Patent Application
20240105391
This application claims the benefit of priority to Japanese Patent Application No. 2020-166431 filed on Sep. 30, 2020. The entire contents of this application are hereby incorporated herein by reference.
The present invention relates to a multilayer ceramic capacitor.
Conventionally, a multilayer ceramic capacitor includes external electrodes at both ends of a multilayer body including side gap portions on both side surfaces of a laminate chip including internal electrodes and dielectrics laminated therein (see Japanese Unexamined Patent Application Publication No. 2018-148117).
The external electrodes each may include a base electrode layer and a plated layer on an outer side thereof, and the base electrode layer may include glass. In this case, when the plating process is performed, the glass component is dissolved from the base electrode layer by the influence of the plating solution, and as a result, cracks are generated in the base electrode layer, and moisture resistance may be lowered.
Preferred embodiments of the present invention provide multilayer ceramic capacitors each having improved moisture resistance.
A preferred embodiment of the present invention provides a multilayer ceramic capacitor that includes a multilayer body including dielectric layers and internal electrode layers alternately laminated therein, base electrode layers respectively provided on both end surfaces of the multilayer body in a length direction intersecting a lamination direction, and each connected to the internal electrode layers and each including glass and copper, and plated layers respectively provided on an outer side of the base electrode layers, in which a protective layer including sulfur is provided between the glass included in the base electrode layers and the plated layers.
According to preferred embodiments of the present invention, it is possible to provide multilayer ceramic capacitors each having improved moisture resistance.
The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawings.
Preferred embodiments of the present invention will be described in detail below with reference to the accompanying drawings.
A multilayer ceramic capacitor 1 according to a preferred embodiment of the present invention will be described.
The multilayer ceramic capacitor 1 has a rectangular or substantially rectangular parallelepiped shape, and includes a multilayer body 2, and a pair of external electrodes 3 provided at both ends of the multilayer body 2. The multilayer body 2 includes an inner layer portion 11 including a plurality of sets of dielectric layers 14 and internal electrode layers 15.
In the following description, as terms representing the orientations of the multilayer ceramic capacitor 1, a direction in which the pair of external electrodes 3 are provided is defined as a length direction L. A direction in which the dielectric layers 14 and the internal electrode layers 15 are laminated (stacked) is defined as a lamination (stacking) direction T. A direction intersecting both the length direction L and the lamination direction T is defined as a width direction W. In the present preferred embodiment, the width direction is perpendicular or substantially perpendicular to both the length direction L and the lamination direction T.
Furthermore, a cross-section extending in the length direction L and the lamination direction T is defined as an LT cross-section, a cross-section extending in the length direction L and the width direction W is defined as an LW cross-section, and a cross-section extending in the width direction W and the lamination direction T is defined as a WT cross-section.
Furthermore, among the six outer surfaces of the multilayer body 2, a pair of outer surfaces opposing each other in the lamination direction T is defined as a first main surface A1 and a second main surface A2, a pair of outer surfaces opposing each other in the width direction W is defined as a first side surface B1 and a second side surface B2, and a pair of outer surfaces opposing each other in the length direction L is defined as a first end surface C1 and a second end surface C2.
When it is not necessary to particularly distinguish the first main surface A1 and the second main surface A2 from each other, they are collectively referred to as the main surface A, when it is not necessary to particularly distinguish between the first side surface B1 and the second side surface B2, they are collectively referred to as a main surface B, and when it is not necessary to particularly distinguish between the first end surface C1 and the second end surface C2, they are collectively referred to as an end surface C.
The dimension of the multilayer ceramic capacitor 1 is not particularly limited. However, for example, it is preferable that the dimension in the length direction L is about 0.2 mm or more and about 1.2 mm or less; the dimension in the width direction W is about 0.1 mm or more and about 0.7 mm or less, and the dimension in the lamination direction T is about 0.1 mm or more and about 0.7 mm or less.
The multilayer body 2 includes a laminate chip 10, and side gap portions 20 provided on both sides in the width direction W of the laminate chip 10. In the multilayer body 2, ridge portions R1 of the two surfaces of the main surface A, the side surface B, and the end surface C are chamfered and rounded.
The laminate chip 10 includes the inner layer portion 11, an upper outer layer portion 12a in the vicinity of the first main surface A1 of the inner layer portion 11, and a lower outer layer portion 12b in the vicinity of the second main surface A2 of the inner layer portion 11. When it is not necessary to particularly distinguish between the upper outer layer portion 12a and the lower outer layer portion 12b, they are collectively referred to as an outer layer portion 12.
The inner layer portion 11 includes the plurality of sets of dielectric layers 14 and internal electrode layers 15 which are alternately laminated along the lamination direction T.
The dielectric layers 14 each preferably have a thickness of, for example, about 0.4 μm or more and about 1.0 μm or less, and more preferably, about 0.4 μm or more and about 0.6 μm or less.
