The present disclosure generally relates to milling, and more particularly, to techniques for a continuous ball milling machine that produces powders for metal additive manufacturing.
Additive manufacturing (AM) refers to various processes for fabrication of solid three-dimensional (3-D) objects. Thus, AM includes 3-D printing techniques. Many AM processes fabricate objects from metallic powders. For use in many AM processes, however, metallic powders may be expected to be within a very small and specific size range. In addition, many AM processes may be adapted to use metallic powders of specific shapes, such as substantially spherical metallic powders. Such characteristics may be difficult to achieve.
Some approaches to creating metallic powders involve gas atomization, in which a gas is used to atomize a liquid stream of metal. However, gas atomization may be inefficient and/or otherwise undesirable due to cost and/or energy expenditures. For example, as gas atomization uses a liquid stream of metal, metal that has already been smelted must be melted again in order to produce metallic powder. In addition, gas itself has a poor transfer of momentum to a liquid stream of metal, which may cause potential energy in the gas to be inefficiently converted to velocity rather than transferred into the liquid stream of metal. Further, the energy present in the gas temperature and velocity are generally unrecoverable.
Consequently, gas atomization may be an unsatisfactory approach to creating metallic powders.
A need exists for approaches to efficiently producing metallic powders that are suitable for use in some, many, or all powder-based metal additive manufacturing (AM) processes (e.g., Direct Metal Deposition (DMD), Powder Bed Fusion (PBF)). The following presents a simplified summary of one or more aspects in order to provide a basic understanding of such aspects. This summary is not an extensive overview of all contemplated aspects, and is intended to neither identify key or critical elements of all aspects nor delineate the scope of any or all aspects. Its sole purpose is to present some concepts of one or more aspects in a simplified form as a prelude to the more detailed description that is presented later.
AM processes involve the use of a stored geometrical model for accumulating layered materials on a “build plate” to produce three-dimensional (3-D) objects having features defined by the model. AM techniques are capable of printing complex components using a wide variety of materials. A 3-D object is fabricated based on a computer aided design (CAD) model. The AM process can create a solid three-dimensional object using the CAD model.
One such method is called Direct Metal Deposition (DMD). DMD is an AM technology that uses a laser to melt metallic powder and thereby transform it into a solid metal object. Unlike many of the other AM technologies, DMD is not based on a powder bed. Instead, DMD uses a feed nozzle to propel the powder into the laser beam. The powdered metal is then fused by the laser. While supports or a freeform substrate may in some cases be used to maintain the structure being built, almost all the powder in DMD is transformed into solid metal and consequently little waste powder is left to recycle. Using a layer by layer strategy, the print head, composed of the laser beam and the feed nozzle, can scan the substrate to deposit successive layers. All kinds of metallic materials can be processed using this technology including, for example, steel, aluminum, nickel alloys, titanium, cobalt, copper, and the like.
Other AM processes, such as powder bed fusion (PBF), may use a laser to sinter or melt metallic powder deposited in a powder bed, which then bonds the powder particles together in targeted areas to produce a 3-D structure having the desired geometry. For example, selective laser sintering (SLS) uses a laser to sinter metallic powder as the surface of a powder bed is scanned across. The laser is directed at specific points defined by a CAD model, and the metallic powder is bound together at the specific points to create a sold structure. Similar to SLS, selective laser melting (SLM) uses a high power-density laser to melt and fuse metallic powder. In SLM, however, the metallic powder may be fully melted into a solid 3-D part.
The metallic powders used in various AM processes, such as SLS and/or SLM, may be necessarily within a well-defined size distribution—e.g., 10 micrometers (μm) to 100 μm. In addition, such AM processes may use metallic powders with a specific shape—e.g., substantially spherical metal powder. Controlling metallic powders for relative consistency (e.g., including size and shape characteristics) may provide for reproducibility and/or quality assurance in AM processes.
The present disclosure describes various techniques and solutions to creating metallic powder suitable for AM processes through a ball milling machine, which may be continuous and may include multiple different media. According to the techniques and solutions described herein, ball milling utilizes solid media (e.g., “balls”) to refine particle sizes to achieve near-spherical powder, e.g., in a manner that is appreciably more efficient in terms of cost and efficiency than gas atomization, given that melting is avoided. Further, ball milling techniques and solutions of the present disclosure may occur at temperatures that reduce (or preclude) dangerous conditions, such as those present during gas atomization. The metallic powders may be of aluminum or aluminum alloys, although other types of metals and alloys may also be powdered for use in AM processes.
In addition, ball milling techniques and solutions of the present disclosure may provide the possibility to re-alloy materials on an ongoing basis. Advantageously, metallic powder can be recycled in ball milling. For example, rejected and/or missed metallic powders and metals (e.g., from cleaned or sorting parts of various geometries) can be directly fed back into the input of the ball milling machine, including metal support material, over/undersized powder rejected in quality assurance/quality control processes, failed part builds, machining chips, powder from cleaning and/or de-powdering operations, and/or other sources of metals.
According to some embodiments of the present disclosure, methods and apparatuses for efficiently creating metallic powder that is sufficiently spherical for use in some AM processes are described using continuous ball milling machines. Such continuous ball milling machines of the present disclosure may include an inlet or other entrance point in which metallic pellets or other shaped metal can be fed. Further, continuous ball milling machines described herein may include a dispenser or other exit point at which metallic powder within a defined size distribution and defined morphology is collected, e.g., with or without additional operations preparing the metallic powder for use in some AM processes.
In some embodiments of the present disclosure, an apparatus for producing a metallic powder through grinding is described. The apparatus comprises a comminution component including an inlet to receive a metallic material at a first region within the comminution component and an outlet to dispense the metallic powder from a second region within the comminution component. The apparatus further comprises a plurality of grinding components to grind the metallic material, the plurality of grinding components being arranged within the comminution component. In addition, the apparatus comprises a drive component, connected with the comminution component, to induce movement of the metallic material and the plurality of grinding components within the comminution component such that the metallic material is fragmented through contact with the plurality of grinding components at the first region within the comminution component and an external surface of the fragmented metallic material is altered at the second region within the comminution component to produce the metallic powder.
In one embodiment, the plurality of grinding components comprises a set of first grinding components and a set of second grinding components, and each first grinding component has at least a greater weight or a larger dimension than each second grinding component. In another embodiment, the first grinding components are comprised of a different material than the second grinding components. In still another embodiment, the set of first grinding components is spatially separated from the set of second grinding components within the comminution component. In a further embodiment, an interior of the comminution component is configured with one of a conical shape or geometric walls to spatially separate the first set of grinding components from the second set of grinding components.
In one embodiment, the comminution component is configured such that a first temperature at the first region is different by at least 20 degrees Celsius (° C.) than a second temperature at the second region. In a further embodiment, the first temperature is less than or equal to −100° C., and the second temperature is greater than or equal to 100° C. In another embodiment, the drive component comprises at least one shaft defining an axis of rotation of the comminution component. In yet a further embodiment, an aspect ratio of the at least one shaft is different at the first region than at the second region.
In one embodiment, the comminution component is configured to receive at least one additive at the first region or the second region. In a further embodiment, the at least one additive is configured to prevent welding of the metallic powder, prevent coagulation of the metallic powder, lubricate the metallic powder, modulate impact frequency of the metallic powder, increase energy transfer of the metallic powder, or prevent chemical hardening of the metallic powder. In still another embodiment, each grinding component comprises a ball having a diameter inclusively between 1 millimeter (mm) and 40 mm.
In one embodiment, the apparatus further comprises one or more filters or sieves between the first region and the second region, the one or more filters or sieves being configured to allow the fragmented metallic material to pass from one of the first region or the second region toward another of the first region or the second region and being further configured to prevent at least one grinding component from passing from one of the first region or the second region toward another of the first region or the second region.
In one embodiment, the apparatus further comprises a set of arms arranged within the comminution component and configured to affect at least force or frequency of contact between at least a portion of the plurality of grinding components and the fragmented metallic material. In a further embodiment, each arm is connected with at least the drive component or interior surface of the comminution component, and each arm is configured to rotate to affect the at least the force or the frequency of the contact between the at least the portion of the plurality of grinding components and the fragmented metallic material.
In some other embodiments of the present disclosure, a ball mill is described. The ball mill comprises a first mill section containing first grinding media configured to strike metallic chips to obtain metallic granules. The ball mill further comprises a second mill section containing second grinding media configured to configured strike the metallic granules to obtain metallic powder, the second grinding media being configured to strike the metallic granules with a greater frequency and lesser force than the first grinding media strikes the metallic chips. In addition, the ball mill comprises a dispensation section configured to dispense the metallic powder configured for use in additive manufacturing.
In one embodiment, the metallic powder is spherical with diameters inclusively between 10 μm and 100 μm. In another embodiment, each first and second grinding medium is spherical, and each first grinding medium has a diameter of at least 30 mm and each second grinding medium has a diameter of at most 5 mm. In still another embodiment, at least the first or second mill sections further contains at least one surfactant, lubricant, or abrasive.
In one embodiment, the ball mill further comprises at least one drive shaft configured to cause at least the first or second grinding media to strike the metallic chips or the metallic granules, respectively. In another embodiment, the ball mill further comprises a set of arms extending from the at least one drive shaft, the set of arms being configured to facilitate at least the first or second grinding media striking the metallic chips or the metallic granules, respectively. In a further embodiment, at least one of the set of arms is blade-shaped or triangular. In an additional embodiment, the at least one drive shaft comprises at least two drive shafts, each drive shaft being connected with a set of arms. In still another embodiment, the at least two drive shafts are configured to rotate at different speeds, and the sets of arms are different in at least size, shape, aspect ratio, or surface texture.
In still further embodiments of the present disclosure, a method of ball milling is described. The method of ball milling comprises receiving a metallic material at a first region of a comminution component. The method further comprises causing the metallic material to fragment through contact with a plurality of first grinding components at a first impact force and a first impact frequency. The method further comprises altering surface characteristics of the fragmented metallic material to obtain metallic powder through contact of the fragmented metallic material with a plurality of second grinding components at a second impact force lower than the first impact force and a second impact frequency higher than the first impact frequency. In addition, the method comprises outputting the metallic powder, the metallic powder being spherical with a diameter inclusively between 10 μm and 100 μm.
In one embodiment, the method further comprises driving rotation of a first set of arms, the metallic material being fragmented based on the rotation of the first set of arms; and driving rotation of a second set of arms, the surface characteristics of the fragmented metallic power being altered to obtain the metallic power based on the rotation of the second set of arms. In another embodiment, a speed of the rotation of the first set of arms is different from a speed of the rotation of the second set of arms, and the first set of arms is one of a different size or a different shape than the second set of arms.
In one embodiment, the method further comprises filtering the fragmented metallic material into position for the surface characteristics to be altered; and maintaining separation of the plurality of first grinding components and the plurality of second grinding components.
In one embodiment, the method further comprises providing at least one additive for one of the contact of the metallic material with the plurality of first grinding components or the contact of the fragmented metallic material with the plurality of second grinding components. In another embodiment, the at least one additive is configured to prevent welding of the metallic powder, prevent coagulation of the metallic powder, lubricate the metallic powder, modulate impact frequency of the metallic powder, increase energy transfer of the metallic powder, or prevent chemical hardening of the metallic powder.
To the accomplishment of the foregoing and related ends, the one or more aspects comprise the features hereinafter fully described and particularly pointed out in the claims. The following description and the annexed drawings set forth in detail certain illustrative features of the one or more aspects. These features are indicative, however, of but a few of the various ways in which the principles of various aspects may be employed, and this description is intended to include all such aspects and their equivalents.
The detailed description set forth below in connection with the appended drawings is intended to provide a description of various exemplary embodiments and is not intended to represent the only embodiments within the scope of the present disclosure. The term “exemplary” used throughout this disclosure means “serving as an example, instance, or illustration,” and should not necessarily be construed as preferred or advantageous over other embodiments presented in this disclosure. The detailed description includes specific details for the purpose of providing a thorough and complete disclosure that fully conveys the scope of that which is claimed herein to those skilled in the art. However, some embodiments of that which is claimed herein may be practiced without these specific details. In some instances, well-known structures and components may be shown in block diagram form, or omitted entirely, in order to avoid obscuring the various concepts presented throughout this disclosure. In addition, the figures may not be drawn to scale and instead may be drawn in a way that attempts to most effectively highlight various features relevant to the subject matter described.
