Methods for manufacturing bulked continuous filament

Information

  • Patent Grant
  • 10654211
  • Patent Number
    10,654,211
  • Date Filed
    Friday, December 14, 2018
    6 years ago
  • Date Issued
    Tuesday, May 19, 2020
    4 years ago
Abstract
A method of manufacturing bulked continuous carpet filament which, in various embodiments, comprises: (A) grinding recycled PET bottles into a group of flakes; (B) washing the flakes; (C) identifying and removing impurities, including impure flakes, from the group of flakes; (D) passing the group of flakes through an expanded surface area extruder while maintaining a pressure within the expanded surface area extruder below about 25 millibars; (E) passing the resulting polymer melt through at least one filter having a micron rating of less than about 50 microns; and (F) forming the recycled polymer into bulked continuous carpet filament that consists essentially of recycled PET.
Description
BACKGROUND

Because pure virgin PET polymer is more expensive than recycled PET polymer, and because of the environmental benefits associated with using recycled polymer, it would be desirable to be able to produce bulked continuous carpet filament from 100% recycled PET polymer (e.g., PET polymer from post-consumer PET bottles).


SUMMARY

A method of manufacturing bulked continuous carpet filament, according to various embodiments, comprises: (A) providing a first extruder comprising a first extruder inlet, a first extruder outlet and a pressure regulation system that is adapted to maintain a pressure within the first extruder below about 25 millibars; (B) using the pressure regulation system to reduce a pressure within the first extruder to below about 25 millibars; (C) while maintaining the pressure within the first extruder below about 25 millibars, passing a plurality of flakes of recycled PET through the first extruder via the first extruder inlet to at least partially melt the plurality of flakes into a polymer melt; (D) providing at least one spinning machine comprising at least one spinning machine inlet, wherein the at least one spinning machine inlet is substantially directly coupled to the first extruder outlet; (E) after the step of passing the polymer melt through the first extruder, substantially immediately forming the polymer melt into bulked continuous carpet filament using the at least one spinning machine.


A method of manufacturing bulked continuous carpet filament, according to various embodiments: (A) providing an expanded surface area extruder, wherein the expanded surface area extruder defines an expanded surface area extruder inlet and an expanded surface area extruder outlet; (B) providing a pressure regulation system configured to reduce a pressure within at least a portion of the expanded surface area extruder below about 12 mbar; (C) providing a spinning machine defining a spinning machine inlet, wherein the spinning machine inlet is operatively coupled to the expanded surface area extruder outlet; (D) using the pressure regulation system to reduce the pressure within the at least a portion of the expanded surface area extruder below about 12 mbar; (E) passing a plurality of flakes consisting essentially of PET flakes through the expanded surface area extruder via the expanded surface area extruder inlet to at least partially melt the plurality of flakes to form a polymer melt; and (F) substantially immediately after passing the plurality of flakes through the expanded surface area extruder, using the spinning machine to form the polymer melt into bulked continuous carpet filament.


A method of manufacturing carpet filament, in particular embodiments, comprises the steps of: (A) grinding a plurality of recycled PET bottles into a group of polymer flakes; (B) washing the group of polymer flakes to remove at least a portion of one or more contaminants from a surface of the flakes, the group of flakes comprising a first plurality of flakes that consist essentially of PET and a second plurality of flakes that do not consist essentially of PET; (C) after the step of washing the first plurality of flakes: (i) scanning the washed group of flakes to identify the second plurality of flakes, and (ii) separating the second plurality of flakes from the first plurality of flakes; (D) providing an expanded surface area extruder having an extruder inlet and an extruder outlet; (E) providing a pressure regulation system configured to reduce a pressure within the expanded surface area extruder between about 0 mbar and about 25 mbar; (F) providing a spinning machine having a spinning machine inlet, wherein the spinning machine inlet is directly coupled to the extruder outlet; (G) using the pressure regulation system to reduce the pressure within the expanded surface area extruder between about 0 mbar and about 5 mbar; (H) while maintaining the pressure within the expanded surface area extruder between about 0 mbar about 5 mbar, passing the second plurality of flakes through the expanded surface area extruder via the first inlet; (I) melting the second plurality of flakes using the expanded surface area extruder to produce a polymer melt; and (J) substantially immediately after passing the second plurality of flakes through the expanded surface area extruder, spinning the polymer melt into bulked continuous carpet filament using the spinning machine.





BRIEF DESCRIPTION OF THE DRAWINGS

Having described various embodiments in general terms, reference will now be made to the accompanying drawings, which are not necessarily drawn to scale, and wherein:



FIG. 1 depicts a process flow, according to a particular embodiment, for manufacturing bulked continuous carpet filament.



FIG. 2 is a perspective view of an MRS extruder that is suitable for use in the process of FIG. 1.



FIG. 3 is a cross-sectional view of an exemplary MRS section of the MRS extruder of FIG. 2.



FIG. 4 depicts a process flow depicting the flow of polymer through an MRS extruder and filtration system according to a particular embodiment.



FIG. 5 is a high-level flow chart of a method, according to various embodiments, of manufacturing bulked continuous carpet filament.





DETAILED DESCRIPTION OF VARIOUS EMBODIMENTS

Various embodiments will now be described in greater detail. It should be understood that the invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like numbers refer to like elements throughout.


I. Overview

New processes for making fiber from recycled polymer (e.g., recycled PET polymer) are described below. In various embodiments, this new process: (1) is more effective than earlier processes in removing contaminates and water from the recycled polymer; and/or (2) does not require the polymer to be melted and cooled as many times as in earlier processes. In at least one embodiment, the improved process results in a recycled PET polymer having a polymer quality that is high enough that the PET polymer may be used in producing bulked continuous carpet filament from 100% recycled PET content (e.g., 100% from PET obtained from previously used PET bottles). In particular embodiments, the recycled PET polymer has an intrinsic viscosity of at least about 0.79 dL/g (e.g., of between about 0.79 dL/g and about 1.00 dL/g).


II. More Detailed Discussion

A BCF (bulked continuous filament) manufacturing process, according to a particular embodiment, may generally be broken down into three steps: (1) preparing flakes of PET polymer from post-consumer bottles for use in the process; (2) passing the flakes through an extruder that melts the flakes and purifies the resulting PET polymer; and (3) feeding the purified polymer into a spinning machine that turns the polymer into filament for use in manufacturing carpets. These three steps are described in greater detail below.


Step 1: Preparing Flakes of PET Polymer from Post-Consumer Bottles


In a particular embodiment, the step of preparing flakes of PET polymer from post-consumer bottles comprises: (A) sorting post-consumer PET bottles and grinding the bottles into flakes; (B) washing the flakes; and (C) identifying and removing any impurities or impure flakes.


A. Sorting Post-Consumer PET Bottles and Grinding the Bottles into Flakes


In particular embodiments, bales of clear and mixed colored recycled post-consumer (e.g., “curbside”) PET bottles (or other containers) obtained from various recycling facilities make-up the post-consumer PET containers for use in the process. In other embodiments, the source of the post-consumer PET containers may be returned ‘deposit’ bottles (e.g., PET bottles whose price includes a deposit that is returned to a customer when the customer returns the bottle after consuming the bottle's contents). The curbside or returned “post-consumer” or “recycled” containers may contain a small level of non-PET contaminates. The contaminants in the containers may include, for example, non-PET polymeric contaminants (e.g., PVC, PLA, PP, PE, PS, PA, etc.), metal (e.g., ferrous and non-ferrous metal), paper, cardboard, sand, glass or other unwanted materials that may find their way into the collection of recycled PET. The non-PET contaminants may be removed from the desired PET components, for example, through one or more of the various processes described below.


In particular embodiments, smaller components and debris (e.g., components and debris greater than 2 inches in size) are removed from the whole bottles via a rotating trammel. Various metal removal magnets and eddy current systems may be incorporated into the process to remove any metal contaminants. Near Infra-Red optical sorting equipment such as the NRT Multi Sort IR machine from Bulk Handling Systems Company of Eugene, Oreg., or the Spyder IR machine from National Recovery Technologies of Nashville, Tenn., may be utilized to remove any loose polymeric contaminants that may be mixed in with the PET flakes (e.g., PVC, PLA, PP, PE, PS, and PA). Additionally, automated X-ray sorting equipment such as a VINYLCYCLE machine from National Recovery Technologies of Nashville, Tenn. may be utilized to remove remaining PVC contaminants.


In particular embodiments, a binary segregation of the clear materials from the colored materials is achieved using automated color sorting equipment equipped with a camera detection system (e.g., an Multisort ES machine from National Recovery Technologies of Nashville, Tenn.). In various embodiments, manual sorters are stationed at various points on the line to remove contaminants not removed by the sorter and any colored bottles. In particular embodiments, the sorted material is taken through a granulation step (e.g., using a 50B Granulator machine from Cumberland Engineering Corporation of New Berlin, Wis.) to size reduce (e.g., grind) the bottles down to a size of less than one half of an inch. In various embodiments, the bottle labels are removed from the resultant “dirty flake” (e.g., the PET flakes formed during the granulation step) via an air separation system prior to entering the wash process.


