Patent Application
20180223107
Polymeric coating materials described herein exhibit high optical transmittance in the visible spectrum. The materials of the present disclosure may be easily coated onto the surface of desired substrates via common coating processes, such as by spin coating, screen printing, dip, roll-to-roll, slot die, draw bar, or spray coating, for many electronic applications. The thickness of coatings described herein may range from tens of nanometers to millimeters, as may be required for specific applications. The materials of the present disclosure are unique in additionally providing a high refractive, high transparency film or coating or layer, as may be desirable in electronics applications where these properties are important to the performance.
For example, in a traditional Organic Light Emitting Diode (OLED), only 25% of light generated is emitted to the environment, while the remaining light is generally lost in the device. A high percentage of this loss is due to the low refractive index (RI) of the encapsulation materials. A high refractive index high transparency organic coating, with a refractive index around 1.8 or higher, as may be produced with a material of the present disclosure, may dramatically enhance the efficacy of the OLED lighting and display devices including same. High refractive index coatings of the present disclosure will also be advantageously incorporated in other devices, such as light emitting diode (LED) lighting, light emitting diode (LED) displays, touch screens, sensors, and solar cells.
The present disclosure provides a dispersion containing capped nanocrystals in a solvent such as but not limited to propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The nanocrystals of the present disclosure may comprise nanocrystals of metal oxides, such as zirconium oxide, titanium oxide, hafnium oxide, or zinc oxide, which high bulk refractive indexes, typically larger than 2 in the visible spectrum, as well as exceptional transparency.
The nanocrystals of the presently disclosure may be capped with specific functional group, also referred to as capping agents, or capping groups. These specific functional groups are grafted to the surface of the nanocrystals. As used herein capped nanocrystals and at least partially capped nanocrystals are functionally equivalent.
The capping agent of capped nanocrystals in the present disclosure may include 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, benzoic acid, or any combination thereof.
Capping of nanocrystals may require a solvent exchange and as-synthesized nanocrystals may be surface modified in a solvent other than the solvent of nanocrystals synthesis. Solvent exchange may be accomplished by, for example, decanting reaction mixture and rinsing the nanocrystals with the capping solvent, which may then be used as a washing or rinsing solvent that is itself decanted to produce a wet cake of nanocrystals.
The capped nanocrystals of the presently disclosed dispersion may constitute less than 10% by weight of the total dispersion, or 10%-20% by weight of the total dispersion, or 20%-30% by weight of the total dispersion, or polymer, or 30%-40% by weight of the total dispersion, or 40%-50% by weight of the total dispersion, or 50%-60% by weight of the total dispersion, or 60%-70% by weight of the total dispersion, or 70%-80% by weight of the total dispersion, or 80%-90% by weight of the total dispersion, or 90%-93% by weight of the total dispersion.
Optical transmittance is a common technique to evaluate the quality of a dispersion, formulation, and a nanocomposite film or coating. Light propagating through a sample can be absorbed, scattered, or transmitted. The normal transmittance at a given wavelength is defined as Tn=I/I0, where I0 is the intensity of incident light and I is the intensity of the light in the forward direction collected by the detector, which includes both light that is transmitted without scattering and light that is scattered into the forward direction. Theoretically the forward direction is defined as the same direction of the incident light, and however the detector usually collects light within a small solid angle around this direction due to the finite size of the detector. This transmittance is called normal transmittance or just transmittance, throughout this disclosure. When measuring normal transmittance, measurement artifacts, such as Fresnel reflections off of various interfaces and absorption by cuvette walls, need to be accounted for and removed. This can be taken care of by using a reference, either by measuring the sample and reference side by side in the instrument, or by measuring the sample and reference sequentially and then correcting the data mathematically afterward. The liquid nanocrystal dispersion sample can be measured in a cuvette made of glass, quartz, or plastic, and due to the finite thickness of the cuvette wall, there are four interfaces where Fresnel reflections can occur, and two walls where absorption can occur. Using a cuvette with same material, wall thickness, and path length as the reference may produce results with sufficient accuracy.
For a thin film sample, the coated substrate is measured against a blank substrate made of same material with same thickness and surface smoothness, either side by side, or sequentially, to correct absorption and reflection at interfaces. Because the coating may have a different refractive index than the substrate and air, the reflection off the front face of the film and the substrate may be slightly different, often resulting in higher than 100% transmittance based on the algorithm used by the spectrophotometer. The effect can be corrected but the step is complicated and the error is usually small. For convenience, the transmittance data shown in this disclosure are as measured without correction.
Light that is neither transmitted nor scattered nor reflected is absorbed. The absorbance can be calculated by subtracting the transmitted, scattered, and reflected light from the incident light.
The optical transmittance at 650 nm of the presently disclosed dispersion with 50% PGMEA by weight of the total dispersion as solvent, when measured in a cuvette with 1 cm path length using a Perkin Elmer Lambda 850 spectrophotometer, may be 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
The capped nanocrystals of the present disclosure have a narrow size distribution, with an average size range of 3-8 nm, measured with Transmission Electron Microscopy (TEM).
The capped nanocrystals of the present disclosure are, for example, mono-dispersible, with an average size range of 5-10 nm, measured with Dynamic Light Scattering (DLS) when dispersed in a solvent, such as PGMEA, at a concentration less than or equal to 5% by weight. The DLS measures the particle size together with the solvent shell surrounding the nanocrystal. The capped nanocrystals of present disclosure maintain dispersibility or remain agglomeration-free in an organic or polymer or monomer matrix. Such physical characteristics of the presently disclosed materials not only reduce light scattering but also make for an exceptional processability.
The presently disclosed dispersion may be stable for more than 1 week, or more than 2 weeks, or more than 3 weeks, or more than 6 weeks, or more than 8 weeks, 3 months, or more than 6 months, or more than 12 months, or more than 36 months, with no visible precipitation and less than 10% increase in transmittance, or less than 20% increase in transmittance, or 30% increase in transmittance, 40% increase in transmittance, or less than 50% increase in transmittance at 450 nm.
The presently disclosed dispersion may be analyzed using a TA instrument Q500 thermal gravimetric analyzer (TGA) to determine the inorganic solid content. The procedure for the analysis of the presently disclosed formulation include: 1.) Turn on data storage, 2.) Isothermal at room temperature for 5 minutes, 3.) Set temperature to 80° C., 4.) equilibrate at 80° C., 5.) Ramp 10 C/min to 198° C., 6.) Isothermal for 5 min at 198° C., 7.) Ramp 10° C./min to 800° C., 8.) Ramp 40° C./min to 950° C., 9.) Isothermal for 5 min at 950° C., 10.) Turn off data storage. The percent mass at 200° C. relative to the initial mass is regarded as capped nanocrystals and the percent mass at 700° C. relative to the initial mass is regarded as inorganic portion of the capped nanocrystal, i.e. inorganic solid content. The organic content is defined as the difference between the percent mass at 200° C. and at 700° C. divided by percent mass at 200° C., i.e. (M200C−M700C)/M200C.
The organic content of the presently disclosed dispersion may range from 10%-20% as measured by TGA.
Description of the Formulation
The present disclosure provides a formulation comprising a mixture of capped nanocrystals, optionally a solvent, a monomer, oligomer, or polymer, a curing agent, and optionally an anti-oxidant.
The presently disclosed formulation may comprise nanocrystals of metal oxides, such as zirconium oxide, titanium oxide, hafnium oxide, or zinc oxide, which high bulk refractive indexes, typically larger than 2 in the visible spectrum, as well as exceptional transparency.
By combining the organic coating materials of the present disclosure with metal oxide nanocrystals as described herein, the presently described materials make it possible to produce easily processable unique flexible and thin film coatings with a high refractive index and high optical transparency.
The capping agent of capped nanocrystals in the presently disclosed formulation may include 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, benzoic acid, or any combination thereof.
The solvent of presently disclosed formulation may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The solvent of the presently disclosed formulation may constitute less than 10% by weight of the total formulation, or 10%-20% by weight of the total formulation, or 20%-30% by weight of the total formulation, or 30%-40% by weight of the total formulation, or 40%-50% by weight of the total formulation, or 50%-60% by weight of the total formulation, or 60%-70% by weight of the total formulation, or 70%-80% by weight of the total formulation, or 80%-90% by weight of the total formulation.
The presently disclosed formulation may be analyzed using a TA instrument Q500 thermal gravimetric analyzer (TGA) to determine the inorganic solid content. The procedure is the same as described previously. The percent mass at 200° C. relative to the initial mass is regarded as total formulation weight minus solvent content, and the percent mass at 700° C. relative to the initial mass is regarded as inorganic portion of the formulation, i.e. solid content.