The dielectric layers 14 are each made of a ceramic material. As the ceramic material, for example, a dielectric ceramic including BaTiO3 as a main component is used. The number of dielectric layers 14 of the laminate chip 10 in addition to the upper outer layer portion 12a and the lower outer layer portion 12b is preferably, for example, 15 or more and 700 or less.
In the present preferred embodiment, the dielectric layers 14 do not include Ni (nickel), or alternatively, the Ni content in the dielectric layers 14 is less than the Ni content in the outer layer portion 12. Thus, it is possible to increase the size of the particles of the dielectrics in the dielectric layers 14, such that it is possible to increase the capacitance.
The internal electrode layer 15 preferably has a thickness of, for example, about 0.2 μm or more and about 0.8 μm or less. The number of the internal electrode layers 15 is preferably, for example, 15 or more and 700 or less.
The average thickness of each of the plurality of internal electrode layers 15 and the plurality of dielectric layers 14 is measured as follows. First, a cross section perpendicular or substantially perpendicular to the length direction L of the multilayer body 2 exposed by polishing is observed by a scanning electron microscope. Next, the thicknesses of the total of five lines including a center line along the lamination direction T passing through the center of the cross-section of the multilayer body 2, and two lines respectively drawn on both sides at equal or substantially equal intervals from the center line are measured. The average of these five measurements is calculated. To obtain a more accurate average thickness, the above five measurements are obtained at each of the upper portion, the middle portion, and the lower portion in the lamination direction T are obtained, and the average value of these measurements is used as the average thickness.
The internal electrode layer 15 includes a plurality of first internal electrode layers 15A and a plurality of second internal electrode layers 15B. The first internal electrode layers 15A and the second internal electrode layers 15B are alternately provided. When it is not necessary to particularly distinguish between the first internal electrode layer 15A and the second internal electrode layer 15B, they will be collectively referred to as an internal electrode layer 15.
The first internal electrode layers 15A each include a first opposing portion 152a facing the second internal electrode layer 15B, and a first lead-out portion 151a extending from the first opposing portion 152a toward the first end surface C1. The end portion of the first lead-out portion 151a is exposed to the first end surface C1, and electrically connected to the first external electrode 3A to be described later.
The second internal electrode layers 15B each include a second opposing portion 152b facing the first internal electrode layer 15A, and a second lead-out portion 151b extending from the second opposing portion 152b toward the second end surface C2. The end portion of the second lead-out portion 151b is electrically connected to the second external electrode 3B to be described later.
Furthermore, a charge is accumulated in the first opposing portion 152a of the first internal electrode layer 15A and the second opposing portion 152b of the second internal electrode layer 15B, and the characteristics of the capacitor are provided.
Furthermore, the positional deviation d2 between the end portion which is in the vicinity of the side surface B and located outermost in the width direction W and the end portion which is located innermost in the width direction W among all of the internal electrode layers 15 is, for example, about 10 μm or less.
That is, the end portions in the width direction W of the laminated internal electrode layers 15 are located at the same or substantially the same position in the width direction W. In other words, the positions of the end portions are aligned or substantially aligned in the lamination direction T.
In the present preferred embodiment, the internal electrode layers 15 are, for example, made mainly of Ni (nickel) including Sn (tin). However, the present invention is not limited thereto, and the internal electrode layers 15 may be made of, for example, a metallic material such as Cu, Ag, Pd, a Ag—Pd, and Au.
Furthermore, Mg (magnesium) included in the side gap portions 20 is segregated at the side gap portions 20 on both side surfaces of the internal electrode layers 15.
Sn-Layer 16 Extending from Internal Electrode Layer 15
The Sn-layer 16 is provided on the surfaces of the internal electrode layers 15. The Sn-layer 16 is formed by migrating from the inside to the surface during firing. The Sn-layer 16 extends from the surfaces of the internal electrode layers 15 to a boundary region Z1 between the external electrode 3, and the dielectric layers 14 and the internal electrode layers 15 adjacent to one another in the lamination direction T. Furthermore, the Sn-layer 16 also covers the boundary surfaces of the internal electrode layers 15 with the external electrode 3.
It should be noted that it is not necessary for the Sn-layer 16 to cover the entire internal electrode layers 15, and the Sn-layer 16 can only cover a portion of the internal electrode layers 15.
In the multilayer ceramic capacitor 1 of the present preferred embodiment, since the Sn-layer 16 extends to the boundary region Z1 between the dielectric layers 14 and the external electrode 3, for example, it is possible to reduce or prevent moisture through the boundary surface between the external electrode 3 and the multilayer body 2 from flowing in the interior of the inner layer portion 11, which provides high humidity resistance.
In the present preferred embodiment, the Sn-layer 16 extending from one of the internal electrode layers 15 is not coupled to the Sn-layer 16 extending from another internal electrode layer 15 adjacent to the one internal electrode layer 15, and there is also a portion where the Sn-layer 16 is not provided in the boundary region Z1 between the dielectric layer 14 and the external electrode 3. However, it is sufficiently effective to improve the humidity resistance of the multilayer ceramic capacitor 1 even in such a case.