B. Washing the Flakes


In particular embodiments, the “dirty flake” is then mixed into a series of wash tanks. As part of the wash process, in various embodiments, an aqueous density separation is utilized to separate the olefin bottle caps (which may, for example, be present in the “dirty flake” as remnants from recycled PET bottles) from the higher specific gravity PET flakes. In particular embodiments, the flakes are washed in a heated caustic bath to about 190 degrees Fahrenheit. In particular embodiments, the caustic bath is maintained at a concentration of between about 0.6% and about 1.2% sodium hydroxide. In various embodiments, soap surfactants as well as defoaming agents are added to the caustic bath, for example, to further increase the separation and cleaning of the flakes. A double rinse system then washes the caustic from the flakes.


In various embodiments, the flake is centrifugally dewatered and then dried with hot air to at least substantially remove any surface moisture. The resultant “clean flake” is then processed through an electrostatic separation system (e.g., an electrostatic separator from Carpco, Inc. of Jacksonville, Fla.) and a flake metal detection system (e.g., an MSS Metal Sorting System) to further remove any metal contaminants that remain in the flake. In particular embodiments, an air separation step removes any remaining label from the clean flake. In various embodiments, the flake is then taken through a flake color sorting step (e.g., using an OPTIMIX machine from TSM Control Systems of Dundalk, Ireland) to remove any remaining color contaminants remaining in the flake. In various embodiments, an electro-optical flake sorter based at least in part on Raman technology (e.g., a Powersort 200 from Unisensor Sensorsysteme GmbH of Karlsruhe, Germany) performs the final polymer separation to remove any non-PET polymers remaining in the flake. This step may also further remove any remaining metal contaminants and color contaminants.


In various embodiments, the combination of these steps delivers substantially clean (e.g., clean) PET bottle flake comprising less than about 50 parts per million PVC (e.g., 25 ppm PVC) and less than about 15 parts per million metals for use in the downstream extrusion process described below.


C. Identifying and Removing Impurities and Impure Flakes


In particular embodiments, after the flakes are washed, they are fed down a conveyor and scanned with a high-speed laser system 300. In various embodiments, particular lasers that make up the high-speed laser system 300 are configured to detect the presence of particular contaminates (e.g., PVC or Aluminum). Flakes that are identified as not consisting essentially of PET may be blown from the main stream of flakes with air jets. In various embodiments, the resulting level of non-PET flakes is less than 25 ppm.


In various embodiments, the system is adapted to ensure that the PET polymer being processed into filament is substantially free of water (e.g., entirely free of water). In a particular embodiment, the flakes are placed into a pre-conditioner for between about 20 and about 40 minutes (e.g., about 30 minutes) during which the pre-conditioner blows the surface water off of the flakes. In particular embodiments, interstitial water remains within the flakes. In various embodiments, these “wet” flakes (e.g., flakes comprising interstitial water) may then be fed into an extruder (e.g., as described in Step 2 below), which includes a vacuum setup designed to remove—among other things—the interstitial water that remains present in the flakes following the quick-drying process described above.


Step 2: Using an Extrusion System to Melt and Purify PET Flakes


In particular embodiments, an extruder is used to turn the wet flakes described above into a molten recycled PET polymer and to perform a number of purification processes to prepare the polymer to be turned into BCF for carpet. As noted above, in various embodiments, after STEP 1 is complete, the recycled PET polymer flakes are wet (e.g., surface water is substantially removed (e.g., fully removed) from the flakes, but interstitial water remains in the flakes). In particular embodiments, these wet flakes are fed into a Multiple Rotating Screw (“MRS”) extruder 400. In other embodiments, the wet flakes are fed into any other suitable extruder (e.g., a twin screw extruder, a multiple screw extruder, a planetary extruder, or any other suitable extrusion system). An exemplary MRS Extruder 400 is shown in FIGS. 2 and 3. A particular example of such an MRS extruder is described in U.S. Published Patent Application 2005/0047267, entitled “Extruder for Producing Molten Plastic Materials”, which was published on Mar. 3, 2005, and which is hereby incorporated herein by reference.


As may be understood from this figure, in particular embodiments, the MRS extruder includes a first single-screw extruder section 410 for feeding material into an MRS section 420 and a second single-screw extruder section 440 for transporting material away from the MRS section.


In various embodiments, the wet flakes are fed directly into the MRS extruder 400 substantially immediately (e.g., immediately) following the washing step described above (e.g., without drying the flakes or allowing the flakes to dry). In particular embodiments, a system that feeds the wet flakes directly into the MRS Extruder 400 substantially immediately (e.g., immediately) following the washing step described above may consume about 20% less energy than a system that substantially fully pre-dries the flakes before extrusion (e.g., a system that pre-dries the flakes by passing hot air over the wet flakes for a prolonged period of time). In various embodiments, a system that feeds the wet flakes directly into the MRS Extruder 400 substantially immediately (e.g., immediately) following the washing step described above avoids the need to wait a period of time (e.g., up to eight hours) generally required to fully dry the flakes (e.g., remove all of the surface and interstitial water from the flakes).



FIG. 4 depicts a process flow that illustrates the various processes performed by the MRS Extruder 400 in a particular embodiment. In the embodiment shown in this figure, the wet flakes are first fed through the MRS extruder's first single-screw extruder section 410, which may, for example, generate sufficient heat (e.g., via shearing) to at least substantially melt (e.g., melt) the wet flakes.


The resultant polymer melt (e.g., comprising the melted flakes), in various embodiments, is then fed into the extruder's MRS section 420, in which the extruder separates the melt flow into a plurality of different streams (e.g., 4, 6, 8, or more streams) through a plurality of open chambers. FIG. 3 shows a detailed cutaway view of an MRS Section 420 according to a particular embodiment. In particular embodiments, such as the embodiment shown in this figure, the MRS Section 420 separates the melt flow into eight different streams, which are subsequently fed through eight satellite screws 425A-H. As may be understood from FIG. 2, in particular embodiments, these satellite screws are substantially parallel (e.g., parallel) to one other and to a primary screw axis of the MRS Machine 400.


In the MRS section 420, in various embodiments, the satellite screws 425A-H may, for example, rotate faster than (e.g., about four times faster than) in previous systems. As shown in FIG. 3, in particular embodiments: (1) the satellite screws 425A-H are arranged within a single screw drum 428 that is mounted to rotate about its central axis; and (2) the satellite screws 425A-H are configured to rotate in a direction that is opposite to the direction in which the single screw drum rotates 428. In various other embodiments, the satellite screws 425A-H and the single screw drum 428 rotate in the same direction. In particular embodiments, the rotation of the satellite screws 425A-H is driven by a ring gear. Also, in various embodiments, the single screw drum 428 rotates about four times faster than each individual satellite screw 425A-H. In certain embodiments, the satellite screws 425A-H rotate at substantially similar (e.g., the same) speeds.


In various embodiments, as may be understood from FIG. 4, the satellite screws 425A-H are housed within respective extruder barrels, which may, for example be about 30% open to the outer chamber of the MRS section 420. In particular embodiments, the rotation of the satellite screws 425A-H and single screw drum 428 increases the surface exchange of the polymer melt (e.g., exposes more surface area of the melted polymer to the open chamber than in previous systems). In various embodiments, the MRS section 420 creates a melt surface area that is, for example, between about twenty and about thirty times greater than the melt surface area created by a co-rotating twin screw extruder. In a particular embodiment, the MRS section 420 creates a melt surface area that is, for example, about twenty five times greater than the melt surface area created by a co-rotating twin screw extruder


In various embodiments, the MRS extruder's MRS Section 420 is fitted with a Vacuum


Pump 430 that is attached to a vacuum attachment portion 422 of the MRS section 420 so that the Vacuum Pump 430 is in communication with the interior of the MRS section via a suitable opening 424 in the MRS section's housing. In still other embodiments, the MRS Section 420 is fitted with a series of Vacuum Pumps. In particular embodiments, the Vacuum Pump 430 is configured to reduce the pressure within the interior of the MRS Section 420 to a pressure that is between about 0.5 millibars and about 5 millibars. In particular embodiments, the Vacuum Pump 430 is configured to reduce the pressure in the MRS Section 420 to less than about 1.5 millibars (e.g., about 1 millibar or less). The low-pressure vacuum created by the Vacuum Pump 430 in the MRS Section 420 may remove, for example: (1) volatile organics present in the melted polymer as the melted polymer passes through the MRS Section 420; and/or (2) at least a portion of any interstitial water that was present in the wet flakes when the wet flakes entered the MRS Extruder 400. In various embodiments, the low-pressure vacuum removes substantially all (e.g., all) of the water and contaminants from the polymer stream.


In a particular example, the Vacuum Pump 430 comprises three mechanical lobe vacuum pumps (e.g., arranged in series) to reduce the pressure in the chamber to a suitable level (e.g., to a pressure of about 1.0 millibar). In other embodiments, rather than the three mechanical lobe vacuum pump arrangement discussed above, the Vacuum Pump 430 includes a jet vacuum pump fit to the MRS extruder. In various embodiments, the jet vacuum pump is configured to achieve about 1 millibar of pressure in the interior of the MRS section 420 and about the same results described above regarding a resulting intrinsic viscosity of the polymer melt. In various embodiments, using a jet vacuum pump can be advantageous because jet vacuum pumps are steam powered and therefore substantially self-cleaning (e.g., self-cleaning), thereby reducing the maintenance required in comparison to mechanical lobe pumps (which may, for example, require repeated cleaning due to volatiles coming off and condensing on the lobes of the pump). In a particular embodiment, the Vacuum Pump 430 is a jet vacuum pump is made by Arpuma GmbH of Bergheim, Germany.


