Claims
- 1. An article capable of taking up and dispersing a liquid substance which comprises an elastomeric matrix having interconnecting cavities distributed therethrough and having from about 1 to about 100 parts per 100 parts by weight of elastomeric material of discrete fibers dispersed therethrough, said fibers having a diameter in the range of about 0.0005 to about 0.004 inch and a length in the range of about 0.005 to about 0.250 inch, wherein said fibers increase the liquid take-up and dispensing capability of said article.
- 2. The article of claim 1 wherein said elastomeric matrix is a rubber.
- 3. The article of claim 2 wherein said rubber is a butadiene-acrylonitrile copolymer containing about 28 percent acrylonitrile.
- 4. The article of claim 1 wherein the amount of said fibers is in the range of about 10 to about 40 parts.
- 5. The article of claim 1 wherein the amount of said fibers is about 20 parts.
- 6. A method of making a microporous elastomeric article having increased liquid take-up and dispensing capability comprising the steps of preparing an elastomeric matrix material by admixing an elastomeric material, from about 0.5 to 80 volume percent of sized particles of hydrated magnesium sulfate, from about 1 to about 100 parts by weight per 100 parts by weight of said elastomeric material of discrete fibers and vulcanizing ingredients, forming said matrix material into a desired shape, curing the resulting shaped matrix material while simultaneously causing liberation of waters of crystallization from said hydrated magnesium sulfate which provides a blowing effect providing the formation of interconnecting passages between said particles, leaching said particles from said matrix material and thereafter recovering the cured microporous article having said fibers dispersed therethrough, wherein said fibers increase the liquid take-up and dispensing capability of said cured articles.
- 7. The method of claim 6 wherein the amount of said fibers is in the range of about 10 to about 40 parts.
- 8. The method of claim 6 wherein the amount of said fibers is about 20 parts.
- 9. The method of claim 6 wherein said curing and leaching steps are achieved in a simultaneous manner.
- 10. The method of claim 6 wherein said preparing step comprises grinding and sizing hydrated magnesium sulfate containing 7 molecules of magnesium sulfate.
- 11. The method of claim 10 wherein said magnesium sulfate is ground and sized to provide particles wherein about 95% of said particles pass through a 100 mesh screen and about 81% of said particles pass through a 140 mesh screen.
- 12. The method of claim 6 wherein said leaching step further comprises the step of rinsing the cured and leached material.
- 13. The method of claim 9 wherein said curing and leaching steps are achieved using hot water at a temperature in excess of 150.degree. F.
- 14. The method of claim 12 wherein said recovering step comprises drying the cured, leached and rinsed material at a temperature in the range of about 300.degree. to 350.degree. F.
- 15. A composition vulcanizable to form a microporous vulcanizate comprising an elastomeric material having substantially uniformly dispersed throughout from 0.5 to about 80 volume percent of hydrated magnesium sulfate particles and from 1 to about 100 parts of discrete fibers per 100 parts by weight of said elastomeric material, said fibers having a diameter in the range of about 0.0005 to about 0.004 inch and a length in the range of about 0.005 to about 0.250 inch, together with vulcanizing ingredients including sulfur sufficient to convert the unvulcanized composition on curing to said vulcanizate, wherein said fibers increase the liquid take-up and dispersing capability of the resulting vulcanizate.
- 16. The composition of claim 1 wherein said elastomeric material is rubber.
- 17. The composition of claim 2 wherein said elastomeric material is a butadiene-acrylonitrile copolymer containing about 28 percent acrylonitrile.
- 18. The composition of claim 1 wherein said magnesium sulfate contains 7 molecules of water of crystallization per molecule of magnesium sulfate.
- 19. The composition of claim 1 wherein said hydrated magnesium sulfate has a particle size of about 100 mesh.
- 20. The composition of claim 1 wherein the amount of said hydrated magnesium sulfate is in the range of about 40 to 75 volume percent.
- 21. The composition of claim 1 wherein said fibers are nylon flock.
- 22. The composition of claim 1 wherein the amount of said fibers is about 20 parts.
- 23. The composition of claim 1 wherein the amount of said fibers is in the range of about 10 to about 40 parts.
Parent Case Info
This is a continuation-in-part of application Ser. No. 884,792, filed Mar. 9, 1978 now abandoned.