This disclosure is generally directed to creating spherical metallic powders using ball milling machines. According to the present disclosure, a ball mill machine may be “continuous” in that metallic material (e.g., metallic parts or “chips”) are input into the ball milling machine and the metallic material is continuously grinded at different regions of the ball milling machine until spherical metallic powder within a defined size range is output from the ball milling machine. Specifically, the different regions of the ball milling machine includes at least a first region including a first grinding media (e.g., “balls”) and a second region including a second grinding media (e.g., relatively smaller balls).
In the first region, the metallic material is fragmented using the first grinding media, which is configured to strike the metallic material with a first impact force and a first impact frequency. In the second region, surface characteristics of the metallic material is altered (e.g., to be substantially spherical) using the second grinding media, which is configured to strike the metallic material with a second impact force lower than the first impact force and a second impact frequency greater than the first impact frequency.
Other regions in addition to the aforementioned first and second regions may be included in ball milling machines without departing from the scope of the present disclosure. Such other regions may be configured to fragment and/or alter surface characteristics of metallic material to create spherical metallic powders. For example, a third region may be positioned between the first and second regions, and the third region may include third grinding media of a size smaller than the first grinding media but larger than the second grinding media.
Manufacturers and various other entities stand to benefit from the ball milling techniques and solutions for creating spherical metallic powders described in this disclosure. Specifically, manufacturers and other entities involved in additive manufacturing (AM) and three-dimensional (3-D) printing. For example, metallic powders created using the techniques and solutions provided for in the present disclosure may be applicable in selective laser melting (SLM), selective laser sintering (SLS), and other powder-bed fusion (PBF)-based AM methods and practices. In some other examples, metallic powders created using the techniques and solutions provided for in the present disclosure may be applicable in Direct Metal Deposition (DMD) AM and/or other AM methods and practices.
In particular, the ball milling techniques and solutions described herein can create metallic powders suitable for AM and 3-D printing of virtually any mechanized form of transport, which often rely heavily on complex and labor intensive machine tools and molding techniques, and whose products often require the development of complex panels, nodes, structures, extrusions, and/or interconnects to be integrated with intricate machinery such as combustion engines, transmissions and increasingly sophisticated electronics. Examples of such transport structures include, among others, trucks, trains, tractors, boats, aircraft, motorcycles, busses, and the like.
Additive Manufacturing (3-D Printing).
AM is advantageously a non-design specific manufacturing technique. AM provides the ability to create complex structures within a part. For example, nodes can be produced using AM. A node is a structural member that may include one or more interfaces used to connect to other spanning components such as tubes, extrusions, panels, other nodes, and the like. Using AM, a node may be constructed to include additional features and functions, depending on the objectives. For example, a node may be printed with one or more ports that enable the node to secure two parts by injecting an adhesive rather than welding multiple parts together, as is traditionally done in manufacturing complex products. Alternatively, some components may be connected using a brazing slurry, a thermoplastic, a thermoset, or another connection feature, any of which can be used interchangeably in place of an adhesive. Thus, while welding techniques may be suitable with respect to certain embodiments, additive manufacturing provides significant flexibility in enabling the use of alternative or additional connection techniques.
A variety of different AM techniques have been used to 3-D print components composed of various types of materials. Numerous available techniques exist, and more are being developed. For example, Directed Energy Deposition (DED) AM systems use directed energy sourced from laser or electron beams to melt metal. These systems utilize both powder and wire feeds. The wire feed systems advantageously have higher deposition rates than other prominent AM techniques. Single Pass Jetting (SPJ) combines two powder spreaders and a single print unit to spread metal powder and to print a structure in a single pass with apparently no wasted motion. As another illustration, electron beam additive manufacturing processes use an electron beam to deposit metal via wire feedstock or sintering on a powder bed in a vacuum chamber. Single Pass Jetting is another exemplary technology claimed by its developers to be much quicker than conventional laser-based systems. Atomic Diffusion Additive Manufacturing (ADAM) is still another recently developed technology in which components are printed, layer-by-layer, using a metal powder in a plastic binder. After printing, plastic binders are removed and the entire part is sintered at once into a desired metal.
One of several such AM techniques, as noted, is DMD.
The powdered metal is then fused by the laser 106 in a melt pool region 108, which may then bond to the workpiece 112 as a region of deposited material 110. The dilution area 114 may include a region of the workpiece where the deposited powder is integrated with the local material of the workpiece. The feed nozzle 102 may be supported by a computer numerical controlled (CNC) robot or a gantry, or other computer-controlled mechanism. The feed nozzle 102 may be moved under computer control multiple times along a predetermined direction of the substrate until an initial layer of the deposited material 110 is formed over a desired area of the workpiece 112. The feed nozzle 102 can then scan the region immediately above the prior layer to deposit successive layers until the desired structure is formed. In general, the feed nozzle 102 may be configured to move with respect to all three axes, and in some instances to rotate on its own axis by a predetermined amount.
3-D modeling software, in turn, may include one of numerous commercially available 3-D modeling software applications. Data models may be rendered using a suitable computer-aided design (CAD) package, for example in an STL format. STL is one example of a file format associated with commercially available stereolithography-based CAD software. A CAD program may be used to create the data model of the 3-D object as an STL file. Thereupon, the STL file may undergo a process whereby errors in the file are identified and resolved.
Following error resolution, the data model can be “sliced” by a software application known as a slicer to thereby produce a set of instructions for 3-D printing the object, with the instructions being compatible and associated with the particular 3-D printing technology to be utilized (operation 220). Numerous slicer programs are commercially available. Generally, the slicer program converts the data model into a series of individual layers representing thin slices (e.g., 100 microns thick) of the object be printed, along with a file containing the printer-specific instructions for 3-D printing these successive individual layers to produce an actual 3-D printed representation of the data model.
The layers associated with 3-D printers and related print instructions need not be planar or identical in thickness. For example, in some embodiments depending on factors like the technical sophistication of the 3-D printing equipment and the specific manufacturing objectives, etc., the layers in a 3-D printed structure may be non-planar and/or may vary in one or more instances with respect to their individual thicknesses.
A common type of file used for slicing data models into layers is a G-code file, which is a numerical control programming language that includes instructions for 3-D printing the object. The G-code file, or other file constituting the instructions, is uploaded to the 3-D printer (operation 230). Because the file containing these instructions is typically configured to be operable with a specific 3-D printing process, it will be appreciated that many formats of the instruction file are possible depending on the 3-D printing technology used.
In addition to the printing instructions that dictate what and how an object is to be rendered, the appropriate physical materials necessary for use by the 3-D printer in rendering the object are loaded into the 3-D printer using any of several conventional and often printer-specific methods (operation 240). In DMD techniques, for example, one or more metal powders may be selected for layering structures with such metals or metal alloys. In SLM, SLS, and other PBF-based AM methods (see below), the materials may be loaded as powders into chambers that feed the powders to a build platform. Depending on the 3-D printer, other techniques for loading printing materials may be used.
The respective data slices of the 3-D object are then printed based on the provided instructions using the material(s) (operation 250). In 3-D printers that use laser sintering, a laser scans a powder bed and melts the powder together where structure is desired, and avoids scanning areas where the sliced data indicates that nothing is to be printed. This process may be repeated thousands of times until the desired structure is formed, after which the printed part is removed from a fabricator. In fused deposition modelling, as described above, parts are printed by applying successive layers of model and support materials to a substrate. In general, any suitable 3-D printing technology may be employed for purposes of this disclosure.
Another AM technique includes PBF. Like DMD, PBF creates “build pieces” layer-by-layer. Each layer or “slice” is formed by depositing a layer of powder and exposing portions of the powder to an energy beam. The energy beam is applied to melt areas of the powder layer that coincide with the cross-section of the build piece in the layer. The melted powder cools and fuses to form a slice of the build piece. The process can be repeated to form the next slice of the build piece, and so on. Each layer is deposited on top of the previous layer. The resulting structure is a build piece assembled slice-by-slice from the ground up.
Referring specifically to
In various embodiments, the deflector 305 can include one or more gimbals and actuators that can rotate and/or translate the energy beam source to position the energy beam. In various embodiments, energy beam source 303 and/or deflector 305 can modulate the energy beam, e.g., turn the energy beam on and off as the deflector scans so that the energy beam is applied only in the appropriate areas of the powder layer. For example, in various embodiments, the energy beam can be modulated by a digital signal processor (DSP).
Referring now to
Furthermore, the various techniques and solutions for creating metallic powders using ball milling apparatuses and methods described in the present disclosure are advantageous over other approaches to creating metallic powders, such as gas atomization. For example, creating metallic powders using ball milling as described herein is more efficient than gas atomization because the embodiments described herein avoid melting metallic materials to create metallic powders, which simultaneously confers safety advantages to the ball milling described herein through the lower temperatures than those commensurate with gas atomization.
In addition, ball milling techniques and solutions of the present disclosure are more efficient than other approaches to creating metallic powders as less metallic material is irrevocably wasted during creation. Specifically, metallic materials may be re-alloyed using the ball milling apparatuses and methods described herein. For example, metallic powder that does not fall within the controlled distribution parameters and/or metallic powder recovered from cleaning/de-powdering operations may be reintroduced into a ball mill to be further fragmented or altered until satisfying the controlled distribution parameters.
Ball mill 400 may be configured to receive some metallic material 420 at inlet 406. Metallic material 420 may be substantially composed of any metal suitable to be powdered and used in one or more of the AM or 3-D processes described herein, such as SLS, SLM, or other PBF-based process.
For example, metallic material 420 may be aluminum or an aluminum alloy, such as an aluminum alloy having less than twenty (20) percent (%) by weight of one or more of magnesium (Mg), manganese (Mn), silicon (Si), iron (Fe), titanium (Ti), zirconium (Zr), chromium (Cr), yttrium (Y), and/or copper (Cu) with a balance of aluminum. Potentially, however, metallic material 420 may be other metals or metal alloys, with or without aluminum. In some embodiments, metallic material 420 may be uniform throughout; although metallic material 420 may contain a mix of two or more metals/alloys, or metallic material 420 may be substantially uniform with trace amounts of one or more other metals/alloys included therein.
Metallic material 420 may be of any geometry (e.g., shape and/or dimension) that inlet 406 is capable of accommodating. For example, metallic material 420 may include machining chips, metal pellets, metal support material, parts from failed AM and 3-D printing processes, and so forth. Further, metallic material 420 may include metallic powder, such as metallic powder that is rejected for failing to satisfy quality assurance/quality control processes and/or metallic powder that is recovered during cleaning and/or de-powdering operations of/on ball mill 400. Such metallic powder may be recovered during operational cycles of ball mill 400 (e.g., while ball mill 400 is creating metallic powder) and/or between operational cycles of ball mill 400 (e.g., while ball mill 400 is being cleaned or de-powdered).
While some materials can be recycled or recovered for use with ball mill 400, recycled or recovered materials may need to be cleaned or altered to be in an acceptable feedstock state (e.g., alloy, chemical composition, morphology, grain state, etc.) for ball mill 400. For example, some AM processes may alter the chemical composition of metals or alloys used therein, such as through the loss of some volatile elements (e.g., Zr, Mg, etc.), and so the chemical composition of some metals or alloys may need to be altered (e.g., by adding one or more elements) to return the metals or alloys to a state suitable for use in future AM processes.
In some embodiments, ball mill 400 includes a grinder 412. Grinder 412 may be configured to receive metallic material 420 and grind metallic material 420 to a suitable size to be fed into a comminution component 402, where metallic powder is created via some media (e.g., “balls”). For example, grinder 412 may be configured to grind metal parts and/or structures of various sizes down to metallic chips or pellets suitable for ball milling.