The thickness of the outer layer portion 12 is preferably about 9.5 μm or more and about 30 μm or less, and more preferably about 9.5 μm to about 20 μm, for example, for both the upper outer layer portion 12a and the lower outer layer portion 12b.
Both the upper outer layer portion 12a and the lower outer layer portion 12b of the outer layer portion 12 are made of a dielectric ceramic material including BaTiO3 as a main component, similar to the dielectric layer 14 of the inner layer portion 11, for example. However, the upper outer layer portion 12a and the lower outer layer portion 12b differ from the dielectric layer 14 of the inner layer portion 11 in that the former includes Ni, or the content of Ni is higher in the former than in the latter. As schematically shown in
Since the multilayer ceramic capacitor 1 of the present preferred embodiment includes Ni in the outer layer portion 12, particles of the dielectric ceramic after firing are densified.
Furthermore, since the pores provided in the dielectric ceramic in the outer layer portion 12 are filled with Ni, humidity resistance is increased in the multilayer ceramic capacitor 1.
Furthermore, Ni in the outer layer portion 12 is diffused into the Cu-layer of the external electrode 3, such that the adhesion with the external electrode 3 is improved.
Although Mg is not included in the outer layer portion 12 in the present preferred embodiment, Mg may be included in the outer layer portion 12.
The side gap portions 20 include side gap portions 20 which are respectively provided in the vicinity of the first side surface B1 of the laminate chip 10 and the second side surface B2 of the laminate chip 10. When it is not necessary to particularly distinguish between the first side gap portion 20a and the second side gap portion 20b, they will be collectively referred to as a side gap portion 20.
The side gap portions 20 each cover, along the end portions, the end portions in the width direction W of the internal electrode layers 15 exposed at the both side surfaces of the laminate chip 10. There is an interface U shown in
The side gap portions 20 are made of, for example, a dielectric ceramic material including BaTiO3 as a main component, similarly to the dielectric layers 14, but further include Mg as a sintering aid. The content of Mg is, for example, about 0.2 mol % or more and about 2.8 mol % or less with respect to 100 moles of Ti at the middle portion in the length direction L of the side gap portion 20. When Mg is about 2.8 mol % or less, since the grain growth of the dielectric is not reduced or prevented in the dielectric layer 14 in the vicinity of the outermost layer of the internal electrode layers 15, a capacitance decrease is less likely to occur.
Furthermore, Mg of the side gap portion 20 and Ni of the outer layer portion 12 are segregated in a boundary region Z2 between the side gap portion 20 and the outer layer portion 12 during firing. A portion of the segregated Ni and a portion of the segregated Mg provides a Ni—Mg oxide.
That is, Ni—Mg oxide is segregated in the boundary region Z2. A portion of Ni segregated in the boundary region Z2 is present in the form of Ni in the boundary region Z2. A portion of Mg segregated in the boundary region Z2 is present in the form of Mg in the boundary region Z2. Therefore, Ni—Mg oxide, Ni, and Mg are segregated in the boundary region Z2.
Ni is not included in the dielectric layer 14. Therefore, the segregation of Ni and Ni—Mg oxide in the boundary region between the dielectric layer 14 and the side gap portion 20 is smaller than the segregation of Ni and Ni—Mg oxide in the boundary region Z2.
Since the dielectric layers 14 do not include Ni, the grain growth of the particles of the dielectric layers 14 is not reduced or prevented. Therefore, the particles of the dielectric layers 14 become large, such that it is possible to increase the capacitance of the multilayer ceramic capacitor 1.
A Ni—Mg alloy, which is an alloy of Mg included in the side gap portion 20 and Ni included in the outer layer portion 12, is segregated in the boundary region Z2 between the side gap portion 20 and the outer layer portion 12. The boundary region Z2 tends to become the penetration path of moisture. A portion of the pores in the boundary region Z2 is filled with Ni—Mg oxide. A portion of the pores present in the boundary region Z2 is filled with Ni or Mg. Thus, the multilayer ceramic capacitor 1 of the present preferred embodiment has high humidity resistance.
Regarding the end portions of the internal electrode layers 15 as described above, the positional deviation d1 between the adjacent internal electrode layers 15 on the WT cross-section including the width direction W and the lamination direction T at the middle portion in the length direction L shown in
The boundary region Z2 between the side gap portion 20 and the outer layer portion 12 is a substantially band-shaped region of about 3 μm in the width direction W around the extended line e extending in the lamination direction T on the middle in the width direction W between the end portion of the internal electrode layer 15 located outermost in the width direction W, and the end portion of the internal electrode layer 15 located innermost in the width direction W.
