Patent Application
20230393063
The present disclosure relates to a meta-material and a preparation method and a detection method thereof. In particular, the present disclosure relates to a preparation method of a multi-scale meta-material and a method for comprehensively detecting a sample in different wavebands by using the multi-scale meta-material.
Spectroscopy technology has always been the focus of research due to its fast detection speed and non-destructiveness. As an important means to identify the structure of substances, spectroscopy technology has a wide range of applications in life science, food science, material science, archaeology, agriculture, etc. The ultraviolet-visible (UV-Vis) absorption spectrum is produced due to the transition of valence electrons. The composition, content, and structure of the substance can be analyzed, measured, and inferred through the UV-Vis spectrum and the degree of absorption of UV-Vis light by molecules or ions of the substance. The infrared (IR) spectrum is produced by the transition of vibrational and rotational energy levels in molecules due to the selective absorption of IR rays of certain wavelengths by the molecules. The IR absorption spectrum of the substance is also known as a vibrational spectrum or vibrational rotational spectrum, which can be acquired by detecting the absorption of IR rays. Additional information about the sample can be acquired by detecting the sample through multiple spectral detection techniques. However, most of the currently used meta-materials in sample detection only apply to a single waveband and cannot achieve responses in multiple wavebands. In addition, in practical detection applications, the surface of the detected sample is usually curved, so it is necessary to realize the close contact between the detected sample surface and the sensor surface.
A technical problem to be solved by the present disclosure is to provide a multi-scale meta-material and a multi-waveband photoelectric device to overcome the above-mentioned deficiencies of the related art. The photoelectric device applies to different wavebands, for example, a first waveband (such as UV waveband and Vis waveband) and a second waveband (such as IR waveband, terahertz waveband, and microwave waveband). The photoelectric device can perform biochemical molecular sensing in the Vis waveband and the terahertz waveband and is flexible, stretchable, sensitive, fast, and convenient as a detection device.
The multi-scale meta-material of the present disclosure has a tunable function in multiple wavebands, can sense biochemical molecules by utilizing the advantages of multiple wavebands, is simple and fast to operate, and is suitable for various detection needs.
The present disclosure adopts the following technical solutions1. A multi-waveband-tunable multi-scale meta-material includes:
In the present disclosure, nanoparticles are self-assembled on the metal layer to form the nanoparticle layer. The structure can simultaneously absorb and reflect in the first waveband (such as UV waveband and Vis waveband) and the second waveband (such as IR waveband, terahertz waveband, and microwave waveband) to amplify a Raman signal in the first waveband and a terahertz signal in the second waveband.
The stretchable layer is provided thereon with multiple basic units that are arranged in an array at intervals. The basic units each include the non-stretchable support layer, the metal layer, and the nanoparticle layer which are sequentially stacked from bottom to top.
The PI that forms the non-stretchable support layer is a flexible low-stretch film. The present disclosure uses the PI as the non-stretchable support layer to protect the integrity of the metal layer and the nanoparticle layer. When the PDMS layer is stretched, a part not covered with the PI will be deformed, and a part covered with the PI will not be easily deformed.
2. A preparation method for the multi-waveband-tunable multi-scale meta-material includes the following steps:
The nanoparticle layer is formed by self-assembling 10 nm-80 nm silver-coated gold nanoparticles on the water surface. Therefore, the nanoparticle layer is formed by self-assembling gold or silver nanoparticles.
The metal layer is formed by sputtering or evaporating a material, which includes, but is not limited to, gold, silver, copper, iron, and nickel.
The etching technique includes, but is not limited to, photolithography, X-ray etching, electron beam etching, ion beam etching, wet etching, and laser engraving.
The PDMS of the stretchable layer has a thickness of 10 μm-200 μm, and the PI of the non-stretchable support layer has a thickness of 1 μm-10 μm.
A localized surface plasmon resonance spectrum of the first waveband is tuned by changing the material, morphology, and size of the nanoparticles, and a resonance peak of the second waveband is tuned by adjusting the preset pattern.
The preset pattern is formed by multiple basic units that are arranged in an array at intervals, and the basic units each include the non-stretchable support layer, the metal layer, and the nanoparticle layer that are sequentially stacked from bottom to top.