To that end, ball mill 400 may include a filter, sieve, or other mechanism to separate metallic material having geometries unsuitable for ball milling from metallic material having geometries suitable for ball milling. Such a filter, sieve, or other mechanism may be configured to allow metallic material of suitable geometries (e.g., metallic chips or pellets) to pass through in comminution component 402, while preventing metallic material of unsuitable geometries from doing so. The metallic material of unsuitable geometries may be contained within grinder 412, which may continue to grind such metallic material until the suitable geometry is obtained (e.g., until the size/dimensions of metallic material is sufficiently reduced).
In some embodiments, the initial point of the ball milling process itself may begin as metallic material 420 is deposited in comminution component 402 through inlet 406, e.g., after being reduced in size/dimension by grinder 412. Comminution component 402 may have an interior that is a substantially hollow configured for the ball milling process to occur—e.g., the interior of comminution component 402 may be one or more mostly hollow chamber(s).
The interior of comminution component 402 may be of any dimension and/or geometry suitable for the ball milling processes described herein to occur. For example, the interior of comminution component 402 may be substantially smooth and cylindrical, and therefore, may be devoid of any sharp corners or angles, such as right angles. Additionally, a least a portion of the interior of comminution component 402 may be substantially conical. For example, comminution component 402 may taper toward outlet 408.
Metallic material 420 may be substantively transformed within comminution component 402 in order to create metallic powder 422; doing so, however, may involve at a minimum both refinement, or fragmentation, of the metallic material to obtain a suitable powder granule size and altering surface characteristics or morphology of the metallic material to obtain spherical, or nearly spherical, powder granules. The refinement, or fragmentation, of metallic material relies upon an impact force between grinding media and metallic material to be greater than a critical impact force at which the metallic material cracks, whereas propagating morphology changes (and so to ensphere or sphericalize) depends upon the impact force being less than that critical impact force. In addition, the impact frequency between grinding media and metallic material to propagate morphology changes is appreciably greater than the impact frequency to induce fragmentation.
In order to accommodate and facilitate such differences within one continuous ball mill, comminution component 402 may include two or more regions within. For example, as illustrated, comminution component 402 includes a first region 404a, a second region 404b, and a third region 404c. In some other embodiments, however, comminution component 402 may include more or fewer regions than the three illustrated. The regions within comminution component 402 may or may not be physically separated in any of one or more ways, as further described below.
Each of the regions within comminution component 402 may have respective impact components or grinding media arranged therein. As shown in
In some embodiments, each grinding media 410a-c may be a ball or substantially spherical object. In some other embodiments, at least one of grinding media 410a-c may be configured with a different shape. The size (e.g., diameter) and weight of each grinding media 410a-c may be substantially uniform within a respective one of regions 404a-c. Further, the size and/or weight of each grinding media 410a-c respectively arranged in each region 404a-c may progressively decrease from the region closest to inlet 406 (and furthest from outlet 408) to the region closest to outlet 408 (and furthest from inlet 406). For example, first grinding media 410a may each have a diameter of approximately forty (40) millimeters (mm), second grinding media 410b may each have a diameter of approximately twenty (20) mm, and third grinding media 410c may each have a diameter of approximately one (1) mm.
Each grinding media 410a-c may be made of metal or metal alloy, which may be uniform within each grinding media 410a-c. Across the different regions, the respective metal or metal alloy of each grinding media 410a-c may be the same or may be different between some or all of grinding media 410a-c. In other words, first grinding media 410a may all be composed of a first metal or metal alloy, second grinding media 410b may all be composed of a second metal or metal alloy, and third grinding media 410c may all be composed of a third metal or metal alloy; however, the first, second, and/or third metals or metal alloys may be the same or may be different. For example, first grinding media 410a may be composed of a metal or metal alloy having a greater strength and/or hardness than third grinding media 410c.
In relation to metallic material 420, the respective metal or metal alloy of each grinding media 410a-c may have a greater strength (e.g., yield strength, compressive strength, etc.) and/or hardness than metallic material 420. In some embodiments, each grinding media 410a-c may be composed of steel or other iron-carbon alloy. In some other embodiments, first grinding media 410a may have a weight approximately sixty (60) times the weight of a granule of metallic powder 422, second grinding media 410b may have a weight approximately thirty (30) times the weight of a granule of metallic powder 422, and third grinding media 410c may have a weight approximately equal to the weight of a granule of metallic powder 422.
According to various embodiments, the regions of comminution component 402 may be considered as separate based on the difference(s) between one or more of the following parameters, which may be controlled to refine the size and/or morphology of metallic material before reaching outlet 408 as metallic powder 422: the ratio of the weight of grinding media to the weight of metallic powder (e.g., inclusively ranging from 60:1 to 1:1), the size of grinding media (e.g., inclusively ranging from 40 mm to 1 mm), the material(s) of grinding media, the temperature (e.g., inclusively ranging from −200 degrees Celsius (° C.) or temperature of liquid nitrogen to +200° C.), additives (e.g., surfactants, lubricants, abrasives, etc.), aspect ratio(s) of drive shaft(s) of ball mill 400, and/or surface texture(s) of drive shaft(s) of ball mill 400.
One or more parameters used to refine the size and/or morphology of metallic material may be controlled via one or more processes regulated by a computer system 450, which may be connected with ball mill 400 via at least one wired and/or wireless communications link. Computer system 450 may be configured to automatically execute some processes.
In some configurations, computer system 450 may detect various conditions within comminution component 402, and specifically within regions 404a-c, and computer system 450 may tune one or more parameters based on the detected various conditions (e.g., as with a closed-loop feedback system). For example, computer system 450 may detect the size/dimensions and/or morphology of metallic material 420 in one region, and adjust one or more parameters in the next region (e.g., temperature, additive(s), rotation speed(s), vibration movement(s), vibration intensity, etc.) based on the detected size/dimensions and/or morphology. In some other configurations, computer system 450 may adjust one or more parameters independent of the various conditions within comminution component 402.
Using temperature as one illustration, the temperature within comminution component 402 may be controlled to reach some minimum temperature at or near the middle region(s) of comminution component 402 (e.g., second region 404b). In so doing, the critical point (e.g., minimum impact force) to further fragment already-fragmented metallic material 420 may be reduced, and cold welding may be avoided. The temperature may then warm again at region(s) relatively more proximate to outlet 408 to increase the critical point to fragment metallic material 420, and facilitate morphology alteration.
Referring to additives, one or more additives may be added at specific region(s). The one or more additives may be configured to prevent cold welding of metallic material 420, prevent coagulation of metallic material 420, prevent chemical hardening of metallic material 420, lubricate metallic material 420, alter impact force between grinding media 410a-c and metallic material 420, alter impact frequency between grinding media 410a-c and metallic material 420, increase energy transfer between grinding media 410a-c and metallic material 420, and/or alter the amount of shear force between grinding media 410a-c and metallic material 420.
One or more other additives may be added at specific region(s) (e.g., relatively proximate to outlet 408) to alter the final properties of metallic powder 422 created through ball mill 400, such as flowability of metallic powder 422. Some additive(s) may be introduced to create well-mixed, bulk finalized chemical composition of metallic powder 422, which may be effectively re-alloyed in a later AM process. For example, specific elements or compounds may be added to recondition or re-alloy the metallic powder 422, e.g., so that the metallic powder 422 includes some properties desirable for AM processes, such as alloy, chemical composition, morphology, and/or grain state.
As described herein, ball mill 400 may be designed for milling through different regions at which the respective impact frequencies and impact forces are controlled to cause continuous fragmentation, disaggregation, and morphology alteration of metallic material 420 in order to create metallic powder 422. In some embodiments, such continuous milling is at least partially achieved through differently sized grinding media 410a-c at different regions 404a-c (e.g., regions 404a-c may correspond to different travel lengths of metallic material 420 or different travel heights of metallic material for a vertically oriented ball mill).
Accordingly, ball mill 400 may be configured to cause impacts between metallic material 420 and respective grinding media 410a-c as metallic material 420 travels between different regions 404a-c of comminution component 402. Movement of metallic material 420 and grinding media 410a-c may be induced by a drive component 414. Specifically, drive component 414 may be a part of or may be connected to comminution component 402, and drive component 414 may be configured to drive movement of comminution component 402, thereby causing metallic material 420 and grinding media 410a-c within to move.
In some embodiments, drive component 414 may be a gear or similar cog, which may interact with another gear or cog, e.g., causing comminution component 402 to move according to movement of drive component 414. In some other embodiments, drive component 414 may be a shaft (e.g., drive shaft), e.g., similar to an axle, which comminution component 402 may rotate about. Drive component 414 may define an axis of rotation of comminution component 402. For example, comminution component 402 may rotate with or about drive component 414.
In still other embodiments, drive component 414 may cause comminution component 402 to translate, e.g., in addition to or as an alternative to rotation. For example, drive component 414 may cause comminution component 402 to vibrate. Such vibration may include rapid repetition of at least vertical and/or horizontal translation—e.g., drive component 414 may cause comminution component 402 to quickly travel up and down, forward and backward, and/or side to side within a defined travel distance(s).
Potentially, comminution component 402 may include or may be connected with two or more drive components, and at least one of regions 404a-c may be connected with a respective one of the two or more drive components. For example, at least two of regions 404a-c may be configured for independent movement, and one drive component may cause one of regions 404a-c to rotate at a different speed than another drive component causes another of regions 404a-c to rotate.
Comminution component 402 may receive metallic material 420 at first region 404a having first grinding media 410a arranged therein, and drive component 414 may induce movement of first grinding media 410a and metallic material 420. As first grinding media 410a and metallic material 420 mix with one another due to the induced movement, first grinding media 410a may impact metallic material 420. Such impacts in first region 404a may cause metallic material 420 to fragment, e.g., so that the size of metallic material 420 is reduced and the surface area is increased. In other words, the impact force and/or frequency of first grinding media 410a causing fragmentation of metallic material 420 may increase the number of “pieces” of the metallic material.
Therefore, first grinding media 410a may impact metallic material 420 with a minimum impact force and/or impact frequency that is sufficient to fragment metallic material 420. In other words, the minimum impact force and/or impact frequency may exceed a critical point (e.g., minimum impact force) at which metallic material 420 cracks when struck by first grinding media 410a.
Such a critical point may be modulated by controlling one or more parameters of first region 404a, e.g., in order to reduce the critical point, and therefore facilitate fragmentation of metallic material 420. Some parameters may include the weight, size (e.g., diameter), and/or material of first grinding media 410a. Some other parameters may include temperature, additives, an aspect ratio of drive component 414, and/or a surface texture of drive component 414 (e.g., a number and/or size of teeth of drive component 414).
In some embodiments, comminution component 402 may include one or more channel(s) 416 or injection point(s), e.g., from the exterior surface through the interior surface and opening into one of regions 404a-c. Such channel(s) 416 (or injections points) may allow various parameters to be controlled by providing mechanism(s) for introducing one or more external substances or elements directly into one or more regions 404a-c. Such external substances or elements may be manually added and/or may be added through some process(es) controlled/regulated by computer system 450.
Metallic material 420 may enter inlet 406 at or near a room temperature. That is, the temperature of ball mill 400 may be unmodulated at inlet 406. The unmodulated temperature may extend through grinder 412—e.g., grinder 412 may be at or near room temperature so that metallic material 420 is likewise at or near room temperature during grinding.
However, the temperature within first region 404a may be modulated. In so doing, the critical point of metallic material 420 (e.g., the minimum impact force applied to crack the metallic material) may be reduced. One or more types of cryogens and/or refrigerated air may be introduced (e.g., via channel(s) 416) in order to reduce the temperature within first region 404a, and therefore, reduce the temperature of metallic material 420. In some embodiments, first region 404a may cooled to a temperature of approximately 0° C.; however, the temperature within first region 404a may be different according to different embodiments.
