Methods and systems using molecular glue for covalent bonding of solid substrates

Abstract
A method for bonding together two substrates includes providing a molecular glue including glue molecules, each of the glue molecules having at least two —O—Si or —O—Al moieties; reacting a surface of a first substrate with the molecular glue to attach the glue molecules to the surface of the first substrate by at least one of the —O—Si or —O—Al moieties; and reacting a surface of a second substrate with the molecular glue to attach the glue molecules to the surface of the second substrate by at least another one of the —O—Si or —O—Al moieties. The method can be used for a variety of applications including manufacturing a vapor cell.
Description
FIELD

The present disclosure is directed to the area of solid substrate bonding. The present disclosure is also directed to methods and systems for bonding solid substrates, as well as the articles or devices that include the bonded solid substrates.


BACKGROUND

In semiconductor processes, particularly for Microfabricated Electro-Mechanical Systems (MEMS), wafer substrates can be bonded together as part of the manufacture of devices. In many instances, the bonding is performed using anodic bonding (e.g., silicon to glass) or fusion bonding (glass-to-glass or sapphire-to-sapphire) techniques. The development of precision covalent binding techniques for sapphire and related materials, such as corundum, is useful for engineering advanced devices. Many conventional methods utilize bases, such as NaOH and KOH, under aqueous conditions which may not be suitable for at least some applications.


BRIEF SUMMARY

One embodiment is a method for bonding together two substrates. The method includes providing a molecular glue including glue molecules, each of the glue molecules having at least two —O—Si or —O—Al moieties; reacting a surface of a first substrate with the molecular glue to attach the glue molecules to the surface of the first substrate by at least one of the —O—Si or —O—Al moieties; and reacting a surface of a second substrate with the molecular glue to attach the glue molecules to the surface of the second substrate by at least another one of the —O—Si or —O—Al moieties.


In at least some embodiments, the glue molecules are selected from Al(OR)3 or Si(OR)4, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl. In at least some embodiments, each R is independently —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3.


In at least some embodiments, the glue molecules each contain two or more aluminum or silicon atoms. In at least some embodiments, the glue molecules are selected from Al(OR)2—O-L-O—Al(OR)2 or Si(OR)3—O-L-O—Si(OR)3, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl and L is a linker group selected from C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene or C6 to C30 arylene. In at least some embodiments, each R is independently —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3. In at least some embodiments, L is —(CH2)x— or benzylene, wherein x is an integer in the range of 1 to 15.


In at least some embodiments, at least one of the first substrate or the second substrate is an inorganic substrate. In at least some embodiments, at least one of the first substrate or the second substrate is a silicon, glass, aluminum oxide, corundum, ruby, or sapphire substrate. In at least some embodiments, both the first and second substrates are silicon, glass, aluminum oxide, corundum, ruby, or sapphire substrates.


In at least some embodiments, reacting the surface of the first substrate with the molecular glue includes disposing the molecular glue on the surface and applying heat or pressure or both heat and pressure to react the molecular glue with the surface. In at least some embodiments, reacting the surface of the first substrate with the molecular glue and reacting the surface of the second substrate with the molecular glue include disposing the molecular glue on the surface of the first substrate, positioning the second substrate on the first substrate, and applying heat or pressure or both heat and pressure to react the molecular glue with the surfaces of the first and second substrates.


Another embodiment is a method for forming a vapor cell. The method includes providing a molecular glue including glue molecules, each of the glue molecules having at least two —O—Si or —O—Al moieties; reacting a surface of a first vapor cell substrate with the molecular glue to attach the glue molecules to the surface of the first vapor cell substrate by at least one of the —O—Si or —O—Al moieties; and reacting a surface of a second vapor cell substrate with the molecular glue to attach the glue molecules to the surface of the second vapor cell substrate by at least another one of the —O—Si or —O—Al moieties.


In at least some embodiments, the first vapor cell substrate is a first cell wall and the second vapor cell substrate is a second cell wall. In at least some embodiments, the first vapor cell substrate is a cell wall and the second vapor cell substrate is an optical component of the vapor cell. In at least some embodiments, the first vapor cell substrate is a first optical component and the second vapor cell substrate is a second optical component. In at least some embodiments, the first optical component is selected from a collimating element, a quarter wave plate, or a lens element.


Yet another embodiment is a vapor cell that includes a first substrate forming either a first cell wall or a first optical component; a second substrate forming either a second cell wall or a second optical component; and a molecular glue disposed between the first and second substrates and bonding the first and second substrates together, wherein a molecular glue includes glue molecules, each of the glue molecules including at least two —O—Si or —O—Al moieties, wherein the —O—Si or —O—Al moieties form silicate or aluminate bonds to the first and second substrates.


In at least some embodiments, the glue molecules are selected from Al(OR)3 or Si(OR)4, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl. In at least some embodiments, the glue molecules are selected from Al(OR)2—O-L-O—Al(OR)2 or Si(OR)3—O-L-O—Si(OR)3, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl and L is a linker group selected from C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene or C6 to C30 arylene.





BRIEF DESCRIPTION OF THE DRAWINGS

Non-limiting and non-exhaustive embodiments of the present invention are described with reference to the following drawings. In the drawings, like reference numerals refer to like parts throughout the various figures unless otherwise specified.


For a better understanding of the present invention, reference will be made to the following Detailed Description, which is to be read in association with the accompanying drawings, wherein:



FIG. 1A is a schematic block diagram of one embodiment of a magnetometer, according to the invention;



FIG. 1B is a schematic block diagram of one embodiment of a magnetic field measurement system, according to the invention;



FIG. 2A is a schematic side view of an embodiment of a portion of a magnetometer, according to the invention;



FIG. 2B is a schematic side view of another embodiment of a portion of a magnetometer, according to the invention;



FIG. 3 is a schematic side view of one embodiment of an array of magnetometers for measuring magnetic fields generated in a brain of a user, according to the invention; and



FIG. 4 is a schematic side view of one embodiment of the array of magnetometers of FIG. 3, a signal source in a brain of a user, and a direction of the ambient background magnetic field.





DETAILED DESCRIPTION

The present disclosure is directed to the area of solid substrate bonding. The present disclosure is also directed to methods and systems for bonding solid substrates, as well as the articles or devices that include the bonded solid substrates.


