The invention relates to the general field of magneto-resistive memory arrays with particular emphasis on how information is stored and, more particularly, with overcoming high programming current and scaling problems.
Magnetic tunneling junction (MTJ) or Giant magneto-Resistance (GMR)/Spin Valve (SV) with two ferromagnetic layer separated by a non-magnetic layer—a tunneling oxide layer for MTJ or a transitional metal for GMR/SV—have been widely studied for use as a memory element in, for example, a Magnetic Random Access Memory (MRAM). Usually, one of these ferromagnetic layers (reference or pinned layer) is magnetized in a fixed direction while the other layer is free to switch its magnetization direction (free layer).
For MRAM applications, the magnetizations of both free and reference layers are in the film plane, as illustrated by
The digital information stored in the MTJ is thus encoded as the direction of magnetization of the free layer.
In a conventional MRAM application, two orthogonal external fields are used to program an MRAM cell such as 35. These are provided by current lines 31 and 32, as shown in
Another shortcoming of this approach is the scaling difficulty: as dimensions grow smaller, thermal agitation may perturb stored information. This thermal effect is described by
where f is the thermal switching frequency, f0 and B are constants, k is the Boltzman constant, T is the temperature. To have a thermally stable stored information in the MRAM cell, the Δ=BHsMstA has to be higher than a certain constant value. As dimension scales down, the area A is decreased, to maintain constant value of Δ, the
has to be increased, hence requiring higher switching current to write.
These two shortcomings can be avoided by thermally assisting the switching of the magnetization during the write operation, as described in Ref [1] as well as in U.S. Pat. Nos. 6,385,082, 6,704,220, and 6,771,534. The latter propose using joule heating to reduce the Ms value, and hence to lower Hs, while maintaining thermal stability when this heat is absent. However, in this scheme the choice of free layer material is limited by the requirement that a large enough magneto-resistance has to be achieved for there to be enough read signal for the detection of stored information. Thus the choice of free layer is usually limited to Co, Fe, Ni, and their mutual alloys. These all have high Curie temperatures so the current required to obtain a significant reduction of Ms is very high. They suggested use of rare earth ferromagnetic materials that have low Curie temperatures and lower magneto-resistance values than Co, Fe, Ni, and their mutual alloys. But these materials and are highly corrosive which makes for great process difficulties.
The other approach to overcoming half-select and scaling issues is an exchange biased design, described in Ref. [1], for current field writing, and in U.S. Pat. No. 7,110,287 for spin torque transfer writing, to couple the free layer to a low blocking temperature (Tb) AFM layer (separate from the AFM used to pin the reference layer which has a high blocking temperature).
A schematic drawing of this design is shown in
The anisotropic field to maintain stored data against thermal agitation is provided by the unidirectional field
where J is the exchange coupling energy per unit area which is determined by the AFM and free layer material properties.
The problem with this design is that, in order to have low Tb, the AFM's thickness has to be small; but He drops, and its variability increases, rapidly with AFM thickness so one ends up with a wide range of He values distributed among the various memory elements. The temperature generated by the heating current has to overcome the AFM with the highest Tb, which means that a high current will be needed.
A routine search of the prior art was performed with the following references of interest being found:
In U.S. 2008/0180991, Wang discloses a free layer containing nano-channels. In U.S. Pat. No. 7,375,405, Fukuzawa et al. show an AFM coupling layer of Rh, Ru, Cr, or Ir where magnetic pinning is performed at a temperature no higher than 300° C. Parkin, in U.S. Pat. No. 7,357,995, teaches a coupling layer comprising alloys of Cr with V, Nb, W, and Fe.
In U.S. Pat. No. 7,309,617, Reuhrig et al. disclose a reference layer oriented by cooling to below the Curie temperature. Their coupling layer comprised Ru, Au, or Co while Deak, in U.S. Pat. No. 7,230,844, teaches heating to near or above the Curie temperature for spin transfer.
It has been an object of at least one embodiment of the present invention to provide a method for eliminating the half-select problem in magnetic memory arrays.
Another object of at least one embodiment of the present invention has been for said method to increase the robustness of stored information in magnetic memory elements, despite size reductions of said memory elements.
Still another object of at least one embodiment of the present invention has been for said method to enable information to be stored in said memory elements in at least two different ways.