Additionally or alternatively, one or more additives may be introduced into first region 404a. For example, the one or more additives may be include an abrasive, silica, stearic acid, graphene, and/or another additive. One or more additives introduced in first region 404a may alter impact force, impact frequency, amount of shear force, and/or properties of metallic material 420 for creation of metallic powder 422. For example, additive(s) may reduce the critical point of metallic material 420 (e.g., the minimum impact force applied to crack the metallic material) and/or may increase the impact force of first grinding media 410a against metallic material 420, thereby increasing the efficacy of first grinding media 410a in fragmenting metallic material 420.
According to some embodiments, the impact frequency between first grinding media 410a and metallic material 420 may be lower relative to the impact frequency of third grinding media 410c and metallic material 420 (having been reduced in size in at least first region 404a). However, the impact force between first grinding media 410a and metallic material 420 may be greater relative to the impact force of third grinding media 410c and metallic material 420. For example, drive component 414 (and potentially other drive component(s)) may differently induce movement in first region 404a and third region 404c to control the relative impact force and/or relative impact frequency.
From first region 404a, metallic material 420 travels to the next region within comminution component 402—that is, second region 404b. In the illustrated embodiment, the next region is one in which the size/dimensions of metallic material 420 is further reduced; in other embodiments, however, the next region may be a region in which surface characteristics of metallic material is altered, such as a region analogous to third region 404c or a region serving as a preparatory stage before third region 404c.
Metallic material 420 may travel from first region 404a to second region 404b based on the movement and/or orientation of comminution component 402. For example, comminution component 402 may be oriented with a (slightly) downward slope, with inlet 406 being relatively higher than outlet 408, or comminution component 402 may be oriented as according to a vertical configuration. Rotation and/or vibration of comminution component 402 (driven by drive component 414) may cause metallic material 420 to travel through regions 404a-c toward outlet 408. Further, the interior geometry of comminution component 402 may cause metallic material 420 to travel from one region to the next—e.g., a conical geometry of the interior of comminution component 402 may facilitate the forward path of metallic material 420 toward outlet 408.
Ball mill 400 may be configured to prevent metallic material 420 from exiting one region and entering the next region until an appropriate size, dimension, and/or morphology is obtained. At least one respective filter or sieve may be positioned between each of regions 404a-c within comminution component 402. For example, at least one first filter or sieve may be positioned within comminution component 402 between first region 404a and second region 404b, and at least one second filter or sieve may be positioned within comminution component 402 between second region 404b and third region 404c.
Once (sufficiently) fragmented in first region 404a, metallic material 420 travels to second region 404b. In second region 404b, drive component 414 induces movement of second grinding media 410b and metallic material 420 causing impact therebetween. Similar to impacts in first region 404a, impacts in second region 404b may cause metallic material 420 to fragment, e.g., so that the size of metallic material 420 is reduced and the surface area is increased. However, the critical point (e.g., minimum impact force) at which metallic material 420 cracks when struck may be different in second region 404b relative to the first due to the reduced size/dimensions of metallic material 420.
Thus, one or more parameters in second region 404b may be controlled differently from one or more parameters in first region 404a, e.g., in order to reduce the critical point of metallic material 420. In particular, parameters including weight, size (e.g., diameter), and/or material of second grinding media 410b may be different than first grinding media 410a. Further, one or more other parameters, such as temperature, additives, an aspect ratio of drive component 414 (or another drive component), and/or a surface texture of drive component 414 (e.g., or another drive component), may be controlled to be different than in first region 404a.
Potentially, the reduced size of metallic material 420 in second region 404b may cause the critical impact point to be increased. Therefore, the temperature in second region 404b may be reduced relative to first region 404a (as well as third region 404c). For example, the temperature of ball mill 400, including the temperature to which metallic material 420 is exposed, may be at its lowest in second region 404b. Comparatively, the temperature of ball mill 400 may be at its highest (warmest) in third region 404c, with the temperature in first region 404a being somewhere in between (e.g., approximately at or below 0° C.).
Illustratively, the temperature in second region 404b may be controlled to be approximately −200° C.; however, the temperature within second region 404b may be different according to different embodiments. The temperature in second region 404b may decrease the critical impact point of metallic material 420, while avoid cold welding (potentially with the aid of additive(s)).
One or more types of cryogens and/or refrigerated air may be introduced in order to reduce the temperature within second region 404b, and so reduce the temperature of metallic material 420. For example, dry ice and/or liquid nitrogen may be added into second region 404b, e.g., via channel(s) 416.
Additionally or alternatively, one or more additives may be introduced into second region 404b, e.g., via channel(s) 416. For example, the one or more additives may be include an abrasive, silica, stearic acid, graphene, and/or another additive. Such additive(s) introduced in second region 404b may alter impact force, impact frequency, amount of shear force, and/or properties of metallic material 420 for creation of metallic powder 422. For example, may reduce the critical point of metallic material 420 (e.g., the minimum impact force applied to crack the metallic material) and/or may increase the impact force of first grinding media 410a against metallic material 420. Additive(s) introduced into second region 404b may be the same or different from additive(s) introduced into first region 404a.
According to some embodiments, the impact frequency between first grinding media 410a and metallic material 420 may be lower relative to the impact frequency of third grinding media 410c and metallic material 420 (having been reduced in size in at least first region 404a). However, the impact force between first grinding media 410a and metallic material 420 may be greater relative to the impact force of third grinding media 410c and metallic material 420. For example, drive component 414 (and potentially other drive component(s)) may differently induce movement in first region 404a and third region 404c to control the relative impact force and/or relative impact frequency.
After metallic material 420 is sufficiently fragmented at one or more preceding regions, the fragmented metallic material may reach one or more regions in which the surface characteristics or morphology of the fragmented metallic material is altered in order to finally create metallic powder 422. For example, fragmented metallic material 420 may traverse the first and second regions to reach third region 404c at which surface characteristics of metallic material 420 is altered, e.g., to obtain (near-) spherical metallic powder 422.
Metallic material 420 may reach third region 404c based on the movement, orientation, and/or interior geometry of comminution component 402. For example, comminution component 402 may be oriented with a (slightly) downward slope, with inlet 406 being relatively higher than outlet 408, comminution component 402 may be oriented as according to a vertical configuration, and/or comminution component 402 may feature a conical interior geometry tapering toward outlet 408.
Similar to configurations described above with respect to the first and second regions, fragmented metallic material 420 may comingle with third grinding media 410c at third region 404c. As drive component 414 induces movement of third grinding media 410c and metallic material 420, third grinding media 410c impacts metallic material 420. Such impacts in first region 404a may alter surface characteristics or morphology of metallic material 420 without causing fragmentation thereof, e.g., so that the exterior surface of granules of metallic powder 422 become spherical or nearly spherical.
Therefore, third grinding media 410c may impact metallic material 420 with a maximum impact force and/or impact frequency that is insufficient to fragment metallic material 420, but sufficient to change the surface characteristics/morphology of fragmented metallic material 420. In other words, the maximum impact force and/or impact frequency of third grinding media 410c against fragmented metallic material 420 may be less than the critical point of the fragmented metallic material 420 (e.g., minimum impact force to cause metallic material 420 to again be fragmented in third region 404c).
In some embodiments, third region 404c may be a region of high energy, e.g., relative to the low-energy of first region 404a, such that the impact frequency between the grinding media and metallic material is increased in third region 404c but the impact force is decreased. In some other embodiments, however, different regions may be regarded as “low energy” and “high energy,” and may be differently arranged in comminution component 402 to alloy and/or alter metallic material 420 as desired for the creation of metallic powder 422 (e.g., nano-grain refinement).
As with the other regions described above, one or more parameters within third region 404c may be controlled, although parameters in third region 404c may be controlled to prevent fragmentation of metallic material 420 (e.g., increase the critical point) while facilitating morphology changes to metallic material 420. Thus, various parameters may include the weight, size (e.g., diameter), and/or material of third grinding media 410c. Various other parameters may include temperature, additives, an aspect ratio of drive component 414, and/or a surface texture of drive component 414 (e.g., a number and/or size of teeth of drive component 414).
By way of illustration, the temperature within third region 404c may be increased, e.g., relative to room temperature. In so doing, the critical point of metallic material 420 (e.g., the minimum impact force applied to crack the metallic material) may be increased but the malleability of the surface of metallic material 420 may be increased. For example, heated air may be introduced (e.g., via channel(s) 416) in order to increase the temperature within third region 404c. In some embodiments, third region 404c may heated to a temperature of approximately +200° C.; however, the temperature within third region 404c may be different according to different embodiments.
Additionally or alternatively, one or more additives may be introduced into first region 404a. For example, the one or more additives may be include an surfactants, lubricants, silica, stearic acid, graphene, and/or another additive. One or more additives introduced in third region 404c may alter impact force, impact frequency, amount of shear force, and/or properties of metallic material 420 for creation of metallic powder 422. For example, additive(s) introduced in third region 404c may increase the critical point of metallic material 420 (e.g., the minimum impact force applied to crack the metallic material) and/or may increase malleability of metallic material 420, thereby increasing the efficacy of third grinding media 410c in altering the morphology of metallic material 420 to be (nearly) spherical.
When the surface characteristics/morphology of fragmented metallic material 420 is satisfactorily altered in the last region (e.g., third region 404c), the (nearly) spherical metallic material may create metallic powder 422. Ball mill 400 may output metallic powder 422 at outlet 408, e.g., into a receptacle or other suitable container for the finished metallic powder. For example, comminution component 402 may be oriented with a (slightly) downward slope, with outlet 408 being relatively lower than third region 404c, or comminution component 402 may be oriented as according to a vertical configuration.
Alternatively or additionally, rotation and/or vibration of comminution component 402 (driven by drive component 414) may cause metallic material 420 to travel toward outlet 408. Further, the interior geometry of comminution component 402 may cause metallic material 420 to travel toward outlet 408—e.g., a conical geometry of the interior of comminution component 402 may facilitate the forward path of metallic material 420 toward outlet 408.
The spherical metallic material may create metallic powder 422 once each granule is both sufficiently spherical and within a defined size (e.g., diameter) range. Thus, ball mill 400 may be configured to fragmented metallic material 420 from exiting outlet 408 until an appropriate size and morphology is obtained. For example, at least one filter or sieve may be positioned between third region 404c and outlet 408. The at least one filter or sieve may prevent metallic material 420 from exiting through outlet 408.
While ball mill 400 is illustrated with one outlet, some other embodiments of ball mill 400 may include two or more outlets and/or output through outlet 408 may be modulated at different point(s) during powder creation. That is, ball mill 400 may be configured to create metallic powders having different characteristics (e.g., different sizes/diameters and/or different morphologies), e.g., potentially during continuous operation of ball mill 400.
Thus, the characteristics of (or constraints on) the final powder may be modulated so that different powder is created and output through outlet 408 and/or additional outlet(s). For example, ball mill 400 may reconfigure the size/diameter of the final powder during the ball milling process, such as by reducing the size/diameter and/or altering the acceptable morphology of the final metallic powder after some metallic powder has already been created. To that end, ball mill 400 may reconfigure or replace one or more filters or sieves that metallic powder passes through to be dispenses through outlet 408, e.g., so that only granules relatively smaller and/or having different morphology than previously created metallic powder are able to travel through the one or more filters or sieves. Additionally or alternatively, ball mill 400 may reconfigure or switch to another outlet (e.g., different from outlet 408) so that only metallic powder of a smaller size/diameter and/or different morphology is permitted to pass through.
In some embodiments, at least one filter or sieve may be vibrated at a certain frequency (or respective frequencies for multiple filters or sieves), which may facilitate the ejection of metallic powder 422 adhering to the size range and morphology constraints for powder creation. Additionally or alternatively, at least one filter or sieve may spin or rotate, e.g., at an offset from at least one other filter or sieve, in order to control the flow of metallic material 420 in third region 404c and so allow only metallic powder 422 within the size range and morphology constraints to be ejected.