The multi-waveband-tunable multi-scale meta-material is used for, but is not limited to, dual-waveband spectral response and can also be used for spectral responses of more than two wavebands. More scales can be achieved by designing the shape of the gold layer to form different patterns. Spectral responses of other wavebands can be achieved by changing the pattern of the gold layer.
The multi-waveband-tunable multi-scale meta-material includes at least two scales: nanoscale, (i.e., the scale of nanoparticles) and microscale (i.e., the scale of the basic units).
The multi-waveband-tunable multi-scale meta-material is not limited to these two scales and also includes millimeter and meter scales, etc.
3. A spectral detection method using the multi-waveband-tunable multi-scale meta-material includes the following steps:
In S1, 10 μL of the sample solution is dripped each time, and the drying is performed at 40° C.-60° C.
In S2, a time-domain signal is at a range of 25 ps, and the frequency-domain signal is at a position of 0.1 THz-1.3 THz.
The sample solution includes, but is not limited to, Pseudomonas aeruginosa and pyocyanine. The Pseudomonas aeruginosa is detected by the Raman spectra, and the pyocyanine is detected by the terahertz spectra.
Preferably, in a specific implementation, the PDMS solution of the present disclosure is, but is not limited to, a DCI84 PDMS solution produced by Dow Corning.
Preferably, in a specific implementation, the fluorosilane may be, but is not limited to, 448931-10G trichloro(1H,1H,2H,2H-perfluorooctyl)silane produced by Sigma.
The PI film of the present disclosure may be replaced with a photoresist, such as SU-8.
Preferably, in a specific implementation, the terahertz time-domain spectroscopy system of the present disclosure is one of model z3 produced by z-omega.
Preferably, in a specific implementation, the Raman spectrometer of the present disclosure is one of the models of the LABRAM HR Evolution produced by the Jobin Yvon HORIBA group.
The multi-waveband-tunable multi-scale meta-material of the present disclosure includes the nanoparticle layer, the metal layer, the non-stretchable support layer, and the stretchable layer. The nanoparticle layer has strong spectral absorption capability in the first waveband (such as UV waveband and Vis waveband), thereby acquiring a localized surface plasmon resonance spectrum and forming an electric field that can amplify the Raman signal on its surface. The metal layer can excite the corresponding resonance peak in the second waveband (such as the IR waveband, the terahertz waveband, and the microwave waveband) through the surface plasmon resonance effect to enhance the interaction between the terahertz wave and the substance, thereby improving the terahertz detection sensitivity. An ordinary meta-material can only act on the spectrum of a certain waveband, so the detection result is single. The outstanding advantage of the present disclosure is that the multi-waveband-tunable multi-scale meta-material can be used for spectral detection of different wavebands and can also be closely attached to the curved surfaces to adapt to different detection objects.
In the present disclosure, in steps S2 and S3, the meta-material is simultaneously applied to the detection of biochemical molecules by terahertz spectroscopy and Raman spectroscopy, but it is not limited to terahertz spectroscopy and Raman spectroscopy.
Thus, the multi-waveband-tunable multi-scale meta-material of the present disclosure has the following beneficial effects.
The multi-waveband-tunable multi-scale meta-material of the present disclosure utilizes the nanoparticle layer to absorb the spectra in the UV and Vis wavebands to generate localized surface plasmon resonance, thereby amplifying the Raman signal of the sample.
The multi-waveband-tunable multi-scale meta-material of the present disclosure utilizes the local electric field induced by the metal layer to amplify the terahertz signal of the sample.
The multi-waveband-tunable multi-scale meta-material of the present disclosure is flexible and has a flat surface, so it can be used for sample detection on curved surfaces.
Compared with traditional spectroscopic techniques, the detection method of the present disclosure utilizes the meta-material to amplify the spectral signal, thus greatly improving the detection sensitivity. Compared with traditional signal amplification methods, the detection method of the present disclosure utilizes the multi-scale meta-material to amplify the spectral signals of different wavebands, thereby expanding the application range of the meta-material. The multi-waveband-tunable multi-scale meta-material is flexible and stretchable and can be tightly attached to curved surfaces. In addition, the detection method of the present disclosure is simple and fast to operate and meets the increasing demand for rapid detection.
Reference Numerals: (1) stretchable layer; (2) non-stretchable support layer; (3) metal layer; and (4) nanoparticle layer.
The present disclosure is described in further detail below by referring to embodiments, but the present disclosure is not limited to these embodiments.