In contrast to conventional anodic or fusion bonding techniques, a molecular glue can be used to bond two solid substrates together. As an example, the molecular glue, as described herein, is suitable for bonding two inorganic substrates, such as silicon, glass, or aluminum oxide substrates including corundum, ruby, and sapphire substrates. The two substrates may be made of the same material or may be made of different materials. For example, the molecular glue can be used to bond a sapphire substrate to another sapphire substrate or to a glass or silicon substrate. It will be recognized that the molecular glues described herein can be used with substrates other than sapphire, glass, or silicon.


Molecular glues include glue molecules that are a class of bi-functional linkers capable of covalently binding two components together. A molecular glue, as defined herein, includes glue molecules having at least one or two silicon or aluminum atoms, or any combination thereof. In at least some embodiments, the glue molecules have at least two bonding moieties such as —O—Si or —O—Al moieties. In at least some embodiments, each silicon or aluminum atom of a glue molecule is part of two or more of the —O—Si or —O—Al moieties. In at least some embodiments with two silicon or aluminum atoms, the silicon or aluminum atoms are coupled together by an organic linker. In at least some embodiments, the silicon and aluminum atoms form covalent silicate or aluminate bonds with the substrates.


In some embodiments, the glue molecules of a molecular glue are all the same. In other embodiments, a molecular glue may be composed of two or more different glue molecules.


Examples of glue molecules include, but at not limited to, Al(OR)3 (with three —O—Al moieties), Si(OR)4 (with four —O—Si moieties), Al(OR)2—O-L-O—Al(OR)2 (with four —O—Al moieties), or Si(OR)3—O-L-O—Si(OR)3 (with six —O—Al moieties). Each R is independently hydrogen or a C1 to C8 branched or unbranched alkyl which may be substituted or unsubstituted. The R groups can be substituted with one or more alkenyl, alkynyl, cycloalkyl (including cycloalkyl groups two or more rings), or aryl (including aryl groups with two or more fused or unfused rings) substituents. Preferably, any substituent of the R groups does not react with the substrate or substantially hinder the bonding of the glue molecule to the substrate. In at least some embodiments, the R groups of the glue molecules are the same. In other embodiments, the R groups of the glue molecules may be different. In at least some embodiments, the R groups are each independently hydrogen or an unsubstituted branched or unbranched alkyl such as, for example, —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3.


L is a linker group which, in at least some embodiments, is a C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene (including cycloalkylene with two or more rings) or C6 to Cao arylene (including arylene with two or more fused or unfused rings), any of which may be substituted or unsubstituted and may include one or more oxygen, nitrogen, or other heteroatoms. The L group can be substituted with one or more alkenyl, alkynyl, cycloalkyl, or aryl substituents. In at least some embodiments, L is —(CH2)x— or benzylene where x is an integer in the range of 1 to 15.


Examples of suitable compounds for molecular glues include, but are not limited to, the following:




embedded image



as well as 1,2-Bis(triethoxysilyl)ethane and 1,4-Bis(triethoxysilyl)benzene, where the R groups are defined above and may be, for example, independently H, —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3. In at least some embodiments, the R groups of the glue molecules are the same. In other embodiments, the R groups of the glue molecules may be different.


An example of sapphire bonding using a molecular glue (in this example, bis-aluminum glue molecules) is illustrated in the equations below:




embedded image


The following is an example of one embodiment of a method of bonding sapphire substrates using a molecular glue. The substrates are sapphire wafers. The wafers are prepared by piranha etch to remove any residual organic residue on the substrates. The wafers are then dried. The molecular glue is spin coated on an unpatterned surface of one of the sapphire wafers. The wafers are then dried again. The wafers are brought into contact with each other and flat aligned. Pressure and temperature are applied to react the molecular glue with the two wafers and bond the wafers together. In at least some embodiments, this step may be performed in a wafer bonder at a given pressure within equipment limits and, at least in some embodiments, temperature not to exceed 100 degrees Celsius.


Other methods of bonding substrates using the molecular glue can be utilized. For example, the molecular glue can be applied to the substrates using any suitable method including, but not limited to, spin coating, dip coating, spray coating, roll coating, knife coating, silk screening, or any other suitable coating method. The molecular glue can be reacted with the substrates using any suitable technique or combination of techniques including, but not limited to, thermal activation, pressure activation, light or ultraviolet activation, or the like or any combination thereof.


In at least some embodiments, the molecular glues and techniques described herein can provide a simple method for wafer bonding that does not require temperatures above 100 degrees Celsius. In at least some embodiments, these techniques can be less sensitive to surface roughness of the substrate that conventional bonding methods. In at least some embodiments, the covalent bonding reaction of the molecular glue to the substrate does not produce water as a side-product.


In at least some embodiments, the methods and techniques described herein can have one or more of the following advantages over conventional bonding methods: 1) more binding sites and stronger bonding, as the glue molecules are used as a limiting reagent; 2) low temperature bonding (for example, the bonding reaction occurs at a temperature of 100, 90, 80, 75, or 50 degrees Celsius or less); 3) water is not a reaction product (which may be beneficial for vapor cells that house alkali metals, as described below); 4) neutral, non-aqueous reaction conditions; 5) allows binding of two heterogeneous materials; and 6) linker length may be fine-tuned depending on, for example, substrate surface roughness.


The molecular glue described above can be utilized in a number of different applications. For example, the molecular glue can be utilized in manufacturing a vapor cell (or gas cell) or a magnetometer (such as an optically pumped magnetometer) that includes a vapor cell (or gas cell).



FIG. 1A is a schematic block diagram of one embodiment of a magnetometer 160 which includes a vapor cell 170 (also referred to as a “cell”) such as an alkali metal vapor cell; a heating device 176 to heat the cell 170; a light source 172; and a detector 174. In addition, coils of a magnetic field generator 162 can be positioned around the vapor cell 170. The vapor cell 170 can include, for example, an alkali metal vapor (for example, rubidium in natural abundance, isotopically enriched rubidium, potassium, or cesium, or any other suitable alkali metal such as lithium, sodium, or francium) and, optionally, one, or both, of a quenching gas (for example, nitrogen) and a buffer gas (for example, nitrogen, helium, neon, or argon). In some embodiments, the vapor cell may include the alkali metal atoms in a prevaporized form prior to heating to generate the vapor.


