The disclosure relates to relates to microchemical (or microfluidic) apparatus as well as related methods for making the same. The methods generally include partial sintering of sintering powder, removal of a fugitive phase material within the powder to create internal cavities, and then fully sintering the partially sintered compact to provide apparatus with controllable, small, and smooth cavity structures.
Current methods for forming apparatus from sintered powders are often limited in that they require additional components or phases such as binders and/or filler materials. The methods can often result in relatively low-density sintered products with relatively rough interior surface finishes. Methods of making microchemical apparatus from silicon or polymeric materials are generally not suitable for extreme conditions that can be experienced within the apparatus for some applications.
The disclosure relates to microchemical (or microfluidic) apparatus as well as related methods for making the same. The methods generally include partial sintering of sintering powder (e.g., binderless or otherwise free-flowing sintering powder) that encloses a fugitive phase material having a shape corresponding to a desired cavity structure in the formed apparatus. Partial sintering removes the fugitive phase and produces a porous compact, which can then be machined if desired and then further fully sintered to form the final apparatus. The process can produce apparatus with small, controllable cavities shaped as desired for various microchemical or microfluidic unit operations, with a generally smooth interior cavity finish, and with materials (e.g., ceramics) able to withstand harsh environments for such unit operations.
In one aspect, the disclosure relates to a method for forming a microchemical (or microfluidic) apparatus, the method comprising: (a) providing a (free) first metal oxide powder or nanopowder (e.g., as a layer of (binderless) free-flowing powder in a die or other container, such as to conform the powder to a desired shape prior to sintering and generally corresponding to the shape of the eventual sintered product); (b) placing a first fugitive phase material in the first metal oxide powder (e.g., setting on or (slightly) impressed into a top or other layer of the free-flowing first metal oxide powder), the first fugitive phase material having a geometry corresponding to a negative cavity geometry in the formed microchemical apparatus; (c) placing a (free) second metal oxide powder or nanopowder over the first metal oxide powder and over the first fugitive phase material (e.g., as a layer of free-flowing powder in the die or other container with the first metal oxide powder and first fugitive phase material, such as to conform the first and second metal oxide powders collectively to a desired shape enveloping the first fugitive phase material); (d) partially sintering the first metal oxide powder and the second metal oxide powder at a temperature and pressure sufficient (i) to convert the first fugitive phase material to a gaseous material (e.g., via decomposition, oxidation, or other process) and (ii) to convert the first metal oxide powder and the second metal oxide powder to a porous, partially sintered compact, thereby allowing the gaseous material to escape from the partially sintered compact interior volume and forming an interior cavity within the partially sintered compact interior volume having a geometry corresponding to the original first fugitive phase material geometry; (e) optionally machining the partially sintered compact (e.g., to form one or more channels providing a gaseous or liquid fluid connection between the interior cavity and the external environment to the partially sintered compact, such as by drilling holes through an exterior surface of the compact into the interior cavity); and (f) fully sintering the partially sintered compact at a temperature and pressure sufficient to form a (non-porous) fully sintered microchemical (or microfluidic) apparatus comprising the interior cavity (e.g., the interior cavity from the partially sintered compact and generally corresponding to the original fugitive phase material, where the cavity geometry could be altered in the final, full sintering process, although the degree of shrinking is generally known and controllable to correspondingly precisely control the desired shape and size of the resulting cavity). The machining step (e) is optional for example when the fugitive phase material is shaped so that one or more of its sides/edges abuts a side/edge of the original powder structure formed by the first and second metal oxide powders, thereby forming an inlet and/or outlet port for fluid connection without need for machining. In some cases, it is desirable to include the machining step when there is a limitation in the shape of the fugitive phase relative to the desired inlet and/or outlet port geometry.
In another aspect, the disclosure relates to microchemical (or microfluidic) apparatus formed according to any of the methods disclosed herein. In a refinement, the apparatus is a unitary structure formed by partially and then fully sintering a single collective arrangement of metal oxide powder and fugitive phase material prior to forming the apparatus (e.g., the apparatus is formed without joining together multiple partially or fully sintered apparatus components).
