Patent Application
20190119027
The present invention relates to a multilayer body, a packaging container, and a food storing method.
Conventionally, in order for prevention of oxidation and long-term storage of a variety of articles represented by foods, beverages, pharmaceuticals, medical supplies, cosmetics, metal products, and electronic products that are likely to be deteriorated or degraded due to the influence of oxygen, an oxygen scavenger is used that removes oxygen in packaging containers and packaging bags accommodating them.
The form of this oxygen scavenger developed in early days and still often used is an air-permeable sachet filled with the oxygen scavenger composed of powdery or granular iron powder, ascorbic acid, and the like.
In recent years, a film oxygen scavenger is also used that is easier to handle, has a broader range of applications, and is extremely unlikely to be accidentally ingested. Among such film oxygen scavengers, various film oxygen scavengers are proposed that are aimed not only at mere oxygen scavenging but also at odor suppression.
For example, Patent Document 1, with an intention to provide a laminate film that suppresses odor causing substances, discloses a laminate film formed by laminating an outer layer/a first adhesive layer/a barrier layer/a second adhesive layer/an oxygen absorption layer/a chemical adsorption layer/a sealing layer in this order, wherein an iron powder oxygen absorber is used in the oxygen absorption layer. The generated odor causing substances are aldehydes and acids, and in the proposed laminate film, amine compound-supported silicon dioxide that chemically adsorbs odor causing substances is used in the chemical adsorption layer.
Also, Patent Document 2, with an intention to provide an oxygen scavenging multilayer body that suppresses generation of odorous organic components produced in association with oxidation and that absorbs oxygen at a high rate, proposes an oxygen scavenging multilayer body formed by laminating an isolation layer (A), an oxygen absorption layer (B), an odor absorption layer (C) containing an odor absorbent, and an oxygen barrier layer (D) in this order. The generated odorous organic components are derived from carboxylic acids and derived from aldehydes. The odorous organic components derived from carboxylic acids are absorbed by the isolation layer (A) containing a basic compound such as a hydroxide or an oxide of metals in Group 1 and Group 2 of the periodic table as an acidic-gas absorbent, and the odorous organic components derived from aldehydes are absorbed by the odor absorption layer (C) containing an odor absorbent such as a hydrazine derivative.
However, when the laminate film described in Patent Document 1 is used in food storing applications, water released from food comes into contact with the odor absorption layer before coming into contact with the oxygen absorption layer, thus water is absorbed by the odor absorption layer, and accordingly the amount of water supplied to the oxygen absorption layer is reduced. As a result, the amount of oxygen absorbed is reduced, and the rate of oxygen absorbed is also lowered.
In the oxygen scavenging multilayer body described in Patent Document 2, the substance used in the oxygen absorption layer to absorb oxygen is an organic macromolecular compound, and therefore the amount of odor generated from the oxygen absorption layer is larger than when the substance that absorbs oxygen is iron powder. As a result, there is a possibility that the odor cannot be removed and remains even when an odor absorbent layer is provided. Also, the organic macromolecular compound tends to degrade as it absorbs oxygen, and therefore the physical strengths (seal strength, bag dropping strength and interlayer peeling strength) of the oxygen absorption layer are possibly impaired. In addition, in Patent Document 2, the basic compound is contained as an acidic-gas absorbent not in the odor absorption layer (C) but in the isolation layer (A), which is the innermost layer that comes into contact with food, and when the amount of water released from the food is large, the basic compound possibly dissolves into water.
After all, both films have room for further improvement with respect to having excellent oxygen absorbing and also reducing an odor.
Moreover, in the case of using an oxygen scavenger, food is hermetically closed in a gas barrier container. Therefore, the odor is confined within the container, and a foreign smell and deterioration of the food taste resulting from the odor become problematic. Possible causes of odor generation are generation of an odor from food, generation of an odor due to the degradation of an oxygen scavenger substance associated with the absorption of oxygen by the oxygen scavenger, generation of an odor due to contact between the oxygen scavenger and substances in the food, and the like.
The present invention was made in view of the above-described circumstances, and one of the objects is to provide a multilayer body having excellent oxygen absorbing and also capable of sufficiently suppressing an odor, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used.
Also, another object of the present invention is to provide a multilayer body capable of highly maintaining the flavor of food by absorbing an odor and suppressing permeation of oxygen from outside air when the food is packed and stored, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used.