The light source 172 can include, for example, a laser to, respectively, optically pump the alkali metal atoms and probe the gas cell. The light source 172 may also include optics (such as lenses, waveplates, collimators, polarizers, and objects with reflective surfaces) for beam shaping and polarization control and for directing the light from the light source to the cell and detector. Examples of suitable light sources include, but are not limited to, a diode laser (such as a vertical-cavity surface-emitting laser (VCSEL), distributed Bragg reflector laser (DBR), or distributed feedback laser (DFB)), light-emitting diode (LED), lamp, or any other suitable light source. In some embodiments, the light source 172 may include two light sources: a pump light source and a probe light source.


The detector 174 can include, for example, an optical detector to measure the optical properties of the transmitted probe light field amplitude, phase, or polarization, as quantified through optical absorption and dispersion curves, spectrum, or polarization or the like or any combination thereof. Examples of suitable detectors include, but are not limited to, a photodiode, charge coupled device (CCD) array, CMOS array, camera, photodiode array, single photon avalanche diode (SPAD) array, avalanche photodiode (APD) array, or any other suitable optical sensor array that can measure the change in transmitted light at the optical wavelengths of interest.


The molecular glue described above can be used to manufacture a gas or vapor cell or to attach optical components (or other components) to a gas or vapor cell. FIG. 2A is an example of one embodiment of a vapor cell 270 with additional optical components integrated together into a structure 290. The vapor cell 270 can be made of any suitable material including, but not limited to, glass, sapphire, silicon, aluminum oxide, or the like or any combination thereof. In at least some embodiments, the molecular glue can be used to attach two or more cell wall substrates together to form the walls 273 of the vapor cell 270. In other embodiments, the vapor cell 270 can be made of single piece of material.


The vapor cell defines a cavity 271 that contains a vapor or vaporizable material, for example, an alkali metal such as lithium, sodium, potassium, rubidium, cerium, or francium. The cavity may also include a buffer gas, quenching gas, or any other suitable material for operation of the magnetometer, or any combination thereof.


The structure 290 can include one or more optical components for laser beam shaping, collimation, and collection that are integrated with, or attached to, the vapor cell 270 to form the structure 290. In some embodiments, the molecular glue described above can be used to attach one or more components to the vapor cell 270.


In the embodiment of FIG. 2A, the structure 290 includes a collimating element 278 (or other beam-shaping element) with, for example, a high conic-constant surface which can collimate the light, a quarter wave plate 280, a vapor cell 270, and a lens element 282. These elements are optical components of the vapor cell 270. Optical components can include, but are not limited to, collimating elements, lens elements, beam-shaping elements, polarizing elements, wave plates, beam splitters, prisms, reflective surfaces, filters, diffusers, gratings, or the like, or any combination thereof. The collimating element 278 and lens element 282 can take shapes other than those illustrated in FIG. 2A. In at least some embodiments, one or more of the collimating element 278, the quarter wave plate 280, or the lens element 282 (or any other optical component(s)) can be attached to the vapor cell 270 or each other using the molecular glue. Light directed from the light source 272 through the alkali metal vapor cell 270 passes through the lens element 282 which concentrates or redirects the light onto the detector 274.



FIG. 2B is another example of an embodiment of a vapor cell 270 with optical components, including a collimating element 278, two quarter wave plates 280a, 280b, and a lens element 282 forming structure 290. These elements are optical components of the vapor cell 270. The structure 290 in FIG. 2B has a symmetric arrangement of elements. In at least some embodiments, one or more of the collimating element 278, the two quarter wave plates 280a, 280b, or the lens element 282 (or any other optical component(s)) can be attached to the vapor cell 270 or each other using the molecular glue.


A magnetometer, such as magnetometer 160 of FIG. 1A, can be used as part of a magnetic field measurement system. FIG. 1B is a block diagram of components of one embodiment of a magnetic field measurement system 140. The system 140 can include a computing device 150 or any other similar device that includes a processor 152, a memory 154, a display 156, an input device 158, one or more magnetometers 160 (for example, an array of magnetometers) which can be optically pumped magnetometers (OPMs), one or more magnetic field generators 162, and, optionally, one or more other sensors 164 (e.g., non-magnetic field sensors). The system 140 and its use and operation will be described herein with respect to the measurement of neural signals arising from one or more magnetic field sources of interest in the brain of a user as an example. It will be understood, however, that the system can be adapted and used to measure signals from other magnetic field sources of interest including, but not limited to, other neural signals, other biological signals, as well as non-biological signals.


The computing device 150 can be a computer, tablet, mobile device, field programmable gate array (FPGA), microcontroller, or any other suitable device for processing information or instructions. The computing device 150 can be local to the user or can include components that are non-local to the user including one or both of the processor 152 or memory 154 (or portions thereof). For example, in at least some embodiments, the user may operate a terminal that is connected to a non-local computing device. In other embodiments, the memory 154 can be non-local to the user.


The computing device 150 can utilize any suitable processor 152 including one or more hardware processors that may be local to the user or non-local to the user or other components of the computing device. The processor 152 is configured to execute instructions stored in the memory 154.


Any suitable memory 154 can be used for the computing device 150. The memory 154 illustrates a type of computer-readable media, namely computer-readable storage media. Computer-readable storage media may include, but is not limited to, volatile, nonvolatile, non-transitory, removable, and non-removable media implemented in any method or technology for storage of information, such as computer readable instructions, data structures, program modules, or other data. Examples of computer-readable storage media include RAM, ROM, EEPROM, flash memory, or other memory technology, CD-ROM, digital versatile disks (“DVD”) or other optical storage, magnetic cassettes, magnetic tape, magnetic disk storage or other magnetic storage devices, or any other medium which can be used to store the desired information and which can be accessed by a computing device.


Communication methods provide another type of computer readable media; namely communication media. Communication media typically embodies computer-readable instructions, data structures, program modules, or other data in a modulated data signal such as a carrier wave, data signal, or other transport mechanism and include any information delivery media. The terms “modulated data signal,” and “carrier-wave signal” includes a signal that has one or more of its characteristics set or changed in such a manner as to encode information, instructions, data, and the like, in the signal. By way of example, communication media includes wired media such as twisted pair, coaxial cable, fiber optics, wave guides, and other wired media and wireless media such as acoustic, RF, infrared, and other wireless media.