The segregation of Ni—Mg oxide, the segregation of Ni, and the segregation of Mg can be observed by WDX (wavelength-dispersive X-ray spectrometry).
The external electrodes 3 each include a first external electrode 3A provided on the first end surface C1 of the multilayer body 2, and a second external electrode 3B provided on the second end surface C2 of the multilayer body 2. When it is not necessary to particularly distinguish between the first external electrode 3A and the second external electrode 3B, they will be collectively referred to as an external electrode 3. The external electrode 3 covers not only the end surface C, but also covers portions of the main surface A and the side surface B which are in the vicinity of the end surface C.
As described above, the end portion of the first lead-out portion 151a of the first internal electrode layer 15A is exposed at the first end surface C1, and electrically connected to the first external electrode layer 3A. Furthermore, the end portion of the second lead-out portion 151b of the second internal electrode layer 15B is exposed at the second end surface C2, and is electrically connected to the second external electrode 3B. Thus, a plurality of capacitor elements are electrically connected in parallel between the first external electrode 3A and the second external electrode 3B.
Since the internal electrode layers 15 are each thin, a plurality of pores 15a are actually extending through the lamination direction T. Therefore, when viewed in the LT cross-section as in
Here, the number of all of the internal electrode layers 15 extending to one of the external electrodes 3 in the LT cross-section shown in
For example, when the number of all of the internal electrode layers 15 extending to one of the external electrodes 3 in the LT cross-section shown in
Furthermore, similarly to the above, when the number of all of the internal electrode layers 15 extending to one of the external electrodes 3 in the LT cross-section shown in
In common multilayer ceramic capacitors that differ from the present preferred embodiment, for example, the connection ratio N1/N0 in the LT cross-section at the position W1 passing through the middle portion in the width direction W, and the connection ratio N2/N0 in the LT cross-section at the position W2 passing through the end portions in the width direction W are greater than about 90% when expressed as a percentage. Furthermore, for example, the difference between the connection ratio N1/N0 at the position W1 passing through the middle portion in the width direction W, and the connection ratio N2/N0 at the position W2 passing through the end portion in the width direction W is smaller than about 10%.
When the connection ratio is smaller than about 90%, and the difference in the connection ratio differs greatly by the position, the connectivity between the internal electrode layer 15 and the external electrode 3 is deteriorated, the flow of electricity is reduced or prevent or becomes unstable, such that the equivalent series resistance (ESR) of the multilayer ceramic capacitor may increase.
However, in the multilayer ceramic capacitor 1 of the present preferred embodiment, the connection ratio N1/N0 at the position W1 passing through the middle portion in the width direction W, and the connection ratio N2/N0 at the position W2 passing through the end portion in the width direction W are about 90% or more when expressed as a percentage. Furthermore, the difference between the connection ratio N1/N0 at the position W1 passing through the middle portion in the width direction W, and the connection ratio N2/N0 at the position W2 passing through the end portion in the width direction W is about 10% or less.
Therefore, according to the multilayer ceramic capacitor 1 of the present preferred embodiment, the contact area between the internal electrode layer 15 and the external electrode 3 is sufficiently secured, there is no variation in the connection ratio, a good connection ratio is ensured, electricity flows well, and the equivalent series resistance (ESR) of the multilayer ceramic capacitor can also be reduced.
The connection ratio between the external electrode 3 and the internal electrode layer 15 is detected as follows.
Polishing starts at the LT side surface of the multilayer ceramic capacitor 1, and the internal electrode layers 15 begin to be exposed, such that the resultant LT cross-section polished about 5 μm is exposed.
Then, the number of the internal electrode layers 15 extending to one of the external electrodes 3 in the LT cross-section and connecting with the one of the external electrodes 3 is defined as N1.
The total number of the internal electrode layers 15 connected to the external electrode 3 provided on the same side is defined as N0.
With N1 and N0 above, the connection ratio N1/N0 at the position W1 is obtained.
Polishing starts at the LT side surface of the multilayer ceramic capacitor 1, and continues up to the middle portion of the internal electrode layers 15 in the width direction, such that the resultant LT cross-section is exposed.
Then, the number of the internal electrode layers 15 extending to one of the external electrodes 3 in the LW cross-section and connecting with the one of the external electrodes 3 is defined as N2.
The total number of the internal electrode layers 15 connected to the external electrode 3 provided on the same side is defined as N0.
With N2 and N0 above, the connection ratio N2/N0 at the position W1 is obtained.
In a case in which the number of the internal electrode layers 15 is large, it is acceptable to check about 20 pieces of the internal electrode layers 15 in the region of the outermost layer and about 40 pieces of the internal electrode layers 15 at the middle portion in the lamination direction T to obtain the number of the internal electrode layers connected to the external electrode 3 and calculate the average value.
In the multilayer ceramic capacitor 1 of the present preferred embodiment, a result of actual measurement showed that the connection ratios at the position W1 and the position W2 were about 90% or more.