As a result of having conducted diligent research to achieve the above objects, the inventors found that by using an oxygen absorption layer and an odor absorption layer containing specific components and laminating the layers of a multilayer body in a specific order, it is possible to provide a multilayer body capable of retaining excellent oxygen absorbing and sufficiently suppressing an odor, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used, and accomplished the present invention. Moreover, the inventors found that by using such a multilayer body and the like for storing food to reduce an odor and, furthermore, suppress permeation of oxygen from outside air, the flavor of the food can be highly maintained, and accomplished the present invention.
That is to say, the present invention is as set forth below.
(1) A multilayer body comprising a sealing layer (A) comprising a thermoplastic resin, an oxygen absorption layer (B) comprising a thermoplastic resin and iron powder, an odor absorption layer (C) comprising a thermoplastic resin and an inorganic base, and an oxygen barrier layer (D) having oxygen barrier properties, the layers being laminated in a described order.
(2) The multilayer body according to (1), wherein the inorganic base is an inorganic base having calcium.
(3) The multilayer body according to (1) or (2), wherein the oxygen absorption layer (B) comprises the iron powder in an amount of 5.0% by mass or more and 60.0% by mass or less based on a total amount thereof, and the odor absorption layer (C) comprises the inorganic base in an amount of 0.10% by mass or more and 20.0% by mass or less based on a total amount thereof.
(4) The multilayer body according to any one of (1) to (3), wherein the iron powder has an average particle size of 10 μm or more and 40 μm or less, and calcium oxide and/or calcium hydroxide contained in the odor absorption layer (C) has an average particle size of 5 μm or more and 25 μm or less.
(5) A packaging container comprising the multilayer body according to any of (1) to (4), with the sealing layer (A) comprising a thermoplastic resin being on inside, and the oxygen barrier layer (D) having oxygen barrier properties on outside.
(6) A food storing method, wherein food is packed and stored in the packaging container according to (5).
(7) The storing method according to (6), wherein the food has a water activity (Aw) of 0.3 or more and 1.0 or less.
(8) The storing method according to (6) or (7), wherein the food is any of a chocolate confection and edible meat containing lipid in an amount of 1% by mass or more and 50% by mass or less.
The present invention can provide a multilayer body having excellent oxygen absorbing and capable of sufficiently suppressing an odor, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used. Moreover, the present invention can provide a multilayer body capable of highly maintaining the flavor of food by absorbing an odor generated from the food and suppressing permeation of oxygen from outside air when the food is packed and stored, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used.
Hereinafter, an embodiment for carrying out the present invention (hereinafter simply referred to as the “present embodiment”) will now be described in detail in reference to the drawings as necessary. However, the present invention is not limited to the present embodiment described below. Various modifications to the present invention can be made without departing from the scope of the present invention. In the drawings, the same components are given the same reference numbers, and repetitive descriptions are omitted. The positional relationship such as top, bottom, right, and left is based on the positional relationship shown in the drawings unless specified otherwise. Moreover, the dimensional ratios in the drawings are not limited to the illustrated ratios.
When such a multilayer body is used, water released from food comes into contact with the oxygen absorption layer (B) before coming into contact with the odor absorption layer (C), therefore the amount of water supplied to the oxygen absorption layer (B) is not reduced and, as a result, a reduction of the amount of oxygen absorbed and a decrease of the rate of oxygen absorbed can be prevented.
The oxygen absorbing substance contained in the oxygen absorption layer (B) is iron powder, and therefore unlike the case where the oxygen absorbing substance is an organic macromolecular compound, the oxygen absorbing substance is not degraded even when it absorbs oxygen, and can suppress odor generation and deterioration of the physical strength of the oxygen absorption layer (B). Moreover, the multilayer body of the present embodiment includes the sealing layer (A) more toward the outside than the oxygen absorption layer (B) and the odor absorption layer (C) containing an inorganic base are. Accordingly, the oxygen absorption layer (B) and the odor absorption layer (C) containing an inorganic base do not directly come into contact with food and dissolve into water. As a result, deterioration of the flavor of the food resulting from the iron powder, the inorganic base, and like substances contained in those layers can be prevented.
The thickness of the multilayer body is suitably set according to the application thereof, and for example, the multilayer body may be a multilayer film having a thickness of 30 μm or more and 250 μm or less, or may be a multilayer sheet having a thickness of more than 250 μm and 3000 μm or less. More specifically, in the case of using the multilayer body of the present embodiment in, for example, a soft packaging container for storing a chocolate confection as described below, the multilayer body is preferably a multilayer film having a thickness of 30 μm or more and 250 μm or less from the viewpoint that it needs to be thin to maintain flexibility. In the case of using the multilayer body of the present embodiment in a hard packaging container in the form of a blister or a tray for storing edible meat as described below, the multilayer body is preferably a multilayer sheet having a thickness of more than 250 μm and 3000 μm or less from the viewpoint that hardness is required to maintain the specific shape of a blister, a tray, or the like.