The display 156 can be any suitable display device, such as a monitor, screen, or the like, and can include a printer. In some embodiments, the display is optional. In some embodiments, the display 156 may be integrated into a single unit with the computing device 150, such as a tablet, smart phone, or smart watch. In at least some embodiments, the display is not local to the user. The input device 158 can be, for example, a keyboard, mouse, touch screen, track ball, joystick, voice recognition system, or any combination thereof, or the like. In at least some embodiments, the input device is not local to the user.


The magnetic field generator(s) 162 can be, for example, Helmholtz coils, solenoid coils, planar coils, saddle coils, electromagnets, permanent magnets, or any other suitable arrangement for generating a magnetic field. The optional sensor(s) 164 can include, but are not limited to, one or more position sensors, orientation sensors, accelerometers, image recorders, or the like or any combination thereof.


The one or more magnetometers 160 can be any suitable magnetometer including, but not limited to, any suitable optically pumped magnetometer (e.g., vector magnetometers). Arrays of magnetometers are described in more detail herein. In at least some embodiments, at least one of the one or more magnetometers (or all of the magnetometers) of the system is arranged for operation in a spin exchange relaxation free (SERF) mode.



FIG. 3 illustrates one embodiment of a magnetic field measurement system shown with several magnetometers, 160a, 160b, 160c placed on or near a user's head 100 to measure neural activity. FIG. 4 illustrates vector magnetic fields (e.g., signals) that might be generated by the neural activity 401 on each of the magnetometers. For each of the magnetometers 160a, 160b, 106c, the magnetic field vector could be different in both direction and amplitude. The ambient background magnetic field 402 (including, for example, the Earth's magnetic field) is about 108 times larger than magnetic field from the neural activity and is not shown to scale. Examples of magnetic field measurement systems are described in U.S. patent application Ser. Nos. 16/213,980; 16/405,382; 16/418,478; 16/418,500; 16/428,871; 16/456,975; and 16/457,655, and U.S. Provisional Patent Applications Ser. Nos. 62/689,696; 62/699,596; 62/719,471; 62/719,475; 62/719,928; 62/723,933; 62/732,327; 62/732,791; 62/741,777; 62/743,343; 62/747,924; 62/745,144; 62/752,067; 62/776,895; 62/781,418; 62/796,958; 62/798,209; 62/798,330; 62/804,539; 62/826,045; 62/827,390; 62/836,421; 62/837,574; 62/837,587; 62/842,818; 62/855,820; 62/858,636; 62/860,001; 62/865,049; 62/873,694; 62/874,887; 62/883,399; 62/883,406; 62/888,858; 62/895,197; and 62/896,929, all of which are incorporated herein by reference in their entireties.


The above specification provides a description of the invention and its manufacture and use. Since many embodiments of the invention can be made without departing from the spirit and scope of the invention, the invention also resides in the claims hereinafter appended.

Claims
  • 1. A method for bonding together two substrates, the method comprising: providing a molecular glue comprising glue molecules, each of the glue molecules having at least two —O—Si or —O—Al moieties, wherein the glue molecules are selected from Al(OR)2—O-L-O—Al(OR)2 or Si(OR)3—O-L-O—Si(OR)3, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl and L is a linker group selected from C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene or C6 to C30 arylene;reacting a surface of a first substrate with the molecular glue to attach the glue molecules to the surface of the first substrate by at least one of the —O—Si or —O—Al moieties; andreacting a surface of a second substrate with the molecular glue to attach the glue molecules to the surface of the second substrate by at least another one of the —O—Si or —O—Al moieties.
  • 2. The method of claim 1, wherein each R is independently —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3.
  • 3. The method of claim 1, wherein L is —(CH2)x- or benzylene, wherein x is an integer in the range of 1 to 15.
  • 4. The method of claim 1, wherein at least one of the first substrate or the second substrate is an inorganic substrate.
  • 5. The method of claim 4, wherein at least one of the first substrate or the second substrate is a silicon, glass, aluminum oxide, corundum, ruby, or sapphire substrate.
  • 6. The method of claim 5, wherein both the first and second substrates are silicon, glass, aluminum oxide, corundum, ruby, or sapphire substrates.
  • 7. The method of claim 1, wherein reacting the surface of the first substrate with the molecular glue comprises disposing the molecular glue on the surface and applying heat or pressure or both heat and pressure to react the molecular glue with the surface.
  • 8. The method of claim 1, wherein reacting the surface of the first substrate with the molecular glue and reacting the surface of the second substrate with the molecular glue comprise disposing the molecular glue on the surface of the first substrate, positioning the second substrate on the first substrate, and applying heat or pressure or both heat and pressure to react the molecular glue with the surfaces of the first and second substrates.
  • 9. A method for forming a vapor cell, the method comprising: providing a molecular glue comprising glue molecules, each of the glue molecules having at least two —O—Si or —O—Al moieties;reacting a surface of a first vapor cell substrate with the molecular glue to attach the glue molecules to the surface of the first vapor cell substrate by at least one of the —O—Si or —O—Al moieties; andreacting a surface of a second vapor cell substrate with the molecular glue to attach the glue molecules to the surface of the second vapor cell substrate by at least another one of the —O—Si or —O—Al moieties.
  • 10. The method of claim 9, wherein the first vapor cell substrate is a first cell wall and the second vapor cell substrate is a second cell wall.
  • 11. The method of claim 9, wherein the first vapor cell substrate is a cell wall and the second vapor cell substrate is an optical component of the vapor cell.
  • 12. The method of claim 9, wherein the first vapor cell substrate is a first optical component and the second vapor cell substrate is a second optical component.
  • 13. The method of claim 12, wherein the first optical component is selected from a collimating element, a quarter wave plate, or a lens element.
  • 14. A vapor cell, comprising: a first substrate forming either a first cell wall or a first optical component;a second substrate forming either a second cell wall or a second optical component; anda molecular glue disposed between the first and second substrates and bonding the first and second substrates together, wherein a molecular glue comprises glue molecules, each of the glue molecules comprising at least two —O—Si or —O—Al moieties, wherein the —O—Si or —O—Al moieties form silicate or aluminate bonds to the first and second substrates.
  • 15. The vapor cell of claim 14, wherein the glue molecules are selected from Al(OR)3 or Si(OR)4, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl.
  • 16. The vapor cell of claim 14, wherein the glue molecules are selected from Al(OR)2—O-L-O—Al(OR)2 or Si(OR)3—O-L-O—Si(OR)3, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl and L is a linker group selected from C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene or C6 to C30 arylene.
  • 17. The method of claim 9, wherein the glue molecules are selected from Al(OR)3 or Si(OR)4, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl.
  • 18. The method of claim 17, wherein each R is independently —CH3, —CH2CH3, —CH2CH2CH3, —CH(CH3)2, —CH2CH2CH2CH3, —CH2CH(CH3)2, —CH(CH3)CH2CH3, or —C(CH3)3.
  • 19. The method of claim 9, wherein the glue molecules are selected from Al(OR)2—O-L-O—Al(OR)2 or Si(OR)3—O-L-O—Si(OR)3, wherein each R is independently hydrogen or C1 to C8 branched or unbranched alkyl and L is a linker group selected from C1 to C30 branched or unbranched alkylene or C6 to C30 cycloalkylene or C6 to C30 arylene.
  • 20. The method of claim 9, wherein both the first and second vapor cell substrates are silicon, glass, aluminum oxide, corundum, ruby, or sapphire substrates.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Applications Ser. Nos. 62/747,924, filed Oct. 19, 2018, and 62/798,330, filed Jan. 29, 2019, which are incorporated herein by reference in their entireties.