In some other embodiments, one or more sensors may be arranged within comminution component 402, such as visual, ultrasonic, and/or acoustic sensors. The one or more sensors may be connected with computer system 450, and therefore, may provide information about the metallic material within one or more of regions 404a-c in which the sensor(s) are positioned. Computer system 450 may use information from the sensor(s) to detect size and/or morphology of metallic material 420 in one or more of regions 404a-c, and computer system 450 may control the travel of metallic material 420 across the regions based on the detected size and/or morphology.
For example, a set of sensors may be located proximate to outlet 408, and may be configured to sense information about the fragmented metallic material in third region 404c. Computer system 450 may receive the information from the set of sensors and, based on the information, may determine whether metallic powder 422 is created—that is, computer system 450 may determine whether metallic material 420 is fragmented to a size and altered to a spherical morphology that is acceptable as metallic powder 422. When computer system 450 determines metallic material 420 is fragmented to a size and altered to a spherical morphology that is acceptable as metallic powder 422, computer system 450 may cause metallic powder 422 to be dispensed through outlet 408, such as by opening a barrier. Otherwise, computer system 450 may retain metallic material 420 with comminution component 402 until the metallic material is fragmented to a size and altered to a spherical morphology that is acceptable as metallic powder 422.
In some aspects, the properties or characteristics of the metallic powder 422 may be configurable. For example, computer system 450 may receiver user input indicating some size/dimension range and/or morphology, and computer system 450 may configure one or more parameters of ball mill 400 so that ball mill 400 creates metallic powder conforming to the size/dimension range and/or morphology. Potentially, such user input may include the type of AM process (e.g., SLS, SLM, or other PBF-based process) and/or type of build of an AM process (e.g., node, structure, load-bearing part, etc.) for which the metallic powder is being created, and computer system 450 may configure ball mill 400 based on the user input including the type of AM process and/or type of AM process build.
In some further embodiments, ball mill 400 may be configured to be cleaned through the addition of additives and/or cleaning agents at inlet 406 (e.g., rather than metallic material 420). That is, ball mill 400 may be “self-cleaning” by executing the ball milling process, but with some cleaning additive(s) and/or cleaning agent(s) instead of metallic material 420 to create metallic powder 422. In some other further embodiments, ball mill 400 may be at least partially cleaned using pressurized liquid and/or gas, and/or introducing liquid nitrogen or other additive, through one or more of inlet 406, outlet 408, channel(s) 416, media entrance/exit point(s), and/or other paths to access the interior of comminution component 402.
According to various embodiments, comminution component 502 may include a conical section 526, which is relatively widest at the point most proximate to inlet 506 and relatively narrowest at the point most proximate to outlet 508. While ball mill 500 is illustrated with conical section 526 spanning only a portion of the entire comminution component 502, in other embodiments, most or all of comminution component 502 may be defined as conical section 526.
In still other embodiments, comminution component 502 may include a second conical section, which may be substantially inverse to conical section 526. In such other embodiments, the narrowest area of comminution component 502 may be relatively near the middle, where the narrowest section of conical section 526 meets the second conical section. Therefore, the widest areas of conical section 526 and the second conical section may be near inlet 506 and outlet 508, respectively.
Within comminution component 502, each of a first grinding media 510a, a second grinding media 510b, and a third grinding media 510c may be respectively arranged in first, second, and third regions 504a-c. Ball mill 500 may be configured to maintain such an arrangement of grinding media, e.g., to prevent or reduce the likelihood of one of grinding media 510a-c from becoming comingled with another one of grinding media 510a-c.
In some configurations, the interior geometry of comminution component 502 may facilitate the prevention of grinding media 510a-c becoming comingled. For example, the interior geometry of comminution component 502 may be configured to reduce or prevent one grinding media arranged within one region from traveling to another region (and mixing with another grinding media of the other region). However, such an interior geometry may still allow the free flow of metallic material therein, e.g., between regions as appropriate.
In some other configurations, which may include vertical or relatively more vertical orientations of ball mill 500, grinding media 510a-c may be quasi-stacked within respective regions 504a-c, and substantially horizontal movement of comminution component 502 may minimize mixing of grinding media 510a-c (e.g., vertical mixing). For example, comminution component 502 may include one or more points of media exit 530. Ball mill 500 may be configured to release one of grinding media 510a-c that is mixed with another of grinding media 510a-c through media exit 530.
One of grinding media 510a-c that is released through media exit 530 may be resorted and then added back into the corresponding one of regions 504a-c, e.g., through a point of media entrance 528. In some embodiments, resorting and returning one of the grinding media to its corresponding region may be automatically executed. Although in other embodiments, resorting and returning one of the grinding media to its corresponding region may be manually performed.
In some embodiments, one or more of grinding media 510a-c may be coated. For example, first grinding media 510a may be coated with a substance that increases the likelihood of fragmenting metallic material upon impact. Conversely, third grinding media 510c may be coated with a substance that decreases the likelihood of fragmenting metallic material upon impact, which may increase the alteration of surface characteristics of metallic material caused upon impact with third grinding media 510c. Illustratively, substances that may be used to coat at least one of grinding media 510a-c may prevent cold welding of metallic material, prevent coagulation of metallic material, prevent chemical hardening of metallic material, lubricate metallic material, alter impact force of at least one grinding media 510a-c, alter impact frequency of at least one grinding media 510a-c, increase energy transfer to or from at least one grinding media 510a-c, and/or alter shear force of at least one grinding media 510a-c.
As coating on the grinding media may chip or otherwise wear off over time, the coating may be redone. For example, grinding media may be recoated between cycles of metallic powder creation. Additionally or alternatively, grinding media may be recoated when removed through media exit 530 and added through media entrance 528, e.g., during cycles of metallic powder creation).
According to various embodiments, ball mill 500 may include a drive component 514 that is different from a gear or cog, such as a gear encircling comminution component 502. For example, drive component 514 may include at least one drive shaft. Potentially, drive component 514 may be connected with or fabricated (e.g., machined) as part of comminution component 502, and may be positioned through at least a portion of the interior of comminution component 502.
Drive component 514 may be configured to rotate (e.g., drive component 514 may be connected with a motor or other engine), which may drive movement of comminution component 502, as well as the components (e.g., grinding media 510a-c, metallic material, etc.) arranged therein. Drive component 514 may define an axis of rotation of comminution component 502.
In some embodiments, the speed and/or force with which drive component 514 causes comminution component 502 to move (rotate) may be based on one of regions 504a-c. For example, drive component 514 may be configured to cause comminution component 502 to rotate at a relatively lower rate when metallic material is arranged within first region 504a, but drive component 514 may be configured to cause comminution component 502 to rotate at a relatively faster rate when metallic material is arranged within third region 504c.
An aspect ratio of drive component 514 may affect movement of comminution component 502, as well as movement of grinding media 510a-c and metallic material therein. The aspect ratio of drive of drive component 514 may be modulated, which may change the impact force and/or impact frequency of grinding media 510a-c and metallic material.
In some other embodiments, drive component 514 may include two or more drive shafts. For example, drive component 514 may include a respective drive shaft for each of regions 504a-c within comminution component 502. The aspect ratios of each of the drive shafts may be configured according to the impact force and/or impact frequency that is desirable for each of regions 504a-c.
Potentially, two or more of regions 504a-c may be configured to move (rotate) independently. For example, drive component 514 may include three drive shafts for the three regions within comminution component 502. Each drive shaft may cause a respective one of regions 504a-c to rotate independently at a respective rate that is configured for the impact force and/or frequency desirable for that region.
In some embodiments, drive component 514 may be coated—e.g., one or more drive shafts of drive component 514 may be individually coated with the same or different substance or additive. For example, in first region 504a, drive component 514 may be coated with a substance that increases the likelihood of fragmenting metallic material upon impact. In third region 504c, however, drive component 514 may be coated with a substance that decreases the likelihood of fragmenting metallic material upon impact, which may increase the alteration of surface characteristics of metallic material. Illustratively, substances that may be used to coat drive component 514 may prevent cold welding of metallic material, prevent coagulation of metallic material, prevent chemical hardening of metallic material, lubricate metallic material, alter impact force, alter impact frequency, increase energy transfer, and/or alter an amount of shear force.
The ball milling process may cause some coating(s) on drive component 514 to wear or “chip off” over time. Therefore, coating(s) on drive component 514 may be reapplied, e.g., between cycles of powder creation. Additionally or alternatively, coating(s) on drive component 514 may be changed, e.g., according to desired characteristics of the final powder, the type of metallic material being milled, and so forth.
According to various embodiments, ball mill 600 includes a drive component 614 that may be at least one drive shaft. For example, drive component 614 may define an axis of rotation of comminution component 602. Potentially, drive component 614 may include two or more drive shafts—e.g., drive component 614 may include three drive shafts, each of which may be configured to drive movement of/in at least one of regions 604a-c within comminution component 602.
When drive component 614 is configured to include two or more drive shafts, some or all of the two or more drive shafts may have some different characteristics. For example, the two of more drive shafts may have different aspect ratios—e.g., one drive shaft configured for first region 604a may have a different aspect ratio than another drive shaft configured for third region 604c. In some other examples, the two or more drive shafts may have different dimensions (e.g., lengths, widths, heights, diameters, etc.) and/or different shapes.
In various embodiments illustrated in
Each of regions 604a-c may have at least one of arms 632 substantially positioned therein. For example, each of one or more drive shafts may have at least one of arms 632 extending therefrom, e.g., such that each of regions 604a-c may have at least one of arms 632 substantially positioned therein. However, the number of arms 632 substantially positioned within each of regions 604a-c may be different.
Arms 632 may be of length(s) that allows movement within comminution component 602. In particular, arms 632 may be of length(s) that allow drive component 614 to rotate 360° (and so cause arms to rotate the same 360°) without contacting the interior surface of comminution component 602. Thus, when the interior geometry of comminution component 602 is cylindrical, arms 632 may be of length(s) that is less than half the radius of comminution component 602.
In some embodiments, arms 632 may each be of one uniform length. In some other embodiments, some or all of arms 632 may have different lengths. For example, the arms substantially positioned in first region 604a may have a greater length than the arms substantially positioned in third region 604c, which may have a relatively smaller volume than first region 604a due to the conical shape of comminution component 602.
Arms 632 may be of any suitable shape(s), which may be uniform for all of arms 632 or may be different for some or all of arms 632. For example, some or all of arms 632 may be substantially cylindrical. Additionally or alternatively, some or all of arms 632 may have a blade shape and/or a triangular shape. Further, some or all of arms 632 may taper down the point of connection (e.g., to drive component 614 or the interior of comminution component 602), so that those arms are wider toward their distal ends.
Arms 632 may have any suitable surface texture(s), which may be uniform for all of arms 632 or may be different for some or all of arms 632. For example, some or all of arms 632 may have some surface texture designed to increase friction or reduce friction.
Within comminution component 602, each of a first grinding media 610a, a second grinding media 610b, and a third grinding media 610c may be respectively arranged in first, second, and third regions 604a-c. Ball mill 600 may be configured to maintain such an arrangement of grinding media, e.g., to prevent or reduce the likelihood of one of grinding media 610a-c from becoming comingled with another one of grinding media 610a-c.
In some configurations, arms 632 may facilitate the prevention of grinding media 610a-c becoming comingled. For example, arms 632 may be configured to reduce or prevent one grinding media arranged within one region from traveling to another region (and mixing with another grinding media of the other region). Further, arms 632 may still allow, or may aid, the free flow of metallic material, e.g., between regions 604a-c as appropriate.
Potentially arms 632 may maintain segregation of grinding media 610a-c from one another based on the frequency of impact with arms 632. For example, different sets of arms 632 may configured to rotate at different rates, which may control the frequency with which arms 632 contact grinding media 610a-c. Each of grinding media 610a-c may contact a respective set of arms 632 with a respective frequency that maintains segregation between grinding media 610a-c.
In some embodiments, ball mill 600 may be vertically oriented, and the frequency with which each set of arms contacts respective grinding media 610a-c may maintain such segregation by keeping respective grinding media 610a-c aloft within its own corresponding one of regions 604a-c. To that end, each set of arms 632 positioned within each of regions 604a-c may be configured with a respective speed, amount, and/or geometry corresponding to maintaining respective grinding media within its own region.