In another aspect, the disclosure relates to microchemical (or microfluidic) apparatus comprising: a fully sintered metal oxide body comprising an interior cavity within the body; wherein: the interior cavity has a minimum dimension (or minimum feature size) in a range from 1 μm to 800 μm (e.g., at least 1, 2, 5, 10, 20, 50, 100, 200, or 300 μm and/or up to 10, 20, 50, 100, 200, 300, 400, 500, 800, or 1000 μm; such as about 100 μm to 500 μm or 100 μm to 1000 μm; minimum dimension or feature size can correspond to a minimum diameter or width of a channel element in the cavity); and the interior cavity has a surface roughness of 20 μm or less (e.g., at least 1,2, 3, or 5 μm and/or up to 5, 8, 10, 15, or 20 μm).
Various refinements of the first and second metal oxide powders are possible. In a refinement, the first metal oxide powder and the second metal oxide powder are substantially free from binder (e.g., completely free from binder and optionally further substantially free from non-metal oxide material such as glass filler; the sintering powders can contain up to 0.01, 0.1, 0.2, 0.5, 1, 2, or 5 wt. % of materials other than metal oxide powders, which can be a single type of metal oxide powder or multiple types of metal oxide powders in admixture prior to sintering; the first and second metal oxide (or other sintering) powders can be combined in any proportions relative to the total powder).
In another refinement, the first metal oxide powder and the second metal oxide powder independently have a particle size in a range from 1 nm to 1000 nm (e.g., a number-, mass-, or volume-average size or diameter, such as at least 1, 10, 20, 50, 100, or 200 nm and/or up to 10, 20, 50, 100, 200, 400, 600, 800, or 1000 nm; such as about 50 nm to 500 nm; same or different size parameter for the first and second powders).
In another refinement, first metal oxide powder and the second metal oxide powder comprise the same or different ceramic material. In some embodiments, the first and second sintering powders can be other than metal oxide powders (e.g., non-metal oxide ceramics). Some ceramics such as nitrides can be used if oxidation does not occur below the fugitive phase (e.g., graphite or otherwise) burnout temperature. For example, silicon nitride can be used where the graphite can be burnout at about 800° C., and the partially sintered silicon nitride can be fully sintered in nitrogen environment at a higher full sintering temperature.
In another refinement, the first metal oxide powder and the second metal oxide powder comprise one or more of aluminum oxide, zirconium oxide, hydroxyapatite, and zirconiatungstate. More generally, any metal oxide (or other sinterable ceramic material) that can be sintered at higher temperature than the fugitive phase burnout temperature is suitable as the sintering powder(s).
Various refinements of the fugitive phase materials are possible. In a refinement, the first fugitive phase material comprises graphite. Other fugitive phases such as carbon pastes and polymeric materials (e.g. epoxy) can be used, but they often have higher coefficients of thermal expansion (CTE) relative to graphite, which can causes structural failure during sintering.
In another refinement, the first fugitive phase material is in the form of a single piece. For example it can be machined as a monolithic form having the desired shape of the cavity to be formed; the single piece can have a generally planar/2-dimensional shape with its structural features and corresponding eventual cavity/channel elements being substantially in a plane. Alternatively, the single piece can have a generally 3-dimensional shape with its structural features and corresponding eventual cavity/channel elements extending substantially three dimensions, such as forming a 3-dimensional channel network; in another embodiment, the first fugitive phase material can be multiple pieces that are placed on the first metal oxide powder so that they are touching and will form a single connected cavity. In another embodiment, the first fugitive phase material can be multiple pieces that are placed on the first metal oxide powder so that they are not touching and will form multiple separate cavities. In cases where the fugitive phase has a 3-dimensional shape, the sintering powder preferably is distributed uniformly and, instead of uniaxial compaction, hydrostatic pressure can be applied. For example, a circular cavity using cylinder-shaped fugitive phase can be formed. Similarly, multilayered cavities (isolated or connected) can be formed.
In another refinement, the first fugitive phase material has a minimum dimension (or minimum feature size) in a range from 1 μm to 1000 μm (e.g., at least 1, 2, 5, 10, 20, 50, 100, 200, or 300 μm and/or up to 10, 20, 50, 100, 200, 300, 400, 500, 800, or 1000 μm; such as about 100 μm to 500 μm or 100 μm to 1000 μm; minimum dimension or feature size can correspond to a minimum diameter or width of a fugitive phase material element that corresponds to a minimum diameter or width of a channel element in the eventual formed cavity)
In another refinement, the first fugitive phase material has a minimum dimension (or minimum feature size) in a range from 1 nm to 1000 nm (e.g., at least 1, 2, 5, 10, 20, 50, 100, 200, or 300 nm and/or up to 10, 20, 50, 100, 200, 300, 400, 500, 800, or 1000 nm; such as about 2 nm to 500 nm or 5 nm to 100 nm; such as when nano-scale fugitive phase material like exfoliated graphene nanoplatelets is used).
