1. Field of the Invention
An embodiment of the present invention relates to microelectronic device fabrication. In particular, an embodiment of the present invention relates to methods for forming a nitrogen-containing barrier layer for conductive interconnects.
2. State of the Art
The microelectronic device industry continues to see tremendous advances in technologies that permit increased integrated circuit density and complexity, and equally dramatic decreases in package sizes. Present semiconductor technology now permits single-chip microprocessors with many millions of transistors, operating at speeds of tens (or even hundreds) of MIPS (millions of instructions per second), to be packaged in relatively small, air-cooled microelectronic device packages. These transistors are generally connected to one another or to devices external to the microelectronic device by conductive traces and contacts through which electronic signals are sent and/or received.
A typical process of forming traces and contacts includes patterning a photoresist material on a dielectric material and etching the dielectric material through the photoresist material pattern to form a hole and/or a trench (hereinafter referred to collectively as an “opening”) extending into the dielectric material. The photoresist material is then removed (typically by an oxygen plasma) and a barrier layer may be deposit within the opening to prevent conductive material (particularly copper and copper-containing alloys), which will be subsequent be deposited into the opening, from migrating into dielectric material. The migration of the conductive material can adversely affect the quality of microelectronic device, such as leakage current and reliability between the interconnects. A barrier layer is deposited onto a dielectric layer to line the opening. In addition to lining the opening, the barrier layer extends across a top surface of the dielectric layer.
A seed material may then be deposited on the barrier layer, followed by performing a conventional plating process to form a conductive material layer. Like the barrier layer, excess conductive material layer may form on the dielectric layer. The resulting structure is planarized, usually by a technique called chemical mechanical polish (CMP), which removes the copper layer and adhesion layer that are not within the opening from the surface of the dielectric material, to form the interconnect.
Copper has superior conductive properties when used as the conductive material, but is very phone to electomigration. Barrier layers used for copper-containing conductive materials are usually nitrogen-containing materials, including, but not limited to, tantalum nitride and titanium nitride. As the nitrogen-containing barrier layer needs to be a thin as possible, it is generally deposited by an atomic layer deposition (ALD). The conformal step coverage characteristics and thickness control of ALD are preferred for processes that require thin, uniform coverage. ALD relies on self-limiting chemisorption of a reactant molecule (precursor) on targeted deposition surfaces, as will be understood to those skilled in the art.
In one example, an ultrathin ALD nitrogen-containing film may be used as a barrier layer for copper-containing interconnect structures abutting a low-k dielectric material (i.e., any material with a dielectric constant lower than silicon dioxide). As the dimensions of the interconnects are reduced, the nitrogen-containing barrier layer must be very thin (˜10-20 Å) to ensure that the fraction of higher resistivity nitrogen-containing barrier layer is kept to a minimum, such that the overall resistivity of the interconnect remains low.
However, the ALD process to form nitrogen-containing barrier creates volatile by-products, particularly organic amines, ammonia, and 1-methyl-2-pyrrolidone (NMP) (in mere parts per billion) that are generated from the organometallic precursors used in the ALD process, such as pentakis(dimethylamido)tantalum, tert-butylimidotris(diethylamido)tantalum, Ta[NC(CH3)2C2H5][N(CH3)2]3, and the like, in combination with a reducing agent of ammonia when forming tantalum nitride barrier layer. These volatile by-products can neutralize photoresists, particularly amplified deep-ultraviolet photoresists, including but not limited to poly(t-butylmethacrylate). Such photoresists use a chemical amplification process that is dependent on photogenerated acid produced during the exposure step. The neutralization of the photogenerated acids by the by-products result in the inability to completely develop the exposed photoresist during the lithographic process leaving only the latent image on the wafer, as will be understood to those skilled in the art. This neutralization can occur during the lithographic process from the by-products which can become trapped in the low-k dielectric and diffuse out during the lithographic process, as well as from the by-products which have become airborne contaminants.
Therefore, it would be advantageous to develop apparatus and techniques to form a barrier layer which does not result in the generation of damaging volatile by-products.
While the specification concludes with claims particularly pointing out and distinctly claiming that which is regarded as the present invention, the advantages of this invention can be more readily ascertained from the following description of the invention when read in conjunction with the accompanying drawings to which:
In the following detailed description, reference is made to the accompanying drawings that show, by way of illustration, specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention. It is to be understood that the various embodiments of the invention, although different, are not necessarily mutually exclusive. For example, a particular feature, structure, or characteristic described herein, in connection with one embodiment, may be implemented within other embodiments without departing from the spirit and scope of the invention. In addition, it is to be understood that the location or arrangement of individual elements within each disclosed embodiment may be modified without departing from the spirit and scope of the invention. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined only by the appended claims, appropriately interpreted, along with the full range of equivalents to which the claims are entitled. In the drawings, like numerals refer to the same or similar functionality throughout the several views.
An embodiment of the present invention relates to the fabrication of a barrier layer for a microelectronic device interconnect, wherein the fabrication process utilizes a nitrogen plasma to form the barrier layer.
One embodiment of a process used to form an interconnect according to the present invention, comprises patterning a photoresist material 102 on a dielectric material layer 104, as shown in
As shown in
The metal layer 108 (
The nitrogen atoms 116 are preferably generated by a nitrogen plasma. Nitrogen plasmas are very stable and long-lived and, thus, can be located remotely from the target where the reaction occurs. Nitrogen plasmas essentially split nitrogen gas into reactive species, including nitrogen atoms, nitrogen ions, and metastable or excited nitrogen molecules. These nitrogen plasmas are free of amines and, thus, do not pose a threat of photoresist poisoning, as discussed above. The nitrogen atoms 116 needed to form the nitrided barrier layer 118 are generated in concentrations which are several orders of magnitude greater than the concentration of the other species generated in the plasma field. Therefore, the other species generated in the plasma will have an insignificant impact on the formation of the stoichiometric TaN barrier layer 118.
As shown in
Referring back to the plasma process in the formation of the nitrided barrier layer 118, as the nitrogen atom concentration remains relatively constant away from or downstream from the plasma field, a suitable ALD reactor 132 could be designed to incorporate a remote nitrogen plasma source, as shown in
It is, of course, understood that the nitrogen plasma 142 may be struck proximate the target 150. As shown in
158. The RF source 156 creates an RF field within the nitrogen gas in the reaction chamber 146 delivered through an inlet 162, and this coupling creates the nitrogen plasma 142.
Having thus described in detail embodiments of the present invention, it is understood that the invention defined by the appended claims is not to be limited by particular details set forth in the above description, as many apparent variations thereof are possible without departing from the spirit or scope thereof.