The sealing layer (A) according to the present embodiment contains at least a thermoplastic resin. The sealing layer (A) plays a role of a sealant and, in a packaging container in which the multilayer body of the present embodiment is used, can also play a role of separating an accommodated item such as food and the oxygen absorption layer (B) by not allowing them to come into contact. Also, the sealing layer (A) can play a role of efficient oxygen permeation so as not to obstruct rapid oxygen absorption by the oxygen absorption layer (B).
The oxygen permeability of the sealing layer (A) is preferably 1000 cc/(m2·24 h·atm) or more. Accordingly, the rate at which the multilayer body of the present embodiment absorbs oxygen can be further increased. Oxygen permeability is measured under conditions having a measurement temperature of 25° C. and a cell area of 50 cm2 using “OX-TRAN-2/21 (manufactured by MOCON Inc.)”.
Examples of the thermoplastic resin contained in the sealing layer (A) include polyolefin resins such as polyethylene, an ethylene-α-olefin copolymer, polypropylene, a propylene-ethylene random copolymer, a propylene-ethylene block copolymer, and an ethylene-cycloolefin copolymer, ethylene copolymers such as an ethylene-(meth)acrylic acid copolymer, ethylene-methyl (meth)acrylate, and an ethylene-vinyl acetate copolymer, synthetic rubber resins such as polybutadiene, polyisoprene, and a styrene-butadiene copolymer, and hydrogenated resins thereof, copolymers of soft polyvinyl chloride, polystyrene, polymethylpentene, silicone resin, and polysiloxane with another resin. One thermoplastic resin is used singly, or two or more are used in combination.
The content of the thermoplastic resin in the sealing layer (A) is preferably 70% by mass or more and 100% by mass or less, more preferably 80% by mass or more and 100% by mass or less, and further preferably 90% by mass or more and 100% by mass or less, based on the total amount (100% by mass) of the sealing layer (A). When the content of the thermoplastic resin is within the above range, the sealing layer (A) can play the above roles more effectively and reliably.
The thickness of the sealing layer (A) is preferably 1 μm or more and 100 μm or less, and more preferably 5 μm or more and 30 μm or less. When the thickness of the sealing layer (A) is within the above range, the sealing layer (A) can more effectively and reliably play the roles of further increasing the rate at which the multilayer body absorbs oxygen and separating the accommodated item and the oxygen absorption layer (B) by not allowing them to come into contact.
The sealing layer (A) may contain a material other than the thermoplastic resin as long as the sealing layer (A) is not inhibited from playing the above roles. Examples of such materials include, but are not particularly limited to, fillers such as calcium carbonate, clay, mica, and silica, desiccants, pigments, dyes, antioxidants, slip agents, antistatic agents, stabilizers, and plasticizers. One of these is used singly, or two or more are used in combination.
The oxygen absorption layer (B) according to the present embodiment contains a thermoplastic resin and iron powder. The oxygen absorption layer (B) plays a role of absorbing oxygen that would permeate the multilayer body, such as oxygen that would enter from outside air the inside of a packaging container in which the multilayer body of the present embodiment is used, and oxygen that remains in the packaging container.
A known thermoplastic resin can be suitably used, and examples include, but are not particularly limited to, low density polyethylene, intermediate density polyethylene, high density polyethylene, linear low density polyethylene, linear ultra low density polyethylene, polypropylene, poly-1-butene, poly-4-methyl-1-pentene, or polyolefins such as random or block copolymers of α-olefins such as ethylene, propylene, 1-butene, and 4-methyl-1-pentene, or mixtures thereof. One thermoplastic resin is used singly, or two or more are used in combination.
The content of the thermoplastic resin in the oxygen absorption layer (B) is not particularly limited, and may be 45% by mass or more and 85% by mass or less, may be 50% by mass or more and 80% by mass or less, and may be 55% by mass or more and 75% by mass or less, based on the total amount (100% by mass) of the oxygen absorption layer (B).
Iron powder is not particularly limited as long as the surface of iron is exposed, and iron powder known in the art is suitably used, such as reduced iron powder, electrolytic iron powder, and atomized iron powder. In addition, ground products, machined articles, and the like of cast iron and the like are also usable. One of these is used singly, or two or more are used in combination. Iron powder acquires oxygen absorbability by undergoing a reaction with water that enters the oxygen absorption layer (B).