The inorganic solid content of the presently disclosed formulation may be 0-10% as measured by TGA, or 10-20% as measured by TGA, or 20-30% as measured by TGA, or 30-40% as measured by TGA, or 40-50% as measured by TGA, or 50-60% as measured by TGA, or 60-70% as measured by TGA, or 70-80% as measured by TGA, or 80-90% as measured by TGA, or 90-93% as measured by TGA.
The monomer, oligomer, or polymer of presently disclosed formulation may include acrylics. The monomer, oligomer, or polymer of presently disclosed formulation may include bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof.
The capped nanocrystals of the presently disclosed formulation may constitute less than 10% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 10%-20% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 20%-30% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 30%-40% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 40%-50% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 50%-60% by weight of the monomer, oligomer, or polymer, or 60%-70% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 70%-80% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 80%-90% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals, or 90%-93% by weight of the monomer, oligomer, or polymer plus at least partially capped nanocrystals.
The curing agent of presently disclosed formulation may comprise Ebecryl® P39, Ebecryl® P115, benzophenone, SpeedCure BEM, diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide, or Irgacure® 184, or any combination thereof.
The curing agent of presently disclosed formulation may include thermal curing agent such as azobisisobutyronitrile (AIBN).
The amount of curing agent of presently disclosed formulation may be less than 0.5% by weight of the monomer, oligomer, or polymer, or 0.5%-1% by weight of the monomer, oligomer, or polymer, or 1%-2% by weight of the monomer, oligomer, or polymer, or 2%-3% by weight of the monomer, oligomer, or polymer, or 3%-4% by weight of the monomer, oligomer, or polymer, or 4%-5% by weight of the monomer, oligomer, or polymer, or 5%-6% by weight of the monomer, oligomer, or polymer, or 6%-7% by weight of the monomer, oligomer, or polymer, or 7%-8% by weight of the monomer, oligomer, or polymer, or 8%-15% by weight of the monomer, oligomer, or polymer.
The anti-oxidant agent of the presently disclosed formulation may include Solsperse® 36000, Solsperse® 41000, SongNox® 1076, SongNox® 1680, SongNox® 2450, or SongLight® 6220.
The amount of anti-oxidant of presently disclosed formulation may be less than 0.5% by weight of the total formulation, or 0.5%-1% by weight of the total formulation, or 1%-2% by weight of the total formulation, or 2%-3% by weight of the total formulation, or 3%-4% by weight of the total formulation, or 4%-5% by weight of the total formulation, or 5%-6% by weight of the total formulation, or 6%-7% by weight of the total formulation, or 7%-8% by weight of the total formulation.
The presently disclosed formulation may further comprise, plasticizer, toughener, thickener, thinner, dispersant, or flexibilizer, or other functional additives.
The viscosity of the presently disclosed formulation may be less than 5 cPs, or 5 cPs-50 cPs, or 50 cPs-200 cPs, or 200 cPs-400 cPs, or 400 cPs-650 cPs, or 650 cPs-1000 cPs, when measured with a Brookfield RVDV II+ cone and plate viscometer.
The optical transmittance at 650 nm of the presently disclosed formulation with 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length using a Perkin Elmer Lambda 850 spectrophotometer, may be 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
Describing a Film or Coating
The present disclosure provides a nanocomposite coating or film comprising a mixture of a polymer matrix, a curing agent, and capped nanocrystals wherein said capped nanocrystals are present in the coating or film in an amount of greater than 50% by weight of the coating and film.
The presently disclosed nanocomposite coating or film may comprise nanocrystals of metal oxides, such as zirconium oxide, titanium oxide, hafnium oxide, or zinc oxide.
The capping agent of capped nanocrystals in the presently disclosed nanocomposite coating or film may include 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, benzoic acid, or any combination thereof.
The inorganic solid content of the presently disclosed nanocomposite coating or film may be analyzed using a TA instrument Q500 thermal gravimetric analyzer (TGA).
The procedure is the same as described previously. The percent at 700° C. relative to the initial mass is regarded as inorganic portion of the formulation, i.e. solid content.
The inorganic solid content of the presently disclosed nanocomposite coating may be 0-10% as measured by TGA, or 10-20% as measured by TGA, or 20-30% as measured by TGA, or 30-40% as measured by TGA, or 40-50% as measured by TGA, or 50-60% as measured by TGA, or 60-70% as measured by TGA, or 70-80% as measured by TGA, or 80-90% as measured by TGA, or 90-93% as measured by TGA.
The monomer units of the polymer matrix of the presently disclosed nanocomposite coating or film may include acrylics. The monomer units of the polymer matrix of the presently disclosed nanocomposite coating or film may include bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof.
The capped nanocrystals of the presently disclosed nanocomposite coating or film may constitute 10%-20%, or 20%-30%, or 30%-40%, or 40%-50%, or 50%-60%, or 60%-70%, or 70%-75%, or 75%-80%, or 80%-85%, or 85%-90%, or 90%-93% by weight of the coating and film.
The curing agent of presently disclosed nanocomposite coating or film may comprise photoinitiator such as Ebecryl® P39, Ebecryl® P115, benzophenone, SpeedCure BEM, diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide, or Irgacure® 184, or any combination thereof.
The curing agent of presently disclosed nanocomposite coating or film may include thermal curing agent such as azobisisobutyronitrile (AIBN).
The amount of curing agent of presently disclosed nanocomposite coating or film may be less than 0.5% by weight of the polymer matrix, or 0.5%-1% by weight of the polymer matrix, or 1%-2% by weight of the polymer matrix, or 2%-3% by weight of the polymer matrix, or 3%-4% by weight of the polymer matrix, or 4%-5% by weight of the polymer matrix, or 5%-6% by weight of the polymer matrix, or 6%-7% by weight of the polymer matrix, or 7%-8% by weight of the polymer matrix, or 8%-10% by weight of the or polymer matrix, or 10%-15% by weight of the or polymer matrix.
The anti-oxidant agent of the presently disclosed nanocomposite coating or film may include Solsperse® 36000, Solsperse® 41000, SongNox® 1076, SongNox® 1680, SongNox® 2450, or SongLight® 6220.
The amount of anti-oxidant of presently disclosed nanocomposite coating or film may be less than 0.5% by weight of the total formulation, or 0.5%-1% by weight of the total formulation, or 1%-2% by weight of the total formulation, or 2%-3% by weight of the total formulation, or 3%-4% by weight of the total formulation, or 4%-5% by weight of the total formulation, or 5%-6% by weight of the total formulation, or 6%-7% by weight of the total formulation, or 7%-8% by weight of the total formulation, or 8%-10% by weight of the total formulation.
The presently disclosed nanocomposite coating or film may further comprise, plasticizer, toughener, thickener, thinner, dispersant, or flexibilizer, or other functional additives.
The presently disclosed nanocomposite coating or film may possess a refractive index of 1.6-1.62, or 1.62-1.64, 1.64-1.66, or 1.66-1.68, or 1.68-1.70, or 1.70-1.72, or 1.72-1.74, or 1.76-1.78, or 1.78-1.80, or 1.80-1.82, or 1.82-1.84, or 1.84-1.86, or 1.86-1.88, or 1.88-1.90 at 400 nm.
The presently disclosed nanocomposite coating or film may possess an Abbe number in the range of 30 to 41.
The presently disclosed nanocomposite coating or film may additionally demonstrate thermal stability at temperatures above 120° C., or above 175° C., or above 200° C., or above 250° C., or above 260° C., or above 300° C. The thermal stability may be measured by subjecting the nanocomposite coating or film at designated temperature in air, nitrogen, or under vacuum for 5 minutes or longer, or 10 minute or longer, or 30 minutes or longer, or 60 minutes or longer, or 120 minutes or longer, without out visually observable coloration, cracking, or delamination.
The thermal stability may be measured by subjecting the coating or film of at 150° C. in air for 60 minutes, the averaged change of optical transmittance from 400 nm to 800 nm is 5%-10%, or 2%-5% or 1%-2%, or 0.1%-1% or 0.001%-0.1%, when normalized to a 1 μm film. The normalization may be carried out by converting the transmittance to absorbance, dividing the absorbance by the film thickness in micrometer, and then converting the result back to transmittance for a 1 μm film.
