Methods of fabricating microsponge deuterated hydrocarbon polymer targets which emit neutrons when irradiated by high energy beams

Abstract

Targets for high energy beams, such as laser beams, produced in laser fusion apparatus are described. The targets are porous spheres of deuterated hydrocarbon material, particularly deuterated polyethylene. The spheres are small and have diameters in the range of 50 to 300 microns. Higher neutron yields are obtained from these targets than from solid targets of similar materials, (viz, spherical targets of much higher density). Methods of fabricating the targets by forming them into solid spheres, cross linking their molecules and causing them to swell such that the resultant targets have a microscopically small sponge-like structure, are also described.

Description

The present invention relates to methods of fabricating targets for high energy beams which are generated in thermo-nuclear apparatus, such as laser fusion apparatus.

The invention is especially suitable for use in providing laser fusion targets. The structure of these targets is such that their implosion dynamics during interaction with a pulse of laser radiation more readily obtains thermo-nuclear burn conditions than is the case with conventional targets.

Conventional laser fusion targets are in the form of solid spherical bodies of deuterium or deuterium containing compounds. Such targets are described in an article by W. D. Friedman, G. M. Halpern and B. A. Brinker, entitled "Target Fabrication and Positioning Techniques for Laser Fusion Experiments," which appeared in the Review of Scientific Instruments, Volume 45, No. 10, October 1974, pages 1245 to 1252. Reference may be had to the aforementioned article and to an article by J. Soures, L. M. Goldman and M. Lubin, entitled "Short-Pulse Laser Heated Plasma Experiments" which appeared in "Nuclear Fusion" Volume 13 (1973) pages 829 to 838; and to M. J. Lubin, U.S. Pat. No. 3,723,246, issued Mar. 27, 1973, for descriptions of laser fusion apparatus in which both solid targets and targets provided by this invention may be used.

The following U.S. patent applications, which are assigned to the same assignee as this application, are related to this application in that they are concerned with targets which are adapted for use in laser fusion and the like apparatus. The applications are: Ser. No. 479,921, filed June 17, 1974 in the name of Gerald M. Halpern and Yehuda Paiss; and Ser. No. 547,143, filed Feb. 5, 1975 in the name of Russell R. Chianelli now U.S. Pat. No. 3,987,590. Publications and patents referred to and cited in the Halpern and Paiss application may also be referred to for further information respecting laser fusion and the like apparatus and targets for use therein.

It is an object of this invention to provide improved methods of fabricating targets which have higher neutron yields than conventional targets when irradiated by high energy beams, such as laser beams.

It is another object of the present invention to provide improved methods of fabricating targets which are especially adapted to be heated and compressed to obtain thermonuclear conditions when high energy beams, such as laser beams, are incident thereon.

It is a further object of the present invention to provide improved methods of fabricating thermonuclear fuel elements which are especially adapted for use in laser fusion apparatus.

It is a still further object of the present invention to provide improved methods of fabricating targets from which high temperature plasmas can be obtained when heated by laser radiation.

It is a still further object of the present invention to provide improved methods of fabricating targets of deuterated hydrocarbon material for use in laser fusion apparatus.

It is a still further object of the present invention to provide improved methods of fabricating targets which are of porous structure and spherical shape from deuterated hydrocarbon materials, such as deuterated polyethylene.

Briefly described, a target provided by the present invention is a ball, preferably spheroidal or spherical in shape, of deuterated hydrocarbon material, preferably a polymer such as deuterated polyethylene, which may be of the type which is commercially available or which may be fabricated in accordance with well known polyethylene fabrication techniques. The targets themselves are exceedingly small, say in the range of 50 to 300 microns in diameter. Notwithstanding their small size, they have a structure extending inwardly from the surface thereof which is porous and sponge-like. The porous sponge-like structure may be a shell about a core of the body which is either solid or completely hollow. The body may have the porous sponge-like structure throughout. For a given amount of energy (e.g., laser pulse energy of the laser beam which is incident on the target as in a laser fusion apparatus) the targets compress and have improved implosion dynamics over solid spheres and produce higher neutron yields than such solid spheres.