In particular embodiments, after the molten polymer is run the through the multi-stream MRS Section 420, the streams of molten polymer are recombined and flow into the MRS extruder's second single screw section 440. In various embodiments, the single stream of molten polymer is next run through a filtration system 450 that includes at least one filter. In a particular embodiment, the filtration system 450 includes two levels of filtration (e.g., a 40 micron screen filter followed by a 25 micron screen filter). Although, in various embodiments, water and volatile organic impurities are removed during the vacuum process as discussed above, particulate contaminates such as, for example, aluminum particles, sand, dirt, and other contaminants may remain in the polymer melt. Thus, this filtration step may be advantageous in removing particulate contaminates (e.g., particulate contaminates that were not removed in the MRS Section 420).


In particular embodiments, a viscosity sensor 460 (see FIG. 4) is used to sense the melt viscosity of the molten polymer stream following its passage through the filtration system 450. In various embodiments, the viscosity sensor 460, measures the melt viscosity of the stream, for example, by measuring the stream's pressure drop across a known area. In particular embodiments, in response to measuring an intrinsic viscosity of the stream that is below a predetermined level (e.g., below about 0.8 g/dL), the system may: (1) discard the portion of the stream with low intrinsic viscosity; and/or (2) lower the pressure in the MRS Section 420 in order to achieve a higher intrinsic viscosity in the polymer melt. In particular embodiments, decreasing the pressure in the MRS Section 420 is executed in a substantially automated manner (e.g., automatically) using the viscosity sensor in a computer-controlled feedback control loop with the vacuum section 430.


In particular embodiments, removing the water and contaminates from the polymer improves the intrinsic viscosity of the recycled PET polymer by allowing polymer chains in the polymer to reconnect and extend the chain length. In particular embodiments, following its passage through the MRS Section 420 with its attached Vacuum Pump 430, the recycled polymer melt has an intrinsic viscosity of at least about 0.79 dL/g (e.g., of between about 0.79 dL/g and about 1.00 dL/g). In particular embodiments, passage through the low pressure MRS Section 420 purifies the recycled polymer melt (e.g., by removing the contaminants and interstitial water) and makes the recycled polymer substantially structurally similar to (e.g., structurally the same as) pure virgin PET polymer. In particular embodiments, the water removed by the vacuum includes both water from the wash water used to clean the recycled PET bottles as described above, as well as from unreacted water generated by the melting of the PET polymer in the single screw heater 410 (e.g., interstitial water). In particular embodiments, the majority of water present in the polymer is wash water, but some percentage may be unreacted water.


In particular embodiments, the resulting polymer is a recycled PET polymer (e.g., obtained 100% from post-consumer PET products, such as PET bottles or containers) having a polymer quality that is suitable for use in producing PET carpet filament using substantially only (e.g., only) PET from recycled PET products.


Step 3: Purified PET Polymer Fed into Spinning Machine to be Turned into Carpet Yarn


In particular embodiments, after the recycled PET polymer has been extruded and purified by the above-described extrusion process, the resulting molten recycled PET polymer is fed directly into a BCF (or “spinning”) machine 500 that is configured to turn the molten polymer into bulked continuous filament. For example, in various embodiments, the output of the MRS extruder 400 is connected substantially directly (e.g., directly) to the input of the spinning machine 500 so that molten polymer from the extruder is fed directly into the spinning machine 500. This process may be advantageous because molten polymer may, in certain embodiments, not need to be cooled into pellets after extrusion (as it would need to be if the recycled polymer were being mixed with virgin PET polymer). In particular embodiments, not cooling the recycled molten polymer into pellets serves to avoid potential chain scission in the polymer that might lower the polymer's intrinsic viscosity.


In particular embodiments, the spinning machine 500 extrudes molten polymer through small holes in a spinneret in order to produce carpet yarn filament from the polymer. In particular embodiments, the molten recycled PET polymer cools after leaving the spinneret. The carpet yarn is then taken up by rollers and ultimately turned into filaments that are used to produce carpet. In various embodiments, the carpet yarn produced by the spinning machine 500 may have a tenacity between about 3 gram-force per unit denier (gf/den) and about 9 gf/den. In particular embodiments, the resulting carpet yarn has a tenacity of at least about 3 gf/den.


In particular embodiments, the spinning machine 500 used in the process described above is the Sytec One spinning machine manufactured by Oerlika Neumag of Neumuenster, Germany. The Sytec One machine may be especially adapted for hard-to-run fibers, such as nylon or solution-dyed fibers, where the filaments are prone to breakage during processing. In various embodiments, the Sytec One machine keeps the runs downstream of the spinneret as straight as possible, uses only one threadline, and is designed to be quick to rethread when there are filament breaks.


Although the example described above describes using the Sytec One spinning machine to produce carpet yarn filament from the polymer, it should be understood that any other suitable spinning machine may be used. Such spinning machines may include, for example, any suitable one-threadline or three-threadline spinning machine made by Oerlika Neumag of Neumuenster, Germany or any other company.


In various embodiments, the improved strength of the recycled PET polymer generated using the process above allows it to be run at higher speeds through the spinning machine 500 than would be possible using pure virgin PET polymer. This may allow for higher processing speeds than are possible when using virgin PET polymer.


Summary of Exemplary Process



FIG. 5 provides a high-level summary of the method of manufacturing bulked continuous filament described above. As shown in the figure, the method begins at Step 602, where recycled PET bottles are ground into a group of flakes. Next, at Step 604, the group of flakes is washed to remove contaminants from the flakes' respective outer surfaces. Next, at Step 606, the group of flakes is scanned (e.g., using one or more of the methods discussed above) to identify impurities, including impure flakes. These impurities, and impure flakes, are then removed from the group of flakes.


Next, at Step 608, the group of flakes is passed through an MRS extruder while maintaining the pressure within an MRS portion of the extruder below about 1.5 millibars. At Step 610, the resulting polymer melt is passed through at least one filter having a micron rating of less than about 50 microns. Finally, at Step 612, the recycled polymer is formed into bulked continuous carpet filament, which may be used in producing carpet. The method then ends at Step 614.


Alternative Embodiments

In particular embodiments, the system may comprise alternative components or perform alternative processes in order to produce substantially continuous BCF from 100% recycled PET, or other recycled polymer. Exemplary alternatives are discussed below.


Non-MRS Extrusion System


In particular embodiments, the process may utilize a polymer flow extrusion system other than the MRS Extruder described above. The alternative extrusion system may include for example, a twin screw extruder, a multiple screw extruder, a planetary extruder, or any other suitable extrusion system. In a particular embodiment, the process may include a plurality of any combination of any suitable conical screw extruders (e.g., four twin screw extruders, three multiple screw extruders, etc.).


Making Carpet Yarn from 100% Recycled Carpet


In particular embodiments, the process described above may be adapted for processing and preparing old carpet (or any other suitable post-consumer product) to produce new carpet yarn comprising 100% recycled carpet. In such embodiments, the process would begin by grinding and washing recycled carpet rather than recycled PET bottles. In various embodiments where old carpet is converted into new carpet yarn comprising 100% recycled carpet, the process may comprise additional steps to remove additional materials or impurities that may be present in recycled carpet that may not be present in recycled PET bottles (e.g., carpet backing, adhesive, etc.).


Other Sources of Recycled PET


In various embodiments, the process described above is adapted for processing recycled PET from any suitable source (e.g., sources other than recycled bottles or carpet) to produce new carpet yarn comprising 100% recycled PET.


The Use of a Crystallizer as Part of BCF Process


In various embodiments, the process for producing recycled BCF may further include a crystallizing step that utilizes one or more PET crystallizers. In particular embodiments, the system is configured to perform the crystallization step on the ground flakes prior to running the flakes through the one or more extruders (e.g., single screw extruder, MRS extruder, etc.). In particular embodiments, the PET crystallizer comprises a housing, a hopper screw (e.g., an auger) disposed at least partially within the housing, a stirring apparatus, one or more heating elements, and one or more blowers.


Hopper Screw


In particular embodiments, the hopper screw comprises any suitable screw conveyor (e.g., such as an Archimedes' screw) for moving liquid or granular materials (e.g., such as PET flakes). In various embodiments, the hopper screw comprises a substantially cylindrical shaft and a helical screw blade disposed along at least a portion of the cylindrical shaft. In particular embodiments, the substantially cylindrical shaft is configured to rotate the screw blade, causing that hopper screw to move material (e.g., the PET flakes) along the cylindrical shaft and into the crystallizer housing. In other embodiments, the hopper screw comprises any other suitable screw conveyer such as, for example, a shaftless spiral. In embodiments in which the hopper screw comprises a shaftless spiral, the shaftless spiral may be substantially fixed at one end and free at the other end and configured to be driven at the fixed end. In various embodiments, the hopper screw is disposed at least partially within the crystallizer housing.


In various embodiments, the hopper screw is configured to feed PET flakes into the crystallizer. In various embodiments, the PET crystallizer is configured to feed the PET flakes into the crystallizer using the hopper screw relatively slowly.