In another refinement, the first fugitive phase material is substantially free from sharp edges (e.g., rounded or otherwise polished or smoothened surfaces (such as by machining) such that sintering powder flow in and around the fugitive phase is not impeded, as sharp fugitive phase material edges deter the powder flow; the corresponding interior cavity walls formed in the final apparatus body can have a low surface roughness, in particular when the fugitive phase material surface is close to perpendicular to the compaction direction and the sintering powder will fill in the all the crevices).
In another refinement, the first fugitive phase material has a surface area of 50% or less of the surface area of a layer of the first metal oxide powder in a plane on which the first fugitive phase material is placed (e.g., a surface area of 50%, 40%, 30%, 20%, 10%, 5%, 2%, or 1% or less and/or at least 0.1%, 1%, 2%, 5%, 10%, or 20% relative to the area of the first metal oxide powder layer).
In another refinement, the first fugitive phase material has a coefficient of thermal expansion of 10 μm/(m*K) or less (e.g., a coefficient of thermal expansion of 1, 2, 4, 5, 6, 8, or 10 μm/(m*K) or less and/or at least 0.01, 0.1, 1, or 2 μm/(m*K), such as 1-8 μm/(m*K) or 2-6 μm/(m*K)).
Various refinements of the sintering steps are possible. In a refinement, partially sintering comprises heating to a temperature in a range from 700° C. to 900° C. (e.g., depending on the burnout temperature of the fugitive phase material, such as based on graphite grade for a specific material).
In another refinement, fully sintering comprises heating to a temperature in a range from 1100° C. to 2000° C. (e.g., where the full sintering temperature depends on the type of metal oxide and final target density; for aluminum oxide, for example, sintering at 1350-1400° C. achieves a density of over 96%, which is sufficient for microreactor applications).
Various refinements of the sintered microchemical apparatus are possible. In a refinement, the fully sintered microchemical apparatus has a density of at least 80% relative to the theoretical density of the first and second metal oxide powders (e.g., at least 80%, 85%, 90%, 95%, or 98% and/or up to 90%, 95%, 98%, 99% or 100% of the theoretical density of the sintering composition/metal oxide powder components thereof, taking into account the solid structure of the apparatus but excluding the void interior volume/cavity therein, where higher density corresponds to lower porosity and higher mechanical strength).
In another refinement, the interior cavity of the microchemical apparatus has a surface roughness of 20 μm or less (e.g., at least 1,2, 3, or 5 μm and/or up to 5, 8, 10, 15, or 20 μm).
In another refinement, the microchemical apparatus has a structure adapted to function as a microchemical system selected from the group consisting of a chemical reactor (e.g., packed bed reactor), a heat exchanger, a combustor, a separator (e.g., gas/solid or liquid/solid separator), a flame ionization detector.
In another refinement, the interior cavity is fully enclosed by the fully sintered metal oxide body (e.g., corresponding to an interior cavity as originally formed during partial sintering and without drilling or otherwise machining access channels from the body exterior to the interior cavity).
In another refinement, the interior cavity is partially enclosed by the fully sintered metal oxide body (e.g., corresponding to a fully enclosed interior cavity as originally formed during partial sintering but with further drilling or machining of access channels from the body exterior to the interior cavity; alternatively can correspond to a partially enclosed interior cavity as originally formed during partial sintering with a fugitive phase material that abuts an external edge or surface of the metal oxide body in its original powder form).