Briefly described the method of producing such improved targets includes the forming of the deuterated hydro-carbon material (viz, deuterated polyethylene) into solid bodies which may be spheroidal or spherical in shape. The molecules of the material of these bodies are then cross-linked as by being irradiated with gamma rays. Then the cross-linked bodies are increased in size by causing these bodies to swell, with the aid of a fluid. The fluid is then removed (say by vacuum drying). The resultant bodies have the aforementioned porous sponge-like structure.

The foregoing and other features, objects and advantages of the invention as well as the best mode for practicing and carrying out the invention and the presently preferred embodiments thereof will become more apparent from the following description and the accompanying drawings in which:

FIG. 1 is a perspective view, broken away to show the cross-sectional structure thereof, of a target which is provided in accordance with the invention;

FIG. 2 is a view similar to FIG. 1 of a target provided in accordance with another embodiment of the invention; and

FIG. 3 is a view similar to FIG. 1 of a target provided in accordance with still another embodiment of the invention.

FIG. 1 illustrates a target in the form of a sphere of deuterated polyethylene which, instead of being solid, has a porous sponge-like structure throughout. The sphere may be of a diameter in the range of about 300 microns and by virtue of the porous structure thereof has a density of from 0.1 to 0.2 grams per cubic centimeter. This is approximately 10 to 20 percent of the density of solid polyethylene. Inasmuch as the pores in the structure are microscopic in size the target may be referred to as a "microsponge" target.

The target may be located at the focus of one or more laser beams in laser fusion apparatus of the type described in the above referenced articles, and/or in the Lubin patent. When laser pulse energy is incident on the target the target implodes and compresses. The result is a laser fusion reaction since the target material is heated to thermonuclear burn condition. Neutrons result from the reaction. By virtue of the structure of the target, the neutron yield may be one or two orders of magnitude greater than the yield obtained from a solid sphere of like diameter for a like amount of laser pulse energy, (viz, an increase of a factor of about 100 neutron yields may be realized with a microsponge target as shown in FIG. 1).

FIG. 2 illustrates a microsponge target of similar size and shape as the target shown in FIG. 1. It will be noted, however, that only the outer shell 14 of the target is of the microsponge structure. The target has a core 16 which is solid. Both the shell 14 and the core 16 are of the same deuterated hydrocarbon material (e.g., polyethylene).

FIG. 3 shows a target of similar size and shape to the target shown in FIGS. 1 and 2. The target has an outer shell 18 of microsponge structure and a core 19 which is hollow. The hollow core provides a target which can be even more compressible and may have better implosion dynamics than the structure which is porous (microsponge) throughout, as shown in FIG. 1 or has a microsponge outer shell 14 and a solid core 16.

To fabricate targets such as shown in FIG. 1, the starting material used may for example be commercially available deuterated linearpolyethylene. A preferred material is polyethylene having a low molecular weight such that it flows at temperatures just above its melting point. Polyethylene having a melt index of from about 10 to about 15 may be used. The deuterated polyethylene which is obtainable from Bendix Corporation, Kansas City Division, Kansas City, Mo., 64141, having a melt index of 14.4 is suitable, by way of specific example.

The polyethylene polymer is then ground to a fine powder preferably by a micro blender, such as Model No. 4300 manufactured by Cole-Parmer of Chicago, Ill., which is chilled with liquid nitrogen so as to make the polymer essentially brittle and enhance the pulverization thereof into fine powder. The material is pulverized to desired size (e.g., from 25 to 200 microns in diameter) by utilizing a sufficiently long grinding time in the micro blender and then sieving the particles which are below the maximum size desired (e.g., of about 200 microns maximum diameter).