One or More Heating Elements


In various embodiments, the crystallizer comprises one or more heating elements for raising a temperature within the crystallizer. In particular embodiments, the one or more heating elements comprise one or more electric heating elements, one or more gas-fired heating elements, or any other suitable heating elements. In some embodiments, the one or more heating elements may be substantially electrically powered. In various embodiments, the one or more heating elements comprise one or more infra-red heating elements. In other embodiments, the one or more heating elements may utilize natural gas such, for example, propane. In particular embodiments, the one or more heating elements are configured to raise a temperature within the crystallizer to between about 100 degrees Fahrenheit and about 180 degrees Fahrenheit. In still other embodiments, the one or more heating elements are configured to raise a temperature within the crystallizer to between about 100 degrees Celsius and 180 degrees Celsius. In some embodiments, the one or more heating elements are configured to maintain a temperature within the crystallizer that is substantially about a maximum crystallization temperature of PET. In particular embodiments, the maximum crystallization temperature of PET is between about 140 degrees Celsius and about 230 degrees Celsius


One or More Blowers


In various embodiments, the crystallizer further comprises one or more blowers configured to blow air over the flakes as the flakes passes through the crystallizer. In particular embodiments, the one or more blowers comprise any suitable blowers for moving air substantially across a surface area of the flakes as the flakes pass through the crystallizer. For example, in some embodiments, the one or more blowers comprise one or more suitable fans or other suitable mechanisms for moving air. In various embodiments, the one or more blowers are configured to blow air that has been at least partially heated by the one or more heating elements. In particular embodiments, the one or more blowers are configured to blow air having a temperature of at least about 140 degree Fahrenheit. In another particular embodiments, the one or more blowers are configured to blow air having a temperature of at least about 140 degree Celsius. In other embodiments, the one or more blowers are configured to maintain the temperature in the crystallizer between about 140 degrees Fahrenheit and about 180 degrees Fahrenheit. In some embodiments, the one or more blowers are configured to blow hot air from a bottom portion of the crystallizer and draw air from an upper portion of the crystallizer.


Stirring Apparatus


In various embodiments, the crystallizer comprises a stirring apparatus that comprises any suitable apparatus for stirring the PET flakes while the PET flakes are passing through the crystallizer. In various embodiments, the stirring apparatus may be operated, for example, by any suitable gear motor. In a particular embodiment, the stirring apparatus comprises a suitable rod or other suitable mechanism mounted to rotate, or otherwise stir the PET flakes as the PET flakes are passing through the crystallizer. In other embodiments, the stirring apparatus may comprise any suitable tumbler, which may, for example, comprise a drum mounted to rotate via the gear mother such that the PET flakes are at least partially stirred and/or agitated while the PET flakes are within the drum. In still other embodiments, the stirring apparatus comprises one or more screws and/or augers configured to rotate and stir the PET flakes. In particular embodiments, the stirring apparatus comprises the hopper screw.


As may be understood from this disclosure, the stirring apparatus is configured to agitate or stir the PET flakes as the one or more blowers blow air heated by the one or more heating elements across the PET flakes. In particular embodiments, the stirring apparatus is configured to at least partially reduce agglomeration (e.g., sticking or clumping of the flake) while the flake is at least partially crystallizing in the crystallizer.


In particular embodiments, the crystallizer at least partially dries the surface of the PET flakes. In various embodiments, the PET crystallizer is configured to reduce a moisture content of the PET flakes to about 50 ppm. In other embodiments the PET crystallizer is configured to reduce a moisture content of the PET flakes to between about 30 and about 50 ppm.


In various embodiments, the use of drier flakes may enable the system to run the flakes through the MRS extruder more slowly, which may allow for higher pressure within the MRS extruder during extrusion (e.g., may enable the system to maintain a higher pressure within the MRS extruder, rather than very low pressure). In various embodiments of the process, the pressure regulation system may be configured to maintain a pressure within the MRS extruder of between about 0 millibars and about 25 millibars. In particular embodiments, such as embodiments in which the PET flakes have been run through a crystallizer before being extruded in the MRS extruder, the pressure regulation system may be configured to maintain a pressure within the MRS extruder of between about 0 and about 18 millibars. In other embodiments, the pressure regulation system may be configured to maintain a pressure within the MRS extruder between about 0 and about 12 millibars. In still other embodiments, the pressure regulation system may be configured to maintain a pressure within the MRS extruder between about 0 and about 8 millibars. In still other embodiments, the pressure regulation system may be configured to maintain a pressure within the MRS extruder between about 5 millibars and about 10 millibars. In particular embodiments, the pressure regulation system may be configured to maintain a pressure within the MRS extruder at about 5 millibars, about 6 millibars, about 7 millibars, about 8 millibars, about 9 millibars, or about any suitable pressure between about 0 millibars and about 25 millibars.


In particular embodiments, the crystallizer causes the flakes to at least partially reduce in size, which may, for example, reduce a potential for the flakes to stick together. In particular embodiments, the crystallizer may particularly reduce stickiness of larger flakes, which may, for example, include flakes comprising portions of the ground PET bottles which may be thicker than other portions of the PET bottles (e.g., flakes ground from a threaded portion of the PET bottle on which a cap would typically be screwed).


Use of Curbside Recycling v. Deposit Bottles in Process


In various embodiments, the system is configured to utilize recycled PET of varying quality in the process described above. For example, in various embodiments, the system is configured to produce bulked continuous carpet filament from PET derived from PET bottles sourced from curbside recycling sources (e.g., PET bottles that were collected as part of a general bulk recycling program or other recycling source) as well as deposit PET bottles (e.g., bottles returned as part of a deposit program). In various embodiments, Curbside recycled bottles may require more thorough processing in order to produce bulked continuous filament, as curbside recycled PET bottles may be mixed in with and otherwise include contaminants such as, for example: other recyclable goods (e.g., paper, other plastics, etc.), garbage, and other non-PET bottle items due to imperfect sorting of recycled goods or for any other reason. Deposit PET bottles may include PET bottles with fewer unwanted contaminants due in part because deposit PET bottles may be collected separately from other recyclable or disposable goods.


In various embodiments, curbside recycled PET bottles acquired during particular times of year may include more impurities and other contaminants than at other times of the year. For example, curbside recycled PET bottles collected during summer months may comprise a higher percentage of clear PET bottles (e.g., water bottles) at least in part due to additional water consumption during summer months.


In various embodiments, the system described above may be configured to adjust particular components of the process based at least in part on the source of recycled PET being used to produce the bulked continuous carpet filament. For example, because deposit PET bottles include fewer impurities that need to be removed during the initial cleaning and sorting phases of the process, the pressure regulation system may be configured to maintain a pressure within the MRS extruder that is higher than a pressure that it would be configured to maintain for PET flake derived from curbside recycled PET bottles. In a particular embodiment, the pressure regulation system may be configured to maintain a pressure within the MRS extruder of between about 0 millibars and about 12 millibars when flakes derived from deposit PET bottles are passing through the MRS extruder. In still other embodiments, the pressure regulation system may be configured to maintain a pressure within the MRS extruder of between about 5 millibars and about 10 millibars in such instances.


In various embodiments, the system is configured to determine a suitable pressure at which to maintain the pressure within the MRS extruder based at least in part on the source of the recycled PET. In other embodiments, the system is configured to omit one or more of the steps above or include one or more additional steps to the steps described above based at least in part on the source of the recycled PET.


Direct Coupling of Various Process Components


Direct Coupling of MRS Extruder to Spinning Machine


In particular embodiments, the output of the MRS machine may be substantially directly coupled (e.g., directly coupled) to a spinning machine for forming the resulting molten polymer into bulked continuous filament. In such embodiments, after the recycled PET polymer has been extruded and purified by the above-described extrusion process, the resulting molten recycled PET polymer is fed substantially directly (e.g., directly) into the spinning machine. This process may be advantageous because molten polymer may, in certain embodiments, not need to be cooled into pellets after extrusion (as it would need to be if the recycled polymer were being mixed with virgin PET polymer) prior to spinning the molten polymer into filament. In particular embodiments, not cooling the recycled molten polymer into pellets serves to avoid potential chain scission in the polymer that might lower the polymer's intrinsic viscosity.


Direct Coupling of Non-MRS Extruder to Spinning Machine


In various embodiments of the process for recycling PET (e.g., or other polymers) into BCF, the recycled PET flakes are passed through an extruder other than an MRS extruder (e.g., a “first extruder”) prior to spinning the resultant molten polymer into BCF. In particular embodiments, the first extruder is substantially directly coupled (e.g., directly coupled) to the spinning machine (e.g., an outlet of the first extruder is substantially directly coupled to an inlet of the spinning machine). For example, in various embodiments, an outlet of the first extruder is substantially directly coupled (e.g., via a suitable pipe, connector, etc.) to one or more inlets of one or more spinning machines. In particular embodiments, the first extruder may include any suitable expanded surface area extruder. In various embodiments, the first extruder may include, for example, a twin screw extruder, a multiple screw extruder, a planetary extruder, or any other suitable extrusion system (e.g., any other suitable expanded surface area extruder). In various embodiments, the first extruder is any suitable extruder for increasing an amount of surface area of a polymer melt being extruded by the first extruder that is exposed to a low pressure within the first extruder (e.g., a low pressure caused by a pressure regulation system, such as any suitable pressure regulation system described above). In a particular embodiment, the first extruder is an MAS extruder manufactured by Maschinen and Anlagenbau Schulz GmbH of Pucking, Austria.