The disclosed methods can be extended to a repetitive process to build more complex structures. For example, the general method can further comprise comprising before partially sintering in part (d): placing a second fugitive phase material in the second metal oxide powder, the second fugitive phase material having a geometry corresponding to a negative cavity geometry in the formed microchemical apparatus; and placing a (free) third metal oxide powder over the second metal oxide powder and over the second fugitive phase material; wherein partially sintering in part (d) further comprises: partially sintering the first, second, and third metal oxide powders at a temperature and pressure sufficient (i) to convert the first and second fugitive phase materials to a gaseous material and (ii) to convert the first, second, and third metal oxide powders to a porous, partially sintered compact, thereby allowing the gaseous material to escape from the partially sintered compact interior volume and forming one or more interior cavities within the partially sintered compact interior volume having a geometry corresponding to the original first and second fugitive phase material geometries. Generally, the process can be extended to further repetitions of placing/layering fugitive phase materials and metal oxide powders before partial and full sintering to form a final product. The multiple fugitive phase materials can be separate from each other as originally placed in the powder such that corresponding multiple, separate interior cavities are formed. In other cases, the multiple fugitive phase materials can be contacting each other as originally placed in the powder such that a corresponding single interior cavity is formed.
While the disclosed methods, apparatus, compounds, and compositions are susceptible of embodiments in various forms, specific embodiments of the disclosure are illustrated (and will hereafter be described) with the understanding that the disclosure is intended to be illustrative, and is not intended to limit the claims to the specific embodiments described and illustrated herein.
Microfabrication for most microchemical (or microfluidic) systems (MCSs) has matured around material made of silicon or polymeric materials, which are not suitable for harsh environments such as high pressure, high temperature, and corrosive reactants. Disclosed herein is a powder-based fabrication framework that suitably withstands harsh operating environments and minimizes processing efforts while integrating various components through new processing techniques. Various MCS components can be made, for example micro-reactionware, microchannels, heat exchangers, pack-bed reactors (e.g., a micro-biomass reformer consisting of a pack-bed microreactor for filtration), combustion chambers, high-temperature gas clean-up separators, and high-temperature heat exchangers in addition to a micro flame ionization detector (μFID) serving as an on-chip diagnosis tool. Individual MCS components can be subsequently assembled in a modular fashion for system-level integration.
The disclosed methods provide several advantages, both in terms of processing and the final formed apparatus. A one-pot fabrication method can be used to make an apparatus with open and/or fully enclosed cavities (e.g., as internal channels for the MCS devices). Nearly full-density apparatus can be formed after fully sintering, and without the need for other phases such as binders or fillers. An intermediate, partially sintered structure is suitable for machining additional structure/cavities into the apparatus before final/full sintering. Control of the process permits formation of cavities with desirably small sizes and smooth interior finishes.
Ceramic-based MCSs are more suitable for operation under harsh environments such as high temperature and corrosive reactants compared to the more conventional MCS materials such as silicon and polymers. With the recent renewed interests in chemical manufacturing and process intensification, simple, inexpensive, and reliable ceramic manufacturing technologies are needed. The disclosed powder-based fabrication framework is a one-pot, cost-effective, and versatile process for ceramic MCS component fabrication. The process includes the compaction of metal-oxide nanopowders with a graphite or other fugitive phase that is burned out to create internal cavities and microchannels before full sintering. In illustrative embodiments, pure alumina powder has been used without any binder phase to form a micro-burner/combustion chamber, enabling more precise dimensional control and less structure deformation upon sintering. Process steps such as powder compaction, graphite burnout during partial sintering, machining in a conventional machine tool, and final densification have been examined to characterize the process and impact on the resulting MCS component. This near-full density ceramic structure with the combustion chamber and various internal channels was fabricated to be used as a micro-burner for a gas sensing application.
Miniaturization of chemical system has garnered significant attentions in chemistry and biology due to many advantages such as enhancement in heat/mass transfer rates at small scale, reduction in expensive reagents and hazardous wastes, and facilitation of massive parallelization in reaction/catalyst screening and optimization. The significant technological advancements for MCSs have been focused on chemical reactions, separation, and sensing in a low-to-medium temperature range (20° C. to 600° C.). One notable example is a lab-on-a-chip or micro total analytical system, in which the total sequence of laboratory processes is integrated to perform chemical synthesis, transport, and analysis, and it has profound influence in chemistry and biomedical areas. In some cases, the microreactors and heat exchangers in MCSs need to be operated at high temperatures (>600° C.) and/or under highly corrosive environments like solid-oxide fuel cells, fuel reformers, combustion burners, and gasifiers. However, high-temperature μCSs with sophisticated design and similar level of integration found in low-temperature counterpart have rarely been realized mainly because the conventional MCS materials such as silicon, glass, polymers, metals and conventional metal alloys are not stable at these high operating temperatures. Ceramic materials offer excellent high-temperature compatibility and corrosion resistances, but pose significant manufacturing challenges due to their hardness and brittleness.