(1) Preparation of a Flexible Base
A flat quartz wafer or silicon wafer is ultrasonically cleaned in acetone, ethanol, and water for 5 min respectively, and dried. PDMS is spin-coated and heat-cured on the surface of the quartz or silicon wafer to form a stretchable layer. PI is spin-coated and heat-cured on the surface of the heat-cured PDMS to form a non-stretchable support layer for supporting and protecting a metal layer. 200 nm gold is deposited on the surface of the PI by evaporation of gold in a vacuum to form the metal layer.
(2) Preparation of a Nanoparticle Layer
A 50 nm silver nanocube is synthesized and is filtered three times using a water filter element with a diameter of 0.22 μm. A 0.1 mg/mL solution of polyethylene glycol compound with sulfhydryl groups (PEG-SH) in chloroform is prepared. A silver nanocube solution, the PEG-SH chloroform solution, and a methanol solution are thoroughly mixed at a volume ratio of 1:1:1. The resulting mixture is centrifuged at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-tenth of its original size with the chloroform solution. The resulting mixture is slowly injected onto the surface of an aqueous solution by a syringe at a rate of 0.4 m/min. Tension at the water surface is monitored by a Langmuir-Blodgett (LB) film analyzer, and a uniform and dense monolayer of the silver nanocube is completely transferred to the surface of the metal layer. The silver nanocube layer serves as the nanoparticle layer to amplify a Raman signal.
(3) Preparation of a Multi-Scale Meta-Material
The non-stretchable support layer, the metal layer, and the nanoparticle layer are etched into the desired pattern.
(4) Acquisition of a Pseudomonas aeruginosa Solution and its Secretion Pyocyanine
1 mL of Pseudomonas aeruginosa cultured for 12 h is taken. In this embodiment, OD600=1.
(5) Dripping of the Pseudomonas aeruginosa Solution onto the Surface of the Meta-Material 10 μL of Pseudomonas aeruginosa solution (with pyocyanine) is dripped onto the surface of the multi-scale meta-material and dried at 60° C. The above steps are repeated three times to obtain three sample points to be detected. The detection area of each sample point to be detected is about 20 mm2. Three reference sample points (multi-scale meta-material only, not dripped) are also provided.
(6) Acquisition of Terahertz Time-Domain Spectra of the Sample Points to be Detected and the Reference Sample Points on the Surface of the Multi-Scale Meta-Material
A terahertz time-domain spectrometer and a computer are started. The multi-scale meta-material is put on a sample holder for detection, and a terahertz time-domain system is filled with nitrogen to reduce the internal humidity to less than 0.2% for detection. The terahertz time-domain spectra of the sample points to be detected and the reference sample points on the same multi-scale meta-material in a range of 0.1 THz-2 THz are acquired at the humidity of less than 0.2%. The terahertz time-domain spectrum of each sample point is acquired according to the above method, and a terahertz time-domain spectrum data set of all the sample points is acquired. A terahertz time-domain signal of the sample point is converted into a terahertz frequency-domain signal through a fast Fourier transform, and a reflectivity and transmittance of the sample point to be detected are acquired through the terahertz frequency-domain signal. A frequency corresponding to a maximum value of a resonance peak is calculated based on the reflectivity and transmittance, and a frequency of a resonance peak of the sample point to be detected is subtracted from a frequency of a resonance peak of the reference sample point to obtain a change in the frequency of the resonance peak.
(7) Acquisition of Raman Spectral Signals of the Pyocyanine on the Surface of the Multi-Waveband-Tunable Multi-Scale Meta-Material
The pyocyanine is dripped onto the multi-waveband-tunable multi-scale meta-material. Laser intensity is adjusted, the sample is adjusted to a horizontal state, and the Raman spectra of the sample points to be detected on the multi-waveband-tunable multi-scale meta-material are acquired. The Raman spectra of the multi-waveband-tunable multi-scale meta-material in the presence and absence of the pyocyanine are shown in
(1) Preparation of a Flexible Base
A flat PI film is ultrasonically cleaned in ethanol and water for 5 min respectively, and dried. The PI is attached to PDMS, such that PDMS forms a stretchable layer, and PI forms a non-stretchable support layer for supporting and protecting a metal layer. 200 nm gold is deposited on the surface of the PI film by evaporation of gold in a vacuum to form the metal layer.