In addition, or as an alternative, to maintain segregation of grinding media 610a-c, arms 632 may be configured to affect the impact force and/or impact frequency of grinding media 610a-c against metallic material within regions 604a-c. For example, the number, size, surface texture, and/or rotation speed of some of arms 632 may be controlled to increase impact force and decrease impact frequency in region(s) in which metallic material is to be fragmented (e.g., first region 604a), whereas the number, size, surface texture, and/or rotation speed of some other of arms 632 may be controlled to decrease impact force and increase impact frequency in region(s) in which surface characteristics of metallic material is to be altered (e.g., third region 604c).
In some embodiments, some or all of arms 632 may be coated—e.g., some or all of arms 632 may be coated with the same or different substance or additive. For example, in first region 604a, one set of arms 632 may be coated with a substance that increases the likelihood of fragmenting metallic material upon impact. In third region 604c, however, another set of arms 632 may be coated with a substance that decreases the likelihood of fragmenting metallic material upon impact, which may increase the alteration of surface characteristics of metallic material. Illustratively, substances that may be used to coat some or all of arms 632 may prevent cold welding of metallic material, prevent coagulation of metallic material, prevent chemical hardening of metallic material, lubricate metallic material, alter impact force, alter impact frequency, increase energy transfer, and/or alter an amount of shear force.
In some embodiments, regions 704a-b within comminution component 702 may be separated by a set of one or more filters 734a-c. Potentially, one or more of filters 734a-c may implemented as a sieve. Although three filters are illustrated in
Each of filters 734a-c may include a set of holes or throughways. Potentially, filters 734a-c may all include the same number of holes or throughways; however, some or all of filters 734a-c may include different numbers of holes or throughways. The holes or throughways of filters 734a-c may be aligned and/or may be offset.
Each of the holes or throughways may be of a size/dimension and/or morphology configured to allow satisfactorily fragmented/altered metallic material to pass through from first region 704a to second region 704b, while preventing unsuitable metallic material from passing through (e.g., metallic material that is too large or too misshapen to be accommodated at second region 704). Furthermore, ball mill 700 may be configured to prevent metallic material 720 within one region from traveling backward to a previously traversed region.
According to some embodiments, filters 734a-c may be configured to vibrate in order to control the flow of metallic material progressively toward second region 704b. Filters 734a-c may vibrate at one uniform frequency, or some or all of filters 734a-c may vibrate at different frequencies. According to some other embodiments, filters 734a-c may rotate or spin at one uniform rate, or some or all of filters 734a-c may rotate or spin at different rates. Potentially, one or more of filters 734a-c may be connected to the interior of comminution component 702, and therefore, the one or more filters may rotate or vibrate according to rotation/movement of comminution component 702 (e.g., as induced by a drive component).
Within comminution component 702, a first grinding media 710a and a second grinding media 710b may be respectively arranged in regions 704a-b. Ball mill 700 may be configured to maintain such an arrangement of grinding media, e.g., to prevent or reduce the likelihood of one of grinding media 710a-b from becoming comingled with another one of grinding media 710a-b.
In some configurations, filters 734a-c may facilitate the prevention of grinding media 710a-b becoming comingled. For example, filters 734a-c may be configured to reduce or prevent first grinding media 410a arranged within first region 404a from traveling to second region 404b, and vice versa. Specifically, the holes of throughways of filters 734a-c may obstruct grinding media 710a-b, and so prevent grinding media 710a-b from migrating out of its corresponding region.
Initially, a metallic material is received at a first region of a comminution component (operation 802). The comminution component may include at least a first region having a plurality of first grinding components arranged therein and a second region having a plurality of second grinding components arranged therein. Within the comminution component, the metallic material may by fragmented by contact with the plurality of first grinding components when in the first region, and the fragmented metallic material may have morphology altered by contact with the plurality of second grinding components when in the second region.
In some embodiments, at least one additive may be provided for one of the contact of the metallic material with the plurality of first grinding components or the contact of fragmented metallic material with the plurality of second grinding components (operation 804). For example, the at least one additive may be configured to prevent cold welding of the metallic powder, prevent coagulation of the metallic powder, lubricate the metallic powder, modulate impact frequency with the metallic powder, increase energy transfer with the metallic powder, or prevent chemical hardening of the metallic powder.
In some embodiments, rotation of a first set of arms positioned at the first region within the comminution component may be driven (operation 806). The metallic material may be fragmented based on the rotation of the first set of arms. The metallic material is fragmented through contact with the plurality of first grinding components at a first impact force and a first impact frequency (operation 808).
The fragmented metallic material may be filtered into position for surface characteristics of the fragmented metallic material to be altered (operation 810). Further, separation of the plurality of first grinding components and the plurality of second grinding components may be maintained (operation 812).
In some embodiments, rotation of a second set of arms positioned at the second region within the comminution component may be driven (operation 814). Surface characteristics of the fragmented metallic material may be altered to obtain metallic powder based on the rotation of the second set of arms. The surface characteristics of the fragmented metallic material are altered through contact with the plurality of second grinding components at a second impact force lower than the first impact force and a second impact frequency higher than the first impact frequency (operation 816).
Metallic powder is then output, and the metallic powder is spherical with a diameter inclusively between 10 μm and 100 μm (operation 818).
It is understood that the specific order or hierarchy of blocks in the processes/flowcharts disclosed is an illustration of example approaches. Based upon design preferences, it is understood that the specific order or hierarchy of blocks in the processes/flowcharts may be rearranged. Further, some blocks may be combined or omitted. The accompanying method claims present elements of the various blocks in a sample order, and are not meant to be limited to the specific order or hierarchy presented.
The previous description is provided to enable any person skilled in the art to practice the various aspects described herein. Various modifications to these aspects will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other aspects. Thus, the claims are not intended to be limited to the aspects shown herein, but is to be accorded the full scope consistent with the language claims, wherein reference to an element in the singular is not intended to mean “one and only one” unless specifically so stated, but rather “one or more.” Terms such as “if,” “when,” and “while” should be interpreted to mean “under the condition that” rather than imply an immediate temporal relationship or reaction. That is, these phrases, e.g., “when,” do not imply an immediate action in response to or during the occurrence of an action, but simply imply that if a condition is met then an action will occur, but without requiring a specific or immediate time constraint for the action to occur. The word “exemplary” is used herein to mean “serving as an example, instance, or illustration.” Any aspect described herein as “exemplary” is not necessarily to be construed as preferred or advantageous over other aspects. Unless specifically stated otherwise, the term “some” refers to one or more. Combinations such as “at least one of A, B, or C,” “one or more of A, B, or C,” “at least one of A, B, and C,” “one or more of A, B, and C,” and “A, B, C, or any combination thereof” include any combination of A, B, and/or C, and may include multiples of A, multiples of B, or multiples of C. Specifically, combinations such as “at least one of A, B, or C,” “one or more of A, B, or C,” “at least one of A, B, and C,” “one or more of A, B, and C,” and “A, B, C, or any combination thereof” may be A only, B only, C only, A and B, A and C, B and C, or A and B and C, where any such combinations may contain one or more member or members of A, B, or C. All structural and functional equivalents to the elements of the various aspects described throughout this disclosure that are known or later come to be known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the claims. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the claims. The words “module,” “mechanism,” “element,” “device,” and the like may not be a substitute for the word “means.” As such, no claim element is to be construed as a means plus function unless the element is expressly recited using the phrase “means for.”