A further object of at least one embodiment of the present invention has been to provide a structure that is suitable for the implementation of said method.
These objects have been achieved by pinning the free layer magnetization via an AFM or antiferromagnetic layer (unrelated to the AFM that serves to pin the reference layer magnetization). As a key feature of the invention, a control valve layer (CV) is inserted between this AFM and the free layer (referred to as NF since it is a normal free layer). CV comprises ferromagnetic material that exchange couples this AFM to the free layer.
When CV is heated above its Curie temperature it becomes paramagnetic and no longer exchange-couples the AFM to the free layer so the magnetization of the latter is no longer pinned and can be switched, if so desired. Once switching is complete, CV is allowed to cool below its Curie temperature so that the AFM pins free layer NF once more. The necessary heating of CV is supplied by Joule heating that is generated by passing a current through the MTJ (or GMR) device. This Joule heating can be generated in the body of the device or in CV itself by giving CV the form of a matrix of ferromagnetic nano-channels embedded within an insulator.
Storing of information while free layer NF is in its unpinned state can be accomplished by generating magnetic fields in an additional wire having a bi-directional current capability which can provide a bi-directional setting field parallel or anti-parallel to the pinned layer, after passing a uni-directional heating current through the cell, or by a bi-directional current through the cell which provides heating and also sets the magnetization of the free layer through spin-torque transfer.
a, 1b, and 2 illustrate the basic operation of an MTJ device.
a illustrates how, in the present invention, a coupling layer has been inserted between a second AFM layer and the normal ferromagnetic free layer.
b illustrates using an anti-parallel coupling layer, between CV and the free layer, to further increase the robustness of the stored data
Referring now to
1) A normal ferromagnetic layer 51 (NF) immediately adjacent to tunneling layer 12 (for highest MR value),
2) a coupling valve layer 52 (CV), and
3) a 2nd antiferromagnetic (AFM) layer 53 having a high blocking temperature.
As a key feature of the invention, the coupling valve layer is engineered to behave in the following manner:
during storage (including read operations) it is ferromagnetic and is exchange coupled to both free layer NF and the 2nd AFM layer so that the unidirectional field He from second AFM 53 acts on free layer NF via CV to maintain the magnetizations of both the NF and CV layers along the desired direction.
During a write operation, the CV layer has been heated above its Curie point by a current through the MTJ, causing it to lose its ferromagnetic property, so it can no longer provide exchange coupling between AFM layer 53 and free layer NF 51 whereby free layer NF no longer experiences the exchange field He of the AFM layer. Since free layer NF has intrinsically low or zero magnetic anisotropy, its magnetization can be easily set in the desired direction. Two methods are available for setting the magnetization of free layer NF 53:
1) by an external magnetic field generated by current flowing through the word line or the bit line, similar to the approach portrayed in
2) by spin torque transfer from a spin polarized current flowing through MTJ itself.
For (1), the external field case, CV layer 52 becomes ferromagnetic again when the heating current is turned off and it is magnetized in the direction set by the external field and free layer NF's exchange coupling. Then, when the current that generates the external field is turned off, the magnetizations of NF and CV will be set to be parallel or anti-parallel to the pinned layer, depending the word line (or bit line) current direction.
For (2), the spin torque transfer writing case, the direction of current flowing through the MTJ sets the magnetization direction of the free layer NF. The CV layer is chosen to be a magnetic layer with low Curie temperature (Tc) so, when the MTJ temperature is above Tc, the CV layer transforms from a ferromagnetic to a paramagnetic phase whereby exchange coupling is reduced to zero, thereby decoupling the free layer NF from AFM layer 53 and allowing easy writing of the free layer's magnetic direction through the spin-torque-transfer effect.
The blocking temperature of 2nd AFM layer 53 needs to exceed the maximum temperature experienced by the MTJ so that its magnetic properties can remain unchanged during and after the write operation.
For the current generated (i.e. external) field writing case, the writing procedure can be further detailed as follows:
1) turn on the word (or bit) line current appropriate for the desired field direction,
2) send a pulse current through the MTJ via a diode (or transistor) so as to raise the MTJ free layer temperature above the CV layer's Tc,
3) allow the free layer to cool down with the word or bit line current field still present in order to set the NF and CV layers' magnetizations in their desired directions.