(2) Preparation of a Nanoparticle Layer
A 50 nm silver nanocube is synthesized and is filtered three times using a water filter element with a diameter of 0.22 μm. A 0.1 mg/mL solution of polyethylene glycol compound with sulfhydryl groups (PEG-SH) in chloroform is prepared. A silver nanocube solution, the PEG-SH chloroform solution, and a methanol solution are thoroughly mixed at a volume ratio of 1:1:1. The resulting mixture is centrifuged at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-tenth of its original size with the chloroform solution. The resulting mixture is slowly injected onto a surface of an aqueous solution by a syringe at a rate of 0.4 mL/min. Tension at the water surface is monitored by a Langmuir-Blodgett (LB) film analyzer, and a uniform and dense monolayer of the silver nanocube is completely transferred to the surface of the metal layer. The silver nanocube layer serves as the nanoparticle layer to amplify a Raman signal.
(3) Preparation of a Multi-Scale Meta-Material
The non-stretchable support layer, the metal layer, and the nanoparticle layer are etched into the desired pattern.
(4) Acquisition of a Pseudomonas aeruginosa Solution and its Secretion Pyocyanine
1 mL of Pseudomonas aeruginosa cultured for 12 h is taken. In this embodiment, OD600=1.
(5) Dripping of the Pseudomonas Aeruginosa Solution onto the Surface of the Meta-Material
10 mL of Pseudomonas aeruginosa solution (with pyocyanine) is dripped onto the surface of the multi-scale meta-material and dried at 60° C. The above steps are repeated three times to obtain three sample points to be detected. The detection area of each sample point to be detected is about 25 mm2. Three reference sample points (multi-scale meta-material only, not dripped) are also provided.
(6) Acquisition of Terahertz Time-Domain Spectra of the Sample Points to be Detected and the Reference Sample Points on the Surface of the Multi-Waveband-Tunable Multi-Scale Meta-Material
A terahertz time-domain spectrometer and a computer are started. The multi-waveband-tunable multi-scale meta-material is put on a sample holder for detection, and a terahertz time-domain system is filled with nitrogen to reduce the internal humidity to less than 0.2% for detection. The terahertz time-domain spectra of the sample points to be detected and the reference sample points on the same multi-scale meta-material in a range of 0.1 THz-2 THz are acquired at the humidity of less than 0.2%. The terahertz time-domain spectrum of each sample point is acquired according to the above method, and a terahertz time-domain spectrum data set of all the sample points is acquired. A terahertz time-domain signal of the sample point is converted into a terahertz frequency-domain signal through a fast Fourier transform, and a reflectivity and transmittance of the sample point to be detected are acquired through the terahertz frequency-domain signal. A frequency corresponding to a maximum value of a resonance peak is calculated based on the reflectivity and transmittance, and a frequency of a resonance peak of the sample point to be detected is subtracted from a frequency of a resonance peak of the reference sample point to obtain a change in the frequency of the resonance peak.
(1) Preparation of a Stretchable Layer
A flat quartz wafer or silicon wafer is ultrasonically cleaned in acetone, ethanol, and water for 5 min and dried. PDMS is spin-coated on the surface of the quartz or silicon wafer and cured at 80° C. for 30 min to form the stretchable layer.
(2) Preparation of a Non-Stretchable Support Layer
PI is spin-coated on the surface of the stretchable layer and cured at 200° C. for 1 h to form the non-stretchable support layer for supporting and protecting a metal layer.
(3) Preparation of the Metal Layer
200 nm gold is deposited on the surface of the non-stretchable support layer (PI) by evaporation of gold in a vacuum to form the metal layer. A piece of sample is directly used to make a meta-material without a nanoparticle layer (step 5), and another piece of sample is used to make a meta-material with the nanoparticle layer (step 4).
(4) Preparation of a Nanoparticle Layer
A 50 nm silver nanocube is synthesized and filtered three times using a water filter element with a diameter of 0.22 μm. A 0.1 mg/mL solution of polyethylene glycol compound with sulfhydryl groups (PEG-SH) in chloroform is prepared. A silver nanocube solution, the PEG-SH chloroform solution, and a methanol solution are thoroughly mixed at a volume ratio of 1:1:1. A resulting mixture is centrifuged at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-tenth of its original size with the chloroform solution. The resulting mixture is slowly injected onto a surface of an aqueous solution by a syringe at a rate of 0.4 mL/min. Tension at the water surface is monitored by a Langmuir-Blodgett (LB) film analyzer, and a uniform and dense monolayer of the silver nanocube is completely transferred to the surface of the metal layer. The silver nanocube layer serves as the nanoparticle layer to amplify a Raman signal.