The average particle size of iron powder is preferably 0.1 μm or more and 200 μm or less, and more preferably 1 μm or more and 50 μm or less. When the average particle size of the iron powder is within the above range, contact with oxygen is better, the oxygen absorbability of the oxygen absorption layer (B) is increased, and also the film formability of the oxygen absorption layer (B) can be further increased. The average particle size of iron powder is measured with a particle size analyzer such as Microtrac MT3000 II (trade name) manufactured by Nikkiso Co., Ltd., laser diffraction particle size distribution analyzer SALD-3000 (trade name) manufactured by Shimadzu Corporation, or the like.
The content of iron powder is not particularly limited, and is preferably 5.0% by mass or more and 60% by mass or less, more preferably 15% by mass or more and 50% by mass or less, and further preferably 20% by mass or more and 40% by mass or less, based on the total amount (100% by mass) of the oxygen absorption layer (B). Accordingly, the oxygen absorbability of the oxygen absorption layer (B) is further increased, also degradation of food-derived oil or the like due to iron powder is further suppressed, and therefore generation of gas that causes a foreign smell can be further reduced.
The oxygen absorption layer (B) may contain a material other than the thermoplastic resin and iron powder as long as the oxygen absorption layer (B) is not inhibited from playing the above role. Examples of such materials include desiccants, adsorbents, antibacterial agents, colorants, and deodorizers. One of these is used singly, or two or more are used in combination.
The desiccant means an agent that absorbs water from air, and examples include silica gel, quicklime (calcium oxide), calcium chloride, phosphorus pentaoxide, and aluminum oxide. The adsorbent means an agent that physically fixes atoms, molecules, fine particles, and the like to the surface thereof, and specific examples include activated carbon, zeolite, silica gel, and aluminum oxide. In particular, silica gel and aluminum oxide also function as desiccants and are thus preferable. When the oxygen absorption layer (B) contains a desiccant and an adsorbent, the contents thereof are preferably smaller than that of iron powder (for example, more than 0.0% and less than 5.0% based on the total amount of the oxygen absorption layer (B)). The desiccant and the adsorbent normally have water absorbability, and therefore by configuring the contents thereof to be smaller than that of iron powder, the reactivity of iron powder with water can be increased.
The thickness of the oxygen absorption layer (B) is not particularly limited, and is preferably 1 μm or more and 300 μm or less, and more preferably 10 μm or more and 200 μm or less. Accordingly, the rate at which the multilayer body absorbs oxygen can be further increased, and also deterioration of the flexibility of the multilayer body can be prevented.
The odor absorption layer (C) contains a thermoplastic resin and an inorganic base. The odor absorption layer (C) plays a role of absorbing an odor that comes into contact with the multilayer body. In a packaging container in which the multilayer body of the present embodiment is used, an odor generated from an accommodated item such as food can be absorbed.
A known thermoplastic resin can be suitably used, and examples include, but are not particularly limited to, low density polyethylene, intermediate density polyethylene, high density polyethylene, linear low density polyethylene, linear ultra low density polyethylene, polypropylene, poly-1-butene, and poly-4-methyl-1-pentene, or polyolefins such as random or block copolymers of α-olefins such as ethylene, propylene, 1-butene, and 4-methyl-1-pentene, or mixtures thereof. One thermoplastic resin is used singly, or two or more are used in combination.
The content of the thermoplastic resin in the odor absorption layer (C) is not particularly limited, and may be 70% by mass or more and 98% by mass or less, may be 75% by mass or more and 98% by mass or less, and may be 80% by mass or more and 95% by mass or less, based on the total amount (100% by mass) of the odor absorption layer (C).
The inorganic base is an inorganic compound that exhibits basicity, and absorbs an odor-causing gas. Examples of the inorganic base include hydroxides, carbonates, hydrogencarbonates, and oxides of metals in Group 1 and Group 2 of the periodic table. More specific examples include lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide, magnesium hydroxide, sodium carbonate, potassium carbonate, calcium carbonate, magnesium carbonate, sodium hydrogencarbonate, potassium hydrogencarbonate, calcium hydrogencarbonate, calcium oxide, and magnesium oxide. Among these, from the viewpoint of more effectively and reliably demonstrating the action and effect provided by the present invention, an inorganic base having a metal in Group 2 of the periodic table is preferable, an inorganic base having calcium or magnesium is more preferable, an inorganic base having calcium is further preferable, one or more inorganic bases selected from the group consisting of calcium oxide, calcium hydroxide, calcium oxide, and calcium hydroxide are furthermore preferable, and one or more inorganic bases selected from the group consisting of calcium oxide and calcium hydroxide are particularly preferable.