The reason why it is possible to obtain high connection ratios in this way will be described in the manufacturing method described later.
The external electrode 3 includes a base electrode layer 30 and a plated layer 31 in order from the multilayer body 2.
As shown in
Furthermore, the first region 30a, the second region 30b, and the third region 30c may be divided according to the ratio of glass G. For example, in the LT cross-section, when the area ratio of glass to Cu in the entire base electrode layer 30 (area of glass/area of Cu) is defined as P, the first region 30a may be defined as a region of about 0.1P or less, the second region 30b may be defined as a region of about 1.2P or more, and the third region 30c may be defined as a region lower than about 1.0P. It should be noted that a second region may or may not be included. The second region can belong to the first region or the third region when the second region satisfies either one of the defined thickness or P of them.
The first region 30a, the second region 30b, and the third region 30c of the base electrode layer 30 are formed by firing a Cu paste in which glass G including Ba (barium) for densification is mixed, and thus, are electrodes by post-fire which are separately fired after the firing of the multilayer body 2.
The thickness of the first region 30a in the length direction L is, for example, about 0.1 μm or more and about 5 μm or less.
As schematically shown in
Ni is included in a higher density, in particular, on a side of the first region 30a in the vicinity of the inner layer portion 11, than in the other regions such as a side of the first region 30a in the vicinity of the second region 30b, the second region 30b, and the third region 30c. A Ni-rich layer is provided on the side of the first region 30a in the vicinity of the inner layer portion 11. Furthermore, the density of Ni near the internal electrode layers 15 in the side of the first region 30a in the vicinity of the inner layer portion 11 is higher than the density of Ni adjacent to the dielectric layers 14 in the side of the first region 30a in the vicinity of the inner layer portion 11. Furthermore, Ni makes a solid solution with Cu in the first region 30a, and is alloyed.
As described above, the first region 30a includes a Ni component more than the second region 30b and the third region 30c. Therefore, the internal electrode layers 15 and the base electrode layer 30 have a better connection ratio.
Particle Size of Cu being Large in Side in the Vicinity of Multilayer Body 2
Furthermore, the particle size of Cu in the first region 30a is larger than that in the second region 30b and the third region 30c. In addition, the thickness decreases as approaching the second region 30b and the third region 30c.
The particle size of Cu is specified based on the area in the LT cross-section shown in
The second region 30b corresponds to a region other than the first region 30a and the third region 30c. The second region 30b is preferably thicker than the total value of the thicknesses of the first region 30a and the third region 30c, and is, for example, about 10 μm or more and about 40 μm or less.
The second region 30b includes more glass G than the first region 30a and the third region 30c. When the area ratio of glass to Cu (area of glass/area of Cu) in the entire base electrode layer 30 in the LT cross-section is P, the glass G is, for example, equal to or larger than about 1.2P. The ratio of the glass G is obtained by measuring the area of Si by WDX, and calculating the area of Si with respect to the total area.
The third region 30c includes more Cu than the first region 30a and the second region 30b. The content of the glass is, for example, less than about 1.0P in the LT cross-section shown in
The third region 30c includes more Cu than the second region 30b and the third region 30c. Therefore, the connection ratio when mounting the multilayer ceramic capacitor 1 on a board is favorable.
Furthermore, it is possible to determine the adhesiveness of the Ni plated layer 31a by counting portions where plating is not provided by visually checking 100 locations on the surface of the plated layer 31.
The third region 30c contains Cu in the greatest amount. Therefore, the Ni plated layer 31a on the outer side is easily adhered thereto. Furthermore, the plated layer 31 overall is hardly peeled off therefrom. In the present preferred embodiment, there was no portion without plating.
In the multilayer ceramic capacitor 1 of the present preferred embodiment, since the ratio of the glass G in the second region 30b is, for example, about 1.2P or more, the multilayer ceramic capacitor 1 has a high sealability property and high moisture resistance. Regarding humidity resistance of the multilayer ceramic capacitor 1, it was determined that the humidity resistance was low when a voltage of about 6.3V was applied and the resistance was below about 100 MΩ under an environment of temperature about 85° C. and humidity about 85%. The threshold of about 100 MΩ is for the case of a capacitance of about 1 μF.
Unlike the present preferred embodiment, among 100 pieces of the multilayer ceramic capacitors 1 for comparison having the ratio of glass G smaller than about 1.2P in the second region 30b, the resistance was below about 100 MΩ in eleven pieces of the multilayer ceramic capacitors. Among 100 pieces of the multilayer ceramic capacitors 1 in the present preferred embodiment having the ratio of glass G of equal to or larger than about 1.2P in the second region 30b, there was no multilayer ceramic capacitors in which the resistance is below about 100 MΩ.
As described above, the multilayer ceramic capacitor 1 of the present preferred embodiment has favorable moisture resistance because the ratio of the glasses G in the second regions 30b, for example, about 1.2P or more.