The thermal stability may also be measured by subjecting the coating or film at 200° C. in air, vacuum, or nitrogen for 60 minutes, the averaged change of optical transmittance from 400 nm to 800 nm is 5%-10%, or 2%-5% or 1%-2%, or 0.1%-1% or 0.001%-0.1%, when normalized to a 1 μm film.
The thermal stability may also be measured by subjecting the coating or film at 250° C. in air, vacuum or nitrogen for 60 minutes, the averaged change of optical transmittance from 400 nm to 800 nm is 5%-10%, or 2%-5% or 1%-2%, or 0.1%-1% or 0.001%-0.1%, when normalized to a 1 μm film.
The presently disclosed nanocomposite coating or film may additionally demonstrate pencil hardness 3H or higher, or 4H or higher, or 5H or higher, or 6H or higher.
The presently disclosed nanocomposite coating or film may possess high optical (440-800 nm) transmittance of 99.9%-99%, or 99%-98%, or 98%-97%, or 97%-96%, or 96%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10% for films that are less than 5 microns thick. The transmittance of a film according to the present disclosure may be normal transmittance measured with a Perkin-Elmer UV-Vis Lambda 850 spectrophotometer, wherein the film is coated on an optically transparent substrate, such as fused silica or glass substrates, and a blank substrate of the same type and thickness is used as a reference.
The presently disclosed nanocomposite coating or film may be resistant to processing chemicals, for examples, hydrochloric acid, KOH, de-ionized water (DI water), acetone, isopropanol, N-methyl-2-pyrrolidone, etc. The chemical resistance may be measured in one of the two procedures.
In the first procedure (Procedure 1), a substrate coated with the presently disclosed nanocomposite coating or film is submerged in the chemical being tested, in a sonication bath, for 1 minutes, 5 minutes, 30 minutes, or 60 minutes, and then rinsed with DI water and dried in air.
The second procedure (Procedure 2), a few drops of the chemical being tested is placed on top of a substrate coated with the presently disclosed nanocomposite coating or film, and wait for 1 minutes, 5 minutes, 30 minutes, or 60 minutes, and then the substrate is rinsed with DI water and dried in air.
The excellent chemical resistance is defined as after either the first procedure or the second procedure, there is no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity, of the coating or film.
The chemical resistance can also be characterized by measuring the weight change of the film. This can be achieved by any suitable method such as quartz crystal microbalance.
Acid resistance was determined herein in solutions of 1:1 HCl and 1:3 HCl; and base resistance was determined herein in a solution of 5 wt % KOH solution. Chemical resistance was also determined in acetone, isopropanol, and N-methyl-2-pyrrolidone.
Films and coatings of the present disclosure demonstrate no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity, after chemical resistance treatment as described herein.
Alternatively, the films and coating described herein demonstrate less than 5% weight change after chemical resistance testing, such as is described in Procedure 1 above. Alternatively, the films and coating described herein demonstrate weight change in range of 4-5% or 3-4% or 2-3% or 1-2% or 0-1% after chemical resistance testing, such as is described in Procedure 1 above.
A Method of Making a Film
The present disclosure provides a method of making the presently disclosed nanocomposite coating or film using the presently disclosed formulation.
The presently disclosed method of making a nanocomposite coating or film may comprise spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, and any combination thereof.
The film thickness of presently disclosed method of making a nanocomposite coating or film may range from 50 nanometers to 100 micrometers.
The film of presently disclosed method of making a nanocomposite coating or film may possess a root mean square (RMS) surface roughness of 3 nm-10 nm, or 2 nm-3 nm, or 1 nm-2 nm, or 0.6 nm-1 nm, or 0.1 nm-0.6 nm. The RMS surface roughness may be measured using an Atomic Force Microscopy (AFM) over a 5 micron by 5 micron square.
An OLED Device
The present disclosure provides an OLED lighting device comprising an internal light extraction layer, said internal light extraction layer comprising a high refractive index nanocomposite coating or film of the present disclosure.
The present disclosure further provides an active component comprising or containing an LED, organic LED, touch screen, display, sensor, or a solar cell, said active component, comprising or containing a coating or a film or a layer of the present disclosure.
Table 1: Exemplary experimental “spin curve” of film thickness and standard deviation produced with the formulation described in EXAMPLE 3 by the different spin speed and different solid content.
The present disclosure provides the following additional embodiments.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, and wherein the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a composition containing a dispersion of at least partially capped metal oxide nanocrystals and a solvent, wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water, and the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides, and the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyltrimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, and wherein the at least partially capped metal oxide nanocrystals are present in the composition in an amount of less than 10% by weight of the composition, or 10%-20% by weight of the composition, or 20%-30% by weight of the composition, or 30%-40% by weight of the composition, or 40%-50% by weight of the composition, or 50%-60% by weight of the composition, or 60%-70% by weight of the composition, or 70%-80% by weight of the composition, or 80%-90% by weight of the composition, or 90%-95% by weight of the composition, and wherein the solvent is PGMEA, PGME, toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone or mixtures thereof.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The at least partially capped metal oxide nanocrystals are present in formulations of the present disclosure in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
Formulations of the present disclosure alternatively have an optical transmittance at 650 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
Formulations of the present disclosure alternatively have an optical transmittance at 450 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
Formulations of the present disclosure may have a viscosity of less than 5 cPs, or 5 cPs-50 cPs, or 50 cPs-200 cPs, or 200 cPs-400 cPs, or 400 cPs-650 cPs, or 650 cPs-1000 cPs, when measured at 25° C. with a Brookfield RVDV II+cone and plate viscometer.
Formulations of the present disclosure include the at least partially capped metal oxide nanocrystals in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein wherein the at least partially capped metal oxide nanocrystals are present in formulations of the present disclosure in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein wherein the formulation alternatively has an optical transmittance at 650 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein wherein the formulation alternatively has an optical transmittance at 450 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein wherein the formulation has a viscosity of less than 5 cPs, or 5 cPs-50 cPs, or 50 cPs-200 cPs, or 200 cPs-400 cPs, or 400 cPs-650 cPs, or 650 cPs-1000 cPs, when measured at 25° C. with a Brookfield RVDV II+cone and plate viscometer.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation includes the at least partially capped metal oxide nanocrystals in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing bisphenol A glycerolate dimethacrylate, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA), wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation as described herein.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation containing a binder formulation and further containing scattering particles wherein the binder formulation contains a formulation containing a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer containing a monomer, oligomer, or polymer of bisphenol A glycerolate dimethacrylate, biphenyl-2-ol, ethoxylated, esters with acrylic acid (OPPEOA), bisphenol A ethoxylate diacrylates, bisphenol A propoxylate diacrylate, bisphenol F ethoxylate (2 EO/phenol) diacrylate, bisphenol A glycerolate diacrylates, bisphenol A ethoxylate dimethacrylate, benzyl methacrylate (BMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxylate (1 EO/OH) methyl ether diacrylate, 1,6-hexanediol diacrylate, tri(ethyleneglycol) diacrylate, ethylene glycol diacrylate, poly(ethylene glycol) diacrylate, glycerol 1,3-diglycerolate diacrylate, di(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, 1,6-hexanediol ethoxylate diacrylate, ethylene glycol phenyl ether acrylate, or any combination thereof, optionally further containing a solvent, a curing agent, an antioxidant, crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer, wherein the at least partially capped metal oxide nanocrystals are at least partially capped in the presence of water, wherein the metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of the oxides, wherein the at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid, wherein the at least partially capped metal oxide nanocrystals are present in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 10%-20% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 20%-30% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 30%-40% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 40%-50% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 50%-60% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 60%-70% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 70%-80% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 80%-90% by weight of the acrylic and at least partially capped nanocrystals, or in an amount of 90%-93% by weight of the acrylic and at least partially capped nanocrystals.
The present disclosure provides a scattering formulation as described herein wherein the average size of the scattering particles is in the range of 50 nm-2 μm, or 50-100 nm, or 100-200 nm, or 200-300 nm, or 300-400 nm, or 400-500 nm, or 500-600 nm, or 600-700 nm, or 700-800 nm, or 800-900 nm or 900 nm to 1 μm, or 1-1.5 μm, or 1.5-2 μm.
The present disclosure provides a scattering formulation as described herein wherein the scattering particles are present in an amount of 0.1-40% by weight of the total weight of the formulation.
The present disclosure provides a scattering formulation as described herein wherein scattering particles have a higher refractive index than the refractive index of the binder formulation.
The present disclosure provides a scattering formulation as described herein wherein scattering particles have a lower refractive index than the refractive index of the binder formulation.