In various embodiments, the first extruder is a conical co-rotating twin screw extruder. In such embodiments, the first extruder comprises an extruder housing in which two, co-rotating conical screws are disposed (e.g., a first conical screw and a second conical screw). In various embodiments, each conical screw is substantially conical (e.g., conical) such that the screw narrows from a first diameter at a base end of each respective conical screw to a second diameter at a vertex end of each respective conical screw that is less than the first diameter. In various embodiments, each particular conical screw may have any suitable thread or threading. In some embodiments, each conical screw has a substantially uniform (e.g., uniform) thread pitch and thread crest along at least a portion of the conical screw. In other embodiments, thread pitch and crest may at least partially vary along a length of the particular conical screw. In still other embodiments, a difference between a major and minor diameter of the conical screw may vary along a length of the conical screw (e.g., the screw thread may be larger or smaller along particular portions of the conical screw). In a particular embodiment, the pitch of thread of a particular conical screw may decrease along the conical screw from the base portion to the vertex portion. In particular embodiments, the first and second conical screws are substantially structurally identical (e.g., structurally identical).


In particular embodiments, the two conical screws are oriented within the conical twin screw extruder such that the base portion of each screw is disposed adjacent an intake (e.g., inlet) of the conical twin screw extruder, and the vertex portion of each screw is disposed adjacent an outlet of the conical twin extruder. In particular embodiments, a central axis of the first conical screw forms an acute angle with the central axis of the second conical screw. In various embodiments, the first and second conical screws are disposed such that at least a portion of the thread of the first conical screw at least partially mates with (e.g., mates with) at least a portion of the thread of the second conical screw. In other embodiments, at least a portion of the thread of the first conical screw at least partially engages with (e.g., engages with) at least a portion of the thread of the second conical screw


In particular embodiments, the conical twin screw extruder may be configured to at least partially melt the plurality of flakes into a polymer melt. In such embodiments, the conical twin screw extruder may, for example, generate sufficient heat (e.g., via shearing) to at least substantially melt (e.g., melt) the flakes. In particular embodiments, the first extruder is configured to increase a surface area of the polymer melt. In various embodiments, the conical design of the conical twin screw extruder may result in an intake volume that is substantially greater (e.g., greater) than a discharge volume of the conical twin screw extruder. This higher intake volume, in various embodiments, may result in a high volume throughput per revolution of the twin conical screws. In various embodiments, the first extruder is configured to receive a plurality of polymer flakes (e.g., PET flakes) via a first extruder inlet, melt the plurality of flakes into a polymer melt while extruding the plurality of flakes, and pass the resulting polymer melt though an extruder outlet.


In various embodiments, the first extruder comprises a pressure regulation system configured to reduce a pressure within the first extruder. In a particular embodiment, the first extruder is fitted with a suitable vacuum pump such that the vacuum pump is in communication with an interior of the first extruder's housing via a suitable opening in the first extruder's housing. In still other embodiments, the first extruder is fitted with a series of vacuum pumps. In particular embodiments, the vacuum pump is configured to reduce the pressure within the interior of the first extruder to a pressure that is between about 0 millibars and about 25 millibars. In other embodiments, the vacuum pump is configured to reduce a pressure within the first extruder to between about 5 millibars and about 18 millibars. In still other embodiments, the vacuum pump is configured to reduce a pressure within the first extruder to any particular suitable pressure between about 0 millibars and about 25 millibars. In various embodiments, the low-pressure vacuum created by the vacuum pump in the first extruder may remove, for example: (1) volatile organics present in the melted polymer as the melted polymer passes through the first extruder; and/or (2) at least a portion of any interstitial water that was present in the wet flakes when the wet flakes entered the first extruder. In various embodiments, the low-pressure vacuum removes substantially all (e.g., all) of the water and contaminants from the polymer stream. In various embodiments, the vacuum pump may include any suitable vacuum pump, such as any vacuum pump described above or any other suitable vacuum pump.


In embodiments in which the system includes a first extruder directly coupled to the spinning machine, the process may include passing the plurality of flakes (e.g., a plurality of wet flakes after a washing step) through the first extruder to at least partially melt the plurality of flakes into a polymer melt and remove at least a portion of the impurities from the polymer melt. The polymer melt is then fed substantially directly (e.g., directly) into the spinning machine for spinning into bulked continuous carpet filament.


CONCLUSION

Many modifications and other embodiments of the invention will come to mind to one skilled in the art to which this invention pertains having the benefit of the teachings presented in the foregoing descriptions and the associated drawings. For example, although the vacuum system discussed above is described as being configured to maintain the pressure in the open chambers of the MRS extruder to about 1 mbar, in other embodiments, the vacuum system may be adapted to maintain the pressure in the open chambers of the MRS extruder at pressures greater than, or less than, 1 mbar. For example, the vacuum system may be adapted to maintain this pressure at between about 0.5 mbar and about 12 mbar.


Similarly, although various embodiments of the systems described above may be adapted to produce carpet filament from substantially only recycled PET (so the resulting carpet filament would comprise, consist of, and/or consist essentially of recycled PET), in other embodiments, the system may be adapted to produce carpet filament from a combination of recycled PET and virgin PET. The resulting carpet filament may, for example, comprise, consist of, and/or consist essentially of between about 80% and about 100% recycled PET, and between about 0% and about 20% virgin PET.


Also, while various embodiments are discussed above in regard to producing carpet filament from PET, similar techniques may be used to produce carpet filament from other polymers. Similarly, while various embodiments are discussed above in regard to producing carpet filament from PET, similar techniques may be used to produce other products from PET or other polymers.


In addition, it should be understood that various embodiments may omit any of the steps described above or add additional steps.


In light of the above, it is to be understood that the invention is not to be limited to the specific embodiments disclosed and that modifications and other embodiments are intended to be included within the scope of the appended claims. Although specific terms are employed herein, they are used in a generic and descriptive sense only and not for the purposes of limitation.

