Patent Application
20130008622
1. Field of the Invention
The present invention relates to a paper machine clothing, and more particularly, to the composition of monofilaments used in the paper machine clothing.
2. Description of the Related Art
A paper machine clothing (PMC) fabric is typically manufactured with a specific set of design and quality specifications for a particular paper machine's performance requirements. These specifications include surface characteristics, open area, void volume, permeability and smoothness, among others. The need to implement an effective PMC fabric cleaning and inspection program is crucial to newer, faster machines, higher quality requirements and the desire for extended fabric life.
All fabrics, especially dryer fabrics, should be periodically cleaned and inspected so that their original properties are retained as long as possible and their value is optimized. The fabric of the paper machine clothing must be cleaned in order to maintain the required permeability and to prevent sheet streaking due to non-uniform dewatering and drying profiles, sheet drop-offs in vacuum assisted transfers, uniruns and single dryer runs. Fabric cleaning is accomplished both mechanically, for example by showering, and chemically. Some of the more common consequences resulting from fabric contamination are, for example, sheet moisture profile unevenness, sheet instability and the transfer of deposits from the fabric to the paper. In addition, dryer fabric contamination can lead to issues related to non-uniform heat transfer, reduced heat transfer resulting from deposits left on the drying cylinders, and plugged vacuum rolls.
What is needed in the art is a PMC fabric which allows for effective monitoring of the cleanliness and overall condition of a fabric.
The present invention provides a PMC fabric which may be effectively cleaned and efficiently inspected or examined for defects or contamination and, further to a method of making and inspecting the PMC fabric. More specifically, the present invention provides a PMC fabric including a plurality of monofilament yarns, at least some of which have a composition including an additive for detecting a defect on the PMC fabric using a light or radiation source. The additive may, for example, be an ultraviolet (UV) additive, an infrared (IR) additive or a metallic powder additive. The UV additive may be a stilbene, for example 4,4′-bis(benzoxazol)stilbene.
The present invention further provides a PMC fabric yarn for a PMC fabric. At least some of the monofilament yarns have a composition including between approximately 100 and 10,000 parts per million (ppm), for example 1,000 ppm, of an additive such as an ultraviolet (UV) additive for detecting a defect on the PMC fabric using short wavelength radiation at a wavelength of between approximately 300 nanometers (nm) to 400 nm.
The present invention further provides a PMC fabric yarn for a PMC fabric. The PMC yarn has a composition which includes between approximately 100 and 10,000 ppm of a UV additive for detecting a defect, contaminant or imperfection on the PMC fabric using short wavelength radiation at a wavelength of between approximately 300 nm to 400 nm.
The invention in another form is directed to a method of manufacturing a PMC fabric yarn including the steps of melt blending a mixture of an additive and a thermoplastic resin, spinning the mixture into a filament and drawing the filament into a monofilament PMC fabric yarn. The method further includes the step of then using a light source to increase visibility of the PMC fabric yarn and detect a defect in the PMC fabric yarn. The additive is, for example, a UV additive, an IR additive or a metal powder additive. The composition includes, for example, between 100 and 10,000 ppm of the additive.
The invention in another form is directed to a method of inspecting a PMC fabric including the steps of providing a PMC fabric including monofilament yarns, at least some of which include between approximately 100 and 10,000 ppm of a UV additive, and then using short wavelength radiation at a wavelength of between approximately 300 nm and 400 nm to detect a defect on the PMC fabric.
The present invention further provides a method of manufacturing a PMC fabric yarn including the steps of spinning a thermoplastic resin into a filament, drawing the filament into a monofilament PMC fabric yarn and coating the yarn with a coating having a composition which includes an additive for detecting a defect on the PMC fabric yarn and/or a PMC fabric formed by the PMC fabric yarn.
An advantage of the present invention is that defects such as contamination and/or imperfections or holes may quickly be detected and addressed in order to avoid sheet moisture profile unevenness, sheet instability, and the transfer of deposits from the PMC fabric to the paper.
Another advantage of the present invention is that the addition of the UV additive does not substantially alter the physical properties of the monofilament yarn.
The above-mentioned and other features and advantages of this invention, and the manner of attaining them, will become more apparent and the invention will be better understood by reference to the following description of embodiments of the invention taken in conjunction with the accompanying drawings, wherein:
Corresponding reference characters indicate corresponding parts throughout the several views. The exemplifications set out herein illustrate embodiments of the invention and such exemplifications are not to be construed as limiting the scope of the invention in any manner.
Referring now to the drawings, and more particularly to
The composition of the monofilament yarns includes an additive such as a UV additive, for example Eastobrite OB-1™ which is manufactured by Eastman Chemicals, and a thermoplastic resin. In order to monitor the cleanliness and the overall condition of the PMC fabric, a UV additive is added during the monofilament yarn making process. This additive makes the yarn easily visible in the presence, for example, of a black light (which generally emits radiation at wavelengths between approximately 350 nm and 390 nm) and enables quick detection of regions that do not contain UV additives, such as contamination or holes within the PMC fabric. A black light inspection process therefore makes the job easier for inspecting fabric for contaminants or damage during the cleaning process. The monofilament yarn with UV additive may also help the optical guiding mechanism for yarn and fabric.
Referring now to
A UV additive, also known as an optical brightener (OB) or fluorescent whitening agent absorbs the short wavelength electromagnetic radiation from a radiation source 13, such as a black light having a wavelength e.g., between approximately 300 nm and 400 nm, which is invisible to the human eye and converts it into visible light of a longer wavelength, for example between approximately 400 nm and 500 nm, which is emitted either as violet, blue or greenish blue light. This principle is generally illustrated in
Fluorescent whitening agents are compounds that are excited or activated by wavelengths in the near-UV range, for example having a wavelength between approximately 360 nm and 365 nm, and then emit light in the blue range, for example having a wavelength between approximately 400 nm and 440 nm. Electrons in fluorescent molecules are excited into a higher energy state by absorption of light, which then emit a small amount of heat plus fluorescence as the electrons return to their ground state.
A sample PET monofilament yarn without a UV additive was compared with a PET monofilament yarn including a UV additive. Table 1 shows some of the physical properties of the PET monofilament used for a PMC Dryer Fabric. The control sample (with no UV additive) is shown in the first column and the properties of the yarn with the UV additive, 1000 ppm loading, are shown in the second column. Table 1 shows that the physical properties of the yarn with the UV additive are substantially the same as the PET monofilament without the UV additive. Therefore, it is clear that the UV additive according to the present invention does not substantially alter the physical characteristics of the monofilament yarn.
During the manufacture of PMC fabric 10, a screw extruder is used to melt blend thermoplastic resin and an additive, for example a stilbene. (
During the inspection of a PMC fabric according to the present invention, a PMC fabric is provided which includes a plurality of monofilament yarns, at least some of which include between approximately 100 ppm and 10,000 ppm of a UV additive. (
Referring now to
While this invention has been described with respect to at least one embodiment, the present invention can be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practice in the art to which this invention pertains and which fall within the limits of the appended claims.