NiCuZn-BASE FERRITES AND ELECTRONIC PARTS USING THE SAME

Abstract

An NiCuZn-base ferrite of the invention comprises as main components an iron oxide in an amount of 45.0 to 49.0 mol % on Fe2O3 basis, an copper oxide in an amount of 5.0 to 14.0 mol % on CuO basis and a zinc oxide in an amount of 1.0 to 32.0 mol % on ZnO basis with a nickel oxide accounting for the rest mol % on NiO basis. With respect to the main components, a bismuth oxide is contained in an amount of 0.25 exclusive to 0.40% by weight on Bi2O3 basis, and a tin oxide is contained in an amount of 1.00 to 2.50% by weight on SnO2 basis. The invention ensures a leap upward in direct-current bias characteristics.

Description

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a graph indicative of a set of results in Table 1, with initial permeability μi as abscissa and a current Idc (synonymous with I_{dc10% down}) at which the initial permeability μi is 10% down as ordinate.

Claims

1. An NiCuZn-base ferrite comprising as main components an iron oxide in an amount of 45.0 to 49.0 mol % on Fe2O3 basis, an copper oxide in an amount of 5.0 to 14.0 mol % on CuO basis and a zinc oxide in an amount of 1.0 to 32.0 mol % on ZnO basis with a nickel oxide accounting for the rest mol % on NiO basis, wherein, with respect to said main components, a bismuth oxide is contained in an amount of 0.25 exclusive to 0.40% by weight on Bi2O3 basis, and a tin oxide is contained in an amount of 1.00 to 2.50% by weight on SnO2 basis.

2. An electronic part comprising an NiCuZn-base ferrite, wherein said ferrite comprises as main components an iron oxide in an amount of 45.0 to 49.0 mol % on Fe2O3 basis, an copper oxide in an amount of 5.0 to 14.0 mol % on CuO basis and a zinc oxide in an amount of 1.0 to 32.0 mol % on ZnO basis with a nickel oxide accounting for the rest mol % on NiO basis, wherein, with respect to said main components, a bismuth oxide is contained in an amount of 0.25 exclusive to 0.40% by weight on Bi2O3 basis, and a tin oxide is contained in an amount of 1.00 to 2.50% by weight on SnO2 basis.

3. An electronic part as recited in claim 2, wherein said electronic part is a multilayer inductor or LC composite part that includes a coil conductor and a core portion comprising said ferrite, in which said core portion forms a closed magnetic circuit.