Claims
  • 1. A method of manufacturing bulked continuous carpet filament, the method comprising: (A) washing a plurality of flakes comprising recycled PET;(B) providing a PET crystallizer;(C) after the step of washing the plurality of flakes comprising recycled PET, passing at least a portion of the plurality of flakes comprising recycled PET through the PET crystallizer to at least partially dry a surface of the plurality of flakes comprising recycled PET;(D) providing an expanded surface area extruder, wherein the expanded surface area extruder defines an expanded surface area extruder inlet and an expanded surface area extruder outlet and comprises: a plurality of satellite screws, each of the plurality of satellite screws being at least partially housed within a respective extruder barrel and mounted to rotate about its respective central axis; anda satellite screw extruder support system that is adapted to orbitally rotate each of the plurality of satellite screws about a main axis as each of the plurality of satellite screws rotate about its respective central axis, the main axis being substantially parallel to each respective central axis;(E) providing a pressure regulation system configured to reduce a pressure within at least a portion of the expanded surface area extruder below about 25 mbar;(F) providing a spinning machine defining a spinning machine inlet, wherein the spinning machine inlet is operatively coupled to the expanded surface area extruder outlet;(G) using the pressure regulation system to reduce the pressure within the at least a portion of the expanded surface area extruder below about 25 mbar;(H) after passing the plurality of flakes comprising recycled PET through the PET crystallizer, passing the plurality of flakes comprising PET flakes through the expanded surface area extruder via the expanded surface area extruder inlet to at least partially melt the plurality of flakes to form a polymer melt such that at least a portion of the polymer melt passes through each the respective satellite screw; and(I) substantially immediately after passing the plurality of flakes through the expanded surface area extruder, using the spinning machine to form the polymer melt into bulked continuous carpet filament.
  • 2. The method of claim 1, wherein washing the plurality of flakes comprises mixing the plurality of flakes in a series of wash tanks.
  • 3. The method of claim 1, wherein washing the plurality of flakes comprises washing the plurality of flakes in a heated caustic bath.
  • 4. The method of claim 3, wherein the heated caustic bath is maintained at a concentration of between about 0.6% sodium hydroxide and about 1.2% sodium hydroxide.
  • 5. The method of claim 1, wherein washing the plurality of flakes comprising recycled PET comprises washing the plurality of flakes comprising recycled PET to remove at least a portion of one or more contaminants from a surface of the plurality of flakes.
  • 6. The method of claim 5, wherein: the plurality of flakes comprise: a first plurality of flakes that consist essentially of PET; anda second plurality of flakes that do not consist essentially of PET;the method further comprises, after the step of washing the plurality of flakes: (i) scanning the washed group of flakes to identify the second plurality of flakes; and(ii) separating the second plurality of flakes from the first plurality of flakes; andpassing at least a portion of the plurality of flakes comprising recycled PET through the PET crystallizer comprises passing the first plurality of flakes through the PET crystallizer.
  • 7. The method of claim 1, further comprising grinding a plurality of recycled PET bottles into the plurality of flakes comprising recycled PET.
  • 8. A method of manufacturing bulked continuous carpet filament, the method comprising: (A) providing a PET crystallizer;(B) passing a plurality of flakes comprising recycled PET through the PET crystallizer to at least partially dry a surface of the plurality of flakes comprising recycled PET;(C) providing an expanded surface area extruder, wherein the expanded surface area extruder defines an expanded surface area extruder inlet and an expanded surface area extruder outlet and comprises: a plurality of satellite screws, each of the plurality of satellite screws being at least partially housed within a respective extruder barrel and mounted to rotate about its respective central axis; anda satellite screw extruder support system that is adapted to orbitally rotate each of the plurality of satellite screws about a main axis as each of the plurality of satellite screws rotate about its respective central axis, the main axis being substantially parallel to each respective central axis;(D) providing a pressure regulation system configured to reduce a pressure within at least a portion of the expanded surface area extruder below about 25 mbar;(E) providing a spinning machine defining a spinning machine inlet, wherein the spinning machine inlet is operatively coupled to the expanded surface area extruder outlet;(F) using the pressure regulation system to reduce the pressure within the at least a portion of the expanded surface area extruder below about 25 mbar;(G) after passing the plurality of flakes comprising recycled PET through the PET crystallizer, passing the plurality of flakes comprising PET flakes through the expanded surface area extruder via the expanded surface area extruder inlet to at least partially melt the plurality of flakes to form a polymer melt such that at least a portion of the polymer melt passes through each the respective satellite screw; and(H) substantially immediately after passing the plurality of flakes through the expanded surface area extruder, using the spinning machine to form the polymer melt into bulked continuous carpet filament.
  • 9. The method of claim 8, further comprising, before the step of passing the plurality of flakes comprising recycled PET through the PET crystallizer, washing the plurality of flakes.
  • 10. The method of claim 9, wherein washing the plurality of flakes comprising recycled PET comprises washing the plurality of flakes comprising recycled PET to remove at least a portion of one or more contaminants from a surface of the plurality of flakes.
  • 11. The method of claim 9, further comprising, before the step of washing the plurality of flakes, grinding a plurality of recycled PET bottles into the plurality of flakes comprising recycled PET.
  • 12. The method of claim 11, wherein washing the plurality of flakes comprises using aqueous density separation to separate remnants of bottle caps from the plurality of recycled PET bottles from the plurality of flakes comprising recycled PET.
  • 13. The method of claim 8, wherein the method comprises manufacturing bulked continuous carpet filament from 100% recycled PET.
  • 14. A method of manufacturing bulked continuous carpet filament, the method comprising: (A) providing a PET crystallizer;(B) passing a plurality of flakes comprising recycled PET through the PET crystallizer to at least partially dry a surface of the plurality of flakes comprising recycled PET;(C) providing an expanded surface area extruder, wherein the expanded surface area extruder defines an expanded surface area extruder inlet and an expanded surface area extruder outlet and comprises: a plurality of satellite screws, each of the plurality of satellite screws being at least partially housed within a respective extruder barrel and mounted to rotate about its respective central axis; anda satellite screw extruder support system that is adapted to orbitally rotate each of the plurality of satellite screws about a main axis as each of the plurality of satellite screws rotate about its respective central axis, the main axis being substantially parallel to each respective central axis;(D) providing a pressure regulation system configured to reduce a pressure within at least a portion of the expanded surface area extruder below about 25 mbar;(E) providing a spinning machine defining a spinning machine inlet, wherein the spinning machine inlet is operatively coupled to the expanded surface area extruder outlet;(F) using the pressure regulation system to reduce the pressure within the at least a portion of the expanded surface area extruder below about 25 mbar;(G) after passing the plurality of flakes comprising recycled PET through the PET crystallizer, passing the plurality of flakes comprising PET flakes through the expanded surface area extruder via the expanded surface area extruder inlet to at least partially melt the plurality of flakes to form a polymer melt such that at least a portion of the polymer melt passes through each the respective satellite screw;(H) after passing the plurality of flakes through the expanded surface area extruder, filtering the polymer melt through at least one filter; and(I) substantially immediately after passing the plurality of flakes through the expanded surface area extruder and filtering the polymer melt through the at least one filter, using the spinning machine to form the polymer melt into bulked continuous carpet filament.
  • 15. The method of claim 14, wherein the at least one filter has a micron rating of less than about 50 microns.
  • 16. The method of claim 14, further comprising, before the step of passing the plurality of flakes comprising recycled PET through the PET crystallizer, washing the plurality of flakes.
  • 17. The method of claim 16, further comprising, before the step of washing the plurality of flakes, grinding a plurality of recycled PET bottles into the plurality of flakes comprising recycled PET.
  • 18. The method of claim 14, wherein the method comprises manufacturing bulked continuous carpet filament from 100% recycled PET.
  • 19. The method of claim 18, wherein manufacturing bulked continuous carpet filament from 100% recycled PET substantially immediately after extruding the recycled PET comprises spinning the polymer melt into bulked continuous carpet filament without substantially cooling the polymer melt.
  • 20. The method of claim 14, wherein the at least one filter comprises a 40 micron screen filter followed by a 25 micron screen filter.
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 15/473,402, filed Mar. 29, 2017, now U.S. Pat. No. 10,232,542, issued Mar. 19, 2019, entitled “Systems and Methods for Manufacturing Bulked Continuous Filament,” which is a continuation of U.S. patent application Ser. No. 14/546,819, filed Nov. 18, 2014, now U.S. Pat. No. 9,630,353, issued Apr. 25, 2017, entitled “Systems and Methods for Manufacturing Bulked Continuous Filament,” which is a continuation-in-part of U.S. patent application Ser. No. 13/892,740, filed May 13, 2013, entitled “Systems and Methods for Manufacturing Bulked Continuous Filament,” which is a divisional of U.S. patent application Ser. No. 13/721,955, filed Dec. 20, 2012, now U.S. Pat. No. 8,597,553, issued Dec. 3, 2013, entitled “Systems and Methods for Manufacturing Bulked Continuous Filament, which claimed the benefit of U.S. Provisional Patent Application No. 61/654,016, filed May 31, 2012, entitled “Systems and Methods for Manufacturing Bulked Continuous Fiber,” all of which are hereby incorporated herein by reference in their entirety.