| Number | Name | Date | Kind |
|---|---|---|---|
| 1125921 | Atkins | Jan 1915 | A |
| 1185342 | O'Shaughnessy | May 1916 | A |
| 1246775 | Mushett | Nov 1917 | A |
| 1361205 | Van Zandt | Dec 1920 | A |
| 1361281 | Newhouse | Dec 1920 | A |
| 1394334 | Newhouse | Oct 1921 | A |
| 1427234 | Sherban | Aug 1922 | A |
| 1513952 | Apted | Nov 1924 | A |
| 1587769 | Fisher | Jun 1926 | A |
| 1591941 | Newhouse | Jul 1926 | A |
| 1598933 | Read | Sep 1926 | A |
| 1683627 | Read | Sep 1928 | A |
| 1692974 | Barker | Nov 1928 | A |
| 1710659 | Greisen | Apr 1929 | A |
| 1739855 | Newhouse | Dec 1929 | A |
| 1788825 | Danks | Jan 1931 | A |
| 2131260 | Temple | Sep 1938 | A |
| 2160169 | Pontoppidan | May 1939 | A |
| 2256841 | Hardinge | Sep 1941 | A |
| 3314614 | Daniel | Apr 1967 | A |
| 3459380 | Kartman | Aug 1969 | A |
| 3624797 | Waddell | Nov 1971 | A |
| 3856214 | Kaltenbach | Dec 1974 | A |
| 3949940 | Horning | Apr 1976 | A |
| 3964717 | Hansen | Jun 1976 | A |
| 4026479 | Bradburn | May 1977 | A |
| 4303205 | Geiger | Dec 1981 | A |
| 4469282 | Booz | Sep 1984 | A |
| 4949907 | Bogdanov | Aug 1990 | A |
| 5203226 | Hongou et al. | Apr 1993 | A |
| 5328501 | McCormick et al. | Jul 1994 | A |
| 5702060 | Matteazzi et al. | Dec 1997 | A |
| 5716013 | Benson | Feb 1998 | A |
| 5742385 | Champa | Apr 1998 | A |
| 5865385 | Arnett | Feb 1999 | A |
| 5990444 | Costin | Nov 1999 | A |
| 6010085 | Angeletakis | Jan 2000 | A |
| 6010155 | Rinehart | Jan 2000 | A |
| 6086242 | Rajamani et al. | Jul 2000 | A |
| 6096249 | Yamaguchi | Aug 2000 | A |
| 6140602 | Costin | Oct 2000 | A |
| 6250533 | Otterbein et al. | Jun 2001 | B1 |
| 6252196 | Costin et al. | Jun 2001 | B1 |
| 6318642 | Goenka et al. | Nov 2001 | B1 |
| 6365057 | Whitehurst et al. | Apr 2002 | B1 |
| 6391251 | Keicher et al. | May 2002 | B1 |
| 6409930 | Whitehurst et al. | Jun 2002 | B1 |
| 6468439 | Whitehurst et al. | Oct 2002 | B1 |
| 6554345 | Jonsson | Apr 2003 | B2 |
| 6585151 | Ghosh | Jul 2003 | B1 |
| 6644721 | Miskech et al. | Nov 2003 | B1 |
| 6811744 | Keicher et al. | Nov 2004 | B2 |
| 6827303 | Yanase | Dec 2004 | B2 |
| 6866497 | Saiki | Mar 2005 | B2 |
| 6919035 | Clough | Jul 2005 | B1 |
| 6926970 | James et al. | Aug 2005 | B2 |
| 7152292 | Hohmann et al. | Dec 2006 | B2 |
| 7152819 | Ford | Dec 2006 | B2 |
| 7344186 | Hausler et al. | Mar 2008 | B1 |
| 7500373 | Quell | Mar 2009 | B2 |
| 7586062 | Heberer | Sep 2009 | B2 |
| 7637134 | Burzlaff et al. | Dec 2009 | B2 |
| 7710347 | Gentilman et al. | May 2010 | B2 |
| 7716802 | Stern et al. | May 2010 | B2 |
| 7745293 | Yamazaki et al. | Jun 2010 | B2 |
| 7766123 | Sakurai et al. | Aug 2010 | B2 |
| 7767151 | Downs | Aug 2010 | B2 |
| 7852388 | Shimizu et al. | Dec 2010 | B2 |
| 7908922 | Zarabadi et al. | Mar 2011 | B2 |
| 7951324 | Naruse et al. | May 2011 | B2 |
| 8094036 | Heberer | Jan 2012 | B2 |
| 8163077 | Eron et al. | Apr 2012 | B2 |
| 8286236 | Jung et al. | Oct 2012 | B2 |
| 8289352 | Vartanian et al. | Oct 2012 | B2 |
| 8297096 | Mizumura et al. | Oct 2012 | B2 |
| 8354170 | Henry et al. | Jan 2013 | B1 |
| 8383028 | Lyons | Feb 2013 | B2 |
| 8408036 | Reith et al. | Apr 2013 | B2 |
| 8429754 | Jung et al. | Apr 2013 | B2 |
| 8437513 | Derakhshani et al. | May 2013 | B1 |
| 8444903 | Lyons et al. | May 2013 | B2 |
| 8452073 | Taminger et al. | May 2013 | B2 |
| 8599301 | Dowski, Jr. et al. | Dec 2013 | B2 |
| 8606540 | Haisty et al. | Dec 2013 | B2 |
| 8610761 | Haisty et al. | Dec 2013 | B2 |
| 8631996 | Quell et al. | Jan 2014 | B2 |
| 8675925 | Derakhshani et al. | Mar 2014 | B2 |
| 8678060 | Dietz et al. | Mar 2014 | B2 |
| 8686314 | Schneegans et al. | Apr 2014 | B2 |
| 8686997 | Radet et al. | Apr 2014 | B2 |
| 8694284 | Berard | Apr 2014 | B2 |
| 8720876 | Reith et al. | May 2014 | B2 |
| 8752166 | Jung et al. | Jun 2014 | B2 |
| 8755923 | Farahani et al. | Jun 2014 | B2 |
| 8787628 | Derakhshani et al. | Jul 2014 | B1 |
| 8818771 | Gielis et al. | Aug 2014 | B2 |
| 8873238 | Wilkins | Oct 2014 | B2 |
| 8978535 | Ortiz et al. | Mar 2015 | B2 |
| 9006605 | Schneegans et al. | Apr 2015 | B2 |
| 9071436 | Jung et al. | Jun 2015 | B2 |
| 9101979 | Hofmann et al. | Aug 2015 | B2 |
| 9104921 | Derakhshani et al. | Aug 2015 | B2 |
| 9126365 | Mark et al. | Sep 2015 | B1 |
| 9128476 | Jung et al. | Sep 2015 | B2 |
| 9138924 | Yen | Sep 2015 | B2 |
| 9149988 | Mark et al. | Oct 2015 | B2 |
| 9156205 | Mark et al. | Oct 2015 | B2 |
| 9186848 | Mark et al. | Nov 2015 | B2 |
| 9244986 | Karmarkar | Jan 2016 | B2 |
| 9248611 | Divine et al. | Feb 2016 | B2 |
| 9254535 | Buller et al. | Feb 2016 | B2 |
| 9266566 | Kim | Feb 2016 | B2 |
| 9269022 | Rhoads et al. | Feb 2016 | B2 |
| 9327452 | Mark et al. | May 2016 | B2 |
| 9329020 | Napoletano | May 2016 | B1 |
| 9332251 | Haisty et al. | May 2016 | B2 |
| 9346127 | Buller et al. | May 2016 | B2 |
| 9389315 | Bruder et al. | Jul 2016 | B2 |
| 9399256 | Buller et al. | Jul 2016 | B2 |
| 9403235 | Buller et al. | Aug 2016 | B2 |
| 9418193 | Dowski, Jr. et al. | Aug 2016 | B2 |
| 9457514 | Schwärzler | Oct 2016 | B2 |
| 9469057 | Johnson et al. | Oct 2016 | B2 |
| 9478063 | Rhoads et al. | Oct 2016 | B2 |
| 9481402 | Muto et al. | Nov 2016 | B1 |
| 9486878 | Buller et al. | Nov 2016 | B2 |
| 9486960 | Paschkewitz et al. | Nov 2016 | B2 |
| 9502993 | Deng | Nov 2016 | B2 |
| 9525262 | Stuart et al. | Dec 2016 | B2 |
| 9533526 | Nevins | Jan 2017 | B1 |
| 9555315 | Aders | Jan 2017 | B2 |
| 9555580 | Dykstra et al. | Jan 2017 | B1 |
| 9557856 | Send et al. | Jan 2017 | B2 |
| 9566742 | Keating et al. | Feb 2017 | B2 |
| 9566758 | Cheung et al. | Feb 2017 | B2 |
| 9573193 | Buller et al. | Feb 2017 | B2 |
| 9573225 | Buller et al. | Feb 2017 | B2 |
| 9586290 | Buller et al. | Mar 2017 | B2 |
| 9595795 | Lane et al. | Mar 2017 | B2 |
| 9597843 | Stauffer et al. | Mar 2017 | B2 |
| 9600929 | Young et al. | Mar 2017 | B1 |
| 9609755 | Coull et al. | Mar 2017 | B2 |
| 9610737 | Johnson et al. | Apr 2017 | B2 |
| 9611667 | GangaRao et al. | Apr 2017 | B2 |
| 9616623 | Johnson et al. | Apr 2017 | B2 |
| 9626487 | Jung et al. | Apr 2017 | B2 |
| 9626489 | Nilsson | Apr 2017 | B2 |
| 9643361 | Liu | May 2017 | B2 |
| 9662840 | Buller et al. | May 2017 | B1 |
| 9665182 | Send et al. | May 2017 | B2 |
| 9672389 | Mosterman et al. | Jun 2017 | B1 |
| 9672550 | Apsley et al. | Jun 2017 | B2 |
| 9676145 | Buller et al. | Jun 2017 | B2 |
| 9684919 | Apsley et al. | Jun 2017 | B2 |
| 9688032 | Kia et al. | Jun 2017 | B2 |
| 9690286 | Hovsepian et al. | Jun 2017 | B2 |
| 9700966 | Kraft et al. | Jul 2017 | B2 |
| 9703896 | Zhang et al. | Jul 2017 | B2 |
| 9713903 | Paschkewitz et al. | Jul 2017 | B2 |
| 9718302 | Young et al. | Aug 2017 | B2 |
| 9718434 | Hector, Jr. et al. | Aug 2017 | B2 |
| 9724877 | Flitsch et al. | Aug 2017 | B2 |
| 9724881 | Johnson et al. | Aug 2017 | B2 |
| 9725178 | Wang | Aug 2017 | B2 |
| 9731730 | Stiles | Aug 2017 | B2 |
| 9731773 | Gami et al. | Aug 2017 | B2 |
| 9741954 | Bruder et al. | Aug 2017 | B2 |
| 9747352 | Karmarkar | Aug 2017 | B2 |
| 9764415 | Seufzer et al. | Sep 2017 | B2 |
| 9764520 | Johnson et al. | Sep 2017 | B2 |
| 9765226 | Dain | Sep 2017 | B2 |
| 9770760 | Liu | Sep 2017 | B2 |
| 9773393 | Velez | Sep 2017 | B2 |
| 9776234 | Schaafhausen et al. | Oct 2017 | B2 |
| 9782936 | Glunz et al. | Oct 2017 | B2 |
| 9783324 | Embler et al. | Oct 2017 | B2 |
| 9783977 | Alqasimi et al. | Oct 2017 | B2 |
| 9789548 | Golshany et al. | Oct 2017 | B2 |
| 9789922 | Dosenbach et al. | Oct 2017 | B2 |
| 9796137 | Zhang et al. | Oct 2017 | B2 |
| 9802108 | Aders | Oct 2017 | B2 |
| 9809977 | Carney et al. | Nov 2017 | B2 |
| 9817922 | Glunz et al. | Nov 2017 | B2 |
| 9818071 | Jung et al. | Nov 2017 | B2 |
| 9821339 | Paschkewitz et al. | Nov 2017 | B2 |
| 9821411 | Buller et al. | Nov 2017 | B2 |
| 9823143 | Twelves, Jr. et al. | Nov 2017 | B2 |
| 9829564 | Bruder et al. | Nov 2017 | B2 |
| 9846933 | Yuksel | Dec 2017 | B2 |
| 9854828 | Langeland | Jan 2018 | B2 |
| 9858604 | Apsley et al. | Jan 2018 | B2 |
| 9862833 | Hasegawa et al. | Jan 2018 | B2 |
| 9862834 | Hasegawa et al. | Jan 2018 | B2 |
| 9863885 | Zaretski et al. | Jan 2018 | B2 |
| 9870629 | Cardno et al. | Jan 2018 | B2 |
| 9879981 | Dehghan Niri et al. | Jan 2018 | B1 |
| 9884663 | Czinger et al. | Feb 2018 | B2 |
| 9898776 | Apsley et al. | Feb 2018 | B2 |
| 9914150 | Pettersson et al. | Mar 2018 | B2 |
| 9919360 | Buller et al. | Mar 2018 | B2 |
| 9931697 | Levin et al. | Apr 2018 | B2 |
| 9933031 | Bracamonte et al. | Apr 2018 | B2 |
| 9933092 | Sindelar | Apr 2018 | B2 |
| 9957031 | Golshany et al. | May 2018 | B2 |
| 9958535 | Send et al. | May 2018 | B2 |
| 9962767 | Buller et al. | May 2018 | B2 |
| 9963978 | Johnson et al. | May 2018 | B2 |
| 9971920 | Derakhshani et al. | May 2018 | B2 |
| 9976063 | Childers et al. | May 2018 | B2 |
| 9987792 | Flitsch et al. | Jun 2018 | B2 |
| 9988136 | Tiryaki et al. | Jun 2018 | B2 |
| 9989623 | Send et al. | Jun 2018 | B2 |
| 9990565 | Rhoads et al. | Jun 2018 | B2 |
| 9994339 | Colson et al. | Jun 2018 | B2 |
| 9996890 | Cinnamon et al. | Jun 2018 | B1 |
| 9996945 | Holzer et al. | Jun 2018 | B1 |