For the spin torque transfer writing case, the writing procedure can be further detailed as follows:
Since the coupling valve layer acts like a switching valve that turns exchange coupling between AFM and free layer NF on and off, so MRAMs having this type of free layer structure can be referred to as “coupling valve RAMs”.
To further increase thermal stability, a synthetic antiferromagnetic structure (SAF) can be employed, as shown by
Implementation Details:
For the spin torque transfer version discussed above, the invention requires that the MTJ be accessed through a transistor able to provide, in addition to its normal service, a bidirectional current in the form of a short pulse at a high current level followed by a long pulse at a lower current level. Said bidirectional current is required to cause electrons to flow from the reference layer into the free layer when writing the free layer magnetization parallel to the reference layer's magnetization, and vice versa.
Note, too, that the invention can be implemented so that magnetization in both the free layer NF and the reference layers lies in the plane of the deposited film or the magnetization may be perpendicular to the film plane. In a perpendicular design, both magnetizations of the free layer and reference (pinned) layer are perpendicular to the film plane. The free layer magnetization can be set to be along or against the reference layer magnetization.
The perpendicular configuration is achievable in magnetic films such as FePt, CoPt, CoFeTb, CoFeGd, etc or in multilayer structures such as Fe/Pt, Co/Pt, Co/Ni, Fe/Pd, and Co/Pd, which have high perpendicular anisotropy; this overcomes the de-magnetization field enabling the magnetization to be stable perpendicular to the film plane. The advantages of the perpendicular configuration are that a very low current is needed and the MTJ cell can be given a circular shape which is smaller than the more conventional elliptical shape.
To construct the invention, a first preferred embodiment is to have the coupling valve layer made of magnetic material with low curie temperature, ranging from 85-˜300° C. The free layer NF can be made of Co, Fe, Ni or their alloys, all of which have high curie temperatures (Tc of pure Ni ˜358° C., pure bcc Co ˜1130° C., pure Fe ˜770° C.). The coupling valve layer can be any conducting, semiconducting or weakly insulating magnetic material with a curie temperature between 85 and ˜300° C. Some examples are given below:
Ni, Fe, Co or alloys of form XY (where X=Ni, Fe, or Co, Y=Mo, Pt, V, Cr, Si, Al, Zn, Mn, Cu, Pd, C, Ce, B, S, or P, etc.) as shown in
A NiFe alloy with a Ni concentration around 30-35% can have a curie temperature around 120 to 250° C., as shown in
A second preferred embodiment is illustrated in
Note that the use of a nano-channel in this environment is quite different from its role in a CPP GMR spacer layer. In the latter, the nano-channel serves to make the resistance component of the resistance area product as high as possible whereas in the device that forms the present invention the resistance of the NCC should be as low as possible while still concentrating the current to a sufficient degree to raise the local temperature above the Tc of the MAGNETIC material used to form the channels. This is unlike a GMR micro-channel, which need not be, and preferably shouldn't be, magnetic.
Number | Name | Date | Kind |
---|---|---|---|
6385082 | Abraham et al. | May 2002 | B1 |
6535416 | Daughton et al. | Mar 2003 | B1 |
6704220 | Leuschner | Mar 2004 | B2 |
6744086 | Daughton et al. | Jun 2004 | B2 |
6771534 | Stipe | Aug 2004 | B2 |
6963098 | Daughton et al. | Nov 2005 | B2 |
7023723 | Daughton et al. | Apr 2006 | B2 |
7110287 | Huai et al. | Sep 2006 | B2 |
7148531 | Daughton et al. | Dec 2006 | B2 |
7177178 | Daughton et al. | Feb 2007 | B2 |
7230844 | Deak | Jun 2007 | B2 |
7266013 | Daughton et al. | Sep 2007 | B2 |
7309617 | Ruehrig et al. | Dec 2007 | B2 |
7357995 | Parkin | Apr 2008 | B2 |
7375405 | Fukuzawa et al. | May 2008 | B2 |
7813165 | Daughton et al. | Oct 2010 | B2 |
7868404 | Deak | Jan 2011 | B2 |
7929370 | Min | Apr 2011 | B2 |
20070063237 | Huai et al. | Mar 2007 | A1 |
20080180991 | Wang | Jul 2008 | A1 |
20100002501 | Leuschner et al. | Jan 2010 | A1 |
Number | Date | Country | |
---|---|---|---|
20100232215 A1 | Sep 2010 | US |