US Referenced Citations (143)
Number Name Date Kind
1490918 Gaede Apr 1924 A
2146532 Crane Feb 1939 A
3217783 Rodenacker Nov 1965 A
3310837 Wittrock Mar 1967 A
3357049 Spindler Dec 1967 A
3608001 Kowalski et al. Sep 1971 A
3825236 Hussmann et al. Jul 1974 A
3865528 Roess Feb 1975 A
3938924 Abella et al. Feb 1976 A
4057376 Berger Nov 1977 A
4057607 Soehngen et al. Nov 1977 A
4128386 Wissinger et al. Dec 1978 A
4172477 Reich Oct 1979 A
4192617 Spielhoff Mar 1980 A
4268176 Muller May 1981 A
4289409 Brand Sep 1981 A
4370302 Suzuoka et al. Jan 1983 A
4564349 Brown Jan 1986 A
4591487 Fritsch May 1986 A
4919872 Fintel Apr 1990 A
5102594 Burlet et al. Apr 1992 A
5108711 Chszaniecki Apr 1992 A
5143308 Hally et al. Sep 1992 A
5224383 Pinto et al. Jul 1993 A
5225130 Deiringer Jul 1993 A
5266601 Kyber et al. Nov 1993 A
5306803 Arlt et al. Apr 1994 A
5393140 Blach Feb 1995 A
5424013 Lieberman Jun 1995 A
5427881 Sacripante Jun 1995 A
5459168 Nasr et al. Oct 1995 A
5497562 Pikus Mar 1996 A
5503788 Lazareck et al. Apr 1996 A
5510073 Kaegi et al. Apr 1996 A
5532035 Corbin et al. Jul 1996 A
5549957 Negola et al. Aug 1996 A
5554657 Brownscombe Sep 1996 A
5613285 Chester et al. Mar 1997 A
5623012 Hwo Apr 1997 A
5715584 Coons, III et al. Feb 1998 A
5804115 Burton et al. Sep 1998 A
5836682 Blach Nov 1998 A
5886058 Van Erden et al. Mar 1999 A
5893702 Conrad et al. Apr 1999 A
5932691 Khanin et al. Aug 1999 A
5945215 Bersted et al. Aug 1999 A
5951159 Schobert-Csongor et al. Sep 1999 A
5958548 Negola et al. Sep 1999 A
5961054 Nishibori Oct 1999 A
6007892 Harwood et al. Dec 1999 A
6074084 Kolossow Jun 2000 A
6113825 Chuah Sep 2000 A
6265533 Regel et al. Jul 2001 B1
6394644 Streiff May 2002 B1
6492485 Gohr et al. Dec 2002 B1
6620354 Bessemer et al. Sep 2003 B1
6627127 Piovoso et al. Sep 2003 B1
6722117 Belcher, Jr. et al. Apr 2004 B2
6773718 Seth et al. Aug 2004 B2
6784214 Bacher et al. Aug 2004 B1
6852256 Borer et al. Feb 2005 B2
6866171 Ickinger Mar 2005 B2
6984694 Blasius, Jr. et al. Jan 2006 B2
7025491 Blach et al. Apr 2006 B2
7192545 Ekart et al. Mar 2007 B2
7198400 Unterlander et al. Apr 2007 B2
7204945 Bonner Apr 2007 B2
7262380 Ulrichsen et al. Aug 2007 B1
7320589 Babin et al. Jan 2008 B2
7354988 Charati et al. Apr 2008 B2
7380973 Goedicke et al. Jun 2008 B2
7485685 Mihan et al. Feb 2009 B2
7513677 Gneuss et al. Apr 2009 B2
7594453 Blach Sep 2009 B2
7628892 Fini Dec 2009 B2
7654725 Sturm et al. Feb 2010 B2
7700015 Kern et al. Apr 2010 B2
7744788 Portier et al. Jun 2010 B2
7799835 Smith et al. Sep 2010 B2
7828538 Fellinger Nov 2010 B2
7902262 Armstrong et al. Mar 2011 B2
7935737 Gopal et al. May 2011 B2
7980834 Maguire Jul 2011 B2
8080190 Ichikawa et al. Dec 2011 B2
8147738 Boczon et al. Apr 2012 B2
8187512 Eloo et al. May 2012 B2
8398752 Brownstein et al. Mar 2013 B2
8404755 Sequeira Mar 2013 B2
8444886 Herve May 2013 B2
8471972 Tsubata Jun 2013 B2
8557155 Deiss et al. Oct 2013 B2
8597553 Clark Dec 2013 B1
8735457 Booth et al. May 2014 B2
8741972 Booth et al. Jun 2014 B2
8795811 Cloutier et al. Aug 2014 B2
9061442 Gneuss et al. Jun 2015 B2
9168718 Westwood et al. Oct 2015 B2
9409363 Clark Aug 2016 B2
9550338 Clark Jan 2017 B2
9630353 Clark Apr 2017 B2
9630354 Clark Apr 2017 B2
9636860 Clark May 2017 B2
9908263 Pichler et al. Mar 2018 B2
9975278 Rabiser et al. May 2018 B2
20020086077 Noller et al. Jul 2002 A1
20040053047 Jackson et al. Mar 2004 A1
20040082672 Zeng et al. Apr 2004 A1
20040140248 Dauzvardis et al. Jul 2004 A1
20040155374 Hutchinson et al. Aug 2004 A1
20050047267 Gneuss et al. Mar 2005 A1
20050263941 Reutter et al. Dec 2005 A1
20060012074 Booth et al. Jan 2006 A1
20060076705 Fowler et al. Apr 2006 A1
20060284334 Christel Dec 2006 A1
20070052131 Fujimaki et al. Mar 2007 A1
20070261777 Steckelberg et al. Nov 2007 A1
20080069916 Regalia Mar 2008 A1
20080139700 Roden et al. Jun 2008 A1
20080157425 Rodgers et al. Jul 2008 A1
20080214701 Wilms et al. Sep 2008 A1
20080272508 Culbert et al. Nov 2008 A1
20080292831 Juriga et al. Nov 2008 A1
20090004325 Bacher et al. Jan 2009 A1
20090039542 Morton-Finger Feb 2009 A1
20090270564 Gorlier et al. Oct 2009 A1
20090286919 Moeller et al. Nov 2009 A1
20100102475 Moon et al. Apr 2010 A1
20100113626 Liu May 2010 A1
20100152309 Booth Jun 2010 A1
20110177283 Juriga Jul 2011 A1
20110257345 Hoover, Jr. et al. Oct 2011 A1
20120070615 Shi et al. Mar 2012 A1
20120279023 Burout et al. Nov 2012 A1
20150069652 Clark Mar 2015 A1
20150069655 Clark Mar 2015 A1
20150076725 Clark Mar 2015 A1
20150076744 Clark Mar 2015 A1
20170136761 Sieradzki et al. May 2017 A1
20170152611 Clark Jun 2017 A1
20170275785 Williams et al. Sep 2017 A1
20180126595 Clark May 2018 A1
20180127893 Clark May 2018 A1
20180362723 Gneuss et al. Dec 2018 A1
Foreign Referenced Citations (45)
Number Date Country
2013267847 Mar 2014 AU
2014215998 Sep 2014 AU
170967 Aug 1934 CH
1391511 Jan 2003 CN
101444954 Jun 2009 CN
101778705 Jul 2010 CN
201872322 Jun 2011 CN
202072825 Dec 2011 CN
102990903 Mar 2013 CN
104040040 Sep 2014 CN
204265905 Apr 2015 CN
2243024 Mar 1973 DE
3801574 Aug 1989 DE
4433593 Jun 1995 DE
19722278 Dec 1998 DE
102006033089 Oct 2007 DE
102008018686 Oct 2009 DE
102011082769 Mar 2013 DE
102013000316 Jul 2014 DE
102017111275 Nov 2018 DE
0846860 Jun 1998 EP
0881054 Dec 1998 EP
1400332 Mar 2004 EP
2748358 Jul 2014 EP
3375916 Sep 2018 EP
2059864 Apr 1981 GB
1601699 Nov 1981 GB
2141844 Jan 1985 GB
63191823 Aug 1988 JP
2003530478 Oct 2003 JP
2007186830 Jul 2007 JP
2001021373 Mar 2001 WO
2002038276 May 2002 WO
2003033240 Apr 2003 WO
2004026557 Apr 2004 WO
2008017843 Feb 2008 WO
2008083035 Jul 2008 WO
2008083820 Jul 2008 WO
2010133531 Nov 2010 WO
2011088437 Jul 2011 WO
2011095361 Aug 2011 WO
2012119165 Sep 2012 WO
2013180941 Dec 2013 WO
2016081495 May 2016 WO
2018089346 May 2018 WO
Non-Patent Literature Citations (102)
Entry
Restriction Requirement, dated Feb. 5, 2019, from corresponding U.S. Appl. No. 16/220,733.
Notice of Allowance, dated Aug. 1, 2019, from corresponding U.S. Appl. No. 15/396,143.
Office Action, dated Jun. 18, 2019, from corresponding U.S. Appl. No. 16/402,583.
Restriction Requirement, dated Jul. 15, 2019, from corresponding U.S. Appl. No. 16/432,579.
Office Action, dated Jul. 23, 2019, from corresponding U.S. Appl. No. 16/041,442.
“MRS extrusion technology offers new options in PET”, Plastics Additives and Compounding, Elsevier Science, Oxofrd, GB, vol. 11, No. 2, Mar. 1, 2009 (Mar. 1, 2009), pp. 24-26, XP026067788, ISSN: 1464-391X. DOI:10.1016/S1464-391X(09)70050-9 [retrieved on Mar. 1, 2009] the whole document.
“Processing Technology: Processing of Polymer Melts,” Oct. 31, 2007, Gneuss Kunststofftechnik GmbH, Dusseldorf, Germany.
Australian Office Action, dated Aug. 26, 2015, from corresponding Australian Patent Application No. 2014215998.
Australian Office Action, dated Dec. 5, 2016, from corresponding Australian Patent Application No. 2016234917.
Australian Office Action, dated May 9, 2014, from corresponding Australian Patent Application No. 2013267847.
Chinese Office Action, dated May 12, 2016, from corresponding Chinese Patent Application No. 201380003461.8.
Chinese Office Action, dated Sep. 14, 2015, from corresponding Chinese Patent Application No. 201380003461.8.
Decision of Patent Grant, dated Dec. 12, 2014, from corresponding Korean Patent Application No. 10-2014-7016621.
European Office Action, dated Dec. 12, 2016, from corresponding European Patent Application No. 15158377.0.
Extended European Search Report, dated Aug. 26, 2015, from corresponding European Application No. 15158377.0.
Extended European Search Report, dated Jul. 24, 2018, from corresponding European Patent Application No. 18170112.9.
Final Office Action, dated Dec. 24, 2015, from corresponding U.S. Appl. No. 14/256,261.
Final Office Action, dated Oct. 19, 2016, from corresponding U.S. Appl. No. 14/546,819.
Final Office Action, dated Oct. 19, 2016, from corresponding U.S. Appl. No. 14/546,837.
Final Office Action, dated Oct. 19, 2016, from corresponding U.S. Appl. No. 14/546,847.
Final Office Action, dated Oct. 20, 2016, from corresponding U.S. Appl. No. 14/546,796.
Gneuss M: “Multi Rotation System Extruder Leads to Breakthrough in Polymer Evacuation”, International Fiber Journal, International Media Group, Charlotte, NC, US, vol. 23, No. 1, Feb. 1, 2008 (Feb. 1, 2008), pp. 40-41, XP001514827, ISSN: 1049-801X the whole document.
Hannemann, Innovative Aufbereitungslösung für PET mit uneingeschränkter FDA—Lebensmittelzulassung, Presentation, Mar. 15, 2012, 37 pages total, Gneuss Kunststofftechnik GmbH, Germany.
International Search Report, dated Apr. 12, 2018, from corresponding International Application No. PCT/US2018/015751.
International Search Report, dated Feb. 2, 2016, from corresponding International Application No. PCT/US2015/061116.