(5) Preparation of a Multi-Scale Meta-Material
The non-stretchable support layer, the metal layer, and the nanoparticle layer are etched into the desired pattern.
(6) Acquisition of Terahertz Time-Domain Spectra of the Multi-Waveband-Tunable Multi-Scale Meta-Material
A terahertz time-domain spectrometer and a computer are started. The multi-waveband-tunable multi-scale meta-material is put on a sample holder for detection, and a terahertz time-domain system is filled with nitrogen to reduce the internal humidity to less than 0.2% for detection. The terahertz time-domain spectra of the sample points to be detected and the reference sample points on the multi-scale meta-material in a range of 0.1 THz-2 THz are acquired at the humidity of less than 0.2%. The terahertz time-domain spectrum of each sample point is acquired according to the above method, and a terahertz time-domain spectrum data set of all the sample points is acquired. A terahertz time-domain signal of the sample point is converted into a terahertz frequency-domain signal through a fast Fourier transform, and a reflectivity and transmittance of the sample point to be detected are acquired through the terahertz frequency-domain signal. The position of a resonance peak is calculated based on reflectivity and transmittance.
(7) Tuning of the Terahertz Spectrum by Stretching the Multi-Scale Meta-Material
The multi-scale meta-material is fixed on a uniaxial stretching stage and is stretched along a U-shaped opening with an elongation of 0-110%. 10% of the original length is stretched each time, and terahertz time-domain signals are acquired at three points after each stretch.
(1) Preparation of a Stretchable Layer
A flat quartz wafer or silicon wafer is ultrasonically cleaned in acetone, ethanol, and water for 5 min and dried. PDMS is spin-coated on the surface of the quartz or silicon wafer and cured at 80° C. for 30 min to form the stretchable layer.
(2) Preparation of a Non-Stretchable Support Layer
PI is spin-coated on the surface of the stretchable layer and cured at 200° C. for 1 h to form the non-stretchable support layer for supporting and protecting a metal layer.
(3) Preparation of the Metal Layer
200 nm gold is deposited on the surface of the non-stretchable support layer (PI) by evaporation of gold in a vacuum to form the metal layer. A piece of sample is directly used to make a meta-material without a nanoparticle layer (step 5), and another piece of sample is used to make a meta-material with the nanoparticle layer (step 4).
(4) Preparation of a Nanoparticle Layer
A 50 nm silver nanocube is synthesized and filtered three times by a water filter element with a diameter of 0.22 μm. A 0.1 mg/mL solution of polyethylene glycol compound with sulfhydryl groups (PEG-SH) in chloroform is prepared. A silver nanocube solution, the PEG-SH chloroform solution, and a methanol solution are thoroughly mixed at a volume ratio of 1:1:1. The resulting mixture is centrifuged at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-tenth of its original size with the chloroform solution. The resulting mixture is slowly injected onto a surface of an aqueous solution by a syringe at a rate of 0.4 mL/min. Tension at the water surface is monitored by a Langmuir-Blodgett (LB) film analyzer, and a uniform and dense monolayer of the silver nanocube is completely transferred to the metal layer/non-stretchable support layer. The silver nanocube layer serves as the nanoparticle layer to amplify a Raman signal.
(5) Preparation of the Meta-Material with or without the Metal Layer
The non-stretchable support layer, the metal layer, and the nanoparticle layer are etched into the desired pattern to form the meta-material with the nanoparticle layer. The non-stretchable support layer and the metal layer are etched into the desired pattern to form the meta-material without the nanoparticle layer.
(6) Acquisition of a Pseudomonas aeruginosa Solution and its Secretion Pyocyanine
1 mL of Pseudomonas aeruginosa cultured for 12 h is taken. In this embodiment, OD600=1.
(7) Dripping of the Pseudomonas aeruginosa Solution onto the Surface of the Meta-Material
10 μL of Pseudomonas aeruginosa solution (with pyocyanine) is dripped onto the surface of the meta-material with or without the nanoparticle layer and dried at 60° C. The above steps are repeated three times to obtain three sample points to be detected. The detection area of each sample point to be detected is about 20 mm2.