The average particle size of the inorganic base is preferably 0.1 μm or more and 200 μm or less, more preferably 1 μm or more and 50 μm or less, and particularly preferably 5 μm or more and 25 μm or less. When the average particle size of the inorganic base is within the above range, contact with an odor is better, the odor absorbability of the odor absorption layer (C) is increased, and also the film formability of the odor absorption layer (C) can be further increased. The average particle size of the inorganic base is measured with a particle size analyzer such as Microtrac MT3000 II (trade name) manufactured by Nikkiso Co., Ltd., laser diffraction particle size distribution analyzer SALD-3000 (trade name) manufactured by Shimadzu Corporation, or the like.
The content of the inorganic base in the odor absorption layer (C) is preferably 0.10% by mass or more and 20.0% by mass or less, more preferably 0.50% by mass or more and 17.0% by mass or less, and further preferably 1.0% by mass or more and 15.0% by mass or less, based on the total amount (100% by mass) of the odor absorption layer (C). When the content of the inorganic base is within the above range, the odor absorbability of the odor absorption layer (C) is further increased, and also a decrease of the oxygen absorbability of the oxygen absorption layer (B) associated with the absorption of water by the odor absorption layer (C) can be further suppressed.
The odor absorption layer (C) may contain a material other than the thermoplastic resin and the inorganic base as long as the odor absorption layer (C) is not inhibited from playing the above role. Examples of such materials include desiccants, adsorbents, antibacterial agents, colorants, and deodorizers (except for those regarded as inorganic bases). One of these is used singly, or two or more are used in combination. Examples of desiccants and adsorbents are as those described above and, in particular, silica gel and aluminum oxide are preferable. When the odor absorption layer (C) contains a desiccant and an adsorbent, the contents thereof are preferably smaller than that of the inorganic base (for example, more than 0.0% and less than 5.0% based on the total amount of the odor absorption layer (C)). Accordingly, it is possible to further suppress the creation of a site where the inorganic base is not present in the odor absorption layer (C) due to the uneven distribution of the inorganic base in the odor absorption layer (C).
The thickness of the odor absorption layer (C) is not particularly limited, and is preferably 1 μm or more and 300 μm or less, and more preferably 10 μm or more and 200 μm or less. Accordingly, the odor absorbability of the multilayer body can be further increased, and also deterioration of the flexibility of the multilayer body can be prevented.
The oxygen barrier layer (D) is a layer having oxygen barrier properties and, for example, by containing an oxygen barrier substance, can attain the oxygen barrier properties thereof. The oxygen barrier substance means a substance having an oxygen permeability of 100 cc/(m2·24 h·atm) or less. Examples of oxygen barrier substances that can be contained in the oxygen barrier layer (D) include polyester (such as polyethylene terephthalate), polyamide, Nylon MXD6, an ethylene-vinyl alcohol copolymer, and vinylidene chloride on which silica or alumina is vapor-deposited. The oxygen barrier layer (D) may be metal foil such as aluminum foil. The thickness of the oxygen barrier layer (D) is preferably 1 μm or more and 300 μm or less, and more preferably 1 μm or more and 100 μm or less. When the thickness of the oxygen barrier layer (D) is within the above range, the oxygen barrier effect can be further increased, and deterioration of flexibility can be prevented. As for a method for measuring oxygen permeability, the method exemplified as a method for measuring the oxygen permeability of the sealing layer (A) can be used.
In addition to the sealing layer (A), the oxygen absorption layer (B), the odor absorption layer (C), and the oxygen barrier layer (D), the multilayer body of the present embodiment may include another layer as long as it does not inhibit the present invention from achieving the objects. Examples of such layers include an adhesive layer, a light-shielding layer, a peelable layer, and a tearable layer.
For example, from the viewpoint of further increasing adhesion between two adjacent layers, the multilayer body of the present embodiment may include an adhesive layer between the two layers. The adhesive layer preferably contains a thermoplastic resin that has adhesion. Examples of the thermoplastic resin that has adhesion include acid-modified polyolefin resins obtained by modifying a polyolefin resin such as polyethylene or polypropylene with an unsaturated carboxylic acid such as acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, or itaconic acid; and polyester thermoplastic elastomers containing a polyester block copolymer as a main component. The thickness of the adhesive layer is not particularly limited and, from the viewpoint of demonstrating practical adhesive strength and ensuring molding processability, is preferably 2 μm or more and 100 μm or less.