The present disclosure provides a scattering formulation as described herein wherein the scattering particles are selected from a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide, cerium oxide or mixtures of any two of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide and cerium oxide.
The present disclosure provides a scattering formulation as described herein wherein the scattering formulation is storage stable for at least 1 week, or 2 weeks, or 3 weeks, or 4 weeks, or 3 months, or at least 5 months, or at least 6 months, or at least 7 months, or at least 8 months, or at least 9 months, or at least 10 months, or at least 11 months, or at least 1 year, or at least 2 years or at least 3 years, when the scattering formulation is stored at a temperature in the range of 18-25° C. without deliberate shaking or mixing of the scattering formulation.
The present disclosure provides a scattering formulation as described herein wherein the scattering formulation is storage stable and the weight percentage of scattering particles in a sample from the upper third of a stored sample of the scattering formulation changes by less than 1%, or 1-2%, or 2-3%, or 3-4%, or 4-5%, or 5-7%, or 7-10%, or 10-15%, or 15-20%, or 20-25%, or 25-30%, or 30-35% over the storage time.
A nanocomposite film is described herein containing a cured or partially cured formulation of the present disclosure. A nanocomposite film of the present disclosure may have a refractive index of between 1.6-1.62, or 1.62-1.64, 1.64-1.66, or 1.66-1.68, or 1.68-1.70, or 1.70-1.72, or 1.72-1.74, or 1.76-1.78, or 1.78-1.80, or 1.80-1.82, or 1.82-1.84, or 1.84-1.86, or 1.86-1.88, or 1.88-1.90 when measured at 400 nm. A nanocomposite film of the present disclosure may have a normal transmittance of 99.99%-99%, or 99%-98%, or 98%-97%, or 97%-96%, or 96%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10% for films that are 4.9-5 microns thick, when measured at a wavelength of 450 nm or 650 nm.
The present disclosure provides a nanocomposite film wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane, and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment, wherein the chemical treatment may involve treatment with an acid, a base, an organic compound or water; wherein the chemical treatment resistance may be determined by visual inspection after submerging the film in the chemical for at least 5 minutes or for at least 10 minutes, or for at least 15 minutes, or for at least 20 minutes, or for at least 30 minutes, or for at least 45 minutes, or for at least 60 minutes, or for at least 90 minutes, or for at least 120 minutes, or for at least 150 minutes, or for at least 180 minutes water rinse and air drying.
The present disclosure provides a nanocomposite film wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane, and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment, wherein the chemical treatment may involve treatment with an acid, a base, an organic compound or water; wherein the chemical treatment resistance may be determined by weight change after submerging the film in the chemical for at least 5 minutes or for at least 10 minutes, or for at least 15 minutes, or for at least 20 minutes, or for at least 30 minutes, or for at least 45 minutes, or for at least 60 minutes, or for at least 90 minutes, or for at least 120 minutes, or for at least 150 minutes, or for at least 180 minutes water rinse and air drying. The weight change may be less than 0.1%, 0.1-1%, or 1-2%, or 2-3%, or 3-4%, 4-5%, or 5-6%, or 6-7%, or 7-8%, or 8-9%, 9-10%, or 10-11%, 11-12%, or 12-15%, or 15-20%, or 25-30%.
The present disclosure provides a nanocomposite film as described herein wherein the film has an averaged change of optical transmittance from 400 nm to 800 nm is 5%-10%, or 2%-5% or 1%-2%, or 0.1%-1% or 0.001%-0.1% after the film has been maintained at a temperature of 150 C or 200 C or 250 C for 60 minutes in air or vacuum or nitrogen.
The present disclosure provides a nanocomposite film as described herein wherein a film of at least 1 μm has a surface roughness of 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm.
The present disclosure provides a nanocomposite film as described herein wherein the Abbe number is in the range of 20 to 60 or 30 to 41.
The present disclosure provides a nanocomposite film as described herein wherein the at least partially capped nanocrystals have an average size of less than 20 nm.
The present disclosure provides a nanocomposite film as described herein wherein the amount of the at least partially capped nanocrystals in the film is 10%-20%, or 20%-30%, or 30%-40%, or 40%-50%, or 50%-60%, or 60%-70%, or 70%-75%, or 75%-80%, or 80%-85%, or 85%-90%, or 90%-93% by weight of the nanocomposite film.
The present disclosure provides a nanocomposite film as described herein wherein the film is produced by spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, or any combination thereof.
The present disclosure provides a scattering film containing a cured or partially cured scattering formulation of as described herein wherein the cured or partially cured binder formulation forms a nanocomposite binder.
The present disclosure provides a scattering film as described herein wherein the nanocomposite binder has a refractive index of between 1.6-1.62, or 1.62-1.64, 1.64-1.66, or 1.66-1.68, or 1.68-1.70, or 1.70-1.72, or 1.72-1.74, or 1.76-1.78, or 1.78-1.80, or 1.80-1.82, or 1.82-1.84, or 1.84-1.86, or 1.86-1.88, or 1.88-1.90 when measured at 400 nm.
The present disclosure provides a scattering film as described herein wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment; wherein the chemical treatment may involve treatment with an acid, a base, an organic compound or water; wherein chemical treatment resistance may be determined by visual inspection after submerging the film in the chemical for at least 5 minutes or for at least 10 minutes, or for at least 15 minutes, or for at least 20 minutes, or for at least 30 minutes, or for at least 45 minutes, or for at least 60 minutes, or for at least 90 minutes, or for at least 120 minutes, or for at least 150 minutes, or for at least 180 minutes, water rinse and air drying.
The present disclosure provides a scattering film as described herein wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment; wherein the chemical treatment may involve treatment with an acid, a base, an organic compound or water; wherein chemical treatment resistance may be determined by weight change after submerging the film in the chemical for at least 5 minutes or for at least 10 minutes, or for at least 15 minutes, or for at least 20 minutes, or for at least 30 minutes, or for at least 45 minutes, or for at least 60 minutes, or for at least 90 minutes, or for at least 120 minutes, or for at least 150 minutes, or for at least 180 minutes, water rinse and air drying. The weight change may be less than 0.1%, 0.1-1%, or 1-2%, or 2-3%, or 3-4%, 4-5%, or 5-6%, or 6-7%, or 7-8%, or 8-9%, 9-10%, or 10-11%, 11-12%, or 12-15%, or 15-20%, or 25-30%.
The present disclosure provides a scattering film as described herein wherein a film of at least 1 μm has a surface roughness of 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm.
The present disclosure provides a scattering film as described herein wherein the at least partially capped nanocrystals of the nanocomposite binder have an average size of less than 20 nm.
The present disclosure provides a scattering film as described herein wherein the amount of the at least partially capped nanocrystals in the scattering film is 10%-20%, or 20%-30%, or 30%-40%, or 40%-50%, or 50%-60%, or 60%-70%, or 70%-75%, or 75%-80%, or 80%-85%, or 85%-90%, or 90%-93% by weight of the nanocomposite binder.
The present disclosure provides a scattering film as described herein wherein the film is produced by spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, or any combination thereof.
The present disclosure provides a method of making at least partially capped nanocrystals involving mixing nanocrystals in a capping solvent with at least one capping agent in the presence of water; wherein the at least partially capped nanocrystals may be separated from the capping solvent; wherein the nanocrystals may be zirconia nanocrystals; wherein the capping agent may be at least one of methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane; wherein the capping solvent may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The present disclosure provides a formulation as described herein wherein the at least partially capped nanocrystals are made by a process involving mixing nanocrystals in a capping solvent with at least one capping agent in the presence of water; wherein the at least partially capped nanocrystals may be separated from the capping solvent; wherein the nanocrystals may be zirconia nanocrystals; wherein the capping agent may be at least one of methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane; wherein the capping solvent may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The present disclosure provides scattering formulation as described herein wherein the at least partially capped nanocrystals of the binder formulation are made by a process involving mixing nanocrystals in a capping solvent with at least one capping agent in the presence of water; wherein the at least partially capped nanocrystals may be separated from the capping solvent; wherein the nanocrystals may be zirconia nanocrystals; wherein the capping agent may be at least one of methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane; wherein the capping solvent may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The present disclosure provides a nanocomposite film as described herein wherein the at least partially capped nanocrystals are made by a process involving mixing nanocrystals in a capping solvent with at least one capping agent in the presence of water; wherein the at least partially capped nanocrystals may be separated from the capping solvent; wherein the nanocrystals may be zirconia nanocrystals; wherein the capping agent may be at least one of methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane; wherein the capping solvent may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The present disclosure provides a scattering film as described herein wherein the at least partially capped nanocrystals of the binder formulation are made by a process involving mixing nanocrystals in a capping solvent with at least one capping agent in the presence of water; wherein the at least partially capped nanocrystals may be separated from the capping solvent; wherein the nanocrystals may be zirconia nanocrystals; wherein the capping agent may be at least one of methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane; wherein the capping solvent may include propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), toluene, ethyl acetate, xylene, THF, heptane, hexane, acetone, or any combination thereof.
