etching method of forming the ITO electrode generally includes the steps of:
- providing an ITO layer on the substrate 10 by, e.g., an evaporating method or a sputtering method, the ITO layer having a thickness in the range from about 5 nanometers to about 100 nanometers;
- forming an etching protective layer (e.g., a photo resist layer) on a surface of the ITO layer;
- developing and removing a selective portion of the photo-resist, in order to selectively expose a portion of the ITO layer;
- providing an electrolyte etchant including a non-reactant, that is selected from one of a neutral salt, an acid and a base and does not react with the ITO layer via an etching reaction, and an oxide reactant, that reacts with the ITO layer via an etching reaction, the etchant etching and removing the exposal portion of the ITO layer via an electrochemical or chemical reaction; and
- removing a remaining etching protective layer using a solvent (e.g., acetone), and a remaining portion of the ITO layer forming the ITO electrode.
In step (vi), a function of the process of heating the substrate 10 up to the predetermined temperature in the flow of the protective gas is to protect the oxidized catalyst particles from a further oxidization during the synthesis of the SWNTs, thereby ensuring a desired condition for synthesizing the SWNTs. The predetermined temperature is different in accordance with different kinds of the catalyst. Generally, the predetermined temperature is in the range from about 400° C. to about 750° C. If iron is selected to be the catalyst, the predetermined temperature is advantageously about 650° C. The protective gas is selected from one of nitrogen (N2) and inert gases, and, preferably, the protective gas is Ar. After the process of the heating the substrate 10 up to the predetermined temperature in the flow of the protective gas, hydrogen or an ammonia gas could be introduced to deoxidize the oxidized catalyst particles thereby obtaining nano-scaled catalyst particles. The carbon source gas in the mixing gas can be a hydrocarbon, such as acetylene or ethylene, preferably, the carbon source gas is acetylene. The protective gas in the mixing gas is advantageously Ar.
Referring to FIG. 2, a Raman scattering spectrum of SWNTs synthesized by a method in accordance with the present method is shown. A series of wave crests between 175 1/cm and 300 1/cm shows breathing mode characteristics of the SWNTs. The detailed method synthesizing the SWNTs having the characteristics in FIG. 2 includes the steps:
- providing a substrate with a ITO upper portion and a glass lower portion;
- sputtering an aluminum layer with a thickness of about 40 nanometers on the upper portion of the substrate;
- sputtering an Fe catalyst layer with a thickness of about 5 nanometers on the aluminum layer to form a treated susbtrate;
- annealing the treated substrate at a temperature of about 300° C. for a time period of about 10 minutes in air, in order to form ferric oxide particles;
- placing the substrate into a quartz carrier, removing the quartz carrier with the substrate into a reactive room of a tube quartz stove, introducing Ar and heating them to a temperature of about 640° C.;
- introducing hydrogen to deoxidize the ferric oxide particles into nano-scaled Fe particles;
- applying a mixing gas of Ar and acetylene, heating up to a temperature of about 640° C. for a time period of about 40 minutes, thereby obtaining the SWNTs.
Referring to FIGS. 3 and 4, FIG. 3 is a scanning electron microscope (SEM) photo of SWNTs synthesized by a method in accordance with the present method, and FIG. 4 is a transmission electron microscope (TEM) photo of the SWNTs in FIG. 3. The detailed method of synthesizing the SWNTs shown in FIGS. 3 and 4 includes the steps of:
- providing a silicon base;
- evaporating an ITO layer with a thickness of about 100 nanometers on a top surface of the silicon base, the silicon base and the ITO layer forming a substrate;
- sputtering an aluminum layer with a thickness of about 40 nanometers on the ITO layer;
- sputtering an Fe catalyst layer with a thickness of about 5 nanometers onto the aluminum layer to form a treated substrate;
- annealing the treated substrate at a temperature of about 300° C. for a time period of about 10 minutes, to form ferric oxide particles;
- placing the substrate with the ferric oxide particles into a quartz carrier, removing the quartz carrier into a reactive room of a tube quartz stove;
- heating the substrate up to a temperature of about 740° C. in a flow of Ar; and
- introducing a mixing gas of Ar and acetylene, and heating up to a temperature of about 740° C. for a time period of about 40 minutes, thereby obtaining the SWNTs.
In a method of synthesizing carbon nanotubes, that has similar conditions to the present method except for the ITO portion and the aluminum layer of present invention, only multi-wall carbon nanotubes (MWNTs) are found but SWNTs are not found.
Finally, it is to be understood that the above-described embodiments are intended to illustrate rather than limit the invention. Variations may be made to the embodiments without departing from the spirit of the invention as claimed. The above-described embodiments illustrate the scope of the invention but do not restrict the scope of the invention.