The powder is then heated in a vessel containing silicone oil, Dow-Corning 20 Centistoke silicone oil for example, which is maintained at a temperature of about 150.degree. C, for about ten minutes. The vessel containing the oil is gently agitated to minimize agglomeration of the particles. The vessel is then quenched by placing it in ice (ordinary wet ice). The resultant bodies are spherical in shape (spheres or spheroids) due to their melting in the silicone oil. Accordingly, the powder particles are formed into hard or dense spheres of from about 25 to about 200 microns in diameter. These bodies are washed in order to remove any residual silicone oil which may remain thereon. Washing in a solution of trichloroethylene, chloroform and methanol is preferably used to remove the residual silicone oil.

A batch of spherical bodies is then sealed in an evacuated glass tube and exposed to a flux of gamma rays. For example 1 megavolt (MeV) gamma rays derived from a cobalt 60 radiation source may be used. Dosages in a range from about 10 to about 40 megarads (MRad) is suitable, with a dosage in the range of from 20 to 30 MRad being preferred. The density of the resulting targets is a function of dosage, with lower dosages providing lower density and higher dosages providing higher density. Thus, the density can be continuously controlled ranging from about 10 to 100% of the bulk density value of the starting material.

In the event that targets having a hollow core such as shown in FIG. 3 are desired, the cross linking of only the outer layers of the spherical bodies is accomplished by using lower energy radiation. For example, 50 KeV electrons from an electron gun source.

The crosslinked spheres are then removed from the glass tube and caused to be increased in size by swelling to about 1 1/2 to 2 times their original diameters. Swelling may be carried out by means of a fluid which diffuses into the bodies, dissolves the uncrosslinked component and expands the remainder. For example, a bath of hot solvent may be used to cause the crosslinked spheres to swell. The temperature of the bath is preferably from about 90.degree. to about 120.degree. C in order to obtain the swelling without softening of the spheres and agglomeration or deformation thereof. A preferable temperature range for para-xylene is 100.degree. to 110.degree. C. The solvent may for example be para-xylene which is maintained at a temperature of about 105.degree. C. The crosslinked spheres are immersed in the bath and maintained there for about 2 hours. The temperature of the bath and the immersion time determines the extent to which the solvent penetrates and diffuses into the spherical body. In the event that a low density shell surrounded by a high density core is desired (viz, the structure of the target shown in FIG. 2), it is desired that the solvent diffusion be incomplete and extend only into the outer layer of the spherical body. In order to obtain such incomplete diffusion and swelling of the outer shell of the bodies, swelling times of less than 1 hour can be used. The ratio of diameter of shell to diameter of core is controlled by both swelling time and temperature and may be selected accordingly.

The structure shown in FIG. 3 is obtained by virtue of the dissolution of the uncrossed linked core of the bodies by the solvent, while the crosslinked shell is only partially dissolved in a manner to form the highly porous micro structure common to the target shown in FIGS. 1, 2 and 3.

After the swelling time has expired, the vessel containing the bath is rapidly quenched by immersion in wet ice. This rapidly cools the bodies below their crystallization temperature and freezes in the highly porous micro structure. The excess solvent is then drained off and the spherical bodies are vacuum dried at room temperature for several hours to remove any residual solvent.

When the particles are dried they exhibit a snowball-like appearance due to light scattering from the highly porous micro structure. They are soft to the touch, in sharp contrast to solid spherical bodies of similar material. The diameters of the bodies vary from about 50 to 400 microns while the pores or cells which make up the micro structure are typically 1 micron or smaller in size. The densities of the microsponge targets may range from about 0.13 to 0.23 grams per cubic centimeter as compared to solid deuterated polyethylene spheres (before swelling) which is about 0.96 grams per cubic centimeter.