From the viewpoint of further enhancing the light-shielding properties, the multilayer body of the present embodiment may include a light-shielding layer on the opposite side of the oxygen barrier layer (D) from the odor absorption layer (C) especially in the case of using a metal-free layer as the oxygen barrier layer (D). Examples of the light-shielding layer include metal foil and vapor-deposited film. Here, the metal foil is not particularly limited, and is preferably aluminum foil. From the viewpoint of light-shielding properties, flex resistance, and the like, the thickness of the metal foil is preferably 3 μm or more and 50 μm or less, more preferably 3 μm or more and 30 μm or less, and further preferably 5 μm or more and 15 μm or less. The vapor-deposited film is not particularly limited and, for example, is a resin film on which a membrane of a metal such as aluminum or alumina or a metal compound such as a metal oxide is vapor-deposited. Examples of methods for forming a vapor-deposited film include methods wherein a metal or a metal compound is vapor-deposited on a resin film by a physical vapor deposition method such as a vacuum deposition method, a sputtering method, or an ion plating method, a chemical vapor deposition method such as PECVD, or the like. From the viewpoint of light-shielding properties, flex resistance, and the like, the thickness of the vapor-deposited film is preferably 5 nm or more and 500 nm or less, and more preferably 5 nm or more and 200 nm or less.
Moreover, in the case of using the multilayer body of the present embodiment as a packaging container or the like described below, the multilayer body may include a peelable layer or a tearable layer to facilitate the opening of the packaging container. As a peelable layer, for example, a film obtained by blending two or more different polyolefins to control seal strength and peel strength is generally known. As a tearable layer, for example, a tearable film obtained by blending Nylon 6 with Nylon MXD6 is generally known.
The multilayer body of the present embodiment can be produced by, for example, co-extruding with a multilayer film manufacturing apparatus a laminate having a multilayer structure obtained by laminating a resin composition containing the materials of the sealing layer (A), a resin composition containing the materials of the oxygen absorption layer (B), a resin composition containing the materials of the odor absorption layer (C), and a composition containing the materials of the oxygen barrier layer (D) in this order. Alternatively, it is also possible that a laminate having a multilayer structure obtained by laminating a resin composition containing the materials of the sealing layer (A), a resin composition containing the materials of the oxygen absorption layer (B), and a resin composition containing the materials of the odor absorption layer (C) is produced by co-extrusion with a multilayer film manufacturing apparatus, and then the oxygen barrier layer (D) is adhered to the odor absorption layer (C) with an adhesive. Also, in co-extrusion, an adhesive layer may be provided between the layers as necessary.
The multilayer body of the present embodiment can be used as a part of or the entirety of a packaging container such as a packaging bag as an oxygen scavenging packaging material.
Moreover, the multilayer body of the present embodiment can be used as an oxygen scavenger formed into a sheet or a film, or as an oxygen scavenger package body in a form obtained by placing it in an air-permeable sachet. Also, the multilayer body of the present embodiment can be molded into label, card, packing, and like forms and used as an oxygen scavenging body.
Applications of the multilayer body of the present embodiment are not limited, and the multilayer body demonstrates highly practical oxygen scavenging performance and odor absorbability in the field of storage and quality retention of foods, beverages, pharmaceuticals, medical supplies, cosmetics, metal products, electronic products, and the like. In the field of food storage among these, the multilayer body can demonstrate effectively high oxygen scavenging performance and odor absorbability in particular.
The food storing method of the present embodiment is a method wherein food is packed and stored in the packaging container of the present embodiment. In the present embodiment, absorption of oxygen (oxygen scavenging) is carried out by iron powder reacted with water in the oxygen absorption layer (B), and therefore it is preferable that the food contains a predetermined amount of water. Specifically, the food preferably has a water activity (Aw) of 0.3 or more and 1.0 or less. Here, the water activity is a measure of the content of free water in an article and expressed as a numerical value of 0.0 or more and 1.0 or less. A water-free article has 0.0, and pure water has 1.0. That is to say, the water activity (Aw) of a given article is defined by the following formula where P is the water vapor pressure in a space after the article is hermetically sealed and an equilibrium is reached, P0 is the water vapor pressure of pure water, and RH(%) is the relative humidity in the same space:
Aw=P/P0=RH/100
In the food storing method of the present embodiment, examples of the food to be stored include water-containing foods represented by confections such as chocolate confections, jelly with fruit flesh, yokan (sweet bean paste), and pudding; fruits such as pineapples, oranges, peaches, apricots, pears, and apples; vegetables such as lettuces, radishes, and cucumbers; edible meat such as beef, pork, and chicken; seasonings such as liquid broth, mayonnaise, miso (fermented soybean paste), and grated spices; pasty foods such as jam, cream, and chocolate paste; liquid foods represented by liquid processed foods such as curry, liquid soup, simmered foods, pickles, and stew; beverages represented by drinking water, tea drinks, coffee drinks, soft drinks, alcoholic drinks, and milk; uncooked noodles and boiled noodles such as soba (buckwheat noodles), udon (wheat-flour noodles), and ramen noodles; uncooked rice such as milled rice, humidity-controlled rice, and no-wash rice, and cooked rice; processed rice products such as gomoku-meshi (Japanese pilaf), red rice, and rice gruel; and powdered seasonings such as powdered soup and soup stock powder.