In the third region 30c in the multilayer ceramic capacitor 1 of the present preferred embodiment, protective layers 33 including S (sulfur) and Ba (barium) are each provided on a surface of the glass G facing the Ni plated layer 31a. The protective layers 33 cover about 50% or more of the portions containing the glass G on the surface of the third region 30c, that is, the surface of the base electrode layer 30, and preferably cover about 70% or more thereof. The thicknesses of the protective layers 33 are, for example, each about 10 nm or more and about 1 μm or less.
The protective layers 33 can be confirmed by imaging a region including glass G, the third region 30c, and the Ni plated layer 31a in the region within the region in the external electrode 3 in the LT cross-section in the middle portion in the width direction by TEM (Transmission Electron Microscope)-EDX (Energy Dispersive X-ray Spectroscopy).
The thickness of the protective layer 33 is obtained by measuring the thicknesses of S and Ba from the glass G toward the interior of the Ni plated layer 31a based on the observed S and Ba images. When the surface of the glass G is a curved surface, the thickness in the normal direction is used. If the thickness varies depending on locations, average values of the regions divided into three equal portions in the lamination direction in the LT cross section may be used.
The coverage of the protective layer 33 can be obtained by dividing the length of the protective layer 33 by the length of the surface of the base electrode layer 30 including the surface of the glass G, measured on the LT cross-section.
The plated layer 31 includes, for example, the Ni plated layer 31a and the Sn plated layer 31b in order from the base electrode layer 30.
The method of manufacturing the multilayer ceramic capacitor 1 includes a multilayer body preparing step S1 of preparing the multilayer body 2, a barrel step S2, a base electrode layer forming step S3, and a plated layer forming step S4.
The multilayer body preparing step S1 includes a material sheet preparing step S11, a material sheet laminating step S12, a mother block forming step S13, a mother block cutting step S14, a side gap portion forming step S15, and the firing step S16.
A ceramic slurry including a ceramic powder including, for example, BaTiO3 as a main component, a binder, and a solvent is prepared. In the present preferred embodiment, the ceramic slurry does not include Ni, or the Ni content therein is smaller than that in the outer layer portions 12.
The ceramic slurry is molded into a sheet shape or substantially a sheet shape using, for example, a die coater, a gravure coater, a micro gravure coater, etc. on a carrier film, such that an inner layer ceramic green sheet 101 is manufactured.
Furthermore, an upper outer layer portion ceramic green sheet 112 defining and functioning as the upper outer layer portion 12a, and a lower outer layer portion ceramic green sheet 113 defining and functioning as the lower outer layer portion 12b are also manufactured in the same or substantially the same manner.
The upper outer layer portion ceramic green sheet 112 and the lower outer layer portion ceramic green sheet 113 are manufactured by a ceramic slurry including, for example, a ceramic powder including BaTiO3 as a main component, a binder, and a solvent, similarly to the inner layer ceramic green sheet 101. However, unlike the inner layer ceramic green sheet 101, the upper outer layer portion ceramic green sheet 112 and the lower outer layer portion ceramic green sheet 113 include Ni, or have a higher Ni content than the inner layer ceramic green sheet 101.
Subsequently, the conductive paste 102 including Ni, glass (Si oxide), and Sn is printed by, for example, screen-printing, ink jet printing, gravure printing, or the like, so as to have a strip-shaped pattern or substantially a strip-shaped pattern, on the inner layer ceramic green sheet 101.
Thus, the material sheet 103 is prepared by printing the conductive paste 102 defining and functioning as the internal electrode layer 15 on the surface of the inner layer ceramic green sheet 101 defining and functioning as the dielectric layer 14.
Next, in the material sheet laminating step S12, a plurality of material sheets 103 are laminated.
Specifically, the plurality of material sheets 103 are stacked such that the strip-shaped conductive pastes 102 are directed in the same or substantially the same direction and shifted by half pitch in the width direction between the adjacent material sheets 103.
Furthermore, the upper outer layer portion ceramic green sheet 112 defining and functioning as the upper outer layer portion 12a is stacked on one side of the plurality of laminated material sheets 103, and the lower outer layer portion ceramic green sheet 113 defining and functioning as the lower outer layer portion 12b is stacked on the other side thereof.
Subsequently, in the mother block forming step S13, the upper outer layer portion ceramic green sheet 112, the plurality of stacked material sheets 103, and the lower outer layer portion ceramic green sheet 113 are subjected to thermocompression bonding. As a result, the mother block 110 is formed.
Then, in the mother block cutting step S14, the mother block 110 is cut along a cutting line X and a cutting line Y intersecting the cutting line X corresponding to the dimension of the laminate chip 10. As a result, the laminate chip 10 is manufactured. It should be noted that, in the present preferred embodiment, the cutting line Y is perpendicular or substantially perpendicular to the cutting line X.