From the foregoing description it will be apparent that there has been provided improved targets for use in laser fusion apparatus or like apparatus which uses high energy beams in order to produce plasma and/or yield neutrons as a result of interactions of the particles with the beams. The balls of microsponge material are thus improved laser fusion targets. Variations and modifications in the targets themselves as well as in the methods of fabrication as described herein, within the scope of the invention, will undoubtedly suggest themselves to those skilled in the art. Accordingly, the foregoing description should be taken merely as illustrative and not in any limiting sense.

Claims

1. A method for the fabrication of elements, for use as targets for a high energy beam, and which provide neutrons by interaction with said beam, said method comprising the steps of

(a) forming deuterated hydrocarbon polymer material into solid bodies which are of sizes which are less than about 300 microns diametrically,

(b) cross-linking the molecules of the material with radiation, and

(c) increasing the size of said cross linked bodies while reducing the mass thereof with the aid of a fluid which is a solvent for the un-cross-linked portions of the material and a swelling agent for the cross-linked portions thereof which causes said bodies to partially dissolve and to swell, thereby providing said bodies with a micro-sponge structure of cells of a size which does not exceed about 1 micron, said microsponge structure bodies providing said elements.

2. The invention as set forth in claim 1 wherein said beam is a beam of laser radiation, and laser fusion reactions with said targets are the source of said neutrons.

3. The invention as set forth in claim 1 wherein said material of said body is a deuterated ethylenic hydrocarbon polymer.

4. The invention as set forth in claim 3 wherein said polymer is deuterated polyethylene.

5. The invention as set forth in claim 4 wherein said polyethylene has a low molecular weight characterized by a melt index of from about 10 to about 15.

6. The invention as set forth in claim 3 wherein said forming step is carried out by forming said material into spheroids.

7. The invention as set forth in claim 6 wherein said forming step is carried out by pulverizing said material into powder, and thereafter agitating and melting the individual particles of the powder, and cooling said melted powder particles while continuing to agitate them thereby forming them into hard, dense spheres.

8. The invention as set forth in claim 7 wherein said material is polyethylene having a melt index of from about 10 to 15 and said agitating and melting steps are carried out by heating said powder particles in a vessel containing silicone oil having a temperature of about 150.degree. C for about 10 minutes while agitating the container sufficiently to prevent agglomeration of the particles, and said cooling step is carried out by quenching the container in wet ice.

9. The invention as set forth in claim 8 wherein said forming step includes the further steps of filtering said particles from said oil, and washing said filtered particles to remove residual oil therefrom.

10. The invention as set forth in claim 1 wherein said crosslinking is carried out with the aid of gamma radiation to which said bodies are exposed.

11. The invention as set forth in claim 10 wherein said material is an ethylenic hydrocarbon polymer.

12. The invention as set forth in claim 11 wherein the dosage of said radiation to which said polymer is exposed is within the range of dosage greater than that which results in complete dissolution of said bodies by said solvent, and is less than that which results in negligible swelling of said bodies.

13. The invention as set forth in claim 12 wherein said range is from 10 to 40 MRads.

14. The invention as set forth in claim 13 wherein said polymer is polyethylene.

15. The invention as set forth in claim 1 wherein said fluid is a solvent for the un-cross-linked portions of said material and a swelling agent for the cross-linked portions thereof, and said size increasing step is carried out by emersing said cross-linked bodies in a bath of said solvent until they increase in size about 1 and 11/2 to twice in size.

16. The invention as set forth in claim 15 wherein after said immersing step, said solvent is removed from said bodies.

17. The invention as set forth in claim 16 wherein said bath is heated, and wherein after said bodies have reached their increased size, said bath is cooled below the crystallization temperature of said material.

18. The invention as set forth in claim 16 wherein said material is polyethylene, said bodies are formed into spherical shape and said solvent heated to a temperature in the range of from about 100.degree. to 110.degree. C.

19. The invention as set forth in claim 17 wherein said cooling step is carried out by quenching the container for said bath in ice.

20. The invention as set forth in claim 18 wherein said immersing step is carried out for at least 1 hour.

21. The invention as set forth in claim 19 wherein said solvent is para-xylene.