Among these, a food that contains lipid in an amount of 1% by mass or more and 50% by mass or less is preferable. In addition to being likely to be degraded by oxygen, such a food is likely to generate an odor. Moreover, by using the multilayer body of the present embodiment as a packaging container or the like, the generated odor is more effectively and reliably absorbed. More specific examples of such foods include chocolate confections containing lipid in an amount of 1% by mass or more and 50% by mass or less and edible meat (such as beef) containing lipid in an amount of 1% by mass or more and 50% by mass or less. In the case of the above chocolate confection, the packaging container of the present embodiment or the like is particularly useful when storing it at normal temperature, and in the case of edible meat, the packaging container of the present embodiment or the like is particularly useful when storing it under refrigerated conditions (such as 5° C. or higher and 10° C. or lower).
Hereinafter, the present invention will now be described in more detail by way of Examples, but the present invention is not limited to these Examples.
A packaging container in the form of a bag as shown in
A packaging container in the form of a bag as shown in
67.5 parts by mass of polyethylene (trade name “Novatec LD: LC8001” manufactured by Japan Polyethylene Corporation), 30.0 parts by mass of iron powder (trade name “sponge iron powder” manufactured by Höganäs Japan, average particle size 30 μm), and 2.5 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm) were melt-kneaded at 200° C. using a biaxial kneader-extruder having two screws each having a diameter of 37 mm, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (b1) for an oxygen absorption layer (B1) was obtained.
Also, 94.2 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) and 5.9 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (c1) for an odor absorption layer (C1) was obtained.
Then, using a three-layer multilayer sheet molding apparatus equipped with first to third extruders, a feed block, a T-die, a chill roll, and a sheet take-up unit, polyethylene for a sealing layer (A) (trade name “Sumikathene L705” manufactured by Sumitomo Chemical Co., Ltd.) was extruded from the first extruder, the resin composition (b1) was extruded from the second extruder, and the resin composition (c1) was extruded from the third extruder, respectively, and a three-layer film was obtained through the feed block. The layer configuration of the three-layer film was, from the inner layer, sealing layer (A) (thickness 20 μm)/oxygen absorption layer (B1) (thickness 45 μm)/odor absorption layer (C1) (thickness 23 μm). An oxygen barrier layer (D) that had a thickness of 12 μm and was composed of silica-deposited polyethylene terephthalate (trade name “Barrierlocks” manufactured by Toray Advanced Film Co., Ltd.) was adhered to the odor absorption layer (C1) side of the obtained three-layer film by dry lamination, with the silica-deposited surface being the adhered surface, and thereby a multilayer body was obtained.