Several groups have demonstrated the promise of ceramic-based microreactors for medium-to-high temperature reactions such as hydrogen production from continuous reforming of propane, oxidative coupling of methane, catalytic combustion, and nanoparticle synthesis. Despite these efforts and as discussed below, the current ceramic fabrication techniques still have some or all of the following challenges: (1) These structures are fabricated as open channel/reactors, requiring a joining process to create a fully enclosed system; (2) It is difficult to join or bond ceramic structures—high temperature adhesive typically used may create thermal mismatch, therefore with temperature cycling the joining areas are susceptible to failure; (3) It is difficult to establish a robust fluidic connection using conventional fitting to ceramic structures; and/or (4) It is difficult to monolithically integrate functionally diverse structures. For example, one of the paramount challenges in fabricating ceramic MCSs is that the microfabrication techniques borrowed from well-established microelectronics and microelectromechanical system (MEMS), which are very effective for silicon- or polymer-based MCSs, are not compatible with ceramic materials. Instead, the conventional and non-conventional ceramic processing techniques have been utilized to create ceramic microreactors and other components of MCSs. These techniques include rapid prototyping using low-pressure injection molding, micromachining, sol-gel/nanoparticle casting, and tape casting. In the rapid prototyping process, a negative silicone mold is first created from the original polymer mold fabricated by micro-steoreolithography, which is used directly for low-pressure injection molding. The resolution and surface quality of the ceramic components depend on the stereolithography quality of the original polymer mold, and the critical dimension of hundreds of microns (which is a relevant length scale in most MCSs) can be easily obtained. More recently, the smallest feature size on the order of a few microns in ceramic structures has been fabricated using the soft-lithographic molding technique like micromolding in capillaries combined with sol-gel casting. However, these molding/casting-based techniques can create only the open channel or chamber structures due to the demolding requirement. To utilize them in MCS applications, the fabricated structures need to be bonded with or packaged in another high-temperature material to form sealed microchannels or microreactors. Tape casting with low-temperature co-fired ceramic (LTCC) is perhaps the most widely used technique when it comes to the fabrication of the ceramic microreactors and microchannels. While low co-firing/sintering temperature (<900° C.) is beneficial for integrating metal electrodes and other applications, the operation temperature is typically limited due to the presence of the glass phase. Unlike the various molding techniques, tape casting is capable of producing suspended structures, enclosed cavity or microchannels for MCSs. However, the suspended structures tend to deform and sag due to high lamination pressures and the softening of the glass component in the ceramic composite during sintering. Multilayer lamination with fugitive materials such as waxes, polymeric materials, and carbon materials was used to support the embedded structures during lamination and sintering. Wax- and polymer-based fugitive materials, however, were completely burnt out even before the sintering of LTCC, and therefore sagging of the suspended region cannot be prevented during sintering. Moreover, in tape casting, each machined layer needs to be aligned to the previous layers before lamination, entailing some special equipment for alignment and lamination.
The disclosed methods and apparatus address the problems associated with ceramic MCSs and are directed to a simple, inexpensive, reliable, and reproducible ceramic manufacturing technology for high-temperature μCSs and microdevice application. The disclosed methods employ the cold compaction of metal-oxide powders with a graphite or other fugitive phase for the embedded features. In embodiments without a binder phase in the powder mix, the final chemistry and dimension of the sintered ceramic structures can be more precisely tuned. The advantages of the disclosed powder-based technique include one or more of (1) a one-pot, cost-effective process to create either open or fully-enclosed ceramic microreactors and microchannels, (2) near-full density ceramic structures without any other phases (e.g., organic or glass materials) in the final devices, (3) partially-sintered ceramic structures facilitating machining, and (4) abilities to control the surface finish of the internal cavity walls and easily incorporate additional features on the cavity surface. Process steps such as powder compaction, graphite burn-out during partial sintering, machining of partially sintered ceramics, and final densification can be selected/controlled to optimize the process and the properties of the resulting apparatus. As described in the examples below, a fully-enclosed ceramic structure with sub-millimeter internal cavities was formed according to the disclosure to provide an MCS component for micro-burner and micro flame ionization detector (μFID) applications.
The examples illustrate the disclosed apparatus, processes, and compositions, but are not intended to limit the scope of any claims thereto. In particular, the examples include illustrative embodiments of the disclosed methods for forming a ceramic microchemical apparatus in the specific context of a ceramic micro-burner.