US Referenced Citations (114)
Number Name Date Kind
4951674 Zanakis et al. Aug 1990 A
5030699 Motoyama Jul 1991 A
5181417 Nishida Jan 1993 A
5189368 Chase Feb 1993 A
5192921 Chantry et al. Mar 1993 A
5254947 Chaillout et al. Oct 1993 A
5309095 Ahonen et al. May 1994 A
5442289 Dilorio et al. Aug 1995 A
5444372 Wikswo, Jr. et al. Aug 1995 A
5471985 Warden Dec 1995 A
5506200 Hirschkoff et al. Apr 1996 A
5526811 Lypchuk Jun 1996 A
5713354 Warden Feb 1998 A
6144872 Graetz Nov 2000 A
6339328 Keene et al. Jan 2002 B1
6472869 Upschulte et al. Oct 2002 B1
6665553 Kandori et al. Dec 2003 B2
6806784 Hollberg et al. Oct 2004 B2
6831522 Kitching et al. Dec 2004 B2
7038450 Romalis et al. May 2006 B2
7102451 Happer et al. Sep 2006 B2
7145333 Romalis et al. Dec 2006 B2
7521928 Romalis Apr 2009 B2
7656154 Kawabata et al. Feb 2010 B2
7826065 Okandan et al. Nov 2010 B1
7872473 Kitching et al. Jan 2011 B2
7994783 Ledbetter et al. Aug 2011 B2
8054074 Ichihara et al. Nov 2011 B2
8212556 Schwindt et al. Jul 2012 B1
8258884 Borwick, III et al. Sep 2012 B2
8319156 Borwick, III et al. Nov 2012 B2
8334690 Kitching et al. Dec 2012 B2
8373413 Sugioka Feb 2013 B2
8405389 Sugioka et al. Mar 2013 B2
8587304 Budker et al. Nov 2013 B2
8836327 French et al. Sep 2014 B2
8906470 Overstolz et al. Dec 2014 B2
8941377 Mizutani et al. Jan 2015 B2
9095266 Fu Aug 2015 B1
9116201 Shah et al. Aug 2015 B2
9140590 Waters et al. Sep 2015 B2
9140657 Ledbetter et al. Sep 2015 B2
9169974 Parsa et al. Oct 2015 B2
9244137 Kobayashi et al. Jan 2016 B2
9291508 Biedermann et al. Mar 2016 B1
9343447 Parsa et al. Mar 2016 B2
9366735 Kawabata et al. Jun 2016 B2
9383419 Mizutani et al. Jul 2016 B2
9395425 Diamond et al. Jul 2016 B2
9417293 Schaffer et al. Aug 2016 B2
9429918 Parsa et al. Aug 2016 B2
9568565 Parsa et al. Feb 2017 B2
9575144 Kornack et al. Feb 2017 B2
9601225 Parsa et al. Mar 2017 B2
9638768 Foley et al. May 2017 B2
9639062 Dyer et al. May 2017 B2
9677905 Waters et al. Jun 2017 B2
9726626 Smith et al. Aug 2017 B2
9726733 Smith et al. Aug 2017 B2
9791536 Alem et al. Oct 2017 B1
9829544 Bulatowicz Nov 2017 B2
9846054 Waters et al. Dec 2017 B2
9851418 Wolf et al. Dec 2017 B2
9869731 Hovde et al. Jan 2018 B1
9915711 Kornack et al. Mar 2018 B2
9927501 Kim et al. Mar 2018 B2
9948314 Dyer et al. Apr 2018 B2
9964609 Ichihara et al. May 2018 B2
9964610 Shah et al. May 2018 B2
9970999 Larsen et al. May 2018 B2
10024929 Parsa et al. Jul 2018 B2
10088535 Shah Oct 2018 B1
10162016 Gabrys et al. Dec 2018 B2
20040232912 Tsukamoto et al. Nov 2004 A1
20050007118 Kitching et al. Jan 2005 A1
20050046851 Riley, Jr. et al. Mar 2005 A1
20050206377 Romalis et al. Sep 2005 A1
20060142146 Gao Jun 2006 A1
20070120563 Kawabata et al. May 2007 A1
20070167723 Park et al. Jul 2007 A1
20070205767 Xu et al. Sep 2007 A1
20090079426 Anderson Mar 2009 A1
20090101806 Masuda Apr 2009 A1
20100219820 Skidmore et al. Sep 2010 A1
20110062956 Edelstein et al. Mar 2011 A1
20120112749 Budker et al. May 2012 A1
20130082700 Mizutani et al. Apr 2013 A1
20130082701 Mizutani et al. Apr 2013 A1
20130265042 Kawabata et al. Oct 2013 A1
20140306700 Kamada et al. Oct 2014 A1
20140354275 Sheng et al. Dec 2014 A1
20150022200 Ichihara et al. Jan 2015 A1
20150054504 Ichihara et al. Feb 2015 A1
20150378316 Parsa et al. Dec 2015 A1
20160061913 Kobayashi et al. Mar 2016 A1
20160116553 Kim et al. Apr 2016 A1
20160223627 Shah et al. Aug 2016 A1
20160313417 Kawabata et al. Oct 2016 A1
20170023653 Kobayashi et al. Jan 2017 A1
20170023654 Kobayashi et al. Jan 2017 A1
20170199138 Parsa et al. Jul 2017 A1
20170261564 Gabrys et al. Sep 2017 A1
20170331485 Gobet et al. Nov 2017 A1
20170343617 Manickam et al. Nov 2017 A1
20170343695 Stetson et al. Nov 2017 A1
20180003777 Sorenson et al. Jan 2018 A1
20180038921 Parsa et al. Feb 2018 A1
20180100749 Waters et al. Apr 2018 A1
20180128885 Parsa et al. May 2018 A1
20180156875 Herbsommer et al. Jun 2018 A1
20180219353 Shah Aug 2018 A1
20180238974 Shah et al. Aug 2018 A1
20180313908 Knappe et al. Nov 2018 A1
20180313913 DeNatale et al. Nov 2018 A1
Foreign Referenced Citations (12)
Number Date Country
104730484 Jun 2015 CN
107562188 Jan 2018 CN
2738627 Jun 2014 EP
2385028 Oct 2015 EP
3037836 Sep 2017 EP
2004-307655 Nov 2004 JP
2009-299042 Dec 2009 JP
2016109665 Jun 2016 JP
2018004462 Jan 2018 JP
2005081794 Sep 2005 WO
2014031985 Feb 2014 WO
2017095998 Jun 2017 WO
Non-Patent Literature Citations (67)
Entry
Allred, J. C., Lyman, R. N., Kornack, T. W., & Romalis, M. V. (2002). High-sensitivity atomic magnetometer unaffected by spin-exchange relaxation. Physical review letters, 89(13), 130801.
Balabas et al. Polarized alkali vapor with minute-long transverse spin-relaxation time, Phys. Rev. Lett. 105, 070801—Published Aug. 12, 2010.