The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
94.8 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation), 2.9 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm), and 2.3 parts by mass of silica gel (trade name “Sylysia 710” manufactured by Fuji Silysia Chemical Ltd.) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (c2) for an odor absorption layer (C2) was obtained. Except that the resin composition (c2) was used in place of the resin composition (c1), a multilayer body including an odor absorption layer (C2) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
88.3 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) and 11.7 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (c3) for an odor absorption layer (C3) was obtained. Except that the resin composition (c3) was used in place of the resin composition (c1), a multilayer body including the odor absorption layer (C3) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
89.7 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation), 5.9 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm), and 4.5 parts by mass of silica gel (trade name “Sylysia 710” manufactured by Fuji Silysia Chemical Ltd.) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (c4) for an odor absorption layer (C4) was obtained. Except that the resin composition (c4) was used in place of the resin composition (c1), a multilayer body including an odor absorption layer (C4) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
Except that polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) was used in place of the resin composition (c1) for the odor absorption layer (C), a multilayer body including a polyethylene layer (PE) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
64.6 parts by mass of polyethylene (trade name “Novatec LD: LC8001” manufactured by Japan Polyethylene Corporation), 30.0 parts by mass of iron powder (trade name “sponge iron powder” manufactured by Höganäs Japan, average particle size 30 μm), and 5.4 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (e2) was obtained. Except that the resin composition (e2) was used in place of the resin composition (b1) for the oxygen absorption layer (B1), and polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) was used in place of the resin composition (c1) for the odor absorption layer (C1), a multilayer body including a layer (E2) in place of the oxygen absorption layer (B1) and including the polyethylene layer (PE) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
66.3 parts by mass of polyethylene (trade name “Novatec LD: LC8001” manufactured by Japan Polyethylene Corporation), 30.0 parts by mass of iron powder (trade name “sponge iron powder” manufactured by Höganäs Japan, average particle size 30 μm), 2.5 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm), and 1.3 parts by mass of silica gel (trade name “Sylysia 710” manufactured by Fuji Silysia Chemical Ltd.) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (e3) was obtained. Except that the resin composition (e3) was used in place of the resin composition (b1) for the oxygen absorption layer (B1), and polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) was used in place of the resin composition (c1) for the odor absorption layer (C1), a multilayer body including a layer (E3) in place of the oxygen absorption layer (B1) and including the polyethylene layer (PE) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
95.5 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) and 4.5 parts by mass of silica gel (trade name “Sylysia 710” manufactured by Fuji Silysia Chemical Ltd.) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (e4) was obtained. Except that the resin composition (e4) was used in place of the resin composition (c1) for the odor absorption layer (C1), a multilayer body including a layer (E4) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
91.0 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) and 9.0 parts by mass of silica gel (trade name “Sylysia 710” manufactured by Fuji Silysia Chemical Ltd.) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (e5) was obtained. Except that the resin composition (e5) was used in place of the resin composition (c1) for the odor absorption layer (C1), a multilayer body including a layer (E5) in place of the odor absorption layer (C1) was obtained in the same manner as in Example 1. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
97.1 parts by mass of polyethylene (trade name “Novatec LD: LC606” manufactured by Japan Polyethylene Corporation) and 2.9 parts by mass of calcium oxide (manufactured by Calfine Co., Ltd., average particle size 5 μm) were melt-kneaded at 200° C. using the above biaxial kneader-extruder, strands were extruded from the extruder head, cooled, and then pelletized, and thereby a resin composition (c6) for an odor absorption layer (C6) was obtained.
Then, a three-layer film was obtained in the same manner as in Example 1 except that the resin composition (c6) was extruded from the second extruder and the resin composition (b1) was extruded from the third extruder. The layer configuration of the three-layer film was, from the inner layer, sealing layer (A) (thickness 20 μm)/odor absorption layer (C6) (thickness 23 μm)/oxygen absorption layer (B1) (thickness 45 μm). An oxygen barrier layer (D) that had a thickness of 12 μm and was composed of silica-deposited polyethylene terephthalate (trade name “Barrierlocks” manufactured by Toray Advanced Film Co., Ltd.) was adhered to the oxygen absorption layer (B1) side of the obtained three-layer film by dry lamination, with the silica-deposited surface being the adhered surface, and thereby a multilayer body was obtained.
The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
Except that an oxidizable thermoplastic resin (trade name “Cryovac (R) OS Films” manufactured by Sealed Air) was used in place of the resin composition (b1) for the oxygen absorption layer (B1), a multilayer body including an oxidizable thermoplastic resin layer (EO) in place of the oxygen absorption layer (B1) was obtained in the same manner as in Example 3. The obtained multilayer body was evaluated by the above “multilayer body evaluation method 1” and “multilayer body evaluation method 2”. Results are shown in Table 1 together with the configuration of the multilayer body.
The present application is based on a Japanese patent application (Japanese Patent Application No. 2016-239684) filed on Dec. 9, 2016, the contents of which are incorporated herein by reference.
The present invention can provide a multilayer body having excellent oxygen absorbing and capable of sufficiently suppressing an odor, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used. Moreover, the present invention can provide a multilayer body capable of highly maintaining the flavor of food by absorbing an odor and suppressing permeation of oxygen from outside air when the food is packed and stored, a packaging container in which the multilayer body is used, and a food storing method in which the packaging container is used. Therefore, the present invention has industrial applicability in fields where such effects are required, such as food packaging.
(A) Sealing layer
(B) Oxygen absorption layer
(C) Odor absorption layer
(D) Oxygen barrier layer
10 Multilayer body
100 Packaging container
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-239684 | Dec 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2017/039379 | 10/31/2017 | WO | 00 |