This example illustrates the disclosed powder processing processes and related apparatus for a micro-burner whose critical dimension is below 1 mm. The micro-burner structural design in the examples was adopted from Kim et al. (2012) without major modifications. Unlike most ceramic processing techniques that start with ceramic powders or sols mixed with polymeric binder phases, however, the disclosed processes employ cold compaction of raw powders while utilizing a graphite fugitive phase to create internal cavities and channels. The processes allow the fabrication of open and fully-enclosed cavities/microchannels, and both configurations were formed in the examples. A micro-burner device with an open ceramic structure covered with a transparent quartz top was employed to visualize and optimize the flame in the micro-burner before the fabrication of the micro-burner with the fully-enclosed combustion chamber. A flat circular disc with a small thickness-to-diameter ratio (˜0.1) was selected for the micro-burner apparatus overall geometry, because the thin circular disc is one of the simplest shapes known to successfully compact the powder in a uniform density under a uniaxial load.
Fabrication Procedure: The overall fabrication protocols for the two open and closed configurations are depicted in
Alpha-phase alumina (AKP-50, Sumitomo in Japan) powder with the purity higher than 99.99% and the particle size between 0.1 and 0.3 micrometer was purchased for fabricating the proposed micro-burners. The common first step is to cut the 0.9 mm thick graphite sheet (EDM-3, Saturn Industries) in a CNC machine into the integrated shape of the combustion chamber and the internal channels. This graphite piece served as a fugitive phase 200 (e.g., first fugitive phase material 210 with a specific shape/geometry 212) that would later burn out during partial sintering and leave the interior cavities 310 for the combustion chamber and the internal channels. Once the graphite fugitive phase 200 was machined, half of the alumina powder to be used (about 2 grams) as the metal oxide powder 100 was poured into a die 20 to serve as the first metal oxide powder 110 (
Material Characterization: In order to determine an appropriate partial-sintering temperature and graphite burn-out behavior, a thermogravimetric analysis (TGA Q500, TA Instruments, USA) was conducted at a constant ramping rate (15° C.·min−1), which is the same as the temperature ramping rate used in the fabrication process for the examples. TGA measures a change in weight of the sample as a function of temperature, revealing the kinetics of graphite vaporization. During the TGA experiments, air was constantly flowing at 60 mL·min−1 to ensure complete oxidation of graphite. The densification process of alumina powder compact during sintering was investigated using a thermomechanical analyzer (TMA, Setaram 95, France). TMA results present the correlation between sintering temperature and sample densification kinetics in real time. A flat compacted sample was placed in between an alumina plate as a base and an alumina probe. The probe was then adjusted to zero. A change in dimension of the sample was measured by recording the movement of the alumina probe. Scanning electron microscopy (SEM) was used to evaluate the microstructures of the partially-sintered alumina samples that were sintered at different temperatures. The presence of the cavity and channels embedded in the fully-enclosed alumina sample was visualized by a computerized tomography (CT) scan (GE eXplore Locus RS micro CT) that has the highest resolution up to 27 μm.
Micro-burner Testing Setup: Both configurations of the micro-burners (as schematically shown in
Fabrication Results:
Processing Characterization: The fully-enclosed design of the alumina micro-burner was used for process characterization including powder compaction, optimization of the sintering temperature profile, and thermogravimetric analysis (TGA) experiments for graphite burn-out. Control of powder compaction during fabrication is important, because the presence of stiff graphite with a complex shape impedes the powder flow, frequently causing non-uniform stress distribution and resulting in cracks in the final component. One simple remedy is to remove sharp edges and geometric complexities in the machined graphite layer. The rounded edges and corners facilitate the powder to flow around them, preventing undesirable cracks due to the non-uniform density distribution. The edges of the graphite after cut in a CNC machine were smoothened by manual grinding. In addition, the sharp protrusion or the feature of graphite with a high aspect ratio makes the resulting powder structure susceptible to crack formation during fully sintering because of the non-uniform density distribution. For example, the region intersecting two gas channels to the combustion chamber was found to be prone to the crack formation (see circled region of
In a typical LTCC process, the burning of fugitive materials requires large openings because ceramic tapes consisting of the ceramic matrix infiltrated with polymeric or glassy phases are non-porous, leaving little room for gas diffusion. When the pure alumina powder is compacted without any binder phase, the powder compact is still substantially porous, allowing gases (e.g., O2 and CO/CO2) to diffuse in and out. Among many materials serving as fugitive phases, graphite was selected for two reasons. First, graphite has a very low coefficient of the thermal expansion (2˜6 μm·m−1·K−1), which minimizes the stress exerted onto the powder compact during partial sintering. This is important because the ceramic powders are in an extremely fragile state when the graphite is burnt out. Also the dimension of the integrated cavity can be predicted with better accuracy compared to other polymer-based fugitive phases. Secondly, the graphite burns out before the alumina powder starts to consolidate. Adequate interstitial spaces are provided for the byproducts of graphite oxidation, mainly CO and CO2, to escape. However, each graphite grade is slightly different in its oxidation temperature, and appropriate temperature ramp rate, soaking temperature, and soaking duration values can be determined/modified as desired.