Barbieri, F., Trauchessec, V., Caruso, L., Trejo-Rosillo, J., Telenczuk, B., Paul, E., . . . & Ouanounou, G. (2016). Local recording of biological magnetic fields using Giant Magneto Resistance-based micro-probes. Scientific reports, 6, 39330.
Dmitry Budker and Michael Romalis, “Optical Magnetometry,” Nature Physics, 2008, https://arxiv.org/abs/physics/0611246v1.
Anthony P. Colombo, Tony R. Carter, Amir Borna, Yuan-Yu Jau, Cort N. Johnson, Amber L. Dagel, and Peter D. D. Schwindt, “Four-channel optically pumped atomic magnetometer for magnetoencephalography,” Opt. Express 24, 15403-15416 (2016).
Dang, H.B. & Maloof, A.C. & Romalis, Michael. (2009). Ultra-high sensitivity magnetic field and magnetization measurements with an atomic magnetometer. Applied Physics Letters. 97. 10.1063/1.3491215.
Donley, E.A. & Hodby, E & Hollberg, L & Kitching, J. (2007). Demonstration of high-performance compact magnetic shields for chip-scale atomic devices. The Review of scientific instruments. 78. 083102.
Hämäläinen, Matti & Hari, Riitta & Ilmoniemi, Risto J. & Knuutila, Jukka & Lounasmaa, Olli V. Apr. 1993. Magnetoencephalograph—theory, instrumentation, and applications to noninvasive studies of the working human brain. Reviews of Modern Physics. vol. 65, Issue 2. 413-497.
Hunter, D. and Piccolomo, S. and Pritchard, J. D. and Brockie, N. L. and Dyer, T. E. and Riis, E. (2018) Free-induction-decay magnetometer based on a microfabricated Cs vapor cell. Physical Review Applied (10).ISSN 2331-7019.
Jiménez-Martínez, R., Griffith, W. C., Wang, Y. J., Knappe, S., Kitching, J., Smith, K., & Prouty, M. D. (2010). Sensitivity comparison of Mx and frequency-modulated bell-bloom Cs magnetometers in a microfabricated cell. IEEE Transactions on Instrumentation and Measurement, 59(2), 372-378.
Kiwoong Kim, Samo Begus, Hui Xia, Seung-Kyun Lee, Vojko Jazbinsek, Zvonko Trontelj, Michael V. Romalis, Multi-channel atomic magnetometer for magnetoencephalography: A configuration study. NeuroImage 89 (2014) 143-151 http://physics.princeton.edu/romalis/papers/Kim_2014.pdf.
Knappe, Svenja & Sander, Tilmann & Trahms, Lutz. (2012). Optically-Pumped Magnetometers for MEG. Magnetoencephalography: From Signals to Dynamic Cortical Networks. 993-999. 10.1007/978-3-642-33045-2_49.
Kominis, I.K., Kornack, T.W., Allred, J.C. and Romalis, M.V., 2003. A subfemtotesla multichannel atomic magnetometer. Nature, 422(6932), p. 596.
Korth, H., K. Strohbehn, F. Tejada, A. G. Andreou, J. Kitching, S. Knappe, S. J. Lehtonen, S. M. London, and M. Kafel (2016), Miniature atomic scalarmagnetometer for space based on the rubidium isotope 87Rb, J. Geophys. Res. Space Physics, 121, 7870-7880, doi:10.1002/2016JA022389.
Lenz, J. and Edelstein, S., 2006. Magnetic sensors and their applications. IEEE Sensors journal, 6(3), pp. 631-649.
Li, S & Vachaspati, Pranjal & Sheng, Dehong & Dural, Nezih & Romalis, Michael. (2011). Optical rotation in excess of 100 rad generated by Rb vapor in a multipass cell. Phys. Rev. A. 84. 10.1103/PhysRevA.84.061403.
Maze, J. R., Stanwix, P. L., Hodges, J. S., Hong, S., Taylor, J. M., Cappellaro, P., . . . & Yacoby A. (2008). Nanoscale magnetic sensing with an individual electronic spin in diamond. Nature, 455(7213), 644.
Sander TH, Preusser J, Mhaskar R, Kitching J, Trahms L, Knappe S. Magnetoencephalography with a chip-scale atomic magnetometer. Biomed Opt Express. 2012;3(5):981-90.
J. Seltzer, S & Romalis, Michael. (2010). High-temperature alkali vapor cells with antirelaxation surface coatings. Journal of Applied Physics. 106. 114905-114905. 10.1063/1.3236649.
Seltżer, S. J., and Romalis, M.V., “Unshielded three-axis vector operation of a spin-exchange-relaxation-free atomic magnetometer.” Applied physics letters 85.20 (2004): 4804-4806.
Sheng, Dang & R. Perry, Abigail & Krzyzewski, Sean & Geller, Shawn & Kitching, John & Knappe, Svenja. (2017). A microfabricated optically-pumped magnetic gradiometer. Applied Physics Letters. 110. 10.1063/1.4974349.
Sheng, Dehong & Li, S & Dural, Nezih & Romalis, Michael. (2013). Subfemtotesla Scalar Atomic Magnetometry Using Multipass Cells. Physical review letters. 110. 160802. 10.1103/PhysRevLett.110.160802.
Volkmar Schultze et al. An Optically Pumped Magnetometer Working in the Light-Shift Dispersed Mz Mode, Sensors 2017, 17, 561; doi:10.3390/s17030561.
Fang, J. and Qin, J., 2012. In situ triaxial magnetic field compensation for the spin-exchange-relaxation-free atomic magnetometer. Review of Scientific Instruments, 83(10), p. 103104.
Joon Lee, Hyun & Shim, Jeong & Moon, Han Seb & Kim, Kiwoong. (2014). Flat-response spin-exchange relaxation free atomic magnetometer under negative feedback. Optics Express. 22. 10.1364/OE.22.019887.