(8) Acquisition of Raman Spectral Signals of the Pyocyanine on the Surface of the Meta-Material
The Pseudomonas aeruginosa solution (with pyocyanine) is dripped onto the meta-material, and the meta-material is put on a sample stage of a Raman spectrometer. Laser intensity is adjusted, and the sample is adjusted to a horizontal state. The Raman spectra of the sample points to be detected on the meta-material without or without the nanoparticle layer are acquired respectively.
(1) Preparation of a Stretchable Layer
A flat quartz wafer or silicon wafer is ultrasonically cleaned in acetone, ethanol, and water for 5 min and dried. PDMS is spin-coated on the surface of the quartz or silicon wafer and cured at 80° C. for 30 min to form the stretchable layer.
(2) Preparation of a Non-Stretchable Support Layer
PI is spin-coated on the surface of the stretchable layer and cured at 200° C. for 1 h to form the non-stretchable support layer for supporting and protecting a metal layer. A piece of sample is directly used to make a meta-material without a metal layer (step 4), and another piece of sample is used to make a meta-material with the metal layer (step 3).
(3) Preparation of the Metal Layer
200 nm gold is deposited on the surface of the non-stretchable support layer (PI) by evaporation of gold in a vacuum to form the metal layer.
(4) Preparation of a Nanoparticle Layer
A 50 nm silver nanocube is synthesized and filtered three times by a water filter element with a diameter of 0.22 μm. A 0.1 mg/mL solution of polyethylene glycol compound with sulfhydryl groups (PEG-SH) in chloroform is prepared. A silver nanocube solution, the PEG-SH chloroform solution, and a methanol solution are thoroughly mixed at a volume ratio of 1:1:1. The resulting mixture is centrifuged at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-third of its original size with the chloroform solution. Centrifuging is performed at 8,000 rpm for 15 min. A supernatant is discarded, and a precipitate is re-dissolved to one-tenth of its original size with the chloroform solution. The resulting mixture is slowly injected onto a surface of an aqueous solution by a syringe at a rate of 0.4 mL/min. Tension at the water surface is monitored by a Langmuir-Blodgett (LB) film analyzer, and a uniform and dense monolayer of the silver nanocube is completely transferred to the metal layer/non-stretchable support layer. The silver nanocube layer serves as the nanoparticle layer to amplify a Raman signal.
(5) Preparation of the Meta-Material with or without the Metal Layer
The non-stretchable support layer, the metal layer, and the nanoparticle layer are etched into the desired pattern to form the meta-material with the metal layer. The non-stretchable support layer and the nanoparticle layer are etched into the desired pattern to form the meta-material without the metal layer.
(6) Acquisition of Terahertz Time-Domain Spectra of the Sample Points to be Detected on the Surface of the Meta-Material with or without the Metal Layer
A terahertz time-domain spectrometer and a computer are started. The meta-material is put on a sample holder for detection, and a terahertz time-domain system is filled with nitrogen to reduce the internal humidity to less than 0.2% for detection. The terahertz time-domain spectra of the sample points to be detected on the meta-material in a range of 0.1 THz-2 THz are acquired at a humidity of less than 0.2%. A terahertz time-domain spectrum data set of all the sample points is acquired. A terahertz time-domain signal of the meta-material is converted into a terahertz frequency-domain signal through a fast Fourier transform, and a reflectivity and transmittance of the sample point to be detected are acquired through the terahertz frequency-domain signal.
In conclusion, in the multi-waveband-tunable multi-scale meta-material of the present disclosure, the metal layer is on the micrometer scale, and the nanoparticle layer is on the nanometer scale. The microstructure of the metal layer enables the meta-material to amplify the terahertz spectral signal, and the nanostructure of the nanoparticle layer enables the meta-material to amplify the Raman spectral signal, thereby realizing both terahertz and Raman spectral detection. The detection method of the present disclosure is sensitive, simple, and fast to operate, and satisfies the increasing demand for rapid detection. The meta-material of the present disclosure is flexible and stretchable, can be closely attached to various samples, and realizes the function of spectral tuning by stretching.
The above specific implementations are intended to explain the present disclosure, rather than to limit the present disclosure. Any modification and change to the present disclosure within the spirit of the present disclosure and the protection scope of the claims should fall into the protection scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202110704566.2 | Jun 2021 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2021/117103 | 9/8/2021 | WO |