Crack formation, crack propagation, and structural integrity of the sintered ceramic structure could affected by the sintering temperature profile for several reasons. On one hand, a higher ramp rate would induce a higher temperature gradient within the structure and in turn cause internal stresses to be developed, leading to crack propagation. On the other hand, an insufficient amount of time for graphite to completely burn out would generate a pressure build-up in the internal cavity as the consolidation of alumina powders progresses. The former factor is believed to be less important since no crack was observed in the open-channel configuration regardless of the ramp rate. In the open-channel sample, the graphite phase is fully exposed to outer environment, and therefore there is no restriction for CO/CO2 to be released. Conversely, a competition between graphite volatilization and powder consolidation exists in the fully-enclosed sample. If the alumina powders become consolidated before all graphite phases are burnt out, CO/CO2 has little interstitial space to escape and the pressure will build up until the structure bursts open. This net increase in pressure within the cavity can be attributed to the different gas permeabilities of O2 and CO2 in porous metal oxide structures (see Supplementary Information). To facilitate graphite volatilization, a soaking step holding at a constant temperature of 800° C. was added—the temperature high enough for graphite to burn out while low enough for alumina powders not to sinter (or consolidate) significantly. The modified sintering cycle resulted in crack-free ceramic structures with the internal cavities (
To understand the kinetics of the graphite burn-out with and without the presence of alumina powders, thermogravimetric analysis (TGA) was performed on a small piece of graphite and a graphite piece embedded in the alumina powder compact. First, a pure graphite sample was tested to determine the onset temperature of decomposition (or oxidation) for the graphite materials used in this study.
Next, the TGA experiment for the graphite piece embedded in the alumina powder compact was performed to model the graphite decomposition process in the fabrication of the micro-burner. A small (˜7 mm diameter) alumina compact encapsulating a graphite piece was fabricated in the same way that the micro-burner was made. The size of the graphite piece was scaled proportional to the alumina structure such that the mass and volume ratio of graphite to alumina remained the same as the original burner structure. The temperature profile used in the experiment was similar to the partial sintering step of the alumina micro-burner and consisted of (i) temperature rise from room temperature to 800° C. at the ramp rate of 15° C.·min−1, (ii) soaking at 800° C. for 2 hours, and (iii) ramping again to 900° C. at the ramp rate of 15° C.·min−1. The weight loss as a function of temperature is shown for the “graphite with alumina” sample in
The linear shrinkage of alumina in air was measured by thermomechanical analysis (TMA) and is shown as a function of time and temperature in
The TMA results were compared to the dimensional change of the micro-burner measured from the cross-sectional image (
Machining of Partially Sintered Ceramic (PSC): Fully sintered ceramics including alumina are known to have poor machinability due to their stiffness and brittleness. Machining green or white ceramic compacts would be easier if the final tolerance is not strict. Green machining is referred to as the machining of a ceramic in the unfired state, i.e., a powder compact before exposing to high temperature. In green machining, the powder is usually mixed with a binder phase (typically organic polymer or wax) to achieve the sufficient strength for machining. In these examples according to the disclosure, pure alumina powder was utilized without any binder phase. Therefore, the compacted powder was too difficult to handle and prone to fragment during machining, preventing performance of green machining. On the other hand, white machining is an approach to machining on partially sintered ceramics (PSC). The powder compacts can be partially sintered by firing at a temperature substantially below their typical sintering temperature. The formation of necks among the individual powder particles during partial sintering provides PSCs with the strength to withstand machining. These examples use a white machining technique to create fluidic connections to the enclosed channels in the micro-burner.