The present disclosure provides an OLED device containing a nanocomposite film as described herein.
The present disclosure provides an OLED device containing a scattering film as described herein.
The present disclosure provides the following further non-limiting numbered embodiments as further examples of the disclosed technology:
1. A scattering formulation comprising scattering particles and a binder formulation, said binder formulation comprising a dispersion of at least partially capped metal oxide nanocrystals and a monomer, oligomer and/or polymer.
2. The scattering formulation of embodiment 1 wherein the D50, as measured by a number distribution, of said scattering particles is in the range of 50 nm-2 μm, or 50-100 nm, or 100-200 nm, or 200-300 nm, or 300-400 nm, or 400-500 nm, or 500-600 nm, or 600-700 nm, or 700-800 nm, or 800-900 nm or 900 nm to 1 μm, or 1-1.5 μm, or 1.5-2 μm.
3. The scattering formulation of embodiment 1 wherein the D50, as measured by a volume distribution, of said scattering particles is in the range of 50 nm-2 μm, or 50-100 nm, or 100-200 nm, or 200-300 nm, or 300-400 nm, or 400-500 nm, or 500-600 nm, or 600-700 nm, or 700-800 nm, or 800-900 nm or 900 nm to 1 μm, or 1-1.5 μm, or 1.5-2 μm.
4. The scattering formulation of embodiment 1 wherein D99, as measured by a number distribution, of said particles have a size less than 3 μm, 2.8 μm, 2.6 μm, 2.5 μm, 2.4 μm, 2.3 μm, 2.1 μm, 2.0 μm, 1.9 μm, 1.8 μm, 1.7 μm, 1.6 μm, 1.5 μm, 1.4 μm, 1.3 μm, 1.2 μm, 1.1 μm, 1.0 μm, 0.9 μm, 0.8 μm, 0.7 μm, 0.6 μm, or 0.5 μm.
5. The scattering formulation of embodiment 1 wherein D99, as measured by a volume distribution, of said particles have a size less than 3 μm, 2.8 μm, 2.6 μm, 2.5 μm, 2.4 μm, 2.3 μm, 2.1 μm, 2.0 μm, 1.9 μm, 1.8 μm, 1.7 μm, 1.6 μm, 1.5 μm, 1.4 μm, 1.3 μm, 1.2 μm, 1.1 μm, 1.0 μm, 0.9 μm, 0.8 μm, 0.7 μm, 0.6 μm, or 0.5 μm.
6. The scattering formulation of embodiment 1 wherein D99.99, as measured by a number distribution, of said particles have a size less than 3 μm, 2.8 μm, 2.6 μm, 2.5 μm, 2.4 μm, 2.3 μm, 2.1 μm, 2.0 μm, 1.9 μm, 1.8 μm, 1.7 μm, 1.6 μm, 1.5 μm, 1.4 μm, 1.3 μm, 1.2 μm, 1.1 μm, 1.0 μm, 0.9 μm, 0.8 μm, 0.7 μm, 0.6 μm, or 0.5 μm.
7. The scattering formulation of embodiment 1 wherein D99.99, as measured by a volume distribution, of said particles have a size less than 3 μm, 2.8 μm, 2.6 μm, 2.5 μm, 2.4 μm, 2.3 μm, 2.1 μm, 2.0 μm, 1.9 μm, 1.8 μm, 1.7 μm, 1.6 μm, 1.5 μm, 1.4 μm, 1.3 μm, 1.2 μm, 1.1 μm, 1.0 μm, 0.9 μm, 0.8 μm, 0.7 μm, 0.6 μm, or 0.5 μm.
8. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1 μm by 1 μm.
9. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5 μm by 5 μm.
10. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10 μm by 10 μm.
11. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 25 μm by 25 μm.
12. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 50 μm by 50 μm.
13. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 100 μm by 100 μm.
14. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 500 μm by 500 μm.
15. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1000 μm by 1000 μm.
16. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5000 μm by 5000 μm.
17. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Ra is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10000 μm by 10000 μm.
18. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1 μm by 1 μm.
19. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5 μm by 5 μm.
20. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10 μm by 10 μm.
21. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 25 μm by 25 μm.
22. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 50 μm by 50 μm.
23. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 100 μm by 100 μm.
24. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 500 μm by 500 μm.
25. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1000 μm by 1000 μm.
26. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5000 μm by 5000 μm.
27. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness Rpv is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10000 μm by 10000 μm.
28. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1 μm by 1 μm.
29. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5 μm by 5 μm.
30. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10 μm by 10 μm.
31. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 25 μm by 25 μm.
32. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 50 μm by 50 μm.
33. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 100 μm by 100 μm.
34. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 500 μm by 500 μm.
35. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 1000 μm by 1000 μm.
36. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 5000 μm by 5000 μm.
37. A film of at least 1 μm made with the scattering formulation of embodiment 1 wherein the surface roughness RMS is less than 1 nm, 3 nm, 5 nm, 7 nm, 10 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 55 nm, 60 nm, 65 nm, 70 nm, 75 nm, 80 nm, 85 nm, 90 nm, 95 nm, 100 nm, 250 nm, and 500 nm over an area of 10000 μm by 10000 μm.
38. The scattering formulation of embodiment 1 wherein the monomer, oligomer and/or polymer comprises at least one of an acrylate, (meth)acrylate, epoxy, epoxy-acrylate, or epoxy-silane monomer, oligomer and/or polymer.
39. The scattering formulation of embodiment 38, said binder formulation further comprising a curing agent.
40. The scattering formulation of embodiment 39 wherein the curing agent is a photo-initiator.
41. The scattering formulation of embodiment 40 wherein the photoinitiator is selected from the group consisting of Ebecryl® P39, Ebecryl® P115, SpeedCure® BEM, benzophenone, diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide, 1-hydroxy-cyclohexyl phenyl ketone (Irgacure® 184), phenylbis(2,4,6-trimethylbenzyoyl)-phoshine oxide (Irgacure® 819), camphoquinone (CQ), 2-dimethylaminoethyl methacrylate (DMAEMA), ethyl 4-(dimethylamino)benzoate (EDAB), diphenyliodonium hexafluorophosphate (DPIHFP), 4-octyloxydiphenyliodoniumhexfluoroantimonate (OPPI).
42. The scattering formulation of embodiment 39 wherein the curing agent is a thermal curing agent such as azobisisobutyronitrile (AIBN).
43. The scattering formulation of embodiment 39 wherein the dispersant include acidic polyester.
44. The scattering formulation of embodiment 1 wherein the scattering particles is selected from the group consisting of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide, cerium oxide, diamond, silicon nitride, or voids.
45. A formulation comprising a dispersion of at least partially capped metal oxide nanocrystals and an acrylic polymer comprising bisphenol A glycerolate dimethacrylate, optionally further comprising a solvent, a curing agent or an antioxidant.
46. The formulation of embodiment 45 wherein the at least partially capped metal oxide nanocrystals are produced in the presence of water.
47. The formulation of embodiment 45 or embodiment 2 wherein said metal oxide nanocrystals are zirconium oxide, titanium oxide, hafnium oxide, zinc oxide or a mixture of at least two of said oxides.
48. The formulation of one of embodiments 45-47 wherein said at least partially capped metal oxide nanocrystals are at least partially capped with at least one capping agent selected from the group consisting of 2-[2-(2-methoxyethoxy) ethoxy]acetic acid, methoxy(triethyleneoxy) propyltrimethoxysilane, 3-(methacryloyloxy)propyl trimethoxysilane, n-octyl trimethoxysilane, dodecyltrimethoxysilane, m,p-ethylphenethyl trimethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane, 2-[methoxy(polyethyleneoxy)propyl]-trimethoxysilane, 3-aminopropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane, and glycidoxypropyltrimethoxysilane, heptanol, hexanol, octanol, benzyl alcohol, phenol, ethanol, propanol, butanol, oleylalcohol, dodecylalcohol, octadecanol and triethylene glycol monomethyl ether, octanoic acid, acetic acid, propionic acid, acetic acid, oleic acid, and benzoic acid.