Next, a ceramic slurry in which Mg is added as a sintering aid to the dielectric powder, which is the same or substantially the same as that of the inner layer ceramic green sheet 101, is prepared. Then, the ceramic slurry is applied on a resin film, and dried to manufacture a side gap portion ceramic green sheet. It should be noted that a plurality of side gap portion ceramic green sheets may be manufactured.
Then, the side gap portion ceramic green sheet is affixed on the side portion where the internal electrode layers 15 of the laminate chip 10 are exposed, such that a layer defining and functioning as the side gap portion 20 is formed.
Thus, the side gap portion 20 is affixed to the LT side surface of the laminate chip 10, such that the multilayer body 2 in a state before firing is formed.
The layer defining and functioning as the side gap portion 20 is formed in the laminate chip 10, and the resultant body is subjected to degreasing treatment in a nitrogen atmosphere under a predetermined condition, and then fired and sintered at a predetermined temperature in a nitrogen-hydrogen-steam mixed atmosphere to form the multilayer body 2.
Since the side gap portion 20 is affixed to the laminate chip 10 including the dielectric layers 14, there is an interface between the side gap portion 20 and the laminate chip 10 even after firing.
Here, a Ni—Mg alloy, which is an alloy of Mg included in the side gap portion 20 and Ni included in the outer layer portion 12, is segregated in the boundary region Z2 between the side gap portion 20 and the outer layer portion 12. The boundary region Z2 tends to become the penetration path of moisture. Therefore, the pores existing in this portion are filled, and the moisture resistance becomes high.
Here, as shown in
As shown in
Next, barrel polishing is performed on the multilayer body 2. As a result, the ridge portion R1 of the multilayer body 2 is rounded.
Since the internal electrode layer 15 shrinks during the firing step S16, a portion of the internal electrode layers 15 may not be exposed at the end surface C. However, since the barrel step S2 is provided, the end surface C of the multilayer body 2 is also polished, such that the number of the internal electrode layers 15 which are not exposed at the end surface C is reduced.
Furthermore, the positional deviation d2 between the end portion which is in the vicinity of the side surface B and located outermost in the width direction W and the end portion which is located innermost in the width direction W among all of the internal electrode layers 15 is, for example, about 10 μm or less.
That is, the end portions in the width direction W of the laminated internal electrode layers 15 are located at the same or substantially the same position in the width direction W. In other words, the positions of the end portions are aligned or substantially aligned in the lamination direction T.
The base electrode layer forming step S3 includes a first region forming step S31, a second region forming step S32, a third region forming step S33, and a firing step S34.
In the first region forming step S31, both end surfaces C of the multilayer body 2 are immersed in a glass-containing Cu paste to form the first region 30a. To form the first region 30a, the Cu paste including Cu particles having a small particle size is used. The particle size of the Cu particles is, for example, about 0.05 μm or more and about 3 μm or less. Furthermore, it is preferable that the thickness is, for example, about 0.05 μm or more and about 1 μm or less.
Here, the positional deviation d of the internal electrode layers 15 in the vicinity of the end surface C is smaller in the barrel step. However, there is a possibility that the positional deviation d remains somewhat in the internal electrode layers 15 in the vicinity of the end surface C.
In the present preferred embodiment, since the Cu paste having a small particle size is used, the Cu paste can enter the portion of the positional deviation d remaining in the internal electrode layers 15 in the vicinity of the end surface C, leading to the favorable contact with the internal electrode layers 15.
Next, in the second region forming step S32, both end surfaces C of the multilayer body 2 are immersed in Cu pastes, each having a higher glass content than that of the first region 30a and the third region 30c, to form the second region 30b. The second region 30b includes more glass G than the first region 30a and the third region 30c. In the LT cross-section, when the area ratio of glass to Cu in the entire base electrode layer 30 (area of glass/area of Cu) is defined as P, the second region 30b may be defined as a region of, for example, about 1.2P or more. Since the ratio of the glass G in the second region 30b is about 1.2P or more, the sealing property and the moisture resistance are improved.
However, in order to reduce or prevent the deterioration of the conductivity of the second region 30b, the ratio of the glasses G in the second region 30b is preferably, for example, about 2.5P or less.
It should be noted that the particle size of the Cu particles included in the Cu paste may be the same or substantially the same as the particle size of the Cu particles included in the Cu paste, or may be larger than the particle size of the Cu particles included in the Cu paste.
Next, in the third region forming step S33, both end surfaces C of the multilayer body 2 are immersed in a Cu paste having a higher Cu content than the Cu pastes of the second region 30b and the third region 30c, to form the third region 30c. The Cu paste 118 includes glass G. The glass G includes, for example, BaO—B2O3—SiO2 glass or BaO—B2O3—SiO2—LiO—NaO glass including Ba. In addition, sulfur (S) is included in the glass G.
Then, the resultant body is heated for a predetermined time in a nitrogen atmosphere at a set firing temperature. As a result, the base electrode layer 30 is burned onto the multilayer body 2.