International Search Report, dated Feb. 2, 2016, from corresponding International Application No. PCT/US2015/061145.
International Search Report, dated Feb. 5, 2016, from corresponding International Application No. PCT/US2015/061174.
International Search Report, dated Jan. 20, 2016, from corresponding International Application No. PCT/US2015/061288.
International Search Report, dated Mar. 1, 2018, from corresponding International Application Serial No. PCT/US2017/060359.
International Search Report, dated Nov. 19, 2018, from corresponding International Application No. PCT/US2018/051043.
International Search Report, dated Sep. 2, 2013, from corresponding International Application No. PCT/US2013/040753.
Invitation to Pay Additional Search Fees, dated Jan. 5, 2018, from corresponding International Application Serial No. PCT/US2017/060359.
Jaecker M: “The Conceptual Concept of the Future // Advantages of the Negative-Conical Gangti EGE on Double-Screw Extruders”, Kunststoffe, Carl Hanser Verlag, Munchen, DE, vol. 99, No. 12, Dec. 1, 2000 (2000-12-91), p. 64,66, XP990976191, ISSN: 9923-5563, figure 1.
Ex Parte Quayle Action, dated Mar. 11, 2019, from corresponding U.S. Appl. No. 16/220,733.
Final Office Action, dated May 22, 2019, from corresponding U.S. Appl. No. 15/396,143.
Notice of Allowance, dated Apr. 17, 2019, from corresponding U.S. Appl. No. 16/220,733.
Notice of Allowance, dated May 1, 2019, from corresponding U.S. Appl. No. 15/419,955.
Office Action, dated May 6, 2019, from corresponding U.S. Appl. No. 15/348,591.
Notice of Allowance, dated Jan. 24, 2019, from corresponding U.S. Appl. No. 15/473,402.
Office Action, dated Aug. 18, 2014, from corresponding Korean Patent Application No. 10-2014-7016621.
Notice of Acceptance, dated Jun. 21, 2016, from corresponding Australian Patent Application No. 2014215998.
Notice of Acceptance, dated Nov. 10, 2014, from corresponding Australian Patent Application No. 2013267847.
Notice of Allowance, dated Apr. 13, 2016, from corresponding U.S. Appl. No. 14/256,261.
Notice of Allowance, dated Dec. 13, 2018, from corresponding U.S. Appl. No. 15/473,385.
Notice of Allowance, dated Feb. 2, 2017, from corresponding U.S. Appl. No. 14/546,819.
Notice of Allowance, dated Feb. 2, 2017, from corresponding U.S. Appl. No. 14/546,837.
Notice of Allowance, dated Feb. 2, 2017, from corresponding U.S. Appl. No. 14/546,847.
Notice of Allowance, dated Feb. 3, 2017, from corresponding U.S. Appl. No. 14/546,796.
Notice of Allowance, dated Jul. 5, 2018, from corresponding U.S. Appl. No. 15/204,645.
Notice of Allowance, dated Oct. 28, 2013, from corresponding U.S. Appl. No. 13/721,955.
Notice of Allowance, dated Sep. 12, 2016, from corresponding U.S. Appl. No. 13/892,713.
Notice of Opposition, dated Dec. 17, 2015, from corresponding European Application No. 13728264.6.
Office Action, dated Apr. 9, 2018, from corresponding U.S. Appl. No. 15/204,645.
Office Action, dated Aug. 21, 2015, from corresponding U.S. Appl. No. 14/256,261.
Office Action, dated Aug. 27, 2018, from corresponding U.S. Appl. No. 15/473,385.
Office Action, dated Aug. 27, 2018, from corresponding U.S. Appl. No. 15/473,402.
Office Action, dated Jun. 1, 2016, from corresponding U.S. Appl. No. 14/546,837.
Office Action, dated Jun. 10, 2013, from corresponding U.S. Appl. No. 13/721,955.
Office Action, dated Jun. 13, 2016, from corresponding U.S. Appl. No. 14/546,847.
Office Action, dated Jun. 22, 2016, from corresponding U.S. Appl. No. 14/546,796.
Office Action, dated Jun. 30, 2016, from corresponding U.S. Appl. No. 13/892,740.
Office Action, dated Mar. 24, 2016, from corresponding U.S. Appl. No. 13/892,713.
Office Action, dated May 26, 2016, from corresponding U.S. Appl. No. 14/546,819.
Office Action, dated Oct. 9, 2018, from corresponding U.S. Appl. No. 15/419,955.
Office Action, dated Sep. 7, 2018, from corresponding U.S. Appl. No. 15/396,143.
Restriction Requirement, dated Apr. 30, 2013, from corresponding U.S. Appl. No. 13/721,955.
Schiefer,Process Engineering, Rowohlt Taschenbuch Verlag GmbH, Aug. 1972.
Vietnamese Office Action, dated Jul. 13, 2016, from corresponding Vietnamese Patent Application No. 1-2014-01079.
Wikipedia, Polyethylene terephthalate, https://en.wikipedia.org/w/index.php?title=Polyethylene_terephthalate&oldid=491494734.
Written Opinion of the International Searching Authority, dated Apr. 12, 2018, from corresponding International Application No. PCT/US2018/015751.
Written Opinion of the International Searching Authority, dated Feb. 2, 2016, from corresponding International Application No. PCT/US2015/061116.
Written Opinion of the International Searching Authority, dated Feb. 2, 2016, from corresponding International Application No. PCT/US2015/061145.
Written Opinion of the International Searching Authority, dated Feb. 5, 2016, from corresponding International Application No. PCT/US2015/061174.
Written Opinion of the International Searching Authority, dated Jan. 20, 2016, from corresponding International Application No. PCT/US2015/061288.
Written Opinion of the International Searching Authority, dated Mar. 1, 2018, from corresponding International Application Serial No. PCT/US2017/060359.
Written Opinion of the International Searching Authority, dated Nov. 19, 2018, from corresponding International Application No. PCT/US2018/051043.
Written Opinion of the International Searching Authority, dated Sep. 2, 2013, from corresponding International Application No. PCT/US2013/040753.
Office Action, dated Aug. 8, 2019, from corresponding U.S. Appl. No. 16/409,599.
International Preliminary Report on Patentability, dated Aug. 8, 2019, from corresponding International Application No. PCT/US2018/015751.
Office Action, dated Aug. 13, 2019, from corresponding U.S. Appl. No. 16/213,694.
Botos, J., et al., “Color Measurement of Plastics—from Compounding via Pelletizing, up to Injection Molding and Extrusion,” AIP Conference Proceedings 1593, 16 (2014), https://doi.org/10.1063/1.4873725, Feb. 17, 2015.
Machado, Almir De Souza, “Fundamentals of Cast Film Extrusion Technology,” https://www.slideshare.net/ASMachado/fundamentals-of-cast-film-extrusion-technology, Dec. 2, 2013.
Notice of Allowance, dated Aug. 19, 2019, from corresponding U.S. Appl. No. 16/402,583.
Austrian Patent Application No. A 330/2011, filed Mar. 10, 2011, entitled “Verfahren und Vorrichtung zum Entfernen von Verunreinigungen aus einer Kunststoffschmelze”.
International Search Report, dated Jul. 5, 2012, from corresponding International Application No. PCT/AT2012/000052.
International Search Report, dated Oct. 30, 2019, from corresponding International Application No. PCT/US2019/042456.
Invitation to Pay Additional Fees, dated Oct. 18, 2019, from corresponding International Application No. PCT/US2019/042458.
Office Action, dated Nov. 25, 2019, from corresponding U.S. Appl. No. 15/804,501.
Written Opinion of the International Searching Authority, dated Oct. 30, 2019, from corresponding International Application No. PCT/US2019/042456.
Office Action, dated Dec. 2, 2019, from corresponding U.S. Appl. No. 16/664,730.
Office Action, dated Nov. 29, 2019, from corresponding U.S. Appl. No. 16/557,076.
Office Action, dated Sep. 12, 2019, from corresponding U.S. Appl. No. 16/432,579.
Notice of Allowance, dated Oct. 10, 2019, from corresponding U.S. Appl. No. 16/432,579.
Final Office Action, dated Jan. 9, 2020, from corresponding U.S. Appl. No. 15/348,591.
International Search Report, dated Dec. 10, 2019, from corresponding International Application No. PCT/US2019/042458.
Office Action, dated Jan. 29, 2020, from corresponding U.S. Appl. No. 16/684,490.
Written Opinion of the International Searching Authority, dated Dec. 10, 2019, from corresponding International Application No. PCT/US2019/042458.
Notice of Allowance, dated Feb. 3, 2020, from corresponding U.S. Appl. No. 16/041,442.
Office Action, dated Feb. 21, 2020, from corresponding U.S. Appl. No. 15/910,853.
Notice of Allowance, dated Feb. 28, 2020, from corresponding U.S. Appl. No. 16/664,730.
Notice of Allowance, dated Mar. 3, 2020, from corresponding U.S. Appl. No. 16/213,694.
International Preliminary Report on Patentability, dated Mar. 26, 2020, from corresponding International Application No. PCT/US2018/051043.
Related Publications (1)
Number Date Country
20190118450 A1 Apr 2019 US
Provisional Applications (1)
Number Date Country
61654016 May 2012 US
Divisions (1)
Number Date Country
Parent 13721955 Dec 2012 US
Child 13892740 US
Continuations (2)
Number Date Country
Parent 15473402 Mar 2017 US
Child 16220905 US
Parent 14546819 Nov 2014 US
Child 15473402 US
Continuation in Parts (1)
Number Date Country
Parent 13892740 May 2013 US
Child 14546819 US