Griffith, Clark & Jimenez-Martinez, Ricardo & Shah, Vishal & Knappe, Svenja & Kitching, John. (2009). Miniature atomic magnetometer integrated with flux concentrators. Applied Physics Letters—Appl Phys Lett. 94. 10.1063/1.3056152.
Lee, S.-K & Romalis, Michael. (2008). Calculation of Magnetic Field Noise from High-Permeability Magnetic Shields and Conducting Objects with Simple Geometry. Journal of Applied Physics. 103. 084904-084904. 10.1063/1.2885711.
Vovrosh, Jamie & Voulazeris, Georgios & Petrov, Plamen & Zou, Ji & Gaber Beshay, Youssef & Benn, Laura & Woolger, David & Attallah, Moataz & Boyer, Vincent & Bongs, Kai & Holynski, Michael. (2018). Additive manufacturing of magnetic shielding and ultra-high vacuum flange for cold atom sensors. Scientific Reports. 8. 10.1038/s41598-018-20352-x.
Kim, Young Jin & Savukov, I. (2016). Ultra-sensitive Magnetic Microscopy with an Optically Pumped Magnetometer, Scientific Reports. 6. 24773. 10.1038/srep24773.
Navau, Carles & Prat-Camps, Jordi & Sanchez, Alvaro. (2012). Magnetic Energy Harvesting and Concentration at a Distance by Transformation Optics. Physical review letters. 109. 263903. 10.1103/PhysRevLett.109.263903.
Orang Alem, Rahul Mhaskar, Ricardo Jiménez-Martínez, Dong Sheng, John LeBlanc, Lutz Trahms. Tilmann Sander, John Kitching, and Svenja Knappe, “Magnetic field imaging with microfabricated optically-pumped magnetometers,” Opt. Express 25, 7849-7858 (2017).
Slocum et al., Self-Calibrating Vector Magnetometer for Space, https://esto.nasa.gov/conferences/estc-2002/Papers/B3P4(Slocum).pdf.
Dupont-Roc, J & Haroche, S & Cohen-Tannoudji, C. (1969). Detection of very weak magnetic fields (10-9gauss) by 87Rb zero-field level crossing resonances. Physics Letters A—Phys Lett A. 28. 638-639. 10.1016/0375-9601(69) 90480-0.
J. A. Neuman, P. Wang, and A. Gallagher, Robust high-temperature sapphire cell for metal vapors, Review of Scientific Instruments, vol. 66, Issue 4, Apr. 1995, pp. 3021-3023.
Borna, Amir, et al. “A 20-channel magnetoencephalography system based on optically pumped magnetometers.” Physics in Medicine & Biology 62.23 (2017): 8909.
R. E. Slocum & L. J. Ryan, Design and operation of the minature vector laser magnetometer, Nasa Earth Science Technology Conference 2003.
Schoenmaker, Jeroen & R Pirota, K & Teixeira, Julio. (2013). Magnetic flux amplification by Lenz lenses. The Review of scientific instruments. 84. 085120. 10.1063/1.4819234.
Hu, Yanhui & Hu, Zhaohul & Liu, Xuejing & Li, Yang & Zhang, Ji & Yao, Han & Ding, Ming. (2017). Reduction of far off-resonance laser frequency drifts based on the second harmonic of electro-optic modulator detection in the optically pumped magnetometer. Applied Optics. 56. 5927. 10.1364/AO.56.005927.
Masuda, Y & Ino, T & Skoy, Vadim & Jones, G.L. (2005). 3He polarization via optical pumping in a birefringent cell. Applied Physics Letters. 87. 10.1063/1.2008370.
A.B. Baranga et al., An atomic magnetometer for brain activity imaging, Real Time Conference 2005. 14th IEEE—NPSS. pp. 417-418.
Larry J. Ryan, Robert E. Slocum, and Robert B. Steves, Miniature Vector Laser Magnetometer Measurements of Earth's Field, May 10, 2004, 4 pgs.
Lorenz, V. O., Dai, X., Green, H., Asnicar, T. R., & Cundiff, S. T. (2008). High-density, high-temperature alkali vapor cell. Review of Scientific Instruments, 79(12), 4 pages.
F. Jackson Kimball, D & Dudley, J & Li, Y & Thulasi, Swecha & Pustelny, Szymon & Budker, Dmitry & Zolotarev, Max. (2016). Magnetic shielding and exotic spin-dependent interactions. Physical Review D. 94. 10.1103/PhysRevD.94.082005.
Huang, Haichao, et al. “Single-beam three-axis atomic magnetometer.” Applied Physics Letters 109.6 (2016): 062404. (Year: 2016).
Scott Jeffrey Seltzer: “Developments in alkali-metal atomic magnetometry”, Nov. 1, 2008 (Nov. 1, 2008), XP055616618, ISBN: 978-0-549-93355-7 Retrieved from the Internet: URL:http://physics.princeton.edu/atomic/romalis/papers/Seltzer%20Thesis.pdf [retrieved on Aug. 29, 2019] pp. 148-159.
Haifeng Dong et al: “Atomic-Signal-Based Zero-Field Finding Technique for Unshielded Atomic Vector Magnetometer”, IEEE Sensors Journal, IEEE Service Center, New York, NY, US, vol. 13, No. 1, Jan. 1, 2013 (Jan. 1, 2013), pp. 186-189.
S. Knappe, V. Shah, P. Schwindt, L. Hollberg, J. Kitching, L. Liew, and J. Moreland. A microfabricated atomic clock. Applied Physics Letters, 85(9):1460-1462, 2004.
L. Nieradko, C. Gorecki, A. Douahi, V. Giordano, J.-C. Beugnot, J. Dziuban, and M. Moraja. New approach of fabrication and dispensing of micromachined cesium vapor cell. Journal of Micro/Nanolithography, MEMS, and MOEMS, 7(3):033013, 2008.
