Claims
- 1. A molded product having a low coefficient of linear expansion, comprising:
- (I) 60-85% by weight of a polymer mixture comprising, per 100 parts by weight of said mixture:
- (A) 30-70 parts by weight of a polypropylene and, correspondingly,
- (B) 70-30 parts by weight of ethylene-.alpha.-olefin copolymer particles wherein the copolymer has substantially no crystalline regions formed therein and has a Mooney viscosity lower than 70;
- (II) 2-10% by weight of a fibrous filler; and
- (III) 5-38% by weight of an extender; wherein the ethylene-.alpha.-olefin copolymer is combined with the fibrous filler to form particles having an aspect ratio of at least 5 dispersed in the molded product as an elongated disperse phase.
- 2. A molded product as set forth in claim 1, wherein said polypropylene is a copolymer of propylene and ethylene.
- 3. A molded product as set forth in claim 2, wherein said polypropylene contains 1.0 to 15% by weight of ethylene.
- 4. A molded product as set forth in claim 1, wherein said copolymer is ethylene propylene rubber.
- 5. A molded product as set forth in claim 1, wherein said copolymer comprises:
- ethylene and
- at least one alpha-olefin selected from the group consisting of propylene, butene-1, hexene-1, decene-1, 4-methylbutene-1 and 4-methylpentene-1.
- 6. A molded product as set forth in claim 1, wherein said filler comprises at least one material selected from the group consisting of potassium titanate whiskers, zinc oxide whiskers, wollastonite, glass fibers, and carbon fibers.
- 7. A molded product as set forth in claim 1, wherein said filler has an average fiber length of 1 to 50 microns.
- 8. A molded product as set forth in claim 1, wherein said extender comprises at least one material selected from the group consisting of talc, mica and calcium carbonate.
- 9. A molded product as set forth in claim 1, wherein said copolymer comprises a copolymer of ethylene and propylene, said filler comprises potassium titanate whiskers, and said extender comprises talc.
- 10. A moldable composition comprising:
- (I) 60-85% by weight of a polymer mixture comprising, per 100 parts by weight of said mixture:
- (A) 30-70 parts by weight of a polypropylene and, correspondingly,
- (B) 70-30 parts by weight of an ethylene-.alpha.-olefin copolymer having substantially no crystalline regions formed therein and a Mooney viscosity lower than 70;
- (II) 2-10% by weight of a fibrous filler; and
- (III) 5-38% by weight of an extender; wherein the ethylene-.alpha.-olefin copolymer combines with the fibrous filler to form particles having an aspect ratio of at least 5 dispersed in a molded product prepared therefrom as an elongated disperse phase.
- 11. A moldable composition according to claim 10, wherein said polypropylene is a copolymer of propylene and ethylene.
- 12. A moldable composition according to claim 11, wherein said polypropylene contains 1.0 to 15% by weight of ethylene.
- 13. A moldable composition according to claim 10, wherein said copolymer is ethylene propylene rubber.
- 14. A moldable composition according to claim 10, wherein said copolymer comprises:
- ethylene and
- at least one alpha-olefin selected from the group consisting of propylene, butene-1, hexene-1, decene-1, 4-methylbutene-1 and 4-methylpentene-1.
- 15. A moldable composition according to claim 10, wherein said filler comprises at least one kind of material selected from the group consisting of potassium titanate whiskers, zinc oxide whiskers, wollastonite, glass fibers, and carbon fibers.
- 16. A moldable composition according to claim 10, wherein said filler has an average fiber length of 1 to 50 microns.
- 17. A moldable composition according to claim 10, wherein said extender comprises at least one material selected from the group consisting of talc, mica and calcium carbonate.
- 18. A moldable composition according to claim 10, wherein said copolymer comprises a copolymer of ethylene and propylene, said filler comprises potassium titanate whiskers, and said extender comprises talc.
- 19. A moldable composition according to claim 10, wherein said composition is molded into a shaped article.
- 20. A method of preparing a molded polypropylene product comprising the steps of:
- a. blending a polypropylene with an ethylene-.alpha.-olefin copolymer having substantially no crystalline regions formed therein and a Mooney viscosity lower than 70 to form a blended polymer mixture;
- b. forming the blended polymer mixture into pellets;
- c. mixing the thus-formed pellets with a fibrous filler and an extender under molten conditions to form a molten mixture;
- d. forming the thus-formed molten mixture into pellets in which the ethylene-.alpha.-olefin copolymer is combined with the fibrous filler to form particles having an aspect ratio of at least 5 dispersed in the polypropylene;
- e. air-drying the thus-formed pellets;
- f. subsequently heating the air-dried pellets to form a molten polypropylene material; and
- g. molding the molten polypropylene material into a desired shape.
Priority Claims (1)
Number |
Date |
Country |
Kind |
2-111316 |
Apr 1990 |
JPX |
|
Parent Case Info
This is a continuation of application Ser. No. 07/690,281, filed on Apr. 24, 1991, which was abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4521487 |
Mitsuno et al. |
Jun 1985 |
|
4891399 |
Ohkawa et al. |
Jan 1990 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
690281 |
Apr 1991 |
|