49. The formulation of one of embodiments 45-48 wherein said dispersion does not contain benzyl methacrylate (BMA) or trimethylolpropane triacrylate (TMPTA).
50. The formulation of any one of embodiments 45-49, further comprising at least one of a solvent, a curing agent or an antioxidant.
51. The formulation of any one of embodiments 45-50, further comprising at least one of a crosslinking agent, a thickener, an adhesion promoter, a plasticizer, or a flexibilizer.
52. The formulation of any one of embodiments 45-51 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals, or 10%-20% by weight of the of the acrylic and at least partially capped nanocrystals, or 20%-30% by weight of the of the acrylic and at least partially capped nanocrystals, or 30%-40% by weight of the of the acrylic and at least partially capped nanocrystals, or 40%-50% by weight of the of the acrylic and at least partially capped nanocrystals, or 50%-60% by weight of the of the acrylic and at least partially capped nanocrystals, or 60%-70% by weight of the of the acrylic and at least partially capped nanocrystals, or 70%-80% by weight of the of the acrylic and at least partially capped nanocrystals, or 80%-90% by weight of the of the acrylic and at least partially capped nanocrystals, or 90%-95% by weight of the of the acrylic and at least partially capped nanocrystals.
53. The formulation of any one of embodiments 45-52 the optical transmittance at 650 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
54. The formulation of any one of embodiments 45-52 the optical transmittance at 450 nm of the formulation in 50% PGMEA by weight of the total formulation as solvent, when measured in a cuvette with 1 cm path length is 99%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10%.
55. The formulation of any one of embodiments 45-53 wherein the viscosity of the dispersion is less than 5 cPs, or 5 cPs-50 cPs, or 50 cPs-200 cPs, or 200 cPs-400 cPs, or 400 cPs-650 cPs, or 650 cPs-1000 cPs, when measured at 25° C. with a Brookfield RVDV II+cone and plate viscometer.
56. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of less than 10% by weight of the acrylic and at least partially capped nanocrystals,
57. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 10%-20% by weight of the of the acrylic and at least partially capped nanocrystals,
58. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 20%-30% by weight of the of the acrylic and at least partially capped nanocrystals,
59. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 30%-40% by weight of the of the acrylic and at least partially capped nanocrystals,
60. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 40%-50% by weight of the of the acrylic and at least partially capped nanocrystals,
61. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 50%-60% by weight of the of the acrylic and at least partially capped nanocrystals, or 60%-70% by weight of the of the acrylic and at least partially capped nanocrystals,
62. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 70%-80% by weight of the of the acrylic and at least partially capped nanocrystals,
63. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 80%-90% by weight of the of the acrylic and at least partially capped nanocrystals,
64. The formulation of embodiment 55 wherein the at least partially capped metal oxide nanocrystals are present in the formulation in an amount of 90%-95% by weight of the of the acrylic and at least partially capped nanocrystals.
65, The formulation of any one of embodiments 45-64 wherein the average diameter of the at least partially capped nanocrystals is less than 20 nm, or in the range of 1-20 nm.
66. A scattering formulation comprising a binder formulation and further comprising scattering particles wherein said binder formulation comprises the formulation of any one of embodiments 45-65.
67. The scattering formulation of embodiment 66 wherein the average size of said scattering particles is in the range of 50 nm-2 μm, or 50-100 nm, or 100-200 nm, or 200-300 nm, or 300-400 nm, or 400-500 nm, or 500-600 nm, or 600-700 nm, or 700-800 nm, or 800-900 nm or 900 nm to 1 μm, or 1-1.5 μm, or 1.5-2 μm.
68. The scattering formulation of embodiment 66 or embodiment 23 wherein said scattering particles are present in an amount of 0.1-40% by weight of the total weight of the formulation.
69. The scattering formulation of any one of embodiments 66-68 wherein scattering particles have a higher refractive index than the refractive index of the binder formulation.
70. The scattering formulation of any one of embodiments 66-68 wherein scattering particles have a lower refractive index than the refractive index of the binder formulation.
71. The scattering formulation of any of embodiments 66-69 wherein the scattering particles are selected from a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide, cerium oxide or mixtures of any two of a polymer, titanium oxide, silicon dioxide, niobium pentoxide, zirconium oxide, zinc oxide, aluminum oxide and cerium oxide.
72. The scattering formulation of any one of embodiments 66-70 wherein the scattering formulation is storage stable for at least 1 week, or 2 weeks, or 3 weeks, or 4 weeks, or 3 months, or at least 5 months, or at least 6 months, or at least 7 months, or at least 8 months, or at least 9 months, or at least 10 months, or at least 11 months, or at least 1 year, or at least 2 years or at least 3 years, when said scattering formulation is stored at a temperature in the range of 18-25° C. without deliberate shaking or mixing of the scattering formulation.
73. The scattering formulation of any one of embodiments 66-71 wherein the scattering formulation is storage stable and the weight percentage of scattering particles in a sample from the upper third of a stored sample of the scattering formulation changes by less than 1%, or 1-2%, or 2-3%, or 3-4%, or 4-5%, or 5-7%, or 7-10%, or 10-15%, or 15-20%, or 20-25%, or 25-30%, or 30-35% over the storage time.
74. A nanocomposite film comprising a cured or partially cured formulation of any one of embodiments 45-65.
75. The nanocomposite film of embodiment 73 wherein said film has a refractive index of between 1.6-1.62, or 1.62-1.64, 1.64-1.66, or 1.66-1.68, or 1.68-1.70, or 1.70-1.72, or 1.72-1.74, or 1.76-1.78, or 1.78-1.80, or 1.80-1.82, or 1.82-1.84, or 1.84-1.86, or 1.86-1.88, or 1.88-1.90 when measured at 400 nm.
76. The nanocomposite film of embodiments 73 or embodiment 30 wherein said film has a normal transmittance of 99.99%-99%, or 99%-98%, or 98%-97%, or 97%-96%, or 96%-95%, or 95%-90%, or 90%-85%, or 85%-80%, 80%-75%, or 75%-70%, or 70%-65%, or 65%-60%, or 60%-55%, or 55%-50%, or 50%-45%, or 45%-40%, or 40%-35%, or 35%-30%, or 30%-25%, or 25%-20%, or 20%-15%, or 15%-10% for films that are 4.9-5 microns thick, when measured at a wavelength of 450 nm or 650 nm.
77. The nanocomposite film of any one of embodiments 73-75 wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane, and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment.
78. The nanocomposite film of embodiment 76 wherein the chemical treatment comprises treatment with an acid, a base, an organic compound or water.
79. The nanocomposite film of embodiment 77 wherein chemical treatment resistance is determined by visual inspection after submerging the film in said chemical for at least 5 minutes, water rinse and air drying.
80. The nanocomposite film of any one of embodiments 73-78 wherein the film has an averaged change of optical transmittance from 400 nm to 800 nm is 5%-10%, or 2%-5% or 1%-2%, or 0.1%-1% or 0.001%-0.1% after the film has been maintained at a temperature of 150 C or 200 C or 250 C for 60 minutes in air or vacuum or nitrogen.
81. The nanocomposite film of any one embodiments 73-79 wherein a film of at least 1 μm has a surface roughness of 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm.
82. The nanocomposite film of any one of embodiments 73-80 wherein the Abbe number is in the range of 20 to 60 or 30 to 41.
83. The nanocomposite film of any one of embodiments 73-81 wherein the at least partially capped nanocrystals have an average size of less than 20 nm.
84. The nanocomposite film of any one of embodiments 73-82 wherein the amount of the at least partially capped nanocrystals in the film is 10%-20%, or 20%-30%, or 30%-40%, or 40%-50%, or 50%-60%, or 60%-70%, or 70%-75%, or 75%-80%, or 80%-85%, or 85%-90%, or 90%-93% by weight of the nanocomposite film.
85. The nanocomposite film of any one of embodiments 73-83 wherein the film is produced by spin coating, slot-die coating, slit-coating, screen-printing, ink-jet printing, dip coating, draw-bar coating, roll-to-roll printing, spray coating, or any combination thereof.
86. A scattering film comprising a cured or partially cured scattering formulation of any one of embodiments 66-72, wherein said cured or partially cured binder formulation forms a nanocomposite binder.