V. Maurice, J. Rutkowski, E. Kroemer, S. Bargiel, N. Passilly, R. Boudot, C. Gorecki, L. Mauri, and M. Moraja. Microfabricated vapor cells filled with a cesium dispensing paste for miniature atomic clocks. Applied Physics Letters, 110(16):164103, 2017.
V. Maurice, J. Rutkowski, E. Kroemer, S. Bargiel, N. Passilly, R. Boudot, R. Chutani, S. Galliou, and C. Gorecki. Microfabricated vapor cells for miniature atomic clocks based on post-sealing activated cesium dispensers. In International Frequency Control Symposium (IFCS), Joint with the 31st European Frequency and Time Forum (EFTF), pp. 636-637, Besançon, France, 2017.
F. Gong, Y. Jau, K. Jensen, and W. Happer. Electrolytic fabrication of atomic clock cells. Review of Scientific Instruments, 77(7):711-714, 2006.
M. Bick, H. Prinz, and A. Steinmetz. Ullmann's Encyclopedia of Industrial Chemistry, chapter Cesium and Cesium Compounds. Wiley Online Library, 2000.
L. Liew, S. Knappe, J. Moreland, H. Robinson, L. Hollberg, and J. Kitching. Microfabricated alkali atom vapor cells. Applied Physics Letters, 84(14):2694-2696, 2004.
L. Liew, J. Moreland, and V. Gerginov. Wafer-level filling of microfabricated atomic vapor cells based on thin-film deposition and photolysis of cesium azide. Applied Physics Letters, 90(11):114106, 2007.
S. Woetzel, V. Schultze, R. IJsselsteijn, T. Schulz, S. Anders, R. Stolz, and H. Meyer. Microfabricated atomic vapor cell arrays for magnetic field measurements. Review of Scientific Instruments, 82(3):033111, 2011.
W. Wei, J. Shang, W. Kuai, S. Qin, T. Wang, and J. Chen. Fabrication of wafer-level spherical Rb vapor cells for miniaturized atomic clocks by a chemical foaming process. In 13th International Conference on Electronic Packaging Technology & High Density Packaging (ICEPTHDP), pp. 1639-1641, Guilin, Guangxi, China, 2012.
Larry J. Ryan, Robert E. Slocum, and Robert B. Steves; Miniature Vector Laser Magnetometer Measurements of Earth's Field; Polatomic, Inc.; May 10, 2004; 4 pages.
S. Theppakuttai, D. Shao, and S. Chen. Localized Laser Transmission Bonding for Microsystem Fabrication and Packaging. Journal of Manufacturing Processes, 6(1):24-31, 2004.
Evangelina Pensa, Emiliano Cortés, Gastón Corthey, Pilar Carro, Carolina Vericat, Mariano H. Fonticelli, Guillermo Benítez, Aldo A. Rubert, and Roberto C. Salvarezza; The Chemistry of the Sulfur-Gold Interface: In Search of a Unified Model; Accounts of Chemical Research 2012 45 (8), 1183-1192.
Helmut Hinterwirth, Stefanie Kappel, Thomas Waitz, Thomas Prohaska, Wolfgang Lindner, and Michael Lämmerhofer; Quantifying Thiol Ligand Density of Self-Assembled Monolayers on Gold Nanoparticles by Inductively Coupled Plasma-Mass Spectrometry; ACS Nano 2013 7 (2), 1129-1136.
Sasan Asiaei, Patricia Nieva, and Mathilakath M. Vijayan; Fast Kinetics of Thiolic Self-Assembled Monolayer Adsorption on Gold: Modeling and Confirmation by Protein Binding; The Journal of Physical Chemistry B 2014 118 (47), 13697-13703.
Dong Yan, Jeremy A. Saunders, and, and G. Kane Jennings; Kinetics of Formation for n-Alkanethiolate Self-Assembled Monolayers onto Gold in Aqueous Micellar Solutions of C12E6 and C12E7; Langmuir 2002 18 (26), 10202-10212.
Sahoo, H. K., Ottaviano, L., Zheng, Y., Hansen, O., & Yvind, K. (2018). Low temperature bonding of heterogeneous materials using Al2O3 as an intermediate layer. In Proceedings of SPIE (vol. 10535). [105350V] SPIE—International Society for Optical Engineering. (Proceedings of S P I E—International Society for Optical Engineering). DOI: 10.1117/12.2289526.
Douglas, R., van Veggel, A. A., Cunningham, L., Haughian, K., Hough, J., & Rowan, S. (2014). Cryogenic and room temperature strength of sapphire jointed by hydroxide-catalysis bonding. Class. Quantum Grav. 31 (2014) DOI: 10.1088/0264-9381/31/4/045001.
Syvain Karlen—Doctorate Thesis—“Fabrication and characterization of MEMS alkali vapor cells used in chip-scale atomic clocks and other atomic devices”—University of Neuchatel—Dec. 2017. (Relevant pp. Chapter 3 44-48).
A. Pelton. The Ca—Rb (Calcium-Rubidium) system. Bulletin of Alloy Phase Diagrams, 6(1):37, 1985.
Abstract for C.-H Lee, H. Guo, S. Radhakrishnam, A. Lal, C. Szekely, T. McClellan, and A. Pisano. A batch fabricated rubidium-vapor resonance cell for chip-scale atomic clocks. In Solid-State Sensors, Actuators and Microsystems Workshop, Hilton Head Island, SC, United States, 2005. (Abstract only found at https://www.jstage.jst.go.jp/article/ieejsmas/131/7/131_7_251/_article/-char/ja/).
Related Publications (1)
Number Date Country
20200123416 A1 Apr 2020 US
Provisional Applications (2)
Number Date Country
62798330 Jan 2019 US
62747924 Oct 2018 US