| 10002215 | Dowski et al. | Jun 2018 | B2 |
| 10006156 | Kirkpatrick | Jun 2018 | B2 |
| 10011089 | Lyons et al. | Jul 2018 | B2 |
| 10011685 | Childers et al. | Jul 2018 | B2 |
| 10012532 | Send et al. | Jul 2018 | B2 |
| 10013777 | Mariampillai et al. | Jul 2018 | B2 |
| 10015908 | Williams et al. | Jul 2018 | B2 |
| 10016852 | Broda | Jul 2018 | B2 |
| 10016942 | Mark et al. | Jul 2018 | B2 |
| 10017384 | Greer et al. | Jul 2018 | B1 |
| 10018576 | Herbsommer et al. | Jul 2018 | B2 |
| 10022792 | Srivas et al. | Jul 2018 | B2 |
| 10022912 | Kia et al. | Jul 2018 | B2 |
| 10027376 | Sankaran et al. | Jul 2018 | B2 |
| 10029415 | Swanson et al. | Jul 2018 | B2 |
| 10040239 | Brown, Jr. | Aug 2018 | B2 |
| 10046412 | Blackmore | Aug 2018 | B2 |
| 10048769 | Selker et al. | Aug 2018 | B2 |
| 10052712 | Blackmore | Aug 2018 | B2 |
| 10052820 | Kemmer et al. | Aug 2018 | B2 |
| 10055536 | Maes et al. | Aug 2018 | B2 |
| 10058764 | Aders | Aug 2018 | B2 |
| 10058920 | Buller et al. | Aug 2018 | B2 |
| 10061906 | Nilsson | Aug 2018 | B2 |
| 10065270 | Buller et al. | Sep 2018 | B2 |
| 10065361 | Susnjara et al. | Sep 2018 | B2 |
| 10065367 | Brown, Jr. | Sep 2018 | B2 |
| 10068316 | Holzer et al. | Sep 2018 | B1 |
| 10071422 | Buller et al. | Sep 2018 | B2 |
| 10071525 | Susnjara et al. | Sep 2018 | B2 |
| 10072179 | Drijfhout | Sep 2018 | B2 |
| 10074128 | Colson et al. | Sep 2018 | B2 |
| 10076875 | Mark et al. | Sep 2018 | B2 |
| 10076876 | Mark et al. | Sep 2018 | B2 |
| 10081140 | Paesano et al. | Sep 2018 | B2 |
| 10081431 | Seack et al. | Sep 2018 | B2 |
| 10086568 | Snyder et al. | Oct 2018 | B2 |
| 10087320 | Simmons et al. | Oct 2018 | B2 |
| 10087556 | Gallucci et al. | Oct 2018 | B2 |
| 10099427 | Mark et al. | Oct 2018 | B2 |
| 10100542 | GangaRao et al. | Oct 2018 | B2 |
| 10100890 | Bracamonte et al. | Oct 2018 | B2 |
| 10107344 | Bracamonte et al. | Oct 2018 | B2 |
| 10108766 | Druckman et al. | Oct 2018 | B2 |
| 10113600 | Bracamonte et al. | Oct 2018 | B2 |
| 10118347 | Stauffer et al. | Nov 2018 | B2 |
| 10118579 | Lakic | Nov 2018 | B2 |
| 10120078 | Bruder et al. | Nov 2018 | B2 |
| 10124546 | Johnson et al. | Nov 2018 | B2 |
| 10124570 | Evans et al. | Nov 2018 | B2 |
| 10137500 | Blackmore | Nov 2018 | B2 |
| 10138354 | Groos et al. | Nov 2018 | B2 |
| 10144126 | Krohne et al. | Dec 2018 | B2 |
| 10145110 | Carney et al. | Dec 2018 | B2 |
| 10151363 | Bracamonte et al. | Dec 2018 | B2 |
| 10152661 | Kieser | Dec 2018 | B2 |
| 10160278 | Coombs et al. | Dec 2018 | B2 |
| 10161021 | Lin et al. | Dec 2018 | B2 |
| 10166752 | Evans et al. | Jan 2019 | B2 |
| 10166753 | Evans et al. | Jan 2019 | B2 |
| 10171578 | Cook et al. | Jan 2019 | B1 |
| 10173255 | TenHouten et al. | Jan 2019 | B2 |
| 10173327 | Kraft et al. | Jan 2019 | B2 |
| 10178800 | Mahalingam et al. | Jan 2019 | B2 |
| 10179640 | Wilkerson | Jan 2019 | B2 |
| 10183330 | Buller et al. | Jan 2019 | B2 |
| 10183478 | Evans et al. | Jan 2019 | B2 |
| 10189187 | Keating et al. | Jan 2019 | B2 |
| 10189240 | Evans et al. | Jan 2019 | B2 |
| 10189241 | Evans et al. | Jan 2019 | B2 |
| 10189242 | Evans et al. | Jan 2019 | B2 |
| 10190424 | Johnson et al. | Jan 2019 | B2 |
| 10195693 | Buller et al. | Feb 2019 | B2 |
| 10196539 | Boonen et al. | Feb 2019 | B2 |
| 10197338 | Melsheimer | Feb 2019 | B2 |
| 10200677 | Trevor et al. | Feb 2019 | B2 |
| 10201932 | Flitsch et al. | Feb 2019 | B2 |
| 10201941 | Evans et al. | Feb 2019 | B2 |
| 10202673 | Lin et al. | Feb 2019 | B2 |
| 10204216 | Nejati et al. | Feb 2019 | B2 |
| 10207454 | Buller et al. | Feb 2019 | B2 |
| 10209065 | Estevo, Jr. et al. | Feb 2019 | B2 |
| 10210662 | Holzer et al. | Feb 2019 | B2 |
| 10213837 | Kondoh | Feb 2019 | B2 |
| 10214248 | Hall et al. | Feb 2019 | B2 |
| 10214252 | Schellekens et al. | Feb 2019 | B2 |
| 10214275 | Goehlich | Feb 2019 | B2 |
| 10220575 | Reznar | Mar 2019 | B2 |
| 10220881 | Tyan et al. | Mar 2019 | B2 |
| 10221530 | Driskell et al. | Mar 2019 | B2 |
| 10226900 | Nevins | Mar 2019 | B1 |
| 10232550 | Evans et al. | Mar 2019 | B2 |
| 10234342 | Moorlag et al. | Mar 2019 | B2 |
| 10237477 | Trevor et al. | Mar 2019 | B2 |
| 10252335 | Buller et al. | Apr 2019 | B2 |
| 10252336 | Buller et al. | Apr 2019 | B2 |
| 10254499 | Cohen et al. | Apr 2019 | B1 |
| 10257499 | Hintz et al. | Apr 2019 | B2 |
| 10259044 | Buller et al. | Apr 2019 | B2 |
| 10268181 | Nevins | Apr 2019 | B1 |
| 10269225 | Velez | Apr 2019 | B2 |
| 10272860 | Mohapatra et al. | Apr 2019 | B2 |
| 10272862 | Whitehead | Apr 2019 | B2 |
| 10275564 | Ridgeway et al. | Apr 2019 | B2 |
| 10279580 | Evans et al. | May 2019 | B2 |
| 10285219 | Fetfatsidis et al. | May 2019 | B2 |
| 10286452 | Buller et al. | May 2019 | B2 |
| 10286603 | Buller et al. | May 2019 | B2 |
| 10286961 | Hillebrecht et al. | May 2019 | B2 |
| 10289263 | Troy et al. | May 2019 | B2 |
| 10289875 | Singh et al. | May 2019 | B2 |
| 10291193 | Dandu et al. | May 2019 | B2 |
| 10294552 | Liu et al. | May 2019 | B2 |
| 10294982 | Gabrys et al. | May 2019 | B2 |
| 10295989 | Nevins | May 2019 | B1 |
| 10303159 | Czinger et al. | May 2019 | B2 |
| 10307824 | Kondoh | Jun 2019 | B2 |
| 10310197 | Droz et al. | Jun 2019 | B1 |
| 10313651 | Trevor et al. | Jun 2019 | B2 |
| 10315252 | Mendelsberg et al. | Jun 2019 | B2 |
| 10336050 | Susnjara | Jul 2019 | B2 |
| 10337542 | Hesslewood et al. | Jul 2019 | B2 |
| 10337952 | Bosetti et al. | Jul 2019 | B2 |
| 10339266 | Urick et al. | Jul 2019 | B2 |
| 10343330 | Evans et al. | Jul 2019 | B2 |
| 10343331 | McCall et al. | Jul 2019 | B2 |
| 10343355 | Evans et al. | Jul 2019 | B2 |
| 10343724 | Polewarczyk et al. | Jul 2019 | B2 |
| 10343725 | Martin et al. | Jul 2019 | B2 |
| 10350823 | Rolland et al. | Jul 2019 | B2 |
| 10356341 | Holzer et al. | Jul 2019 | B2 |
| 10356395 | Holzer et al. | Jul 2019 | B2 |
| 10357829 | Spink et al. | Jul 2019 | B2 |
| 10357957 | Buller et al. | Jul 2019 | B2 |
| 10359756 | Newell et al. | Jul 2019 | B2 |
| 10369629 | Mendelsberg et al. | Aug 2019 | B2 |
| 10382739 | Rusu et al. | Aug 2019 | B1 |
| 10384393 | Xu et al. | Aug 2019 | B2 |
| 10384416 | Cheung et al. | Aug 2019 | B2 |
| 10389410 | Brooks et al. | Aug 2019 | B2 |
| 10391710 | Mondesir | Aug 2019 | B2 |
| 10392097 | Pham et al. | Aug 2019 | B2 |
| 10392131 | Deck et al. | Aug 2019 | B2 |
| 10393315 | Tyan | Aug 2019 | B2 |
| 10400080 | Ramakrishnan et al. | Sep 2019 | B2 |
| 10401832 | Snyder et al. | Sep 2019 | B2 |
| 10403009 | Mariampillai et al. | Sep 2019 | B2 |
| 10406750 | Barton et al. | Sep 2019 | B2 |
| 10412283 | Send et al. | Sep 2019 | B2 |
| 10416095 | Herbsommer et al. | Sep 2019 | B2 |
| 10421496 | Swayne et al. | Sep 2019 | B2 |
| 10421863 | Hasegawa et al. | Sep 2019 | B2 |
| 10422478 | Leachman et al. | Sep 2019 | B2 |
| 10425793 | Sankaran et al. | Sep 2019 | B2 |
| 10427364 | Alves | Oct 2019 | B2 |
| 10429006 | Tyan et al. | Oct 2019 | B2 |
| 10434573 | Buller et al. | Oct 2019 | B2 |
| 10435185 | Divine et al. | Oct 2019 | B2 |
| 10435773 | Liu et al. | Oct 2019 | B2 |
| 10436038 | Buhler et al. | Oct 2019 | B2 |
| 10438407 | Pavanaskar et al. | Oct 2019 | B2 |
| 10440351 | Holzer et al. | Oct 2019 | B2 |
| 10442002 | Benthien et al. | Oct 2019 | B2 |
| 10442003 | Symeonidis et al. | Oct 2019 | B2 |
| 10449696 | Elgar et al. | Oct 2019 | B2 |
| 10449737 | Johnson et al. | Oct 2019 | B2 |
| 10461810 | Cook et al. | Oct 2019 | B2 |
| 20030006329 | Yanase | Jan 2003 | A1 |
| 20030226920 | Yanase | Dec 2003 | A1 |
| 20040177723 | Van Daam | Sep 2004 | A1 |
| 20050258288 | Dalziel | Nov 2005 | A1 |
| 20060108783 | Ni et al. | May 2006 | A1 |
| 20130153694 | Held | Jun 2013 | A1 |
| 20140277669 | Nardi et al. | Sep 2014 | A1 |
| 20160067716 | Blanchard et al. | Mar 2016 | A1 |
| 20170113344 | Schönberg | Apr 2017 | A1 |
| 20170341309 | Piepenbrock et al. | Nov 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 1996036455 | Nov 1996 | WO |
| 1996036525 | Nov 1996 | WO |
| 1996038260 | Dec 1996 | WO |
| 2003024641 | Mar 2003 | WO |
| 2004108343 | Dec 2004 | WO |
| 2005093773 | Oct 2005 | WO |
| 2007003375 | Jan 2007 | WO |
| 2007110235 | Oct 2007 | WO |
| 2007110236 | Oct 2007 | WO |
| 2008019847 | Feb 2008 | WO |
| 2007128586 | Jun 2008 | WO |
| 2008068314 | Jun 2008 | WO |
| 2008086994 | Jul 2008 | WO |
| 2008087024 | Jul 2008 | WO |
| 2008107130 | Sep 2008 | WO |
| 2008138503 | Nov 2008 | WO |
| 2008145396 | Dec 2008 | WO |
| 2009083609 | Jul 2009 | WO |
| 2009098285 | Aug 2009 | WO |
| 2009112520 | Sep 2009 | WO |
| 2009135938 | Nov 2009 | WO |
| 2009140977 | Nov 2009 | WO |
| 2010125057 | Nov 2010 | WO |
| 2010125058 | Nov 2010 | WO |
| 2010142703 | Dec 2010 | WO |
| 2011032533 | Mar 2011 | WO |
| 2014016437 | Jan 2014 | WO |
| 2014187720 | Nov 2014 | WO |
| 2014195340 | Dec 2014 | WO |
| 2015193331 | Dec 2015 | WO |
| 2016116414 | Jul 2016 | WO |
| 2017036461 | Mar 2017 | WO |
| 2019030248 | Feb 2019 | WO |
| 2019042504 | Mar 2019 | WO |
| 2019048010 | Mar 2019 | WO |
| 2019048498 | Mar 2019 | WO |
| 2019048680 | Mar 2019 | WO |
| 2019048682 | Mar 2019 | WO |
| Entry |
|---|
| US 9,202,136 B2, 12/2015, Schmidt et al. (withdrawn) |
| US 9,809,265 B2, 11/2017, Kinjo (withdrawn) |
| US 10,449,880 B2, 10/2019, Mizobata et al. (withdrawn) |
| International Search Report and the Written Opinion issued for corresponding International Application No. PCT/2021/51380, Feb. 14, 2022. |
| Number | Date | Country | |
|---|---|---|---|
| 20220088608 A1 | Mar 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| 63081806 | Sep 2020 | US |