87. The scattering film of embodiment 85 wherein said nanocomposite binder has a refractive index of between 1.6-1.62, or 1.62-1.64, 1.64-1.66, or 1.66-1.68, or 1.68-1.70, or 1.70-1.72, or 1.72-1.74, or 1.76-1.78, or 1.78-1.80, or 1.80-1.82, or 1.82-1.84, or 1.84-1.86, or 1.86-1.88, or 1.88-1.90 when measured at 400 nm.
88. The scattering film of embodiment 85 or embodiment 86 wherein the at least partially capped nanocrystals are capped with methoxy(triethyleneoxy) propyltrimethoxysilane and 3-(methacryloyloxy)propyl trimethoxysilane, and wherein the film is resistant to chemical treatment.
89. The scattering film of embodiment 87 wherein the chemical treatment comprises treatment with an acid, a base, an organic compound or water.
90. The scattering film of embodiment 88 wherein chemical treatment resistance is determined by visual inspection after submerging the film in said chemical for at least 5 minutes, water rinse and air drying.
91. The scattering film of any one embodiments 85-89 wherein a film of at least 1 μm has a surface roughness of 5-4 nm, or 4-3 nm, or 3-2 nm, or 2-1 nm, or 1-0.5 nm, or 0.5-0.1 nm.
The following are non-limiting exemplifications of embodiments of the disclosure.
The capping of zirconia nanocrystals with two different capping agents, methoxy(triethyleneoxy) propyltrimethoxysilane and 3-methacryloyloxypropyltrimethoxylsilane, is performed by suspending the as-synthesized nanocrystals in the solvent of choice, for example, PGMEA for methoxy(triethyleneoxy) propyltrimethoxysilane modification, at a loading of 10% by weight or greater, calculated based on the wet cake weight of the nanocrystals. While the suspension is being stirred, the first capping agent, methoxy(triethyleneoxy) propyltrimethoxysilane, is added slowly to the suspension. The amount of capping agent used is 1-8% by weight to the wet cake. The suspension is refluxed at the boiling point of the solvent for 30-50 minutes under nitrogen flow. After the set reaction time, the reaction is stopped and the suspension is cooled slowly to 70-100° C. Upon reaching said temperature, the second capping agent, 3-methacryloyloxypropyltrimethoxylsilane, is added slowly to the suspension. The amount of the capping agent used is 30-60% by weight to the wet cake. The suspension is again refluxed at the boiling point of the solvent for 30-50 minutes under nitrogen flow. After the second reflux step, the suspension is slowly cooled to 50-70° C. Upon reaching said temperature, distilled water is added to the suspension slowly. The amount of water used is 1-5 wt % to the wet cake. The suspension is refluxed at 70-100° C. for 30-50 minutes under nitrogen flow. Upon the completion of the allotted heating time, the clear solution is cooled slowly to room temperature. The capped nanocrystals are precipitated out of the capping solvent using heptane. The precipitated nanocrystals are collected using centrifugation. The nanocrystals collected by centrifugation are further cleaned by dispersing it in THF and again re-precipitated out using heptane. The process is repeated twice. The wet cake obtained after the final step is dried under vacuum for 10-12 hours. The capped nanocrystals can then be re-dispersed into dispersion solvent such as PGMEA.
b)
b)
The capping of zirconia nanocrystals with two different capping agents, methoxy(triethyleneoxy) propyltrimethoxysilane and 3-methacryloyloxypropyltrimethoxylsilane is performed by suspending the as-synthesized nanocrystals in the solvent of choice, for example, PGMEA for methoxy(triethyleneoxy) propyltrimethoxysilane modification, at a loading of 10% or greater, calculated based on the wet cake weight of the nanocrystals. While the suspension is being stirred, the first capping agent is added slowly to the suspension. The amount of capping agent used is 5-8 wt % to the wet cake. The suspension is refluxed at the boiling point of the solvent for 30-50 minutes under nitrogen flow. After the set reaction time, the reaction is stopped heating and the suspension is cooled slowly to 70-100° C. Upon reaching that temperature, the second capping agent is added slowly to the suspension. The amount of the capping agent used is 30-60 wt % to the wet cake. The suspension is again refluxed at the boiling point of the solvent for 30-50 minutes under nitrogen flow. Upon the completion of the allotted heating time, the clear solution is cooled slowly to room temperature. The capped nanocrystals are precipitated out of the capping solvent using heptane. The precipitated nanocrystals are collected using centrifuge. The nanocrystals collected by centrifuge are further cleaned by dispersing it in THF and again re-precipitating using heptane. The process is repeated twice. The wet cake obtained after the final step is dried under vacuum for 10-12 hours. The capped nanocrystals can then be re-dispersed into dispersion solvent such as PGMEA.
An exemplary formulation comprises PGMEA as solvent, bisphenol A diglycerolate dimethacrylate monomer, capped zirconia nanocrystals (with 90% by weight to the monomer), 3% of EBecryl P-39 by weight to the monomer, 6% of EBecryl P-115 by weight to the monomer.
The zirconia nanocrystals used in this formulation are capped with two different capping agents, methoxy(triethyleneoxy) propyltrimethoxysilane and 3-methacryloyloxypropyltrimethoxylsilane. The capping process is performed by suspending the as-synthesized nanocrystals in PGMEA, at a loading of 35% by weight calculated based on the wet cake weight of the nanocrystals. While the suspension is being stirred, the first capping agent, methoxy(triethyleneoxy) propyltrimethoxysilane, is added slowly to the suspension. The amount of capping agent used is 1% by weight to the wet cake. The suspension is refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow. After the set reaction time, the reaction is stopped and the suspension is cooled slowly to 100° C. Upon reaching said temperature, the second capping agent, 3-methacryloyloxypropyltrimethoxylsilane, is added slowly to the suspension. The amount of the capping agent used is 60% by weight to the wet cake. The suspension is again refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow. After the second reflux step, the suspension is slowly cooled to 70° C. Upon reaching said temperature, distilled water is added to the suspension slowly. The amount of water used is 5 wt % to the wet cake. The suspension is refluxed at 100° C. for 30 minutes under nitrogen flow. Upon the completion of the allotted heating time, the clear solution is cooled slowly to room temperature. The capped nanocrystals are precipitated out of the capping solvent using heptane. The precipitated nanocrystals are collected using centrifugation. The nanocrystals collected by centrifugation are further cleaned by dispersing it in THF and again re-precipitated out using heptane. The process is repeated twice. The wet cake obtained after the final step is dried under vacuum for 10-12 hours. The capped nanocrystals can then be re-dispersed into dispersion solvent such as PGMEA.
The viscosity of the formulation can be adjusted from about 5 cPs to more than 400 cPs by adjusting the PGMEA solvent amount.
Table 1 shows an exemplary experimental “spin curve” of film thickness and standard deviation produced by the different spin speed and different solid content in the formulation. The standard deviation represents the film thickness uniformity across a 2 inch wafer. The spin-coater used here is a Laurell WS-650 Mz. The substrate used is glass. The films are produced with 100° C. pre-bake on a hot plate in air after the films are spin coated, the films are then cured for 120 seconds using a Dymax EC-5000 system with a mercury “H” bulb with ˜73 mW/cm2. Finally the films are subjected to a 10 minutes post bake on a hot plate in air. The film thickness is measured using a Tencor P-2 surface profilometer.
Similarly,
The TGA result of the capped nanocrystals of the current example dispersed in PGEMA by themselves with 50% by weight is shown in
The optical transmittance of the formulation of the current example with 50% of capped nanocrystals by weight is shown in
The refractive index of the film produced with the formulation in this example is obtained by a Woollam M2000 ellipsometer.
The films produced with the formulation in this example demonstrate high optical transmittance. The spectrum 101 in
The films produced with the formulation in this example demonstrate high thermal resistance.
In another thermal resistance study, the solid line in
The films produced with the formulation in this example demonstrate chemical resistance to 1:1 HCl (prepared by mixing 38 wt % hydrochloric acid water solution with water in 1:1 volume ratio), 1:3 HCl (prepared by mixing 38% hydrochloric acid water solution with water in 1:3 volume ratio), 5 wt % KOH water solution, DI water, acetone, isopropanol, N-methyl-2-pyrrolidone. After the previously described Procedure 1 for 5 minutes, the film shows no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity for all chemicals except KOH solution. After the previously described Procedure 1 for 5 minutes in 5 wt % KOH solution, the film shows slight discoloration, but no visible swelling, cracking, delamination, peeling off, or loss of integrity. After the previously described Procedure 1 for 15 minutes in with 1:1 HCl, acetone, and isopropanol, the film shows no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity. After the previously described Procedure 1 for 15 minutes in 5 wt % KOH solution, the film shows slight discoloration, but no visible swelling, cracking, delamination, peeling off, or loss of integrity.