The extent of neck formation in PSCs, which determines the strength of the powder compact, highly depends on partial sintering temperature. For this reason, the partial sintering condition such as pre-sintering temperature and its duration has been shown to significantly affect the quality of the machined features. To understand the effect of partial sintering temperature on the machined features on PSCs, four alumina samples were prepared that were partially sintered at four different temperatures (600° C., 800° C., 1000° C., and 1200° C.). The conventional machining processes such as drilling and milling were performed on these PSC samples using a small bench-top CNC machine. The quality of the machined features was correlated to the amount of chips and cracks generated around holes during machining. The optimal machining parameters for the PSCs included a feed rate of 1 mm·min−1 and cutting speed of 1500 rpm for these examples.
Micro-burner Testing: The fully-sintered alumina sample was tested for micro-burner applications. Both open-channel and embedded-channel configurations were tested.
After identifying the H2 and air flow rates that anchored the flame inside the combustion chamber, the enclosed micro-burner was tested with the similar flow conditions. The flame generated within the enclosed micro-burner cannot be observed due to the opaque nature of the alumina walls. Therefore, the presence and approximate location of the flame was indirectly determined by recording the outer wall temperature of the micro-burner.
Finally, the alumina micro-burner was tested as a micro flame ionization detector (μFID). Two tungsten wires (0.5 mm diameter) were inserted into the exhaust to serve as electrodes. A flame was ignited and anchored into the micro-burner cavity with the flow rate conditions of H2 45 sccm and O2 22.5 sccm/air 20 scccm. This oxy-hydrogen flame ionizes hydrocarbon molecules, and the produced ions are driven by the applied electric field and collected by the electrodes. Without further optimization, train of 0.1 mL of natural gas was injected through the analyte port using a gas-tight syringe at times shown by the arrows in
Summary: These examples illustrate methods and apparatus according to the disclosure for processing ceramic metal oxide powders to fabricate ceramic structures with internal cavities and channels for microchemical system applications. High-purity, binder-free alumina micron-powder was compacted with a graphite fugitive phase embedded in the powder bed. The graphite was later burnt out during partial sintering, leaving the cavity and channels. The sintering schedule used in partial (and full) sintering critically influenced the structural integrity of the final alumina structure. Instead of the continuous temperature ramping to the full sintering temperature, the compacted alumina was partially sintered at 800° C. for two hours, which not only facilitated the removal of the graphite fugitive phase but also promoted the optimal neck formation for the subsequent machining processes. The TGA and TMA results showing graphite oxidation and alumina densification kinetics supported the competing nature of graphite burn-out and powder consolidation. The quality of the machined features on the partially sintered alumina was investigated using various imaging techniques, revealing that the partial sintering temperature is an important parameter for machining. Finally, the fabricated open-channel and fully-enclosed alumina micro-burners were tested in various flow rate conditions of hydrogen and oxygen/air, demonstrating that the fully-enclosed device functioned as designed without failing over long-term and cyclic operations.
Because other modifications and changes varied to fit particular operating requirements and environments will be apparent to those skilled in the art, the disclosure is not considered limited to the example chosen for purposes of illustration, and covers all changes and modifications which do not constitute departures from the true spirit and scope of this disclosure.
Accordingly, the foregoing description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications within the scope of the disclosure may be apparent to those having ordinary skill in the art.
All patents, patent applications, government publications, government regulations, and literature references cited in this specification are hereby incorporated herein by reference in their entirety. In case of conflict, the present description, including definitions, will control.
Throughout the specification, where the compounds, compositions, methods, apparatus, and processes are described as including components, steps, or materials, it is contemplated that the compositions, processes, or apparatus can also comprise, consist essentially of, or consist of, any combination of the recited components or materials, unless described otherwise. Component concentrations can be expressed in terms of weight concentrations, unless specifically indicated otherwise. Combinations of components are contemplated to include homogeneous and/or heterogeneous mixtures, as would be understood by a person of ordinary skill in the art in view of the foregoing disclosure.
Priority is claimed to U.S. Provisional Application No. 62/378,932 filed Aug. 24, 2016, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62378932 | Aug 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15685095 | Aug 2017 | US |
| Child | 17184509 | US |