At this time, the Sn-layer 16 formed on the surfaces of the internal electrode layers 15 extends from the surfaces of the internal electrode layers 15 to the boundary region Z1 between the external electrode 3, and the internal electrode layers 15 and the dielectric layers 14 adjacent to the internal electrode layers 15 in the lamination direction T.
Furthermore, as schematically shown in
The plated layer forming step S4 includes a Ni plated layer forming step S41, and a Sn plated layer forming step S42.
In the Ni plated layer forming step S41, the third region 30c of the base electrode layer 30 is immersed in a plating solution for forming the plated layer 31, to form the Ni plated layer 31 on the outer periphery of the external electrode 3.
At this time, the third region 30c includes more Cu than the first region 30a and the second region 30b. The amount of Cu can be measured by calculating the area of Cu detected by WDX. The third region 30c includes more Cu than the second region 30b and the third region 30c. Therefore, the connection ratio when mounting the multilayer ceramic capacitor 1 on a board is preferable.
Here, when the third region 30c of the base electrode layer 30 is immersed in a process liquid in which the plating solution and S (sulfur) are mixed, the mixed process liquid containing the plating solution and S erodes the glass G which is exposed at the surface of the third region 30c.
However, according to the present preferred embodiment, since the glass G includes S and Ba, the S and Ba begin to gradually form the protective layer 33 on the surface of the glass G on which the erosion by the plated layer 31 is progressing.
When the formation of the protective layer 33 progresses, the erosion of the glass G by the plating solution is gradually reduced or prevented, and once the protective layer 33 is formed to have a predetermined thickness, the glass G is hardly eroded.
On the other hand, unlike the present preferred embodiment, if the protective layer 33 is not formed, the plating solution continues to erode the glass G, and advances to the second region 30b and the first region 30a in the interior of the base electrode layer 30.
However, according to the present preferred embodiment, at an initial stage in which the third region 30c of the base electrode layer 30 is immersed in the plating solution in this way, the protective layer 33 is formed by the process liquid including Ba and S included in the glass G. Furthermore, the protective layer 33 defining and functioning as a barrier of the glass G to the plating solution, and thus, further erosion of the glass G by the plating solution is reduced or prevented.
Therefore, it is possible to obtain the multilayer ceramic capacitor 1 in which the erosion of the base electrode layer 30 by the plating solution is small, and the heat resistance, the water resistance, and the moisture resistance are high.
The third region 30c includes Cu in the most amount. Therefore, the Ni plated layer 31a on the outer side is easily adhered thereto. Furthermore, the plated layer 31 overall is hardly peeled off therefrom.
Then, the Sn plated layer 31b is formed on the outer side of the Ni plated layer 31a.
Through the above steps, the multilayer ceramic capacitor 1 of the present preferred embodiment is manufactured. Although preferred embodiments of the present invention have been described above, the present invention is not limited to this preferred embodiment, and various modifications may be made within the scope thereof.
For example, in the present preferred embodiment, the base electrode layer 30 is provided with the three regions. However, the present invention is not limited to this, and the base electrode layer 30 may include only the first region 30a and the third region 30c without the second region 30b. Furthermore, the base electrode layer 30 may include only one region.
In the present preferred embodiment, the base electrode layer 30 including the three regions is manufactured by three coating steps of the first region forming step S31, the second region forming step S32, and the third region forming step S33. However, the present invention is not limited to this, and the base electrode layer 30 including a plurality of regions may be manufactured by adjusting the material and the temperature profile, for example.
In the present preferred embodiment, the glass G includes Ba. However, the glass G may not include Ba. In this case, the protective layer 33 does not include Ba. However, the protective layer 33 includes S by the process liquid including S.
In the present preferred embodiment, the Cu paste having a small particle size is used in the barrel step when the first region 30a of the base electrode layer 30. However, the present invention is not limited thereto. In order to improve the connection ratio, for example, either one of performing the barrel step or using a Cu paste having a small size may be used.
In the present preferred embodiment, the multilayer ceramic capacitor 1 is manufactured by manufacturing the laminate chip 10 following which the side gap portions 20 are affixed on both sides of the laminate chip 10. However, the present invention is not limited to this, and the side gap portions 20 may be manufactured together at the time of manufacturing the laminate chip 10.
In the present preferred embodiment, two plated layers are provided. However, the present invention is not limited thereto, and the plated layer may include a single layer.
Furthermore, the size of the multilayer ceramic capacitor 1, and the thickness and the number of layers of the internal electrode layers 15, the dielectric layers 14, the outer layer portions 12, and the external electrodes 3, which are specified in the present preferred embodiment, are not limited to the numerical values described, and may vary therefrom.
Furthermore, the components included in each layer are not limited to those described in the present preferred embodiment.
While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing from the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-166431 | Sep 2020 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17487346 | Sep 2021 | US |
| Child | 18524673 | US |