The films produced with the formulation in this example demonstrate high surface smoothness, as shown by the AFM image in
An exemplary formulation comprises PGMEA as solvent, bisphenol A diglycerolate dimethacrylate monomer, capped zirconia nanocrystals (with 90% by weight to the monomer), 3% of EBecryl P-39 by weight to the monomer, 6% of EBecryl P-115 by weight to the monomer.
The zirconia nanocrystals used in this formulation are capped with two different capping agents, methoxy(triethyleneoxy) propyltrimethoxysilane and 3-methacryloyloxypropyltrimethoxylsilane. The capping process is performed by suspending the as-synthesized nanocrystals in PGMEA, at a loading of 35% by weight calculated based on the wet cake weight of the nanocrystals. While the suspension is being stirred, the first capping agent, methoxy(triethyleneoxy) propyltrimethoxysilane, is added slowly to the suspension. The amount of capping agent used is 5% by weight to the wet cake. The suspension is refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow. After the set reaction time, the reaction is stopped and the suspension is cooled slowly to 100° C. Upon reaching said temperature, the second capping agent, 3-methacryloyloxypropyltrimethoxylsilane, is added slowly to the suspension. The amount of the capping agent used is 60% by weight to the wet cake. The suspension is again refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow. After the second reflux step, the suspension is slowly cooled to 70° C. Upon reaching said temperature, distilled water is added to the suspension slowly. The amount of water used is 5 wt % to the wet cake. The suspension is refluxed at 100° C. for 30 minutes under nitrogen flow. Upon the completion of the allotted heating time, the clear solution is cooled slowly to room temperature. The capped nanocrystals are precipitated out of the capping solvent using heptane. The precipitated nanocrystals are collected using centrifugation. The nanocrystals collected by centrifugation are further cleaned by dispersing it in THF and again re-precipitated out using heptane. The process is repeated twice. The wet cake obtained after the final step is dried under vacuum for 10-12 hours. The capped nanocrystals can then be re-dispersed into dispersion solvent such as PGMEA.
The films are produced with 100° C. pre-bake on a hot plate in air after the films are spin coated, the films are then cured for 120 seconds using a Dymax EC-5000 system with a mercury “H” bulb with ˜73 mW/cm2. Finally the films are subjected to a 10 minutes post bake on a hot plate in air.
The TGA result of the capped nanocrystals of the current example dispersed in PGEMA by themselves with 50% by weight is shown in
The refractive index of the film produced with the formulation in this example is obtained by a Woollam M2000 ellipsometer.
The films produced with the formulation in this example demonstrate high optical transmittance. The solid lines in
The thickness of the film is about 1 micrometer.
The films produced with the formulation in this example demonstrate high thermal resistance. The dotted lines in
The films produced with the formulation in this example demonstrate chemical resistance to 1:1 HCl, 1:3 HCl, 5 wt % KOH water solution, DI water, acetone, isopropanol, and methyl pyrrolidone. After the previously described Procedure 1 for 5 minutes, the film shows no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity for all listed chemicals except KOH solution. After the previously described Procedure 1 for 5 minutes in 5 wt % KOH solution, the film shows slight discoloration, but no visible swelling, cracking, delamination, peeling off, or loss of integrity. After the previously described Procedure 1 for 15 minutes in 1:1 HCl, acetone, and isopropanol, the film shows no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity. After the previously described Procedure 1 for 15 minutes in 5 wt % KOH solution, the film shows slight discoloration, but no visible swelling, cracking, delamination, peeling off, or loss of integrity.
The chemical resistance of the film does not chance when the weight percentage of the P39 is varied from 2% to 5%. The chemical resistance of the film does not chance when the weight percentage of the P115 is varied from 4% to 15%.
When the P39 and P115 in the current example are replaced with 5%, 6%, or 8% Irgacure 184 by weight to the monomer, the chemical resistance remained same except for 5 wt % KOH solution. Film is completely removed after 5 minutes with Procedure 1 in 5% KOH.
The films produced with the formulation in this example demonstrate high surface smoothness, as shown by the AFM image in
After a thermal treatment of 250° C. for 5 minutes on a hotplate in air, the surface roughness did not change significantly, as shown in
An exemplary formulation comprises PGMEA as solvent, bisphenol A diglycerolate dimethacrylate monomer, capped zirconia nanocrystals (with 90% by weight to the monomer), 3% of EBecryl P-39 by weight to the monomer, 6% of EBecryl P-115 by weight to the monomer.
The zirconia nanocrystals used in this formulation are capped with 3-methacryloyloxypropyltrimethoxylsilane. The capping process is performed by suspending the as-synthesized nanocrystals in PGMEA, at a loading of 35%, calculated based on the wet cake weight of the nanocrystals. While the suspension is being stirred, the first capping agent is added slowly to the suspension. The amount of capping agent used is 8 wt % to the wet cake. The suspension is refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow. After the set reaction time, the reaction is stopped heating and the suspension is cooled slowly to 100° C. Upon reaching that temperature, the second capping agent is added slowly to the suspension.
The amount of the capping agent used is 60 wt % to the wet cake. The suspension is again refluxed at the boiling point of the solvent for 40 minutes under nitrogen flow.
Upon the completion of the allotted heating time, the clear solution is cooled slowly to room temperature. The capped nanocrystals are precipitated out of the capping solvent using heptane. The precipitated nanocrystals are collected using centrifuge. The nanocrystals collected by centrifugation are further cleaned by dispersing it in THF and again re-precipitating using heptane. The process is repeated twice. The wet cake obtained after the final step is dried under vacuum for 10-12 hours. The capped nanocrystals can then be re-dispersed into dispersion solvent such as PGMEA.
The films are produced with 100° C. pre-bake on a hot plate in air after the films are spin coated, the films are then cured for 120 seconds using a Dymax EC-5000 system with a mercury “H” bulb with ˜73 mW/cm2. Finally the films are subjected to a minutes post bake on a hot plate in air.
The TGA result of the capped nanocrystals of the current example dispersed in PGEMA by themselves with 50% by weight is shown in
The optical transmittance of the formulation of the current example with 50% of capped nanocrystals by weight is shown in
The refractive index of the film produced with the formulation in this example is obtained by a Woollam M2000 ellipsometer.
The films produced with the formulation in this example demonstrate high optical transmittance. The solid line in
The films produced with the formulation in this example demonstrate high thermal resistance. The dotted line in
The films produced with the formulation in this example demonstrate chemical resistance to DI water, acetone, isopropanol, methyl pyrrolidone. After subjecting to the previously described Procedure 1 for 5 minutes, the film shows no visible discoloration, swelling, cracking, delamination, peeling off, or loss of integrity for all listed chemicals. After the previously described Procedure 1 for 5 minutes 1:1 HCl and 1:3 HCl, the film shows slight discoloration, but no visible swelling, cracking, delamination, peeling off, or loss of integrity. After the previously described Procedure 1 for 5 minutes in 5 wt % KOH solution, the film is completely removed.
The films produced with the formulation in this example demonstrate a pencil hardness up to 8H.using a BYK Gardner PH-5800 pencil harness tester following ASTM test method D3363 (ASTM D3363-05(2011)e2, Standard Test Method for Film Hardness by Pencil Test (24 C, 50% relative humidity).
As shown in
The high index smoothing layer has a refractive index higher than the substrate, typically about 1.5, and equal or lower than the refractive index of the OLED active layer, typically about 1.8. The high index smoothing layer has high surface smoothness, less 1 nm measured by AFM on a 5 μm by 5 μm square. The high index smoothing layer has high optical transmittance, higher than 90% in the visible spectrum. The high index smoothing can withstand at least 200 C in air for 60 minutes with no visible change in appearance, delamination, or cracking. Combined with the scattering layer, the internal light extraction layer improves the light extraction efficiency of the OLED lighting device compared with device with no light extraction layer.
The present application claims benefit of U.S. Provisional Patent Application No. 62/290,941, filed Feb. 4, 2016 and U.S. Provisional Patent Application No. 62/199,845, filed Jul. 31, 2015, the entire contents of each of which is incorporated herein by reference.
This application is partially supported by US Dept. of Energy Small Business Innovation Research (SBIR) Phase I and II Grant No. DE-SC0011295 and US Dept. of Energy Solid State Lighting Grant No. DE-EE0006673.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2016/044243 | 7/27/2016 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62199845 | Jul 2015 | US | |
| 62290941 | Feb 2016 | US |